Abstract

Ag-Sn/CeO2 catalysts were synthesized by the co-precipitation method with different Ag-Sn wt.% loadings and were tested for the oxidation of CO. The catalysts were characterized by powder X-ray diffractometry (XRD), scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM), energy dispersive X-ray spectroscopy (EDS), and selected area electron diffraction (SAED) techniques. UV-Vis measurements were carried out to elucidate the ionic states of the silver particles, and the temperature-programmed reduction (TPR) technique was employed to check the reduction temperature of the catalyst supported on CeO2. There are peaks for silver crystallites in the X-ray diffraction patterns and the presence of SnO was not well evidenced by the XRD technique due to sintering inside the 3D array channels of CeO2 during the calcination process. The Ag-Sn/CeO2 (4%) catalyst was the most efficient and exhibited 100% CO oxidation at 100 ºC due to small particle size and strong electronic interaction with the SnO/CeO2 support.

co-precipitation; crystallites; energy dispersive X-ray spectroscopy; reducibility


Introduction

Silver oxide nanoparticles (NPs) are considered excellent catalysts for many catalytic reactions such as formaldehyde synthesis, NOx abatement, ethylene epoxidation, oxidative coupling of methane, selective oxidation of ammonia and ethylene glycol, partial oxidation of benzyl alcohol and oxidation of styrene and carbon monoxide.1Dai, W. L.; Yong, C.; Ren, L. P.; Yang, X. L.; Xu, J. H.; Li, H. X.; He, H. Y.; Fan, K. N.; J. Catal. 2004, 228, 80.

Shi, C.; Cheng, M. J.; Qu, Z. P.; Bao, X. H.; J. Mol. Catal. A: Chem. 2005, 235, 35.

Lee, J. H.; Schmieg, S. J.; Oh, S. H.; Appl. Catal., A 2008, 342, 78.

van Santen, R. A.; Kuipers, H. P. C. E.; Adv. Catal. 1987, 35, 265.

Zhang, L.; Zhang, C. B.; He, H.; J. Catal. 2009, 261, 101.

Nagy, A. J.; Mestl, G.; Schlögl, R.; J. Catal. 1999, 188, 58.

Yamamoto, R.; Sawayama, Y.; Shibahara, H.; Ichihashi, Y.; Nishiyama, S.; Tsuruya, S.; J. Catal. 2005, 234, 308.

Purcar, V.; Donescu, D.; Petcu, C.; Luque, R.; Macquarrie, D. J.;Appl. Catal., A 2009, 363, 122.

Magaev, O. V.; Knyazev, A. S.; Vodyankina, O. V.; Dorofeeva, N. V.; Salanov, A. N.; Boronin, A. I.; Appl. Catal., A 2008, 344, 142.

10 Frey, K.; Iablokov, V.; Melaet, G.; Guczi, L.; Kruse, N.; Catal. Lett. 2008, 124, 74.

11 Song, K. S.; Kang, S.; Sim, S. D.; Catal. Lett. 1997, 49, 65.

12 Xu, R.; Wang, X.; Wang, D. S.; Zhou, K. B.; Li, Y. D.; J. Catal. 2006, 237, 426.

13 Wang, A. Q.; Liu, J. H.; Lim, S. D.; Lin, T. S.; Mou, C. Y.; J. Catal. 2005, 233, 186.

14 Wang, A. Q.; Hsieh, Y. P.; Chen, Y. F.; Mou, C. Y.; J. Catal. 2006, 237, 197.

15 Liu, X. Y.; Wang, A. Q.; Yang, X. F.; Zhang, T.; Mou, C. Y.; Su, D. S.; Li, J.; Chem. Mater.2009, 21, 410.

16 Liu, H. Y.; Ma, D.; Blackley, R. A.; Zhou, W. Z.; Bao, X. H.; Chem. Commun. 2008, 23, 2677.
-1717 Zhang, X.; Qu, Z.; Li, X.; Wen, M.; Quan, X.; Ma, D.; Wu, J.; Sep. Purif. Technol. 2010, 72, 395. The catalytic performance of silver NPs largely depends on surface area, surface texture, synthetic methods and reaction conditions. It has been reported by researchers that pretreatment of silver oxide in O2 at high temperature results in the formation of subsurface oxygen which activates the catalyst.1818 Bao, X.; Muhler, M.; Pettinger, B.; Schlögl, R.; Ertl, G.; Catal. Lett. 1993, 22, 215.

19 Bao, X.; Muhler, M.; Pettinger, B.; Schlögl, R.; Ertl, G.; Catal. Lett. 1995, 32, 185.

20 Schubert, H.; Tegtmeyer, U.; Herein, D.; Bao, X.; Muhler, M.; Schlögl, R.; Catal. Lett. 1995, 33, 305.

21 Su, D. S.; Jacob, T.; Hansen, T. W.; Wang, D.; Schlögl, R.; Freitag, B.; Kujawa, S.; Angew. Chem., Int. Ed.2008, 47, 5005.

22 Qu, Z. P.; Cheng, M. J.; Huang, W. X.; Bao, X. H.; J. Catal. 2005, 229, 446.
-2323 Christopher, J. B.; Charles, A. M.; J. Catal. 1999, 184, 224. There are endorsements that Ag0 species is an excellent catalyst below 140 ºC, while above 140 ºC, Ag+ is much active for CO oxidation.5Zhang, L.; Zhang, C. B.; He, H.; J. Catal. 2009, 261, 101. CO catalytic oxidation has been extensively studied for its widespread applications in the subject of environmental protection, closed cycle CO laser and selective oxidation of CO in reformer gases for fuel cell applications, etc.2424 Gardner, S. D.; Hoflund, G. B.; Upchurch, B. T.; Schryer, D. R.; Kielin, E. J.; Schryer, J.; J. Catal.1991, 129, 114.

25 Gardner, S.; Hoflund, G.; Schryer, D.; Schryer, J.; Upchurch, B.; Kielin, E.; Langmuir 1991, 7, 2135.
-2626 Qu, Z.; Cheng, M.; Huang, W.; Bao, X.; J. Catal. 2005, 229, 446. A number of metal nanocatalysts (e.g., Au/TiO2, Pt/Al2O3, etc.) have been recognized to be very effective in CO oxidation reaction.2727 Pietron, J.; Stroud, R.; Rolison, D.; Nano Lett. 2002, 2, 545.

28 Qu, Z. P.; Huang, W. X.; Cheng, M. J.; Bao, X. H.; J. Phys. Chem. B 2005, 109, 15842.
-2929 Bamwenda, G.; Tsubota, S.; Nakamura, T.; Haruta, M.; Catal. Lett. 1997, 44, 83. It has been accepted that silver dispersed on silica is more dynamic and stable than silver supported on carbon nanotubes or reducible oxides (Mn2O3, TiO2).3030 Hu, R. R.; Xie, L. Y.; Ding, S.; Hou, J.; Cheng, Y.; Wang, D. Z.; Catal. Today 2008, 131, 513.

31 Comsup, N.; Panpranot, J.; Praserthdam, P.; Catal. Commun. 2010, 11, 1238.
-3232 Dai, Y. M.; Pan, T. C.; Liu, W. J.; Jehng, J. M.; Appl. Catal., B 2010, 103, 221. Afanasev et al.3333 Afanasev, D. S.; Yakovina, O. A.; Kuznetsova, N. I.; Lisitsyn, A. S.; Catal. Commun. 2012, 22, 43. have reported that Ag supported on fumed silica (4 wt.%) is very effective in CO oxidation reaction [T100 = 30 ºC]. On the other hand, Yu et al.3434 Yu, L. B.; Shi, Y. Y.; Zhao, Z.; Yin, H. B.; Wei, Y. C.; Liu, J.; Kang, W. B.; Jing, T. S.; Wang, A. L.; Catal. Commun. 2011, 12, 616. testified that the catalytic efficiency of silver NPs supported on SiO2 for CO oxidation at ambient temperature is quite low due to particle agglomeration and single phase of the support materials. Zhang et al.3535 Zhang, X.; Qu, Z.; Yu, F.; Wang, Y.; J. Catal. 2013, 297, 264. have also reported that silver NPs on mesoporous silica (SBA-15) is an ideal candidate for CO oxidation (T98 = 20 ºC) and they have proposed evaporation-deposition-diffusion mechanism for metal-supported interactions. Zhu et al.3636 Zhu, H. G.; Liang, C. D.; Yan, W. F.; Overbury, S. H.; Dai, S.; J. Phys. Chem. B 2006, 110, 10842. have published that gold NPs confined within the mesoporous silica are stable after heat treatment. Sun et al.3737 Sun, J. M.; Ma, D.; Zhang, H.; Liu, X. M.; Han, X. W.; Bao, X. H.; Weinberg, G.; Pfänder, N.; Su, D. S.; J. Am. Chem. Soc. 2006, 128, 15756. explored that due to the confinement effect of mesoporous channels of the support for silver NPs, the particles are located outside as well as inside the channels even after thermal treatment at high temperature (500 ºC).

The surface defects, morphology and re-crystallization of solids play an important role in the surface reaction of gases, gas diffusion and adsorption.3838 Backx, C.; de Groot, C. P. M.; Biloen, P.; Surf. Sci. 1981, 104, 300.

39 Wei, T. C.; Phillips, J.; Adv. Catal. 1996, 41, 359.
-4040 Bao, X.; Barth, J. V.; Lehmpfuhl, G.; Schuster, R.; Uchida, Y.; Schlögl, R.; Ertl, G.; Surf. Sci. 1993, 284, 14. The unsaturated bonds present on the surface of solid hybrid/composite materials act as active sites for gas adsorption. The changes in morphology may be thermal or reaction induced.3939 Wei, T. C.; Phillips, J.; Adv. Catal. 1996, 41, 359. The thermally induced morphological changes occur with or without the presence of reacting atmosphere while reaction induced morphological change takes place only in a reacting atmosphere. These induced changes result in a structure different from those formed even after thermal treatment in inert atmosphere or vacuum.3939 Wei, T. C.; Phillips, J.; Adv. Catal. 1996, 41, 359.,4141 Marta, C. N.; de Carvalho, A.; Passos, F. B.; Schmal, M.; J. Catal. 2007, 248, 124.

42 Bron, M.; Teschner, D.; Wild, U.; Steinhauer, B.; Knop Gericke, A.; Volckmar, C.; Wootsch, A.; Schlögl, R.; Claus, P.; Appl. Catal., A 2008, 341, 127.
-4343 Shimizu, K.; Miyamoto, Y.; Satsuma, A.; ChemCatChem 2010, 2, 84. This phenomenon is called adsorbate-induced alterations of the surface free energy. The adsorption of O2 on solids at elevated temperature decreases the surface free energy. However, the thermal treatment of silver at high temperature is not affordable due to low melting point (960 ºC), reversible redox behavior, sintering inside the support channels and morphological changes.1717 Zhang, X.; Qu, Z.; Li, X.; Wen, M.; Quan, X.; Ma, D.; Wu, J.; Sep. Purif. Technol. 2010, 72, 395. Thus, there is a need of third body metal to facilitate the redox behavior of silver and also its sintering inside the support channels without severe thermal treatment.

In the present work, Ag-Sn (with equal wt.% loading) bimetallic nanocatalysts supported on ceria were synthesized for CO oxidation reaction using co-precipitation method. It was observed that the tin oxide sintered in the 3D array of ceria during thermal treatment (at 400 ºC) formed a platform for silver NPs. The tin oxide particles facilitated the silver sintering and controlled its redox behavior for catalytic purposes.4444 Li, K.; Wang, Y.; Wang, S.; Zhu, B.; Zhang, S.; Huang, W.; Wu, S.; J. Nat. Gas Chem. 2009, 18, 1.

45 Avgouropoulos, G.; Ioannides, T.; Appl. Catal., A 2003, 244, 155.
-4646 Chen, Y.; Zhang, L. F.; Catal. Lett. 1992, 12, 51. Our research group is still interested to further investigate and propose a mechanism for this dual function of tin oxide NPs in catalysis.

Experimental

Synthesis of ceria and catalysts

For the synthesis of ceria, Ce(NO3)3⋅6H2O (1.5 g; 3.45 mmol) was dissolved in 25 mL of distilled water. To the cerium salt solution, aqueous NaOH (2 mol L-1; pH > 12) was added dropwise under magnetic stirring at room temperature leading to the formation of a yellow precipitate. The product was obtained at folded filter paper, washed with excess distilled water and dried at 105 ºC.4747 Djuričić, B.; Pickering, S.; J. Eur. Ceram. Soc. 1999, 19, 1925.

Similarly, co-precipitation method was employed for the synthesis of Ag-Sn/CeO2 catalysts for which CeO2 slurry was prepared in distilled water (25 mL) and the salt solutions (AgNO3 and SnCl2⋅2H2O) with an appropriate quantity for the catalysts were added dropwise. The salt solutions were added separately to avoid the precipitation of Ag+ and Cl (Ag+ + Cl → AgClppt). pH of the mixture was maintained at 12 by adding NaOH solution dropwise under gentle stirring at room temperature. Powdered catalysts were obtained after washing with distilled water till the pH came to neutral. After drying, the catalysts were thermally treated at 400 ºC to remove impurities. The different catalysts were synthesized like Ag-Sn/CeO2 (1%), Ag-Sn/CeO2 (2%), Ag-Sn/CeO2 (3%) and Ag-Sn/CeO2 (4%) in accordance with the successive increase in the Ag-Sn wt.% loadings.

Characterization techniques

PANalytical diffractometer (X'Pert PRO 3040/60) with a Cu Kα (λ = 1.544206 Å) radiation generated at 40 kV and 30 mA was used for X-ray diffractometry (XRD) measurements, which were carried out at a speed of 0.015 degree s-1. Surface morphology of catalysts was examined by scanning electron microscopy (SEM) (JEOL JSM-6610LV) and high-resolution transmission electron microscopy (HRTEM) of samples was conducted with FEI Company Titan 80-300 CT TEM by operating it with the acceleration voltage of 300 kV. Moreover, the energy dispersive X-ray spectra (EDS) of samples were also acquired during their conventional transmission electron microscopic (CTEM) investigations. Finally the selected area electron diffraction (SAED) patterns from various regions of samples were acquired for the determination of crystal structures. It should be noted that the entire electron micrographs acquired with TEM were recorded on a 4 k × 4 k charge coupled device (CCD) camera of model US4000 from Gatan, Inc. The UV-Visible (diffuse reflectance) spectra were recorded with a UV-1800 spectrophotometer (Shimadzu). The temperature-programmed reduction (TPR) analyses of the samples were carried out on a Micromeritics (Chemisorb-2750) with H2/Ar (10 vol.%) as a reducing agent (flow rate of 35 cm3 min-1) at a heating rate of 15 ºC min-1 from room temperature to 800 ºC. Hydrogen consumption was measured by thermal conductivity detector (TCD). Prior to the reduction, the samples (120 mg) were pretreated in helium at 300 ºC for 90 min.

CO oxidation experiments

The CO oxidation catalytic activity was conducted by a fixed bed flow reactor system with a quartz tube (5 mm outer diameter) fixed in a tube furnace (Nabertherm B 180) at atmospheric pressure and 0.3 g of catalyst load. The reactant gas, consisting of CO, O2 (1:2 vol.%) and balanced with Ar, was supplied with mass flow controller and mixed with each other, and then the final reactant gas mixture (35 cm3 min-1) was passed through the catalyst bed. The samples were activated at 350 ºC for 120 min by Ar flow (35 cm3 min-1) before the reaction. The CO oxidation reaction was studied in the temperature range of 25-250 ºC and the reactor effluent was analyzed using an online gas chromatograph system (GC-2010 Plus, Shimadzu) with Molecular Sieves 5A (30 m) column and TCD. Conversion of CO to CO2 was calculated from the gas chromatographic (GC) data according to the equation: Xco = [CO]* – [CO] / [CO]*; where Xco is CO conversion, [CO]* and [CO] are the inlet and outlet gas concentrations (ppm), respectively.

Results and Discussion

Characterization of the catalysts

Powder X-ray diffractometry (PXRD) technique was used to investigate the chemical composition and crystalline phases of the synthesized catalysts. The X-ray diffraction pattern of the free support (CeO2) and catalysts with different Ag-Sn wt.% loading is presented in Figure 1 after calcination at 400 ºC. There are peaks in the diffraction pattern a (Figure 1) at 2θ = 28.6, 47.3, 56.4, and 72.4º corresponding to the (111), (220), (311) and (400) lattice planes, respectively, (Joint Committee on Powder Diffraction Standards (JCPDS) cards file No. 00-004-0593) of CeO2. The X-ray pattern shows the three-dimensional cubic structure of CeO2 with Fm-3m space group. The calculated crystallite size from the respective 2θ values falls in the range of 4.6-10 nm and the average size is 7 nm. It is also obvious from the diffraction pattern of CeO2 that all the characteristic peaks are broad and of quite low intensity due to small particle size. In catalysis, small particle size of the support plays an important role in metal particles distribution and reaction selectivity like CO oxidation. In the X-ray diffraction, patterns (Figure 1, patterns b, c, d and e) of the nanocatalyst peaks are present for CeO2, SnO, Ag2O and Ag. Ag characteristic peaks are present at 2θ = 44.4, 64.6 and 77.6º due to the (200), (220) and (311) lattice planes, respectively, in all the catalysts systems. Small peaks at 2θ = 54.3º, (Figure 1, patterns b and c), 69.2º (Figure 1, pattern d) and 82.4º (Figure 1, patterns d and e) correspond to the (220), (222) and (400) lattice planes, respectively, of Ag2O in the synthesized catalysts. Peak at 2θ = 38.4º corresponds to the (111) lattice plane of Ag and (200) lattice plane of Ag2O. The observed mirror indices for Ag and Ag2O reflect cubic (fcc) geometry (JCPDS cards file No. 00-001-1164 for Ag and 00-001-1041 for Ag2O) with space groups Fm-3m and Pm-3m, respectively. Peak at 2θ = 33.4º corresponds to the (002) lattice plane of CeO2 and to the (111) lattice plane of Ag2O and this peak can also be assigned to SnO (JCPDS cards file No. 00-001-0902) in all the catalyst diffraction patterns. Other corresponding peaks of SnO do not appear in the diffraction pattern of the catalysts probably due to two possible reasons: (i) the particle size is very small, i.e., below the detection limit of X-ray radiation; and (ii) SnO is intermingled in the 3D array of cerium(IV) oxide in such a way that it forms a combined plate form for silver NPs and is not explored in the XRD analysis. Peaks responsible for Ag and Ag2O crystallites become intense and sharper in the XRD pattern of Ag-Sn/CeO2 (3%) catalyst system (Figure 1, pattern d), suggesting comparatively large particle size. It is clear from Figure 1 that the diffraction peaks for Ag and Ag2O are not of equal intensity suggesting that the crystallites are not of equal size. The crystallite size (d) calculated for Ag and Ag2O at 2θ = 77.6 and 38.4º using the Scherrer equation is given in Table 1. There is no linear relationship between particle size and Ag-Sn wt.% loading. Possible reason for this nonlinear relationship is the phenomenon of particle agglomeration that takes place during co-precipitation synthesis. In case of Ag-Sn/CeO2 (3%), the particle size of Ag and Ag2O reaches up to 18.32 and 22.12 nm (Table 1), respectively, showing maximum crystallite aggregates formation. The calculated crystallite size (d) at 2θ = 33.5º for SnO via Scherrer equation ranges from 2 to 4 nm in all the catalysts systems.

Figure 1
XRD pattern of: (a) CeO2 support; (b) (Ag-Sn/CeO2) (1%); (c) (Ag-Sn/CeO2) (2%); (d) (Ag-Sn/CeO2) (3%); and (e) (Ag-Sn/CeO2) (4%). Cu Kα (λ = 1.544206 Å) X-ray radiation source generated at 40 kV and 30 mA was used for XRD analysis.
Table 1
Ag/Ag2O crystallite size from powder XRD at 2θ = 77.6 and 38.4º, mean particle size of catalysts from TEM analysis

An EDS spectrum of Ag-Sn/CeO2 (4%) catalyst acquired in CTEM mode is shown in Figure 2, which ratifies peaks for oxygen, silver, tin and cerium. There is a single point at 3 keV for silver, two peaks at 3.4 and 3.55 keV for tin and two peaks at about 3.9 and 5.2 keV for cerium metal. Peaks are originated at 8 and 0.35 keV due to copper grid and carbon polish, used for sample analysis. The EDS analysis illustrates that tin is the part of catalyst system but its presence is not confirmed by PXRD technique.

For surface morphology investigation, SEM analysis was carried out and the images are presented in Figures 3a-d. The SEM images clearly show the three dimensional cubic morphology of the CeO2 supported nanocatalysts. HRTEM and SAED techniques were employed to investigate the size and distribution of nanoparticles supported on CeO2. The results compiled by these techniques are presented in Figures 4a-d, which illustrate that the silver-tin particles are well dispersed on ceria matrix with narrow size distribution and small average particle size (3-8 nm) (Figure 5) after calcination in air at 400 ºC. It has been reported by Zhang et al.1717 Zhang, X.; Qu, Z.; Li, X.; Wen, M.; Quan, X.; Ma, D.; Wu, J.; Sep. Purif. Technol. 2010, 72, 395. that when the catalysts are treated at 500 ºC temperature in O2 silver's particles, dispersion increases but no such changes have been observed in this case which may be due to the stability of the silver NPs in the presence of tin oxide providing synergistically a platform along with ceria. No clear distinction can be drawn between silver and tin particles in the HRTEM micrographs due to a small difference in their atomic numbers. Collectively the particle size of the Ag-Sn in 4 and 2% metal loading catalysts is small in comparison to 3 and 1% metal loading catalysts (Table 1 and Figure 5). So, no clear correlation with increasing metal loading and particle size is observed in this study. SAED results are in good agreement with PXRD patterns of the catalysts.

Figure 2
Representative EDS spectrum of Ag-Sn/CeO2 (4%) catalyst shows Ag, Sn and Ce as the main constituents of catalyst's combination. The EDS spectrum of sample was acquired during their TEM investigation.
Figure 3
SEM images showing the cubic morphology (a, b, c and d) and porous plane (inset of image d) of the Ag-Sn/CeO2 nanocatalysts.
Figure 4
HRTEM images for: (a) Ag-Sn/CeO2 (4%); (b) Ag-Sn/CeO2 (1%); (c) Ag-Sn/CeO2 (3%); and (d) Ag-Sn/CeO2 (2%) catalysts. The inset pictures are the SAED pattern of the respective catalyst. The HRTEM analysis was carried out with an acceleration voltage of 300 kV.
Figure 5
Particle size distribution from TEM analysis of CeO2 supported nanocatalysts: (a) 1%; (b) 2%; (c) 3%; and (d) 4%.

The ionic states of silver in Ag-Sn/CeO2 catalysts were further studied by UV-Vis measurements after thermal treatment at 400 ºC in air. Figure 6 is the UV-Vis spectra of Ag-Sn/CeO2 catalysts with different Ag-Sn wt.% loading. Generally, there are three bands from different oxidation states of silver reported in different research articles. These are absorption bands at 220 nm for Ag+, at 275 nm for Agnδ+ clusters and at 410 nm for metallic Ag0 NPs.1717 Zhang, X.; Qu, Z.; Li, X.; Wen, M.; Quan, X.; Ma, D.; Wu, J.; Sep. Purif. Technol. 2010, 72, 395. In the work presented, in the absorption spectra of Ag-Sn/CeO2 catalysts, no band is observed at 410 nm for Ag0 in all catalysts combinations suggesting the non-interaction mode of Ag0 with support because of the reduced form. There are two surface resonance plasmon centered at 310 and 350 nm in the catalysts having 1, 2, and 3 wt.% loading of metals while the catalyst with 4 wt.% metal loading has only a small band at 350 nm. The band, centered at 310 nm, is attributed to the transition of electron from 4d10 to 4d95s1 of highly dispersed Ag+ ions, while band centered at 350 nm is due to the Agnδ+ clusters. The observed red shift for Ag+ (from 220 to 310 nm) and for Agnδ+ (from 275 to 350 nm) in case of Ag-Sn/CeO2 (3%), Ag-Sn/CeO2 (2%), and Ag-Sn/CeO2 (1%) catalysts is due to the strong interaction of silver particles with SnO/CeO2 support, which synergistically facilitates the electronic transition.1Dai, W. L.; Yong, C.; Ren, L. P.; Yang, X. L.; Xu, J. H.; Li, H. X.; He, H. Y.; Fan, K. N.; J. Catal. 2004, 228, 80. In UV-Vis measurements the intensity of the band is related to the average size of the NPs. When the particles aggregate and particle size increases comparatively (up to certain extent), the intensity of the absorption band increases as in the case of Ag-Sn/CeO2 (3%) catalyst while band of 310 nm for Ag+ disappeared in Ag-Sn/CeO2 (4%) catalyst combination, which is due to small particle size as confirmed by HRTEM and PXRD analysis. In the UV-Vis spectrum of pure CeO2 support, there is a broad absorption band, centered at 370 nm for localized oxygen-cerium charge transfer transition.4848 Bensalem, A.; Bozon-Verduraz, F.; Delamar, M.; Bugli, G.; Appl. Catal., A1995,121, 81. The CeO2 characteristic band in the different catalysts combination does not appear at the respective λmax probably due to the electronic interaction between the metal load and support. The absence of CeO2 absorption band distinctly in the catalyst systems further confirm the red shift for Ag+ and Agnδ+ clusters and blue shift for CeO2 due to silver support (SnO/CeO2) interaction.4949 Kharlamova, T.; Mamontov, G.; Salaev, M.; Zaikovskii, V.; Popova, G.; Sobolev, V.; Knyazev, A.; Vodyankina, O.; Appl. Catal., A 2013, 467, 519. The UV-Vis studies strongly suggest the interaction of silver ionic species with SnO/CeO2 which affects its redox properties during catalysis. The primary focus of this work is to control the redox property of silver without harsh thermal treatment by incorporating a third body metal, which is conclusively shown by UV-Vis studies.

Figure 6
UV-Vis absorption spectra of: (a) Ag-Sn/CeO2 (4%); (b) Ag-Sn/CeO2 (1%); (c) Ag-Sn/CeO2 (2%); (d) Ag-Sn/CeO2 (3%); and (e) CeO2.

The reducibility of the synthesized catalysts was examined by TPR technique and the H2-TPR profiles are presented in Figure 7. In the examined temperature range (25-800 ºC) the catalyst's H2-TPR profiles consist of three reduction zones, which are in the temperature range of 50-280 ºC (α), 280-430 ºC (β) and 430-750 ºC (γ), respectively. According to the reported literature work, there is no reduction peak below 400 ºC for pure support (ceria).5050 Yen, H.; Seo, Y.; Kaliaguine, S.; Kleitz, F.; Angew. Chem., Int. Ed. 2012, 51, 12031. In our studies several reduction peaks are present in the H2-TPR profiles of the Ag-Sn/CeO2 catalysts in the whole temperature range. Peaks in the temperature range of 50-280 ºC (α-temperature zone) can be assigned to the reduction of oxygen adsorbed on the surface of catalyst and to the reduction of Ag2O to Ag.5151 Yatsimirskii, V. K.; Oleksenko, L. P.; Lutsenko, L. V.; Chen, Y.; Russ. J. Phys. Chem. A 2008, 82, 1460. In the total amount of silver, the oxidized species (Ag2O) is not of equal amount; so, the peak responsible for Ag+ reduction is not of equal intensity in all the catalyst combinations. Consequently, the peak area for Ag+ reduction, i.e., the amount of consumed hydrogen does not increase gradually with increasing amount of silver loading. Peaks in the β-temperature zone (280-430 ºC) of the four catalysts are due to the reduction of surface capping oxygen of SnO.4444 Li, K.; Wang, Y.; Wang, S.; Zhu, B.; Zhang, S.; Huang, W.; Wu, S.; J. Nat. Gas Chem. 2009, 18, 1. There is an intense peak and a small shoulder in the γ-temperature zone (430-750 ºC) in the H2-TPR profiles of Ag-Sn/CeO2 (1%), Ag-Sn/CeO2 (2%) and Ag-Sn/CeO2 (3%) catalysts. The intense peak can be assigned to the reduction of bulk cerium(IV) oxide while the shoulder is due to the reduction of surface capping oxygen of ceria.5252 Giordano, F.; Trovarelli, A.; Leitenburg, C.; Giona, M.; J. Catal. 2000, 193, 273. In the H2-TPR profile of Ag-Sn/CeO2 (4%) catalyst, there is a small peak and a shoulder with almost the same intensity in the γ-temperature zone for the reduction of bulk and surface capping oxygen of ceria. The decrease in peak intensity for ceria reduction in Ag-Sn/CeO2 (4%) catalyst is probably due to the small particle size and high surface area of CeO2, which ensures the dispersion of metals over the surface. The dispersion of metals over the support surface further facilitates the electronic interaction of metal with support and lower hydrogen consumption for CeO2 reduction. Alternatively, it is obvious from the β-temperature zone that the peak responsible for the reduction of surface capping oxygen of SnO is comparatively intense in the H2-TPR profile of Ag-Sn/CeO2 (4%) catalyst, presenting high consumption of hydrogen because of their enhanced electronic interaction. Kharlamova et al.4949 Kharlamova, T.; Mamontov, G.; Salaev, M.; Zaikovskii, V.; Popova, G.; Sobolev, V.; Knyazev, A.; Vodyankina, O.; Appl. Catal., A 2013, 467, 519. have also reported that Ag2O and CeO2 interact with each other strongly and there is a simultaneous reduction of both in α-temperature zone. Therefore, the peak responsible for CeO2 reduction in γ-temperature zone is very minute for Ag-Sn/CeO2 (4%) catalyst in comparison with other options. There is shifting of peaks with changing metal wt.% loading on support due to interaction with support up to different extent. In the H2-TPR profiles of Ag-Sn/CeO2 (2%) and Ag-Sn/CeO2 (3%) catalysts the reduction maxima for Ag+ ion shift toward low temperature as compared to Ag-Sn/CeO2 (1%) catalyst profile probably due to: (i) comparatively weak interaction of Ag+ with support; and (ii) the increasing quantity of SnO also facilitates the reducibility of Ag+. The peak intensity in the TPR profile has a relationship with the size of nanocatalysts particle. The present TPR studies have shown that Ag-Sn/CeO2 (4%) catalyst system consists of small reduction peaks due to very fine particle size of metals and support as well.

Figure 7
H2-TPR profiles of CeO2 supported nanocatalysts in the temperature range of 25 to 800 ºC. The H2-TPR of samples were carried out with H2/Ar (10 vol.%) as a reducing agent (flow rate of 35 cm3 min-1) at a heating rate of 15 ºC min-1.

Catalytic activity

Catalytic activities of Ag-Sn/CeO2 catalysts and pure support CeO2 prepared by co-precipitation method and later calcination at 400 ºC towards CO oxidation are shown in Figure 8. The CO conversion increases with reaction temperature and all the silver catalysts can completely oxidize CO to CO2 at certain temperature. For 99% conversion of CO, the temperature for catalysts with 1, 2, 3, and 4% metal loading are 152, 133, 157, and 98 ºC, respectively (Table 2). Meanwhile, pure support CeO2 is also active in CO oxidation reaction and demonstrates 99% conversion at about 170 ºC. The activity slope of CeO2 can be divided into three temperature events. The first event is below 60 ºC - its activity is lower than Ag-Sn/CeO2 (3%) catalyst and presents 8% CO conversion at about 58 ºC. The second temperature event is in the range of 60 to 120ºC, where its activity is almost equal to Ag-Sn/CeO2 (1%) catalyst. The third event is beyond 120 ºC, where the slope again goes beneath the slope of Ag-Sn/CeO2 (3%) catalyst. This irregular behavior of CeO2 with temperature toward CO oxidation in comparison with other catalysts is due to the particle size, oxygen capturing property and thermal changes. At the same temperature, the four catalysts have exhibited relatively higher activities than the catalysts reported by Yu et al.3434 Yu, L. B.; Shi, Y. Y.; Zhao, Z.; Yin, H. B.; Wei, Y. C.; Liu, J.; Kang, W. B.; Jing, T. S.; Wang, A. L.; Catal. Commun. 2011, 12, 616. supplying the reaction mixture with flow rate of 50 cm3 min-1. This is because of silver loading with appropriate quantity and the incorporation of SnO in support platform for controlling the redox behavior of silver ion. The important factor that influences the activity of nanocatalysts is the particle size. The surface-to-volume ratio becomes larger and the concentration of partially coordinated surface sites becomes higher when the particle size decreases.3434 Yu, L. B.; Shi, Y. Y.; Zhao, Z.; Yin, H. B.; Wei, Y. C.; Liu, J.; Kang, W. B.; Jing, T. S.; Wang, A. L.; Catal. Commun. 2011, 12, 616. It has been usually observed by different researchers that the activity increases with decrease in particle size. In the present research work, there is a relationship between silver particle size and catalytic activity. Based on 99% CO conversion the activity of the four catalysts is in the order Ag-Sn/CeO2 (4%) > Ag-Sn/CeO2 (2%) > Ag-Sn/CeO2 (1%) > Ag-Sn/CeO2 (3%). In comparison, the particle size was also in the same order: Ag-Sn/CeO2 (4%) > Ag-Sn/CeO2 (2%) > Ag-Sn/CeO2 (1%) > Ag-Sn/CeO2 (3%), as illustrated from HRTEM and PXRD data (Table 1 and Figure 5). Particle size smaller than 3 nm is also the worst for Ag catalytic activity because it leads to a wider band gap and results in metal to nonmetal transition owing to which it cannot dissociate molecular oxygen for the catalytic conversion of CO to CO2. In the present studies, the particle size of Ag in Ag-Sn/CeO2 (4%) catalyst is below 3 nm but presents superb catalytic activity among the other options. This behavior of the catalysts can be assigned to the electron donating effect of Sn (Electronegativity (E. N.) = 1.8 eV) for being less electronegative than Ag (E. N. = 1.9 eV), which results in shorter band gap and enhanced catalytic activity. In comparison to the work reported by Zhang et al.,3535 Zhang, X.; Qu, Z.; Yu, F.; Wang, Y.; J. Catal. 2013, 297, 264.,5353 Qian, K.; Jiang, Z. Q.; Huang, W. X.; J. Mol. Catal. A: Chem. 2006, 264, 26. that Ag/SBA-0500 and Au/SiO2,catalysts have 98% CO conversion at 190 and 400 ºC, respectively. El-Shall and co-workers5454 Yang, Y.; Saoud, K. M.; Abdelsayed, V.; Glaspell, G.; Deevi, S.; El-Shall, M. S.; Catal. Commun. 2006, 7, 281.

55 Glaspell, G.; Hassan, H. M. A.; Elzatahry, A.; Abdalsayed, V.; El-Shall, M. S.; Top. Catal. 2008, 47, 22.

56 Glaspell, G.; Fuoco, L.; El-Shall, M. S.; J. Phys. Chem. B 2005, 109, 17350.
-5757 Abdalsayed, V.; Aljarash, A.; El-Shall, M. S.; Al Othman, Z. A.; Alghamdi, A. H.; Chem. Mater. 2009, 21, 2825. have reported the synthesis of Ag, Pd and Au (5 wt.%) nanoparticles and AuPd, PdAg (5 wt.%) bimetallic nanoalloys supported on CeO2 for CO oxidation by two different methods, like laser vaporization and microwave irradiation. They found out that Pd/CeO2 and Au/CeO2nanocatalysts, developed by laser vaporization technique, have converted CO to CO2 with 100% efficiency at 108 and 163 ºC, respectively, while the catalyst combinations Ag/CeO2, Pd/CeO2 and Au/CeO2 synthesized via microwave irradiation showed 100% CO to CO2 conversion at 266, 151, and 301 ºC, respectively (Table 2). The bimetallic nanoalloys, supported on CeO2 and synthesized by microwave irradiation, have demonstrated 93% CO conversion at 186 ºC. The catalyst combination Ag-Sn/CeO2 (4%), presented in this study, has demonstrated 100% CO to CO2 conversion at 100 ºC, which is the superb catalytic activity among the other options. This excellent catalytic performance could be attributed to the strong metal-support electronic interaction, which controls the redox behavior of silver nanoparticles.

Figure 8
Catalytic activity for CO oxidation of Ag-Sn/CeO2 catalysts with different Ag-Sn wt.% loading and CeO2 support. The reactor effluent was analyzed using an online gas chromatograph system with Molecular Sieves 5A (30 m) column and TCD detector.
Table 2
CO oxidation over Ag-Sn/CeO2 catalysts with different Ag-Sn wt.% loading and literature reported catalytic activities of Pd, Au, Ag nanoparticles and AuPd, PdAg bimetallic nanoalloys supported on CeO2

To evaluate the long term stability and reproducibility of the designed nanocatalysts stability, tests were performed under stationary condition and fixed temperature. The stability of CeO2 supported nanocatalysts was tested for 900 min (15 h) at 110 ºC and the results are shown in Figure 9. In the selected time period, the stability of the catalysts is in the order: Ag-Sn/CeO2 (4%) > Ag-Sn/CeO2 (3%) > Ag-Sn/CeO2 (2%) > Ag-Sn/CeO2 (1%) = CeO2. Surprisingly, the CO conversion over the 4, 2 and 3% catalysts is as high as 97, 85 and 64%, respectively, for about 700 min. These values decrease slowly to 95, 80 and 60% after keeping the catalysts at 110 ºC for 900 min. The 4, 2 and 3% catalysts have demonstrated 5, 8 and 6% stability loss in the whole testing period, respectively. Possible explanation for the long term stability of these catalysts is the appropriate quantity of metal loading on support and their mutual interaction for reproducing their electronic states, which is a key factor for catalytic recycling. The behavior of Ag-Sn/CeO2 (1%) catalyst is different from the other options and the CO conversion percentage decreases from 79 to 40% with 39% stability loss for 900 min at 110 ºC. Similar behavior to Ag-Sn/CeO2 (1%) catalyst for pure CeO2 support was observed under the same testing conditions.

Figure 9
Stability performance of the nanocatalysts supported on CeO2: (a) 4%; (b) 2%; (c) 3%; and (d) 1%. Testing condition: 1 vol.% CO, 2 vol.% O2 and Ar balanced, 110 ºC, 35 cm3 min-1.

Conclusions

In summary, catalyst combinations like Ag-Sn/CeO2 with different Ag-Sn wt.% loading were synthesized by co-precipitation method, characterized by a range of instrumental techniques and tested for catalytic CO oxidation reaction. PXRD and HRTEM analyses confirmed that these catalysts have small particles with narrow size distribution over support surface. UV-Vis and H2-TPR measurements have recommended strong metal-support interaction, which expedites the catalytic activity and catalysts stability. The catalysts are classified by increasing the order of their activity as Ag-Sn/CeO2 (3%) < Ag-Sn/CeO2 (1%) < Ag-Sn/CeO2 (2%) < Ag-Sn/CeO2 (4%) after their testing for CO oxidation reaction. The Ag-Sn/CeO2 (4%) catalyst is the most promising catalyst combination of this study among the other options, which presents 100% CO oxidation at 100 ºC and only 5% stability loss at 110 ºC for 900 min due to small particle size and strong metal-support interaction.

Acknowledgments

This work was supported by the Higher Education Commission (HEC) of Pakistan (No. 20-1638/R&D/09/2900). The authors thank PhD Dalaver Hussain Anjum (KAUST Saudi Arabia) for high resolution TEM and SAED analyses.

References

  • 1
    Dai, W. L.; Yong, C.; Ren, L. P.; Yang, X. L.; Xu, J. H.; Li, H. X.; He, H. Y.; Fan, K. N.; J. Catal. 2004, 228, 80.
  • 2
    Shi, C.; Cheng, M. J.; Qu, Z. P.; Bao, X. H.; J. Mol. Catal. A: Chem. 2005, 235, 35.
  • 3
    Lee, J. H.; Schmieg, S. J.; Oh, S. H.; Appl. Catal., A 2008, 342, 78.
  • 4
    van Santen, R. A.; Kuipers, H. P. C. E.; Adv. Catal. 1987, 35, 265.
  • 5
    Zhang, L.; Zhang, C. B.; He, H.; J. Catal. 2009, 261, 101.
  • 6
    Nagy, A. J.; Mestl, G.; Schlögl, R.; J. Catal. 1999, 188, 58.
  • 7
    Yamamoto, R.; Sawayama, Y.; Shibahara, H.; Ichihashi, Y.; Nishiyama, S.; Tsuruya, S.; J. Catal. 2005, 234, 308.
  • 8
    Purcar, V.; Donescu, D.; Petcu, C.; Luque, R.; Macquarrie, D. J.;Appl. Catal., A 2009, 363, 122.
  • 9
    Magaev, O. V.; Knyazev, A. S.; Vodyankina, O. V.; Dorofeeva, N. V.; Salanov, A. N.; Boronin, A. I.; Appl. Catal., A 2008, 344, 142.
  • 10
    Frey, K.; Iablokov, V.; Melaet, G.; Guczi, L.; Kruse, N.; Catal. Lett. 2008, 124, 74.
  • 11
    Song, K. S.; Kang, S.; Sim, S. D.; Catal. Lett. 1997, 49, 65.
  • 12
    Xu, R.; Wang, X.; Wang, D. S.; Zhou, K. B.; Li, Y. D.; J. Catal. 2006, 237, 426.
  • 13
    Wang, A. Q.; Liu, J. H.; Lim, S. D.; Lin, T. S.; Mou, C. Y.; J. Catal. 2005, 233, 186.
  • 14
    Wang, A. Q.; Hsieh, Y. P.; Chen, Y. F.; Mou, C. Y.; J. Catal. 2006, 237, 197.
  • 15
    Liu, X. Y.; Wang, A. Q.; Yang, X. F.; Zhang, T.; Mou, C. Y.; Su, D. S.; Li, J.; Chem. Mater.2009, 21, 410.
  • 16
    Liu, H. Y.; Ma, D.; Blackley, R. A.; Zhou, W. Z.; Bao, X. H.; Chem. Commun. 2008, 23, 2677.
  • 17
    Zhang, X.; Qu, Z.; Li, X.; Wen, M.; Quan, X.; Ma, D.; Wu, J.; Sep. Purif. Technol. 2010, 72, 395.
  • 18
    Bao, X.; Muhler, M.; Pettinger, B.; Schlögl, R.; Ertl, G.; Catal. Lett. 1993, 22, 215.
  • 19
    Bao, X.; Muhler, M.; Pettinger, B.; Schlögl, R.; Ertl, G.; Catal. Lett. 1995, 32, 185.
  • 20
    Schubert, H.; Tegtmeyer, U.; Herein, D.; Bao, X.; Muhler, M.; Schlögl, R.; Catal. Lett. 1995, 33, 305.
  • 21
    Su, D. S.; Jacob, T.; Hansen, T. W.; Wang, D.; Schlögl, R.; Freitag, B.; Kujawa, S.; Angew. Chem., Int. Ed.2008, 47, 5005.
  • 22
    Qu, Z. P.; Cheng, M. J.; Huang, W. X.; Bao, X. H.; J. Catal. 2005, 229, 446.
  • 23
    Christopher, J. B.; Charles, A. M.; J. Catal. 1999, 184, 224.
  • 24
    Gardner, S. D.; Hoflund, G. B.; Upchurch, B. T.; Schryer, D. R.; Kielin, E. J.; Schryer, J.; J. Catal.1991, 129, 114.
  • 25
    Gardner, S.; Hoflund, G.; Schryer, D.; Schryer, J.; Upchurch, B.; Kielin, E.; Langmuir 1991, 7, 2135.
  • 26
    Qu, Z.; Cheng, M.; Huang, W.; Bao, X.; J. Catal. 2005, 229, 446.
  • 27
    Pietron, J.; Stroud, R.; Rolison, D.; Nano Lett. 2002, 2, 545.
  • 28
    Qu, Z. P.; Huang, W. X.; Cheng, M. J.; Bao, X. H.; J. Phys. Chem. B 2005, 109, 15842.
  • 29
    Bamwenda, G.; Tsubota, S.; Nakamura, T.; Haruta, M.; Catal. Lett. 1997, 44, 83.
  • 30
    Hu, R. R.; Xie, L. Y.; Ding, S.; Hou, J.; Cheng, Y.; Wang, D. Z.; Catal. Today 2008, 131, 513.
  • 31
    Comsup, N.; Panpranot, J.; Praserthdam, P.; Catal. Commun. 2010, 11, 1238.
  • 32
    Dai, Y. M.; Pan, T. C.; Liu, W. J.; Jehng, J. M.; Appl. Catal., B 2010, 103, 221.
  • 33
    Afanasev, D. S.; Yakovina, O. A.; Kuznetsova, N. I.; Lisitsyn, A. S.; Catal. Commun. 2012, 22, 43.
  • 34
    Yu, L. B.; Shi, Y. Y.; Zhao, Z.; Yin, H. B.; Wei, Y. C.; Liu, J.; Kang, W. B.; Jing, T. S.; Wang, A. L.; Catal. Commun. 2011, 12, 616.
  • 35
    Zhang, X.; Qu, Z.; Yu, F.; Wang, Y.; J. Catal. 2013, 297, 264.
  • 36
    Zhu, H. G.; Liang, C. D.; Yan, W. F.; Overbury, S. H.; Dai, S.; J. Phys. Chem. B 2006, 110, 10842.
  • 37
    Sun, J. M.; Ma, D.; Zhang, H.; Liu, X. M.; Han, X. W.; Bao, X. H.; Weinberg, G.; Pfänder, N.; Su, D. S.; J. Am. Chem. Soc. 2006, 128, 15756.
  • 38
    Backx, C.; de Groot, C. P. M.; Biloen, P.; Surf. Sci. 1981, 104, 300.
  • 39
    Wei, T. C.; Phillips, J.; Adv. Catal. 1996, 41, 359.
  • 40
    Bao, X.; Barth, J. V.; Lehmpfuhl, G.; Schuster, R.; Uchida, Y.; Schlögl, R.; Ertl, G.; Surf. Sci. 1993, 284, 14.
  • 41
    Marta, C. N.; de Carvalho, A.; Passos, F. B.; Schmal, M.; J. Catal. 2007, 248, 124.
  • 42
    Bron, M.; Teschner, D.; Wild, U.; Steinhauer, B.; Knop Gericke, A.; Volckmar, C.; Wootsch, A.; Schlögl, R.; Claus, P.; Appl. Catal., A 2008, 341, 127.
  • 43
    Shimizu, K.; Miyamoto, Y.; Satsuma, A.; ChemCatChem 2010, 2, 84.
  • 44
    Li, K.; Wang, Y.; Wang, S.; Zhu, B.; Zhang, S.; Huang, W.; Wu, S.; J. Nat. Gas Chem. 2009, 18, 1.
  • 45
    Avgouropoulos, G.; Ioannides, T.; Appl. Catal., A 2003, 244, 155.
  • 46
    Chen, Y.; Zhang, L. F.; Catal. Lett. 1992, 12, 51.
  • 47
    Djuričić, B.; Pickering, S.; J. Eur. Ceram. Soc. 1999, 19, 1925.
  • 48
    Bensalem, A.; Bozon-Verduraz, F.; Delamar, M.; Bugli, G.; Appl. Catal., A1995,121, 81.
  • 49
    Kharlamova, T.; Mamontov, G.; Salaev, M.; Zaikovskii, V.; Popova, G.; Sobolev, V.; Knyazev, A.; Vodyankina, O.; Appl. Catal., A 2013, 467, 519.
  • 50
    Yen, H.; Seo, Y.; Kaliaguine, S.; Kleitz, F.; Angew. Chem., Int. Ed. 2012, 51, 12031.
  • 51
    Yatsimirskii, V. K.; Oleksenko, L. P.; Lutsenko, L. V.; Chen, Y.; Russ. J. Phys. Chem. A 2008, 82, 1460.
  • 52
    Giordano, F.; Trovarelli, A.; Leitenburg, C.; Giona, M.; J. Catal. 2000, 193, 273.
  • 53
    Qian, K.; Jiang, Z. Q.; Huang, W. X.; J. Mol. Catal. A: Chem. 2006, 264, 26.
  • 54
    Yang, Y.; Saoud, K. M.; Abdelsayed, V.; Glaspell, G.; Deevi, S.; El-Shall, M. S.; Catal. Commun. 2006, 7, 281.
  • 55
    Glaspell, G.; Hassan, H. M. A.; Elzatahry, A.; Abdalsayed, V.; El-Shall, M. S.; Top. Catal. 2008, 47, 22.
  • 56
    Glaspell, G.; Fuoco, L.; El-Shall, M. S.; J. Phys. Chem. B 2005, 109, 17350.
  • 57
    Abdalsayed, V.; Aljarash, A.; El-Shall, M. S.; Al Othman, Z. A.; Alghamdi, A. H.; Chem. Mater. 2009, 21, 2825.

Publication Dates

  • Publication in this collection
    Apr 2015

History

  • Received
    31 May 2015
  • Accepted
    06 Feb 2015
Sociedade Brasileira de Química Instituto de Química - UNICAMP, Caixa Postal 6154, 13083-970 Campinas SP - Brazil, Tel./FAX.: +55 19 3521-3151 - São Paulo - SP - Brazil
E-mail: office@jbcs.sbq.org.br