Abstract
This work is a study of the microstructural properties of the polycrystalline ternary compounds AgIn5S8, AgIn5Se8, and AgIn5Te8 by X-ray diffraction technique (XRD). The full-width-half-maximum (FWHM) of the XRD profile is measured as function of the diffraction angle and used to estimate the microstructural parameters. In general, a microstructural characterization by XRD is principally performed by Strain/Size analysis based on the modified Scherrer formula, which in turn, allows for mean grain size and average microstrain to be computed. However, when applied to polycrystalline bulk semiconductors, the modified Scherrer formula gives grain sizes of the order of a few hundreds of nanometers, which is not usually observed in bulk materials. Instead, a new theoretical scheme with misfit dislocations and plastic deformations would be used to calculate the grain size into a bulk. Assuming that these dislocations are of elastic origin, we were able to calculate the misfit dislocations density as function of the elastic constants of the materials. With this, the modified Scherrer formula is corrected to explain the additional XRD line broadening. All microstructure parameters of our samples increase as the atomic radius of the VI-element increases, with elastic constants similar to related semiconducting compounds.
Keywords:
Strain/Size analysis; Modified Scherrer Equation; microstructural parameters; ternary semiconductors AgIn5VI8; Poisson ratio
1. Introduction
Ternary semiconductors provide a natural way of tuning the desired band gap and flexibility to control other material parameters by changing the relative composition of the pure elements in the alloy. A special group of ternaries are those based on the groups of elements I-III-VI, such as Ag(In, Ga)(S, Te, Se), CuInSe2 and AgGaTe2.11 Delgado GE, Mora AJ. Structural characterization of the semiconductor chalcogenide system Ag-In-VI (VI=S, Se, Te) by X-ray power diffraction. Chalcogenide Letters. 2009;51:635-639.
2 Zhang SB, Wei S, Zunger A. Stabilization of Ternary Compounds via Ordered Arrays of Defect Pairs. Physical Review Letters. 1997;78(21):4059.-33 Burger A, et al. Preparation and thermophysical properties of AgGaTe2 crystals. Journal of Crystal Growth. 2001;225(2-4):505-511. These alloys crystallize in the non-centrosymmetric chalcopyrite structure, leading to non-zero second order nonlinear susceptibility. This gives these compounds promising features for technological applications, including infrared optoelectronic devices and solar cells applications.44 Matsushita H, Takashi M, Katsui A, Takizawa T. Thermal analysis andsynthesis from the melts of Cu-based quaternary compounds Cu-III-IV-VI4 and Cu2-II-IV-VI4 (II=Zn, Cd; III=Ga, In; IV=Ge, Sn; VI=Se). Journal of Crystal Growth. 2000;208(1-4):416-422.,55 Krustok J, Jagomägi A, Grossberg M, Raudoja J, Danilson M. Photoluminescence properties of polycrystalline AgGaTe2. Solar Energy Materials & Solar Cells. 2006;90:1973-1982. Another group of semiconductors that have gained much attention during recent years are those from the family of I-III5-VI8 compounds.66 Sánchez A, et al. Structural, optical, and electrical properties of AgIn5Te8. Journal of Applied Physics. 2005;97(5):053505-4.
7 Charoenphakdee A, Kurosaki K, Muta H, Uno M, Yamanaka S. Thermal conductivity of the ternary compounds: AgMTe2 and AgM5Te8 (M = Ga or In). Materials Transactions. 2009;50(7):1603-1606.-88 Rincón CAD, Durán LT, Medina JE, Castro JA, León M, Fermín JR. Structural and optical properties of AgIn5S8. International Journal of Modern Physics B. 2017;31(31):1750246-10. These alloys present a tetragonal or orthorhombic structure depending on the ion of group III, and a cubic-spinel or tetragonal structure depending on the group VI element,77 Charoenphakdee A, Kurosaki K, Muta H, Uno M, Yamanaka S. Thermal conductivity of the ternary compounds: AgMTe2 and AgM5Te8 (M = Ga or In). Materials Transactions. 2009;50(7):1603-1606. and have optical band gaps suitable for optimum energy conversion solar cells, and thermoelectric properties useful for applications in waste-heat recovery, air conditioning, and refrigeration.
The optical and thermal properties of semiconductor materials are closely related to morphology and grain size.99 Kalihari V, Tadmor EB, Haugstad G, Frisbie CD. Grain Orientation Mapping of Polycrystalline Organic Semiconductor Films by Transverse Shear Microscopy. Advanced Materials. 2008;20(21):4033-4039. Understanding this relationship is critically important to many industrial processes. Furthermore, the physical properties of the semiconductor elements involved in the design of microelectronic devices are highly dependent on their microstructural parameters, such as degree of crystallinity, crystallographic orientation, grain size, elastic/plastic deformation, etc.1010 deWit R. Elastic Constants and Thermal Expansion Averages of a Nontextured Polycrystral. Jounal of Mechanics and Structures. 2008;3(2):193-212. Among the various experimental methods used for determination of the microstructural parameters in polycrystalline solids, X-ray diffraction (XRD)-based techniques play an important role in materials science.1111 Warren BE. X-Ray Diffraction. Massachusetts: Addison-Wesley Pub. Co.; 1969. This is because the XRD patterns are very sensitive to the crystallographic structure and orientation, phase changes, structural defects, chemical composition, etc., which are essential in the interpretation of the physical data. On the other hand, any XRD measurement must be followed by a theoretical analysis method in order to provide a suitable interpretation of the diffraction spectra, and this turns into an essential issue in materials science research. The most widely-used method in microstructural analysis in bulk materials is the Strain/Size method.1212 Mittemeijer EJ, Welzel U. The "state of the art" of the diffraction analysis of crystallite size and lattice strain. Zeitschrift für Kristallographie. 2008;223:552-560. This technique for analysis is based on the interpretation of the broadening of the diffraction lines on the framework of the Scherrer equation,1313 Pérez FV, Gando NJ, Castro JÁ, Rincón CAD, Durán L, Fermin JR. Structural properties of and morphology of the quaternary semiconductor AgIn4GaTe8. Journal of Material Sciences & Engineering. 2015;4(1):1-4. from which, microstructural parameters, such as grain size and average microstrain, are determined. It is apparent that these two parameters are the most relevant in the description of a microstructure; however, when an actual sample is subjected to strain forces, structural defects must be introduced in order to stabilize the crystalline lattice. These structural defects are called misfit dislocations and contribute to an extra broadening in the experimental full-width at half-maximum (FWHM) of the XRD lines. These defects are not usually taken into account in a conventional microstructural analysis based on the Scherrer equation, so some corrections are needed in order to provide a more realistic description of a microstructure.
2. Experimental Methods
Three polycrystalline ingots of AgIn5S8, AgIn5Se8, and AgIn5Te8 were prepared by direct fusion of the stoichiometric mixture (DFSM) of the elements of at least 5N purity, following a synthesis program similar to that outlined by Pérez et al.1313 Pérez FV, Gando NJ, Castro JÁ, Rincón CAD, Durán L, Fermin JR. Structural properties of and morphology of the quaternary semiconductor AgIn4GaTe8. Journal of Material Sciences & Engineering. 2015;4(1):1-4. The samples were synthesized inside evacuated quartz ampoules (≈ 10-6 Torr). The ampoules were very slowly heated in a vertical furnace, from room temperature up to 858 °Cat a heating rate of about 5 °C/h, lower enough to prevent an explosion due to exothermic reactions between group III and group VI elements. The samples are kept at this temperature during 48 hours, and rocked at regular intervals to achieve a homogeneous mixing of the liquid phase of the reacting mixture, and then cooled at the same rate of5 °C/h. At such slow cooling rate the formation of undesirable phases is also prevented.
The X-ray diffraction patterns were performed using a Bruker D8 Focus powder diffractometer with the CuKα1 characteristic line (1.5405 Å), and in the Bragg-Brentano geometry. The diffraction patterns were collected in the range 5°≤ 2θ≤ 100°, with a step size of 0.02, and a step time of 15.0 sec. The diffraction spectra were indexed by using the WINPLOTR/TREOR 90 graphic interface, and the lattice parameters were then calculated. The microstructural parameters of the samples were determined from the full-width-half-maximum (FWHM) of their XRD profiles, using a Strain/Size analysis method based on a theoretical model which will subsequently be described in more detail.
3. Theoretical Considerations
3.1 The Modified Scherrer Equation
The microstructural analysis by XRD of solid materials is based on the calculation of certain physical parameters, such as grain size, strain forces, crystalline materials dislocations, and elastic modulii. In general, the grain is a composite of several crystallites made-up of unit cells, and is often related to the full-width-half-maximum (FWHM) of the diffraction pattern, by means of the well-known Scherrer equation.1414 Patterson AL. The Scherrer Formula for X-Ray Particle Size Determination. Physical Review. 1939;56:978.
where βL is the FWHM in radians; K=2[ln(2)/π]1/2 is a constant related to the grain shape, and is of the order of ≅ 0.93 for spherical grains; λ is the X-ray wavelength in Å, L the average size of the grain/crystallite in Å, and θ the Bragg angle in degrees. The Scherrer formula is useful when the grain/crystallite size is considered to be primarily responsible for the broadening of XRD peaks and predicts real L-values in the case when the grain and crystallite sizes are similar. The limit of application of Scherrer Equation stills a matter of discussion, and in fact some authors set this limit below 100 nm,1515 Monshi A, Foruoghi MR, Monshi MR. Modified Scherrer Equation to Estimate More Accurately Nano-Crystallite Size Using XRD. World Journal of Nano Science and Engineering. 2012;2(3):154-160. while some others argue that it is only valid for grain sizes less than 200 nm.1313 Pérez FV, Gando NJ, Castro JÁ, Rincón CAD, Durán L, Fermin JR. Structural properties of and morphology of the quaternary semiconductor AgIn4GaTe8. Journal of Material Sciences & Engineering. 2015;4(1):1-4. More recently, Muniz et al.1616 Muniz FTL, Miranda MA, Santos CM, Sasaki JM. The Scherrer equation and the dynamical theory of X-ray diffraction. Acta Crystallographica. Section A, Foundations and Advances. 2016;72(Pt 3):385-390. establish a criterion according to which, the limit of applicability of the Scherrer Equation depends on the crystalline reflections and on the XRD absorption.
In a polycrystalline sample, the assumption that the crystallite size matches the grain size is not always valid. In these materials, grains are made up of small crystallites oriented in all directions. In this case, the size effects could be overwhelmed by an anisotropic microstructure, characterized by the presence of microstrains between atomic planes. In order to stabilize the grain size, the microstrains must be compensated by local elastic forces, as a consequence inducing misfit dislocations and mosaicities, deformations, stacking faults, vacancies, composition gradients, etc. Due to this relaxation process, the lines of the XRD profile display an additional broadening, represented by the expression,1717 Danilchenko S, Kukharenko OG, Moseke C, Protsenko IY, Sukhodub LF, Sulkio-Cleff B. Determination of the Bone Mineral Crystallite Size and Lattice Strain from Diffraction Line Broadening. Crystal Research and Technology. 2002;37(11):1234-1240.
where ε = (d'-d)/d is the microstrain between crystalline planes and is a measure of the elastic deformation; d and d' are the interplanar distances before and after deformation, respectively. Another aspect to be considered in our analysis is the aberration introduced by the diffractometer to the FWHM, or instrumental broadening, βinst. The instrumental broadening is parameterized from a reference silicon data using the Caglioti's formula,1818 Caglioti G, Paoletti A, Ricci FP. On resolution and luminosity of a neutron diffraction spectrometer for single crystal analysis. Nucl Instrum Methods. 1960;9(2):195-198.
where U, V and W are fitting parameters to the base XRD-line. In our case, U= 0.000010, V= 0.0000015, and W= 0.0000055. With this, the FWHM, β(θ), relates to microstructure parameters through the direct sum of each contribution1919 Pavel K, Woodward PM. Liquid-Mix Disorder in Crystalline Solids: ScMnO3. Journal of Solid State Chemistry. 1998;141(1):78-88.
Eq. (4) is often used when the profile of the diffraction line corresponds to a Lorentzian function. These profiles are typically observed when the micro-deformations field is isotropic, and size effects overwhelm the microstrains distribution. In the case of many polycrystalline solids the deformation field is anisotropic, however, contributing to the line broadening with a Gaussian profile, and with FWHM given by the quadratic expression2020 Balzar D, Popovic DS. Advances in X-ray Analysis. Journal of Applied Crystallography. 1996;29:16-23.
Expressions (4) and (5) are known as the modified Scherrer formulae and are the fundamental basis for the Strain/Size analysis by XRD in solid materials. In general, in polycrystalline materials with low crystallinity, the profile of the XRD spectrum corresponds to a linear combination of a Lorentzian line to a Gaussian line, making the FWHM analysis rather complicated. The microstructural parameters L and ε are determined from least square fits with Eqs. (4) or (5), according to the case. The L-values predicted by the modified Scherrer Equations are still of the order of some hundreds of nm, which are in most cases unrealistic in the case of bulk polycrystalline materials. This is because as the polycrystalline sample approaches the bulk, grain sizes of the order of a few microns are observed. In this range of sizes, the density of lattice dislocations increases and must be explicitly taken into account, introducing an additional line broadening given by β2D = 9b2ρD,2121 Yazici R, Kalyon D. Microstrain and defect analysis of CL-20 crystals by novel methods. Journal of Energetic Materials. 2005;23(1):43-58. where ρD is the misfit dislocation density per unit area, and b is the module of the Burger vector which defines the direction of the dislocations line perpendicular to the hkl plane. The problem now becomes finding an analytical expression for the function ρD. This is not an easy task, since the structure of a dislocation line is in general very complex. However, since the lattice dislocations are strictly elastic in origin, the problem reduces to calculation of the dislocation density at mechanical equilibrium, as will be shown in the following section.
3.2 Elastic Relaxation. Mechanical Properties
The problem of elastic relaxation in semiconductors has been a subject of great interest during the past decades.2222 Matthews JW, Mader S, Light TB. Accomodation of misfit across the interface between crystals of semiconducting elements or compounds. Journal of Applied Physics. 1970;41(9):3800-3804. This is because strain/stress forces give adequate information regarding materials' elastic constant, and in turn, provide a way to control the mechanical properties. Intuitively, at equilibrium, the energy of elastic forces along dislocation lines must satisfy the condition Eel = ED, with Eel and ED being the strain energy density and the energy density stored by misfit dislocations, respectively. This is a necessary condition for mechanical stabilization of the material, and it is useful in the study of elastic properties, as will be shown in greater detail. The energy density of elastic deformations is given by (within the Hooke's law approximation)
where ε is the average microstrain, and B is the bulk modulus related to the elastic constants of the material, which are,2323 Nye JF. Physical properties of crystals. London: Oxford University Press; 1957.
In particular, for a single cubic crystal B = (C11+2C12)/3. As mentioned above, accurate calculations of the misfit dislocations energy are further complicated, since a dislocation line is a complex structure. In the usual case the energy of an array of dislocations is the elastic energy stored within the dislocation line. If the strain field is distributed along screw and edge dislocations, the misfit dislocation energy density is calculated following the model discussed by Sutton and Balluffi.2424 Sutton AP, Balluffi RW. Interfaces in crystalline materials. Oxford: Oxford Science Publications; 1995. v. 51. It is then obtained that,
with μ being the effective shear modulus, ν the Poisson ratio, L the size of a grain/crystallite intercepting a dislocation line, b the modulus of the corresponding Burger vector, ρD the misfit dislocation density per unit area, and ϕ the angle between the Burger vector and the dislocation line, in the range from 0 (screw) to π/2 (edge). The Poisson ratio gives information on the material's plasticity and is defined as the negative ratio "transversal-strain/longitudinal-strain" for the unit cell (-1 <ν< 0.5). Most semiconductors exhibit positive ν-values, which indicate that when subjected to a strain force the material elongates longitudinally, while it is compressed transversally. In contrast, there are certain special man-made materials that can exhibit a negative Poisson's ratio and are called "auxetic". In order for any solid structure be stable, elastic energy must be absorbed in the same amount along each crystalline direction. Integrating Eq. (8) gives the total energy density due to misfit dislocations as,
After applying the elastic equilibrium condition, Eel = ED, to energies (6) and (9), we obtain that the misfit dislocation density due to plastic deformations is given by,
Considering the constitutive relation β/μ = 2(1+ν)/3(1-2ν),2525 Den Toonder JMJ, Van Dommelen JAW, Baaijens FPT. The relation between single crystal elasticity and the effective elastic behavior of polycrystalline materials: theory, measurement and computation. Modelling and Simulation in Materials Science and Engineering. 1999;7(6):909-928. and the Burger vector satisfying Bragg's law, the correction to the XRD line broadening due to misfit dislocations is,
With this, the modified Scherrer formulae for Lorentzian and Gaussian profiles are now corrected and expressed in the form,
According to this framework, the effect of the strain forces is two-fold: as the material is stretched/compressed, misfit dislocations and plastic deformations are necessarily introduced in order for the lattice structure can be sustained. In this new scheme, the modified Scherrer equations are redefined and now allow estimation not only of grain sizes and micro strains, but also of the fundamental Poisson ratio.
4. Results and Discussion
The XRD spectrum of the ternary semiconductor AgIn5S8 is shown in Fig. 1. This profile corresponds to a cubic-spinel structure with lattice parameter a = 10.8217 Å, in agreement with previous reports.88 Rincón CAD, Durán LT, Medina JE, Castro JA, León M, Fermín JR. Structural and optical properties of AgIn5S8. International Journal of Modern Physics B. 2017;31(31):1750246-10. The cubic-spinel crystalline structure is characteristic of a class of minerals called aluminum spinels, whose general crystalline formula is A2+B3+O2-. The AB cations alternate between octahedral and tetrahedral sites, while the O anions arrange into a closed-pack cubic structure. The insert in Fig. 1 presents a characteristic peak of this profile, which fits reasonably to a Gaussian line shape (continuous curve).
Profile of the XRD spectrum of the compound AgIn5S8.The lineshape of the diffraction peaks correspond in general to a Gaussian profile, as observed from the inserted figure.
On the other hand, the XRD spectra for AgIn5Se8 and AgIn5Te8 are shown in Figs. 2-3 and are in agreement with results published earlier.2626 Medina JE, Durán LT, Castro J, Fermín JR, Hernández J, Rincón CAD. Structural and optical properties of AgIn5Se8. Materials Science: An Indian Journal. 2015;12(5):178-184.,2727 Sánchez A, Meléndez L, Castro J, Hernández JA, Hernández E, Rincón CAD. Structural, optical, and electrical properties of AgIn5Te8. Journal of Applied Physics. 2005;97(5):053505. Both systems display tetragonal structures with lattice parameters a = 5.795224 Å, c = 11.622806 Å in AgIn5Se8, and a = 6.2120 Å, c = 12.4561 Å in AgIn5Te8; with characteristic c/a ≅ 2.005 tetragonal distortion in both samples. As in the case of AgIn5S8 these profiles are almost Gaussian, as is demonstrated by the continuous curves shown in the inserted panels. This fact assures that the FWHM of the XRD profile and the diffraction angle satisfy the relation (13).
Profile of the XRD spectrum of the compound AgIn5Se8. The lineshape of the diffraction peaks correspond in general to a Gaussian profile, as observed from the inserted figure.
Profile of the XRD spectrum of the compound AgIn5Te8. The lineshape of the diffraction peaks fit in general to a Gaussian profile, as observed from the inserted figure.
The values of the XRD FWHM, βFWHM, determined from the experimental spectra of all samples, are plotted in Fig. 4. It is observed that βFWHM is almost constant at small diffraction angles, up to a critical value, θC, at which the line broadening increases nonlinearly. Similar behavior has been reported in related semiconducting compounds such as AgIn4GaTe8.1616 Muniz FTL, Miranda MA, Santos CM, Sasaki JM. The Scherrer equation and the dynamical theory of X-ray diffraction. Acta Crystallographica. Section A, Foundations and Advances. 2016;72(Pt 3):385-390. Notice that the θC value coincides with the strongest reflection peak, with a shift from ≅ 13.65° to ≅ 12.39° as the atomic number, z, of the anion VI increases from 16 up to 54. This shift can be understood considering Bragg's law, senθC=λ/2d(z), from which we can verify that the interplanar distance calculated at θC satisfies the inequality d(S) <d(Se) <d(Te). The continuous curves in Fig. 4 are non-linear numerical fits to the experimental data using Eq. (13), following a Levenberg-Marquardt scheme.2828 Vetterling WT, Teukolsky SA, Press WH, Flannery BP. Numerical Recipes. 2nd ed. Cambridge: Cambridge University Press; 1992. The values of the parameters obtained from these fits are listed in Table 1. The agreement between theory and experiment is good for the set of parameters (L, ε, ν), satisfying the theoretical conditions discussed in section 3.2. Notice that both grain size and microstrain increase along with the atomic number of the anion VI, with increasing Poisson ratio. This means that our samples are highly anisotropic with the Poisson ratio typical of other related ternaries.2929 Martínez AM, Soriano R, Faccio R, Trigubó AB. Mechanical Properties Calculation of II-VI Semiconductors: Cd1-yZnyTe (0≤y≤1). Procedia Materials Science. 2015;8:656-664. The grain sizes obtained with our model are of the order of a few microns, which is reasonable in bulk polycrystalline materials.3030 Berbenni S, Favier V, Berveiller M. Impact of the grain size distribution on the yield stress of heterogeneous materials. International Journal of Plasticity. 2007;23(1):114-142.,3131 He Y, Winnubst L, Burggraaf AJ, Verweij H, Van der Varst PG, With B. Grain-Size Dependence of Sliding Wear in Tetragonal Zirconia Polycrystals. Journal of the American Ceramic Society. 1996;79(12):3090-96.
Full-Width-Half-Maximum (βFWHM) as function of the diffraction angle for each sample. The solid curves are numerical fits of the experimental data using equation (13). The fitting parameters obtained from these fits are listed in Table 1. The dashed-dotted curve is calculated with the modified Scherrer formula (5), and the dashed curve corresponds to the conventional Scherrer formula.
Microstructural parameters (L,ε,ν) of the system AgIn5VI8 determined from numerical fits with Equation (13), as discussed in Section 4. For comparison, the parameters obtained from the modified Scherrer (MS) and conventional Scherrer (S) formulae are also included.
By comparison, the curves obtained from the Scherrer (S) and the Modified Scherrer (MS) equations are also shown in Fig.4. Notice that the agreement between experimental data and the MS equation is also reasonable for the corresponding pair of parameters (LMS, εMS) listed in Table 1. Although the average microstrain, εMS, is comparable to the value of ε, the grain size, LMS, is of the order of ≈ 250 nm. However, as mentioned before, such small grain sizes are not usually observed in bulk polycrystalline materials. On the other hand, the conventional Scherrer formula (1), can only fit the experimental line broadening at diffraction angles smaller than θC, and departs from the experimental data at diffraction angles θ>θC, giving much smaller grain sizes of the order of ≈ 50 nm.
5. Conclusions
The microstructural properties of polycrystalline semiconductors AgIn5VI8 (VI=S, Se, Te) are studied applying the Strain/Size method to the Full-Width-Half-Maximum of the x-ray diffraction profiles. From our analysis we can conclude:
-
The FWHM of the diffraction line as a function of θ cannot be explained by the modified Scherrer formulae in their original forms, since these give in most cases unrealistic grain sizes for a polycrystalline sample.
-
In order to give a more realistic interpretation of the FWHM, misfit dislocations must be included explicitly. In this framework, plastic deformations are important. The Poisson ration, ν, then appears as a fundamental microstructural parameter beside the mean grain size, L, and the average microstrain, ε. In this way, the modified Scherrer formulae are then corrected with an additional line broadening, βD.
-
The values of the microstructural parameters (L, ε, ν) for the ternary system AgIn5VI8 depend on the atomic radius of the VI element. In particular, according to our model, the Poisson ration is positive in all samples and of the same order than those found in related semiconducting materials, which indicate that all these semiconductors have similar mechanical properties.
The detection and quantification of microstrains and microstructural defects in polycrystalline compounds and granular systems are, in general, complex tasks, since several parameters are involved, requiring highly sensitive techniques and more fundamental theoretical studies. However, the results reported here could be of relevance for future applications of AgIn5VI8 in diverse semiconducting processes and microelectronic devices.
6. Acknowledgements
The Authors wish to thank the agencies Consejo de Desarrollo Científico y Humanístico-LUZ (CONDES) (CC-0595-10), and FONACIT (201100542) by their financial support. At the same time we also thank the staff of the Centro Nacional de DRX (ULA) for technical support in the XRD measurements.
7. References
-
1Delgado GE, Mora AJ. Structural characterization of the semiconductor chalcogenide system Ag-In-VI (VI=S, Se, Te) by X-ray power diffraction. Chalcogenide Letters 2009;51:635-639.
-
2Zhang SB, Wei S, Zunger A. Stabilization of Ternary Compounds via Ordered Arrays of Defect Pairs. Physical Review Letters 1997;78(21):4059.
-
3Burger A, et al. Preparation and thermophysical properties of AgGaTe2 crystals. Journal of Crystal Growth 2001;225(2-4):505-511.
-
4Matsushita H, Takashi M, Katsui A, Takizawa T. Thermal analysis andsynthesis from the melts of Cu-based quaternary compounds Cu-III-IV-VI4 and Cu2-II-IV-VI4 (II=Zn, Cd; III=Ga, In; IV=Ge, Sn; VI=Se). Journal of Crystal Growth 2000;208(1-4):416-422.
-
5Krustok J, Jagomägi A, Grossberg M, Raudoja J, Danilson M. Photoluminescence properties of polycrystalline AgGaTe2. Solar Energy Materials & Solar Cells 2006;90:1973-1982.
-
6Sánchez A, et al. Structural, optical, and electrical properties of AgIn5Te8 Journal of Applied Physics 2005;97(5):053505-4.
-
7Charoenphakdee A, Kurosaki K, Muta H, Uno M, Yamanaka S. Thermal conductivity of the ternary compounds: AgMTe2 and AgM5Te8 (M = Ga or In). Materials Transactions 2009;50(7):1603-1606.
-
8Rincón CAD, Durán LT, Medina JE, Castro JA, León M, Fermín JR. Structural and optical properties of AgIn5S8 International Journal of Modern Physics B 2017;31(31):1750246-10.
-
9Kalihari V, Tadmor EB, Haugstad G, Frisbie CD. Grain Orientation Mapping of Polycrystalline Organic Semiconductor Films by Transverse Shear Microscopy. Advanced Materials 2008;20(21):4033-4039.
-
10deWit R. Elastic Constants and Thermal Expansion Averages of a Nontextured Polycrystral. Jounal of Mechanics and Structures 2008;3(2):193-212.
-
11Warren BE. X-Ray Diffraction Massachusetts: Addison-Wesley Pub. Co.; 1969.
-
12Mittemeijer EJ, Welzel U. The "state of the art" of the diffraction analysis of crystallite size and lattice strain. Zeitschrift für Kristallographie 2008;223:552-560.
-
13Pérez FV, Gando NJ, Castro JÁ, Rincón CAD, Durán L, Fermin JR. Structural properties of and morphology of the quaternary semiconductor AgIn4GaTe8. Journal of Material Sciences & Engineering 2015;4(1):1-4.
-
14Patterson AL. The Scherrer Formula for X-Ray Particle Size Determination. Physical Review 1939;56:978.
-
15Monshi A, Foruoghi MR, Monshi MR. Modified Scherrer Equation to Estimate More Accurately Nano-Crystallite Size Using XRD. World Journal of Nano Science and Engineering 2012;2(3):154-160.
-
16Muniz FTL, Miranda MA, Santos CM, Sasaki JM. The Scherrer equation and the dynamical theory of X-ray diffraction. Acta Crystallographica. Section A, Foundations and Advances 2016;72(Pt 3):385-390.
-
17Danilchenko S, Kukharenko OG, Moseke C, Protsenko IY, Sukhodub LF, Sulkio-Cleff B. Determination of the Bone Mineral Crystallite Size and Lattice Strain from Diffraction Line Broadening. Crystal Research and Technology 2002;37(11):1234-1240.
-
18Caglioti G, Paoletti A, Ricci FP. On resolution and luminosity of a neutron diffraction spectrometer for single crystal analysis. Nucl Instrum Methods 1960;9(2):195-198.
-
19Pavel K, Woodward PM. Liquid-Mix Disorder in Crystalline Solids: ScMnO3. Journal of Solid State Chemistry 1998;141(1):78-88.
-
20Balzar D, Popovic DS. Advances in X-ray Analysis. Journal of Applied Crystallography 1996;29:16-23.
-
21Yazici R, Kalyon D. Microstrain and defect analysis of CL-20 crystals by novel methods. Journal of Energetic Materials 2005;23(1):43-58.
-
22Matthews JW, Mader S, Light TB. Accomodation of misfit across the interface between crystals of semiconducting elements or compounds. Journal of Applied Physics 1970;41(9):3800-3804.
-
23Nye JF. Physical properties of crystals London: Oxford University Press; 1957.
-
24Sutton AP, Balluffi RW. Interfaces in crystalline materials Oxford: Oxford Science Publications; 1995. v. 51.
-
25Den Toonder JMJ, Van Dommelen JAW, Baaijens FPT. The relation between single crystal elasticity and the effective elastic behavior of polycrystalline materials: theory, measurement and computation. Modelling and Simulation in Materials Science and Engineering 1999;7(6):909-928.
-
26Medina JE, Durán LT, Castro J, Fermín JR, Hernández J, Rincón CAD. Structural and optical properties of AgIn5Se8 Materials Science: An Indian Journal 2015;12(5):178-184.
-
27Sánchez A, Meléndez L, Castro J, Hernández JA, Hernández E, Rincón CAD. Structural, optical, and electrical properties of AgIn5Te8 Journal of Applied Physics 2005;97(5):053505.
-
28Vetterling WT, Teukolsky SA, Press WH, Flannery BP. Numerical Recipes 2nd ed. Cambridge: Cambridge University Press; 1992.
-
29Martínez AM, Soriano R, Faccio R, Trigubó AB. Mechanical Properties Calculation of II-VI Semiconductors: Cd1-yZnyTe (0≤y≤1). Procedia Materials Science 2015;8:656-664.
-
30Berbenni S, Favier V, Berveiller M. Impact of the grain size distribution on the yield stress of heterogeneous materials. International Journal of Plasticity 2007;23(1):114-142.
-
31He Y, Winnubst L, Burggraaf AJ, Verweij H, Van der Varst PG, With B. Grain-Size Dependence of Sliding Wear in Tetragonal Zirconia Polycrystals. Journal of the American Ceramic Society 1996;79(12):3090-96.
Publication Dates
-
Publication in this collection
14 Nov 2019 -
Date of issue
2019
History
-
Received
23 Nov 2018 -
Reviewed
07 Aug 2019 -
Accepted
18 Sept 2019