vol.25 número5The effects of porosity in friction performance of brake pad using waste tire dustRheological, mechanical and morphological properties of poly(methyl methacrylate)/poly(ethylene terephthalate) blend with dual reactive interfacial compatibilization índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados




Links relacionados



versão impressa ISSN 0104-1428versão On-line ISSN 1678-5169


MIGHANI, Hossein; FATHOLLAHI, Ehsan  e  GHAEMY, Moosa. Synthesis and characterization of novel polyester containing Schiff-base unit. Polímeros [online]. 2015, vol.25, n.5, pp.447-450. ISSN 1678-5169.

A new Schiff base type of polyester containing 2,2-dimethyl-1,3-diaminopropane was prepared by solution polycondensation of 1,4-benzenedicarbonyl dichloride with Bis(4-hydroxybenzilaldehid)-2,2-dimethyl-1,3-propildiimine (H2HB2P) which is derived from a 2,2-dimethyl-1,3-diaminopropane Schiff base reacted with a 4-hydroxybenzaldehyde monomer. The monomer and the polyester were characterized by FTIR,1HNMR, and elemental analysis. The prepared polyester showed inherent viscosity of 0.29 dl/g in NMP at 25 °C, indicating their moderate molecular weight. The Polyester was completely soluble in aprotic polar solvents such asN -methylpyrolidone (NMP), dimethylformamide (DMF), Dimethyl Acetamid (DMAC), dimthylsulfoxide (DMSO). TGA determined the 10% weight loss temperature (T10) at 280 °C and residual weight at 600 °C ca. 41% under nitrogen atmosphere.

Palavras-chave : polyester; Schiff base; 2; 2-dimethyl-1; 3-diaminopropane; thermal stability.