ANALYSIS OF A COMMERCIAL PORTABLE LITHIUM-ION BATTERY UNDER LOW CURRENT CHARGE-DISCHARGE CYCLES

Abstract

The dependence between the transferred charge and the corresponding transference time to charge and discharge a portable cell phone Li-ion battery (LiCoO2/C) under cycles of low intensity currents was studied in detail. The voltage curve profile between 3.0 and 4.2 V and the charging and discharging time are strongly influenced by the applied current intensity. A linear dependence between the stored and extracted charges, into and from the battery, with the intensity of applied current was also observed. Allometric equations were found to describe the correlation between the charge transference time and the applied current intensity to charge and discharge the battery.

Keywords:
lithium-ion battery; charging and discharging; CC protocol, low currents


INTRODUCTION

Batteries of Li-ions (BILs) operate over reversible electrochemical oxidation and reduction reactions between a LixMO2 cathode (M: Co, Ni, Mn and its compounds) and a carbon (graphite) based anode, with Li salts dissolved in organic compound solution as the electrolyte. Under conditions of electrolyte chemical stability and redox reaction reversibility, the batteries of LixCoO2 cathodes operate between the voltages of 3.7 to 4.2 V, with the Li concentration in the 0.5 < x < 1.0 range.11 Zhang, S. S.; Xu, K.; Jow, T. R.; J. Power Sources 2006, 160, 1403. The spontaneous reaction (in discharge) occurs by the electrochemical insertion of Li+ cations into the LixCoO2 compound (under Co reduction) in conjunction with the oxidation of the C anode (with the output of Li+ ions from the C material to the electrolyte), lowering the battery voltage. When x ≅ 1.0 the battery is fully discharged and external electric power should be provided to cathode oxidation and anode reduction reactions. When x = 0.5 the battery is fully charged and its voltage is 4.2 V.22 Reimers, J. N.; Dahn, J. R.; J. Electrochem. Soc. 1992, 139, 2091. Due to the redox reaction simplicity, the BIL's are very stable devices when properly operated between its voltage and current limits. However, its charge capacity decreases progressively with the number of charge-discharge cycles.

Different protocols have been proposed to charge the BILs, including: application of a constant current followed by a constant voltage (CC+CV protocol),33 Zhang, S. S.; Xu, K.; Jow, T. R.; J. Power Sources 2006, 160, 1349. current pulses,44 Li, J.; Murphy, E.; Winnick, J.; Kohl, P.; J. Power Sources 2001, 102, 302. continuously decreasing or multi-stage currents,55 Sikha, G.; Ramadass, P.; Haran, B. S.; White, R. E.; Popov, B. N.; J. Power Sources 2003, 122, 67.,66 Liu, Y.-H.; Teng, J.-H.; Lin, Y.-C.; IEEE Trans. Ind. Electron. Control Instrum. 2005, 52, 1328. constant current (CC),77 Zhang, S. S.; J. Power Sources 2006, 161, 1385. and other strategies and algorithms that seek to maximize the storage charge and minimize the charging time.88 Huang, S.-J.; Huang, B.-G.; Pai, F.-S.; IEEE Transactions on Power Electronics 2013, 28, 1555. They have in common the feature that at some stage in the charging process, a continuous, variable or pulsed current is applied, which may be preceded or followed by the application of a voltage.

Commercial battery chargers commonly use the CC+CV protocol, where a constant current (CC) is applied until the battery reaches 4.2 V, followed by a step where the voltage is maintained at this value (CV) until the current between the battery electrodes fall to a predetermined low value.33 Zhang, S. S.; Xu, K.; Jow, T. R.; J. Power Sources 2006, 160, 1349. Studies show that the CC step in the CC+CV charging protocol can charge up to 80% or even more of the battery charge capacity, for currents up to 0.5C.77 Zhang, S. S.; J. Power Sources 2006, 161, 1385. The storage charge and the charging time will depend, in this step, on the battery states of charge (SOC) and health (SOH) and on the intensity of the applied electrical current, since low charging current intensities imply long charging times and high charge storage, while under highly charging currents (higher than 0.5 C), the charge stored in the battery will be lower, but within shorter charging times.99 Lian-xing, L.; Xin-cun, T.; Yi, Q.; Hong-tao, L.; J. Cent. South Univ. Technol. (Engl. Ed.) 2011, 18, 319

Apart from directly influencing the charge capacity and the battery charging time, the intensity of the charging current contributes to the kinetics of formation of the solid-electrolyte interface passivation layer (SEI) on the anode surface, during the first battery charging cycles.1010 Verma, P.; Maire, P.; Novák, P.; Electrochim. Acta 2010, 55, 6332. This can be responsible for Li electroplating the graphite anode during the charging processes1111 Li, Z.; Huang, J.; Liaw, B. Y.; Metzler, V.; Zhang, J.; J. Power Sources 2014, 254, 168.,1212 Legrand, N.; Knosp, B.; Desprez, P.; Lapicque, F.; Raël, S.; J. Power Sources 2014, 245, 208. and for increasing the battery potential during their charging and discharging, due to polarization effects. The SEI, the electrodeposited Li and polarization potential have influences on battery performance and determine, together with other parameters, its life cycle.

A BIL is discharged when operating as a power sources for electrical and electronic devices. The intensity of the discharging current will depend on the power required by the device. The discharging time is a function of the battery SOH, the stored charge in it, the battery SOC, and the current intensity required along the discharge. Discharges can occur under continuous current or even for high-frequency current pulses as in cell phones, in the GSM protocol.1313 Jossen, A.; J. Power Sources 2006, 154, 530.

Although many studies about charge and discharge processes on BIL can be found, most of them are performed by applying charging and discharging currents from medium to high intensities (higher than 0.5 C). We present a detailed analysis of charge and discharge parameters of a commercial cell-phone lithium-ion battery, when submitted to continuous charge and discharge cycles under constant charging and discharging currents of low intensities (0.04C to 0.52 C). The effects of the applied current intensity on the voltage profile, on the charging and discharging time, on the stored charge (charge capacity) and extracted charge (discharge capacity), and the functional dependence between the charging and discharging time with the applied current intensity were studied.

EXPERIMENTAL

The studies were performed on a commercial LiCoO2/C cell phone battery, with nominal discharge capacity equal to 960 mA h (technically the battery charge capacity) and a SOH equal to 98%. These batteries have a prismatic case, both the cathode and anode are strips, with a polymeric insulating separator between them, containing the electrolyte. The three strips are wound as a jelly roll and inserted into the battery case.

Table 1 and 2 show the matrices designed for the battery charging and discharging tests, performed under the CC protocol, as well as the results obtained. The variables studied were: the intensity of the charging (ic) and discharging (id) currents, the corresponding charging (tc) and discharging (td) times, the inserted (Qc) and extracted (Qd) charges into and from the battery, respectively (charge and discharge capacities).

Table 1
Matrix of tests designed to charge the battery with seven CC, each one followed by three CC discharges, and the obtained results for tc, Qc, td and Qd
Table 2
Matrix of tests designed to discharge the battery with seven discharging currents id, after three different charging processes, and the results obtained for td and Qd

In the charging tests (Table 1) ic currents equal to 40, 80, 120, 200, 300, 400 and 500 mA (C rate between 0,04C and 0,52C) were applied to charge the battery from 3.0 to 4.2 V. At 4.2 V, the battery circuit was open (OCV) until equilibrium voltage was reached after 15 minutes, followed by discharges at constant currents, id, of -80 mA (0.8C), -210 mA (0.22C) and -300 mA (0.31C), down to 3.0 V. The OCV assures the relaxation of battery overvoltage before each discharge.

For each one of the seven charging currents, the battery was discharged under the three discharging currents, resulting in twenty one charge-discharge cycles, as shown in Table 1. Discharged to 3.0 V, the battery was kept at this voltage until the current dropped to 5 mA. So, each new charging cycle was started with the battery on the same residual charge and at 3.0 V.

Table 2 shows the test matrix designed to perform the battery discharge studies in CC of different intensities and the obtained results. The variables were the intensity of the CC applied to discharge (id) the battery, the corresponding discharging time (td), the extracted charge (Qd) (discharge capacity) and the CC and CC+CV charging protocols, employed to charge the battery. Discharges were performed after charging at 120 and 500 mA (CC protocol) and under 500 mA + 4.2 V (CC+CV protocol). In the CV step of the CC+CV protocol the battery was kept at 4.2 V until the current decays to 1.0 mA. The CC discharges were performed at currents equal to -40, -80, -120, -200, -300, -400 and -500 mA, as shown in Table 2. The battery was cycled between 3.0 and 4.2 V. At 4.2 V, the battery circuit was opened for 15 minutes and at 3.0 V the voltage was maintained until the battery current dropped to 5.0 mA, when a new charging cycle is then started. In total, twenty one charge-discharge cycles were continuously performed, wherein seven discharges were carried out for each one of three charging processes.

A capacity fading experiment was conducted to follow how the charge-discharge cycles performed during all the experiments of this work could change the battery SOH and, accordingly, have influence on the results to be shown, by continuously cycling an identical battery between 3.0 and 4.2 voltage limits, under the CC+CV (0.7C + 4.2 V) and CC (0.5 C) protocols, to charge and discharge the battery, respectively.

An Arbin BT2000 battery tester was used in the charge-discharge experiments, by connecting the auxiliary and work cables to the negative and positive battery poles, respectively.

RESULTS AND DISCUSSIONS

Figure 1 shows the first three and last three of twenty-one continuous charge-discharge cycles, for the experiments described in Table 1. Similar curves were obtained for the experiments described in Table 2. Results extracted from these curves were displayed on Tables 1 and 2 and on Figures 2 to 5.

Figure 1
The first three and last three of twenty-one charge and discharge cycles applied to the battery, as described in Table 1. The numbers on the cur ves are the applied currents (in mA) to charge (+) and discharge (-) the battery

Figure 2
Voltage curves in charging (---) and discharging the battery (-) under various currents (indicated on the curves, in mA) (a), the OCV after discharge down to 3.0 V (---) and charging voltage curves from 3.0 V (-)(b)

Figure 3
Charge capacity and discharge capacity as function of the current intensity. The battery was discharged after being charged at 120 mA, 500 mA and on 500 mA + 4.2 V

Figure 4
Charge capacity as function of the seven charging currents and the discharge capacity as function of three discharging currents (-80, -210 and -300 mA). The numbers beside the symbols indicate the charging currents and the lines are linear fittings for the discharge current data

Figure 5
Discharging time (open symbols) and charging time (black sym bol) as a function of discharging and charging currents and fitted curves described in Table 3

Figure 1 and Figure 2a show that the voltage curve profile between 3.0 and 4.2 V and the corresponding charging and discharging times are both dependent on the intensity of the applied current. Two distinct regions can be identified in these voltage curves, one for which the voltage rapidly changes in the 3.0 to 3.7 V range, followed by a second region in which the voltage change more smoothly between 3.7 and 4.2 V, with a profile very dependent on the applied current intensity.

The change in the battery voltage between 3.7 and 4.2 V is due mainly to Li+ insertion (the voltage decreases) and extraction (the voltage increases) into and from the LiCoO2 cathode, as evidenced by the cyclic voltammetries of the LiCoO2/Li cell presented in the literature, wherein redox currents are set up only in this voltage range, with an oxidation peak around 3.7 V.1414 Scrosati, B.; Garche, J.; J. Power Sources 2010, 195, 2419. High currents imply fast changes in the concentration of Li+ ions into the lamellar planes in the LiCoO2 structure22 Reimers, J. N.; Dahn, J. R.; J. Electrochem. Soc. 1992, 139, 2091. and, as a consequence, fast changes in the battery voltage in a short time. Under low currents the opposite occurs. Given that the carbon anode voltage does not change more than 0.2 V whereas the battery voltage change between 3.7 to 4.2 V,11 Zhang, S. S.; Xu, K.; Jow, T. R.; J. Power Sources 2006, 160, 1403. the concentration of Li+ ions into the LiCoO2 cathode accounts for the battery voltage in this range.

The fast voltage increase from 3.0 to 3.7 V at the beginning of battery charging is due to rapid polarization overvoltage.1515 Bernardi, D. M.; Go, J.-Y.; J. Power Sources 2011, 196, 412. In fact, Figure 2b shows the OCV curves after the discharge at 3.0 V and the charging curves from 3.0 V, for the three currents (80, 300 and 500 mA). Equal overvoltages are observed for the same discharging and charging currents.

Under discharge, the fast change in the battery voltage from 3.7 to 3.0 V occurs as a consequence of almost full occupancy of the Li ion sites in the LiCoO2 crystalline structure. So, any further discharge to 3.0 V will occur by the electrode polarizations, at the expense of fast decreases in the battery voltage.

The charge Qc, stored in the battery in the charging from 3.0 to 4.2 V by the seven currents ic, as described in Figure 1 and Table 1, is shown in Figure 3. A linear decrease of the charge capacity with the intensity of the charging current was obtained, a behavior that is also observed from published data for charging currents lower than 1C, but that departs from linearity for higher currents.1616 Ramadass, P.; Haran, B.; White, R.; Popov, B. N.; J. Power Sources 2002, 111, 210.,1717 Guo, Z.; Liaw, B. Y.; Qiu, X.; Gao, L.; Zhang, C.; J. Power Sources 2015, 274, 957.

Figure 3 shows also the extracted charge Qd by the seven discharging currents id, after the battery was charged by the 120 and 500 mA currents and by the 500 mA + 4.2 V CC+CV protocol, as described in Table 2. The extracted charge also decreases linearly with the intensity of the discharging current, for each of these three battery charging procedures. However, literature data indicates a non-linear discharge capacity decreasing for discharge currents higher than 1 C.55 Sikha, G.; Ramadass, P.; Haran, B. S.; White, R. E.; Popov, B. N.; J. Power Sources 2003, 122, 67. The observed decrease in the charge and discharge capacities with the current intensity is caused by the polarization overvoltage, with the value being proportional to the current intensity.

Figure 3 (open circles) shows that when charged at 40 mA, the battery charging capacity is 180 mA h greater than when charged at 500 mA. However, after being charged by the 120 and 500 mA CC charging currents and by the CC+CV protocol, almost all stored charge is extracted from the battery, even at the higher discharging currents: the discharging capacity for the 40 mA discharging current is only16.0 ± 1 mA h higher than the discharging capacity under the 500 mA discharging current. This effect stems from the asymmetric kinetics of insertion and extraction of Li+ ions into and from the LiCoO2 cathode. The thermodynamic response for this effect is the asymmetry in the charging and discharging voltage curves under de same current intensity, as can be observed in Figure 2a.

The effect of the charging protocol on the battery charging capacity can be observed from Table 2 and Figure 3: battery charge capacities equal to 907.9 ± 2.3, 787.7 ± 4.0 and 971.4 ± 0.6 mA h, were obtained for charging at 120 mA, 500 mA and at 500 mA + 4.2 V (CV), respectively. The CV step increases the battery charge capacity in 7% and 23% on the charge stored by the 120 and 500 mA CC steps, respectively. These results show that the battery SOC depends on the intensity of the charging current applied in the CC step but also on the charging protocol. A detailed study about the effect of the CC and CV protocols on the charge capacity was presented for the MCMB/LiCoO2 cell.33 Zhang, S. S.; Xu, K.; Jow, T. R.; J. Power Sources 2006, 160, 1349.

Figure 4 shows the charge extracted (Qd) in discharges performed at -80, -210 and -300 mA as a function of the stored charge (Qc) in the battery for the seven charging currents, as described in Table 1. A linear dependence between Qd and Qc is observed, with the charge capacity increasing with decreasing charging current intensity. The battery discharge capacity diminishes when the discharging current increases from -80 mA to -300 mA and this effect is more pronounced the greater the battery charge capacity. The slope of the linear fittings show coulombic efficiencies equals to 0.987, 0.973 and 0.969 for discharges at -80, -210 and -300 mA, respectively.

The time to charge the battery from 3.0 to 4.2 V and to discharge it from 4.2 to 3.0 V is very dependent on the current intensity as shown in Figure 5, drawn from data of Table 1 for battery charging and from data of Table 2, for the three battery dischargings. Both, the charging and discharging times, decreases asymptotically with the current intensity, as also observed in other studies performed on LiCoO2 cells.33 Zhang, S. S.; Xu, K.; Jow, T. R.; J. Power Sources 2006, 160, 1349.,1717 Guo, Z.; Liaw, B. Y.; Qiu, X.; Gao, L.; Zhang, C.; J. Power Sources 2015, 274, 957.

Figure 5 shows that the discharge time, td, depends on the discharge current intensity, id, but also on the battery state of charge (SOC) before the discharges. At low discharging currents an appreciable difference between the td values with the battery SOC is observed, that progressively decreases as the discharge current intensity increases. The battery state of health (SOH) must be also considered if it is not new in use.1818 Floriano, R.; Santos, A. O.; Urbano, A.; Cardoso, L. P.; Scarminio, J.; Int. J. Res. Rev. Appl. Sci. 2013, 17, 158.

The experimental data of Figure 5 can be fitted by allometric equations, as shown in Table 3, where the equation on line a) refers to battery charging and the items b), c) and d) refer to battery discharging, for the three chargings described in Table 2.

Table 3
Fitted equations for the charging and discharging times, as a function of applied current. C5: battery charge capacity measured in a discharge of five hours.

The fitted equations are similar to those proposed by Peukert (t . ik = C, where k and C are constants) to describe the dependence between the current intensity to discharge a fully charged lead-acid battery and the discharging time.1919 Doerffel, D., Sharkh, S. A.; J. Power Sources 2006, 155, 395. This equation has been improved for lithium-ion batteries considering thermal effects, high discharge currents and long discharge times.2020 Omar, N.; Van den Bossche, P.; Coosemans, T.; Van Mierlo, J.; Energies 2013, 6, 5625.

Table 3 shows that allometric equations can be employed to fit the data of not only battery discharging but also the data of the battery charging. k values around 1.01 were obtained for the b), c) and d) discharges. The C values can be related to the battery discharge capacity since they increase in the sequence b) to c) to d).

From the allometric equations of Table 3, the discharging current (i5) applied to discharge the battery in five hours (t5 = 5 h) can be calculated, and from this the corresponding charge C5 = i5.t5 is obtained, as showed in Table 3. The C5 value is the charge extracted from the battery in a discharge of 5 hours, after it was fully charged, as described in items b), c) and d) of Table 3. Technically, C5 is the battery charge.

In battery cycling experiments, besides the battery SOC also the battery SOH, or equivalently the charge capacity, should be considered since it decreases with the number of charge-discharge cycles, as showed in Figure 6 obtained from a battery of the same manufacturer and model as employed in this study. It can be seen that for a fresh battery, significant losses in the battery SOH for charge-discharge cycles below than one hundred are not observed. Considering that in the study presented here, no more than sixty charge-discharge cycles were performed on a fresh battery (SOH = 98%), the decrease in the battery SOH during all cycles was very small, having a secondary effect on the results presented.

Figure 6
The battery SOH dependence upon continuous charge-discharge cycles. Note: the measured SOH in a pristine battery is higher than the nominal value furnished by the manufacturer

CONCLUSION

We show that to charge and discharge a portable lithium-ion battery between 3.0 and 4.2 V under low charging and discharging currents (0.04 C to 0.52 C), the stored and extracted charge (charge and discharge capacities), into and from the battery, decrease linearly with the intensity of the applied current. The time to charge or to discharge the battery between these voltages decreases with increasing applied current intensity, with a functional dependence fitted by an allometric function, as already obtained by Peukert for lead-acid batteries. Under discharge currents of low intensities battery coulometric efficiency higher than 97% was obtained. The results presented here may be useful to design batteries for portable electric devices, avoiding the fast deleterious effects of high current operations. It should be stressed that the cycling experiments were performed under the condition of very small change in the battery SOH value of the fresh battery (SOH = 98%).

ACKNOWLEDGMENTS

The authors wish to thank Sercomtel Celular SA for providing the battery samples employed in this study. S. P. da Silva and J. Scarminio are grateful to the Conselho Nacional de Pesquisa (CNPq - Brazil) for their scholarships.

REFERENCES

  • 1
    Zhang, S. S.; Xu, K.; Jow, T. R.; J. Power Sources 2006, 160, 1403.
  • 2
    Reimers, J. N.; Dahn, J. R.; J. Electrochem. Soc. 1992, 139, 2091.
  • 3
    Zhang, S. S.; Xu, K.; Jow, T. R.; J. Power Sources 2006, 160, 1349.
  • 4
    Li, J.; Murphy, E.; Winnick, J.; Kohl, P.; J. Power Sources 2001, 102, 302.
  • 5
    Sikha, G.; Ramadass, P.; Haran, B. S.; White, R. E.; Popov, B. N.; J. Power Sources 2003, 122, 67.
  • 6
    Liu, Y.-H.; Teng, J.-H.; Lin, Y.-C.; IEEE Trans. Ind. Electron. Control Instrum. 2005, 52, 1328.
  • 7
    Zhang, S. S.; J. Power Sources 2006, 161, 1385.
  • 8
    Huang, S.-J.; Huang, B.-G.; Pai, F.-S.; IEEE Transactions on Power Electronics 2013, 28, 1555.
  • 9
    Lian-xing, L.; Xin-cun, T.; Yi, Q.; Hong-tao, L.; J. Cent. South Univ. Technol. (Engl. Ed.) 2011, 18, 319
  • 10
    Verma, P.; Maire, P.; Novák, P.; Electrochim. Acta 2010, 55, 6332.
  • 11
    Li, Z.; Huang, J.; Liaw, B. Y.; Metzler, V.; Zhang, J.; J. Power Sources 2014, 254, 168.
  • 12
    Legrand, N.; Knosp, B.; Desprez, P.; Lapicque, F.; Raël, S.; J. Power Sources 2014, 245, 208.
  • 13
    Jossen, A.; J. Power Sources 2006, 154, 530.
  • 14
    Scrosati, B.; Garche, J.; J. Power Sources 2010, 195, 2419.
  • 15
    Bernardi, D. M.; Go, J.-Y.; J. Power Sources 2011, 196, 412.
  • 16
    Ramadass, P.; Haran, B.; White, R.; Popov, B. N.; J. Power Sources 2002, 111, 210.
  • 17
    Guo, Z.; Liaw, B. Y.; Qiu, X.; Gao, L.; Zhang, C.; J. Power Sources 2015, 274, 957.
  • 18
    Floriano, R.; Santos, A. O.; Urbano, A.; Cardoso, L. P.; Scarminio, J.; Int. J. Res. Rev. Appl. Sci. 2013, 17, 158.
  • 19
    Doerffel, D., Sharkh, S. A.; J. Power Sources 2006, 155, 395.
  • 20
    Omar, N.; Van den Bossche, P.; Coosemans, T.; Van Mierlo, J.; Energies 2013, 6, 5625.

Publication Dates

  • Publication in this collection
    Sept 2016

History

  • Received
    16 Nov 2015
  • Accepted
    18 Apr 2016
Sociedade Brasileira de Química Secretaria Executiva, Av. Prof. Lineu Prestes, 748 - bloco 3 - Superior, 05508-000 São Paulo SP - Brazil, C.P. 26.037 - 05599-970, Tel.: +55 11 3032.2299, Fax: +55 11 3814.3602 - São Paulo - SP - Brazil
E-mail: quimicanova@sbq.org.br