vol.28 número2Eletrocatálise da reação de redução de oxigênio sobre eletrodos de grafite modificados com ftalocianina tetracarboxilada de ferroCaracterísticas da adsorção de piridina sobre Au(111) e Au(210) estudadas por ajustes dos parâmetros de EIE índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados

Journal

Artigo

Indicadores

Links relacionados

Compartilhar


Eclética Química

versão impressa ISSN 0100-4670versão On-line ISSN 1678-4618

Resumo

GIZ, M. J.; MARENGO, M. C.; TICIANELLI, E. A.  e  GONZALEZ, E. R.. Electrochemical and physical characterization of Ni-Cu-Fe alloy for chlor-alkali hydrogen cathodes. Eclet. Quím. [online]. 2003, vol.28, n.2, pp.21-28. ISSN 1678-4618.  https://doi.org/10.1590/S0100-46702003000200003.

This work describes the development of an alternative acetate bath for the electrochemical codeposition of Ni-Cu-Fe electrodes at low pH that is stable for several weeks and produces electrodes with good performance for chlor-alkali electrolysis. Physical characterization of the electrode surface was made using X ray absorption spectroscopy (XAS), scanning electron microscopy (SEM) and energy dispersive analysis (EDX). The evaluation of the material as electrocatalyst for the hydrogen evolution reaction (her) was carried out in brine solution (160 g L-1 NaCl + 150 g L-1 NaOH) at different temperatures through steady-state polarization curves. The Ni-Cu-Fe electrodes obtained with this bath have shown low overpotentials for the her, around 0.150 V at 353 K, and good stability under continuous long-term operation for 260 hours. One positive aspect of this cathode is that the polarization behavior of the material shows only one Tafel slope over the temperature range of 298 - 353 K.

Palavras-chave : hydrogen production; cathodes; electrolysis; chlor-alkali.