Longevity of ceramic restoring materials in the confection of endocrowns restorations: an in vitro study on surface roughness and mechanical strength

Longevidade de materiais restauradores cerâmicos na confecção de restaurações endocrowns: um estudo in vitro sobre rugosidade superficial e resistência mecânica

ABSTRACT

Objectives:

The objective was to evaluate the longevity of ceramic restorative materials in the manufacture of endocrown restorations, through an in vitro study on surface roughness and mechanical strength.

Methods:

Three restorative materials were evaluated and assigned to experimental groups (n=10 disc specimens): Leucite Reinforced Ceramic, Lithium Disilicate and Nanoceramic Resin. These restorative materials were evaluated for surface before and after aging (n=02 specimens) under a stereomicroscope. The specimens were submitted to the average surface roughness test (Ra) (n=10) in a contact roughness meter before and after aging. As well as the biaxial flexural strength test (n=10), after aging, up to a test speed of 0.5 mm/min. Aging was carried out in a thermocycler, with 5,000 cycles with baths of 5 °C ± 1 ° and 55 °C ± 1 °. Fragments after fracture were observed under a stereomicroscope. The data obtained were tabulated and analyzed using the Minitab statistical program.

Results:

The surfaces of the specimens do not show changes between the restorative materials and also in relation to aging. For the roughness data, the restorative material factors (p=0.867) and aging (p=0.321) were not statistically significant. The DIS group presented the highest values of fracture resistance (p=0.000), in relation to the LEU and REN groups, which were statistically similar. The same statistical pattern was identified for post-fracture fragment data (p=0.030).

Conclusions:

The aging factors and restorative material do not interfere with the surface roughness performance. However, the mechanical performance and number of fragments after fracture is affected by the restorative material.

Indexing terms
Ceramics; Computer-aided design; Flexural strength

RESUMO

Objetivos:

Objetivou-se avaliar a longevidade de materiais restauradores cerâmicos na confecção de restaurações endocrowns, através de um estudo in vitro sobre rugosidade superficial e resistência mecânica.

Métodos:

Três materiais restauradores foram avaliados e distribuídos em grupos experimentais (n=10 espécimes em disco): Cerâmica Reforçada por Leucita, Dissilicato de Lítio e Resina Nanocerâmica. Estes materiais restauradores foram avaliados quanto a superfície antes e após ao envelhecimento (N=2 espécimes) em estereomicroscópio. Os espécimes foram submetidos ao ensaio de rugosidade superficial média (Ra) (N=10) em rugosímetro de contato antes e após o envelhecimento. Como também, ao teste de resistência à flexão biaxial (N=10), após envelhecimento, em uma velocidade de ensaio de 0,5 mm/min. O envelhecimento foi realizado uma termocicladora, sendo 5.000 ciclos com banhos de 5 °C ± 1° e 55 °C ± 1°. Os fragmentos após fratura foram observados em estereomicroscópio. Os dados obtidos foram tabulados e analisados no programa estatístico Minitab.

Resultados:

As superfícies dos espécimes não mostram alterações entre os materiais restauradores e também em relação ao envelhecimento. Para os dados de rugosidade, os fatores materiais restauradores (p=0,867) e envelhecimento (p=0,321) não foram estatisticamente significativos. O grupo DIS apresentou os maiores valores de resistência à fratura (p=0,000), em relação aos grupos LEU e REN que foram estatisticamente semelhantes. O mesmo padrão estatístico foi identificado para os dados de fragmentos após a fratura (p=0,030).

Conclusão:

Os fatores envelhecimento e material restaurador não interferem quanto a performance da rugosidade superficial. No entanto, o desempenho mecânico e número de fragmentos após a fratura é afetado pelo material restaurador.

Termos de Indexação
Cerâmica; Desenho assistido por computador; Resistência à flexão

INTRODUCTION

Rehabilitating devitalized posterior elements combining aesthetics, resistance, efficiency, speed and durability is one of the challenges in the daily clinic. Endocrown restorations emerge as an alternative to the classic way of using intraradicular retainers and crowns. Endocrowns are monoblock restorations, which do not require retention pins, reduce wear on the remnant and weakening of the root canal, in addition to reducing clinical time [11 Poluha R, Mello Neto C, Sage S. Reabilitação estética em elemento posterior: endocrown. Rev Odontol Araçatuba. 2015;36(1):75-81.]. The study by El Ghoul et al. [22 El Ghoul W, Özcan M, Silwadi M, Salameh Z. Fracture resistance and failure modes of endocrowns manufactured with different CAD/CAM materials under axial and lateral loading. J Esthet Restor Dent. 2019;31(4):378-387. http://dx.doi.org/10.1111/jerd.12486
https://doi.org/10.1111/jerd.12486...
] showed that endocrowns made of lithium, zirconia-reinforced lithium silicate and nanoceramic resin showed higher fracture strength values compared to glass fiber post-supported lithium disilicate crowns.

To make an endocrown, it is necessary to use a resistant material to withstand the masticatory loads incident on the crown. Currently, due to the evolution of restorative materials, it is possible to make a restoration with the ideal characteristics [33 Gracis S, Thompson V, Ferencz J, Silva N, Bonfante E. A new classification system for all-ceramic and ceramic-like restorative materials. Int J Prosthodont. 2015;28(3):227-35. http://dx.doi.org/10.11607/ijp.4244
https://doi.org/10.11607/ijp.4244...
]. Several studies have evaluated restoration materials to be indicated for the fabrication of endocrowns [44 Ramírez-Sebastià A, Bortolotto T, Roig M, Krejci I. Composite vs ceramic computer-aided design/computer-assisted manufacturing crowns in endodontically treated teeth: analysis of marginal adaptation. Oper Dent. 2013;38(6):663-673. http://dx.doi.org/10.2341/12-208-L
https://doi.org/10.2341/12-208-L...

5 Ramírez-Sebastià A, Bortolotto T, Cattani-Lorente M, Giner L, Roig M, Krejci I. Adhesive restoration of anterior endodontically treated teeth: influence of post length on fracture strength. Clin Oral Investig. 2014;18(2):545-554. http://dx.doi.org/10.1007/s00784-013-0978-3
https://doi.org/10.1007/s00784-013-0978-...

6 Ramírez-Sebastià A, Bortolotto T, Roig M, Krejci I. Composite vs ceramic computer-aided design/computer-assisted manufacturing crowns in endodontically treated teeth: analysis of marginal adaptation. Oper Dent. 2013;38(6):663-673. http://dx.doi.org/10.2341/12-208-L
https://doi.org/10.2341/12-208-L...

7 Pedrollo Lise D, Van Ende A, De Munck J, Umeda Suzuki TY, Cardoso Vieira LC, Van Meerbeek B. Biomechanical behavior of endodontically treated premolars using different preparation designs and CAD/CAM materials. J Tooth. 2017;59:54-61. http://dx.doi.org/10.1016/j.jdent.2017.02.007
https://doi.org/10.1016/j.jdent.2017.02....

8 Taha D, Spintzyk S, Sabet A, Wahsh M, Salah T. Assessment of marginal adaptation and fracture resistance of endocrown restorations utilizing different machinable blocks subjected to thermomechanical aging. J Esthet Restor Dent. 2018;30(4):319-328. http://dx.doi.org/10.1111/jerd.12396
https://doi.org/10.1111/jerd.12396...

9 Taha D, Spintzyk S, Schille C, Sabet A, Wahsh M, Salah T, Geis-Gerstorfer J. Fracture resistance and failure modes of polymer infiltrated ceramic endocrown restorations with variations in margin design and occlusal thickness. J Prosthodont Res. 2018;62(3):293-297. http://dx.doi.org/10.1016/j.jpor.2017.11.003
https://doi.org/10.1016/j.jpor.2017.11.0...

10 Rocca GT, Daher R, Saratti CM, Sedlacek R, Suchy T, Feilzer AJ, Krejci I. Restoration of severely damaged lithium endodontically treated: The influence of the endo-core length on marginal integrity and fatigue resistance disilicate CAD-CAM ceramic. J Dent. 2018;68:41-50. http://dx.doi.org/10.1016/j.jdent.2017.10.011
https://doi.org/10.1016/j.jdent.2017.10....

11 de Kuijper M, Gresnigt M, van den Houten M, Haumahu D, Schepke U, Cune MS. Fracture strength of various types of large direct composite and indirect glass ceramic restorations. Oper Dent. 2019;44(4):433-442. http://dx.doi.org/10.2341/18-111-L
https://doi.org/10.2341/18-111-L...

12 Acar DH, Kalyoncuoğlu E. The fracture strength of endocrowns manufactured from different hybrid blocks under axial and lateral forces. Clin Oral Investig. 2021;25(4):1889-1897. http://dx.doi.org/10.1007/s00784-020-03495-y
https://doi.org/10.1007/s00784-020-03495...

13 Dartora NR, Maurício Moris IC, Poole SF, Bacchi A, Sousa-Neto MD, Silva-Sousa YT, et al. Mechanical behavior of endocrowns manufactured with different CAD-CAM ceramic systems. J Prosthet Dent. 2021;125(1):117-125. http://dx.doi.org/10.1016/j.prosdent.2019.11.008
https://doi.org/10.1016/j.prosdent.2019....

14 Ghoul WE, Özcan M, Tribst JPM, Salameh Z. Fracture resistance, failure mode and stress concentration in a modified endocrown design. Biomater Investig Dent. 2020;7(1):110-119. http://dx.doi.org/10.1080/26415275.2020.1801348
https://doi.org/10.1080/26415275.2020.18...
-1515 Ahmed MAA, Kern M, Mourshed B, Wille S, Chaar MS. Fracture resistance of maxillary premolars restored with different endocrown designs and materials after artificial aging. J Prosthodont Res. 2022;66(1):141-150. http://dx.doi.org/10.2186/jpr.JPR_D_20_00082
https://doi.org/10.2186/jpr.JPR_D_20_000...
].

Laboratory and clinical studies are extremely important for the evolution of the technique and materials used in these restorations [1616 Bettencourt MVM, Ismerim AB, Lima EMCX, Carvalho AO. Restaurações endocrown: uma revisão de literatura. J Dent Pub H.2021;12(2):105-14. http://dx.doi.org/10.17267/2596-3368dentistry.v12i2.3678
https://doi.org/10.17267/2596-3368dentis...
]. The mechanical behavior of ceramic materials varies with the structure and mechanical properties. The fracture strength and failure mode of endocrowns can be influenced by several factors, such as material type, occlusal load, aging, cervical termination, restoration design, restoration processing, and the cementation method [1717 Heintze SD, Cavalleri A, Zellweger G, Büchler A, Zappini G. Fracture frequency of all-ceramic crowns during dynamic loading in a chewing simulator using different loading and luting protocols. Tooth Mater. 2008;24(10):1352-1361. http://dx.doi.org/10.1016/j.dental.2008.02.019
https://doi.org/10.1016/j.dental.2008.02...
,1818 Porto TS, Park SJ, Faddoul AJ, Faddoul FF, Cesar PF. Evaluation of the surface roughness and accelerated aging of CAD/CAM materials. Int J Prosthodont. 2020;33(4):418-428. http://dx.doi.org/10.11607/ijp.6556
https://doi.org/10.11607/ijp.6556...
]. Thus, further investigation is needed. are needed to explore the biomechanical behavior of recent materials when used to make endocrowns prior to clinical trials [88 Taha D, Spintzyk S, Sabet A, Wahsh M, Salah T. Assessment of marginal adaptation and fracture resistance of endocrown restorations utilizing different machinable blocks subjected to thermomechanical aging. J Esthet Restor Dent. 2018;30(4):319-328. http://dx.doi.org/10.1111/jerd.12396
https://doi.org/10.1111/jerd.12396...
].

Based on the above, the objective was to evaluate the longevity of ceramic restorative materials in the manufacture of endocrown restorations, through an in vitro study on surface roughness and mechanical strength. The expected results for this research, based on the proposed objective, are: Null Hypothesis (H0) - There will be no statistically significant difference for surface roughness and mechanical strength between the materials tested; Alternative Hypothesis 1 (H1) - There will be a statistically significant difference for surface roughness and mechanical strength between the materials tested; Alternative Hypothesis 2 (H2) - There will be a statistically significant difference only for surface roughness and not for mechanical strength between the materials teste.

METHODS

Specimens manufacturim

Circular discs with approximately 12 mm in diameter and 1.2 mm in thickness were obtained from blocks for CAD-CAM of three indirect restorative materials, namely: Leucite-reinforced ceramic (IPS Empress CAD, Ivoclar Vivadent, Switzerland), Disilicate Lithium (IPS Emax CAD, Ivoclar Vivadent, Switzerland) and Nanoceramic Resin (Lava Ultimate, 3M ESPE, Germany) (table 1).

Table 1
Characteristics of the restorative materials used in the study.* * Data obtained in the literature [19,20].

First, slices were cut from the blocks for CAD-CAM in a cutting machine (Struers Accutom 100, Ballerup, Denmark) with a diamond disc at a speed of 250 rpm and water cooling. Then, with a truncated conical diamond tip in a high rotation pen and constant cooling, the slices were rounded to obtain a circular shape. Finally, the specimens were polished with SiC sandpaper of 300, 600 and 1200 grit. According to ISO/CD 6872, the specimens have final dimensions of 12 mm in diameter and 1.2 mm in thickness. The IPS Emax CAD specimens were cut prior to crystallization, which after polishing was performed according to the manufacturer’s recommendations regarding oven use and temperature cycles.

Experimental groups

The experimental groups are defined by LEU (Leucite-reinforced ceramic), DIS (Lithium disilicate) and REN (Nanoceramic Resin). The sample value of this study was calculated using the Minitab statistical program (version 17 for windows, Pennsylvania USA), based on the standard deviation (0.668) of the Skalskyi et al. [2121 Skalskyi V, Makeev V, Stankevych O, Pavlychko R. Features of fracture of prosthetic tooth-endocrown constructions by means of acoustic emission analysis. Tooth Mater. 2018;34(3):e46-e55. http://dx.doi.org/10.1016/j.dental.2018.01.023
https://doi.org/10.1016/j.dental.2018.01...
] study, which also evaluated the performance of ceramic materials with specimens in disk. Thus, N=10 presented a sampling power of 80.0% in relation to the maximum differences and this value of N will be adopted for both analyses, surface roughness and mechanical strength.

Surface roughness

The specimens were evaluated for mean surface roughness (Ra - µm) using a Taylor Hobson contact roughness meter, which is connected to a computerized unit with a computer program, Tayle Profile Gold. In each specimen, three roughness values were obtained, the readings were performed parallel to each other and in a horizontal direction. Finally, the average of the Ra values was calculated, representing the average roughness value of the specimen.

Aging

Thermal aging was performed through thermal cycling in a thermocycler (Nova Ethics, São Paulo, Brazil). 5,000 cycles were performed with baths of 5 °C ± 1° and 55 °C ± 1°, as adopted in endocrown studies [66 Ramírez-Sebastià A, Bortolotto T, Roig M, Krejci I. Composite vs ceramic computer-aided design/computer-assisted manufacturing crowns in endodontically treated teeth: analysis of marginal adaptation. Oper Dent. 2013;38(6):663-673. http://dx.doi.org/10.2341/12-208-L
https://doi.org/10.2341/12-208-L...
,88 Taha D, Spintzyk S, Sabet A, Wahsh M, Salah T. Assessment of marginal adaptation and fracture resistance of endocrown restorations utilizing different machinable blocks subjected to thermomechanical aging. J Esthet Restor Dent. 2018;30(4):319-328. http://dx.doi.org/10.1111/jerd.12396
https://doi.org/10.1111/jerd.12396...
,1212 Acar DH, Kalyoncuoğlu E. The fracture strength of endocrowns manufactured from different hybrid blocks under axial and lateral forces. Clin Oral Investig. 2021;25(4):1889-1897. http://dx.doi.org/10.1007/s00784-020-03495-y
https://doi.org/10.1007/s00784-020-03495...
,1515 Ahmed MAA, Kern M, Mourshed B, Wille S, Chaar MS. Fracture resistance of maxillary premolars restored with different endocrown designs and materials after artificial aging. J Prosthodont Res. 2022;66(1):141-150. http://dx.doi.org/10.2186/jpr.JPR_D_20_00082
https://doi.org/10.2186/jpr.JPR_D_20_000...
] The immersion time in each bath was 30 seconds and the transfer time between the two baths took place at 2-second interval.

Biaxial bending resistance

The biaxial flexural strength test was performed on a testing machine (Emic DL-1000, Emic, São José dos Pinhais, PR, Brazil) with a blunt tip of 1.6 mm in diameter. Initially, the specimens were positioned on a metallic circular base with three spheres of 3.2 mm in diameter, forming a plane and equally distant from each other, according to ISO 6872, and received the load applied by the testing machine. During the receipt of the load, the specimen was covered with an adhesive tape to prevent contact with the blunt tip in order to keep the fragments in position [2222 Ramos NDC. Caracterização microestrutural e crescimento subcrítico de trincas em cerâmicas odontológicas [dissertação]. São José dos Campos: Universidade Estadual Paulista (UNESP); 2014.].

The test was conducted with a speed of 0.5 mm/min and a load cell of 100 kgf. The calculation of biaxial flexural strength (σ) (MPa) of the discs was obtained according to the description of ISO 6872 (Formula 1): where P is the load in kgf, X and Y are parameters related to the elastic properties of the material (Poisson Ratio in Elastic Modulus) and b is the thickness of the specimen at the origin of the fracture in mm. [2222 Ramos NDC. Caracterização microestrutural e crescimento subcrítico de trincas em cerâmicas odontológicas [dissertação]. São José dos Campos: Universidade Estadual Paulista (UNESP); 2014.] The reference values X and Y were obtained from the study by Wendler et al. [2020 Wendler M, Belli R, Petschelt A, Mevec D, Harrer W, Lube T, et al. Chairside CAD/CAM materials. Part 2: Flexural strength testing. Dent Mater. 2017;33(1):99-109. http://dx.doi.org/10.1016/j.dental.2016.10.008
https://doi.org/10.1016/j.dental.2016.10...
].

σ = ( 0 , 2387 P ( X Y ) b 2 (Formula 1: Calculation of biaxial flexural strength)

Fracture analysis

Disc fracture characteristics were analyzed with the aid of a stereomicroscope (Discovery V20, CarlZeiss, Germany). After that, specimens were selected to represent each of the experimental groups.

Analysis of results

The results were tabulated and analyzed in Minitab (version 17 for windows, Pennsylvania, USA), with a significance level of 5%. The surface roughness data were submitted to the Anova 2 Factor statistical test (p< 0.05), to evaluate the effect of the material and aging. Meanwhile, the Anova 1 Factor statistical test (p<0.05) was adopted to evaluate the effect of the material in relation to mechanical strength and number of fragments after fracture. Fisher’s test was adopted to identify differences between groups for the analysis of fracture resistance and number of fragments after fracture.

RESULTS

The research results are presented according to the analyzes performed.

Surface roughness

The observation of the surfaces of the specimens in a stereomicroscope did not show surface changes between the restorative materials, also before and after aging. For the roughness data, the restorative material factors (p=0.867) and aging (p=0.321) were not statistically significant, in addition to showing no interaction between the variables (p=0.774). Descriptive data regarding the experimental groups are seen in table 2.

Table 2
Ra (µm) data before and after aging.

Mechanical strength and fracture analysis

The mechanical performance of restorative materials after aging showed a statistically significant difference (p=0.000) and differences between experimental groups (table 3). The same statistical pattern was identified for the data on fragments after fracture (P=0.030) (table 4). Representative stereomicroscope images of the fractures for the experimental groups are seen in figures 1, 2, 3.

Table 3
Mechanical Strength (Mpa) data after aging.* * Different letters mean difference between groups.
Table 4
Data on the number of fragments after fracture.* * Different letters mean difference between groups.
Figure 1
DIS Group - Specimen 1, 07 fragments after fracture. 0.65x magnification.
Figure 2
LEU Group- Specimen 2, 06 fragments after fracture. 0.65x magnification.
Figure 3
Group REN- Specimen 1, 03 fragments after fracture. 0.65x magnification.

DISCUSSION

Based on the results of this research, alternative hypothesis 3 (H3) was accepted and the other tested hypotheses were rejected. That is, there was a statistically significant difference only for mechanical strength and not for surface roughness between the materials tested. The findings of this research corroborate the study by El Ghoul et al. [22 El Ghoul W, Özcan M, Silwadi M, Salameh Z. Fracture resistance and failure modes of endocrowns manufactured with different CAD/CAM materials under axial and lateral loading. J Esthet Restor Dent. 2019;31(4):378-387. http://dx.doi.org/10.1111/jerd.12486
https://doi.org/10.1111/jerd.12486...
] and Acar and Kalyoncuoğlu [1212 Acar DH, Kalyoncuoğlu E. The fracture strength of endocrowns manufactured from different hybrid blocks under axial and lateral forces. Clin Oral Investig. 2021;25(4):1889-1897. http://dx.doi.org/10.1007/s00784-020-03495-y
https://doi.org/10.1007/s00784-020-03495...
] for fracture resistance under endocrown restorations and are in agreement with other published studies [1313 Dartora NR, Maurício Moris IC, Poole SF, Bacchi A, Sousa-Neto MD, Silva-Sousa YT, et al. Mechanical behavior of endocrowns manufactured with different CAD-CAM ceramic systems. J Prosthet Dent. 2021;125(1):117-125. http://dx.doi.org/10.1016/j.prosdent.2019.11.008
https://doi.org/10.1016/j.prosdent.2019....
,1515 Ahmed MAA, Kern M, Mourshed B, Wille S, Chaar MS. Fracture resistance of maxillary premolars restored with different endocrown designs and materials after artificial aging. J Prosthodont Res. 2022;66(1):141-150. http://dx.doi.org/10.2186/jpr.JPR_D_20_00082
https://doi.org/10.2186/jpr.JPR_D_20_000...
].

Lithium disilicate showed superior mechanical performance compared to Leucite Reinforced Ceramics and Nanoceramic Resin after thermal aging. As observed in the study by El Ghoul et al. [22 El Ghoul W, Özcan M, Silwadi M, Salameh Z. Fracture resistance and failure modes of endocrowns manufactured with different CAD/CAM materials under axial and lateral loading. J Esthet Restor Dent. 2019;31(4):378-387. http://dx.doi.org/10.1111/jerd.12486
https://doi.org/10.1111/jerd.12486...
], for axial load Lithium Disilicate proved to be more resistant to fracture than Lithium Silicate reinforced by Zirconia and similar to Nanoceramic Resin after thermomechanical aging. Acar and Kalyoncuoğlu [1212 Acar DH, Kalyoncuoğlu E. The fracture strength of endocrowns manufactured from different hybrid blocks under axial and lateral forces. Clin Oral Investig. 2021;25(4):1889-1897. http://dx.doi.org/10.1007/s00784-020-03495-y
https://doi.org/10.1007/s00784-020-03495...
] also observed that Lithium Disilicate was the material that supports greater lateral load until fracture, in relation to hybrid materials such as Nanoceramic Resin. Lithium disilicate has been a suitable material for making endocrown [1111 de Kuijper M, Gresnigt M, van den Houten M, Haumahu D, Schepke U, Cune MS. Fracture strength of various types of large direct composite and indirect glass ceramic restorations. Oper Dent. 2019;44(4):433-442. http://dx.doi.org/10.2341/18-111-L
https://doi.org/10.2341/18-111-L...
], due to its excellent mechanical properties, such as high flexural strength [1818 Porto TS, Park SJ, Faddoul AJ, Faddoul FF, Cesar PF. Evaluation of the surface roughness and accelerated aging of CAD/CAM materials. Int J Prosthodont. 2020;33(4):418-428. http://dx.doi.org/10.11607/ijp.6556
https://doi.org/10.11607/ijp.6556...
,1919 Sonmez N, Gultekin P, Turp V, Akgungor G, Sem D, Mijiritsky E. Evaluation of five CAD/CAM materials by microstructural characterization and mechanical tests: an in vitro comparative study. BMC Oral Health. 2018;18(1):1-13. http://dx.doi.org/10.1186/s12903-017-0458-2
https://doi.org/10.1186/s12903-017-0458-...
] and hardness after thermal aging [2323 Hampe R, Lümkemann N, Sener B, Stawarczyk B. The effect of artificial aging on Martens hardness and indentation modulus of different dental CAD/CAM restorative materials. J Mech Behav Biomed Mater. 2018;86:191-198. http://dx.doi.org/10.1016/j.jmbbm.2018.06.028
https://doi.org/10.1016/j.jmbbm.2018.06....
].

Articles that disagree with the findings of this research, choose zirconia as the most fracture resistant material. However, this ceramic material had a higher rate of non-restorable failures compared to endocrown restorations [1313 Dartora NR, Maurício Moris IC, Poole SF, Bacchi A, Sousa-Neto MD, Silva-Sousa YT, et al. Mechanical behavior of endocrowns manufactured with different CAD-CAM ceramic systems. J Prosthet Dent. 2021;125(1):117-125. http://dx.doi.org/10.1016/j.prosdent.2019.11.008
https://doi.org/10.1016/j.prosdent.2019....
,1515 Ahmed MAA, Kern M, Mourshed B, Wille S, Chaar MS. Fracture resistance of maxillary premolars restored with different endocrown designs and materials after artificial aging. J Prosthodont Res. 2022;66(1):141-150. http://dx.doi.org/10.2186/jpr.JPR_D_20_00082
https://doi.org/10.2186/jpr.JPR_D_20_000...
]. Zirconia is a ceramic of the polycrystalline group, which among all-ceramic materials has greater mechanical strength [33 Gracis S, Thompson V, Ferencz J, Silva N, Bonfante E. A new classification system for all-ceramic and ceramic-like restorative materials. Int J Prosthodont. 2015;28(3):227-35. http://dx.doi.org/10.11607/ijp.4244
https://doi.org/10.11607/ijp.4244...
]. This characteristic makes this restorative material be limited to endocrown restorations, as it does not favor restorative biomedical principles and promotes catastrophic fractures to the dental structure [2424 Awada A, Nathanson D. Mechanical properties of resin-ceramic CAD/CAM restorative materials. The Journal of Prosthetic Dentistr. 2015;114(4):587-593. http://dx.doi.org/10.1016/j.prosdent.2015.04.016
https://doi.org/10.1016/j.prosdent.2015....
].

Ceramics Reinforced by Leucite and Resin Nanoceramics statistically presented equivalent mechanical performance after thermal aging, which was also observed in the study by Sonmez et al. [2424 Awada A, Nathanson D. Mechanical properties of resin-ceramic CAD/CAM restorative materials. The Journal of Prosthetic Dentistr. 2015;114(4):587-593. http://dx.doi.org/10.1016/j.prosdent.2015.04.016
https://doi.org/10.1016/j.prosdent.2015....
] However, the study by Porto et al. [1818 Porto TS, Park SJ, Faddoul AJ, Faddoul FF, Cesar PF. Evaluation of the surface roughness and accelerated aging of CAD/CAM materials. Int J Prosthodont. 2020;33(4):418-428. http://dx.doi.org/10.11607/ijp.6556
https://doi.org/10.11607/ijp.6556...
] showed that there was mechanical superiority of Ceramics Reinforced by Leucite and aging negatively affected only the Nanoceramic Resin. The same is repeated with Lava Ultimate in a study with endocrown restorations, that is, lower values of fracture resistance after thermomechanical aging, when this material was compared to Hybrid Ceramic, Hybrid Composite and Lithium Disilicate. research in question, are due to the methodology adopted regarding the specimen, aging and fracture resistance. Making discs for the biaxial bending test is complex, CAM are rectangular. Factor that makes it difficult to standardize specimens [2424 Awada A, Nathanson D. Mechanical properties of resin-ceramic CAD/CAM restorative materials. The Journal of Prosthetic Dentistr. 2015;114(4):587-593. http://dx.doi.org/10.1016/j.prosdent.2015.04.016
https://doi.org/10.1016/j.prosdent.2015....
]. Lava Ultimate has been affected by aging, according to the literature, because the organic matrix undergoes thermal degradation [1919 Sonmez N, Gultekin P, Turp V, Akgungor G, Sem D, Mijiritsky E. Evaluation of five CAD/CAM materials by microstructural characterization and mechanical tests: an in vitro comparative study. BMC Oral Health. 2018;18(1):1-13. http://dx.doi.org/10.1186/s12903-017-0458-2
https://doi.org/10.1186/s12903-017-0458-...
. And different mechanical tests can influence the values of mechanical strength. Therefore, the results that corroborate the article by Sonmez et al. 1919 Sonmez N, Gultekin P, Turp V, Akgungor G, Sem D, Mijiritsky E. Evaluation of five CAD/CAM materials by microstructural characterization and mechanical tests: an in vitro comparative study. BMC Oral Health. 2018;18(1):1-13. http://dx.doi.org/10.1186/s12903-017-0458-2
https://doi.org/10.1186/s12903-017-0458-...
] should be close to the number of thermal cycles with the research in question, while Porto et al. [1818 Porto TS, Park SJ, Faddoul AJ, Faddoul FF, Cesar PF. Evaluation of the surface roughness and accelerated aging of CAD/CAM materials. Int J Prosthodont. 2020;33(4):418-428. http://dx.doi.org/10.11607/ijp.6556
https://doi.org/10.11607/ijp.6556...
] have specimens in bar and three-point bending test, finally Acar and Kalyoncuoğlu [1212 Acar DH, Kalyoncuoğlu E. The fracture strength of endocrowns manufactured from different hybrid blocks under axial and lateral forces. Clin Oral Investig. 2021;25(4):1889-1897. http://dx.doi.org/10.1007/s00784-020-03495-y
https://doi.org/10.1007/s00784-020-03495...
] edocrows restorations and compression test.

As for the surface roughness findings, the restorative materials and thermal aging were not statistically significant. As well, no research was identified that investigated the surface wear of endocronws restorations, which limits the discussion of the results. In a study for polished specimens without aging, it showed that the roughness visibly increased as the surface treatment was more aggressive and this surface change does not influence the flexural strength of Lava Ultimate, VITA ENAMIC, Shofu Block HC and IPS Empress CAD, which in a way it corroborates the research in question [1818 Porto TS, Park SJ, Faddoul AJ, Faddoul FF, Cesar PF. Evaluation of the surface roughness and accelerated aging of CAD/CAM materials. Int J Prosthodont. 2020;33(4):418-428. http://dx.doi.org/10.11607/ijp.6556
https://doi.org/10.11607/ijp.6556...
]. For Ludovichetti et al. [2525 Ludovichetti FS, Trindade FZ, Werner A, Kleverlaan CJ, Fonseca RG. Wear resistance and abrasiveness of CAD-CAM monolithic materials. J Prosthet Dent. 2018 Aug;120(2):318.e1-318.e8. http://dx.doi.org/10.1016/j.prosdent.2018.05.011
https://doi.org/10.1016/j.prosdent.2018....
] who studied the wear resistance and abrasiveness of monolithic materials for CAD-CAM in the absence of aging, Vita Enamic and Lava Ultimate showed the highest surface roughness values, while IPS e.max CAD and Vita Suprinity showed the lowest mean values, these results were statistically significant and are in line with the research presented. In the study by Awada et al. [2424 Awada A, Nathanson D. Mechanical properties of resin-ceramic CAD/CAM restorative materials. The Journal of Prosthetic Dentistr. 2015;114(4):587-593. http://dx.doi.org/10.1016/j.prosdent.2015.04.016
https://doi.org/10.1016/j.prosdent.2015....
], there was a statistically significant difference in the edge of restorations between Nanoceramic Resin and Leucite-Reinforced Ceramic in the absence of aging, with the second material having higher surface roughness. The lack of statistical difference between the results of Ra of the research in question, can be explained by the specimens being evaluated only polished. As for the Nanoceramic Resin not having been superficially affected after thermal aging, Lava Ultimate belongs to the Ceramics with resin matrix group, which is characterized by an organic matrix with inorganic particles on the surface such as SiO2 and ZrO2, which may make the surface of this material more resistant to thermal action [33 Gracis S, Thompson V, Ferencz J, Silva N, Bonfante E. A new classification system for all-ceramic and ceramic-like restorative materials. Int J Prosthodont. 2015;28(3):227-35. http://dx.doi.org/10.11607/ijp.4244
https://doi.org/10.11607/ijp.4244...
].

Regarding the number of fragments after fracture, the Leucite-Reinforced Ceramic was statistically similar to Lithium Disilicate and Nanoceramic Resin. IPS Emax CAD being the material that obtained the highest number of fragments after fracture. Lithium disilicate endocrown restorations had a higher frequency of irreparable failures [22 El Ghoul W, Özcan M, Silwadi M, Salameh Z. Fracture resistance and failure modes of endocrowns manufactured with different CAD/CAM materials under axial and lateral loading. J Esthet Restor Dent. 2019;31(4):378-387. http://dx.doi.org/10.1111/jerd.12486
https://doi.org/10.1111/jerd.12486...
,1212 Acar DH, Kalyoncuoğlu E. The fracture strength of endocrowns manufactured from different hybrid blocks under axial and lateral forces. Clin Oral Investig. 2021;25(4):1889-1897. http://dx.doi.org/10.1007/s00784-020-03495-y
https://doi.org/10.1007/s00784-020-03495...
,1313 Dartora NR, Maurício Moris IC, Poole SF, Bacchi A, Sousa-Neto MD, Silva-Sousa YT, et al. Mechanical behavior of endocrowns manufactured with different CAD-CAM ceramic systems. J Prosthet Dent. 2021;125(1):117-125. http://dx.doi.org/10.1016/j.prosdent.2019.11.008
https://doi.org/10.1016/j.prosdent.2019....
,1515 Ahmed MAA, Kern M, Mourshed B, Wille S, Chaar MS. Fracture resistance of maxillary premolars restored with different endocrown designs and materials after artificial aging. J Prosthodont Res. 2022;66(1):141-150. http://dx.doi.org/10.2186/jpr.JPR_D_20_00082
https://doi.org/10.2186/jpr.JPR_D_20_000...
]. Leucite-reinforced Nanoceramic and Ceramic Resins showed a more repairable fracture scenario [33 Gracis S, Thompson V, Ferencz J, Silva N, Bonfante E. A new classification system for all-ceramic and ceramic-like restorative materials. Int J Prosthodont. 2015;28(3):227-35. http://dx.doi.org/10.11607/ijp.4244
https://doi.org/10.11607/ijp.4244...
,1212 Acar DH, Kalyoncuoğlu E. The fracture strength of endocrowns manufactured from different hybrid blocks under axial and lateral forces. Clin Oral Investig. 2021;25(4):1889-1897. http://dx.doi.org/10.1007/s00784-020-03495-y
https://doi.org/10.1007/s00784-020-03495...
,1313 Dartora NR, Maurício Moris IC, Poole SF, Bacchi A, Sousa-Neto MD, Silva-Sousa YT, et al. Mechanical behavior of endocrowns manufactured with different CAD-CAM ceramic systems. J Prosthet Dent. 2021;125(1):117-125. http://dx.doi.org/10.1016/j.prosdent.2019.11.008
https://doi.org/10.1016/j.prosdent.2019....
]. The unfavorable results of Lithium Disilicate are due to the high modulus of elasticity, thus promoting greater fracture load and tensions in the dental structure [22 El Ghoul W, Özcan M, Silwadi M, Salameh Z. Fracture resistance and failure modes of endocrowns manufactured with different CAD/CAM materials under axial and lateral loading. J Esthet Restor Dent. 2019;31(4):378-387. http://dx.doi.org/10.1111/jerd.12486
https://doi.org/10.1111/jerd.12486...
]. While the Nanoceramic Resin has a modulus of elasticity that approximates the dental structure, favoring the indication of indirect restorations according to biomimetic perspectives [2424 Awada A, Nathanson D. Mechanical properties of resin-ceramic CAD/CAM restorative materials. The Journal of Prosthetic Dentistr. 2015;114(4):587-593. http://dx.doi.org/10.1016/j.prosdent.2015.04.016
https://doi.org/10.1016/j.prosdent.2015....
]. The greater number of fragments after Lithium Disilicate fracture is due to the material presenting greater mechanical strength, thus absorbing a greater amount of energy until fracture [2020 Wendler M, Belli R, Petschelt A, Mevec D, Harrer W, Lube T, et al. Chairside CAD/CAM materials. Part 2: Flexural strength testing. Dent Mater. 2017;33(1):99-109. http://dx.doi.org/10.1016/j.dental.2016.10.008
https://doi.org/10.1016/j.dental.2016.10...
,2222 Ramos NDC. Caracterização microestrutural e crescimento subcrítico de trincas em cerâmicas odontológicas [dissertação]. São José dos Campos: Universidade Estadual Paulista (UNESP); 2014.]. The nanoceramic resin, due to its lower mechanical performance, supports lower stresses until fracture. Finally, Leucite Reinforced Ceramics proved to be an intermediate material, perhaps due to its chemical composition not having oxides that would guarantee greater mechanical strength.

If it were possible to extrapolate the data from this research to the daily clinic, which is not because it is an in vitro study. Leucite Reinforced Ceramics would be a restorative material, for use in CAD-CAM, with a favorable indication for the fabrication of an endocrown restoration. Because this material, showed resistance to fracture and fracture fragments in intermediate values to Lithium Disilicate and Nanoceramic Resin. In addition to the excellent aesthetic performance and scientific knowledge that this ceramic has in the dental environment, it is a more predictable material for single-unit restorations.

The limitation of this research is due to the non-use of specimens that represent the endocrown restoration, making the comparison between the results more difficult. The complexity in the standardization of disk specimens, especially Lithium Disilicate for being more resistant. Not having performed mechanical aging, which would be important to bring the findings closer to the clinical condition. Having an experimental group with zirconia, since this restorative material is evaluated in most studies on endocrown restorations. New studies should look at the surface roughness after thermomechanical aging of restorative materials for CAD-CAM, research on the wear of endocrown restoration and its antagonist is necessary in the long term so that it is possible to understand mechanical behavior. Finally, randomized clinical studies that evaluate the performance of restorative materials in patients over the years with several variables under observation.

CONCLUSION

Based on the limitations of this study, the following conclusions were presented:

  1. The aging factors and restorative material do not interfere with the surface roughness performance;

  2. Mechanical performance and number of fragments after fracture are affected by the restorative material.

Acknowledgment

INTM Recife-PE for providing the equipment for research development.

How to cite this article

  • Silva CML, Souza TFS, Raimundo ACM, Torres Neto A, Grangeiro MTV, Figueiredo VMG. Longevity of ceramic restoring materials in the confection of endocrowns restorations: an in vitro study on surface roughness and mechanical strength. RGO, Rev Gaúch Odontol. 2023;71:e20230050. http://dx.doi.org/10.1590/1981-86372023005020230003

REFERENCES

  • 1
    Poluha R, Mello Neto C, Sage S. Reabilitação estética em elemento posterior: endocrown. Rev Odontol Araçatuba. 2015;36(1):75-81.
  • 2
    El Ghoul W, Özcan M, Silwadi M, Salameh Z. Fracture resistance and failure modes of endocrowns manufactured with different CAD/CAM materials under axial and lateral loading. J Esthet Restor Dent. 2019;31(4):378-387. http://dx.doi.org/10.1111/jerd.12486
    » https://doi.org/10.1111/jerd.12486
  • 3
    Gracis S, Thompson V, Ferencz J, Silva N, Bonfante E. A new classification system for all-ceramic and ceramic-like restorative materials. Int J Prosthodont. 2015;28(3):227-35. http://dx.doi.org/10.11607/ijp.4244
    » https://doi.org/10.11607/ijp.4244
  • 4
    Ramírez-Sebastià A, Bortolotto T, Roig M, Krejci I. Composite vs ceramic computer-aided design/computer-assisted manufacturing crowns in endodontically treated teeth: analysis of marginal adaptation. Oper Dent. 2013;38(6):663-673. http://dx.doi.org/10.2341/12-208-L
    » https://doi.org/10.2341/12-208-L
  • 5
    Ramírez-Sebastià A, Bortolotto T, Cattani-Lorente M, Giner L, Roig M, Krejci I. Adhesive restoration of anterior endodontically treated teeth: influence of post length on fracture strength. Clin Oral Investig. 2014;18(2):545-554. http://dx.doi.org/10.1007/s00784-013-0978-3
    » https://doi.org/10.1007/s00784-013-0978-3
  • 6
    Ramírez-Sebastià A, Bortolotto T, Roig M, Krejci I. Composite vs ceramic computer-aided design/computer-assisted manufacturing crowns in endodontically treated teeth: analysis of marginal adaptation. Oper Dent. 2013;38(6):663-673. http://dx.doi.org/10.2341/12-208-L
    » https://doi.org/10.2341/12-208-L
  • 7
    Pedrollo Lise D, Van Ende A, De Munck J, Umeda Suzuki TY, Cardoso Vieira LC, Van Meerbeek B. Biomechanical behavior of endodontically treated premolars using different preparation designs and CAD/CAM materials. J Tooth. 2017;59:54-61. http://dx.doi.org/10.1016/j.jdent.2017.02.007
    » https://doi.org/10.1016/j.jdent.2017.02.007
  • 8
    Taha D, Spintzyk S, Sabet A, Wahsh M, Salah T. Assessment of marginal adaptation and fracture resistance of endocrown restorations utilizing different machinable blocks subjected to thermomechanical aging. J Esthet Restor Dent. 2018;30(4):319-328. http://dx.doi.org/10.1111/jerd.12396
    » https://doi.org/10.1111/jerd.12396
  • 9
    Taha D, Spintzyk S, Schille C, Sabet A, Wahsh M, Salah T, Geis-Gerstorfer J. Fracture resistance and failure modes of polymer infiltrated ceramic endocrown restorations with variations in margin design and occlusal thickness. J Prosthodont Res. 2018;62(3):293-297. http://dx.doi.org/10.1016/j.jpor.2017.11.003
    » https://doi.org/10.1016/j.jpor.2017.11.003
  • 10
    Rocca GT, Daher R, Saratti CM, Sedlacek R, Suchy T, Feilzer AJ, Krejci I. Restoration of severely damaged lithium endodontically treated: The influence of the endo-core length on marginal integrity and fatigue resistance disilicate CAD-CAM ceramic. J Dent. 2018;68:41-50. http://dx.doi.org/10.1016/j.jdent.2017.10.011
    » https://doi.org/10.1016/j.jdent.2017.10.011
  • 11
    de Kuijper M, Gresnigt M, van den Houten M, Haumahu D, Schepke U, Cune MS. Fracture strength of various types of large direct composite and indirect glass ceramic restorations. Oper Dent. 2019;44(4):433-442. http://dx.doi.org/10.2341/18-111-L
    » https://doi.org/10.2341/18-111-L
  • 12
    Acar DH, Kalyoncuoğlu E. The fracture strength of endocrowns manufactured from different hybrid blocks under axial and lateral forces. Clin Oral Investig. 2021;25(4):1889-1897. http://dx.doi.org/10.1007/s00784-020-03495-y
    » https://doi.org/10.1007/s00784-020-03495-y
  • 13
    Dartora NR, Maurício Moris IC, Poole SF, Bacchi A, Sousa-Neto MD, Silva-Sousa YT, et al. Mechanical behavior of endocrowns manufactured with different CAD-CAM ceramic systems. J Prosthet Dent. 2021;125(1):117-125. http://dx.doi.org/10.1016/j.prosdent.2019.11.008
    » https://doi.org/10.1016/j.prosdent.2019.11.008
  • 14
    Ghoul WE, Özcan M, Tribst JPM, Salameh Z. Fracture resistance, failure mode and stress concentration in a modified endocrown design. Biomater Investig Dent. 2020;7(1):110-119. http://dx.doi.org/10.1080/26415275.2020.1801348
    » https://doi.org/10.1080/26415275.2020.1801348
  • 15
    Ahmed MAA, Kern M, Mourshed B, Wille S, Chaar MS. Fracture resistance of maxillary premolars restored with different endocrown designs and materials after artificial aging. J Prosthodont Res. 2022;66(1):141-150. http://dx.doi.org/10.2186/jpr.JPR_D_20_00082
    » https://doi.org/10.2186/jpr.JPR_D_20_00082
  • 16
    Bettencourt MVM, Ismerim AB, Lima EMCX, Carvalho AO. Restaurações endocrown: uma revisão de literatura. J Dent Pub H.2021;12(2):105-14. http://dx.doi.org/10.17267/2596-3368dentistry.v12i2.3678
    » https://doi.org/10.17267/2596-3368dentistry.v12i2.3678
  • 17
    Heintze SD, Cavalleri A, Zellweger G, Büchler A, Zappini G. Fracture frequency of all-ceramic crowns during dynamic loading in a chewing simulator using different loading and luting protocols. Tooth Mater. 2008;24(10):1352-1361. http://dx.doi.org/10.1016/j.dental.2008.02.019
    » https://doi.org/10.1016/j.dental.2008.02.019
  • 18
    Porto TS, Park SJ, Faddoul AJ, Faddoul FF, Cesar PF. Evaluation of the surface roughness and accelerated aging of CAD/CAM materials. Int J Prosthodont. 2020;33(4):418-428. http://dx.doi.org/10.11607/ijp.6556
    » https://doi.org/10.11607/ijp.6556
  • 19
    Sonmez N, Gultekin P, Turp V, Akgungor G, Sem D, Mijiritsky E. Evaluation of five CAD/CAM materials by microstructural characterization and mechanical tests: an in vitro comparative study. BMC Oral Health. 2018;18(1):1-13. http://dx.doi.org/10.1186/s12903-017-0458-2
    » https://doi.org/10.1186/s12903-017-0458-2
  • 20
    Wendler M, Belli R, Petschelt A, Mevec D, Harrer W, Lube T, et al. Chairside CAD/CAM materials. Part 2: Flexural strength testing. Dent Mater. 2017;33(1):99-109. http://dx.doi.org/10.1016/j.dental.2016.10.008
    » https://doi.org/10.1016/j.dental.2016.10.008
  • 21
    Skalskyi V, Makeev V, Stankevych O, Pavlychko R. Features of fracture of prosthetic tooth-endocrown constructions by means of acoustic emission analysis. Tooth Mater. 2018;34(3):e46-e55. http://dx.doi.org/10.1016/j.dental.2018.01.023
    » https://doi.org/10.1016/j.dental.2018.01.023
  • 22
    Ramos NDC. Caracterização microestrutural e crescimento subcrítico de trincas em cerâmicas odontológicas [dissertação]. São José dos Campos: Universidade Estadual Paulista (UNESP); 2014.
  • 23
    Hampe R, Lümkemann N, Sener B, Stawarczyk B. The effect of artificial aging on Martens hardness and indentation modulus of different dental CAD/CAM restorative materials. J Mech Behav Biomed Mater. 2018;86:191-198. http://dx.doi.org/10.1016/j.jmbbm.2018.06.028
    » https://doi.org/10.1016/j.jmbbm.2018.06.028
  • 24
    Awada A, Nathanson D. Mechanical properties of resin-ceramic CAD/CAM restorative materials. The Journal of Prosthetic Dentistr. 2015;114(4):587-593. http://dx.doi.org/10.1016/j.prosdent.2015.04.016
    » https://doi.org/10.1016/j.prosdent.2015.04.016
  • 25
    Ludovichetti FS, Trindade FZ, Werner A, Kleverlaan CJ, Fonseca RG. Wear resistance and abrasiveness of CAD-CAM monolithic materials. J Prosthet Dent. 2018 Aug;120(2):318.e1-318.e8. http://dx.doi.org/10.1016/j.prosdent.2018.05.011
    » https://doi.org/10.1016/j.prosdent.2018.05.011

Edited by

Assistant editor: Luciana Butini Oliveira

Publication Dates

  • Publication in this collection
    09 Oct 2023
  • Date of issue
    2023

History

  • Received
    02 Feb 2023
  • Accepted
    05 July 2023
Faculdade São Leopoldo Mandic Rua José Rocha Junqueira, 13, CEP: 13045-755 , Tel.: +55 (19) 3211-3689 - Campinas - SP - Brazil
E-mail: contato@revistargo.com.br