ABSTRACT
Objective
Green tea extract has been advocated as a matrix metalloproteinase (MMP) inhibitor; however, its effect on bond durability to caries-affected dentin has never been reported. Thus, the aim of this in vitro study was to evaluate the effect of two MMP inhibitors (2% chlorhexidine and 2% green tea extract), applied after acid etching, on bond durability of an etch-and-rinse adhesive system to caries-affected dentin.
Material and Methods
Occlusal enamel was removed from third molars to expose the dentin surface, and the molars were submitted to a caries induction protocol for 15 days. After removal of infected dentin, specimens were conditioned with 37% phosphoric acid (15 seconds) and randomly divided into three groups, according to the type of dentin pretreatment (n=10): NT: no treatment; GT: 2% green tea extract; CLX: 2% chlorhexidine. The etch-and-rinse adhesive system (Adper™ Single Bond 2, 3M ESPE, St. Paul, MN, USA) was applied according to the manufacturer's instructions, and composite resin restorations were built on the dentin. After 24 hours, at 37°C, the resin-tooth blocks were sectioned perpendicularly to the adhesive interface in the form of sticks (0.8 mm2 of adhesive area) and randomly subdivided into two groups according to when they were to be submitted to microtensile bond strength (μTBS) testing: immediately or 6 months after storage in distilled water. Data were reported in MPa and submitted to two-way ANOVA for completely randomized blocks, followed by Tukey’s test (α=0.05).
Results
After 24 hours, there was no significant difference in the μTBS of the groups. After 6 months, the GT group had significantly higher μTBS values.
Conclusion
It was concluded that the application of 2% green tea extract was able to increase bond durability of the etch-and-rinse system to dentin. Neither the application of chlorhexidine nor non-treatment (NT - control) had any effect on bond strength after water storage.
Chlorhexidine; Camellia sinensis; Matrix metalloproteinases; Tensile strength
INTRODUCTION
The evolution of adhesive restorative materials and the knowledge of caries lesion progression have led to the development of the minimally invasive Dentistry concept, whose principles advocate minimum intervention in cavitated carious lesions and maximum preservation of sound dental structure2626 - Tyas MJ, Anusavice KJ, Frencken JE, Mount GJ. Minimal intervention dentistry - a review. FDI Commission Project 1-97. Int Dent J. 2000;50:1-12.. This interventionist philosophy separates carious dentin on two levels: the outer layer or infected dentin1010 - Fusayama T. Two layers of carious dentine: diagnosis and treatment. Oper Dent. 1979;4(2):63-70., which must be removed, and the inner layer of dentin, with a lower level of infection, known as caries-affected dentin, which can be remineralized and must be preserved33 - Campos EA, Correr GM, Leonardi DP, Barato-Filho F, Gonzaga CC, Zielak JC. Chlorhexidine diminishes the loss of bond strength over time under simulated pulpal pressure and thermo-mechanical stressing. J Dent. 2009;37(2):108-14.,2626 - Tyas MJ, Anusavice KJ, Frencken JE, Mount GJ. Minimal intervention dentistry - a review. FDI Commission Project 1-97. Int Dent J. 2000;50:1-12.. Caries-affected dentin has greater porosity, partial demineralization and altered ultrastructural collagen2828 - Wang Y, Spencer P, Walker MP. Chemical profile of adhesive/caries-affected dentin interfaces using Raman microspectroscopy. J Biomed Mater Res A. 2007;81:279-86.. These modifications lead to the formation of a more irregular hybrid layer, with greater area of exposed collagen1818 - Sanabe ME, Costa CA, Hebling J. Exposed collagen in aged resin-dentin bonds produced on sound and caries-affected dentin in the presence of chlorhexidine. J Adhes Dent. 2011;13:117-24.,2828 - Wang Y, Spencer P, Walker MP. Chemical profile of adhesive/caries-affected dentin interfaces using Raman microspectroscopy. J Biomed Mater Res A. 2007;81:279-86. and lower bond strength, as compared to sound dentin99 - Erhardt MC, Toledano M, Osorio R, Pimenta LA. Histomorphologic characterization and bond strength evaluation of caries-affected dentin/resin interfaces: effects of long-term water exposure. Dent Mater. 2008;24:786-98.,2929 - Yoshiyama M, Urayama A, Kimochi T, Matsuo T, Pashley DH. Comparison of conventional vs self etching adhesive bonds to caries-affected dentin. Oper Dent. 2000;25:163-9..
In addition, the adhesive interface is susceptible to hydrolytic degradation, expressed by an increase in the caries-affected dentin99 - Erhardt MC, Toledano M, Osorio R, Pimenta LA. Histomorphologic characterization and bond strength evaluation of caries-affected dentin/resin interfaces: effects of long-term water exposure. Dent Mater. 2008;24:786-98.. This degradation occurs in stages1818 - Sanabe ME, Costa CA, Hebling J. Exposed collagen in aged resin-dentin bonds produced on sound and caries-affected dentin in the presence of chlorhexidine. J Adhes Dent. 2011;13:117-24.: water is absorbed by the polymer when hydrolytic degradation first begins; resin components are leached from the hybrid and/or adhesive layer; the exposed collagen fibrils are degraded by endopeptidases present in the dentin matrix (MMPs)1717 - Pashley DH, Tay FR, Yiu C, Hashimoto M, Breschi L, Carvalho RM, et al. Collagen degradation by host-derived enzymes during aging. J Dent Res. 2004;83:216-21. and/or by cysteine cathepsins2727 - Vidal CM, Tjäderhane L, Scaffa PM, Tersariol IL, Pashley D, Nader HB, et al. Abundance of MMPs and cysteine cathepsins in caries-affected dentin. J Dent Res. 2014;93:269-74.. MMPs are secreted as inactive proenzymes, but promote the degradation of collagen fibril, elastin and extracellular matrix components when activated. It is known that these enzymes can be activated at a lower pH – as occurs when dentin is conditioned by acid etching – but function the best in a neutral pH1313 - Mazzoni A, Pashley DH, Nishitani Y, Breschi L, Mannello F, Tjäderhane L, et al. Reactivation of inactivated endogenous proteolytic activities in phosphoric acid-etched dentine by etch-and-rinse adhesives. Biomaterials. 2006;27:4470-6. – as occurs following application of the etch-and-rinse adhesive system. The collagenolytic function of MMPs is also relevant in caries-affected dentin tissue, since they are activated at a low pH, during bacteria lactic fermentation and subsequent neutralization by dentin buffer systems2424 - Tjäderhane L, Larjava H, Sorsa T, Uitto VJ, Larmas M, Salo T. The activation and function of host matrix metalloproteinases in dentin matrix breakdown in caries lesions. J Dent Res 1998;77:1622-9..
The understanding of how the mechanism of action of MMPs and cysteine cathepsins influences collagen degradation has encouraged the development and evaluation of substances that may inhibit their function. Among these substances, chlorhexidine has been promoted as a synthetic inhibitor of MMPs, since it does not interfere with the immediate bonding to the dental substrate33 - Campos EA, Correr GM, Leonardi DP, Barato-Filho F, Gonzaga CC, Zielak JC. Chlorhexidine diminishes the loss of bond strength over time under simulated pulpal pressure and thermo-mechanical stressing. J Dent. 2009;37(2):108-14.,1212 - Komori PC, Pashley DH, Tjäderhane L, Breschi L, Mazzoni A, Goes MF, et al. Effect of 2% chlorhexidine digluconate on the bond strength to normal versus caries-affected dentin. Oper Dent. 2009;34:157-65.,1616 - Monteiro TM, Basting RT, Turssi CP, França FM, Amaral FL. Influence of natural and synthetic metalloproteinase inhibitors on bonding durability of an etch-and-rinse adhesive to dentin. Int J Adhes Adhes. 2013;47:83-8. and increases the longevity of adhesive restorations44 - Carrilho MR, Geraldeli S, Tay F, Goes MF, Carvalho RM, Tjäderhane L, et al. In vivo preservation of the hybrid layer by chlorhexidine. J Dent Res. 2007;86:529-33.,1111 - Hebling J, Pashley DH, Tjäderhane L, Tay FR. Chlorhexidine arrests subclinical degradation of dentin hybrid layers in vivo. J Dent Res. 2005;84:741-16.. Green tea, on the other hand, has been described as a natural inhibitor of MMPs77 - Demeule M, Brossard M, Pagé M, Gingras D, Béliveau R. Matrix metalloproteinase inhibition by green tea catechins. Biochim Biophys Acta. 2000;1478:51-60.. It is made from Camellia sinensis and is composed of polyphenols named catechins, such as epicatechin (EC), epigallocatechin (EGC), epicatechin gallate (ECG) and epigallocatechin gallate (EGCG), pointing out that ECG and EGCG are strongly related to MMP inhibition77 - Demeule M, Brossard M, Pagé M, Gingras D, Béliveau R. Matrix metalloproteinase inhibition by green tea catechins. Biochim Biophys Acta. 2000;1478:51-60.. Results from a previous study1616 - Monteiro TM, Basting RT, Turssi CP, França FM, Amaral FL. Influence of natural and synthetic metalloproteinase inhibitors on bonding durability of an etch-and-rinse adhesive to dentin. Int J Adhes Adhes. 2013;47:83-8. revealed that application of a green tea solution reduced immediate bond strength to dentin, but kept it stable in the long-term. However, the effect of green tea extract application on the bond durability of an etch-and-rinse adhesive to caries-affected dentin has not yet been assessed.
Considering the relevance of studying bond strength to caries-affected dentin, and seeking to find alternative approaches in the context of retarding hybrid layer degradation, this study aimed at making an in vitro assessment of the effect of two metalloproteinase inhibitors, chlorhexidine and green tea, applied after acid etching, on bond durability of an etch-and-rinse adhesive system to caries-affected dentin, after six months of storage in water. The null hypothesis to be tested was that neither the MMP inhibitor solution nor the water storage period would have any effect on bond strength to caries-affected dentin.
MATERIAL AND METHODS
Ethical aspects
The present study was approved by the Local Research Ethics Committee (No. 2012/0200).
Experimental design
This in vitro study involved a microbiological model of dentin caries induction, according to that proposed by Sanabe, et al.1818 - Sanabe ME, Costa CA, Hebling J. Exposed collagen in aged resin-dentin bonds produced on sound and caries-affected dentin in the presence of chlorhexidine. J Adhes Dent. 2011;13:117-24. (2011). The factors under study were: 1. The solution applied to the dentin surface after acid conditioning: 2% green tea extract (GT) or 2% chlorhexidine digluconate solution (CLX), compared with the control group (no treatment – NT); 2. Time points of microtensile bond strength testing: after storage in water for 24 hours or for 6 months.
The quantitative outcome variable was the microtensile bond strength value, in MPa. The bond strength average of sticks from the same tooth became the value for that particular experimental unit. The failure pattern was described in terms of percentages.
The materials cited in the experimental design, as well as their composition and mode of use, are described in Figure 1.
Dentin slab preparation
Thirty human third molars, extracted for reasons not related to those of the present research and stored in thymol (0.1%, pH 7.0) after extraction, were used in this experiment. The teeth were submitted to debriding with scalpel blades and periodontal curettes. Then, they were cross-sectioned using a water-cooled diamond saw (15 HC series, Buehler Ltd., Lake Bluff, IL, USA) in a sectioning machine (Isomet 1000 Precision Diamond Saw, Buehler Ltd., Lake Bluff, IL, USA), which removed the occlusal third from the crown to obtain a large dentin surface in the middle third, perpendicular to the long axis of the tooth. Dentin surfaces were flattened in a water-cooled polishing machine (Politriz Aropol 2V, Arotec, São Paulo, SP, Brazil) with decreasing granulations (#400, #600 and #1200) of water abrasive paper (Imperial Wetordry, 3M, Sumaré, SP, Brazil).
Artificial caries induction protocol
The protocol for artificial caries induction was obtained from the study by Sanabe, et al.1818 - Sanabe ME, Costa CA, Hebling J. Exposed collagen in aged resin-dentin bonds produced on sound and caries-affected dentin in the presence of chlorhexidine. J Adhes Dent. 2011;13:117-24. (2011). In brief, the tooth root apices were sealed with a microhybrid composite resin (Filtek Z250, 3M ESPE, St Paul, MN, USA) and the teeth were rendered waterproof with one layer of epoxy resin (Araldite, Ciba Especialidades Químicas, São Paulo, SP, Brazil) and one layer of an acid resistant varnish (nail polish, Colorama, CEIL, São Paulo, SP, Brazil), leaving only the dentin surface exposed. All the teeth were then autoclaved at 121°C for 20 min.
A 2% Streptococcus mutans strain ATCC 25175 (108 cfu/ml) (André Toselo Foundation Tropical Culture Collection) was inoculated into a pre-autoclaved cariogenic solution. The teeth were immerged in the cariogenic solution and incubated in microaerophilia for 14 days. During this period, the cariogenic solution was renewed every 48 hours, but without inoculation of new S. mutans strains. Autoclaving was repeated after the end of the incubation period. The biofilm was removed with gauze, and the insulating materials (varnish and epoxy resin) were removed with scalpel blades. The teeth were then rinsed with distilled and deionized water.
Adhesive procedures
The infected dentin was removed with a #4 spherical steel bur at low speed, which was replaced after 5 times of use. The softened dentin tissue was removed until obtaining tissue that was harder and more resilient to the touch with a probe, without exerting pressure on the dentin. A single operator was calibrated to perform this procedure.
Dentin slabs were submitted to conditioning with 37% phosphoric acid for 15 seconds and rinsed with distilled water for the same amount of time. They were randomly divided into three groups, according to the solution to be applied to the dentin surface: 2% GT, 2% CLX, or NT (no solution applied, used as control). In brief, solutions of twenty microliters of 2% GT or of 2% CLX were passively applied to dentin for 60 seconds. The dentin was dried gently with absorbent paper. The etch-and-rinse adhesive system was then applied to the dentin fragments, which were restored with a microhybrid resin composite (Filtek Z250, 3M ESPE, St. Paul, MN, USA). The final resin-dentin blocks were 4-mm high. Light polymerization was performed on both the adhesive system (Adper™ Single Bond 2, 3M ESPE, St. Paul, MN, USA) and the microhybrid composite, for the time recommended by the manufacturers (Figure 1), using a visible light-curing unit (Ultralux EL, Dabi Atlante, Ribeirão Preto, SP, Brazil). The output of the light-curing unit was measured periodically with a radiometer (Newdent Equipamentos Ltda., Ribeirão Preto, SP, Brazil), and a minimal range of 630 mW/cm2 was observed.
The resin-dentin blocks were kept in relative humidity at 37°C for 24 hours and sectioned perpendicularly to the bonding surface into 0.9-mm thick slabs, using a water-cooled diamond saw. Multiple beam-shaped sticks were obtained by rotating samples 90° and sectioning them again lengthwise, each with a cross-sectional surface area of 0.8 mm2. Half of the sticks from the same resin-dentin block were submitted to µTBS testing after 24 hours. The other half was kept in distilled water, which was changed every two days, and kept in a bacteriological oven for 6 months.
Microtensile bond strength (µTBS) Testing
The specimens were attached to a µTBS testing device with cyanoacrylate adhesive (Super Bonder Gel, Henkel Ltda., Itapevi, SP, Brazil). They were subjected to tensile stress in a universal testing machine at a crosshead speed of 0.5 mm/min and a 50 N load cell until fracture. The bond strength values were expressed in kgf/cm2 and converted to MPa after measuring of the cross-sectional area at the fracture site with a digital caliper (Mitutoyo Corp, Tokyo, Japan). The comparison was conducted using the average value of each tooth (n=10).
After bond strength testing, the failure pattern of each stick was analyzed under a stereomicroscope (EK3ST, CQA, São Paulo, SP, Brazil) at 30x magnification to assess the failure modes, which were classified as adhesive (lack of adhesion), cohesive in dentin (failure of the dental substrate), cohesive in composite resin (failure of the resin composite) or mixed (adhesive and cohesive failures).
Statistical analysis
Based on the normal distribution of the data, two-way analysis of variance (ANOVA) for completely randomized blocks and Tukey’s test were applied. Statistical calculations were performed with SPSS 20 (SPSS Inc., Chicago, IL, USA). The significance level was set at 5%. The failure pattern was described with descriptive statistics (percentage terms).
RESULTS
The two-way ANOVA for randomized blocks showed that there was significant interaction between the specific treatments and the time periods (p=0.003). Tukey’s test indicated that there was no significant difference in bond strength between the groups treated with green tea and with chlorhexidine, as compared to the control group after 24 hours (Table 1). In contrast, the group to which green tea extract was applied yielded significantly higher bond strength values after 6 months (Table 1). Moreover, there was no significant difference in bond strength values after 6 months of storage, except for the group to which green tea was applied, which showed significant increase in strength, in relation to the 24-hour period.
As for the failure mode (Figure 2), it was observed that, after 24 hours of storage in water, the group that received no treatment (control) presented a predominance of adhesive failure (63%), followed by mixed (18%), cohesive in resin composite (15%) and cohesive in dentin (5%) failures. In comparison, after 6 months of storage, most of the failures in the same group (control) were of the adhesive type (35%), followed by mixed failures (33%), failure of the resin composite (25%) and cohesive failure in dentin (8%).
Most of the failures in the group to which chlorhexidine digluconate was applied were adhesive (48%), followed by cohesive in resin composite (25%), mixed (18%) and cohesive in dentin (10%), at the 24-hour time point, whereas, after 6 months of water storage, most of the failures in the same group were mixed (45%), followed by adhesive (33%), cohesive in dentin (13%), and cohesive in resin composite (10%).
Most of the failures in the group to which green tea was applied were cohesive in dentin (45%), followed by mixed (23%), cohesive in resin composite (20%), and adhesive (13%), at the 24-hour time point, whereas, after 6 months, most of the failures in the same group were adhesive (35%), followed by mixed (33%), cohesive in resin composite (25%), and cohesive in dentin (8%).
DISCUSSION
The knowledge that dentin matrix metalloproteinases and cysteine cathepsins are involved in the hybrid layer degradation process has driven the search for substances that inhibit the action of these enzymes2727 - Vidal CM, Tjäderhane L, Scaffa PM, Tersariol IL, Pashley D, Nader HB, et al. Abundance of MMPs and cysteine cathepsins in caries-affected dentin. J Dent Res. 2014;93:269-74.. Among them, the most prominent substance is chlorhexidine digluconate, a synthetic inhibitor of MMPs and cysteine cathepsins2525 - Tjäderhane L, Nascimento FD, Breschi L, Mazzoni A, Tersariol IL, Geraldeli S, et al. Strategies to prevent hydrolytic degradation of the hybrid layer-A review. Dent Mater. 2013;29:999-1011..
Most of the studies that assess the degradation of the hybrid layer and the role of the MMPs in this process involve performing adhesive system procedures on sound dentin22 - Brackett WW, Tay FR, Brackett MG, Dib A, Sword RJ, Pashley DH. The effect of chlorhexidine on dentin hybrid layers in vivo. Oper Dent. 2007;32:107-11.,44 - Carrilho MR, Geraldeli S, Tay F, Goes MF, Carvalho RM, Tjäderhane L, et al. In vivo preservation of the hybrid layer by chlorhexidine. J Dent Res. 2007;86:529-33.,1111 - Hebling J, Pashley DH, Tjäderhane L, Tay FR. Chlorhexidine arrests subclinical degradation of dentin hybrid layers in vivo. J Dent Res. 2005;84:741-16.,2020 - Soares CJ, Pereira CA, Pereira JC, Santana FR, Prado CJ. Effect of chlorhexidine application on microtensile bond strength to dentin. Oper Dent. 2008;33:183-8.,2222 - Stape TH, Menezes MS, Barreto BC, Aguiar FH, Martins LR, Quagliatto PS. Influence of matrix metalloproteinase synthetic inhibitors on dentin microtensile bond strength of resin cements. Oper Dent. 2012;37:386-96.,3030 - Zheng P, Zaruba M, Attin T, Wiegand A. Effect of different matrix metalloproteinase inhibitors on microtensile bond strength of an etch-and-rinse and a self-etching adhesive to dentin. Oper Dent. 2015;40:80-6.. However, the hybrid layer formed on caries-affected dentin (CAD) is more irregular and has greater collagen exposure1818 - Sanabe ME, Costa CA, Hebling J. Exposed collagen in aged resin-dentin bonds produced on sound and caries-affected dentin in the presence of chlorhexidine. J Adhes Dent. 2011;13:117-24.,2828 - Wang Y, Spencer P, Walker MP. Chemical profile of adhesive/caries-affected dentin interfaces using Raman microspectroscopy. J Biomed Mater Res A. 2007;81:279-86., with reduced bond strength, in comparison with sound dentin99 - Erhardt MC, Toledano M, Osorio R, Pimenta LA. Histomorphologic characterization and bond strength evaluation of caries-affected dentin/resin interfaces: effects of long-term water exposure. Dent Mater. 2008;24:786-98.,2929 - Yoshiyama M, Urayama A, Kimochi T, Matsuo T, Pashley DH. Comparison of conventional vs self etching adhesive bonds to caries-affected dentin. Oper Dent. 2000;25:163-9.. Moreover, hydrolytic degradation is more pronounced in the CAD adhesive interface99 - Erhardt MC, Toledano M, Osorio R, Pimenta LA. Histomorphologic characterization and bond strength evaluation of caries-affected dentin/resin interfaces: effects of long-term water exposure. Dent Mater. 2008;24:786-98., where MMPs and cysteine cathepsins exert substantial activity2727 - Vidal CM, Tjäderhane L, Scaffa PM, Tersariol IL, Pashley D, Nader HB, et al. Abundance of MMPs and cysteine cathepsins in caries-affected dentin. J Dent Res. 2014;93:269-74..
Thus, this study aimed at assessing the effect of both synthetic (2% chlorhexidine) and natural (2% green tea extract) metalloproteinase inhibitor solutions, when applied after acid conditioning, on either immediate or long-term bond strength of an etch-and-rinse adhesive system to caries-affected dentin. The null hypothesis was rejected, since the results of this research have shown that 2% green tea extract (natural inhibitor of metalloproteinases) was able to increase long-term bond strength significantly. On the other hand, the application of 2% chlorhexidine (synthetic inhibitor of metalloproteinases) was able to maintain the long-term bond strength on a level equal to that of the control group.
Studies have shown that 2% chlorhexidine used as a therapeutic dentin pretreatment did not interfere with immediate bond strength22 - Brackett WW, Tay FR, Brackett MG, Dib A, Sword RJ, Pashley DH. The effect of chlorhexidine on dentin hybrid layers in vivo. Oper Dent. 2007;32:107-11.,44 - Carrilho MR, Geraldeli S, Tay F, Goes MF, Carvalho RM, Tjäderhane L, et al. In vivo preservation of the hybrid layer by chlorhexidine. J Dent Res. 2007;86:529-33.,1414 - Mobarak EH. Effect of chlorhexidine pretreatment on bond strength durability of caries-affected dentin over 2-year aging in artificial saliva and under simulated intrapulpal pressure. Oper Dent. 2011;36:649-60.,1616 - Monteiro TM, Basting RT, Turssi CP, França FM, Amaral FL. Influence of natural and synthetic metalloproteinase inhibitors on bonding durability of an etch-and-rinse adhesive to dentin. Int J Adhes Adhes. 2013;47:83-8.,2020 - Soares CJ, Pereira CA, Pereira JC, Santana FR, Prado CJ. Effect of chlorhexidine application on microtensile bond strength to dentin. Oper Dent. 2008;33:183-8., corroborating the results of this study. A recent meta-analytic review1515 - Montagner AF, Sarkis-Onofre R, Pereira-Cenci T, Cenci MS. MMP inhibitors on dentin stability: a systematic review and meta-analysis. J Dent Res. 2014;93:733-43. has shown that 2% chlorhexidine does not affect the immediate bond strength to dentin and improves the bond after 6 months in water storage. However, the control group (no treatment) in the present study also presented bond stability over time; that is, the control and the chlorhexidine groups presented statistically similar results. It is hypothesized that chlorhexidine substantivity does not exceed 8 weeks33 - Campos EA, Correr GM, Leonardi DP, Barato-Filho F, Gonzaga CC, Zielak JC. Chlorhexidine diminishes the loss of bond strength over time under simulated pulpal pressure and thermo-mechanical stressing. J Dent. 2009;37(2):108-14. or 3 months2121 - Souza M, Cecchin D, Farina AP, Leite CE, Cruz FF, Pereira CC, et al. Evaluation of chlorhexidine substantivity on human dentin: a chemical analysis. J Endod. 2012;38:1249-52., and that the specimens in stick form may have facilitated the dissolution of the chlorhexidine solution, therefore curbing a more beneficial effect. Nonetheless, when analyzing the control group, in which no bond strength alteration was observed after 6 months, other considerations should be borne in mind. First, all the teeth were autoclaved, as a measure to promote microbiological caries induction1818 - Sanabe ME, Costa CA, Hebling J. Exposed collagen in aged resin-dentin bonds produced on sound and caries-affected dentin in the presence of chlorhexidine. J Adhes Dent. 2011;13:117-24.. It can be speculated that high temperatures may affect proteinases by denaturing them. Sanabe, et al.1818 - Sanabe ME, Costa CA, Hebling J. Exposed collagen in aged resin-dentin bonds produced on sound and caries-affected dentin in the presence of chlorhexidine. J Adhes Dent. 2011;13:117-24. (2011) stated that MMP-8 is more fragile in resisting high temperatures, whereas gelatinases such as MMP-2 are more resistant. Although autoclaving may reduce enzymatic activity, the study by these authors1818 - Sanabe ME, Costa CA, Hebling J. Exposed collagen in aged resin-dentin bonds produced on sound and caries-affected dentin in the presence of chlorhexidine. J Adhes Dent. 2011;13:117-24. showed that aging in water for 6 months resulted in degradation of the resin-dentin bond, and that this degradation decelerated in the presence of chlorhexidine. Another important hypothesis is related to the researched storage time of 6 months. According to De Munck, et al.66 - De Munck J, Mine A, Poitevin A, Van Ende A, Cardoso MV, Van Landuyt KL, et al. Meta-analytical review of parameters involved in dentin bonding. J Dent Res. 2012;91:351-7. (2012), the simple water storage of specimens has a clear bond-degrading effect. However, the literature makes no definitive conclusion in regard to the minimal period of water storage that promotes degradation in the hybrid layer and a consequent decrease in bond strength. By applying an adhesive system under simulated intrapulpal pressure and storing specimens for two years in artificial saliva, Mobarak, et al.1414 - Mobarak EH. Effect of chlorhexidine pretreatment on bond strength durability of caries-affected dentin over 2-year aging in artificial saliva and under simulated intrapulpal pressure. Oper Dent. 2011;36:649-60. (2011) observed that the bond strength to caries-affected dentin was similar between 2% chlorhexidine-treated and non-treated dentin. However, at a concentration of 5%, chlorhexidine was able to prevent loss in bond strength after 2 years. Another point is related to water as the storage medium. Based on the conclusion that MMPs require zinc and calcium to trigger activity, Tezvergil-Mutluay, et al.2323 - Tezvergil-Mutluay A, Agee KA, Hoshika T, Carrilho M, Breschi L, Tjäderhane L, et al. The requirement of zinc and calcium ions for functional MMP activity in demineralized dentin matrices. Dent Mater. 2010;26:1059-67. (2010) reported that using water as a storage medium underestimates the hydrolytic activity of endogenous dentin MMPs, because it promoted the loss of calcium and zinc ions from dentin matrices, rather than restoring them. In this context, the use of solutions that simulate oral fluids and longer storage periods should be researched in future studies.
The most surprising result of this research is that the 2% green tea extract increased the etch-and-rinse adhesive system bond strength. Bond stability has been reported using 0.05% green tea extract in 9 months of water storage3030 - Zheng P, Zaruba M, Attin T, Wiegand A. Effect of different matrix metalloproteinase inhibitors on microtensile bond strength of an etch-and-rinse and a self-etching adhesive to dentin. Oper Dent. 2015;40:80-6.. The application of diluted green tea obtained from commercially sold tea was found to be prejudicial to the immediate bond strength of the etch-and-rinse adhesive to human dentin; however, after 6 months of storage in water, the bond remained stable, without showing any detrimental or beneficial effects1616 - Monteiro TM, Basting RT, Turssi CP, França FM, Amaral FL. Influence of natural and synthetic metalloproteinase inhibitors on bonding durability of an etch-and-rinse adhesive to dentin. Int J Adhes Adhes. 2013;47:83-8.. Industrialized green tea has many other compounds associated with it, and this may have contributed to the initial, unfavorable results in the study by Monteiro, et al.1616 - Monteiro TM, Basting RT, Turssi CP, França FM, Amaral FL. Influence of natural and synthetic metalloproteinase inhibitors on bonding durability of an etch-and-rinse adhesive to dentin. Int J Adhes Adhes. 2013;47:83-8. (2013). In fact, it has been proposed that the application of a solution containing the main catechin in green tea - epigallocatechin gallate (EGCG) - in pretreatment form1919 - Santiago SL, Osorio R, Neri JR, Carvalho RM, Toledano M. Effect of the flavonoid epigallocatechin-3-gallate on resin-dentin bond strength. J Adhes Dent. 2013;15:535-40. or incorporated into the etch-and-rinse adhesive system88 - Du X, Huang X, Huang C, Wang Y, Zhang Y. Epigallocatechin-3-gallate (EGCG) enhances the therapeutic activity of a dental adhesive. J Dent. 2012;40:485-92. promotes significant bonding stability to dentin, compared with the control group (no treatment), as well as increased bond strength to bleached enamel, due to the antioxidant properties also exhibited by EGCG. Although the studies reporting the effects of EGCG application on dentin MMP inhibition are scant, it has been reported that EGCG significantly enhances both the pro- and active-MMP-2 binding to TIMP-2, the natural MMP inhibitor physiologically present in dentin55 - Cheng XW, Kuzuya M, Kanda S, Maeda K, Sasaki T, Wang QL, et al. Epigallocatechin-3-gallate binding to MMP-2 inhibits gelatinolytic activity without influencing the attachment to extracellular matrix proteins but enhances MMP-2 binding to TIMP-2. Arch Biochem Biophys. 2003;415:126-32..
Moreover, because the studies evaluating green tea extract and EGCG solutions on dentin are scarce, and because most studies have been conducted on sound dentin, the comparison of results has been rendered difficult. It is speculated that green tea extract could have increased the bond strength of the etch-and-rinse adhesive system because it was tested on caries-affected dentin, where the occurrence of MMPs and cysteine cathepsins is aggravated2727 - Vidal CM, Tjäderhane L, Scaffa PM, Tersariol IL, Pashley D, Nader HB, et al. Abundance of MMPs and cysteine cathepsins in caries-affected dentin. J Dent Res. 2014;93:269-74.. Additionally, because green tea polyphenol contains EGCG, it has been classified as a proanthocyanidin (PAC), a highly hydroxylated structure capable of forming an insoluble complex with proteins11 - Bedran-Russo AK, Pauli GF, Chen SN, McAlpine J, Castellan CS, Phansalkar RS, et al. Dentin biomodification: strategies, renewable resources and clinical applications. Dent Mater. 2014;30:62-76.. For this reason, green tea polyphenol has been advocated as a natural collagen cross-linking agent, able to enhance the mechanical properties of dentin and to reduce the dentin biodegradability of host-derived MMPs11 - Bedran-Russo AK, Pauli GF, Chen SN, McAlpine J, Castellan CS, Phansalkar RS, et al. Dentin biomodification: strategies, renewable resources and clinical applications. Dent Mater. 2014;30:62-76.. In fact, cohesive in dentin failures were more prevalent (45%) at the 24-hour period of water storage than at the 6-month period (8%).
As for the failure mode of the experimental groups, there was a predominance of adhesive and mixed failures. Monteiro, et al.1616 - Monteiro TM, Basting RT, Turssi CP, França FM, Amaral FL. Influence of natural and synthetic metalloproteinase inhibitors on bonding durability of an etch-and-rinse adhesive to dentin. Int J Adhes Adhes. 2013;47:83-8. (2013) noted that their reported failures did not seem to follow any pattern according to treatment type, and highlighted the high frequency of adhesive and mixed failures, not only in the control group but also in the 2% chlorhexidine and the green tea groups. Mobarak, et al.1414 - Mobarak EH. Effect of chlorhexidine pretreatment on bond strength durability of caries-affected dentin over 2-year aging in artificial saliva and under simulated intrapulpal pressure. Oper Dent. 2011;36:649-60. (2011) observed that there was a predominance of adhesive and mixed failure modes when using 2% and 5% chlorhexidine as a pretreatment when the specimens were tested for bond strength after 24 hours of storage. After testing the specimens for bond strength after 6 months of water storage under simulated pulpal pressure, Campos, et al.22 - Brackett WW, Tay FR, Brackett MG, Dib A, Sword RJ, Pashley DH. The effect of chlorhexidine on dentin hybrid layers in vivo. Oper Dent. 2007;32:107-11. (2007) observed that most of the failure modes belonged to the adhesive type when using 2% chlorhexidine as a pretreatment.
Considering the above, it is suggested that further studies should be conducted using green tea extract as a metalloproteinase inhibitory and bioactive substance, not only in performing mechanical tests, as in this study, but also in order to ascertain the inhibitory effect of green tea extract on the presence and activity of dentin MMPs.
CONCLUSION
It was concluded that the application of a green tea extract solution was able to increase the long-term bond strength to caries-affected dentin. Neither the application of chlorhexidine nor non-treatment (NT - control) had any effect on the bond strength after water storage.
ACKNOWLEDGEMENTS
We wish to thank the CNPq - National Council for Scientific and Technological Development for its support (Grant No. 126431/2013-2).
REFERENCES
-
1- Bedran-Russo AK, Pauli GF, Chen SN, McAlpine J, Castellan CS, Phansalkar RS, et al. Dentin biomodification: strategies, renewable resources and clinical applications. Dent Mater. 2014;30:62-76.
-
2- Brackett WW, Tay FR, Brackett MG, Dib A, Sword RJ, Pashley DH. The effect of chlorhexidine on dentin hybrid layers in vivo. Oper Dent. 2007;32:107-11.
-
3- Campos EA, Correr GM, Leonardi DP, Barato-Filho F, Gonzaga CC, Zielak JC. Chlorhexidine diminishes the loss of bond strength over time under simulated pulpal pressure and thermo-mechanical stressing. J Dent. 2009;37(2):108-14.
-
4- Carrilho MR, Geraldeli S, Tay F, Goes MF, Carvalho RM, Tjäderhane L, et al. In vivo preservation of the hybrid layer by chlorhexidine. J Dent Res. 2007;86:529-33.
-
5- Cheng XW, Kuzuya M, Kanda S, Maeda K, Sasaki T, Wang QL, et al. Epigallocatechin-3-gallate binding to MMP-2 inhibits gelatinolytic activity without influencing the attachment to extracellular matrix proteins but enhances MMP-2 binding to TIMP-2. Arch Biochem Biophys. 2003;415:126-32.
-
6- De Munck J, Mine A, Poitevin A, Van Ende A, Cardoso MV, Van Landuyt KL, et al. Meta-analytical review of parameters involved in dentin bonding. J Dent Res. 2012;91:351-7.
-
7- Demeule M, Brossard M, Pagé M, Gingras D, Béliveau R. Matrix metalloproteinase inhibition by green tea catechins. Biochim Biophys Acta. 2000;1478:51-60.
-
8- Du X, Huang X, Huang C, Wang Y, Zhang Y. Epigallocatechin-3-gallate (EGCG) enhances the therapeutic activity of a dental adhesive. J Dent. 2012;40:485-92.
-
9- Erhardt MC, Toledano M, Osorio R, Pimenta LA. Histomorphologic characterization and bond strength evaluation of caries-affected dentin/resin interfaces: effects of long-term water exposure. Dent Mater. 2008;24:786-98.
-
10- Fusayama T. Two layers of carious dentine: diagnosis and treatment. Oper Dent. 1979;4(2):63-70.
-
11- Hebling J, Pashley DH, Tjäderhane L, Tay FR. Chlorhexidine arrests subclinical degradation of dentin hybrid layers in vivo. J Dent Res. 2005;84:741-16.
-
12- Komori PC, Pashley DH, Tjäderhane L, Breschi L, Mazzoni A, Goes MF, et al. Effect of 2% chlorhexidine digluconate on the bond strength to normal versus caries-affected dentin. Oper Dent. 2009;34:157-65.
-
13- Mazzoni A, Pashley DH, Nishitani Y, Breschi L, Mannello F, Tjäderhane L, et al. Reactivation of inactivated endogenous proteolytic activities in phosphoric acid-etched dentine by etch-and-rinse adhesives. Biomaterials. 2006;27:4470-6.
-
14- Mobarak EH. Effect of chlorhexidine pretreatment on bond strength durability of caries-affected dentin over 2-year aging in artificial saliva and under simulated intrapulpal pressure. Oper Dent. 2011;36:649-60.
-
15- Montagner AF, Sarkis-Onofre R, Pereira-Cenci T, Cenci MS. MMP inhibitors on dentin stability: a systematic review and meta-analysis. J Dent Res. 2014;93:733-43.
-
16- Monteiro TM, Basting RT, Turssi CP, França FM, Amaral FL. Influence of natural and synthetic metalloproteinase inhibitors on bonding durability of an etch-and-rinse adhesive to dentin. Int J Adhes Adhes. 2013;47:83-8.
-
17- Pashley DH, Tay FR, Yiu C, Hashimoto M, Breschi L, Carvalho RM, et al. Collagen degradation by host-derived enzymes during aging. J Dent Res. 2004;83:216-21.
-
18- Sanabe ME, Costa CA, Hebling J. Exposed collagen in aged resin-dentin bonds produced on sound and caries-affected dentin in the presence of chlorhexidine. J Adhes Dent. 2011;13:117-24.
-
19- Santiago SL, Osorio R, Neri JR, Carvalho RM, Toledano M. Effect of the flavonoid epigallocatechin-3-gallate on resin-dentin bond strength. J Adhes Dent. 2013;15:535-40.
-
20- Soares CJ, Pereira CA, Pereira JC, Santana FR, Prado CJ. Effect of chlorhexidine application on microtensile bond strength to dentin. Oper Dent. 2008;33:183-8.
-
21- Souza M, Cecchin D, Farina AP, Leite CE, Cruz FF, Pereira CC, et al. Evaluation of chlorhexidine substantivity on human dentin: a chemical analysis. J Endod. 2012;38:1249-52.
-
22- Stape TH, Menezes MS, Barreto BC, Aguiar FH, Martins LR, Quagliatto PS. Influence of matrix metalloproteinase synthetic inhibitors on dentin microtensile bond strength of resin cements. Oper Dent. 2012;37:386-96.
-
23- Tezvergil-Mutluay A, Agee KA, Hoshika T, Carrilho M, Breschi L, Tjäderhane L, et al. The requirement of zinc and calcium ions for functional MMP activity in demineralized dentin matrices. Dent Mater. 2010;26:1059-67.
-
24- Tjäderhane L, Larjava H, Sorsa T, Uitto VJ, Larmas M, Salo T. The activation and function of host matrix metalloproteinases in dentin matrix breakdown in caries lesions. J Dent Res 1998;77:1622-9.
-
25- Tjäderhane L, Nascimento FD, Breschi L, Mazzoni A, Tersariol IL, Geraldeli S, et al. Strategies to prevent hydrolytic degradation of the hybrid layer-A review. Dent Mater. 2013;29:999-1011.
-
26- Tyas MJ, Anusavice KJ, Frencken JE, Mount GJ. Minimal intervention dentistry - a review. FDI Commission Project 1-97. Int Dent J. 2000;50:1-12.
-
27- Vidal CM, Tjäderhane L, Scaffa PM, Tersariol IL, Pashley D, Nader HB, et al. Abundance of MMPs and cysteine cathepsins in caries-affected dentin. J Dent Res. 2014;93:269-74.
-
28- Wang Y, Spencer P, Walker MP. Chemical profile of adhesive/caries-affected dentin interfaces using Raman microspectroscopy. J Biomed Mater Res A. 2007;81:279-86.
-
29- Yoshiyama M, Urayama A, Kimochi T, Matsuo T, Pashley DH. Comparison of conventional vs self etching adhesive bonds to caries-affected dentin. Oper Dent. 2000;25:163-9.
-
30- Zheng P, Zaruba M, Attin T, Wiegand A. Effect of different matrix metalloproteinase inhibitors on microtensile bond strength of an etch-and-rinse and a self-etching adhesive to dentin. Oper Dent. 2015;40:80-6.
Publication Dates
-
Publication in this collection
May-Jun 2016
History
-
Received
23 Nov 2015 -
Reviewed
28 Jan 2016 -
Accepted
8 Mar 2016