vol.16 número2Study of crystallization behavior of poly(phenylene sulfide)Impregnation of chelating agent 3,3-bis-N,N bis-(carboxymethyl)aminomethyl-o-cresolsulfonephthalein in biopolymer chitosan: adsorption equilibrium of Cu(II) in aqueous medium índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados

Journal

Artigo

Indicadores

Links relacionados

Compartilhar


Polímeros

versão impressa ISSN 0104-1428versão On-line ISSN 1678-5169

Resumo

ROCHA, Tatiana L. A. C.; JACOBI, Marly M.; SAMIOS, Dimitrios  e  SCHUSTER, Robert H.. Evaluation of the influence of the polymer-filler interaction on compounds based on epoxidized elastomeric matrix and precipitated silica. Polímeros [online]. 2006, vol.16, n.2, pp.111-115. ISSN 1678-5169.  https://doi.org/10.1590/S0104-14282006000200010.

The introduction of epoxy groups into the main chain of elastomers has emerged as a promising alternative, considering the monitoring of polymer-filler interaction leading to changes in the properties of vulcanizates. The epoxidation reaction (in situ) was chosen to modify elastomers, such as polybutadiene (BR) and copolymer of styrene-butadiene-rubber (SBR), because it is a simple, easily controlled reaction, even considering the small epoxidation degree. The modification degree of the polymeric chain was studied with FT-IR and 1H-NMR. The shift of the Tg to high temperatures with the increase of the epoxy group in the polymer chain was monitored through differential scanning calorimetry (DSC). An analysis of the dynamic modulus of the material in relation to its dependence on the amplitude and temperature was carried out. The interaction between epoxidized elastomeric matrix and silica as filler was extremely improved, even in the presence of very low content of epoxy groups into the polymer chain.

Palavras-chave : Epoxidation; SBR; polymer-filler interaction; dynamic properties; precipitated silica.