Grout for structural masonry: study for the use of ceramic residue mixing

Ehrenbring, Hinoel Zamis; Tutikian, Bernardo Fonseca; Medeiros, Daniel Reis

Acessibilidade / Reportar erro

Brasil

Español English

sumário « anterior atual seguinte »

Sumário

Articles • Matéria (Rio J.) 22 (3) • 2017 • https://doi.org/10.1590/S1517-707620170003.0199 copy

Grout for structural masonry: study for the use of ceramic residue mixing

Authorship SCIMAGO INSTITUTIONS RANKINGS

ABSTRACT

This study aims to evaluate the development of grouts, a material that is widely used in the Brazilian civil construction sector, applying recycled ceramic aggregates in different ratios. For that purpose, multiple substitution percentages of rough natural aggregates for the ceramic block residue were studied considering the results of loss of fresh state slump-flow, axial compressive strength, modulus of elasticity, ultrasonic wave transmission velocity, and capillary absorption. The results showed a compressive strength decrease of the grouts, mainly 30% and 50% ratios. On the other hand, all of them met the normative parameters for this application, indicating the potential application of this alternative material in civil construction.

Keywords:
Grouting; Loss of workability; Recycled ceramic aggregates

ENSAIOS	NORMA DE ENSAIO	RESULTADO
Massa específica	ABNT NBR NM 23 [36]	2,74 g/cm³
Tempo de início de pega	ABNT NBR NM 65 [37]	368 min
Tempo de fim de pega	ABNT NBR NM 65 [37]	503 min
Finura na peneira n° 200	ABNT NBR 11579 [38]	0,30%

PENEIRA (mm)	AREIA FINA
PENEIRA (mm)	RETIDA (%)	ACUMULADA (%)
6,3	0	0
4,8	0	0
2,4	0	0
1,2	0,1	0,1
0,6	0,6	0,7
0,3	22,4	23,1
0,15	72,4	95,5
Fundo (<0,15)	4,5	100
Módulo de finura	1,2
Dimensão máxima	0,6 mm

PENEIRA (mm)	BRITA 0
PENEIRA (mm)	RETIDA (%)	ACUMULADA (%)
25,0	0	0
19,0	0	0
12,5	0	0
9,5	0,6	0,6
6,3	29,1	29,7
4,8	32,7	62,4
Fundo (<4,8)	37,6	100
Módulo de finura	6,3
Dimensão máxima	9,5 mm

ABERTURA DA PENEIRA	MATERIAL RETIDO (%)	MATERIAL ACUMULADO (%)
12,5 mm	55%	55%
9,5 mm	11%	66%
6,3 mm	11%	77%
4,8 mm	5%	82%
2,4 mm	7%	89%
1,2 mm	3%	92%
0,6 mm	3%	95%
0,3 mm	2%	96%
0,15 mm	2%	98%
< 0,15 mm	2%	100%

TRAÇO	TEOR DE SUBSTITUIÇÃO (%)	CIM. (KG)	AREIA (KG)	BRITA (KG)	RCC (KG)	ABATIM. (MM)	A/C
Rico	0	13,40	18,76	17,42	0	190	0,45
	10	13,40	18,76	15,68	1,74	205	0,40
	30	13,40	18,76	12,19	5,22	190	0,54
	50	13,40	18,76	8,71	8,71	220	0,54
Interm.	0	10,20	22,45	17,35	0	230	0,59
	10	10,20	22,45	15,62	1,73	195	0,57
	30	10,20	22,45	12,15	5,20	215	0,65
	50	10,20	22,45	8,67	8,67	215	0,67
Pobre	0	8,24	24,72	17,30		185	0,64
	10	8,24	24,72	15,57	1,73	200	0,69
	30	8,24	24,72	12,11	5,19	205	0,78
	50	8,24	24,72	8,65	8,65	185	0,81

	RICO (%)				INTERMEDIÁRIO (%)				POBRE (%)
	0	10	30	50	0	10	30	50	0	10	30	50
Abatimento (mm)	190	205	190	220	230	195	215	215	185	200	205	185
Relação a/c	0,45	0,40	0,54	0,54	0,59	0,57	0,65	0,67	0,64	0,69	0,78	0,81

TEOR DE SUBSTITUIÇÃO	RESISTÊNCIA À COMPRESSÃO (MPa)
	1 DIA	7 DIAS	28 DIAS	63 DIAS	1 DIA	7 DIAS	28 DIAS	63 DIAS	1 DIA	7 DIAS	28 DIAS	63 DIAS
	RICO				INTERMEDIÁRIO				POBRE
0	7,9	22,2	32,0	44,9	4,0	14,4	24,3	30,0	3,9	11,6	20,7	24,9
10	8,1	19,9	30,2	34,6	7,0	18,1	26,3	29,8	3,9	11,8	16,6	22,9
30	6,5	16,8	27,3	32,3	4,0	13,1	20,7	22,5	2,8	9,2	14,4	19,3
50	8,3	20,6	25,6	36,7	5,7	15,7	22,5	25,7	2,9	10,4	18,9	22,9

TEOR DE SUBSTITUIÇÃO (%)	EC (GPa)	V (m/s)	C(g/cm²)	EC (GPa)	V (m/s)	C(g/cm²)	EC (GPa)	V (m/s)	C(g/cm²)
TEOR DE SUBSTITUIÇÃO (%)	RICO			INTERMEDIÁRIO			POBRE
0	6,00	4348	0,72	5,48	4255	0,85	3,40	4184	0,90
10	5,58	4219	0,70	5,28	4211	0,81	2,73	4124	0,95
30	3,74	4107	0,79	3,18	4049	0,89	2,56	3945	0,95
50	3,85	4049	0,66	3,82	4057	0,84	2,88	3884	0,99

Laboratório de Hidrogênio, Coppe - Universidade Federal do Rio de Janeiro, em cooperação com a Associação Brasileira do Hidrogênio, ABH2 Av. Moniz Aragão, 207, 21941-594, Rio de Janeiro, RJ, Brasil, Tel: +55 (21) 3938-8791 - Rio de Janeiro - RJ - Brazil