Simplified recovery process of Ralstonia solanacearum-synthesized polyhydroxyalkanoates via chemical extraction complemented by liquid-liquid phase separation

Abstract

Poly (3-hydroxybutyrate) (P(3HB)) is the most studied thermoplastic biopolymer belonging to the polyhydroxyalkanoate (PHA) family, the main features of which include rapid biodegradability and biocompatibility. The bioplastic recovery process is an important step during production and can directly influence the characteristics of PHAs. However, more efficient methods for the production of P(3HB) are necessary to make it economically viable. The aim of the present study was to improve the standard, chloroform-based, extraction step for the recovery of P(3HB). The polymer was produced using a Ralstonia solanacearum strain. The following parameters were improved in the recovery process: heating time, separation method (filtration or liquid-liquid phase separation), biomass state (fresh or dry cell concentrate) and the solvent:biomass ratio. By improving the chemical extraction of P(3HB) we recovered 98% of the cumulative polymer and reduced the heating time by 75%. Furthermore, we improved the separation process and developed an extraction solution that was faster and more economical.

Keywords:
bioplastic; biopolymer; bioprocess; chloroform; poly (3-hydroxybutyrate)

INTRODUCTION

Conventional plastics derived from petroleum have been used for decades due to their strength, durability and low production costs. While plastics are a major benefit to society, their continued use is being questioned due to the serious impact plastics have on human health and the environment.¹ Bioplastics produced by bacteria and plants are potential replacements for petrochemical derived plastics. Polyhydroxyalkanoates (PHAs) are bio-derived and biodegradable polymers that are used in the production of bioplastics. Poly (3-hydroxybutyrate) (P(3HB)) is one of the most common PHAs and it is produced by a variety of organisms.^1-3 In bacteria, PHAs accumulate in the cytoplasm as insoluble polyester inclusion bodies that can represent up to 90% of the biomass.⁴ PHAs are energy storage metabolites and are produced in response to stress, usually under nutrient limiting conditions.⁵ While over 300 microorganisms can synthesize PHAs, production is usually limited to Ralstonia spp., Cupriavidus necator, Pseudomonas spp. and recombinant Escherichia coli.^6-9Ralstonia spp. tend to be more amenable to production on an industrial scale, demonstrating high yields and production rates,¹⁰ accumulating approximately 80% of its dry weight as polymer.¹¹ The strain used in the present study, R. solanacearum RS was isolated from a cactus in Rio Grande do Sul (RS) and was characterized by 16S rRNA sequeincing.^12,13R. solanacearum is Gram-negative phytopathogen that causes bacterial wilt,¹⁴ a vascular disease of wide range of plants, including crops of high economic value, such as potatoes, tomatoes and tobacco belonging to the Solanum genus.^15,16

With physical properties similar to polypropylene, including melting point, crystallinity, and glass transition temperature, P(3HB) is the most studied and most used biopolymer for the production of bioplastics.⁶ However, the bioprocess used to produce these bioplastics can cost up to five times the price of synthetic plastics. The extraction step is the most problematic and expensive, representing 50% or more of the total cost of production.³ Furthermore, the extraction process directly affects the quality of the recovered polymer. Therefore, research has focused on improving and minimizing the costs associated with extraction. Several extraction methods have been developed for the recovery of PHAs, including solvent extraction using chloroform, sodium hypochlorite digestion, surfactant, chelating enzymes and mechanical disruption.^17-21 However, there is no published method for the extraction of PHAs or P(3HB) that does not directly alter the characteristics of the recovered polymer. Although P(3HB) is a commercial product, the problems associated with the extraction process have been not been resolved. Previous studies have focused on reducing damage to the polymer during the extraction step.^21,22 However, the majority of these methods require extended heating and the use of chlorinated solvents, which are extremely toxic. Specific methodologies for the production of PHAs have been developed, but they are trade secrets or are protected by patents.

Recent research has focused on the microorganisms that are capable of producing PHAs or on their application.^1,7-9,13 Thus, there is an urgent need for research into the improvement of the polymer extraction process. We believe that this study will contribute to a more practical production, efficient recovery of P(3HB), representing an important contribution to this field of study. The aim of this study was to improve the P(3HB) extraction step using chloroform as the solvent and analysing the following variables: heating time, separation methodology, biomass state (fresh or dried concentrate) and the solvent:biomass ratio. Additionally, we evaluated the influence of the different extraction methodologies on the characteristics of the recovered P(3HB).

EXPERIMENTAL

Microorganism

The R. solanacearum RS strain was supplied by the Bacteriology Laboratory, Eliseu Maciel Faculty of Agronomy, Federal University of Pelotas, RS, Brazil. The bacterium was lyophilised and stored at -80 ºC, or sub-cultured monthly on nutrient agar (NA),²³ composed of (in g L^-1) peptone, 5.0 g; glucose, 5.0 g; yeast extract, 1.0 g; meat extract, 3.0 g; and agar, 15.0 g and stored at 4 ºC.

Production of P(3HB)

P(3HB) production was carried out in two steps: 1) Starter culture production, R. solanacearum RS was inoculated onto NA and incubated at 28 ºC for 72 h. The colonies were recovered from the NA plate and resuspended in 40 ml yeast malt (YM)²⁴ culture medium that was used to inoculate 160 ml YM in 500 ml Erlenmeyer finned flasks. The culture was grown at 28 ºC, 150 rpm for 24 h on an orbital shaking incubator. The starter culture was used for 2) Accumulation/production of P(3HB), 160 ml of F4 mineral production medium (composed of (in g L^-1) glucose, 40.0 g; urea, 3.0 g; citric acid, 0.2 g; sodium citrate, 4.0 g; and 1.0 ml trace element solution (MgSO₄ 0.2 g; CaCl₂, 0.01 g; Na₂MoO₄, 0.005 g; Z_nSO₄, 0.1 g; FeCl₃, 0.05 g) was inoculated with 40 ml of the starter culture in 500 ml Erlenmeyer finned flasks and incubated at 28 ºC, 200 rpm for 72 h.

Evaluating the presence of lipophilic bodies

Lipophilic bodies were detected using the Sudan Black staining method as described previously.²⁵ Samples of R. solanacearum were fixed on glass slides and stained with Sudan Black dye (0.3% w v^-1) for 10 min, the slides were rinsed with xylene and water, dried with absorbent paper and stained with 0.5% safranin dye for 15 s, washed with water and allowed to dry. The presence of lipophilic granules was visualised by light microscopy using an immersion lens.

Determination of equivalency between fresh and dry cell concentrates

Following the accumulation step for P(3HB) production, the bacteria were harvested by centrifugation (10,000 ×g for 15 min), the fresh cell concentrate (FCC) was resuspended in 0.89% saline solution, and the biomass was recovered (10,000 ×g for 10 min). The amount of insoluble P(3HB) in the FCC was determined by gravimetry. The dry cell concentrate (DCC) was obtained by drying the FCC at 56 ºC. To compare the quantity of P(3HB) in the FCC compared to the DCC, triplicate FCC samples (1 g) were dried at 56 ºC, after reaching a constant weight the FCC/DCC ratio was calculated.

Extraction of the polymer

Improvement of the extraction time and cellular residue separation/extraction solution

The extraction step was performed using a chloroform:DCC ratio of 40:1 (v w^-1). The sample was heated in a glass test tube in a water bath at 58 ºC^26,27 for 15, 30, 60, 90 and 120 min. The cell residue was separated from the extraction solution using two methods: (1) Filtration through quantitative filter paper, the polymer was transferred to a covered Petri dish, and stored in a gas exhaust hood for slow solvent evaporation and biofilm formation; (2) Liquid-liquid phase separation based on differences in polarity. The sample was transferred to a separator funnel with 40 parts of distilled water, gently agitated and the phases were allowed to separate for 5 min. The organic phase was transferred to a covered Petri dish and stored in a gas exhaust hood for slow evaporation of the solvent and biofilm formation.

Improvement of the biomass state (FCC or DCC) and solvent ratio

To improve the biomass state (FCC or DCC) and the solvent ratio, we used a heating time of 30 min and a cell residue separation/extraction solution using liquid-liquid phase separation. The extraction was performed using the following chloroform:biomass ratios: 40:1; 20:1 and 10:1 (v w^-1) and either the FCC or the DCC. To evaluate the efficiency of the primary extraction step, a secondary extraction was performed by adding solvent to the aqueous phase fraction from the primary extraction. The remainder of the extraction step was carried out as described for the primary extraction step.

Quantification of P(3HB) accumulation by gas chromatography (GC)

GC was used to determine the percentage of P(3HB) accumulation in relation to the biomass. Methanolysis was carried out as described previously²⁸ with modifications.²⁹ 10 mg of the DCC was resuspended in 2 ml of acidified methanol (methanol:sulphuric acid, 85:15 v v^-1) containing benzoic acid 0.4 g L^-1 (internal standard) and 2 ml of chloroform. The sample was incubated at 100 ºC for 140 min, transferred to an ice bath and 1 ml of distilled water was added. The sample was incubated at 25 ºC for 24 h and the cell residue was removed by decanting. The lower organic phase contained the ester solubilized in chloroform. The GC analysis was performed using a Shimadzu GC 17A, equipped with a DB WAXetr column (30 m x 0.25 mm x 0.25 mm) and a flame ionization detector. The carrier gas was hydrogen (1 ml min^-1). The initial temperature was 80 ºC for 1 min, increased (11ºC min^-1) to 200 ºC, for 4 min. A 1 µl sample was manually injected into the GC. The injector and detector temperatures were set at 260 and 280 ºC, respectively. Quantitative analysis was performed by the internal standardization method using benzoic acid as recommended by the manufacturer.

Determination of yield polymer recovery processes

After the extraction steps the biofilms were weighed to calculate the yield, which was expressed as a percentage. The following equation (1) was used to determine the yield:

(1) $\%\mathrm{Y}=\left(\mathrm{P}1÷\mathrm{P}2\right)\times 100$

where P1 is the total weight of the recovered biofilm and P2 is the accumulation of polymer in the cell concentrate. All averages were compared and analysed statistically by the Tukey test using the Statistix 9 program, p <0.05 was considered significant.

P(3HB) characterization

Fourier transform infrared spectroscopy (FTIR)

The polymeric film was dissolved in chloroform and the standard P(3HB) was mixed with KBr to obtain tablets. To manufacture the tablets, 1 mg of sample was dissolved in 1 mL of chloroform. IR spectra were obtained on a Fourier transform spectrometer Model Shimadzu IR Prestige 21. The images were acquired within a range of 4500-500 cm^-1 with a resolution of 4 cm^-1, as described previously.³⁰

Differential scanning calorimetry (DSC) and thermal gravimetric analysis (TGA)

DSC and TGA analyses were performed using a Perkin Elmer Pyris 6. The DSC analysis \ temperatures ranged from 20-200 ºC, increasing at a rate of 10 ºC min^-1, and a nitrogen atmosphere with a flow rate of 20 ml min^-1. To check the influence of heat on the samples, the crystalline melting temperatures (Tm) were analysed during the first heating cycle. However, in order to eliminate the thermal history of the material, the Tm were determined in a second heating cycle. The degree of crystallinity (Xc) was determined from the melting enthalpy (ΔHm) of the sample and was compared to that of pure P(3HB) (ΔHm = 146 J g^-1).³¹ To check the thermal stability [degradation onset temperature (Tonset) and maximum degradation temperature (Tpeak)] of the extracted polymers, the samples were heated from 30 to 500 ºC at a rate of 10 ºC min^-1 under an atmosphere of nitrogen with a flow rate of 50 ml min^-1.

Gel Permeation Chromatography (GPC)

The molar mass of the polymers was estimated by GPC analysis. The assay was developed by analysts at PHB Industrial SA (Serrana, SP, Brazil) and is not commercially available. We used the following Waters GPC equipment and accessories: 1515 isocratic pump, column heater, 717 plus autosampler, 2414 refractive index detector and Styragel columns (10³, 10⁴, 10⁵ and 10⁶; 7.80 x 300 mm). The samples were solubilized in chloroform, filtered through a 0.45 µm membrane and spiked with toluene as a peak marker prior to injection. The mobile phase was HPLC analytical grade chloroform.

RESULTS AND DISCUSSION

Evaluation of lipophilic bodies

A sample of R. solanacearum RS inoculum was stained and viewed under an optical microscope immersion lens, coupled with a camera and recorded photographically to determine the presence of lipophilic bodies, Figure 1. Sudan Black B is a basic dye that acts by diffusing into the bacteria and combining with acidic groups in lipophilic bodies, such as PHA inclusion bodies, staining them bluish-black in colour.²⁵ The presence of stained inclusion bodies when viewed by microscopy indicates the accumulation of PHAs.³² The location and appearance of the stained inclusion bodies in the bacteria corresponded to P(3HB) accumulation as previously reported in the literature for Ralstonia spp.³² The presence of two granules, one at each pole of the cell, is associated with the early stages of PHA accumulation,³³ in several bacteria, including: Xanthobacter autotrophicus, Caryophanon latum, Rhodospirillum rubrum, R. eutropha and recombinant E. coli. It was suggested that granule formation occurred near the site of septum formation during cell division. The presence of a third granule, as observed in our study, typically occurs in the central region of the bacteria.³⁰

Figure 1
R. solanacearum RS cultivated for 24 h, stained with Sudan Black and viewed with an immersion lens with optical microscopy. It was possible to identify (A) R. solanacearum RS bacterial cells containing two lipophilic granules or (B) three lipophilic granules

Extraction of the polymer

Improvement of extraction time and cell residue/extraction solution separation

The P(3HB) produced in the present study was recovered by filtration or liquid-liquid phase separation. The highest yields were obtained using liquid-liquid phase separation, regardless of the heating time, see Figure 2. For the liquid-liquid separation method, the highest yield (96.8% ± 2.0) was obtained with a heating time of 30 min, followed by 15 min (77.2% ± 1.7). These heating times represent a reduction of 75% and 87.5%, respectively, compared to the standard heating time of 120 min.^26,27 As heating time increased, the yield was reduced: 60, 90 and 120 min resulted in 69.0% ± 2.4, 68.2% ± 1.6 and 66.9% ± 2.2 recovery, respectively, and there was no significant difference in yield. Using the filtration methodology, the yield was significantly lower: 45.2% ± 1.9, 48.9% ± 0.7, 52.2 ± 0.7, 52.8% ± 0.2, and 49.5% ± 0.8 for heating times of 15, 30, 60, 90 and 120 min, respectively.

Figure 2
Comparison of two different separation methods for improving P(3HB) extraction and the heating times used. The average % yield of P(3HB) recovered by the filtration method (solid columns) and the liquid-liquid phase separation method (hatched columns) at different heating times are shown, the error bars represent the standard deviation from the mean. Different lower and uppercase letters indicate a significant difference between the means, Tukey test p < 0.05

The low yield observed with the filtration separation method is likely due to adsorption of P(3HB) to the filter paper. This interaction between PHAs and cellulose was previously observed and is being exploited in the manufacture of hybrid materials, e.g. cardboard waterproofing.³⁴ Of note, P(3HB) yield was not proportional to the heating time during the extraction step. The reduction in yield associated with increased heating time was probably due to polymer degradation.

Improvement of P(3HB) biomass state (FCC or DCC) and solvent ratio

Following the observation that the highest P(3HB) yield was obtained using the liquid-liquid phase separation method and a heating time of 30 min, the optimal biomass state (FCC or DCC) and solvent ratio were determined, see Figure 3. The P(3HB) yields obtained for the DCC were 41.8% ± 9.9, 57.9% ± 8.8 and 98% ± 1.6 for solvent ratios of 10:1, 20:1 and 40:1, respectively. To check for the presence of unrecovered P(3HB) following the primary extraction, a secondary extraction was performed. Thus resulted in 21.7% ± 3.5, 8.8% ± 2.8 and 1.4% ± 0.8 polymer yields at ratios of 10:1, 20:1 and 40:1, respectively. The yield was directly proportional to the solvent:biomass ratio used, and 40:1 gave the best yield with the DCC. A secondary extraction was unnecessary using these conditions.

Figure 3
P(3HB) yields from the DCC and the FCC varied with solvent ratios used. The yields from the primary (solid column) and secondary (hatched column) extractions using either the DCC or the FCC are shown, the error bars represent the standard deviation from the mean. Different upper and lowercase letters represent a significant difference between the means, Tukey test, p < 0.05

As a heating or drying step means higher energy costs, therefore we evaluated the recovery of P(3HB) directly from the FCC. However, the highest yield was low, 17.6% ± 2.5, even though it was obtained using the lowest chloroform:biomass ratio, 10:1, the other yields were 16.4% ± 4.6 and 7.2% ± 4.7 for the 20:1 and 40:1 ratios, respectively. A secondary extraction did not improve the recovery of P(3HB), the yields were 0.6% ± 0.4, 1.7% ± 1.2 and 3.3% ± 1.3 for solvent ratios of 40:1, 20:1 and 10:1, respectively. Comparing the DCC to the FCC showed that 1 g of DCC was equivalent to 3.18 g of FCC in terms of P(3HB) yield. If we correct for equivalency between the DCC and the FCC, the highest yield for the FCC were equivalent to 56.0%, at a 10:1 solvent ratio. However, these yields were still significantly lower than those of the DCC, 98% at a solvent:biomass ratio of 40:1.

Increasing the solvent:biomass ratio improved the breakdown of the emulsion formed by the addition of water during the extraction process. This allowed the formation of defined phases during separation, characterized by an aqueous phase containing cellular residue (more polar) and a chloroform extraction or organic phase (less polar). We did not evaluate the impact of different solvent:biomass ratios on extractions from the FCC.

Evaluating solvent use in the secondary extraction

Towards minimising solvent use for the secondary extraction, we evaluated decreasing amounts of solvent and the impact on P(3HB) recovery. The primary extraction yielded 97.8% ± 1.2 and 97.3% ± 1.5 recovery of P(3HB) followed by 1.3% ± 0.8 and 2.1% ± 0.9 after the secondary extraction at solvent ratios of 20:1 and 40:1, respectively. There was no significant improvement with increased solvent use. It was not possible to perform the secondary extraction with a solvent ratio of 10:1 due to emulsion formation, which prevented the separation of the organic and inorganic phases.

Characterization of recovered P(3HB)

Fourier transform infrared spectroscopy (FTIR)

The chemical composition of the biofilms of the recovered polymers was determined, see Table 1. All of the spectra evaluated showed the characteristic vibrational frequencies for P(3HB). The characteristic FTIR bands identified in the P(3HB) produced in this study was in agreement with those reported in the literature.^30,35,36

Table 1
Main vibrational frequencies for the recovered P(3HB)

Functional group	Wave Number (cm-1)	Vibrational modea	Reference
- CH3	2972	υas	37
- CH3	2872	υs	37
- CH2	2933	υas	38
- CH2	2853	υs	38
- C=O	1721-1727	υ	39
- CH2	1454-1459	δs	37
- CH3	1378	δs	37
- C-O	1300-1000	υ	39

• ^a
  Experimentally obtained values, υ: stretching; δ: deformation; s: symmetric; as: asymmetric.

Differential scanning calorimetry (DSC) and thermal gravimetric analysis (TGA)

Although the P(3HB) samples produced in this study had a higher melting temperature (170-175 ºC) than those commercially available from Sigma-Aldrich (144 ºC) and Biocycle (166 ºC), the values fell within the expected temperature range for P(3HB), see Table 2. Melting temperatures have been reported to vary from 131-180 ºC, with an average of approximately 160 ºC.^30,40-43 There was no relationship between the observed melting temperatures and the solvent:biomass ratios used in this study.

Table 2
Characteristics of the P(3HB) produced in this study compared to commercially available P(3HB)

P(3HB) Samplesa	Tm1b(ºC)	Tm2c(ºC)	% Xcd	Tonsete(ºC)	Tpeakf(ºC)	% Weight Loss
Sigma-Aldrich	167	144	19	230	262	99
Biocycle	167	166	49	259	280	100
DCC10	176	172	52	223	289	86
DCC20	176	170	63	220	270	79
DCC40	176	172	52	219	292	82
FCC10	179	172	51	210	269	87
FCC20	178	175	37	213	266	85
FCC40	177	170	44	208	241	76

• ^a
  10: solvent ratio 10:1; 20: solvent ratio 20:1; 40: solvent ratio 40:1;
• ^b
  Crystalline melting temperatures first cycle;
• ^c
  Crystalline melting temperatures second cycle;
• ^d
  Degree of crystallinity;
• ^e
  Degradation onset temperature;
• ^f
  Maximum degradation temperature.

P(3HB) is generally characterised as a semi-crystalline (60-80% crystallinity), hard and brittle material, limiting its application.⁴⁴ However, there are reports of 42 to 50% crystallinity for P(3HB) produced by Bacillus megaterium and 27-45% for Pseudomonas spp.^30,45 In the present study, the crystallinity of the P(3HB) recovered from the DCC ranged from 37-63%. The P(3HB) with the lowest crystallinity was recovered from the FCC at a solvent ratio of 20:1, however the use of FCC in the extraction process resulted in a low yield (18%). The extraction conditions with the highest yield (98%: DCC, solvent ratio 40:1) produced P(3HB) with 52% crystallinity. Reducing the solvent ratio to 10:1 during extraction resulted in a P(3HB) with the same crystallinity, but with a lower yield (42%). The crystallinity of the P(3HB) samples produced in the present were similar to those reported in the literature and this is important for its use in downstream applications. PHA biodegradability is directly influenced by the degree of crystallinity, low crystalline polymers are desirable due to their lower biodegradation times.¹⁸ PHAs with low crystallinity have desirable mechanical properties for applications in the medical field (e.g. sutures) and pharmaceutical field, e.g. controlled-release of drugs.^3,18

Through TGA analysis of the recovered P(3HB) from the DCC, the onset temperature ranged from 219-223 ºC and the maximum degradation temperature varied from 270-292 ºC. These values were higher than those for the polymers recovered from the FCC, the onset temperature ranged from 208-212 ºC, and the maximum degradation temperature varied from 241-269 ºC. These results indicate that the polymers recovered from the DCC were more temperature resistant, enhancing their processability range and allowing safer handling of the biopolymer.

The observed weight loss ranged from 76-87% but it was not directly related to the biomass state (DCC or FCC) or the solvent ratios used during the extraction step. In most of the P(3HB) samples, thermal degradation occurred in only one stage of weight loss, indicating that the process occurred through a single degradation mechanism.⁴⁶ However, we observed two stages of degradation when the extraction process used a 40:1 solvent ratio. This phenomenon is usually associated with the presence of impurities carried over from the extraction process, e.g. cellular residue. However, the methodologies that employ the largest ratio of solvent to biomass during the extraction process should, in theory, have resulted in greater purification and higher polydispersion of the polymer.

Gel Permeation Chromatography (GPC)

The molar mass (Mm) of the polymers recovered from the DCC were lower than those recovered from the FCC. The values ranged from 2.9 to 3.3×10⁵ Da for the DCC polymers and 5.1 to 6.3×10⁵ Da for the FCC polymers, see Table 3. The Mm of native P(3HB) produced by bacteria usually ranges from 1×10⁴ to 3×10⁶ Da, with a polydispersion (Mm/Mn) value of approximately 2.0, in agreement with the finding of this study.⁴⁷ The Mm of a PHA is a factor of extreme importance because it directly affects the mechanical strength of the polymer, as well as the swell ability, hydrolysis and consequently the rate of biodegradation, which is also related to crystallinity. Thus, for the development of a PHA controlled-release systems, the polymer should have a lower Mm.⁴⁸ Furthermore, PHAs with low Mm can be used as components to build various architectures, such as block and grafting copolymers, as they can provide increased flexibility.^49,50 In addition, we observed that the polymers extracted with a 40:1 solvent ratio showed increased polydispersion regardless of the biomass state used in the extraction process.

Table 3
Polydispersion data and average Mm for recovered P(3HB) from DCC or FCC using different solvent ratios

Samplesa	Polydispersion (Mm/Mn)	Average Molar Mass (Da)
		Mn	Mm
DCC10	2.3	1.4×105	3.2×105
DCC20	2.1	1.6×105	3.3×105
DCC40	2.9	1.0×105	2.9×105
FCC10	2.2	2.8×105	6.3×105
FCC20	2.4	2.7×105	6.3×105
FCC40	3.7	1.4×105	5.1×105

• ^a
  10: solvent ratio 10:1; 20: solvent ratio 20:1; 40: solvent ratio 40:1.

CONCLUSION

The present study found that the conventional method of chemical recovery for P(3HB) using chloroform and heating could be improved by reducing the heating time by 75% and using a solvent:biomass ratio of 40:1. Furthermore, recovery of the P(3HB) using a liquid-liquid phase separation step led to faster separation times and lower costs. Although the use of fresh biomass during the extraction phase may be beneficial because of the lower crystallinity of the recovered P(3HB), using the dried biomass significantly improved the yield from 18% to 98%. In addition, the biomass state affected the thermal characteristics and the molar weight of the recovered P(3HB).

ACKNOWLEDGMENTS

We gratefully acknowledge the financial support received from the funding agencies CAPES and FAPERGS. We thank A. B. Moura, Bacteriology Laboratory, FAEM, UFPel for providing the Ralstonia solanacearum RS strain. We also thank S. M. Kesserlingh, PHB Industrial, for carrying out the molar mass analysis.

REFERENCES

• ¹
  Reddy, C. S. K.; Ghai, R.; Rashmi, T.; Kalia, V. C.; Bioresour. Technol. 2003, 87, 137.
• ²
  Luengo, J. M.; García, B.; Sandoval, A.; Naharroy, G.; Oliveira, E. R.; Curr. Opin. Microbiol. 2003, 6, 251.
• ³
  Serafim, L. S.; Lemos, P. C.; Levantesi, C.; Tandoi, V.; Santos, H.; Reis, M. A. M.; J. Microbiol. Methods 2002, 51, 1.
• ⁴
  Kunasundari, B.; Sudesh, K.; Express Polym. Lett. 2011, 5, 620.
• ⁵
  Madison, L. L.; Huisman, G. W.; Microbiol. Mol. Biol. Rev. 1999, 63, 21.
• ⁶
  Chanprateep, S.; J. Biosci. Bioeng 2010, 110, 621.
• ⁷
  Rodríguez-Contreras, A.; Koller, M.; Dias, M. M. S.; Calafell-Monfort, M.; Braunegg, G.; Marqués-Calvo, M. S.; J. Appl. Microbiol. 2013, 114, 1378.
• ⁸
  Sathish, A.; Glaittli, K.; Sims, R. C.; Mille, C. D.; J. Polym. Environ. 2014, 22, 272.
• ⁹
  Rodríguez-Contreras, A.; Koller, M.; Dias, M. M. S.; Calaffel-Monfort, M.; Braunegg, G.; Marqués-Calvo, M. S.; Biochem. Eng. J. 2015, 94, 50.
• ¹⁰
  Ramsay, J. A.; Berger, E.; Voyer, R.; Chavrie, C.; Ramsay, B. A.; Biotechnol. Tech. 1990, 8, 589.
• ¹¹
  Byrom, D.; Trends Biotechnol. 1987, 5, 246.
• ¹²
  Pereira, D. D.; Moura, A. B.; Silva, E. G.; Kunzler, D. P.; Cienc. Rural 2001, 6, 22.
• ¹³
  Rodrigues, A. A.; Macagnan, K. L; Santos, B. C.; Alves, M. I.; Moura, A. B.; Peralba, M. C. R.; Oliveira, P. D.; Pinto, L. S.; Dellagostin, O. A.; Moreira, A. S.; Vendruscolo, C. T.; Revista Brasileira de Tecnologia Agroindustrial 2015, 9, 1771.
• ¹⁴
  Hayward, A. C.; Rev. Phytopathol. 1991, 29, 65.
• ¹⁵
  Peeters, N.; Guidot, A.; Vailleau, F.; Valls, M.; Plant. Pathol. 2013, 14, 651.
• ¹⁶
  Raza, W.; Ling, N.; Yang, L.; Huang, Q.; Shen, Q.; Sci. Rep. 2016, 6, 24856.
• ¹⁷
  Lee, I. Y.; Kim, G. J.; Choi, D. K.; Yeon, B. K.; Park, Y. H.; J. Ferment. Bioeng 1996, 81, 255.
• ¹⁸
  Lee, S. Y.; Biotechnol. Bioeng. 1995, 49, 1.
• ¹⁹
  Kessler, B.; Witholt, B.; J. Biotechnol. 2001, 86, 97.
• ²⁰
  Jacquel, N.; Lo, C. W.; Wei, Y. H.; Wu, H. S.; Wang, S. S.; Biochem. Eng. J. 2008, 39, 15.
• ²¹
  Quines, L. K. M.; Ienczak, J. L.; Schmidt, M.; Zanfonato, K.; Rodrigues, M. I.; Schmidell, W. Quim. Nova 2015, 38, 214.
• ²²
  Fiorese, M. L.; Freitas, F.; Pais, J.; Ramos, A.; Reis, M.; Eng. Life Sci. 2009, 9, 454.
• ²³
  Schaad, N. W.; Jones, J. B.; Chun, W.; Laboratory guide for identification of plant pathogenic bacteria, 3^th ed., APS Press, 2001.
• ²⁴
  Jeanes, A.; Food Technol. 1974, 28, 34.
• ²⁵
  Lelliot, R. A.; Stead, D. E.; Methods for the diagnosis of bacterial diseases of plants, 1^th ed., Palo Alto: Blackwell, 1987.
• ²⁶
  Vanin, M.; Santana, C. C.; Torriani, I. L.; Privelic, T.; Duek, E. A. R.; Polim.: Cienc. Tecnol. 2004, 14, 187.
• ²⁷
  Dalcanton, F.; Dissertação de Mestrado, Universidade Federal de Santa Catarina, Brasil, 2006.
• ²⁸
  Braunegg, G.; Sonnleitner, B.; Lafferty, R. M.; Appl. Microbiol. Biotechnol. 1978, 6, 29.
• ²⁹
  Brandl, H.; Gross, R. A.; Lenz, R. W.; Fuller, R. C.; Appl. Environ. Microbiol. 1988, 54, 1977.
• ³⁰
  Crochemore, A. G.; Mattos, M. L. T.; Vendruscolo, C. T.; Castro, L. A. S.; Moreira, A. S.; Afr. J. Biotechnol. 2012, 11, 15144.
• ³¹
  Gogolewski, S.; Jovanovic, M.; Perren, S. M.; Dillon, J. G.; Hughes, M. K.; J. Biomed. Mater. Res. 1993, 27, 1135.
• ³²
  Anderson, A. J.; Dawes, E. A.; Microbiol. Rev. 1990, 54, 450.
• ³³
  Jendrossek, D.; Selchow, O.; Hoppert, M.; Appl. Environ. Microbiol. 2007, 73, 586.
• ³⁴
  Domingos, L. F.; Dissertação de Mestrado, Universidade Federal de Santa Catarina, Brasil , 2012.
• ³⁵
  Khardenavis, A. A.; Kumar, M. S.; Mudliar, S. N.; Chakrabarti, T.; Bioresour. Technol. 2006, 98, 3579.
• ³⁶
  Lugg, H.; Sammons, R. L.; Marquis, P. M.; Hewitt, C. J.; Yong, P.; Paterson-Beedle, M.; Biotechnol. Lett. 2008, 30, 481.
• ³⁷
  Silverstein, R. M.; Bassler, G. C.; Morri, L. T. C.; Spectrometric Identification of Organic Compounds, 4^th ed., John Wiley e Sons: New York, 1981.
• ³⁸
  Stuart, B. H.; Infrared Spectroscopy: Fundamentals and Applications, John Wiley e Sons: London, 2004.
• ³⁹
  Pavia, D. L.; Lampman, G. M.; George, S.; Kriz, G. S.; Vyvyan, J. R.; Introdução à Espectroscopia, 4ª ed, Cencgage Learning: São Paulo, 2010.
• ⁴⁰
  Valappil, S. P.; Misra, S. K.; Boccaccini, A. R.; Keshavarz, T.; Bucke, C.; Roya, I.; J. Biotechnol. 2007, 132, 251.
• ⁴¹
  Yezza, A.; Halasz, A.; Levadoux, W.; Hawari, J.; Appl. Microbiol. Biotechnol. 2007, 77, 269.
• ⁴²
  Chaijamrus, S.; Udpuay, N.; Agricultural Engineering International: the CIRGE journal 2008, 7, 30.
• ⁴³
  Hong, S. G.; Lin, Y. C.; Lin, C. H.; React. Funct. Polym. 2008, 68, 1516.
• ⁴⁴
  Khanna, S.; Srivastava, A. K.; Process Biochem. 2005, 40, 607.
• ⁴⁵
  Reddy, S. V.; Thirumala, M.; Mahmood, S. K.; World J. Microbiol. Biotechnol. 2009, 25, 391.
• ⁴⁶
  Duarte, M. A. T.; Júlio, C. F.; Martins, E. S.; Pezzin, S. H.; Rev. Mater. 2004, 9, 386.
• ⁴⁷
  Sudesh, K.; Abe, H.; Doi, Y.; Prog. Polym. Sci. 2000, 25, 1503.
• ⁴⁸
  Montoro, S. R.; Shigue, C. Y.; Sordi, M. L. T.; Santos, A. M.; Ré, M. I.; Polim.: Cienc. Tecnol. 2010, 20, 19.
• ⁴⁹
  Zhang, X.; Yang, H.; Liu, Q.; Zhenh, Y.; Xie, H.; Wang, Z.; J. Polym. Sci., Part A: Polym. Chem. 2005, 43, 4857.
• ⁵⁰
  Lao, H.; Renard, E.; Linossier, I.; Langlois, V.; Vallée-Rehel, K.; Biomacromolecules 2007, 8, 416.

Publication Dates

• Publication in this collection
  Feb 2017

History

• Received
  07 Mar 2016
• Accepted
  05 Aug 2016