When multifunctional surface engineering processes that combine purpose-oriented phases are applied to soft substrates, a combination of high wear resistance, high load support and low coefficients of friction can be achieved. In this study, the effects of different nitrided layers on the tribological behaviour of a diamond-like carbon (DLC) film deposited on a SAE 1040 steel were investigated. The nitriding was carried out under different temperatures and gas mixtures to create three distinct nitrided layers: two compound layers with predominant ε and γ' phases and a diffusion layer. All of the surfaces were then coated with DLC deposited via plasma-enhanced chemical vapour deposition (PECVD). The tribological tests indicated that the best performance was achieved for a specific combination of hardness, surface roughness and nitride type. The best load-bearing capacity between the DLC coating and the soft substrate was achieved when the nitrided layer was primarily a diffusion layer.
Keywords:
DLC; Nitriding; Roughness; Friction; Adhesion