Abstract
The objective of this work was to study the reversion of the strain-induced α-martensite to γ-austenite in three sets of AISI 304, 316-L and 347 stainless steels specimens. To obtaining a high amount of αʹ-martensite (γ → αʹ ), the samples were submitted to 63% reduction in thickness by cold rolling at a temperature of –70 ºC. The reversion of martensite to austenite was made by means of 1-hour isothermal heat treatments between 200 and 1000 ºC (αʹ → γ). Martensite amounts were determined by measurements made with a commercial feritscope. The main analysis of reversion was performed by differential scanning calorimetry (DSC) studies with heating rates of 10, 20 and 40 °C/min. It was determined that under continuous heating the deformation-induced reversion is carried out by a superposition of the diffusional and shear mechanisms, for the heating rates tested. The reversion begins via diffusion-controlled mechanism at temperatures between 414 and 453 °C and ends via non-diffusional mechanism between 557 and 633 °C. On the other hand, the energy per unit mass of the transformation turned out to be between 37 and 63 J/g; and it was found that this depends on the heating rate.
Keywords:
αʹ-martensite; reversion; austenitic stainless steel; calorimetry; isothermal-treatments
1. INTRODUCTION
The austenitic stainless steels of the 300 series are metastable, the γ-austenite phase can transform to ε-martensite and to αʹ-martensite phases due to cold plastic deformation. The most likely phase transformation is from γ-austenite (fcc, paramagnetic) to αʹ-martensite (bcc or bct, ferromagnetic), deformation-induced martensite (DIM). The strain-induced martensitic transformation enhances the work hardening of these stainless steels and affects their ductility. The amount of αʹ-martensite obtained depends on the chemical composition, the process temperature and the strain applied. The austenite can be recovered with subsequent heat treatments. Likewise, the amount of recovered austenite depends on the chemical composition of the steel, temperature, time and rate of heat treatment [1[1] SOHRABI, M.J., NAGHIZADEH, M., MIRZADEH, H., “Deformation-induced martensite in austenitic stainless steels: a review”, Archives of Civil and Mechanical Engineering, v. 20, n. 4, p. 124, Oct. 2020. doi: http://dx.doi.org/10.1007/s43452-020-00130-1.
https://doi.org/10.1007/s43452-020-00130...
, 2[2] NAGHIZADEH, M., MIRZADEH, H., “Microstructural evolutions during reversion annealing of cold-rolled AISI 316 austenitic stainless steel”, Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science, v. 49, n. 6, pp. 2248–2256, Mar. 2018. doi: http://dx.doi.org/10.1007/s11661-018-4583-6.
https://doi.org/10.1007/s11661-018-4583-...
].
The martensite to austenite reversion process in austenitic stainless steels has been studied since the 1970’s and 1980’s, intensively in the Japan in 1990’s and a further academic interest has appeared later 2005–2020; JÄRVENPÄÄ et al. [3[3] JÄRVENPÄÄ, A., JASKARI, M., KISKO, A., et al., “Processing and properties of reversion-treated austenitic stainless steels”, Metals, v. 10, n. 2, pp. 281, Feb. 2020. doi: http://dx.doi.org/10.3390/met10020281.
https://doi.org/10.3390/met10020281...
] present an exhaustive review of works that involve the formation of martensite by cold rolling and the reversion process by annealing. This more recent interest in the reversal transformation of αʹ-martensite has received interest due to the possibility of controlling the microstructure to obtain fine or ultrafine grain size in austenitic stainless steels [4[4] DI SCHINO, A., KENNY, J.M., “Grain refinement strengthening of a micro-crystalline high nitrogen austenitic stainless stee”, Materials Letters, v. 57, n. 12, pp. 1830–1834, Mar. 2003. doi: http://dx.doi.org/10.1016/S0167-577X(02)01076-5.
https://doi.org/10.1016/S0167-577X(02)01...
,5[5] DI SCHINO, A., KENNY, J.M., “Grain size dependence of the fatigue behavior of an ultrafine-grained AISI 304 stainless stee”, Materials Letters, v. 57, n. 21, pp. 3182–3185, Jul. 2003. doi: http://dx.doi.org/10.1016/S0167-577X(03)00021-1.
https://doi.org/10.1016/S0167-577X(03)00...
,6[6] LIU, J., WANG, H., HUANG, L., et al., “Microstructure evolution and mechanical properties of heterogeneous nano/ultrafine-grained austenitic stainless steel prepared by low-temperature rolling and annealing”, Steel Research International, v. 94, n. 3, pp. 2200658, Nov. 2022. doi: http://dx.doi.org/10.1002/srin.202200658.
https://doi.org/10.1002/srin.202200658...
,7[7] NAGHIZADEH, M., MIRZADEH, H., “Effects of grain size on mechanical properties and work-hardening behavior of AISI 304 austenitic stainless steel”, Steel Research International, v. 90, n. 10, pp. 1900153, Jun. 2019. doi: http://dx.doi.org/10.1002/srin.201900153.
https://doi.org/10.1002/srin.201900153...
,8[8] NASIRI, Z., GHAEMIFAR, S., NAGHIZADEH, M., et al., “Thermal mechanisms of grain refinement in steels: a review”, Metals and Materials International, v. 27, n. 7, pp. 2078–2094, Apr. 2021. doi: http://dx.doi.org/10.1007/s12540-020-00700-1.
https://doi.org/10.1007/s12540-020-00700...
–9[9] NAGHIZADEH, M., MIRZADEH, H., “Microstructural evolutions during annealing of plastically deformed AISI 304 austenitic stainless steel: martensite reversion, grain refinement, recrystallization, and grain growth”, Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science, v. 47, n. 8, pp. 4210–4216, Jun. 2016. doi: http://dx.doi.org/10.1007/s11661-016-3589-1.
https://doi.org/10.1007/s11661-016-3589-...
]; or to produce localized areas of austenite in a martensitic structure to achieve good formability while maintaining high mechanical strength [10[10] KHEIRI, S., MIRZADEH, H., NAGHIZADEH, M., “Tailoring the microstructure and mechanical properties of AISI 316L austenitic stainless steel via cold rolling and reversion annealing”, Materials Science and Engineering A, v. 759, pp. 90–96, May. 2019. doi: http://dx.doi.org/10.1016/j.msea.2019.05.028.
https://doi.org/10.1016/j.msea.2019.05.0...
, 11[11] JOHANNSEN, D.L., KYROLAINEN, A., FERREIRA, P.J., “Influence of annealing treatment on the formation of nano/submicron grain size AISI 301 austenitic stainless steel”, Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science, v. 37, n. 8, pp. 2325–2338, Aug. 2006. doi: http://dx.doi.org/10.1007/BF02586207.
https://doi.org/10.1007/BF02586207...
].
The result of the reversion reaction depends on multiple factors: steel grade, deformation that caused the DIM, αʹ percentage before reversion HT, temperature and duration of the annealing, and heating rate. There are basically two types of mechanisms proposed for DIM reversion: diffusional and shear (non-diffusional) [12[12] KNUTSSON, A., HEDSTRÖM, P., ODÉN, M., “Reverse martensitic transformation and resulting microstructure in a cold rolled metastable austenitic stainless steel”, Steel Research International, v. 79, n. 6, pp. 433–439, Jun. 2008. doi: http://dx.doi.org/10.1002/srin.200806149.
https://doi.org/10.1002/srin.200806149...
–14[14] MALLICK, P., TEWARY, N.K., GHOSH, S.K., et al., “Microstructure-tensile property correlation in 304 stainless steel after cold deformation and austenite reversion”, Materials Science and Engineering A, v. 707, pp. 488–500, Nov. 2017. doi: http://dx.doi.org/10.1016/j.msea.2017.09.070.
https://doi.org/10.1016/j.msea.2017.09.0...
]. The occurrence of one or the other depends mainly on the chemical composition of the steel, on the heating rate and on the temperature and duration of the HT (in the case of isothermal treatments) [12[12] KNUTSSON, A., HEDSTRÖM, P., ODÉN, M., “Reverse martensitic transformation and resulting microstructure in a cold rolled metastable austenitic stainless steel”, Steel Research International, v. 79, n. 6, pp. 433–439, Jun. 2008. doi: http://dx.doi.org/10.1002/srin.200806149.
https://doi.org/10.1002/srin.200806149...
, 15[15] LEEM, D.S., LEE, Y., JUN, J., et al., “Amount of retained austenite at room temperature after reverse transformation of martensite to austenite in an Fe-13%Cr-7%Ni-3%Si martensitic stainless steel”, Scripta Materialia, v. 45, n. 7, pp. 767–772, 2001. doi: http://dx.doi.org/10.1016/S1359-6462(01)01093-4.
https://doi.org/10.1016/S1359-6462(01)01...
, 16[16] HAN, J., LEE, Y.K., “The effects of the heating rate on the reverse transformation mechanism and the phase stability of reverted austenite in medium Mn steels”, Acta Materialia, v. 67, pp. 354–361, Feb. 2014. doi: http://dx.doi.org/10.1016/j.actamat.2013.12.038.
https://doi.org/10.1016/j.actamat.2013.1...
]. Two of the parameters obtained from the DSC tests are the start and end temperatures of the reversion from martensite to austenite. These temperatures are identified as As and Af when the mechanism is diffusional, and with primes at the same temperatures when the process is diffusionless ( and ). Figure 1 is a schematic representation of the results obtained in [15[15] LEEM, D.S., LEE, Y., JUN, J., et al., “Amount of retained austenite at room temperature after reverse transformation of martensite to austenite in an Fe-13%Cr-7%Ni-3%Si martensitic stainless steel”, Scripta Materialia, v. 45, n. 7, pp. 767–772, 2001. doi: http://dx.doi.org/10.1016/S1359-6462(01)01093-4.
https://doi.org/10.1016/S1359-6462(01)01...
, 16[16] HAN, J., LEE, Y.K., “The effects of the heating rate on the reverse transformation mechanism and the phase stability of reverted austenite in medium Mn steels”, Acta Materialia, v. 67, pp. 354–361, Feb. 2014. doi: http://dx.doi.org/10.1016/j.actamat.2013.12.038.
https://doi.org/10.1016/j.actamat.2013.1...
] and its purpose, in this case, is to show how the start and end temperatures of the reversion reaction depend on the heating rate. According to these authors, there are two regions, denoted as I and II, separated by a heating rate value that depends on the steel and is represented by the vertical dotted line in Figure 1. For example, in LEEM, et al. [15[15] LEEM, D.S., LEE, Y., JUN, J., et al., “Amount of retained austenite at room temperature after reverse transformation of martensite to austenite in an Fe-13%Cr-7%Ni-3%Si martensitic stainless steel”, Scripta Materialia, v. 45, n. 7, pp. 767–772, 2001. doi: http://dx.doi.org/10.1016/S1359-6462(01)01093-4.
https://doi.org/10.1016/S1359-6462(01)01...
] they find that this separation rate is 10 °C/s (600 °C/min), for a cold rolled steel Fe-13%Cr-7%Ni-3%Si; while in HAN and LEE [16[16] HAN, J., LEE, Y.K., “The effects of the heating rate on the reverse transformation mechanism and the phase stability of reverted austenite in medium Mn steels”, Acta Materialia, v. 67, pp. 354–361, Feb. 2014. doi: http://dx.doi.org/10.1016/j.actamat.2013.12.038.
https://doi.org/10.1016/j.actamat.2013.1...
] for a steel also cold rolled Fe-(5–9%)Mn-0.05%C, the separation heating rate resulted 15 °C/s (900 °C/min). In Region I, reversal start and end temperatures tend to increase as the heating rate increases; this indicates that reversal reaction occurs diffusionally or by an overlap of both mechanisms (diffusional and shear) [12[12] KNUTSSON, A., HEDSTRÖM, P., ODÉN, M., “Reverse martensitic transformation and resulting microstructure in a cold rolled metastable austenitic stainless steel”, Steel Research International, v. 79, n. 6, pp. 433–439, Jun. 2008. doi: http://dx.doi.org/10.1002/srin.200806149.
https://doi.org/10.1002/srin.200806149...
, 15[15] LEEM, D.S., LEE, Y., JUN, J., et al., “Amount of retained austenite at room temperature after reverse transformation of martensite to austenite in an Fe-13%Cr-7%Ni-3%Si martensitic stainless steel”, Scripta Materialia, v. 45, n. 7, pp. 767–772, 2001. doi: http://dx.doi.org/10.1016/S1359-6462(01)01093-4.
https://doi.org/10.1016/S1359-6462(01)01...
–17[17] SHIRAZI, H., MIYAMOTO, G., NEDJAD, S.H., et al., “Microstructural evaluation of austenite reversion during intercritical annealing of Fe-Ni-Mn martensitic stee”, Journal of Alloys and Compounds, v. 577, pp. 572–577, Nov. 2013. doi: http://dx.doi.org/10.1016/j.jallcom.2012.02.015.
https://doi.org/10.1016/j.jallcom.2012.0...
]. Then, in region II it is observed that the temperatures of beginning and ending tend to remain constant, which means that the reversal occurs only via shear mechanism, since at such high heating rates there is no time for diffusion.
αʹ-martensite reversion reaction was studied in a set of cold-rolled AISI 304 steels samples in TAMURA [18[18] TAMURA, I., “Deformation-induced martensitic transformation and transformation-induced plasticity in steels”, Metal Science, v. 16, n. 5, pp. 245–253, 1982. doi: http://dx.doi.org/10.1179/030634582790427316.
https://doi.org/10.1179/0306345827904273...
]. These authors applied thermomagnetic analysis of continuous heating between 100 and 800 °C with speeds of 2, 5 and 10 °C/min and isothermal treatments between 250 °C and 560 °C. Thermomagnetic tests showed As values in the range 433–445 °C and Af in the interval 694–724 °C. They do not identify these reversal start and end temperatures with any particular mechanism; but from observing that the αʹ amount decreases by keeping the temperature constant at 560 °C during one of the continuous heating treatments, they point out the transformation can progress diffusionally once it has started.
The reverse transformation αʹ → γ has also been studied by GUY et al. [19[19] GUY, K.B., BUTLER, E.P., WEST, D.R.F., “Reversion of bcc a′ martensite in Fe-Cr-Ni austenitic stainless steels”, Metal Science, v. 17, n. 4, pp. 167–176, Apr. 1983. doi: http://dx.doi.org/10.1179/030634583790420961.
https://doi.org/10.1179/0306345837904209...
] for two austenitic stainless steels: Fe-18%Cr-8%Ni and Fe-18%Cr-12%Ni. DIM was induced by two methods: rolling at –196 °C, and cooling to –196 °C with a 30 min holding time. Reversion to austenite was carried out by rapid heating using a salt bath. The times and temperatures studied were 2 and 30 min between 200 and 900 °C, and up to 10000 min (167 horas) at 550°C.They determine the values of As and Af: 540 and 650 °C for 8/18; and 470 and 610 °C for 12/18; with an uncertainty of 10°C. They postulate that the reverse transformation between As and Af occurs by shear mechanism and then continues as diffusional.
By thermodynamic analysis TOMIMURA et al. [20[20] TOMIMURA, K., TAKAKI, S., TOKUNAGA, Y., “Reversion mechanism from deformation induced martensite to austenite in metastable austenitic stainless steels”, ISIJ International, v. 31, n. 12, pp. 1431–1437, 1991. doi: http://dx.doi.org/10.2355/isijinternational.31.1431.
https://doi.org/10.2355/isijinternationa...
], analyze the Gibbs free energy change between α-ferrite and γ-austenite (∆Gα−γ) for a ternary Fe-Ni-Cr system as a function of temperature and chemical composition, they study 16Cr-10Ni and 18Cr-9Ni steels. When the value of ∆Gα−γ < 0, γ is more stable than α, which occurs from approximately 450 °C for these steels. The temperature at which ∆Gα−γ = 0, is called by them T0, therefore, T0 ≈ 450 °C. However, for the reversion to be carried out via shear mechanism, an additional driving force is necessary. They experimentally determined that for αʹ-martensite to revert to austenite via shear mechanism, in a 90% cold rolled 16Cr-10Ni steel, the minimum temperature must be 650 °C, they call T1 at this temperature. Reversion treatments of deformation induced αʹ were carried out using a salt bath which enables rapid heating (18000 °C/min) to annealing temperatures between 450 and 750 °C, for 10 s, 10 min or 16.7 h; T1 was determined with these HT. They observed that from 650 °C the reversal process became independent of the annealing time (and the reverse transformation begins by shear mechanism), while at lower temperatures there was a dependence on it. TOMIMURA et al. [20[20] TOMIMURA, K., TAKAKI, S., TOKUNAGA, Y., “Reversion mechanism from deformation induced martensite to austenite in metastable austenitic stainless steels”, ISIJ International, v. 31, n. 12, pp. 1431–1437, 1991. doi: http://dx.doi.org/10.2355/isijinternational.31.1431.
https://doi.org/10.2355/isijinternationa...
], also calculate T1 for 18Cr-9Ni steel: for the reversal to be started via shear mechanism, a temperature of at least 750 °C is needed. If, on the other hand, annealing is carried out at 650 °C, the reversal would be diffusional, since at this temperature the driving force necessary for the shear reversion would not be reached, in 18Cr-9Ni steel.
In this paper the reversion of the strain-induced αʹ-martensite to γ-austenite was studied in three sets of AISI 304, 316L and 347 stainless steels. The objectives of this research were to know the temperature range in which the reversion transformation occurs, as well as to determine the amount of the different phases. For this study, DSC test and reversion isothermal heat treatments were considered. The temperature at the beginning and end of the reversion, the energy of the transformation and the amount of each of the phases present after isothermal reversion treatments were determined. Besides, these assays allowed us to study the reversion mechanisms present during the transformation: diffusional and shear.
2. MATERIALS AND METHODS
2.1. Materials
Three sets of austenitic stainless steels samples were used for this research: AISI 304, AISI 316L and AISI 347, [21[21] SALGADO LARA, J.L., “Estudio de la transformación inversa de la martensita inducida por de formación en aceros inoxidables austeníticos”, M.Sc. Thesis, UNSAM/CNEA, San Martín, Buenos Aires, Argentina, 2019. https://www.cnea.gob.ar/cgi-bin/koha/opac-detail.pl?biblionumber=32993, accessed in January 2024.
https://www.cnea.gob.ar/cgi-bin/koha/opa...
, 22[22] FAVA, J.O., CARABEDO, F.D., SPINOSA, C.C., et al., “Assessment of the amount of deformation induced martensite: a calibration curve for a commercial delta-ferrite gauge”, In: Proceedings of the 12th European Conference on Non-Destructive Testing (ECNDT 2018), Gothenburg, Sweden, June 2018. https://www.ndt.net/?id=22684, accessed in January 2024.
https://www.ndt.net/?id=22684...
]; their Wt % compositions are shown in Table 1. The samples were prepared in the same way as those studied in [23[23] FAVA, J., SPINOSA, C., RUCH, M., et al., “Characterization of reverse martensitic transformation in cold-rolled austenitic 316 stainless steel”, Matéria (Rio de Janeiro), v. 23, n. 2, pp. e12114, 2018. doi: http://dx.doi.org/10.1590/s1517-707620180002.04.
https://doi.org/10.1590/s1517-7076201800...
,24[24] FAVA, J.O FAVA, J.O., CARABEDO, F.D., SPINOSA, C.C., “Evaluación del contenido de martensita en aceros inoxidables austeníticos laminados en frío”, Report CNEA: IN-13-E-151-IM/16, Buenos Aires, Argentina, Comisión Nacional de Energía Atómica, pp. 1–16, 2016.–25[25] RUCH, M.C., FAVA, J.O., SPINOSA, C., et al., “Characterization of cold rolling-induced martensite in austenitic stainless steels”, In: Proceedings of the 19th World Conference on Non-Destructive Testing (WCNDT 2016), Munich, Germany, pp. 13–17, June 2016. https://www.ndt.net/?id=19371, accessed in January 2024.
https://www.ndt.net/?id=19371...
]. First, they were submitted to one-hour austenitization annealing at 1050 °C in vacuum and cooled in air. All specimens were subsequently 63% cold rolled at –70 ºC (203 K) to induce γ → αʹ phase transformation, producing a high proportion of martensite, about 80%. This was the initial condition for the studies of the reversion of martensite. The cold-rolled specimens (65 × 30 × 2.3 mm3) were individually submitted to heat treatments (HT) for the partial reversion of the γ phase. These HT consisted of one hour soaking at temperatures between 200 and 1000 °C. The maximum heating rate for these HT was estimated to be around 1100 °C/min, the lower HT temperature the lower heating rate. In this way, the austenitic γ phase was partially recovered back in different quantities for each specimen, thus obtaining series of two-phase specimens with different martensite contents. The phases present in the specimens were identified by XRD. Concentrations of αʹ-martensite were quantified by measurements made with a commercial ferritoscope FischerÒ Feritscope FMP30, by using a calibration curve presented in FAVA et al. [22[22] FAVA, J.O., CARABEDO, F.D., SPINOSA, C.C., et al., “Assessment of the amount of deformation induced martensite: a calibration curve for a commercial delta-ferrite gauge”, In: Proceedings of the 12th European Conference on Non-Destructive Testing (ECNDT 2018), Gothenburg, Sweden, June 2018. https://www.ndt.net/?id=22684, accessed in January 2024.
https://www.ndt.net/?id=22684...
] and updated in SALGADO [21[21] SALGADO LARA, J.L., “Estudio de la transformación inversa de la martensita inducida por de formación en aceros inoxidables austeníticos”, M.Sc. Thesis, UNSAM/CNEA, San Martín, Buenos Aires, Argentina, 2019. https://www.cnea.gob.ar/cgi-bin/koha/opac-detail.pl?biblionumber=32993, accessed in January 2024.
https://www.cnea.gob.ar/cgi-bin/koha/opa...
]; this calibration curve converts the measurements of Wt % δ-ferrite into Wt % of αʹ-martensite.
2.2. Md30
Austenitic stainless steels are susceptible to martensite transformation when they are subjected to cryogenic treatments below a certain temperature called MS, at this temperature the driving force reaches the critical value , which is the minimum required for spontaneous martensitic transformation to happen. However, if an adequate mechanical driving force Uʹ is applied to austenite, martensitic transformation can occur at a temperature T1, higher than MS; since . When a mechanical driving force is involved in transformation, it is classified into two types: stress-assisted martensitic transformation and deformation-induced martensitic transformation. The first involves elastic deformations and occurs at low temperatures; (but above MS). The second takes place in the case of plastic deformations and higher temperatures, e.g., room temperature [1[1] SOHRABI, M.J., NAGHIZADEH, M., MIRZADEH, H., “Deformation-induced martensite in austenitic stainless steels: a review”, Archives of Civil and Mechanical Engineering, v. 20, n. 4, p. 124, Oct. 2020. doi: http://dx.doi.org/10.1007/s43452-020-00130-1.
https://doi.org/10.1007/s43452-020-00130...
, 26[26] OLSON, G.B., COHEN, M., “A mechanism for the strain-induced nucleation of martensitic transformations”, Journal of the Less Common Metals, v. 28, n. 1, pp. 107–118, Jul. 1972. doi: http://dx.doi.org/10.1016/0022-5088(72)90173-7.
https://doi.org/10.1016/0022-5088(72)901...
, 27[27] SOLEIMANI, M., KALHOR, A., MIRZADEH, H., “Transformation-induced plasticity (TRIP) in advanced steels: a review”, Materials Science and Engineering A, v. 795, pp. 140023, Aug. 2020. doi: http://dx.doi.org/10.1016/j.msea.2020.140023.
https://doi.org/10.1016/j.msea.2020.1400...
]. In the latter, martensitic transformation is related to energetically favorable nucleation sites generated by plastic deformation [26[26] OLSON, G.B., COHEN, M., “A mechanism for the strain-induced nucleation of martensitic transformations”, Journal of the Less Common Metals, v. 28, n. 1, pp. 107–118, Jul. 1972. doi: http://dx.doi.org/10.1016/0022-5088(72)90173-7.
https://doi.org/10.1016/0022-5088(72)901...
]. In the case of austenitic stainless steels, it has been shown that the DIM nucleation sites are located at the intersections of two shear bands by the aid of piled-up dislocations and at obstacles such as grain boundaries and twinning boundaries [18[18] TAMURA, I., “Deformation-induced martensitic transformation and transformation-induced plasticity in steels”, Metal Science, v. 16, n. 5, pp. 245–253, 1982. doi: http://dx.doi.org/10.1179/030634582790427316.
https://doi.org/10.1179/0306345827904273...
, 26[26] OLSON, G.B., COHEN, M., “A mechanism for the strain-induced nucleation of martensitic transformations”, Journal of the Less Common Metals, v. 28, n. 1, pp. 107–118, Jul. 1972. doi: http://dx.doi.org/10.1016/0022-5088(72)90173-7.
https://doi.org/10.1016/0022-5088(72)901...
, 28[28] DAS, A., SIVAPRASAD, S., GHOSH, M., et al., “Morphologies and characteristics of deformation induced martensite during tensile deformation of 304 LN stainless steel”, Materials Science and Engineering A, v. 486, n. 1-2, pp. 283-286, Jul. 2008. doi: http://dx.doi.org/10.1016/j.msea.2007.09.005.
https://doi.org/10.1016/j.msea.2007.09.0...
,29[29] MANGONON, P.L., THOMAS, G., “The martensite phases in 304 stainless steel”, Metallurgical Transactions, v. 1, n. 6, pp. 1577–1586, Jun. 1970. doi: http://dx.doi.org/10.1007/BF02642003.
https://doi.org/10.1007/BF02642003...
–30[30] SUZUKI, T., KOJIMA, H., SUZUKI, K., et al., “An experimental study of the martensite nucleation and growth in 18/8 stainless steel”, Acta Metallurgica, v. 25, n. 10, pp. 1151–1162, Oct. 1977. doi: http://dx.doi.org/10.1016/0001-6160(77)90202-4.
https://doi.org/10.1016/0001-6160(77)902...
]. Temperature is crucial in deformation-induced transformation, just as it is for spontaneous transformation. Transformation is enhanced by the decrease in temperature [31[31] HECKER, M.S., STOUT, M.G., STAUDHAMMER, K.P., et al., “Effect of strain state and strain rate on deformation-induced transformation in 304 stainless steels: Part I. Magnetic measurements and mechanical behavior”, Metallurgical Transactions. A, Physical Metallurgy and Materials Science, v. 13, n. 4, pp. 619–626, Apr. 1982. doi: http://dx.doi.org/10.1007/BF02644427.
https://doi.org/10.1007/BF02644427...
, 32[32] HEDSTRÖM, H., “Deformation and martensitic phase transformation in stainless steels”, D.Sc. Thesis, Luleå University of Technology, Luleå, Sweden, 2007.]; in HECKER et al. [31[31] HECKER, M.S., STOUT, M.G., STAUDHAMMER, K.P., et al., “Effect of strain state and strain rate on deformation-induced transformation in 304 stainless steels: Part I. Magnetic measurements and mechanical behavior”, Metallurgical Transactions. A, Physical Metallurgy and Materials Science, v. 13, n. 4, pp. 619–626, Apr. 1982. doi: http://dx.doi.org/10.1007/BF02644427.
https://doi.org/10.1007/BF02644427...
] the authors analyze results of the amount of DIM as a function of the traction strain in a 304 stainless steel and observe an increase in DIM as the temperature decreases. For example, with a true strain of 0.40: at 22 °C it forms around 10% volume fraction of αʹ, at 10 °C 43%, at 0 °C almost 60%, at –30 °C around 80%; and for –30 °C, –70 °C and –188 °C the amount of αʹ appears to saturate at about 85%, for the highest true strains. Since the transformation occurs above MS, the stability of these steels is classified by other temperatures. One of them is Md , which is the limit temperature above which there will be no martensitic transformation induced by deformation due to the application of plastic deformations. However, as this temperature is difficult to measure, ANGEL [33[33] ANGEL, T., “Formation of martensite in austenitic stainless stee”, Journal of the Iron and Steel Institute, n. May, pp. 165–174, 1954.] established another one: Md30 (known also as Md(30/50)). It is the temperature for which 50% martensite is formed by applying 30% true strain, in a tensile test. Md30 is a good measure of metastable stainless steels stability and is determined by the chemical composition, as stated in the empirical ANGEL formula: Md30 (°C) = 413 – 13.7(%Cr) − 9.5(%Ni) − 8.1(%Mn) − 18.5(%Mo) − 9.2(%Si) − 462(%[C+N ]). In this equation the elementary fractions are expressed in weight percent, and it indicates that the higher the proportion of alloying elements, the more they improve the stability of austenite. The resulting Md30 for the studied steels are presented in Table 2. Because AISI 347 steel has the highest Md30, it is the one with the greatest tendency to form martensite when subjected to deformation at a temperature below Md and AISI 316L is the one with the least tendency. In addition to the effect of chemical composition, some authors [1[1] SOHRABI, M.J., NAGHIZADEH, M., MIRZADEH, H., “Deformation-induced martensite in austenitic stainless steels: a review”, Archives of Civil and Mechanical Engineering, v. 20, n. 4, p. 124, Oct. 2020. doi: http://dx.doi.org/10.1007/s43452-020-00130-1.
https://doi.org/10.1007/s43452-020-00130...
, 8[8] NASIRI, Z., GHAEMIFAR, S., NAGHIZADEH, M., et al., “Thermal mechanisms of grain refinement in steels: a review”, Metals and Materials International, v. 27, n. 7, pp. 2078–2094, Apr. 2021. doi: http://dx.doi.org/10.1007/s12540-020-00700-1.
https://doi.org/10.1007/s12540-020-00700...
] also consider the effects of initial grain size by applying NOHARA’s formula NOHARA et al. [34[34] NOHARA, K., ONO, Y., OHASHI, N., “Composition and grain size dependencies of strain-induced martensitic transformation in metastable austenitic stainless steels”, Tetsu To Hagane, v. 63, n. 5, pp. 772–782, Apr. 1977. doi: http://dx.doi.org/10.2355/tetsutohagane1955.63.5_772.
https://doi.org/10.2355/tetsutohagane195...
]; but here ANGEL’s formula was used because all the samples had already been laminated before starting this study, i.e., the initial grain size was not measured before rolling.
2.3. Differential scanning calorimetry
For differential scanning calorimetry studies, the samples that had received the HT at the lowest temperature, 200 °C, were selected. These samples correspond to the first three points in Figure 2 for each of the studied steels; and according to the bibliography the reversal transformation starts between ∼400−800 °C [35[35] SANTOS, T.F.A., ANDRADE, M.S., “Avaliação dilatométrica da reversão das martensitas induzidas por deformação em um aço inoxidável austenítico do tipo ABNT 304”, Matéria (Rio de Janeiro), v. 13, n. 4, pp. 587–596, 2008. doi: http://dx.doi.org/10.1590/S1517-70762008000400003.
https://doi.org/10.1590/S1517-7076200800...
–37[37] GRAHAM, C., LORENZ, B., CITRIN, M., et al., “Reversion of martensite in 304 stainless steel studied by dilatometry and calorimetry.”, Journal of Material Sciences and Ingeneering, v. 7, pp. 434–437, 2018.]. A Setaram LabSys Evo differential scanning calorimeter was used.
Thermal cycles from 50 °C to 1400 °C were programmed with heating rates of 10, 20 and 40 °C/min for all samples, and controlled cooling. Two tests were carried out for each sample and rate. The tests were performed in argon atmosphere with a flow of 50 ml/min. The data obtained was processed using the software provided by the calorimeter manufacturer, called “CALISTO Processing”. From the analysis of the results the following were extracted: temperature at the beginning of the transformation, temperature at the end of the transformation, and energy of the transformation per unit mass of αʹ-martensite transformed, for details on data processing see [21[21] SALGADO LARA, J.L., “Estudio de la transformación inversa de la martensita inducida por de formación en aceros inoxidables austeníticos”, M.Sc. Thesis, UNSAM/CNEA, San Martín, Buenos Aires, Argentina, 2019. https://www.cnea.gob.ar/cgi-bin/koha/opac-detail.pl?biblionumber=32993, accessed in January 2024.
https://www.cnea.gob.ar/cgi-bin/koha/opa...
].
3. RESULTS
3.1. Reversion heat treatments
The results of the reversion HT are shown in Figure 2. As expected, according to the Md30 values, Table 2: AISI 347 steel was the one that formed the highest amount of deformation induced martensite; the amount of αʹ formed by 304 steel is slightly less than that of 347; while the initial concentration of αʹ for 316L steel is approximately half the values corresponding to the other two steels.
For steels 304 and 347, between 300 °C and 400 °C, a slight increase in the amount of DIM was observed, during the reversion HT, as shown in Figure 2. Both steels reach the maximum αʹ concentration around 400 °C: with an increase from 81% to 83% for 304 and from 86% to 88% for 347. This result appears to match the previous peak to the DIM reversal reaction peak in the thermograms obtained from the DSC tests, discussed in the next section. The increase in the amount of αʹ is one of the hardening mechanisms postulated for cold-formed austenitic stainless steels and then heat-treated in static baths between 250 °C and 450 °C and it is called annealing induced martensitic transformation [1[1] SOHRABI, M.J., NAGHIZADEH, M., MIRZADEH, H., “Deformation-induced martensite in austenitic stainless steels: a review”, Archives of Civil and Mechanical Engineering, v. 20, n. 4, p. 124, Oct. 2020. doi: http://dx.doi.org/10.1007/s43452-020-00130-1.
https://doi.org/10.1007/s43452-020-00130...
, 19[19] GUY, K.B., BUTLER, E.P., WEST, D.R.F., “Reversion of bcc a′ martensite in Fe-Cr-Ni austenitic stainless steels”, Metal Science, v. 17, n. 4, pp. 167–176, Apr. 1983. doi: http://dx.doi.org/10.1179/030634583790420961.
https://doi.org/10.1179/0306345837904209...
, 36[36] LEE, S., CHOI, J.Y., NAM, W.J., “Hardening behavior of a 304 stainless steel containing deformation-induced martensite during static strain aging”, Materials Transactions, v. 50, n. 4, pp. 926–299, Mar. 2009. doi: http://dx.doi.org/10.2320/matertrans.MRP2008416.
https://doi.org/10.2320/matertrans.MRP20...
, 38[38] TAVARES, S.S.M., FRUCHART, D., MIRAGLIA, S., “A magnetic study of the reversion of martensite α′ in a 304 stainless steel”, Journal of Alloys and Compounds, v. 307, n. 1-2, pp. 311–317, Jul. 2000. doi: http://dx.doi.org/10.1016/S0925-8388(00)00874-4.
https://doi.org/10.1016/S0925-8388(00)00...
, 39[39] MANGONON, P.L., THOMAS, G., “Structure and properties of thermal-mechanically treated 304 stainless steel”, Metallurgical Transactions, v. 1, n. 6, pp. 1587–1594, Jun. 1970. http://dx.doi.org/10.1007/BF02642004.
http://dx.doi.org/10.1007/BF02642004...
].
3.2. DSC tests
In the DSC tests, all thermograms showed three peaks, Figure 3 highlights them for AISI 347 sample: the endothermic ones (peaks 2) correspond to the reversal transformation of the martensite. As a general observation, it can be said that for the different heating rates a shift of the peaks towards higher temperatures was observed as the heating rate increased.
Zoom of the DSC curves for AISI 347 sample (heat treated at 200 °C). Shift of the peaks towards higher temperatures as the heating rate is increasing.
Literature indicates that the endothermic peaks, analogous to the peaks denoted as 2 in the thermograms of Figure 3, correspond to the reversion reaction αʹ → γ [12[12] KNUTSSON, A., HEDSTRÖM, P., ODÉN, M., “Reverse martensitic transformation and resulting microstructure in a cold rolled metastable austenitic stainless steel”, Steel Research International, v. 79, n. 6, pp. 433–439, Jun. 2008. doi: http://dx.doi.org/10.1002/srin.200806149.
https://doi.org/10.1002/srin.200806149...
, 36[36] LEE, S., CHOI, J.Y., NAM, W.J., “Hardening behavior of a 304 stainless steel containing deformation-induced martensite during static strain aging”, Materials Transactions, v. 50, n. 4, pp. 926–299, Mar. 2009. doi: http://dx.doi.org/10.2320/matertrans.MRP2008416.
https://doi.org/10.2320/matertrans.MRP20...
, 37[37] GRAHAM, C., LORENZ, B., CITRIN, M., et al., “Reversion of martensite in 304 stainless steel studied by dilatometry and calorimetry.”, Journal of Material Sciences and Ingeneering, v. 7, pp. 434–437, 2018., 40[40] CIOS, G., TOKARSKI, T., ŻYWCZAK, A., et al., “The investigation of strain-induced martensite reverse transformation in AISI 304 austenitic stainless steel”, Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science, v. 48A, n. 10, pp. 4999–5008, Jul. 2017. doi: http://dx.doi.org/10.1007/s11661-017-4228-1.
https://doi.org/10.1007/s11661-017-4228-...
]. These endothermic peaks were the ones that were studied in detail and quantitatively in this research. Also, these studies were compared with the results of the static HT with which the samples were prepared, Figure 2. Table 3 contains the temperatures at which the endothermic peaks presented their corresponding minimum. For all DSC tests, at all the peaks corresponding to the reversal reaction the peak start temperature was identified as diffusional, As, and the ending temperature as non-diffusional, , as defined in the Introduction. Those As and temperatures were analyzed as a function of the heating rate. As one of the objectives of this work was the study of the reversal reaction of the DIM; for the exothermic peaks, analogous to peaks 1 and 3 of the thermogram of Figure 3, only a brief analysis was carried out based on the consulted bibliography.
Temperatures where endothermic peaks present the minimum, for each sample and heating rate.
Figure 4 plots the start temperatures of the endothermic reaction (As) and the temperature of its completion () as a function of the heating rates of the DSC tests; Table 4 shows these temperatures. As the heating rate increases, so do the αʹ-martensite reversal start and end temperatures, and therefore the samples should be in region I of Figure 1.
Diffusional reversion start temperatures (As, endothermic peak start temperature) and shear reversion finishing temperatures (, endothermic peak finishing temperature) vs heating rates.
3.3 Transformation energies
Energies per unit mass of αʹ depending on the heating rate for the DSC tests of this work are presented in Figure 5 and Table 5. In these energies it is not possible to distinguish between energy of the diffusional mechanism and energy of the shear mechanism; and it was observed that the energy per unit mass decreases as the heating rate increases.
4. DISCUSSION
4.1. Diffusion-controlled and shear mechanisms
According to the results, we can assume that the reverse martensitic transformation is initiated by diffusion (for this reason we denote the starting temperatures as As). For the three steels, in the conditions of the DSC tests used and considering [12[12] KNUTSSON, A., HEDSTRÖM, P., ODÉN, M., “Reverse martensitic transformation and resulting microstructure in a cold rolled metastable austenitic stainless steel”, Steel Research International, v. 79, n. 6, pp. 433–439, Jun. 2008. doi: http://dx.doi.org/10.1002/srin.200806149.
https://doi.org/10.1002/srin.200806149...
], it can be estimated that the reversion occurred through a superposition of both diffusional and shear mechanisms. This fact is also supported by LEE et al. [41[41] LEE, S.J., PARK, Y., LEE, Y., “Reverse transformation mechanism of martensite to austenite in a metastable austenitic alloy”, Materials Science and Engineering A, v. 515, n. 1–2, pp. 32–37, 2009. doi: http://dx.doi.org/10.1016/j.msea.2009.02.010.
https://doi.org/10.1016/j.msea.2009.02.0...
], where they state that in continuous heating the shear reversal takes place regardless of the heating rate. Therefore, there would be a certain fraction of αʹ-martensite that would be reverting to austenite via a non-diffusional mechanism. That is, for the steels and conditions studied here, diffusion-controlled αʹ reversal begins at the onset of endothermic peaks (between 414 and 453 °C, As temperatures in Table 4), and shear reversion would be activated at higher temperatures [20[20] TOMIMURA, K., TAKAKI, S., TOKUNAGA, Y., “Reversion mechanism from deformation induced martensite to austenite in metastable austenitic stainless steels”, ISIJ International, v. 31, n. 12, pp. 1431–1437, 1991. doi: http://dx.doi.org/10.2355/isijinternational.31.1431.
https://doi.org/10.2355/isijinternationa...
]. However, these temperatures cannot be determined in the experimental conditions of our DSC test, that is, under these conditions the diffusion and shear mechanisms cannot be separated [12[12] KNUTSSON, A., HEDSTRÖM, P., ODÉN, M., “Reverse martensitic transformation and resulting microstructure in a cold rolled metastable austenitic stainless steel”, Steel Research International, v. 79, n. 6, pp. 433–439, Jun. 2008. doi: http://dx.doi.org/10.1002/srin.200806149.
https://doi.org/10.1002/srin.200806149...
]. From bibliographic analysis, it is also assumed that the shear mechanism ends when the endothermic peak ends (between 557 and 633 °C, temperatures in Table 4) [12[12] KNUTSSON, A., HEDSTRÖM, P., ODÉN, M., “Reverse martensitic transformation and resulting microstructure in a cold rolled metastable austenitic stainless steel”, Steel Research International, v. 79, n. 6, pp. 433–439, Jun. 2008. doi: http://dx.doi.org/10.1002/srin.200806149.
https://doi.org/10.1002/srin.200806149...
, 20[20] TOMIMURA, K., TAKAKI, S., TOKUNAGA, Y., “Reversion mechanism from deformation induced martensite to austenite in metastable austenitic stainless steels”, ISIJ International, v. 31, n. 12, pp. 1431–1437, 1991. doi: http://dx.doi.org/10.2355/isijinternational.31.1431.
https://doi.org/10.2355/isijinternationa...
]. In addition, the completion temperature of diffusional reversion (Af) could not be determined under the conditions tested; but it would be at a temperature higher than .
Peak 1, prior to reverse martensitic transformation peak, could be caused by the formation of a small additional amount of αʹ-martensite [36[36] LEE, S., CHOI, J.Y., NAM, W.J., “Hardening behavior of a 304 stainless steel containing deformation-induced martensite during static strain aging”, Materials Transactions, v. 50, n. 4, pp. 926–299, Mar. 2009. doi: http://dx.doi.org/10.2320/matertrans.MRP2008416.
https://doi.org/10.2320/matertrans.MRP20...
, 38[38] TAVARES, S.S.M., FRUCHART, D., MIRAGLIA, S., “A magnetic study of the reversion of martensite α′ in a 304 stainless steel”, Journal of Alloys and Compounds, v. 307, n. 1-2, pp. 311–317, Jul. 2000. doi: http://dx.doi.org/10.1016/S0925-8388(00)00874-4.
https://doi.org/10.1016/S0925-8388(00)00...
, 39[39] MANGONON, P.L., THOMAS, G., “Structure and properties of thermal-mechanically treated 304 stainless steel”, Metallurgical Transactions, v. 1, n. 6, pp. 1587–1594, Jun. 1970. http://dx.doi.org/10.1007/BF02642004.
http://dx.doi.org/10.1007/BF02642004...
]; which is consistent with the αʹ Wt % measurements made on samples of AISI 304 and 347 steels, see Figure 2 and Figure 3. During the reversion HT of AISI 316L steel, this increase in the amount of αʹ-martensite was not observed, Figure 2. This could be because AISI 316L steel has the highest Ni/Cr rate, of the three steels, and Ni tends to stabilize the γ-phase; or the greater thermal stability of AISI 316L could also be due to the Mo content of this steel [42[42] NAGHIZADEH, M., MIRZADEH, H., “Elucidating the effect of alloying elements on the behaviour of austenitic stainless steels at elevated temperatures”, Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science, v. 47, n. 12, pp. 5698–5703, Sep. 2016. doi: http://dx.doi.org/10.1007/s11661-016-3764-4.
https://doi.org/10.1007/s11661-016-3764-...
]. This lower tendency to form martensite also appears in its Md30 value, the lowest for the three steels, Table 2. However peak 1 appears; there is no agreed explanation for the increase in the αʹ amount in the temperature range 300–400 °C [13[13] GHOSH, S.K., JHA, S., MALLICK, P., et al., “Influence of mechanical deformation and annealing on kinetics of martensite in a stainless steel”, Materials and Manufacturing Processes, v. 28, n. 3, pp. 249–255, Mar. 2013. doi: http://dx.doi.org/10.1080/10426914.2012.667893.
https://doi.org/10.1080/10426914.2012.66...
, 19[19] GUY, K.B., BUTLER, E.P., WEST, D.R.F., “Reversion of bcc a′ martensite in Fe-Cr-Ni austenitic stainless steels”, Metal Science, v. 17, n. 4, pp. 167–176, Apr. 1983. doi: http://dx.doi.org/10.1179/030634583790420961.
https://doi.org/10.1179/0306345837904209...
, 36[36] LEE, S., CHOI, J.Y., NAM, W.J., “Hardening behavior of a 304 stainless steel containing deformation-induced martensite during static strain aging”, Materials Transactions, v. 50, n. 4, pp. 926–299, Mar. 2009. doi: http://dx.doi.org/10.2320/matertrans.MRP2008416.
https://doi.org/10.2320/matertrans.MRP20...
, 38[38] TAVARES, S.S.M., FRUCHART, D., MIRAGLIA, S., “A magnetic study of the reversion of martensite α′ in a 304 stainless steel”, Journal of Alloys and Compounds, v. 307, n. 1-2, pp. 311–317, Jul. 2000. doi: http://dx.doi.org/10.1016/S0925-8388(00)00874-4.
https://doi.org/10.1016/S0925-8388(00)00...
, 39[39] MANGONON, P.L., THOMAS, G., “Structure and properties of thermal-mechanically treated 304 stainless steel”, Metallurgical Transactions, v. 1, n. 6, pp. 1587–1594, Jun. 1970. http://dx.doi.org/10.1007/BF02642004.
http://dx.doi.org/10.1007/BF02642004...
]: nucleation of new αʹ particles, growth of the existing αʹ laths, precipitation of carbides which locally decrease the Cr concentration and increase the MS , or to segregation and conglomeration of carbon atoms.
Exothermic peak 3 is most likely to be the recovery of the reverse austenitic structure [12[12] KNUTSSON, A., HEDSTRÖM, P., ODÉN, M., “Reverse martensitic transformation and resulting microstructure in a cold rolled metastable austenitic stainless steel”, Steel Research International, v. 79, n. 6, pp. 433–439, Jun. 2008. doi: http://dx.doi.org/10.1002/srin.200806149.
https://doi.org/10.1002/srin.200806149...
], i.e., by a decrease in defect density. But according to studies done on AISI 304 steels [43[43] HAEßNER, F., PLAUT, R.L., PADILHA, A.F. “Separation of static recrystallization and reverse transformation of deformation-induced martensite in an austenitic stainless steel by calorimetric measurements”, ISIJ International, v. 43, n. 9, pp. 1472–1474, Jan. 2003. doi: http://dx.doi.org/10.2355/isijinternational.43.1472.
https://doi.org/10.2355/isijinternationa...
] and on AISI 301 [12[12] KNUTSSON, A., HEDSTRÖM, P., ODÉN, M., “Reverse martensitic transformation and resulting microstructure in a cold rolled metastable austenitic stainless steel”, Steel Research International, v. 79, n. 6, pp. 433–439, Jun. 2008. doi: http://dx.doi.org/10.1002/srin.200806149.
https://doi.org/10.1002/srin.200806149...
], it could also correspond to the formation of carbides; although our steels have a low C content and in the case of the 347 steel studied, it is stabilized by the formation of Nb carbides.
The hardening behavior of a 40% cold rolled 304 stainless steel containing DIM during static strain ageing was investigated by LEE et al. [36[36] LEE, S., CHOI, J.Y., NAM, W.J., “Hardening behavior of a 304 stainless steel containing deformation-induced martensite during static strain aging”, Materials Transactions, v. 50, n. 4, pp. 926–299, Mar. 2009. doi: http://dx.doi.org/10.2320/matertrans.MRP2008416.
https://doi.org/10.2320/matertrans.MRP20...
]. Particularly, they examined the effect of aging temperature on strength and the amount of αʹ-martensite. The aging treatments were performed on cold rolled stainless steel sheets in a heated salt bath in the temperature range of 200–700 °C for an hour; they also performed DSC thermal analysis with heating rates between 2 and 16 °C/min. They find that the amount of αʹ-martensite is increased for the sample aged at 450 °C from 45.5% to 50%; this increase is well known and as mentioned, was also recorded in this work, Figure 2. In the DSC tests, the reversal αʹ peak is around 500 °C and they postulate that reversion begins after 450°C, so they relate this value to the maximum αʹ-martensite concentration at that same temperature observed in aging treatments. They also find an endothermic peak prior to the exothermic peak corresponding to the αʹ reversion, between 350 °C and 450 °C. Authors say that there is no clear explanation of the mechanism corresponding to this peak and that it could be related to one or more microstructural changes, such as additional formation of αʹ-martensite or recovery of αʹ-martensite (defects removal). But they also relate this peak to the diffusion of C and Cr atoms into austenite to form fine carbide precipitates which would locally increase MS and promote the further αʹ-martensite formation.
Following TOMIMURA et al. [20[20] TOMIMURA, K., TAKAKI, S., TOKUNAGA, Y., “Reversion mechanism from deformation induced martensite to austenite in metastable austenitic stainless steels”, ISIJ International, v. 31, n. 12, pp. 1431–1437, 1991. doi: http://dx.doi.org/10.2355/isijinternational.31.1431.
https://doi.org/10.2355/isijinternationa...
], the temperature at which the isothermal treatment is carried out on the steels would affect the reversion mechanism in the following way: if the temperature of the isothermal treatment is higher than T0 but less than T1, see Introduction, the reversion will be diffusional and if the isothermal treatment is carried out at a temperature higher than T1, the reversion will occur via the non-diffusional mechanism. These conclusions could be applied to our AISI 304, 316L and 347 steels; but it must be kept in mind that in TOMIMURA et al. [20[20] TOMIMURA, K., TAKAKI, S., TOKUNAGA, Y., “Reversion mechanism from deformation induced martensite to austenite in metastable austenitic stainless steels”, ISIJ International, v. 31, n. 12, pp. 1431–1437, 1991. doi: http://dx.doi.org/10.2355/isijinternational.31.1431.
https://doi.org/10.2355/isijinternationa...
] the presence of other alloy elements is not considered and also our heating rates involved in isothermal treatments (1100 °C/min maximum) and in DSC tests (10, 20 and 40 °C/min) are lower than those of isothermal treatments in salt bath (18000 °C/min). What we want to show with the discussion contained in this paragraph is the sequence of the reversal mechanisms: it is initiated by the diffusion mechanism and then, at higher temperatures, the shear mechanism is activated.
In our isothermal treatments, lasting 1 hour, reversal begins around 400 °C, and the greatest decrease in Wt % martensite is for temperatures above 750 °C, Figure 2. For DSC tests, the As temperatures found are close to 450 °C, Table 4; but the maximum value of the reversal completion temperatures is 633 °C (, Table 4). We can say that as DSC heating rates are slow (10, 20 and 40 °C/min) with respect to heating rate in salt bath (18000 °C/min) the samples will have enough time for reversion to begin via diffusional mechanism, when they pass through the temperature range between T0 and T1. These temperatures were initially unknown for the steels studied here. As it was mentioned, in continuous heating conditions (as DSC tests) they are called As and respectively and depend on the heating rate. Then, when in each DSC test the corresponding temperature is exceeded, it will initiate the reversal via shear mechanism; but temperature could not be determined under the conditions of the tests carried out here. As already mentioned, the completion of the endothermic peak is associated with the ending temperature of the non-diffusional mechanism (). In KNUTSSON et al. [12[12] KNUTSSON, A., HEDSTRÖM, P., ODÉN, M., “Reverse martensitic transformation and resulting microstructure in a cold rolled metastable austenitic stainless steel”, Steel Research International, v. 79, n. 6, pp. 433–439, Jun. 2008. doi: http://dx.doi.org/10.1002/srin.200806149.
https://doi.org/10.1002/srin.200806149...
] for a DSC test of a 61% cold worked AISI 301 steel, the authors observed that the reversion peak ended at ∼600 °C, and this temperature was assigned to . This assignment for was supported by the fact that the amount of αʹ-martensite obtained was approximately the same for 1 hour isothermal treatments at temperatures of 600, 650, and 700 °C. Additionally, they observed that samples treated at 650 °C had 8 Wt % of αʹ-martensite, both for 6 min annealing and 1 hour annealing; but if the annealing times were increased to 90 hours, the amount decreased to 3 Wt %. Therefore, they concluded that for long times the reversal was completed in a diffusional way. For 700 °C and 800 °C isothermal HT, Figure 2, αʹ-martensite concentrations remain almost constant, this would indicate that temperature would be between 600 and 700 °C, which roughly coincides with the results presented in Table 4.
Therefore, for the samples studied here, reversion begins as diffusional at As temperature, then at a temperature the shear mechanism begins and overlaps the diffusional one. This overlap exists until the temperature, where the endothermic peaks of the DSC tests ends; and finally, the reversal would be completed by diffusion up to Af temperature. Af and could be determined in the DSC tests, Table 4; but and Af could not be determined under the conditions of this work.
4.2. Transformation energies
In a DSC test at 20 °C/min heating rate, HAEßNER et al. [43[43] HAEßNER, F., PLAUT, R.L., PADILHA, A.F. “Separation of static recrystallization and reverse transformation of deformation-induced martensite in an austenitic stainless steel by calorimetric measurements”, ISIJ International, v. 43, n. 9, pp. 1472–1474, Jan. 2003. doi: http://dx.doi.org/10.2355/isijinternational.43.1472.
https://doi.org/10.2355/isijinternationa...
], for a AISI 304 60% cold rolled steel and 12 Wt % of αʹ-martensite, the authors found that the energy of the endothermic peak, located between 470 and 550 °C, was 8 J/g. This value is very low compared to the values of 43 or 40 J/g obtained for AISI 304 steel heated to 20 °C/min, Table 5. A value of ∼ J/g for martensite formation energy in an Fe-18.5Cr-8.7Ni alloy was reported in TOMIMURA et al. [20[20] TOMIMURA, K., TAKAKI, S., TOKUNAGA, Y., “Reversion mechanism from deformation induced martensite to austenite in metastable austenitic stainless steels”, ISIJ International, v. 31, n. 12, pp. 1431–1437, 1991. doi: http://dx.doi.org/10.2355/isijinternational.31.1431.
https://doi.org/10.2355/isijinternationa...
] (when it is formed in a temperature range between 20 and –117 °C) (formation and reversion energies of martensite should be the same, but opposite in sign for a given material). This value is close to the results obtained for the 40 °C/min heating rate, between 37 and 43 J/g depending on the steel, Table 5; and the steel that comes closest to that energy value is AISI 304 (18.8Cr-9.2Ni).
In GRAHAM et al. [37[37] GRAHAM, C., LORENZ, B., CITRIN, M., et al., “Reversion of martensite in 304 stainless steel studied by dilatometry and calorimetry.”, Journal of Material Sciences and Ingeneering, v. 7, pp. 434–437, 2018.] AISI 304 samples drawn at 0 °C with different degrees of deformation were studied. Using dilatometry, they determined that the reversion transformation was between 425 and 625 °C, when the samples were heated at 1 °C/min. They also determined the reversion energy by means of DSC tests at a heating rate of 50 °C/min and it turned out to be 33 J/g and 40 J/g for samples with 60 and 70 Wt % of αʹ-martensite, respectively. These energy values are like that obtained in our DSC tests for AISI 304 heated at 40 and 20 °C/min.
According to GHOSH et al. [13[13] GHOSH, S.K., JHA, S., MALLICK, P., et al., “Influence of mechanical deformation and annealing on kinetics of martensite in a stainless steel”, Materials and Manufacturing Processes, v. 28, n. 3, pp. 249–255, Mar. 2013. doi: http://dx.doi.org/10.1080/10426914.2012.667893.
https://doi.org/10.1080/10426914.2012.66...
], for an AISI 304 steel, rolled at 0 °C and 25% reduction, DSC tests at a heating rate of 20 °C/min, showed two endothermic peaks, which indicated that the reversion reaction was divided into two stages, according to the authors. The first peak appears between 300 and 400 °C and has an energy of 36 J/g. The authors associate it with the dissolution of martensite and crystalline defects in small regions along the austenite/martensite interface. Then, between 400 and 450 °C, they record an interruption of the reversion due to the diffusion of iron and nickel through the austenite/martensite interface that seemed to stabilize the rest of the martensite. Finally, the second endothermic peak appears between 450 and 550 °C with an energy of 38 J/g. This second energy value is close to the values 43 and 40 J/g observed in the AISI 304 steel heated at 20 °C/min; both temperature ranges are also comparable, 430 and 580 °C, Table 5. It should be mentioned that only in GHOSH et al. [13[13] GHOSH, S.K., JHA, S., MALLICK, P., et al., “Influence of mechanical deformation and annealing on kinetics of martensite in a stainless steel”, Materials and Manufacturing Processes, v. 28, n. 3, pp. 249–255, Mar. 2013. doi: http://dx.doi.org/10.1080/10426914.2012.667893.
https://doi.org/10.1080/10426914.2012.66...
] two endothermic peaks were found.
Figure 5 shows that as heating rates increase, the energy associated with reversion reaction decreases. Therefore, the total martensite reverted percentage at the end of the endothermic reaction (diffusionaly and non-diffusionaly) would be expected to be lower at higher heating rates, and that the remaining martensite has to be reversed only via diffusional mechanism at temperatures greater than that of the end of the endothermic reaction. This reduction in energy could be caused by the decrease in the reversal percentage corresponding to the diffusional mechanism, in the temperature range where the endothermic peak is located. Possibly at very high heating rates the energy would become constant, as would the start and end temperatures of the reversion peak reaction, which become constant for very high heating rates [15–17] where the reversion became completely non-diffusional. Thus, if the energy of the reversal were to become constant for very high heating rates, its value could also be associated with the energy corresponding to the shear reversal exclusively.
5. CONCLUSIONS
Through DSC tests it was estimated that, in continuous heating, most of the reversion occurs during the endothermic peaks: reversion begins via diffusional mechanism at temperature As (between 414 and 453 °C), and the end temperature of the endothermic peak would be the finishing temperature of the shear mechanism (between 557 and 633 °C). However, the endothermic peak completion temperature does not indicate that the reversal is complete, since the reversion is completed by means of diffusional mechanism when a temperature is reached. With the tests carried out, it was not possible to determine the reversal start temperature due to shear mechanism cutting , but based on the literature it is estimated that this temperature falls between As and . The latter indicates that between As and and the two reversal mechanisms overlap. In addition, under the conditions of the tests of this work, the ending temperature of the diffusion reversion mechanism Af could not be determined either.
For 1 hour isothermal treatments the reversion begins at temperatures higher than 400 °C and the greatest amount of martensite reverts between 450 ºC and 700 ºC. In AISI 304 and 347 steels, a small additional amount of martensite was formed in the isothermal HT carried out at 400 °C. This phenomenon is reported in the bibliography and occurs at temperatures prior to and close to the temperature of the start of the reversion.
The energy per unit mass of αʹ for the strain-induced reverse transformation was determined to be in the range 37-63 J/g. For all the steels studied, it was observed that this energy per unit mass decreases as the heating rate increases.
6. ACKNOWLEDGMENTS
This paper was supported by the National Atomic Energy Commission (CNEA) of Argentina. Special thanks to Phase Transformations Division, CNEA, for DSC tests.
7. BIBLIOGRAPHY
-
[1]SOHRABI, M.J., NAGHIZADEH, M., MIRZADEH, H., “Deformation-induced martensite in austenitic stainless steels: a review”, Archives of Civil and Mechanical Engineering, v. 20, n. 4, p. 124, Oct. 2020. doi: http://dx.doi.org/10.1007/s43452-020-00130-1.
» https://doi.org/10.1007/s43452-020-00130-1 -
[2]NAGHIZADEH, M., MIRZADEH, H., “Microstructural evolutions during reversion annealing of cold-rolled AISI 316 austenitic stainless steel”, Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science, v. 49, n. 6, pp. 2248–2256, Mar. 2018. doi: http://dx.doi.org/10.1007/s11661-018-4583-6.
» https://doi.org/10.1007/s11661-018-4583-6 -
[3]JÄRVENPÄÄ, A., JASKARI, M., KISKO, A., et al, “Processing and properties of reversion-treated austenitic stainless steels”, Metals, v. 10, n. 2, pp. 281, Feb. 2020. doi: http://dx.doi.org/10.3390/met10020281.
» https://doi.org/10.3390/met10020281 -
[4]DI SCHINO, A., KENNY, J.M., “Grain refinement strengthening of a micro-crystalline high nitrogen austenitic stainless stee”, Materials Letters, v. 57, n. 12, pp. 1830–1834, Mar. 2003. doi: http://dx.doi.org/10.1016/S0167-577X(02)01076-5.
» https://doi.org/10.1016/S0167-577X(02)01076-5 -
[5]DI SCHINO, A., KENNY, J.M., “Grain size dependence of the fatigue behavior of an ultrafine-grained AISI 304 stainless stee”, Materials Letters, v. 57, n. 21, pp. 3182–3185, Jul. 2003. doi: http://dx.doi.org/10.1016/S0167-577X(03)00021-1.
» https://doi.org/10.1016/S0167-577X(03)00021-1 -
[6]LIU, J., WANG, H., HUANG, L., et al, “Microstructure evolution and mechanical properties of heterogeneous nano/ultrafine-grained austenitic stainless steel prepared by low-temperature rolling and annealing”, Steel Research International, v. 94, n. 3, pp. 2200658, Nov. 2022. doi: http://dx.doi.org/10.1002/srin.202200658.
» https://doi.org/10.1002/srin.202200658 -
[7]NAGHIZADEH, M., MIRZADEH, H., “Effects of grain size on mechanical properties and work-hardening behavior of AISI 304 austenitic stainless steel”, Steel Research International, v. 90, n. 10, pp. 1900153, Jun. 2019. doi: http://dx.doi.org/10.1002/srin.201900153.
» https://doi.org/10.1002/srin.201900153 -
[8]NASIRI, Z., GHAEMIFAR, S., NAGHIZADEH, M., et al, “Thermal mechanisms of grain refinement in steels: a review”, Metals and Materials International, v. 27, n. 7, pp. 2078–2094, Apr. 2021. doi: http://dx.doi.org/10.1007/s12540-020-00700-1.
» https://doi.org/10.1007/s12540-020-00700-1 -
[9]NAGHIZADEH, M., MIRZADEH, H., “Microstructural evolutions during annealing of plastically deformed AISI 304 austenitic stainless steel: martensite reversion, grain refinement, recrystallization, and grain growth”, Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science, v. 47, n. 8, pp. 4210–4216, Jun. 2016. doi: http://dx.doi.org/10.1007/s11661-016-3589-1.
» https://doi.org/10.1007/s11661-016-3589-1 -
[10]KHEIRI, S., MIRZADEH, H., NAGHIZADEH, M., “Tailoring the microstructure and mechanical properties of AISI 316L austenitic stainless steel via cold rolling and reversion annealing”, Materials Science and Engineering A, v. 759, pp. 90–96, May. 2019. doi: http://dx.doi.org/10.1016/j.msea.2019.05.028.
» https://doi.org/10.1016/j.msea.2019.05.028 -
[11]JOHANNSEN, D.L., KYROLAINEN, A., FERREIRA, P.J., “Influence of annealing treatment on the formation of nano/submicron grain size AISI 301 austenitic stainless steel”, Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science, v. 37, n. 8, pp. 2325–2338, Aug. 2006. doi: http://dx.doi.org/10.1007/BF02586207.
» https://doi.org/10.1007/BF02586207 -
[12]KNUTSSON, A., HEDSTRÖM, P., ODÉN, M., “Reverse martensitic transformation and resulting microstructure in a cold rolled metastable austenitic stainless steel”, Steel Research International, v. 79, n. 6, pp. 433–439, Jun. 2008. doi: http://dx.doi.org/10.1002/srin.200806149.
» https://doi.org/10.1002/srin.200806149 -
[13]GHOSH, S.K., JHA, S., MALLICK, P., et al, “Influence of mechanical deformation and annealing on kinetics of martensite in a stainless steel”, Materials and Manufacturing Processes, v. 28, n. 3, pp. 249–255, Mar. 2013. doi: http://dx.doi.org/10.1080/10426914.2012.667893.
» https://doi.org/10.1080/10426914.2012.667893 -
[14]MALLICK, P., TEWARY, N.K., GHOSH, S.K., et al, “Microstructure-tensile property correlation in 304 stainless steel after cold deformation and austenite reversion”, Materials Science and Engineering A, v. 707, pp. 488–500, Nov. 2017. doi: http://dx.doi.org/10.1016/j.msea.2017.09.070.
» https://doi.org/10.1016/j.msea.2017.09.070 -
[15]LEEM, D.S., LEE, Y., JUN, J., et al, “Amount of retained austenite at room temperature after reverse transformation of martensite to austenite in an Fe-13%Cr-7%Ni-3%Si martensitic stainless steel”, Scripta Materialia, v. 45, n. 7, pp. 767–772, 2001. doi: http://dx.doi.org/10.1016/S1359-6462(01)01093-4.
» https://doi.org/10.1016/S1359-6462(01)01093-4 -
[16]HAN, J., LEE, Y.K., “The effects of the heating rate on the reverse transformation mechanism and the phase stability of reverted austenite in medium Mn steels”, Acta Materialia, v. 67, pp. 354–361, Feb. 2014. doi: http://dx.doi.org/10.1016/j.actamat.2013.12.038.
» https://doi.org/10.1016/j.actamat.2013.12.038 -
[17]SHIRAZI, H., MIYAMOTO, G., NEDJAD, S.H., et al, “Microstructural evaluation of austenite reversion during intercritical annealing of Fe-Ni-Mn martensitic stee”, Journal of Alloys and Compounds, v. 577, pp. 572–577, Nov. 2013. doi: http://dx.doi.org/10.1016/j.jallcom.2012.02.015.
» https://doi.org/10.1016/j.jallcom.2012.02.015 -
[18]TAMURA, I., “Deformation-induced martensitic transformation and transformation-induced plasticity in steels”, Metal Science, v. 16, n. 5, pp. 245–253, 1982. doi: http://dx.doi.org/10.1179/030634582790427316.
» https://doi.org/10.1179/030634582790427316 -
[19]GUY, K.B., BUTLER, E.P., WEST, D.R.F., “Reversion of bcc a′ martensite in Fe-Cr-Ni austenitic stainless steels”, Metal Science, v. 17, n. 4, pp. 167–176, Apr. 1983. doi: http://dx.doi.org/10.1179/030634583790420961.
» https://doi.org/10.1179/030634583790420961 -
[20]TOMIMURA, K., TAKAKI, S., TOKUNAGA, Y., “Reversion mechanism from deformation induced martensite to austenite in metastable austenitic stainless steels”, ISIJ International, v. 31, n. 12, pp. 1431–1437, 1991. doi: http://dx.doi.org/10.2355/isijinternational.31.1431.
» https://doi.org/10.2355/isijinternational.31.1431 -
[21]SALGADO LARA, J.L., “Estudio de la transformación inversa de la martensita inducida por de formación en aceros inoxidables austeníticos”, M.Sc. Thesis, UNSAM/CNEA, San Martín, Buenos Aires, Argentina, 2019. https://www.cnea.gob.ar/cgi-bin/koha/opac-detail.pl?biblionumber=32993, accessed in January 2024.
» https://www.cnea.gob.ar/cgi-bin/koha/opac-detail.pl?biblionumber=32993 -
[22]FAVA, J.O., CARABEDO, F.D., SPINOSA, C.C., et al, “Assessment of the amount of deformation induced martensite: a calibration curve for a commercial delta-ferrite gauge”, In: Proceedings of the 12th European Conference on Non-Destructive Testing (ECNDT 2018), Gothenburg, Sweden, June 2018. https://www.ndt.net/?id=22684, accessed in January 2024.
» https://www.ndt.net/?id=22684 -
[23]FAVA, J., SPINOSA, C., RUCH, M., et al, “Characterization of reverse martensitic transformation in cold-rolled austenitic 316 stainless steel”, Matéria (Rio de Janeiro), v. 23, n. 2, pp. e12114, 2018. doi: http://dx.doi.org/10.1590/s1517-707620180002.04.
» https://doi.org/10.1590/s1517-707620180002.04 -
[24]FAVA, J.O FAVA, J.O., CARABEDO, F.D., SPINOSA, C.C., “Evaluación del contenido de martensita en aceros inoxidables austeníticos laminados en frío”, Report CNEA: IN-13-E-151-IM/16, Buenos Aires, Argentina, Comisión Nacional de Energía Atómica, pp. 1–16, 2016.
-
[25]RUCH, M.C., FAVA, J.O., SPINOSA, C., et al, “Characterization of cold rolling-induced martensite in austenitic stainless steels”, In: Proceedings of the 19th World Conference on Non-Destructive Testing (WCNDT 2016), Munich, Germany, pp. 13–17, June 2016. https://www.ndt.net/?id=19371, accessed in January 2024.
» https://www.ndt.net/?id=19371 -
[26]OLSON, G.B., COHEN, M., “A mechanism for the strain-induced nucleation of martensitic transformations”, Journal of the Less Common Metals, v. 28, n. 1, pp. 107–118, Jul. 1972. doi: http://dx.doi.org/10.1016/0022-5088(72)90173-7.
» https://doi.org/10.1016/0022-5088(72)90173-7 -
[27]SOLEIMANI, M., KALHOR, A., MIRZADEH, H., “Transformation-induced plasticity (TRIP) in advanced steels: a review”, Materials Science and Engineering A, v. 795, pp. 140023, Aug. 2020. doi: http://dx.doi.org/10.1016/j.msea.2020.140023.
» https://doi.org/10.1016/j.msea.2020.140023 -
[28]DAS, A., SIVAPRASAD, S., GHOSH, M., et al, “Morphologies and characteristics of deformation induced martensite during tensile deformation of 304 LN stainless steel”, Materials Science and Engineering A, v. 486, n. 1-2, pp. 283-286, Jul. 2008. doi: http://dx.doi.org/10.1016/j.msea.2007.09.005.
» https://doi.org/10.1016/j.msea.2007.09.005 -
[29]MANGONON, P.L., THOMAS, G., “The martensite phases in 304 stainless steel”, Metallurgical Transactions, v. 1, n. 6, pp. 1577–1586, Jun. 1970. doi: http://dx.doi.org/10.1007/BF02642003.
» https://doi.org/10.1007/BF02642003 -
[30]SUZUKI, T., KOJIMA, H., SUZUKI, K., et al, “An experimental study of the martensite nucleation and growth in 18/8 stainless steel”, Acta Metallurgica, v. 25, n. 10, pp. 1151–1162, Oct. 1977. doi: http://dx.doi.org/10.1016/0001-6160(77)90202-4.
» https://doi.org/10.1016/0001-6160(77)90202-4 -
[31]HECKER, M.S., STOUT, M.G., STAUDHAMMER, K.P., et al, “Effect of strain state and strain rate on deformation-induced transformation in 304 stainless steels: Part I. Magnetic measurements and mechanical behavior”, Metallurgical Transactions. A, Physical Metallurgy and Materials Science, v. 13, n. 4, pp. 619–626, Apr. 1982. doi: http://dx.doi.org/10.1007/BF02644427.
» https://doi.org/10.1007/BF02644427 -
[32]HEDSTRÖM, H., “Deformation and martensitic phase transformation in stainless steels”, D.Sc. Thesis, Luleå University of Technology, Luleå, Sweden, 2007.
-
[33]ANGEL, T., “Formation of martensite in austenitic stainless stee”, Journal of the Iron and Steel Institute, n. May, pp. 165–174, 1954.
-
[34]NOHARA, K., ONO, Y., OHASHI, N., “Composition and grain size dependencies of strain-induced martensitic transformation in metastable austenitic stainless steels”, Tetsu To Hagane, v. 63, n. 5, pp. 772–782, Apr. 1977. doi: http://dx.doi.org/10.2355/tetsutohagane1955.63.5_772.
» https://doi.org/10.2355/tetsutohagane1955.63.5_772 -
[35]SANTOS, T.F.A., ANDRADE, M.S., “Avaliação dilatométrica da reversão das martensitas induzidas por deformação em um aço inoxidável austenítico do tipo ABNT 304”, Matéria (Rio de Janeiro), v. 13, n. 4, pp. 587–596, 2008. doi: http://dx.doi.org/10.1590/S1517-70762008000400003.
» https://doi.org/10.1590/S1517-70762008000400003 -
[36]LEE, S., CHOI, J.Y., NAM, W.J., “Hardening behavior of a 304 stainless steel containing deformation-induced martensite during static strain aging”, Materials Transactions, v. 50, n. 4, pp. 926–299, Mar. 2009. doi: http://dx.doi.org/10.2320/matertrans.MRP2008416.
» https://doi.org/10.2320/matertrans.MRP2008416 -
[37]GRAHAM, C., LORENZ, B., CITRIN, M., et al, “Reversion of martensite in 304 stainless steel studied by dilatometry and calorimetry.”, Journal of Material Sciences and Ingeneering, v. 7, pp. 434–437, 2018.
-
[38]TAVARES, S.S.M., FRUCHART, D., MIRAGLIA, S., “A magnetic study of the reversion of martensite α′ in a 304 stainless steel”, Journal of Alloys and Compounds, v. 307, n. 1-2, pp. 311–317, Jul. 2000. doi: http://dx.doi.org/10.1016/S0925-8388(00)00874-4.
» https://doi.org/10.1016/S0925-8388(00)00874-4 -
[39]MANGONON, P.L., THOMAS, G., “Structure and properties of thermal-mechanically treated 304 stainless steel”, Metallurgical Transactions, v. 1, n. 6, pp. 1587–1594, Jun. 1970. http://dx.doi.org/10.1007/BF02642004
» http://dx.doi.org/10.1007/BF02642004 -
[40]CIOS, G., TOKARSKI, T., ŻYWCZAK, A., et al, “The investigation of strain-induced martensite reverse transformation in AISI 304 austenitic stainless steel”, Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science, v. 48A, n. 10, pp. 4999–5008, Jul. 2017. doi: http://dx.doi.org/10.1007/s11661-017-4228-1.
» https://doi.org/10.1007/s11661-017-4228-1 -
[41]LEE, S.J., PARK, Y., LEE, Y., “Reverse transformation mechanism of martensite to austenite in a metastable austenitic alloy”, Materials Science and Engineering A, v. 515, n. 1–2, pp. 32–37, 2009. doi: http://dx.doi.org/10.1016/j.msea.2009.02.010.
» https://doi.org/10.1016/j.msea.2009.02.010 -
[42]NAGHIZADEH, M., MIRZADEH, H., “Elucidating the effect of alloying elements on the behaviour of austenitic stainless steels at elevated temperatures”, Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science, v. 47, n. 12, pp. 5698–5703, Sep. 2016. doi: http://dx.doi.org/10.1007/s11661-016-3764-4.
» https://doi.org/10.1007/s11661-016-3764-4 -
[43]HAEßNER, F., PLAUT, R.L., PADILHA, A.F. “Separation of static recrystallization and reverse transformation of deformation-induced martensite in an austenitic stainless steel by calorimetric measurements”, ISIJ International, v. 43, n. 9, pp. 1472–1474, Jan. 2003. doi: http://dx.doi.org/10.2355/isijinternational.43.1472.
» https://doi.org/10.2355/isijinternational.43.1472
Publication Dates
-
Publication in this collection
12 Feb 2024 -
Date of issue
2024
History
-
Received
25 July 2023 -
Accepted
07 Nov 2023