Abstract
Introduction
Imediate dentin sealing (IDS) is a procedure where a dentin adhesive is applied on the exposed dentin surfaces after its preparation to indirect restorations and before impression procedures.
Objective
The objective of the study was to evaluate the effectiveness of the immediate dentin sealing technique (SDI) in adhesive resistance, using the Universal adhesive system (Single Bond Universal, 3M ESPE).
Material and method
30 bovine incisors were selected and divided into 3 groups (n = 10): Groups S (Without Immediate Dentin Seal), SDI (Immediate Dentin Seal with Adhesive) and SDIF (Immediate Dentin Seal with Adhesive + Flow Resin). The vestibular surface was worn with diamond-tipped conical tips until superficial dentin exposure. The smear layer simulation was carried out with # 600 granulation sandpaper for 30s and the dentin was treated according to the respective group. To simulate the temporary restoration, blocks of bisacrylic resin were cemented with zinc oxide cement. After 7 days, the final cementation of resin blocks with dual resin cement (RelyX ARC, 3M ESPE) was carried out. The specimens were sectioned to obtain 1mm2 fillets and subjected to the microtensile test.
Result
The ANOVA test showed a statistical difference between the groups evaluated. Higher values of bond strength were observed for the SDIF group (23.53 MPa), differing statistically from Group S (17,65 MPa) (p = 0.008). The SDI group showed an average bond strength (19.25 MPa), which did not differ statistically from groups S (p = 0.68) and SDIF (p = 0.07).
Conclusion
Based on the results, it is recommended the immediate dental sealing technique with adhesive + flow resin in dental exposures caused in the dental preparation for indirect restorations.
Descriptors:
Dentin hybridization; adhesives; cementation