Powders of Pr0.70Sr0.30MnO3δ (PSM) and Nd0.70Sr0.30MnO3δ (NSM) compositions are being investigated as alternative cathode materials for Intermediate Temperature Solid Oxide Fuel Cells. The compositions were synthesized by a solution-combustion method using metal nitrates and urea as fuel. Combustion synthesis is a highly suitable synthesis route for achieving fine and homogeneous powders at low temperatures. Single phase pseudo-perovskite was obtained by X-ray diffraction after heat treatment of PSM and NSM powders at 900 ºC. The synthesized and milling powders had an average particle size between 0.27 to 0.07 μm. Chemical analyses of the powders calcined was performed by X-ray fluorescence and morphological analysis by scanning electron microscopy. The results were compared with literature values, indicating characteristics adjusted for preparation of ceramic suspensions.
combustion synthesis; powders; cathode; solid oxide fuel cell