Sericin as compatibilizer in starch/ polyester blown films

Abstract

This study investigated the effects of low concentrations of sericin (≤ 1.5 wt%) in starch- poly(butylene-adipate-co-terephthalate) (PBAT) films. The films were produced by blown extrusion and mechanical, barrier and structural properties were determined. Films containing 1.0 and 1.5 wt% sericin showed higher tensile strength (6.41 and 6.59 MPa) and Young's modulus (90.88 and 132.71 MPa) compared with film without sericin (4.76 MPa and 18.64 MPa). When 0.5 wt% of sericin was used, the elongation was reduced by 62%. The addition of sericin in a concentration of 1.5% (w/w) decreased the water vapor permeability of films from 7.55 to 5.94 g (m s Pa)^-1, likely due to the formation of a more homogeneous and compact matrix. Based on these results, a mechanism of action is proposed, whereby sericin acts at the interface of the polymers (starch and PBAT), reducing the interfacial tension and enhancing compatibility.

Keywords:
biodegradable packaging; compatibilization; extrusion; poly(butylene- adipate-co-terephthalate)