ABSTRACT
This paper describes the polycarbonate acrylic laminated development that can be applied in aeronautics and aerospace transparencies. The case studied is a laminated double-curved transparency (bubble form) used in an observation side window of a military aircraft. Side windows need strength and specific characteristics, similar to windshields, allowing the perfect visualization and image capture. Laminated transparencies composed by different materials have better qualities than the monolithic ones. This kind of transparency can offer high mechanical and chemical resistance, high transparency, no fragmentation and easy maintenance or recovery. A significant amount of information about materials and processes was jointed in order to build the reinforced transparency and validate this study. The final results were analyzed based on two points of view: mechanic resistance and, especially, optical quality.
Keywords
Transparency; Laminated polycarbonate; Acrylic; Window
INTRODUCTION
Whenever it is necessary to see or capture images through a protective barrier, it arises the need to define it and build it as effectively and efficiently as possible. The problem that comes from this observation is to measure all the variables that can influence the requirements and, mostly important, to define the materials that can be used, as well as the methods and processes that will lead to the manufacture of a quality product. The materials chosen, suitable for the construction of reinforced transparencies for aerospace industry, as windshields, must to be taken into account, as well as all loads they are subjected to, including structural terms, mechanical and thermal loads (Fam and Rizkalla 2006Fam A, Rizkalla S (2006) Structural performance of laminated and unlaminated tempered glass under monotonic transverse loading. Construct Build Mater 20(9):761-768. doi: 10.1016/j.conbuildmat.2005.01.051
https://doi.org/10.1016/j.conbuildmat.20...
). In addition, superior optical characteristics are also essential (Fixler 1977Fixler SZ (1977) Thermsstructural and material considerations in the design of the F-14 Aircraft Transparencies. J Aircraft, 14(3):257-264.).
The modern engineering and architecture “design” requires glazing materials that offer high levels of safety and high-performance mechanical properties. These properties include: ballistic resistance; wind loads; explosion; and physical attacks resistance. In some applications, noise level reduction, solar radiation resistance, and thermal barrier behavior are also desirable. The laminated glazing is the union of multiple layers of various materials such as glass, polymeric films, resins, and flexible sheets of transparent polymers (polycarbonate and/or acrylic), usually applied to obtain complex geometric shapes (Fixler 1977Fixler SZ (1977) Thermsstructural and material considerations in the design of the F-14 Aircraft Transparencies. J Aircraft, 14(3):257-264.; Smith et al. 1996Smith FC, Moloney LD, Matthews FL, Hodges J (1996) Fabrication of woven carbon fibre/polycarbonate repair patches. Compos Appl Sci Manuf 27(11):1089-1095. doi: 10.1016/1359-835X(96)00070-X
https://doi.org/10.1016/1359-835X(96)000...
).
It is necessary a prior knowledge of the physicochemical properties of the engineering materials to make the right choice for each application. To the right choice, it is necessary to know the load or the effort to which the transparency must resist and the kind of effort that will be neutralized by the transparent barrier. However, it should be clear that there will always be an effort that can overcome the barrier, because there is no definitive mechanical barrier. Thus, the barrier will be “strengthened” until reaching the desired resistance and including a safety factor.
Besides the mechanical strength, transparent barriers must have optical quality, being able to see or capture images by means of high light transmission level, with a minimum deviation or absorption, until the images reach the observer’s eye or the image capture device.
Reinforced transparencies are not only intended to prevent a mechanical failure, but to perform with maximum efficiency and preferably not releasing fragments that reach whom or what will be protected by the transparent barrier. The objective of this study was to describe the information needed to design and to construct a reinforced transparency for aerospace application made with polymeric materials, which is part of the “observation window” of a military patrol aircraft.
MATERIALS AND METHODS
MATERIALS CHOICE
The materials chosen for the observation window were based on MIL-PRF-5425E (1998) and MIL-P-46144C (1986). The chosen structural materials, in sheet form, were: acrylic or polymethylmethacrylate – PMMA (ASTM D4802-02) (Modified “cast” acrylic ACRYLITE® 249, CYRO Ind, USA); polycarbonate – PC (Fox and Christopher 1962Fox DW, Christopher WF (1962) Polycarbonates. New York: Reinhold Publishing Corporation.; LeGrant and Bendler 2000LeGrant DG, Bendler JT (2000) Handbook of polycarbonate science and technology. New York: Marcel Dekker.) (LEXAN® 9034, GE-Plastics, USA); and, for bonding, in film form, polyurethane – PU (KRYSTALFLEX®PE399, Huntsman, USA), which is the material that allows a good adhesion between acrylic and polycarbonate.
The following sequence was used to prepare the specimens: two outer layers with 3.18 mm thickness of acrylic (PMMA); a central PC layer with 6.35 mm thickness; and between acrylic and PC layers, two aliphatic PU layers with 1.27 mm thickness were inserted. In other words, the final composition was: PMMA + PU + PC + PU + PMMA (Fig. 1).
TEMPERATURE RESISTANCE TEST
Two samples with nominal size (20 × 10 cm) were prepared and laminated in the same way of the shearing test samples. The samples were submitted to 100 °C for 50 min, using a circulating air oven (Kamp).
SPECIMENS PREPARATION
All the raw material plates were cut into dimensions much larger than the finished parts, using a circular saw. After this process, the plates were dehumidified at 100 °C, during 6 h in an air circulating oven.
The dehumidified materials were laminated in the sequence previously defined. A vacuum bag was prepared around the laminated (all the bagging materials are from Airtech®, USA; vacuum film and sealant tape). The set, formed by the laminate and the vacuum bag, was placed in an autoclave (FERLEX®, Brazil) to be bonded. To ensure the bonding material, the set formed by the laminate and the vacuum bag was heat-treated to 120 °C for 2 h at a 2 °C/min heating rate and pressured at 0.7 MPa inside the autoclave. The temperature and pressure were maintained during 3 h; then, it was cooled until the ambient temperature was reached. At the end, the pressure was released and the cycle, finished.
THERMOFORMING PROCESS
After autoclave process, the set was placed on a tool designed for the observation window manufacture. The tooling (Fig. 2) was heated to 180 °C at a 6 °C/min heating rate. After the laminate reached the melting point, it was blown at a pressure of 0.14 MPa to achieve its definitive new shape. The specimen was then cooled at 2 °C/min.
The part trimming was performed in a conventional manner using bandsaw and sander. The polishing was done using fine finishing hand tools and then through sandpapers and finer abrasives, until it reached the desired polishing. The specimen, properly polished, was placed against a reticule grid to check possible optical distortions.
SHEARING TESTS IN PLANE
Six samples with nominal size (4.0 × 5.0 cm; section area: 20 cm2) were prepared using the following materials: an acrylic sheet, with 3.18 mm thickness, adhered to a PC sheet, with 6.35 mm thickness. For the sheets adhesion, it was used an aliphatic PU crystal adhesive film with 1.27 mm thickness.
The samples were laminated in the same way of the observation window. They were tested after 48 h of stabilization. The shearing test was performed in plane (Fig. 3) using MIL-P-25690B (1995) as general references. It was used an electromechanical testing machine for tension and compression Tinus Olsen brand, model H100KS, with maximum capacity of 100 kN. The test speeds were 3 and 5 mm/min.
RESULTS AND DISCUSSION
MATERIALS CHOICE
Nowadays, most of civil and military aircraft windows are made with acrylic (PMMA) due to its transparency, availability, strength and ease maintenance, fulfilling all the aviation requirements and standards (Blass 1985Blass A (1985) Processamento de polímeros. Florianópolis: UFSC.; LaPluma and Bridenbaugh 1988LaPluma PT, Bridenbaugh JC (1988) Specifications and measurement procedures for aircraft transparencies. Wright-Patterson AFB, OH: Armstrong Aerospace Medical Research Laboratory.). This material also meets the requirements for external surfaces of reinforced transparency. However, in case of violent impact, it can shatter, causing sudden aircraft depressurization. To satisfy the high impact strength requirement, the best polymer is PC, already used in military fighter aircraft canopies (Wiser 1971Wiser GL (1971) Transparency applications of polycarbonates. Aircraft Eng 43(8):18-20. doi: 10.1108/eb034797
https://doi.org/10.1108/eb034797...
). Both materials have high light transmission levels and they are thermoformable. To connect these two materials, the aliphatic PU films (Plepis 1991Plepis AMD (1991) Caracterização térmica e viscoelástica de resinas poliuretanas derivadas do óleo de mamona (Master’s thesis). São Paulo: Universidade de São Paulo.; Vilar 1991Vilar WD (1991) Química e tecnologia dos poliuretanos. 2nd ed. Rio de Janeiro: Vilar Consultoria Técnica Ltda.) can be used, providing the adhesion between layers. Table 1 shows the properties of the chosen materials for the manufacture of aircraft observation window.
After materials selection, it was carried out a temperature resistance test to verify the laminate behavior at 100 °C.
There was no appearance of undesirable bubbles, yellowing, delamination or any other conduct that could compromise the functions of the laminate or its general appearance. It was also verified that the temperature would not compromise the good light transmission without distortion or deformation.
SHAPE DETERMINATION
The final shape of the transparency is better defined by the obtaining process than by a geometry defined through engineering software (Fig. 4). The method used to obtain the transparency form was the thermoforming by blowing compressed air (Blass 1985Blass A (1985) Processamento de polímeros. Florianópolis: UFSC.), since it allows the material to expand freely until the desired format is obtained.
Orthogonal views and transparency section. A-A: Height; B-B: Width; L-A: Vertical vision angle; L-B: Horizontal vision angle; H: Depth.
The expansion process by free blowing determines the shape and cooperates with the optical quality, avoiding deformities, and it does not cause undesirable distortions in contact with the tool — they are visible only at the edges of transparency. The result by thermoforming is an elliptical paraboloid shape (Fig. 5), caused by laminated thinning (more in the center than in the edges), because of area increasing and thickness loss.
OPTICAL DISTORTIONS
Samples submitted for verification did not have relevant distortions, detected by the human eye, which could compromise the good appearance of the grid images captured through the transparence (Fig. 6). However, it was detected the presence of a slight optical power due to thickness variation at the center of the part, resulting from thinning, occurred during the thermoforming process, which creates a kind of diverging lenses. The contact with the thermoforming tool produces contact marks that are manifested in the form of distortion of the edge part; however, these distortions do not affect the results, when transparency is in use, since it does not become apparent because this region is covered by the transparency frame.
The optical distortions verification (Fixler 1977Fixler SZ (1977) Thermsstructural and material considerations in the design of the F-14 Aircraft Transparencies. J Aircraft, 14(3):257-264.) is an important parameter in reinforced transparencies (Pardini and Peres 1996Pardini LC, Peres RJC (1996) Tecnologia de fabricação de pré-impregnados para compósitos estruturais utilizados na indústria aeronáutica. Polímeros 6(2):32-42.). The reinforced transparency, besides being considered a barrier to prevent an effort to continue, should allow observing or capturing images through it with the best possible quality, not adding deviations image distortions, retain the light wavelength or filter visible spectrum.
All the images captured during the transparencies flight test had an excellent clarity and no visible distortions, which confirmed the prior results obtained with the grid.
SHEARING RESULTS IN PLANE
Aircraft side windows have a significant temperature differential between inner and outer layer, as much higher as the aircraft flying altitude. The internal temperature is usually around 20 °C, and the outer temperature can be less than −54 °C, so the dimensional variation between layers produces high big shear forces that must be compensated by the polyurethane layer elasticity. In this case, the PU adhesion between acrylic and/or polycarbonate must be verified. The shear test indicates the degree of adhesion acquired by the laminated.
Each trial lasted until a little over 2 min, since the total displacement was around 6 mm. Tables 2 and 3 contain the results obtained in the shear test.
The test speed of 3 mm/min was appropriate, according to the behavior observed, which does not present a premature rupture and produces a clear “load × deflection” curve. The standard deviation in general demonstrates a short range of values, or more reliability in the results obtained. The test speed of 5 mm/min does not produce results with small variation, since the values obtained were two or three times higher than the values obtained with test speed of 3 mm/min.
The maximum shear stress average demonstrates a satisfactory adhesion degree between layers in both speed tests and was greater than the expected.
A more detailed analysis of the displacement data between the sheets of acrylic and polycarbonate may provide an order of magnitude for the lengthening ability of the polyurethane adhesive, but the PU manufacturer (Huntsman, USA) indicates 500% of elongation at the KRYSTALFLEX® PE399 datasheet (Huntsman 2015Huntsman (2015) KRYSTALFLEX® PE399 data sheet on line. [accessed 2015 Oct 15]. http://www.huntsman.com/polyurethanes
http://www.huntsman.com/polyurethanes...
).
All samples tested were broken or showed detachment from plastic layers. The S2 had supported the major load, and S4, the minor one. Figure 7 shows a typical curve of “load × deflection” generated by S2 test.
CONCLUSIONS
The objective was achieved by implementing the proposed road map, which was to organize some of the information needed to design and to construct a reinforced transparency for an aerospace application, which is part of the “observation window” of a military patrol aircraft, as well as to validate such information through the construction of the transparency and analysis of the results.
The combination of the techniques used and the layers union in an appropriate and sequential manner was essential for the construction of transparency, which was successfully completed. Any failure would not allow the following step.
The optical results allow to state that the material choices were appropriate, especially on the composition and position of them. The acrylic usage on the internal and external faces of transparency had ensured the necessary optical quality. The fabrication process chosen, by the free expanding thermoforming, guaranteed a regular format of the visible area because there were no contacts with any tool.
All samples presented a satisfactory adhesion degree between layers during the shearing tests in plane. The parameters of speed test were greater than the expected, but this did not affect the results; the samples showed mechanical resistance parameters required by the aeronautical industry. Therefore, it was possible to demonstrate the technological knowledge necessary for the development and manufacture of reinforced aerospace transparencies for this type of application.
REFERENCES
- Blass A (1985) Processamento de polímeros. Florianópolis: UFSC.
- Fam A, Rizkalla S (2006) Structural performance of laminated and unlaminated tempered glass under monotonic transverse loading. Construct Build Mater 20(9):761-768. doi: 10.1016/j.conbuildmat.2005.01.051
» https://doi.org/10.1016/j.conbuildmat.2005.01.051 - Fixler SZ (1977) Thermsstructural and material considerations in the design of the F-14 Aircraft Transparencies. J Aircraft, 14(3):257-264.
- Fox DW, Christopher WF (1962) Polycarbonates. New York: Reinhold Publishing Corporation.
- Huntsman (2015) KRYSTALFLEX® PE399 data sheet on line. [accessed 2015 Oct 15]. http://www.huntsman.com/polyurethanes
» http://www.huntsman.com/polyurethanes - LaPluma PT, Bridenbaugh JC (1988) Specifications and measurement procedures for aircraft transparencies. Wright-Patterson AFB, OH: Armstrong Aerospace Medical Research Laboratory.
- LeGrant DG, Bendler JT (2000) Handbook of polycarbonate science and technology. New York: Marcel Dekker.
- Pardini LC, Peres RJC (1996) Tecnologia de fabricação de pré-impregnados para compósitos estruturais utilizados na indústria aeronáutica. Polímeros 6(2):32-42.
- Plepis AMD (1991) Caracterização térmica e viscoelástica de resinas poliuretanas derivadas do óleo de mamona (Master’s thesis). São Paulo: Universidade de São Paulo.
- Smith FC, Moloney LD, Matthews FL, Hodges J (1996) Fabrication of woven carbon fibre/polycarbonate repair patches. Compos Appl Sci Manuf 27(11):1089-1095. doi: 10.1016/1359-835X(96)00070-X
» https://doi.org/10.1016/1359-835X(96)00070-X - Vilar WD (1991) Química e tecnologia dos poliuretanos. 2nd ed. Rio de Janeiro: Vilar Consultoria Técnica Ltda.
- Wiser GL (1971) Transparency applications of polycarbonates. Aircraft Eng 43(8):18-20. doi: 10.1108/eb034797
» https://doi.org/10.1108/eb034797
Publication Dates
-
Publication in this collection
Jan-Mar 2016
History
-
Received
19 Nov 2015 -
Accepted
04 Feb 2016