Hydrogen production from aqueous glycerol using titanate nanotubes decorated with Au nanoparticles as photocatalysts

Abstract

Abstract: Protonated titanate nanotubes (HTiNts) were synthesized using the hydrothermal method, followed by proton exchange with acid. Gold nanoparticles decorated titanate nanotubes (AuHTiNts) were obtained by the reduction of AuCl4- under vigorous stirring with an aqueous solution of HTiNts containing 1 wt% of ascorbic acid. To investigate the surface structural chemistry of the titanate and AuHTiNts, the following characterization methods were used: scanning and transmission electron microscopy, X-ray diffraction, UV-Vis diffuse reflectance spectroscopy, Raman spectroscopy and X-ray photo-electron spectroscopy. The mean internal and external diameters for titanate nanotubes were found to be 5.46 ± 0.08 nm and 8.42 ± 0.03 nm, respectively, whereas the mean diameter of gold nanoparticles was measured to be 9.68 nm ± 0.03 nm. The as-synthesized AuHTiNts was used as photocatalyst in hydrogen production from glycerol as a sacrificial agent. The enhancement in the production of hydrogen, using the heterogeneous AuHTiNts catalysts, can be attributed to the intrinsic catalytic potential of gold as well as its interactions with titanate nanostructure.

Key words
Titanate nanotubes; Au nanoparticles; catalytic hydrogen production; glycerol


INTRODUCTION

After Fujishima and Honda (1972FUJISHIMA A and HONDA K. 1972. Electrochemical photolysis of water at a semiconductor electrode. Nature 238: 37-38.) reported the water oxidation with TiO2 as the photo-catalyst for the first time in 1972, generating hydrogen and oxygen, many studies have been developed with different electrolytes (De la Piscina and Homs 2008DE LA PISCINA PR and HOMS N. 2008. Use of biofuels to produce hydrogen (reformation processes). Chem Soc Rev 37: 2459-2467.) and photoelectrodes (Valdes et al. 2012VALDÉS Á et al. 2012. Solar hydrogen production with semiconductor metal oxides: new directions in experiment and theory. Phys Chem Chem Phys 14: 49-70.) to increase the hydrogen production (AhmadAHMAD H, KAMARUDIN SK, MINGGU LJ and KASSIM M. 2015. Hydrogen from photo-catalytic water splitting process: A review. Renew Sust Energ Rev 43: 599-610. et al. 2015). However, the H2 production from the water splitting is too low to meet the industrial demand (CrabtreeCRABTREE GW, DRESSELHAUS MS and BUCHANAN MV. 2004. The hydrogen economy. Phys Today 57: 39-44. et al. 2004). On the other hand, the photocatalytic process of organics with semiconductors has proved to be an efficient and attractive method to produce hydrogen with the aid of solar energy through a clean, sustainable and renewable route (EstahbanatiESTAHBANATI MRK, FEILIZADEH M and ILIUTA MC. 2017. Photocatalytic valorization of glycerol to hydrogen: Optimization of operating parameters by artificial neural network. Appl Catal B 209: 483-492. et al. 2017). Glycerol, a by-product of the biodiesel production (McNutt and Yang 2017MCNUTT J and YANG J. 2017. Utilization of the residual glycerol from biodiesel production for renewable energy generation. Renew Sust Energ Rev 71: 63-76.), has a great potential as a starting material for sustainable hydrogen production (Bowker et al. 2009).

Titanium oxide is one of the most used photocatalysts owing to their exceptional electronic and optical properties, high oxidation power, low-toxicity, chemical stability, abundance and low cost of synthesis (Fang et al. 2017FANG W, XING M and ZHANG J. 2017. Modifications on reduced titanium dioxide photocatalysts: A review. J Photochem Photobiol 32: 21-39.). Titanate nanotubes (TiNts) have mesoporous morphology and high specific surface area (GeGE MZ, CAO CY, HUANG JY, LI SH, ZHANG SN, DENG S, QING-SONG, ZHANG KQ and LAI YK. 2016. Synthesis, modification, and photo/photoelectro- catalytic degradation applications of TiO2 nanotube arrays: a review. Nanotechnology 5: 1-38. et al. 2016), with photocatalytic properties similar to TiO2 (Guimarães et al. 2017GUIMARÃES ZAS, DAMATTA RA, GUIMARÃES RS and FILGUEIRA M. 2017. A Novel Porous Diamond - Titanium Biomaterial: Structure, Microstructure, Physico-Mechanical Properties and Biocompatibility. An Acad Bras Cienc 89: 3111-3121.), which is even better for photocatalysis and therefore, has received much attention in recent years (AbdullahABDULLAH M and KAMARUDIN SK. 2017. Titanium dioxide nanotubes (TNT) in energy and environmental applications: An overview. Renew Sust Energ Rev 76: 212-225. and Kamarudin 2017, Ge et al. 2017GE M, LI Q, CAO C, HUANG J, LI S, ZHANG S, CHEN Z, ZHANG K, AL-DEYAB SS and LAI Y. 2017. One-dimensional TiO 2 Nanotube Photocatalysts for Solar Water Splitting. Adv Sci 4: 1600152.). Still, the usage of TiNts, as well as TiO2 as efficient photocatyst is limited due to their high band gap (3.4 eV) which restricts their capability to capture light beyond the UV region (Liu et al. 2014LIU N, CHEN X, ZHANG J and SCHWANK JW. 2014. A review on TiO2-based nanotubes synthesized via hydrothermal method: Formation mechanism, structure modification, and photocatalytic applications. Catal Today 225: 34-51.). To overcome this barrier, many studies has been focused on the synthesis of suitable hetero-nanostructures based on TiNT and TiO2 nanotubes as substrates which can be decorated with different active catalysts leading to photocatalytic applications (Kukovecz et al. 2016KUKOVECZ Á, KORDÁS K, KISS J and KÓNYA Z. 2016. Atomic scale characterization and surface chemistry of metal modified titanate nanotubes and nanowires. Surf Sci Rep 71: 473-546., Yang et al. 2015YANG X, WU L, DU L and LI X. 2015. Photocatalytic Water Splitting Towards Hydrogen Production on Gold Nanoparticles (NPs) Entrapped in TiO2 Nanotubes. Catal Lett 145: 1771-1777.).

Catalytic hydrogen production from photoreforming of glycerol-water mixture using titanate and related nanostructures had been a great area of interest although its mechanistic insights are yet to be fully understood. Upon irradiation of photons, having higher energy than the band gap of titanate or related nanostructure, the electrons (e-) are excited from valence band to conduction band, leaving behind holes (h+). These photogenerated e-/h+ pair react with available oxi-reducible species, such as surface bond water molecules or dissolved oxygen molecules which further react following many possible oxi-reduction routes, evolving different reactive oxygen species (ROS), such as O•2- , 1O2, H2O2 and OH• etc (Jedsukontorn et al. 2018JEDSUKONTORN T, UENO T, SAITO N and HUNSOM M. 2018. Mechanistic aspect based on the role of reactive oxidizing species (ROS) in macroscopic level on the glycerol photooxidation over defected and defected-free TiO2. J. Photochem Photobiol A: Chemistry 367: 270-281.). These ROS react with glycerol molecules in many possible ways leading to its complete oxidation to CO2 via generation of many organic intermediates with general formulae etc CxHyOz, such as glyceraldehyde (C3H6O3), dihydroxyacetone (C3H6O3), glycolaldehyde (C2H4O2), acetaldehyde (C2H4O), formaldehyde (CH2O) and formic acid (CH2O2) in the liquid phase (SanwaldSANWALD KE, BERTO TF, EISENREICH W, GUTIÉRREZ OY and LERCHER JA. 2016. Catalytic routes and oxidation mechanisms in photoreforming of polyols. J Catal 344: 806-816. et al. 2016). Careful study with D2O showed that both H2O and glycerol molecule takes part in the generation of the H2 (Fujita et al. 2016FUJITA SI, KAWAMORI H, HONDA D, YOSHIDA H and ARAI M. 2016. Photocatalytic hydrogen production from aqueous glycerol solution using NiO/TiO2 catalysts: Effects of preparation and reaction conditions. Appl Catal B Environ 181: 818-824.) and the total oxi-reduction reaction can be written as (Daskalaki et al. 2009):

C 3 H 8 O 3 + 3 H 2 O h ν > B G 3 C O 2 + 7 H 2

Whereas the half reaction can be written as

Anode: C3H8O3+14h++3H2O3CO2+14H+

Cathode: 14H++14e7H2

The noble metals, e.g. Au, Pt and Pd have been reported as efficient dopants for activation in visible light, thus improving the performance of the photocatalysts (BamwendaBAMWENDA GR, TSUBOTA S, NAKAMURA T and HARUTA M. 1995. Photoassisted hydrogen production from a water-ethanol solution: a comparison of activities of AuTiO2 and PtTiO2. J Photochem Photobiol A: Chem 89: 177-189. et al. 1995, Jakob et al. 2003JAKOB M, LEVANON H and KAMAT PV. 2003. Charge Distribution between UV-Irradiated TiO2 and Gold Nanoparticles: Determination of Shift in the Fermi Level. Nano Lett 3: 353-358., JohnJOHN MR ST, FURGALA AJ and SAMMELLS AF. 1983. Hydrogen generation by photocatalytic oxidation of glucose by platinized n-titania powder. J Phys Chem A 87: 801-805. et al. 1983, Sakthivel et al. 2004SAKTHIVEL S, SHANKAR MV, PALANICHAMY M, ARABINDOO B, BAHNEMANN DW and MURUGESAN V. 2004. Enhancement of photocatalytic activity by metal deposition: characterisation and photonic efficiency of Pt, Au and Pd deposited on TiO2 catalyst. Water Res 38: 3001-3008.). The Fermi levels of these noble metals are smaller than those of semiconductors, such as TiO2 and TiNts, which results in an effective transfer of photogeGE M, LI Q, CAO C, HUANG J, LI S, ZHANG S, CHEN Z, ZHANG K, AL-DEYAB SS and LAI Y. 2017. One-dimensional TiO 2 Nanotube Photocatalysts for Solar Water Splitting. Adv Sci 4: 1600152.nerated electrons from the semiconductor conduction band to the metal particles (EtacheriETACHERI V, VALENTIN CD, SCHNEIDER J, BAHNEMANN D and PILLAI SC. 2015. Visible-light activation of TiO2 photocatalysts: Advances in theory and experiments. J Photochem Photobiol C 25: 1-29. et al. 2015). This electron capture process significantly reduces the electron-hole recombination rate, giving rise to more efficient photocatalytic reactions. Among other advantages, gold nanoparticles (AuNPs) allow the photosensitization of the heterostructure due to the possibility of the surface plasmonic resonance effect (SPR) (Cushing et al. 2015CUSHING SK, LI J, BRIGHT J, YOST BT, ZHENG P, BRISTOW AD and WU N. 2015. Controlling Plasmon-Induced Resonance Energy Transfer and Hot Electron Injection Processes in Metal@TiO2 Core–Shell Nanoparticles. J Phys Chem C 119: 16239-16244., PrimoPRIMO A, CORMA A and GARCÍA H. 2011. Titania supported gold nanoparticles as photocatalyst. Phys Chem Chem Phys 13: 886-910. et al. 2011). Also it reduces the energy required to promote the formation of the electron-hole pairs (Ingram et al. 2011INGRAM DB, CHRISTOPHER P, BAUER JL and LINIC S. 2011. Predictive Model for the Design of Plasmonic Metal/Semiconductor Composite Photocatalysts. ACS Catal 1: 1441-1447., PrimoPRIMO A, CORMA A and GARCÍA H. 2011. Titania supported gold nanoparticles as photocatalyst. Phys Chem Chem Phys 13: 886-910. et al. 2011, Rouby et al. 2017ROUBY WMA, COMESAÑA-HERMO M. TESTA-ANTA M, CARBÓ-ARGIBAY E, SALGUEIRIÑO V, PÉREZ-LORENZO M AND CORREA-DUARTE MA. 2017. Au-decorated sodium titanate nanotubes as high-performance selective photocatalysts for pollutant degradation. 2017. J Phys D 50: 144002.). In addition, PusztaiPUSZTAI P, PUSKÁS R and VARGA E. 2014. Influence of gold additives on the stability and phase transformation of titanate nanostructures. Phys Chem Chem Phys 16: 26786-26797. et al. reported that the band gaps of pure titanate nanowires (3.10 eV) and nanotubes (3.07 eV) reduce to 2,84 eV at 1% and 2,74 eV at 2,5% Au doping respectively (Pusztai et al. 2014).

MurdochMURDOCH M, WATERHOUSE GIN, NADEEM MA, METSON JB, KEANE MA, HOWE RF, LLORCA J and IDRISS H. 2011. The effect of gold loading and particle size on photocatalytic hydrogen production from ethanol over Au/TiO2 nanoparticles. Nat Chem 3: 489-492. et al. reported that AuNPs in the range of 3-30 nm on the surface of TiO2 are very active in the production of hydrogen from ethanol (Murdoch et al. 2011). Similar improvement in photocatalytic properties had been observed in the cases of ZnO crystals (WangWANG X, WANG W, MIAO Y, FENG G and ZHANG R. 2016. Facet-selective photodeposition of gold nanoparticles on faceted ZnO crystals for visible light photocatalysis. J Colloid Interface Sci 475: 112-118. et al. 2016), heterogeneous Au-BiVO nanostructures (Cao et al. 2011) and TiNts (DosadoDOSADO AG, CHEN WT, CHAN A, SUN-WATERHOUSE D and WATERHOUSE GIN. 2015. Novel Au/TiO2 photocatalysts for hydrogen production in alcohol–water mixtures based on hydrogen titanate nanotube precursors. J Catal 330: 238-254. et al. 2015) upon AuNPs decoration on the surface of these nanostructures. The surface plasmon resonance effect (SPR) allows direct electron transport directly from the metal to the conducting band of the semiconductor (Primo et al. 2011, Rouby et al. 2017) and improve the photocatalytic activity (Murdoch et al. 2011).

Well-dispersed AuNPs have been used to decorate TiNts in order to increase the efficiency of photocatalytic reactions in general and photocatalytic H2 production, in particular. The reasons for this synergetic effect observed are: the strong absorption ability of AuNPs, owing to the SPR effect that improves the visible light response, and the fast electron transfer from TiNts to AuNPs, which traps the photogenerated electrons and prevent their recombination with holes (Yang et al. 2015). Renhong Li et al. reported that redistribution of surface charge between AuNPs and protonated titanate nanotubes (HTiNts) leads to a high catalytic activity for photocatalytic hydrogen generation from the dehydrogenation of formic acid without any additive (Li et al. 2016LI R, ZHU X, YAN X, SHOU D, ZHOU X and CHEN W. 2016. Single component gold on protonated titanate nanotubes for surface-charge-mediated, additive-free dehydrogenation of formic acid into hydrogen. RSC Adv 6: 100103-100107.). In the attempt of developing more efficient catalysts for water splitting reactions the use of organic capping ligands for AuNPs synthesis lowers the catalyst effectiveness because a part of this organic reagent remains at the interface of the metal and the nanotubes, leading to a poor Schottky barrier between Au and TiNts (Li et al. 2012LI R, KOBAYASHI H, TONG J, YAN X, TANG Y, ZOU S, JIN J, YI W and FAN J. 2012. Radical-involved photosynthesis of AuCN oligomers from Au nanoparticles and acetonitrile. J Am Chem Soc 134: 18286-18294.). Therefore, it is of extreme necessity to develop direct nanoparticle decoration methods without organic moiety on to the hosting nanomaterial surface.

Herein we report an organic capping-agent free method of AuNPs decoration on to the surface of TiNTs after proton exchange to generate gold nanoparticle decorated protonated TiNts (AuHTiNts) which has been used as a photocatalyst for photogeneration of H2 using glycerol as a sacrificial agent. By AuNPs decoration, we have been able to overcome the problem of large band gap of TiNts, a central issue that restricts the optical response in only UV range and thereby lowers the photocatalytic performance of these semiconductors and had been able to extend the application of this material in the wider visible range.

EXPERIMENTAL PROCEDURES

TiO2-Anatase (≥ 99.8 %), HAuCl4·3H2O (99 %) and glycerol (≥ 99%) were purchased from Sigma-Aldrich and used without further purification. HCl (36.5-38 wt.%) and NaOH (98 %) were purchased from Dinâmica, ethylene glycol and ascorbic acid were purchased from Vetec, and also were used without further purification. All solutions were prepared using deionized water.

TITANATE NANOTUBES PREPARATION

Titanate nanotubes were prepared using commercial TiO2 (anatase) (purity 99.8%). Typically, 3.0 g of TiO2 were mixed in 90 mL of a 10 mol L-1 NaOH solution, stirred for 30 minutes in a magnetic stirrer to obtain a homogeneous dispersion, then transferred to a Teflon reactor and taken to a microwave oven (Panasonic - 2.45 MHz, maximum power of 700 W) and heated at 150 ° C for 4 h. After cooling the system to room temperature, a portion of the resulting white solid was washed with deionized water to pH 10 in order to generate Sodium titanate nanotubes (NaTiNts) and the other part with 0.1 mol L-1 aqueous HCl solution to pH 6 to generate proton exchanged titanate nanotubes (HTiNts). Both the samples were vacuum dried for 12 h (Ferreira et al. 2006FERREIRA OP, SOUZA FILHO AG, MENDES FILHO J and ALVES OL. 2006. Unveiling the structure and composition of titanium oxide nanotubes through ion exchange chemical reactions and thermal decomposition processes. J Braz Chem Soc 17: 393-402.).

SYNTHESIS OF AU NANOPARTICLES SUPPORTED ON TITANATE NANOTUBES

To generated AuHTiNts, HTiNts were added to an aqueous solution (60 mL) containing 1 wt% of ascorbic acid (AA) under vigorous stirring. Then, 150mL of a 1 % AuCl4-(aq) solution was added and this mixture was heated to 110 °C and kept on stirring for 2 h.

CHARACTERIZATIONS

Raman spectroscopy experiments were performed in a confocal Raman spectrometer, Bruker Senterra, with objective lenses of 50x and 785 nm laser excitation source. The low laser power density was used to prevent the sample from overheating. A spectral resolution of 3 cm-1 was used and the interval used was 80-1050 cm-1.

The powder X-ray diffraction (XRD) patterns were obtained with a Shimadzu XRD6000 diffractometer using Cu Kα radiation (λ = 1.5406 Å) operating at 30 mA and 40 kV. A sweep rate of 2 ° min-1 was used and the range of 2θ was 5-70 degrees.

The transmission electron microscopy (TEM) images were obtained using a JEOL -JEM-2010F microscope operating at 200 keV. The samples were prepared by dropping an aqueous suspension of powdered sample on to a holey carbon-coated copper grid (300 mesh, SPI supplies) and letting the water evaporate at ambient temperature, during 24 h. Catalyst compositional were acquired by XEDS spectrum imaging (XEDS-SI), Thermo-Noran XEDS.

The scanning electron micrographs (SEM) were collected using a field emission scanning electron microscope, FEI Quanta FEG250. The elemental analysis by X-ray energy dispersion spectroscopy (EDX) was performed using a EDX probe EDAX Apollo X, attached to FESEM. The powdered samples were adhered on to a carbon tape and placed on to the SEM sample holder.

The X-ray photoelectron spectra (XPS) were obtained with a Scienta Omicron ESCA+ spectrometer system equipped with an EA 125 hemispherical analyzer and an Xm 1000 monochromatic X-ray source (Al Kα, 1486.7 eV). The X-ray source was used with a power of 280 W as the spectrometer worked in a constant-pass energy mode of 50 eV. A Scienta Omicron CN10 charge neutralizer with a beam energy of 1.6 eV charge was used to compensate the charge effect while the spectra were obtained. For corrections of peak shifts due to the remaining charge effect, the binding energies of all spectra were scaled with use of the main peak of C 1s at 284.8 eV as a reference. Wide-scan spectra, for peak identification, were recorded with a step of 0.5 eV, and high-resolution spectra for core levels were obtained with the step of 0.03 eV. All the X-ray photoelectron spectra were analyzed with the software program CasaXPS, where the background in high-resolution spectra is computed by the Shirley method. Peak fitting of core levels was done with an asymmetric Gaussian-Lorentzian product function for the peak shape.

The UV-Vis diffuse reflectance spectra were obtained by a UV-Vis spectrophotometer (Agilent, Cary 300) equipped with an accessory for diffuse reflectance sampling using BaSO4 as reference material. 2 g of BaSO4 and 50 mg of titanate material were mixed well and pressed in the form of pellets.

CATALYSIS

Photo-assisted hydrogen generation experiments were carried out in a calibrated 35-mL gas-enclosed photochemical double quartz reactor in which water circulates as an infrared filter and controls the solution temperature (25° C) under continuous magnetic stirring. AuHTiNts (7,5 mg) were dispersed in 15 mL of H2O:Glycerol (5% wt% Glycerol) solution and introduced into the reactor. Prior to the irradiation, the system was de-aerated using Ar-vacuum cycles for about 10 min to reduce the oxygen content.

The system was illuminated by a 600 W solar simulator (Newport, Power solar) and a 450W Xe lamp (Ushio) at one sun intensity. The light intensity incident on the cell was measured with a calibrated Si photodiode. The evolution of H2 production was monitored by collecting 500 μL aliquots of the gas, in duplicates, at intervals of 0.5 h (Sample Lock Syring, Hamilton). The amount of accumulated H2 produced in the headspace of sealed quartz reactor was measured using an Agilent gas chromatography equipment with a TCD detector and HP-PLOT/Q 30 M, HPMOLESIEVE 30 M columns. For rate determination, data were taken at regular intervals from 30 min to 210 min.

Hydrogen evolution was observed under one sun condition as a function of time. The experiment was performed in a 5-cycle sequence without replacing the glycerol solution (Figure 8). In the first cycle, (named cycle-1 in the Fig 8) after 1h light exposure, irradiation was intentionally interrupted for a period of 1h. This procedure was repeated twice to observe in the sample behavior in the dark. In the other four, much longer cycles (named cycle-2, 3, 4 and 5 in the Fig 8), the sample was irradiated for 5 hours and the H2 evolution was measured constantly in each 30 minutes. After 5 hours, the irradiation was stopped and the reactor was left closed in a darkroom for 18 h. After each cycle, the system was fully evacuated, purged repeatedly and the irradiation was restarted for a new cycle.

RESULTS AND DISCUSSION

The Raman spectra of NaTiNts, HTiNts and AuHTiNts are illustrated in Fig. 1a. According to previous studies (Ferreira et al. 2006, MarquesMARQUES TM, FERREIRA O, COSTA JDA, FUJISAWA K, TERRONES M and CRUZ VIANA B. 2015. Study of the growth of CeO2 nanoparticles onto titanate nanotubes. J Phys Chem Solids 87: 213-220. et al. 2015), the vibrational modes centered at around 164 and 195 cm-1 are attributed to the lattice modes (Na+-O-Ti); modes centered at 275, 448 and 662 and 700 cm-1 correspond to Ti-O-Ti stretching from the edge-sharing TiO6 octahedron and the mode at 906 cm-1 represent the stretching of unshared Ti-O bonds in the units of distorted TiO6 of NaTiNts (VianaVIANA BC, FERREIRA OP, FILHO AGS, HIDALGO AA, FILHO JM and ALVES OL. 2011. Alkali metal intercalated titanate nanotubes: A vibrational spectroscopy study. Vib Spectrosc 55: 183-187. et al. 2011). In the HTiNts spectrum, it was observed that the highest (906 cm-1) and the lowest (145 and 195 cm-1) energy modes have their wave numbers and intensities widely affected by the proton ion. The most affected band is the one related to Ti-O bond whose oxygen is not shared among the TiO6 units, the mode around 906 cm-1, which disappears after the protonation reaction (Viana et al. 2011). Comparing the Raman spectra of AuTiNts with those of HTiNts, it was observed that they have the same Raman spectral characteristics of intermediary energy, indicating that the TiO6 octahedron network of TiNts did not suffer major changes after Au decoration. In addition, one of the important aspects to be highlighted is the emergence of new bands centered at 142, 393, 515 and 639 cm-1, which can be related to Eg, B1g, A1g and Eg modes of anatase phase respectively. This phase transformation from TiNT to anatase may be attributed to the similar topochemical reaction reported in the earlier literature where transitions of titanate nanostructures to TiO2 (anatase) nanoparticles had been observed in acidic aqueous dispersions at temperatures close to room temperature (Zhu et al. 2005ZHU HY, LAN Y, GAO XP, RINGER SP, ZHENG ZF, SONG DY and ZHAO JC. 2005. Phase transition between nanostructures of titanate and titanium dioxides via simple wet-chemical reactions. J Am Chem Soc 127: 6730-6736.).

Figure 1
(a) Raman spectra of NaTiNts, HTiNts and AuHTiNts, (b) XRD pattern of NaTiNts, HTiNts and AuHTiNts.

The X-ray diffraction patterns (XRD) provided information about the crystalline structure and the interlamellar distances of NaTiNts and HTiNts, as well can characterize the crystalline nature of decorated AuNPs. The X-ray diffraction data (Fig. 1b) indicate that the crystalline structure and tubular morphology of HTiNts (Dzubiella 2010DZUBIELLA J. 2010. Explicit and implicit modeling of nanobubbles in hydrophobic confinement. An Acad Bras Cienc 82: 3-12.) were preserved after being decorated with AuNPs. The slight changes in the diffractogram profiles of NaTiNts to HTiNts are in accordance with those reported in the literature (Ferreira et al. 2006). It highlights four typical broad diffraction peaks of NaTiNts: i) around 10° (2θ), referring to the interlamellar distance (MarquesMARQUES TMF, LUZ-LIMA C, SACILLOTI M, FUJISAWA K, PEREA-LOPEZ N, TERRONES M, SILVA EM, FERREIRA OP and VIANA BC. 2017. Photoluminescence Enhancement of Titanate Nanotubes by Insertion of Rare Earth Ions in Their Interlayer Spaces. J Nanomater 2017: 1-9. et al. 2017); ii) 24° (2θ), referring to the diagonal plans formed by ion-lamella (MorgadoMORGADO E, MARINKOVIC BA, JARDIM PM, ABREU MAS, ROCHA MGC and BARGIELA P. 2011. Studies on Fe-modified nanostructured trititanates. Mater Chem Phys 126: 118-127. et al. 2011); (iii) 28° (2θ), referring to the diagonal plans formed by lamellar sodium-interaction (Morgado et al. 2006MORGADO E, ABREU MAS, PRAVIA ORC, MARINKOVIC BA, JARDIM PM, RIZZO FC and ARAÚJO AS. 2006. A study on the structure and thermal stability of titanate nanotubes as a function of sodium content. Solid State Sci 8: 888-900.); and (iv) 48° (2θ), referring to the plans formed by the TiO6 network (Bavykin et al. 2006, Chen et al. 2002). These peaks are consistent with the crystallographic information file reported for the phase Na2Ti3O7·nH2O (JCPDS #. 13-3129), indexed to the planes (200), (110), (211) and (020), respectively (Ferreira et al. 2006). In the diffractogram profile of HTiNts, it was observed that the intensity of the peak centered at 2θ = 28 ° decreases compared to the peak located in the same region of the NaTiNts sample, suggesting the exchange of Na+ ions with H+ ions (Morgado et al. 2006), corroborating with the Raman results. The reduction and AuNPs decoration processes on the surface of HTiNts affected the intensity of some crystalline planes of nanotubes, but the overall tubular structure was preserved for the AuHTiNts. The XRD peak at around 10°, corresponding to the plane (200), related to the interlamellar distance, as well the diagonals planes of the nanotubes structure, represented by the peaks between 20° and 40°, exhibited changes in the intensity reflecting the insertion of H+ and Au+ ions from the Au+ exchange reaction in an acid medium, leading to AuNPs decoration. The insertion of Au+ with the removal of H+ and Na+, remaining after the protonation process, resulted in the distortion of these crystalline planes, reducing the intensity of the peaks at 10° and 28° (2θ) along with a peak dislocation at 10° (2θ) to lower values, thereby suggesting the increase of the interlamellar distance through the insertion of Au+ ions between the lamellas of the nanotubes (Viana et al. 2011).

The AuNPs formation was confirmed by indexing the peaks at 38° and 44° with the crystallographic data from the Card JCPDS nº 65-2870, pertinent to the Bragg (111) and (200) reflection pattern for a cubic face-centered phase (CFC) of Au. The average size of the AuNPs was estimated applying the Scherrer equation on full-width at the half maxima of the most of intense reflection (111), which was calculated to be around 9.9 nm of size. Also a diffraction peak at 25° was observed which was indexed as (101) plane reflection of the TiO2 anatase phase (JCPDS Card. nº 21-1272), confirming, the presence of some anatase phase, suggesting occurrence of some TiNT-anatase phase transformation due to the topochemical reaction in the acidic medium, also observed by Zhu et al (2005), corroborating with the findings of Raman spectroscopy.

The TEM images for HTiNts and AuHTiNts were obtained with the purpose to confirm the nanomorphology and to measure the average value of the outer (<dext>) and inner diameter (<dint>) of the nanotubes, as well as the interplanar distance and diameter of AuNPs (Fig. 2). The TEM images of HTiNts confirms the retention of tubular morphology with an open-ended, rolled-up structure (Fig. 2a, b), very characteristic of the titanate nanotubes in general with a non-homogeneous distribution of the length and width (Tang et al. 2013TANG ZR, YIN X, ZHANG Y and XU YJ. 2013. Synthesis of titanate nanotube–CdS nanocomposites with enhanced visible light photocatalytic activity. Inorg Chem 52: 11758-11766., VempatiVEMPATI S, KAYACI-SENIRMAK F, OZGIT-AKGUN C, BIYIKLI N and UYAR T. 2015. Surface ionic states and structure of titanate nanotubes. RSC Adv 5: 82977-82982. et al. 2015). The inner and outer diameter of nanotubes were measured from the images (Fig. 2c, d) and the average for the external diameter distribution (<dext>) and that for the inner diameter distribution (<dint>) were found to be 8.42 ± 0.03 nm and 5.46 ± 0.08 nm, respectively. The interplanar distance was measured for HTiNts to be 0.69 nm. Both the average inner and outer diameters as well as the interplanar distance are in good agreement with those reported in the literature (Ferreira et al. 2006).

Figure 2
TEM images of HTiNts (a, b) and distribution of the external (c) and internal (d) diameter for HTiNts.

The AuNPs formation and interaction on the HTiNts surface resulted in the anchoring of the gold nanoparticles on to the surface of the nanotubes (Fig. 3a, b and d). The distribution of the AuNPs average size (<dAu>) was determined from the TEM images (Fig. 3a) and found to be 9.68 ± 0.03 nm (Fig. 2c), agreeing with the value obtained by XRD measurements, as shown above. The AuNPs morphology and size obtained in the present study are in good agreement with the results presented in the literature (Li et al. 2016). AuHTiNts were subjected to X-ray energy dispersive spectroscopy by TEM (EDS-TEM). The measurement was performed at the indicated region (indicated as “1” in Fig. 3d) between two AuNPs particles (Fig. 3d) to confirm the elemental composition to be pure Au (Fig. 3e), the signal of Cu coming from the TEM grid.

Figure 3
TEM images of AuHTiNts (a, b and d) and distribution of diameter of AuNPs (c) and X-ray spectroscopy of energy dispersion (e).

The elemental composition of NaTiNts, HTiNts and AuHTiNts samples was investigated by EDS. The atomic ratio of Na/Ti was found to be 0.71 and 0.05 for NaTiNts and HTiNts, respectively. The amount of Na+ ions in NaTiNts is in accordance with the chemical formula Na2-xHxTi3O7·nH2O (0 ≤ x ≤ 2 ) (Ferreira et al. 2006, Marques et al. 2017). After washing with HCl, the sodium content decreased drastically (about 90%) in the HTiNts (Morgado et al. 2006), suggesting that ion exchange by H+ to Na+ has occurred successfully. Also the presence of Au has been verified in the AuHTiNts sample, a more detailed study of the chemical environment was performed by X-ray photoelectron spectroscopy (XPS), Fig. 4.

Figure 4
High resolution XPS spectra of (a) Ti 2p, (b) O 1s signals for NaTiNts, HTiNts and AuHTiNts and (c) Au 4f signals for the AuHTiNts samples.

The electronic structure and the surface composition of titanate nanotubes (NaTiNts, HTiNts and AuHTiNts) were studied by XPS. The maximum energy for C 1s (284.8 eV) was used as a reference of binding energy. The detailed spectra of all the TiNT nanotubes are shown in Fig. 4. The Ti 2p signals for NaTiNts, HTiNts and AuHTiNts were shown in Fig. 4a. The spectral doublet line of Ti 2p for the NaTiNts was characterized by binding energy of 457.8 eV (2p3/2) with FWHM of 2.05 eV and 464.3 eV (2p1/2) with FWHM of 2.60 eV with a separation energy of 5.7 eV. The spectral lines of Ti 2p3/2 and Ti 2p1/2 are very similar to the reported values (Kim et al. 2007KIM GS, ANSARI SG, SEO HK, KIM YS and SHIN HS. 2007. Effect of annealing temperature on structural and bonded states of titanate nanotube films. J Appl Phys 101: 24314., Pótári et al. 2013PÓTÁRI G, MADARÁSZ D, NAGY L, LÁSZLÓ B, SÁPI A, OSZKÓ A, KUKOVECZ A, ERDOHELYI A, KÓNYA Z and KISS J. 2013. Rh-induced support transformation phenomena in titanate nanowire and nanotube catalysts. Langmuir 29: 3061-3072.). Ti 2p double-stranded spectral lines for the HTiNts and AuTiNts present similar results, showing the presence of Ti4 + (Deng et al. 2009, Kiss et al. 2014KISS J, PUSZTAI P, ÓVÁRI L, BAÁN K, MERZA G, ERDÖHELYI A, KUKOVECZ A and KÓNYA Z. 2014. Decoration of titanate nanowires and nanotubes by gold nanoparticles: XPS, HRTEM and XRD characterization. e-JSSNT 12: 252-258.). The O 1s spectra for all the TiNts were shown in Fig. 4b. The O 1s spectra of NaTiNts can be deconvoluted in sub-peaks centered at 531.6, 530.3 and 529.1 eV, which can be assigned to the H2O, -OH and Ti-O, respectively (Fig. 5). Similar results were reported by Kim et al. where they discovered that the O 1s peak is formed of Ti-O in TiO2 and OH in Ti-OH (Kim et al. 2007).

Figure 5
High resolution XPS spectra of O 1s signals (a) of NaTiNts (b) HiTiNts and (c) AuHTiNts samples.

The gold chemical environment in AuHTiNts was also investigated by XPS. The Au 4f spectra of AuHTiNts are displayed in Fig. 4c. The metallic 4f7/2 and 4f5/2 Au lines were observed at 84.1 and 87.8 eV, respectively, showing characteristic shoulders at higher energies due to the presence of Au+ (Fig. 4c) (KissKISS J, ÓVÁRI L, OSZKÓ A, PÓTÁRI G, TÓTH M, BAÁN K and ERDÓHELYI A. 2012 Structure and reactivity of Au–Rh bimetallic clusters on titanate nanowires, nanotubes and TiO2 (1 1 0). Catal Today 181: 163-170. et al. 2012, Pusztai et al. 2014). The emergence of shoulder peaks at 4f7/2 (85.4 eV) and 4f5/2 (89.4 eV) indicates that Au deposition may have undergone through an ionic exchange process. The surface composition for all the samples was investigated by XPS (Table I), and in the case of AuHTiNts, the ratio of Au0/Au+ was found to be 1.96, which indicates that approximately 66.22% of Au is in the reduced form (Au0), decorating the external surfaces of the nanotubes external surface as AuNPs. The mixed oxidation state of Au found in this study appeared to be similar to the one that found in the literature (Kiss et al. 2014). This phenomenon can be explained as Au is partially stabilized on the titanate nanotubes in the form of Au+ by ionic exchange as well as in the form of the clusters of Au0. It is likely to occur in titanate nanotubes because they are well known as good ion exchanger (Kiss et al. 2012). The higher energy (85.5 eV) band of Au+ indicates that Au3+ was reduced to Au+ which participates widely in ion exchange reaction with titanate nanotubes as Au+ represents a greater binding energy in the XPS in comparison with the state of the metallic gold (Tsai et al. 2009TSAI JY, CHAO JH and LIN CH. 2009. Low temperature carbon monoxide oxidation over gold nanoparticles supported on sodium titanate nanotubes. J Mol Catal Chem 298: 115-124.).

TABLE I
Surface composition of AuHTiNts and the percentage concentration of Au species.

The UV-Vis diffuse reflectance spectroscopy were performed on HTiNts and AuHTiNts to obtain the optical spectra (Fig. 6) as well as the band gap values (Egap) by extrapolating the straight section of the paraboloid curve obtained from the [F(R∞)hν]2 versus Ephot plot. The HTiNts showed Egap equal to 3.30 eV, agreeing with the values reported by Ferreira et al. 2013 (Ferreira et al. 2013FERREIRA VC, NUNES MR, SILVESTRE AJ and MONTEIRO OC. 2013. Synthesis and properties of Co-doped titanate nanotubes and their optical sensitization with methylene blue. Mater Chem Phys 142: 355-362.). However, when TiNts were decorated with AuNPs there was a slight decrease of Egap to 3.28 eV, corroborating the results reported by PusztaiPUSZTAI P, PUSKÁS R and VARGA E. 2014. Influence of gold additives on the stability and phase transformation of titanate nanostructures. Phys Chem Chem Phys 16: 26786-26797. et al. (2014). The effect is related with the insertion of intermediate levels among the orbitals of the Valence band (O 2p) to the conduction band (Ti 3d) originated from AuNPs, thus facilitating the charge transport in the internal structures of the materials (Rouby et al. 2017). Studies carried out conclude that other metallic nanoparticles and sulfide, such as silver (Rodríguez-González et al. 2012RODRÍGUEZ-GONZÁLEZ V, OBREGÓN-ALFARO S, LOZANO-SÁNCHEZ LM and LEE SW. 2012. Rapid microwave-assisted synthesis of one-dimensional silver–H2Ti3O7 nanotubes. J Mol Catal Chem 353: 163-170.) cadmium sulfide (Tang et al. 2013), cobalt (Ferreira et al. 2013) and zinc (Vempati et al. 2015) show similar effect when NaTiNts and HTiNts surface after decoration with those nanoparticles.

Figure 6
Kubelka-Munk curves versus Photon energy (Ephot = hν) of the (a) HTiNts and (b) AuHTiNts.

Fig. 7 presents the irradiation results of glycerol as a sacrificial agent (glycerol/water solution 5% v/v) on HTiNts and AuHTiNts samples. The photogeneration of H2 in the presence of AuHTiNts was strongly increased in comparison to HTiNts. The values obtained of H2 production was 853 µmol g-1 in 210 min, a value considerably higher than the value showed using HTiNts, which was 121 μmol g-1.

Figure 7
Production of H2 from glycerol versus time of visible light exposure to 1.0% by weight of HTiNts (blue dots) and AuHTiNts (red dots).

The Nanoparticles of Au <30 nm, as observed in this work (Fig. 3), act as photon absorbers in the visible region of the spectrum as a consequence of the SPR effect (Fig.6). This phenomenon allows AuNPs to act as sensitizing agents, injecting hot electron into the titanate conduction band. On the other hand, the AuNPs also behave as local quantum dots concentrators of light, responsible for increasing the generation of electron-hole pairs that are induced by SPR onto semiconductor/liquid interface (Xinhua et al. 2017XINHUA DU, YANG LI, HUI YIN and QUANJUN X. 2017. Preparation of Au/TiO 2/MoS 2 Plasmonic Composite Photocatalysts with Enhanced Photocatalytic Hydrogen Generation Activity. Acta Phy-Chim Sin 34: 414-423.). The combination of these processes decreased the recombination of the excitons resulting in 600% increase of H2 production observed for AuHTiNts in compared to HTiNts.

The stability test of the AuHTiNts samples has been presented in Fig. 8. The experiment carried out in cycle 1 shows that the generation of H2 is not ceased immediately after the absence of light as observed by Jiang et al. (2008)JIANG J, GAO Q and CHEN Z. 2008. Gold nanocatalysts supported on protonic titanate nanotubes and titania nanocrystals. J Mol Catal Chem 280: 233-239.. Such phenomenon is observed due the adsorption of the photogenerated H2 onto outer or inner surface of the interlayers in nanotubes, which is released later, during the absence of light. However, in the presence of light the cycle 1 presented a significantly lower rate than that observed in the cycles 2, 3 and 4 (Table II). In the subsequent cycles 2, 3 and 4 the hydrogen generation rate stays steady, which show the excellent stability of the AuHTiNts since this material does not undergo process of photo-oxidation of the metal phase.

Figure 8
H2 evolution by the catalyst AuHTiNts during five successive cycles.
TABLE II
H2 evolution for AuHTiNts samples during multiple cycles.

In Table II the amount of H2 produced during the longer cycles as well as the rate of production are shown. For example, for cycle-2, 966.54 mol H2 was produced during 5 hours of irradiation with a production rate of 193.17 μmol/g/h. After the irradiation was stopped and the reactor was maintained closed in a dark chamber for 18 hours, it was found that more 161.09 μmol of H2 was produced in dark during this 18 hours, which makes the overall rate (5 hours of irradiation + 18 hours of darkness) changes to of 8.95 μmol/g/h H2 evolution.

It is worth mentioning that the rate of H2 generation during the cycles suggests that the process of glycerol photo-reform occurs slowly compared to the reduction reaction H+H2. This behavior is attributed to the absence of energetic holes, which are evidenced only in nanoparticles of Au ~ 2 nm, unlike the hot electrons that are reported in SPR nanoparticles <30nm (Murdoch et al. 2011).

wAs expected, the deposition of AuNPs on to the nanotubes surface can facilitate the electrons capture, responsible for the reduction reaction giving rise to molecules of H2 (Fujishima et al. 2008FUJISHIMA A, ZHANG X and TRYK DA. 2008. TiO2 photocatalysis and related surface phenomena. Surf Sci Rep 63: 515-582., Murdoch et al. 2011). The presence of Au particles promoted the emergence of absorption band in the visible range, with λmax= 525 nm, due to the SPR effect (Fig. 9), and the AuNPs can generate the charge dissipation in the nanotubes band conduction, improving the charge transfer (PanayotovPANAYOTOV DA, FRENKEL AI and MORRIS JR. 2017. Catalysis and photocatalysis by nanoscale Au/TiO2: Perspectives for renewable energy. ACS Energy Lett 2: 1223-1231. et al. 2017).

Figure 9
Reflectance spectra for HTiNts (blue line) and AuHTiNts (red line). The broad band between 470 and 590 nm in AuHTiNts is associated with the Au structure supported on nanotubes.

CONCLUSIONS

AuHTiNts has been applied as photocatalysts to obtain hydrogen production at elevated rate using glycerol as a sacrificial agent. The photocatalysts were characterized by Raman spectroscopy, presenting typical vibrational modes of titanate nanotubes, which did not undergo major changes after AuNPs decoration. Furthermore, presence of anatase phase was confirmed. From XRD, it was observed that the crystalline structures and morphology of the titanate nanotubes were intact after the AuNPs formation. The TEM images exhibited homogeneous nanoparticles distribution on the surface nanotubes with an average size of 9.6 nm. It was found by XPS that gold is stabilized in/on titanate nanotubes partially in the form of Au+ by ionic exchange and also as clusters of Au0 on the nanotubes surface. This elevated production of hydrogen, using the heterogeneous AuHTiNts catalysts, can be attributed to the intrinsic catalytic potential of gold and its interactions with titanate nanotubes.

ACKNOWLEGMENTS

The authors acknowledge financial support from FAPEPI, FACEPE, Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) and Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq), the technical support of Center for Strategic Technology of the Northeast (CETENE-PE) and Federal Institute of Education, Science and Technology of Piauí (IFPI), São João do Piauí – PI. The authors declare that there is no conflict of interest regarding the publication of this paper.

REFERENCES

  • ABDULLAH M and KAMARUDIN SK. 2017. Titanium dioxide nanotubes (TNT) in energy and environmental applications: An overview. Renew Sust Energ Rev 76: 212-225.
  • AHMAD H, KAMARUDIN SK, MINGGU LJ and KASSIM M. 2015. Hydrogen from photo-catalytic water splitting process: A review. Renew Sust Energ Rev 43: 599-610.
  • BAMWENDA GR, TSUBOTA S, NAKAMURA T and HARUTA M. 1995. Photoassisted hydrogen production from a water-ethanol solution: a comparison of activities of AuTiO2 and PtTiO2. J Photochem Photobiol A: Chem 89: 177-189.
  • BAVYKIN DV, FRIEDRICH JM and WALSH FC.2006. Protonated titanates and TiO2 nanostructured materials: synthesis, properties, and applications. Adv Mater 18: 2807-2824.
  • BOWKER M, DAVIES PR and AL-MAZROAI LS. 2009. Photocatalytic reforming of glycerol over gold and palladium as an alternative fuel source. Catal Letters 128: 253-253.
  • CAO SW, YIN Z, BARBER J, BOEY FYC, LOO SCJ and XUE C. 2011. Preparation of Au-BiVO4 heterogeneous nanostructures as highly efficient visible-light photocatalysts. ACS Appl Mater Interfaces 4: 418-423.
  • CHEN Q, DU GH, ZHANG S and PENG LM. 2002. The structure of trititanate nanotubes. Acta Crystallogr B 58: 587-593.
  • CRABTREE GW, DRESSELHAUS MS and BUCHANAN MV. 2004. The hydrogen economy. Phys Today 57: 39-44.
  • CUSHING SK, LI J, BRIGHT J, YOST BT, ZHENG P, BRISTOW AD and WU N. 2015. Controlling Plasmon-Induced Resonance Energy Transfer and Hot Electron Injection Processes in Metal@TiO2 Core–Shell Nanoparticles. J Phys Chem C 119: 16239-16244.
  • DASKALAKI VM and KONDARIDES DI. 2009. Efficient production of hydrogen by photo-induced reforming of glycerol at ambient conditions. Catal Today 144(1-2): 75-80.
  • DENG L, WANG S, LIU D, ZHU B, HUANG W, WU S and ZHANG S. 2009. Synthesis, Characterization of Fe-doped TiO2 Nanotubes with High Photocatalytic Activity. Catal Lett 129: 513-518.
  • DE LA PISCINA PR and HOMS N. 2008. Use of biofuels to produce hydrogen (reformation processes). Chem Soc Rev 37: 2459-2467.
  • DOSADO AG, CHEN WT, CHAN A, SUN-WATERHOUSE D and WATERHOUSE GIN. 2015. Novel Au/TiO2 photocatalysts for hydrogen production in alcohol–water mixtures based on hydrogen titanate nanotube precursors. J Catal 330: 238-254.
  • DZUBIELLA J. 2010. Explicit and implicit modeling of nanobubbles in hydrophobic confinement. An Acad Bras Cienc 82: 3-12.
  • ESTAHBANATI MRK, FEILIZADEH M and ILIUTA MC. 2017. Photocatalytic valorization of glycerol to hydrogen: Optimization of operating parameters by artificial neural network. Appl Catal B 209: 483-492.
  • ETACHERI V, VALENTIN CD, SCHNEIDER J, BAHNEMANN D and PILLAI SC. 2015. Visible-light activation of TiO2 photocatalysts: Advances in theory and experiments. J Photochem Photobiol C 25: 1-29.
  • FANG W, XING M and ZHANG J. 2017. Modifications on reduced titanium dioxide photocatalysts: A review. J Photochem Photobiol 32: 21-39.
  • FERREIRA OP, SOUZA FILHO AG, MENDES FILHO J and ALVES OL. 2006. Unveiling the structure and composition of titanium oxide nanotubes through ion exchange chemical reactions and thermal decomposition processes. J Braz Chem Soc 17: 393-402.
  • FERREIRA VC, NUNES MR, SILVESTRE AJ and MONTEIRO OC. 2013. Synthesis and properties of Co-doped titanate nanotubes and their optical sensitization with methylene blue. Mater Chem Phys 142: 355-362.
  • FUJISHIMA A and HONDA K. 1972. Electrochemical photolysis of water at a semiconductor electrode. Nature 238: 37-38.
  • FUJISHIMA A, ZHANG X and TRYK DA. 2008. TiO2 photocatalysis and related surface phenomena. Surf Sci Rep 63: 515-582.
  • FUJITA SI, KAWAMORI H, HONDA D, YOSHIDA H and ARAI M. 2016. Photocatalytic hydrogen production from aqueous glycerol solution using NiO/TiO2 catalysts: Effects of preparation and reaction conditions. Appl Catal B Environ 181: 818-824.
  • GE MZ, CAO CY, HUANG JY, LI SH, ZHANG SN, DENG S, QING-SONG, ZHANG KQ and LAI YK. 2016. Synthesis, modification, and photo/photoelectro- catalytic degradation applications of TiO2 nanotube arrays: a review. Nanotechnology 5: 1-38.
  • GE M, LI Q, CAO C, HUANG J, LI S, ZHANG S, CHEN Z, ZHANG K, AL-DEYAB SS and LAI Y. 2017. One-dimensional TiO 2 Nanotube Photocatalysts for Solar Water Splitting. Adv Sci 4: 1600152.
  • GUIMARÃES ZAS, DAMATTA RA, GUIMARÃES RS and FILGUEIRA M. 2017. A Novel Porous Diamond - Titanium Biomaterial: Structure, Microstructure, Physico-Mechanical Properties and Biocompatibility. An Acad Bras Cienc 89: 3111-3121.
  • INGRAM DB, CHRISTOPHER P, BAUER JL and LINIC S. 2011. Predictive Model for the Design of Plasmonic Metal/Semiconductor Composite Photocatalysts. ACS Catal 1: 1441-1447.
  • JAKOB M, LEVANON H and KAMAT PV. 2003. Charge Distribution between UV-Irradiated TiO2 and Gold Nanoparticles: Determination of Shift in the Fermi Level. Nano Lett 3: 353-358.
  • JEDSUKONTORN T, UENO T, SAITO N and HUNSOM M. 2018. Mechanistic aspect based on the role of reactive oxidizing species (ROS) in macroscopic level on the glycerol photooxidation over defected and defected-free TiO2. J. Photochem Photobiol A: Chemistry 367: 270-281.
  • JIANG J, GAO Q and CHEN Z. 2008. Gold nanocatalysts supported on protonic titanate nanotubes and titania nanocrystals. J Mol Catal Chem 280: 233-239.
  • JOHN MR ST, FURGALA AJ and SAMMELLS AF. 1983. Hydrogen generation by photocatalytic oxidation of glucose by platinized n-titania powder. J Phys Chem A 87: 801-805.
  • KIM GS, ANSARI SG, SEO HK, KIM YS and SHIN HS. 2007. Effect of annealing temperature on structural and bonded states of titanate nanotube films. J Appl Phys 101: 24314.
  • KISS J, ÓVÁRI L, OSZKÓ A, PÓTÁRI G, TÓTH M, BAÁN K and ERDÓHELYI A. 2012 Structure and reactivity of Au–Rh bimetallic clusters on titanate nanowires, nanotubes and TiO2 (1 1 0). Catal Today 181: 163-170.
  • KISS J, PUSZTAI P, ÓVÁRI L, BAÁN K, MERZA G, ERDÖHELYI A, KUKOVECZ A and KÓNYA Z. 2014. Decoration of titanate nanowires and nanotubes by gold nanoparticles: XPS, HRTEM and XRD characterization. e-JSSNT 12: 252-258.
  • KUKOVECZ Á, KORDÁS K, KISS J and KÓNYA Z. 2016. Atomic scale characterization and surface chemistry of metal modified titanate nanotubes and nanowires. Surf Sci Rep 71: 473-546.
  • LI R, KOBAYASHI H, TONG J, YAN X, TANG Y, ZOU S, JIN J, YI W and FAN J. 2012. Radical-involved photosynthesis of AuCN oligomers from Au nanoparticles and acetonitrile. J Am Chem Soc 134: 18286-18294.
  • LI R, ZHU X, YAN X, SHOU D, ZHOU X and CHEN W. 2016. Single component gold on protonated titanate nanotubes for surface-charge-mediated, additive-free dehydrogenation of formic acid into hydrogen. RSC Adv 6: 100103-100107.
  • LIU N, CHEN X, ZHANG J and SCHWANK JW. 2014. A review on TiO2-based nanotubes synthesized via hydrothermal method: Formation mechanism, structure modification, and photocatalytic applications. Catal Today 225: 34-51.
  • MARQUES TMF, LUZ-LIMA C, SACILLOTI M, FUJISAWA K, PEREA-LOPEZ N, TERRONES M, SILVA EM, FERREIRA OP and VIANA BC. 2017. Photoluminescence Enhancement of Titanate Nanotubes by Insertion of Rare Earth Ions in Their Interlayer Spaces. J Nanomater 2017: 1-9.
  • MARQUES TM, FERREIRA O, COSTA JDA, FUJISAWA K, TERRONES M and CRUZ VIANA B. 2015. Study of the growth of CeO2 nanoparticles onto titanate nanotubes. J Phys Chem Solids 87: 213-220.
  • MCNUTT J and YANG J. 2017. Utilization of the residual glycerol from biodiesel production for renewable energy generation. Renew Sust Energ Rev 71: 63-76.
  • MORGADO E, ABREU MAS, PRAVIA ORC, MARINKOVIC BA, JARDIM PM, RIZZO FC and ARAÚJO AS. 2006. A study on the structure and thermal stability of titanate nanotubes as a function of sodium content. Solid State Sci 8: 888-900.
  • MORGADO E, MARINKOVIC BA, JARDIM PM, ABREU MAS, ROCHA MGC and BARGIELA P. 2011. Studies on Fe-modified nanostructured trititanates. Mater Chem Phys 126: 118-127.
  • MURDOCH M, WATERHOUSE GIN, NADEEM MA, METSON JB, KEANE MA, HOWE RF, LLORCA J and IDRISS H. 2011. The effect of gold loading and particle size on photocatalytic hydrogen production from ethanol over Au/TiO2 nanoparticles. Nat Chem 3: 489-492.
  • PANAYOTOV DA, FRENKEL AI and MORRIS JR. 2017. Catalysis and photocatalysis by nanoscale Au/TiO2: Perspectives for renewable energy. ACS Energy Lett 2: 1223-1231.
  • PÓTÁRI G, MADARÁSZ D, NAGY L, LÁSZLÓ B, SÁPI A, OSZKÓ A, KUKOVECZ A, ERDOHELYI A, KÓNYA Z and KISS J. 2013. Rh-induced support transformation phenomena in titanate nanowire and nanotube catalysts. Langmuir 29: 3061-3072.
  • PRIMO A, CORMA A and GARCÍA H. 2011. Titania supported gold nanoparticles as photocatalyst. Phys Chem Chem Phys 13: 886-910.
  • PUSZTAI P, PUSKÁS R and VARGA E. 2014. Influence of gold additives on the stability and phase transformation of titanate nanostructures. Phys Chem Chem Phys 16: 26786-26797.
  • RODRÍGUEZ-GONZÁLEZ V, OBREGÓN-ALFARO S, LOZANO-SÁNCHEZ LM and LEE SW. 2012. Rapid microwave-assisted synthesis of one-dimensional silver–H2Ti3O7 nanotubes. J Mol Catal Chem 353: 163-170.
  • ROUBY WMA, COMESAÑA-HERMO M. TESTA-ANTA M, CARBÓ-ARGIBAY E, SALGUEIRIÑO V, PÉREZ-LORENZO M AND CORREA-DUARTE MA. 2017. Au-decorated sodium titanate nanotubes as high-performance selective photocatalysts for pollutant degradation. 2017. J Phys D 50: 144002.
  • SAKTHIVEL S, SHANKAR MV, PALANICHAMY M, ARABINDOO B, BAHNEMANN DW and MURUGESAN V. 2004. Enhancement of photocatalytic activity by metal deposition: characterisation and photonic efficiency of Pt, Au and Pd deposited on TiO2 catalyst. Water Res 38: 3001-3008.
  • SANWALD KE, BERTO TF, EISENREICH W, GUTIÉRREZ OY and LERCHER JA. 2016. Catalytic routes and oxidation mechanisms in photoreforming of polyols. J Catal 344: 806-816.
  • TANG ZR, YIN X, ZHANG Y and XU YJ. 2013. Synthesis of titanate nanotube–CdS nanocomposites with enhanced visible light photocatalytic activity. Inorg Chem 52: 11758-11766.
  • TSAI JY, CHAO JH and LIN CH. 2009. Low temperature carbon monoxide oxidation over gold nanoparticles supported on sodium titanate nanotubes. J Mol Catal Chem 298: 115-124.
  • VALDÉS Á et al. 2012. Solar hydrogen production with semiconductor metal oxides: new directions in experiment and theory. Phys Chem Chem Phys 14: 49-70.
  • VEMPATI S, KAYACI-SENIRMAK F, OZGIT-AKGUN C, BIYIKLI N and UYAR T. 2015. Surface ionic states and structure of titanate nanotubes. RSC Adv 5: 82977-82982.
  • VIANA BC, FERREIRA OP, FILHO AGS, HIDALGO AA, FILHO JM and ALVES OL. 2011. Alkali metal intercalated titanate nanotubes: A vibrational spectroscopy study. Vib Spectrosc 55: 183-187.
  • WANG X, WANG W, MIAO Y, FENG G and ZHANG R. 2016. Facet-selective photodeposition of gold nanoparticles on faceted ZnO crystals for visible light photocatalysis. J Colloid Interface Sci 475: 112-118.
  • XINHUA DU, YANG LI, HUI YIN and QUANJUN X. 2017. Preparation of Au/TiO 2/MoS 2 Plasmonic Composite Photocatalysts with Enhanced Photocatalytic Hydrogen Generation Activity. Acta Phy-Chim Sin 34: 414-423.
  • YANG X, WU L, DU L and LI X. 2015. Photocatalytic Water Splitting Towards Hydrogen Production on Gold Nanoparticles (NPs) Entrapped in TiO2 Nanotubes. Catal Lett 145: 1771-1777.
  • ZHU HY, LAN Y, GAO XP, RINGER SP, ZHENG ZF, SONG DY and ZHAO JC. 2005. Phase transition between nanostructures of titanate and titanium dioxides via simple wet-chemical reactions. J Am Chem Soc 127: 6730-6736.

Publication Dates

  • Publication in this collection
    28 Nov 2019
  • Date of issue
    2019

History

  • Received
    24 Jan 2019
  • Accepted
    11 Apr 2019
Academia Brasileira de Ciências Rua Anfilófio de Carvalho, 29, 3º andar, 20030-060 Rio de Janeiro RJ Brasil, Tel: +55 21 3907-8100 - Rio de Janeiro - RJ - Brazil
E-mail: aabc@abc.org.br