<FONT FACE=Symbol>b</font>-diketonates of Eu3+, red phosphors, supported on sol-gel functionalised silica

Abstract

Silica gel was functionalised with chloropropyl groups through the sol-gel process and then a beta-diketone was incorporated into the support. Afterwards, Eu3+ ion and its chelates of 1,10-phenantroline (phen) and 2,2'-bipyridine (bpy), red phosphors, were supported on such silica. Luminescence studies of Eu3+ bound to this new material have shown that there is an increase in the intensity of the emission when the ion is isolated by ligands in the silica matrix. The energy transfer from the ligands phen and bpy to Eu3+ ion was observed in the excitation spectra, which present new bands ascribed to the ligands and/or complex. The Eu3+-functionalised silica was characterised by TGA and FTIR. TGA analysis showed that there is a large loss of mass around 300 °C, which is ascribed to the organic part of the material. The FTIR spectra presented the vibration modes for Si-C and -CH2-. The luminescent properties of the ions surrounding the Eu3+ ion were studied. The decay curve displayed a bi-exponential behaviour, indicating that there is more than one site of Eu3+ on the surface of the silica.

rare earth; sol-gel process; functionalised silica; luminescence; red phosphor


b-Diketonates of Eu3+, Red Phosphors, Supported on Sol-Gel Functionalised Silica

Eduardo J. Nassar*a,b, Osvaldo A. Serraa, Paulo S. Calefia,

Cynthia M.C.P. Mansoa, Cláudio R. Neria

aRare Earth Laboratory, Chemistry Department, FFCLRP, University of São Paulo,

14040-901 Ribeirão Preto - SP, Brazil

bChemistry Institute - UNESP - Araraquara - SP, Brazil

Present address: UNIFRAN. e-mail: ejnassar@unifran.br

Received: August 16, 2000; Revised: December 22, 2000

Silica gel was functionalised with chloropropyl groups through the sol-gel process and then a b-diketone was incorporated into the support. Afterwards, Eu3+ ion and its chelates of 1,10-phenantroline (phen) and 2,2'-bipyridine (bpy), red phosphors, were supported on such silica. Luminescence studies of Eu3+ bound to this new material have shown that there is an increase in the intensity of the emission when the ion is isolated by ligands in the silica matrix. The energy transfer from the ligands phen and bpy to Eu3+ ion was observed in the excitation spectra, which present new bands ascribed to the ligands and/or complex. The Eu3+-functionalised silica was characterised by TGA and FTIR. TGA analysis showed that there is a large loss of mass around 300 °C, which is ascribed to the organic part of the material. The FTIR spectra presented the vibration modes for Si-C and -CH2-. The luminescent properties of the ions surrounding the Eu3+ ion were studied. The decay curve displayed a bi-exponential behaviour, indicating that there is more than one site of Eu3+ on the surface of the silica.

Keywords : rare earth, sol-gel process, functionalised silica, luminescence, red phosphor

1. Introduction

A light-conversion device consists of two discrete components: an “antenna” (light harvesting ligand) and an emitter. For them to function, an intercomponent energy transfer must occur as efficiently as possible1. Macrocyclic ligands containing heterobiaryl groups bound to Eu3+ and Tb3+ are among the most frequently studied systems. In these complexes, the light is harvested by the heterobiaryl groups, transferred to the rare earth ion and then emitted. The macrocyclic framework protects the rare earth ion and minimises non-radiative deactivations.

In recent years, luminescent lanthanide complexes have been used in photonic devices where light is absorbed by the ligand and energy is transferred to the emitting metal ion (antenna effect)2-6. This effect involves three factors: i) intensity of ligand absorption; ii) efficiency of ligand-metal energy transfer and iii) efficiency of metal emission. Many luminescent lanthanide complexes have been synthesised and their chemical and photophysical properties have been modified through their interaction with different hosts (e.g. a solid interface).

Oxide surfaces have been used as a host for organic and inorganic molecules and the interaction between the support and the guest molecules7-9 has been studied. Inorganic supports have been utilised due to their rigidity, stability and inertness. Materials such as ion exchange resins10, zeolites11,12, clay13 and silica2,14-16 have been used.

In the last decades, the sol-gel technology has called the attention of countless researchers due to its attractive preparation route, which is carried out at low temperature17-20. The sol-gel process has been employed in important technological process such as the production of optical fibres and chemical sensors, just to mention some21. Oxide surfaces modified by organic molecules have also been finding several applications22-24.

In this work, we have functionalised silica gel with chloropropyl groups either through the sol-gel process or through its treatment with 3-chloropropyltrimethoxisilane (TMOSCl). Then one of the following b-diketones antenna ligands: 2,4-pentanedione (acac), 4,4,4-trifluoro-1-phenyl-1,3-butanedione (bta), dibenzoylmethane (dbm) or 1,1,1,5,5,5-hexafluoro-2,4-pentanedione (hfa) was covalently bound to the functionalised silica, so that the latter served as a host for the antenna. Afterwards, Eu3+ ion was supported on such silica. Since the energy of the first triplet excited level of the “harvester” determines the energy transfer to Eu3+, we also added the heterobiaryal molecules 1,10-phenantroline and 2,2'-bipyridine to the silica materials, so that they functioned as an extra antenna (Fig. 1). When the silica gel was functionalised through the sol-gel technique, it was possible to control the amount of chloropropyl groups on the support and, consequently, the quantity of the covalently bound “antenna” ligands on the matrix. This improved the light emission through the rare earth ion, which is not possible to attain through the conventional silica treatment.


2. Experimental

Silica functionalised with 3-chloropropyl groups was prepared through the sol-gel process, using a TEOS (tetraethylorthosilicate) : TMOSCl 1:1 molar ratio and characterized as described by Nassar et al.25. The reagents were purchased from Aldrich. TEOS and TMOSCl were added to the silica in dry ethanol and then acidic water was added to this solution under stirring. The solvent was evaporated at 30 °C and a white solid was obtained. The solid was dried at 60 °C, overnight.

b-diketone (acac, bta, dbm and hfa) ligation to the functionalised silica carried out with the ligands in their sodium salt form26. This procedure led to the obtention of silica functionalised with propyl acetyl (APG), benzoyl (BPG), dibenzoyl (DPG) and hexafluoro (HPG) ligands. The preparation of APGEu, BPGEu, DPGEu and HPGEu, as well as phen and bpy incorporation, have been previously described2.

The functionalised silica was characterised by TGA using Thermal Analyst 2100-TA Instruments SDT 2960 - Simultaneous DTA-TGA analyser, in air with a heating rate of 10 °C/min from 25 to 900 °C. FTIR spectra were recorded on the Nicolet FT-IR SZDX spectrophotometer in KBr pellets.

The luminescence data were obtained on a Spex Fluorolog II spectrofluorometer at room temperature. The sample was placed in a quartz capillary tube (I.D. = 1.0 mm). The emission was collected at 90 °C from the excitation beam. The slits were placed at 2.0 and 0.5 mm for excitation and emission, respectively, giving a band pass of 7 and 0.9 nm; filters: Oriel 59816 (exc.) and Corning 97612 (em.).

3. Results and Discussion

TGA for the silica prepared through the sol-gel process presented a loss of mass of 10% (w/w) around 98 °C, which is ascribed to water molecules. For the other samples we observed an increase in the loss of mass at temperatures above 280 °C. This shows that the silica was functionalised with propyl b-diketonate groups.

In the DTA curve we observed exothermic transformations with a broad peak between 280-450 °C. Such large exothermic transformation indicates the presence of a non-crystalline solid17.

The FTIR spectra of the samples displayed a characteristic strong absorption band due to the Si-O vibrations (1060 and 1082 cm-1). At 1275 cm-1, a sharp peak due to Si-C bond stretching was found. The absorption at 867 cm-1 is due to Si-C bond deformation. At higher frequencies, the asymmetric and symmetric stretching of the methyl C-H bond were detected at 2957 and 2850 cm-1, respectively. This result confirms that the Si-C bond was not broken during the sol-gel process.

The excitation maximum of the Eu3+ ion in the samples without the phen or bpy ligands is at 393 nm, which corresponds to the 5L6 level of Eu3+. All emission spectra present the characteristic transitions arising from the 5D0 to the 7FJ level (J = 0, 1, 2, 3 and 4) manifolds, excited at their maxima.

The excitation maximum for the samples containing the bpy ligand was ascribed to the ligand itself, since the absorption maximum of free bpy occurs at 309 nm. In the sample containing the phen ligand, the excitation maximum was ascribed to the Eu-phen complex.

The energy transfer from the ligand to Eu3+ occurs via triplet states. It was noticed that in the presence of the ligands phen and bpy, the emission intensity increases due to energy transfer from the ligand to the Eu3+ ion. Moreover, the removal of H2O and/or OH around the Eu3+ ion reduces vibrational losses.

The 5D0 level of the ion can be depopulated through water, ligands and matrice by vibrational interactions27. The number of water molecules (or OH groups) can be formulated as proposed by Horrocks28 q = 1,05 (t-1H2O- t-1D2O)even in the absence of measurements in deuterated systems29, considering tD2O = 50 ms. In Table 1, we show the experimental lifetimes measurements for hypersensitive the 5D0® 7F2 transitions of Eu3+ and the number of water molecules calculated by Horrocks formula, for all the samples.

All samples presented a decay curve with a bi-exponential behaviour, but we calculated the number of water molecules for the first decay only, since it is responsible for the major contribution. This behaviour reflects the non-homogeneity of the luminescent species on the silica matrix and is in agreement with the observed asymmetric band corresponding to 5D0® 7F0 transition.

Figures 2, 3 and 4 present the emission and excitation spectra for all the samples containing Eu3+ and phen and bpy ligands, respectively.




The band corresponding to the 5D0® 7F2 transition is more intense than that due to the 5D0® 7F1 transition, for all the samples. This is an indication that the symmetry around the Eu3+ ion does not contain a centre of inversion30-33. The presence of the 5D0® 7F0 transition indicates that Eu3+ is located in one of the Cnv, Cn or Cs symmetry groups29.

4. Conclusion

To sum up, in this work we have made use of the sol-gel process to obtain functionalised silica where it was possible to better control the amount of the reactive chloro alkyl groups that bind to the support. Consequently we have been able to build light harvesting materials containing the desired amount of antenna ligands. The new synthetic procedure presented in this paper resulted in the preparation of better silica based red luminescent materials.

Acknowledgement

To the Brazilian agencies FAPESP and CNPq for financial support.

FAPESP helped in meeting the publication costs of this article

  • 1. Lehn , J.-M. Oppening Lecture at Int. Conf. on f Elem. Abstract Book, p. 52. September, 1997.
  • 2. Serra, O.A.; Nassar, E.J.; Zapparolli, G.; Rosa, I. L.V. J. Alloys Comp., v. 207/208, p. 454, 1994.
  • 3. Serra, O.A.; Nassar, E.J.; Rosa, I.L.V.; Rosa, J. Lumin., v. 71-72, p. 263, 1997.
  • 4. Sabbatini, N.; Mecati, A.; Guardigli, M.; Balzani, V.; Lehn, J.-M.; Zeissel, R.; Ungaro, R.J. Lumin., v. 48-49, p. 463, 1991.
  • 5. Sabbatini, N.; Guardigli, M.; Lehn, J.-M, Coord. Chem. Rev., v. 123, p. 201, 1993.
  • 6. Cicillini, S.A.; Calefi, P.S.; Neri, C.R.; Nassar, E.J.; Serra, O.A. J. Non-Cryt. Solids, v. 247, p. 114, 1999.
  • 7. Hazenkamp, M. F.; Blasse, G.; Sabbatini, N., J. Phys. Chem., v.95, p.783, 1991.
  • 8. Hazenkamp, M.F.; Vander Veen, A.M.H.; Feiken, N.; Blasse, G. J. Chem. Soc., Faraday Trans., v. 88, p. 141, 1992.
  • 9. Levy, D.; Reisfeld, R.; Avnir, D. Chem. Phys. Letters, v. 109, n. 6, p. 593, 1984.
  • 10. Menier, B. Chem. Rev., v. 92, p. 1411, 1992.
  • 11. Heron, N.; Stuchy, G.D.; Tolman, C.A. J. Chem. Soc. Chem. Commun, p. 1521, 1986.
  • 12. Serra, O.A.; Nassar, E.J.; Zapparolli, G.; Rosa, I.L.V. J. Alloys Comp., v. 225, p. 63, 1995.
  • 13. Pinavaia, T.J. Science, p. 220, 1983.
  • 14. Serra, O.A.; Nassar, E.J.; Rosa, I.L.V., J. Lumin. v. 72-74, p. 263, 1997.
  • 15. Nassar, E.J.; Serra, O.A. Química Nova, v. 23, n. 1, p.16, 2000.
  • 16. Airoldi, C.; Farias, R.F. de, Química Nova, v. 23, n. 4, p. 496, 2000.
  • 17. Corriu, R.J.P.; Leclercq, D. Angew Chem. Int. Engl., v. 35, p. 1420, 1996.
  • 18. Hench, L.L.; West, J.K., Chem. Rev., v. 90, n. 1, p. 33, 1990.
  • 19. Rao, R.P. Solid State Communications, v. 99, n. 6, p. 439, 1996.
  • 20. Gonçalves, R.R.; Messaddeq, Y.; Atik, M.; Ribeiro, S.J.L. Materials Research, v. 2, n. 1, p. 11, 1999.
  • 21. Matejec, V.; Hayer, M.; Pospisilova, M.; Kasik, I. J. of Sol-Gel Sci. and Tech., v.8, p.889, 1997.
  • 22. Livage, J.; Materilas Science Forum, v. 152-153, p. 43, 1994.
  • 23. Iamamoto, Y.; Ciuffi, K.J.; Sacco, H.C.; Prado, C.M.C.; Moraes, M. de; Nascimento, O.R.; J. Molecular Catalysis, v. 88, p. 167, 1994.
  • 24. Leyden, E.D.; Luttrell, G.H. Analytical Chemistry, v. 47, n. 9, p. 1612, 1975.
  • 25. Nassar, E.J.; Neri, C.R.; Calefi, P.S.; Serra, O.A. J. Non-Cryst. Solids, v. 247, p. 124, 1999
  • 26. Nassar, E.J.; Serra, O.A.; Rosa, I.L.V. J. Alloys Comp., v. 250, p. 380, 1997.
  • 27. Sammesa, P.G.; Yohioglu, G. Chem. Soc. Rev., v. 23, p. 327, 1994.
  • 28. Horrocks, W. de W.; Sudnick, J.R. Acc. Chem. Res., v. 14, p. 384, 1991.
  • 29. Hazenkamp, M.F.; Blasse, G. Chem. of Materials, v. 2, p. 105, 1990.
  • 30. Sager, W.F.; Filipescu, N.; Serafin, F.A. J. Phys. Chem., v. 69, p. 1092, 1965.
  • 31. Yatsimirkii, K.B.; Davidenko, N.K. Coord. Chem. Ver., v. 27, p. 223, 1979.
  • 32. Jorgensen, C.K.; Reisfeld, R. J. Less. Common Met., v. 93, p. 107, 1983.
  • 33. Sá, G.F. de; Azevedo, W.M. de; Gomes, A.S.L. J. Chem. Research, p. 234, 1994.

Publication Dates

  • Publication in this collection
    09 Mar 2001
  • Date of issue
    Jan 2001

History

  • Reviewed
    22 Dec 2000
  • Received
    16 Aug 2000
ABM, ABC, ABPol UFSCar - Dep. de Engenharia de Materiais, Rod. Washington Luiz, km 235, 13565-905 - São Carlos - SP- Brasil. Tel (55 16) 3351-9487 - São Carlos - SP - Brazil
E-mail: pessan@ufscar.br