This study was carried out in conjunction with the investigation, reported in Part I, on the microstructural characteristics of an alumina-spinel castable with several percentages of MgO content. Bulk density and cold crushing strength of samples were evaluated dried and at three fired states (1000, 1200, 1400 °C). Results indicate little influence of MgO additions on physico-chemical properties of the alumina-magnesia/self-forming spinel castable. Characteristics compared with those reported for conventional alumina-spinel castables did not show large difference in values. Therefore, the alumina-magnesia/self-forming spinel castable could be a possible material for substitution of the conventional alumina-spinel castable.
Refractories; magnesium aluminate; spinel; castable; alumina-magnesia; refractory lining; MgAl2O4; MgO-Al2O3