Chemical modification of the layered K4Nb6O17 material was systematically investigated through the reaction of its proton-exchanged form (H2K2Nb6O17) in alkaline solutions containing tetramethylammonium (tma+), tetraethylammonium (tea+) or tetrapropylammonium (tpa+) cations. The intercalated amount reaches 50% (for tma+), 25% (for tea+) and 15% (for tpa+) of the H2K2Nb6O17 negative charge (concerning the exchange at interlayer I) due to the steric hindrance of larger cations. Hexaniobate samples present (020) basal reflections equal to 23.0, 26.3 and 26.5 Å once intercalated respectively with tma+, tea+ and tpa+. When samples are heated above 200-250 ºC, CO2 evolution is observed; Hofmann elimination reaction is also detected for hexaniobate-tpa+ samples. Scanning electron microscopy images show the predominance of plate-like particles; stick-like particles are also observed for samples containing bulky ions. The intercalation reaction is promoted in the order tma+ > tea+ > tpa+, while the formation of a dispersion of colloidal particles is facilitated in the inverse order.
layered niobate; hexaniobate; tetraalkylammonium; intercalation