Linear low density polyethylene-montmorillonite clay and linear low density polyethylene-organophilic niobate nanocomposites were obtained from dilution of masterbatch with 20% w/w of fillers in the LLDPE matrix by melt intercalation using a twin-screw extruder, obtaining nanocomposites with 1.5% up to 10.0% w/w of filler. In this study mechanical and water vapor and oxygen permeation tests were used to characterize the nanocomposites. In mechanical tests an increase of modulus values and decrease of toughness value by increasing concentration of montmorillonite clay were observed. The behavior of LLDPE-organophilic niobate nanocomposites was similar to LLDPE-montmorillonite clay nanocomposites but softer due to hexaniobate structure. The distribution of the organoclay is more homogeneous than organophilic niobate to concentrations below 10.0% filler using the SEM/FEG. It is possible to see a decrease in the permeability value with increasing concentration of montmorillonite clay for both gases used. In the LLDPE-organophilic niobate nanocomposites a decrease of permeability value occurs followed by an increase of permeability value for both gases used, with increasing concentration of organophilic niobate. Furthermore, it was observed that the polarity of the gas used is an important factor in the diffusion process through the nanocomposite.
Nanocomposite; linear low density polyethylene; montmorillonite clay; potassium hexaniobate; mechanical property and transport property