ARAUJO, Edcleide M.; HAGE JR., Elias  e  CARVALHO, Antônio J. F.. Compatibilization of Polyamide 6/ABS blends using MMA-GMA and MMA-MA reactive acrylic copolymers. Part 2. Thermal-mechanical and morphological behavior of blends. Polímeros [online]. 2004, vol.14, n.1, pp.22-30. ISSN 1678-5169.  https://doi.org/10.1590/S0104-14282004000100010.

Blends of Polyamide 6 (PA6) with acrylonitrile-butadiene-styrene (ABS) were prepared in a corotating twin-screw extruder, using the poly(methyl methacrylate-co-glycidyl methacrylate) (MMA-GMA) and poly(methyl methacrylate-co-maleic anhydride) (MMA-MA) copolymers as compatibilizing agents. The ABS by itself was not capable to toughen PA6 and showed a phase morphology with large and small agglomerates in the PA6 matrix. The introduction of MMA-GMA copolymer as a compatibilizing agent in the system did not significantly improve the impact properties of PA6/ABS blend. Transmission electron microscope (TEM) photomicrographs indicated a morphology with two distinct populations of ABS: agglomerates and small dispersed particles resulting in a non-uniform distribution of ABS domains. The compatibilized blend with MMA-MA was super-tough (> 800 J/m) at room temperature and low temperature (~ -10 °C) with small amounts of MA in the copolymer and small amounts of compatibilizer in the blend. The PA6/ABS compatibilized blends with MMA-MA showed a morphology of well dispersed and distributed rubber particles in PA6 matrix, thus demonstrating the effective presence of the copolymer as a compatibilizing reactive agent of this system.

Palavras-chave : Morphology; toughness; polyamide; ABS.