Abstract
The aim of this study was to evaluate of pre-heating, filler contents and ceramic thickness on film thickness, microshear bond strength, degree of conversion and color change on ceramic veneers. Two experimental composites were prepared (Bis-GMA/UDMA/BisEMA/ TEGDMA), with different amounts of filler (65% or 50%wt) simulating a conventional and a flowable composite. The flowable (F) was used at room temperature and, the conventional either at room temperature (C) or pre-heated (CPH). Disk-shaped ceramics with different thickness (0.4 mm, 0.8 mm, 1.5 mm) were prepared. The film thickness was evaluated according to the ISO 4049 (n=10). The microshear bond strength (n=10) was evaluated in enamel using tubing specimens light-cured through the ceramic veneer. The degree of conversion was evaluated using Raman spectroscopy. The color change of the ceramic restorations (n=10) was evaluated by spectrophotometry. The results were submitted to 2-way ANOVA and Tukey’s post hoc test (a=5%). For the film thickness 1-way ANOVA was used (a=5%). The C presented the thicker film thickness; the CPH produced a similar film thickness in comparison to the F. All composites showed similar microshear bond strength. The degree of conversion of the F was higher than the C and CPH. The degree of conversion of the composites photo-activated through a 0.4 mm was higher than the composites photo-activated through thicker ceramics. The C showed the highest color change, while the CPH showed similar color change to the F. In conclusion, pre-heated conventional composites seem to be a potential alternative to lute ceramic veneers such as the flowable composites.
Key Words:
film thickness; degree of conversion; model composite; experimental composite
Thumbnail
Thumbnail