In the last few years a growing interest in the use of sisal fibers as reinforcement in cement based composites has been observed. However, the main concern for its use is related with the durability of the fibers in the alkaline water of concrete as they can mineralize due to the migration of calcium hydroxide to the fiber lumen and cell walls. In this study, the alkalinity of the matrix was reduced using metakaolin and crushed waste calcined clay bricks as cement replacement. The percentage of cement replacement ranged from 20 to 40% on weight basis. Flexural tests were carried out in the composites after 28 days of cure in water, 135 and 180 days of ageing in the open air and after 94 cycles of wetting and drying. These results indicated that the mixture with cement replacement consumed all calcium hydroxide and kept the toughness over time.
sisal fibers; composites; brick waste; flexural behaviour; accelerated aged