MARTINS, Juliana de Paula; CARVALHO, André Luis Moreira de  e  PADILHA, Angelo Fernando. Texture analysis of cold rolled and annealed aluminum alloy produced by twin-roll casting. Mat. Res. [online]. 2012, vol.15, n.1, pp. 97-102.  Epub 22-Dez-2011. ISSN 1516-1439.  http://dx.doi.org/10.1590/S1516-14392011005000101.

A 7.4 mm thick strip of 3003 aluminum alloy produced by the industrial twin-roll casting (TRC) process was homogenized at 500 °C for 12 hours, after which it was cold rolled in two conditions: 1) to reduce the strip's thickness by 67%, and 2) to reduce it by 91%. The alloy was annealed at 400 °C for 1 hour in both conditions. The results revealed that a rotated cube texture, the {001}<110> component, predominated in the as-cast condition and was transformed into brass, copper and S type textures during the cold rolling process. There was practically no difference between the deformation textures at the two thickness reductions.

Palavras-chave : aluminum alloys; Al-Mn-Fe-Si; twin-roll continuous casting; texture.