vol.16 número2Impregnation of chelating agent 3,3-bis-N,N bis-(carboxymethyl)aminomethyl-o-cresolsulfonephthalein in biopolymer chitosan: adsorption equilibrium of Cu(II) in aqueous mediumStudy of the biodegradation of a polymer derived from castor oil by scanning electron microscopy, thermogravimetry and infrared spectroscopy índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados

Journal

Artigo

Indicadores

Links relacionados

Compartilhar


Polímeros

versão impressa ISSN 0104-1428versão On-line ISSN 1678-5169

Resumo

SANTI, Cristiano R. de; CORREA, Ana Carolina  e  MANRICH, Sati. Films of post-consumer polypropylene composites for the support layer in synthetic paper. Polímeros [online]. 2006, vol.16, n.2, pp.123-128. ISSN 0104-1428.  https://doi.org/10.1590/S0104-14282006000200012.

Composite films were studied as possible candidates for the central or support layer of synthetic paper in a multilayer structure. Recycled post-consumer polypropylene films were reinforced with inorganic fillers at various compositions and under several processing conditions, with the aim of optimizing the physical and mechanical properties of rigidity and low density. Three types of CaCO3, with and without surface treatment of the particles, were used, but only the treated ones were suitable for use in paper films. These samples were then used to analyze possible correlations of properties with composition and processing conditions, varying the CaCO3 particle size distribution and the film processing method, from casting extrusion (flat die) to blown-film extrusion (tubular die). An increase in film stiffness was observed as a function of CaCO3 content and a concentration of 30% CaCO3 was found to be best for the specific application. The flat films were stiffer than the tubular ones. The densities of all the composite films were considered high, compared to a pulp-based paper and a commercial synthetic paper. No significant effect on the physical-mechanical properties analyzed was observed when the CaCO3 particle size distribution was varied. Microcavities were found to form at the surface of flat films submitted to a bi-orientation process performed at laboratory scale; no other sample showed this surface morphology.

Palavras-chave : Polypropylene; synthetic paper; post-consumer waste; composite; oriented film.