CHARACTERIZATION OF SEVERAL GENERATIONS OF NiMo HYDROPROCESSING CATALYSTS EMPLOYED IN THE SAME HYDROTREATER

Abstract

This work details the chemical characterization of four NiMo/Al2O3 hydroprocessing generation catalysts (1979-1986, 1993-1998, 2003-2008 and 2008-2011) employed to perform hydrodesulfurization (HDS) of diesel fractions in the same hydrotreater of a Brazilian refinery. The basic differences are the quality of the feedstocks and the HDS experimental conditions. Samples were characterized by X-ray fluorescence, X-ray diffraction, 13C CP-MAS NMR, elemental analysis, loss of volatiles, specific surface area and average pore volume. The amount and variety of foreign elements deposited on the catalyst increased in the most recent generations due to the higher amounts of impurities in the processed feedstocks. Coke became more aromatic and loss of textural properties was more prominent in these samples as expected from the more drastic HDS conditions and the quality of the crude diesel. On the other hand, loss of volatiles was lower due to the low carbon content, partial oxidation of sulfur to sulfate species and oxidation of some elements deposited on the catalyst. Coke tended to ignite as it became more aromatic. For this reason, leaching of decoked samples from the most recent generations by sulfuric acid presented very low yields due to the formation of refractory oxides that are insoluble in the leachant.

Keywords:
spent catalysts; coke; metals deposition; catalyst characterization; catalyst leaching


INTRODUCTION

Over the years, refineries have been processing heavier and sourer feeds due to shifting crude diversity and sources. Maximizing of liquid products yield from various processes and valorization of residues are of immediate attention to refiners.11 Rodríguez, E.; Félix, G.; Anchyeta, J.; Trejo, F.; Fuel 2018, 225, 118. Hydroprocessing is a key technology for the production of clean fuels in today’s refineries operations because of the high concentrations of sulfur, nitrogen, and metals along with a high proportion of coke precursors in such feedstocks.22 Vogelaar, B. M.; Eijsbouts, S.; Bergwerff, J. A.; Heiszwolf, J. J.; Catal. Today 2010, 154, 256.

3 Leyvaa, C.; Ancheyta, J.; Marieyb, L.; Travertb, A.; Maugé, F.; Catal. Today 2014, 220-222, 89.

4 Kohli, K.; Prajapati, R.; Maity, S. K.; Sal, M.; Sharma, B. K.; Fuel 2019, 235, 437.
-55 Torres-Mancera, P.; Anchyeta, J.; Martínez, J.; Fuel 2018, 234, 326. The petroleum refining industry needs a large amount of catalyst to purify and refine such crudes because a high conversion level is required.66 Wang, L.; Chao, L.; Qu, W.; Xu, S.; Zhang, L.; Peng, J.; Ye, X.; Ultrason. Sonochem. 2018, 49, 24. Hydroprocessing catalysts are mostly based on Ni, Co, Mo and W sulfides.22 Vogelaar, B. M.; Eijsbouts, S.; Bergwerff, J. A.; Heiszwolf, J. J.; Catal. Today 2010, 154, 256.,77 Valverde Jr., I. M.; Paulino, J. F.; Afonso, J. C.; J. Hazard. Mater. 2008, 160, 310. They account for about one-third of the total worldwide catalyst consumption.88 Imam, D. M.; El-Nadi, Y. A.; Hydrometallurgy 2018, 180, 172.,99 Rana, M. S.; Ancheyta, J.; Sahoo, S. K.; Rayo, P.; Catal. Today 2014, 220-222, 97.

At present environmental directories impose severe restrictions concerning gas and particle emissions from refineries and fuels.99 Rana, M. S.; Ancheyta, J.; Sahoo, S. K.; Rayo, P.; Catal. Today 2014, 220-222, 97.,1010 Yang, Y.; Shengming, X.; Li, Z.; Wang, J.; Zhao, Z.; Xu, Z.; J. Hazard. Mater. 2016, 318, 723. Deep hydrodesulfurization (HDS) of diesel has become an important issue in recent years due to stringent regulations that require low sulfur levels (< 10 mg kg-1) in this fuel.77 Valverde Jr., I. M.; Paulino, J. F.; Afonso, J. C.; J. Hazard. Mater. 2008, 160, 310.,1111 Koh, J. H.; Lee, J. J.; Kim, H.; Cho, A.; Moon, S. H.; Appl. Catal. B: Environ. 2009, 86 176.,1212 Guichard, B.; Auberger, M. R.; Devers, E.; Legens, C.; Raybaud, P.; Catal. Today 2008, 130, 97. Those levels can only be reached by hardening the working conditions (increase of temperature, lower space velocity and higher hydrogen partial pressure), improving efficiency of the existing processes1313 Marchala, C.; Uzioa, D.; Merdrignaca, I.; Barreb, L.; Geantet, C.; Appl. Catal. A: Gen. 2012, 411- 412, 35. or using more active catalysts with good tolerance to deactivation.33 Leyvaa, C.; Ancheyta, J.; Marieyb, L.; Travertb, A.; Maugé, F.; Catal. Today 2014, 220-222, 89.,1111 Koh, J. H.; Lee, J. J.; Kim, H.; Cho, A.; Moon, S. H.; Appl. Catal. B: Environ. 2009, 86 176.,1212 Guichard, B.; Auberger, M. R.; Devers, E.; Legens, C.; Raybaud, P.; Catal. Today 2008, 130, 97.,1414 Guichard, B.; Roy-Auberger, M.; Devers, E.; Rebours, B.; Quoineaud, A. A.; Digne, M.; Appl. Catal. A: Gen. 2009, 367, 1.

The heavier and more contaminated feedstock, the faster the catalyst deactivation,11 Rodríguez, E.; Félix, G.; Anchyeta, J.; Trejo, F.; Fuel 2018, 225, 118.,1515 Ramirez, S.; Leyva, C.; Ancheyta, J.; Centeno, G.; Fuel 2009, 88, 2311. particularly when the crude oil has high percentage of asphaltenes,11 Rodríguez, E.; Félix, G.; Anchyeta, J.; Trejo, F.; Fuel 2018, 225, 118.,1616 Gawel, I.; Bociarska, D.; Biskupski, P.; Appl. Catal. A: Gen. 2005, 295, 89. and at severe reaction conditions.44 Kohli, K.; Prajapati, R.; Maity, S. K.; Sal, M.; Sharma, B. K.; Fuel 2019, 235, 437.,99 Rana, M. S.; Ancheyta, J.; Sahoo, S. K.; Rayo, P.; Catal. Today 2014, 220-222, 97. This phenomenon will become more and more critical due to the ongoing trend in increasing hydroprocessing severity and maximizing catalyst performance to meet fuels quality.11 Rodríguez, E.; Félix, G.; Anchyeta, J.; Trejo, F.; Fuel 2018, 225, 118.,22 Vogelaar, B. M.; Eijsbouts, S.; Bergwerff, J. A.; Heiszwolf, J. J.; Catal. Today 2010, 154, 256.,1717 Marafi, M.; Al-Sheeha, H.; Al-Omani, S.; Al-Barood, A.; Fuel Process. Technol. 2009, 90, 264. To maintain constant product yields and/or quality, the loss of catalytic activity must be compensated by periodic increases of reaction temperature.11 Rodríguez, E.; Félix, G.; Anchyeta, J.; Trejo, F.; Fuel 2018, 225, 118.,66 Wang, L.; Chao, L.; Qu, W.; Xu, S.; Zhang, L.; Peng, J.; Ye, X.; Ultrason. Sonochem. 2018, 49, 24.,88 Imam, D. M.; El-Nadi, Y. A.; Hydrometallurgy 2018, 180, 172.

Catalyst deactivation plays an important role in process design and operation within the petrochemical and petroleum industry both from an economic and technological point of view.11 Rodríguez, E.; Félix, G.; Anchyeta, J.; Trejo, F.; Fuel 2018, 225, 118.,22 Vogelaar, B. M.; Eijsbouts, S.; Bergwerff, J. A.; Heiszwolf, J. J.; Catal. Today 2010, 154, 256.,1515 Ramirez, S.; Leyva, C.; Ancheyta, J.; Centeno, G.; Fuel 2009, 88, 2311.,1818 Callejas, M. A.; Martınez, M. T.; Blasco, T.; Sastre, E.; Appl. Catal. A: Gen. 2001, 218, 181.

19 Maity, S. K.; Blanco, E.; Ancheyta, J.; Alonso, F.; Fukuyama, H.; Fuel 2012, 100, 17.
-2020 Torres-Mancera, P.; Rayo, P.; Ancheyta, J.; Marroquín, G.; Centeno, G.; Alonso, F.; Catal. Today 2014, 220-222, 153. Hydroprocessing catalysts are deactivated by coke, oil and elements deposition.1919 Maity, S. K.; Blanco, E.; Ancheyta, J.; Alonso, F.; Fukuyama, H.; Fuel 2012, 100, 17.,2121 Yue, Y.; Tiantian, C.; Yong, X.; GuoYong, H.; Wenqiang, W.; Qi, L.; Shengming, X.; Waste Manage. 2018, 78, 595. They contain sulfur and can ignite spontaneously in air due to presence of the flammable oil and metal sulfides. This is an important factor that endangers the local environmental quality.66 Wang, L.; Chao, L.; Qu, W.; Xu, S.; Zhang, L.; Peng, J.; Ye, X.; Ultrason. Sonochem. 2018, 49, 24. The Environmental Protection Agency (EPA) has considered the spent hydroprocessing catalyst as a hazardous material.1010 Yang, Y.; Shengming, X.; Li, Z.; Wang, J.; Zhao, Z.; Xu, Z.; J. Hazard. Mater. 2016, 318, 723.,1919 Maity, S. K.; Blanco, E.; Ancheyta, J.; Alonso, F.; Fukuyama, H.; Fuel 2012, 100, 17.

Coke deposition on the catalyst is generally believed to be the primary cause of catalyst deactivation.1111 Koh, J. H.; Lee, J. J.; Kim, H.; Cho, A.; Moon, S. H.; Appl. Catal. B: Environ. 2009, 86 176.,1616 Gawel, I.; Bociarska, D.; Biskupski, P.; Appl. Catal. A: Gen. 2005, 295, 89.,1818 Callejas, M. A.; Martınez, M. T.; Blasco, T.; Sastre, E.; Appl. Catal. A: Gen. 2001, 218, 181.,2222 Wood, J.; Gladden, L. F.; Appl. Catal. A: Gen. 2003, 249, 241.,2323 Maity, S. K.; Ancheyta, J.; Alonso, F.; Rayo, P.; Fuel Process. Technol. 2013, 106, 453. It is formed very rapidly at the early stages of hydroprocessing reactions.11 Rodríguez, E.; Félix, G.; Anchyeta, J.; Trejo, F.; Fuel 2018, 225, 118. The pores of the catalyst are physically blocked, preventing the diffusing reactants from entering the pore structure.2222 Wood, J.; Gladden, L. F.; Appl. Catal. A: Gen. 2003, 249, 241.,2323 Maity, S. K.; Ancheyta, J.; Alonso, F.; Rayo, P.; Fuel Process. Technol. 2013, 106, 453. The rate of coke formation enhances with increasing reaction temperature.2323 Maity, S. K.; Ancheyta, J.; Alonso, F.; Rayo, P.; Fuel Process. Technol. 2013, 106, 453. Oil deposition also reduce surface area and pore volume of catalysts with prolonged time of use.2121 Yue, Y.; Tiantian, C.; Yong, X.; GuoYong, H.; Wenqiang, W.; Qi, L.; Shengming, X.; Waste Manage. 2018, 78, 595.

Sintering or segregation of the active phase,1212 Guichard, B.; Auberger, M. R.; Devers, E.; Legens, C.; Raybaud, P.; Catal. Today 2008, 130, 97.,2222 Wood, J.; Gladden, L. F.; Appl. Catal. A: Gen. 2003, 249, 241.

23 Maity, S. K.; Ancheyta, J.; Alonso, F.; Rayo, P.; Fuel Process. Technol. 2013, 106, 453.

24 Afonso, J. C.; Aranda, D. A. G.; Schmal, M.; Fréty, R.; Fuel Process. Technol. 1995, 42, 3.

25 Afonso, J. C.; Schmal, M.; Fréty, R.; Fuel Process. Technol. 1994, 41, 13.
-2626 Guichard, B.; Roy-Auberger, M.; Devers, E.; Pichon, C.; Legens, C.; Appl. Catal. A: Gen. 2009, 367, 9. poisoning by nitrogen-containing compounds and elements deposition (silicon, calcium, iron, arsenic etc.)1111 Koh, J. H.; Lee, J. J.; Kim, H.; Cho, A.; Moon, S. H.; Appl. Catal. B: Environ. 2009, 86 176. also lead to loss of activity. Elements deposition takes place at longer period than coke.11 Rodríguez, E.; Félix, G.; Anchyeta, J.; Trejo, F.; Fuel 2018, 225, 118. The presence of vanadium and nickel in crude feedstocks is of particular interest. These metals are usually distributed between porphyrin and non-porphyrin type structures. They are accumulated as metal sulfides in the pore mouth of the catalyst and block the way of the reactants to enter.2323 Maity, S. K.; Ancheyta, J.; Alonso, F.; Rayo, P.; Fuel Process. Technol. 2013, 106, 453.

The most common characterization techniques to monitor the changes in catalyst activity during commercial operation are textural properties (surface area, pore volume, average pore diameter and pore size distribution),11 Rodríguez, E.; Félix, G.; Anchyeta, J.; Trejo, F.; Fuel 2018, 225, 118.,44 Kohli, K.; Prajapati, R.; Maity, S. K.; Sal, M.; Sharma, B. K.; Fuel 2019, 235, 437. elements88 Imam, D. M.; El-Nadi, Y. A.; Hydrometallurgy 2018, 180, 172.,1010 Yang, Y.; Shengming, X.; Li, Z.; Wang, J.; Zhao, Z.; Xu, Z.; J. Hazard. Mater. 2016, 318, 723. and carbon content.11 Rodríguez, E.; Félix, G.; Anchyeta, J.; Trejo, F.; Fuel 2018, 225, 118.,2121 Yue, Y.; Tiantian, C.; Yong, X.; GuoYong, H.; Wenqiang, W.; Qi, L.; Shengming, X.; Waste Manage. 2018, 78, 595. Carbonaceous deposits have been characterized by solubility tests (solvent extraction) and several instrumental techniques.11 Rodríguez, E.; Félix, G.; Anchyeta, J.; Trejo, F.; Fuel 2018, 225, 118.,66 Wang, L.; Chao, L.; Qu, W.; Xu, S.; Zhang, L.; Peng, J.; Ye, X.; Ultrason. Sonochem. 2018, 49, 24.,1010 Yang, Y.; Shengming, X.; Li, Z.; Wang, J.; Zhao, Z.; Xu, Z.; J. Hazard. Mater. 2016, 318, 723.,1414 Guichard, B.; Roy-Auberger, M.; Devers, E.; Rebours, B.; Quoineaud, A. A.; Digne, M.; Appl. Catal. A: Gen. 2009, 367, 1.,2222 Wood, J.; Gladden, L. F.; Appl. Catal. A: Gen. 2003, 249, 241.,2727 Vogelaar, B. M.; van Langeveld, A. D.; Eijsbouts, S.; Moulijn, J. A.; Fuel 2007, 86, 1122. Solid-state 13C NMR has the unique ability to determine the distribution of aromatic, aliphatic and other carbon types present.1414 Guichard, B.; Roy-Auberger, M.; Devers, E.; Rebours, B.; Quoineaud, A. A.; Digne, M.; Appl. Catal. A: Gen. 2009, 367, 1.,1818 Callejas, M. A.; Martınez, M. T.; Blasco, T.; Sastre, E.; Appl. Catal. A: Gen. 2001, 218, 181.,2222 Wood, J.; Gladden, L. F.; Appl. Catal. A: Gen. 2003, 249, 241.

It is an important issue to study the deactivation of hydroprocessing catalysts by investigating the state and distribution of deposited species (coke and elements) on the catalyst.99 Rana, M. S.; Ancheyta, J.; Sahoo, S. K.; Rayo, P.; Catal. Today 2014, 220-222, 97.,1515 Ramirez, S.; Leyva, C.; Ancheyta, J.; Centeno, G.; Fuel 2009, 88, 2311. The investigation of samples withdrawn from an industrial or pilot reactor provide valuable information to develop recovery processes of valuable metals (Ni, Co, Mo, W) from spent catalysts.11 Rodríguez, E.; Félix, G.; Anchyeta, J.; Trejo, F.; Fuel 2018, 225, 118.,22 Vogelaar, B. M.; Eijsbouts, S.; Bergwerff, J. A.; Heiszwolf, J. J.; Catal. Today 2010, 154, 256.,66 Wang, L.; Chao, L.; Qu, W.; Xu, S.; Zhang, L.; Peng, J.; Ye, X.; Ultrason. Sonochem. 2018, 49, 24.,2222 Wood, J.; Gladden, L. F.; Appl. Catal. A: Gen. 2003, 249, 241.,2424 Afonso, J. C.; Aranda, D. A. G.; Schmal, M.; Fréty, R.; Fuel Process. Technol. 1995, 42, 3.,2828 Afonso, J. C.; Silva, G. C.; Aguiar, R. M.; Stud. Surf. Sci. Catal. 2001, 139, 165.,2929 Pereira, A. L. S.; Silva, C. N.; Mantovano, J. L.; Afonso, J. C.; Quim. Nova 2011, 34, 145. In these studies, coke must be eliminated under an oxidizing atmosphere at high temperature (450‑550 ºC) and low heating rate prior to leaching in order to increase metals exposure to the leachant.77 Valverde Jr., I. M.; Paulino, J. F.; Afonso, J. C.; J. Hazard. Mater. 2008, 160, 310.,2424 Afonso, J. C.; Aranda, D. A. G.; Schmal, M.; Fréty, R.; Fuel Process. Technol. 1995, 42, 3.,2828 Afonso, J. C.; Silva, G. C.; Aguiar, R. M.; Stud. Surf. Sci. Catal. 2001, 139, 165.

This work presents a unique study on the deactivation of several generations of spent hydroprocessing catalysts (covering over 30 years) used in the same hydrotreater to perform hydrodesulfurization (HDS) of crude diesel fractions. Their chemical composition and the nature of coke and elements deposited on the catalyst surfaces were determined to understand the behavior of samples subjected to leaching with sulfuric acid after coke removal.

EXPERIMENTAL

Spent catalysts

Four generations of spent NiMo/Al2O3 catalysts (5 mm cylinder extruded, 1.2 mm diameter) covering a 32 year period (1979-1986, 1993-1998, 2003-2008 and 2008-2011) were employed. These catalysts worked in the sulfided form in the same hydrotreater of a Brazilian refinery. This unit is designed for HDS of crude diesel fractions obtained after processing various crude oils. Table 1 presents some data of the feedstocks processed, the crude diesel fractions and the HDS experimental conditions.

Table 1
Feedstocks, crude diesel and HDS data

Data of Table 1 indicate that the quality of the feedstock became progressively heavier as shown by the higher density and amounts of Ni, V, S and N (there is no significant difference between the feedstocks treated by the third and fourth NiMo generation catalysts). The quality of the crude diesel follows the same trend. The first and second NiMo generation catalysts worked under classical HDS conditions, the third generation worked as such from 2003 to 2007, but ultra-deep HDS was introduced in 2008. The last generation worked only under ultra-deep HDS conditions.1212 Guichard, B.; Auberger, M. R.; Devers, E.; Legens, C.; Raybaud, P.; Catal. Today 2008, 130, 97.,2626 Guichard, B.; Roy-Auberger, M.; Devers, E.; Pichon, C.; Legens, C.; Appl. Catal. A: Gen. 2009, 367, 9.,3030 Kim, T.; Ali, S. A.; Alhooshani, K.; Park, J. I.; Al-Yami, M.; Yoon, S. H.; Mochida, I.; J. Ind. Eng. Chem. 2013, 19, 1577.

31 Song, C.; Turaga, U. T.; Ma, X.; Encyclopedia of Chemical Processing, Taylor & Francis: New York, 2006, p. 651-661.

32 Yoshimura, Y.; Toba, M.; Farag, H.; Sakanishi, K.; Catal. Surv. Asia 2004, 8, 47.
-3333 Pawelec, B.; Navarro, R. M.; Martin, J. M. C.; Fierro, J. L. G.; Catal. Sci. Technol. 2011, 1, 23.

The hydrotreater design remained the same along the period 1979-2011. Only routine maintenance was performed (change of corroded components, removal of accumulated solids etc.). The use of current commercial HDS catalysts without changing the reactor volume means that the catalyst activity must have increased to meet the new diesel regulation.3333 Pawelec, B.; Navarro, R. M.; Martin, J. M. C.; Fierro, J. L. G.; Catal. Sci. Technol. 2011, 1, 23. This can be achieved with high metal loading, minimal support-metal interaction or additional catalyst volume.3232 Yoshimura, Y.; Toba, M.; Farag, H.; Sakanishi, K.; Catal. Surv. Asia 2004, 8, 47.,3333 Pawelec, B.; Navarro, R. M.; Martin, J. M. C.; Fierro, J. L. G.; Catal. Sci. Technol. 2011, 1, 23.

The bed temperature was gradually increased during the reactor run to compensate for the effects of catalyst deactivation and in order to produce consistent product quality in the face of varying catalyst activity and feed quality.11 Rodríguez, E.; Félix, G.; Anchyeta, J.; Trejo, F.; Fuel 2018, 225, 118.,33 Leyvaa, C.; Ancheyta, J.; Marieyb, L.; Travertb, A.; Maugé, F.; Catal. Today 2014, 220-222, 89.,66 Wang, L.; Chao, L.; Qu, W.; Xu, S.; Zhang, L.; Peng, J.; Ye, X.; Ultrason. Sonochem. 2018, 49, 24.,99 Rana, M. S.; Ancheyta, J.; Sahoo, S. K.; Rayo, P.; Catal. Today 2014, 220-222, 97.,1616 Gawel, I.; Bociarska, D.; Biskupski, P.; Appl. Catal. A: Gen. 2005, 295, 89.,2121 Yue, Y.; Tiantian, C.; Yong, X.; GuoYong, H.; Wenqiang, W.; Qi, L.; Shengming, X.; Waste Manage. 2018, 78, 595.

22 Wood, J.; Gladden, L. F.; Appl. Catal. A: Gen. 2003, 249, 241.

23 Maity, S. K.; Ancheyta, J.; Alonso, F.; Rayo, P.; Fuel Process. Technol. 2013, 106, 453.

24 Afonso, J. C.; Aranda, D. A. G.; Schmal, M.; Fréty, R.; Fuel Process. Technol. 1995, 42, 3.

25 Afonso, J. C.; Schmal, M.; Fréty, R.; Fuel Process. Technol. 1994, 41, 13.
-2626 Guichard, B.; Roy-Auberger, M.; Devers, E.; Pichon, C.; Legens, C.; Appl. Catal. A: Gen. 2009, 367, 9.,3333 Pawelec, B.; Navarro, R. M.; Martin, J. M. C.; Fierro, J. L. G.; Catal. Sci. Technol. 2011, 1, 23. H2 pressure was also gradually increased from the first to the last NiMo generation catalyst.2121 Yue, Y.; Tiantian, C.; Yong, X.; GuoYong, H.; Wenqiang, W.; Qi, L.; Shengming, X.; Waste Manage. 2018, 78, 595.,2222 Wood, J.; Gladden, L. F.; Appl. Catal. A: Gen. 2003, 249, 241.,2424 Afonso, J. C.; Aranda, D. A. G.; Schmal, M.; Fréty, R.; Fuel Process. Technol. 1995, 42, 3. This also reflects the more severe conditions required to ultra-deep HDS. Finally, the liquid hourly space velocity (LHSV) decreased along the NiMo generation catalysts. The decrease of LHSV increases the diesel-catalyst contact time. More refractory sulfur compounds require lower space velocity for achieving deeper HDS.2121 Yue, Y.; Tiantian, C.; Yong, X.; GuoYong, H.; Wenqiang, W.; Qi, L.; Shengming, X.; Waste Manage. 2018, 78, 595.,2222 Wood, J.; Gladden, L. F.; Appl. Catal. A: Gen. 2003, 249, 241.

When the catalyst was taken out of the hydrotreater, the residual oil and other impurities adhered to the catalyst surface were removed by Soxhlet extraction in oxygen-free toluene for ~12 h. The spent catalysts were subsequently dried at 110 ºC for 2 h in dried N2 flow.1313 Marchala, C.; Uzioa, D.; Merdrignaca, I.; Barreb, L.; Geantet, C.; Appl. Catal. A: Gen. 2012, 411- 412, 35.

14 Guichard, B.; Roy-Auberger, M.; Devers, E.; Rebours, B.; Quoineaud, A. A.; Digne, M.; Appl. Catal. A: Gen. 2009, 367, 1.
-1515 Ramirez, S.; Leyva, C.; Ancheyta, J.; Centeno, G.; Fuel 2009, 88, 2311. Samples were not ground. They were stored under nitrogen in the dark at room temperature.

Oxidation of samples (loss of volatiles)

Samples were placed in identical ceramic crucibles. Since they were not ground, catalyst height in the crucible was fixed at 5 mm. Oxidation was performed in a furnace at 500 ºC (3 ºC min-1) for 5 h, according to previous studies in our laboratory.77 Valverde Jr., I. M.; Paulino, J. F.; Afonso, J. C.; J. Hazard. Mater. 2008, 160, 310. Temperature of the catalytic bed was monitored by a thermocouple placed on its surface. The roasted mass was cooled down in the furnace and transferred to a desiccator. The experiments were run in triplicate, and errors for each experiment were always below 3%.

Leaching of oxidized samples

Sulfuric acid was used as leachant. According to literature studies, this acid is by far the most common leachant for processing spent catalysts.77 Valverde Jr., I. M.; Paulino, J. F.; Afonso, J. C.; J. Hazard. Mater. 2008, 160, 310.,2121 Yue, Y.; Tiantian, C.; Yong, X.; GuoYong, H.; Wenqiang, W.; Qi, L.; Shengming, X.; Waste Manage. 2018, 78, 595.,3333 Pawelec, B.; Navarro, R. M.; Martin, J. M. C.; Fierro, J. L. G.; Catal. Sci. Technol. 2011, 1, 23. The experimental procedure is described in detail in the literature.77 Valverde Jr., I. M.; Paulino, J. F.; Afonso, J. C.; J. Hazard. Mater. 2008, 160, 310. The experiments were run in triplicate, and errors for each experiment were always below 5%.

Analytical methods

Solid-state CP-MAS 13C NMR was used to determine the carbon types present in the coke. Samples were crushed using a pestle and mortar so as to produce a fine powder, and then packed into a sample rotor to which a serrated cap was fitted. All experiments were performed on an AVANCE III/400 NMR spectrometer equipped with a 4 mm broadband CP/MAS probe using a magic angle spinning rate of 8 kHz. The instrument was tuned to a resonant 1H frequency of 400.25 MHz and a 13C frequency of 100.64 MHz. Hexamethylbenzene (CH3 at 17.3 ppm) was employed as reference for chemical shifts. The acquisitions were carried out using 90º pulses for 1H of 4.5 µs, an acquisition time of 30 ms, a recycle delay of 2 s, a contact time of 2 ms and sweep width of 50 kHz.

Elemental analysis (C and H) were run using a 2400 CHN Perkin Elmer Elemental Analyzer. Sulfur, arsenic and metals were determined by energy dispersive X-ray fluorescence (Shimadzu XRF 800HS). Calibration curves (0.1–1000 mg kg-1) of the elements found were employed for their quantitative analyses. Crystalline phases in oxidized samples were identified by X-ray powder diffraction (Shimadzu XRD 6000) by continuous scanning method at 20 mA and 40 kV, using Co Ka as radiation source. Specific surface (SBET) area and average pore volume are routinely of fresh, coked and oxidized samples were determined by N2 physisorption at 77 K (-196 ºC) using a Quantachrome Nova 1200e instrument. Prior to adsorption, samples (in round-bottomed glass tubes) were pretreated in vacuum (10-5 torr) at 250 ºC for 3 h. Leached elements were determined by atomic absorption spectrometry (Perkin Elmer AAS 3300). pH measurements of aqueous solutions were conducted by using a combination of a glass electrode and a Ag/AgCl reference electrode (Orion 2AI3-JG). All analyses were run in triplicate, and errors were always below 5%.

RESULTS AND DISCUSSION

Chemical characterization of the spent catalysts

The amount and variety of foreign elements (Table 2) deposited on the catalyst particularly increased in the last two NiMo generation catalysts (2003-2008 and 2008-2011). These samples were directly affected by the quality of the crude diesel and their corresponding feedstocks (Table 1).1515 Ramirez, S.; Leyva, C.; Ancheyta, J.; Centeno, G.; Fuel 2009, 88, 2311.,1717 Marafi, M.; Al-Sheeha, H.; Al-Omani, S.; Al-Barood, A.; Fuel Process. Technol. 2009, 90, 264. This effect seemed to be enhanced by the severity of HDS conditions, since the fourth generation only worked under ultra-deep HDS conditions,22 Vogelaar, B. M.; Eijsbouts, S.; Bergwerff, J. A.; Heiszwolf, J. J.; Catal. Today 2010, 154, 256.,99 Rana, M. S.; Ancheyta, J.; Sahoo, S. K.; Rayo, P.; Catal. Today 2014, 220-222, 97.,1717 Marafi, M.; Al-Sheeha, H.; Al-Omani, S.; Al-Barood, A.; Fuel Process. Technol. 2009, 90, 264. whereas the third one worked only in its last year in service. The presence of silicon can be explained by the use of silicone for foam control in offshore petroleum production,77 Valverde Jr., I. M.; Paulino, J. F.; Afonso, J. C.; J. Hazard. Mater. 2008, 160, 310. whereas some iron came from corrosion/abrasion of the hydrotreater.1212 Guichard, B.; Auberger, M. R.; Devers, E.; Legens, C.; Raybaud, P.; Catal. Today 2008, 130, 97.,2626 Guichard, B.; Roy-Auberger, M.; Devers, E.; Pichon, C.; Legens, C.; Appl. Catal. A: Gen. 2009, 367, 9. Vanadium, arsenic and calcium have already been reported in spent catalysts from hydroprocessing of heavy feedstocks under severe conditions.1919 Maity, S. K.; Blanco, E.; Ancheyta, J.; Alonso, F.; Fukuyama, H.; Fuel 2012, 100, 17.,2121 Yue, Y.; Tiantian, C.; Yong, X.; GuoYong, H.; Wenqiang, W.; Qi, L.; Shengming, X.; Waste Manage. 2018, 78, 595.,2323 Maity, S. K.; Ancheyta, J.; Alonso, F.; Rayo, P.; Fuel Process. Technol. 2013, 106, 453.,3434 Stanislaus, A.; Marafi, A.; Rana, M. S.; Catal. Today 2010, 153, 1.

Table 2
Chemical analysis (wt.%, dry basis) of the spent and fresh NiMo/Al2O3 catalysts

The amounts of molybdenum and nickel are the highest in the last two NiMo generation catalysts. This is a way to increase the activity of the current catalyst technology for ultra-deep HDS.3232 Yoshimura, Y.; Toba, M.; Farag, H.; Sakanishi, K.; Catal. Surv. Asia 2004, 8, 47.

33 Pawelec, B.; Navarro, R. M.; Martin, J. M. C.; Fierro, J. L. G.; Catal. Sci. Technol. 2011, 1, 23.

34 Stanislaus, A.; Marafi, A.; Rana, M. S.; Catal. Today 2010, 153, 1.

35 González-Cortés, S. L.; Rugmini, S.; Xiao, T.; Green, M. L. H.; Rodulfo-Baechler, S. M.; Imbert, F. E.; Appl. Catal. A: Gen. 2014, 475, 270.

36 Trejo, F.; Rana, M. S.; Ancheyta, J.; Chávez, S.; Fuel 2014, 138, 104.
-3737 Moreau, C.; Joffre, J.; Saenz, C.; Afonso, J. C.; Portefaix, J. L.; J. Mol. Catal. A: Chem. 2000, 161, 141. This also explains the higher amount of sulfur in these samples since the HDS catalysts work in sulfide form during their time on stream. The higher amount of support additives (P, Si) is another strategy to improve HDS activity via inclusion of acidic functionality.3131 Song, C.; Turaga, U. T.; Ma, X.; Encyclopedia of Chemical Processing, Taylor & Francis: New York, 2006, p. 651-661.,3232 Yoshimura, Y.; Toba, M.; Farag, H.; Sakanishi, K.; Catal. Surv. Asia 2004, 8, 47.,3636 Trejo, F.; Rana, M. S.; Ancheyta, J.; Chávez, S.; Fuel 2014, 138, 104.,3737 Moreau, C.; Joffre, J.; Saenz, C.; Afonso, J. C.; Portefaix, J. L.; J. Mol. Catal. A: Chem. 2000, 161, 141.

Carbon content decreased in the last NiMo generation catalysts despite the more severe HDS conditions (Table 1). This point will be discussed further.

H/C atomic ratio

The H/C atomic ratio (Table 3) decreased, especially for the last NiMo generation catalyst. This result indicates that coke became more aromatic (lower hydrogen content),1212 Guichard, B.; Auberger, M. R.; Devers, E.; Legens, C.; Raybaud, P.; Catal. Today 2008, 130, 97.,1414 Guichard, B.; Roy-Auberger, M.; Devers, E.; Rebours, B.; Quoineaud, A. A.; Digne, M.; Appl. Catal. A: Gen. 2009, 367, 1.,2222 Wood, J.; Gladden, L. F.; Appl. Catal. A: Gen. 2003, 249, 241.,2626 Guichard, B.; Roy-Auberger, M.; Devers, E.; Pichon, C.; Legens, C.; Appl. Catal. A: Gen. 2009, 367, 9. probably due to the combined effect of the feedstock and ultra-deep HDS conditions.99 Rana, M. S.; Ancheyta, J.; Sahoo, S. K.; Rayo, P.; Catal. Today 2014, 220-222, 97.

Table 3
H/C atomic ratio of coke deposited on spent NiMo/Al2O3 catalysts

H/C atomic ratios below 1.3 are typical of the so-called “hard” coke.1919 Maity, S. K.; Blanco, E.; Ancheyta, J.; Alonso, F.; Fukuyama, H.; Fuel 2012, 100, 17.,2525 Afonso, J. C.; Schmal, M.; Fréty, R.; Fuel Process. Technol. 1994, 41, 13. The “soft” coke is formed at the initial stage of hydroprocessing; it is the main cause of the loss of micropores and consequently the surface area and the porosity of the catalyst. The “hard” coke, which is formed in later stages takes up the remaining porosity.99 Rana, M. S.; Ancheyta, J.; Sahoo, S. K.; Rayo, P.; Catal. Today 2014, 220-222, 97.,1919 Maity, S. K.; Blanco, E.; Ancheyta, J.; Alonso, F.; Fukuyama, H.; Fuel 2012, 100, 17.,2424 Afonso, J. C.; Aranda, D. A. G.; Schmal, M.; Fréty, R.; Fuel Process. Technol. 1995, 42, 3.,2525 Afonso, J. C.; Schmal, M.; Fréty, R.; Fuel Process. Technol. 1994, 41, 13. The soft coke has a higher hydrogen to carbon ratio than the hard one.1919 Maity, S. K.; Blanco, E.; Ancheyta, J.; Alonso, F.; Fukuyama, H.; Fuel 2012, 100, 17.,2525 Afonso, J. C.; Schmal, M.; Fréty, R.; Fuel Process. Technol. 1994, 41, 13. As the time on stream increased the structure of the carbonaceous deposits shifted towards increasing aromaticity, forming a graphite-like structure.44 Kohli, K.; Prajapati, R.; Maity, S. K.; Sal, M.; Sharma, B. K.; Fuel 2019, 235, 437.,1212 Guichard, B.; Auberger, M. R.; Devers, E.; Legens, C.; Raybaud, P.; Catal. Today 2008, 130, 97.,1414 Guichard, B.; Roy-Auberger, M.; Devers, E.; Rebours, B.; Quoineaud, A. A.; Digne, M.; Appl. Catal. A: Gen. 2009, 367, 1.,2626 Guichard, B.; Roy-Auberger, M.; Devers, E.; Pichon, C.; Legens, C.; Appl. Catal. A: Gen. 2009, 367, 9.

13C CP-MAS NMR data

All spectra (Figures 1 to 4) present peaks falling in the Csp3 and Csp2 zones (0 – 60 and 120-160 ppm, respectively).3737 Moreau, C.; Joffre, J.; Saenz, C.; Afonso, J. C.; Portefaix, J. L.; J. Mol. Catal. A: Chem. 2000, 161, 141. The shape of these peaks indicates a great variety of saturated and unsaturated carbons, thus reflecting the complex structure of coke deposited on the catalysts. The integral areas of Csp3 and Csp2 peaks give an approximate estimate of the molar composition of the coke deposited on the catalyst, although the extent of transfer of magnetization from the proton system to the carbons depends upon the nature of coke compounds.2222 Wood, J.; Gladden, L. F.; Appl. Catal. A: Gen. 2003, 249, 241.,3737 Moreau, C.; Joffre, J.; Saenz, C.; Afonso, J. C.; Portefaix, J. L.; J. Mol. Catal. A: Chem. 2000, 161, 141. Nevertheless, the peak of the Csp2 region became more important along the NiMo generation catalysts. Over 50% of the carbons of the coke deposited on the last generation are aromatic (Table 4). This correlates to the experimental conditions and the quality of the crude diesel (therefore, the original feedstock) processed in each case (Table 1).99 Rana, M. S.; Ancheyta, J.; Sahoo, S. K.; Rayo, P.; Catal. Today 2014, 220-222, 97.,1212 Guichard, B.; Auberger, M. R.; Devers, E.; Legens, C.; Raybaud, P.; Catal. Today 2008, 130, 97.,1414 Guichard, B.; Roy-Auberger, M.; Devers, E.; Rebours, B.; Quoineaud, A. A.; Digne, M.; Appl. Catal. A: Gen. 2009, 367, 1.,1919 Maity, S. K.; Blanco, E.; Ancheyta, J.; Alonso, F.; Fukuyama, H.; Fuel 2012, 100, 17.,3838 Topsoe, H.; Clausen, B. S.; Massoth, F. E.; Hydrotreating Catalysts - Science and Technology, Springer-Verlag: Berlin, 1996. This result also agrees very well with H/C atomic ratio data (Table 3).

Figure 1
13C CP-MAS NMR spectrum of the spent NiMo/Al2O3 catalyst (1979-1986)

Figure 2
13C CP-MAS NMR spectrum of the spent NiMo/Al2O3 catalyst (1993-1998)

Figure 3
13C CP-MAS NMR spectrum of the spent NiMo/Al2O3 catalyst (2003-2008)

Figure 4
13C CP-MAS NMR spectrum of the spent NiMo/Al2O3 catalyst (2008-2011)

Table 4
Aromatic and aliphatic coke content (mol%) derived from peak areas of 13C CP-MAS NMR spectra

The profile of coke deposited on a catalyst surface is not only dependent on its amount (wt.%), but also on its chemical nature. Although the amount deposited is lower (Table 2), the coke of the last NiMo generation catalyst is more refractory due to its higher aromatic character.1919 Maity, S. K.; Blanco, E.; Ancheyta, J.; Alonso, F.; Fukuyama, H.; Fuel 2012, 100, 17.,2525 Afonso, J. C.; Schmal, M.; Fréty, R.; Fuel Process. Technol. 1994, 41, 13.,2828 Afonso, J. C.; Silva, G. C.; Aguiar, R. M.; Stud. Surf. Sci. Catal. 2001, 139, 165.

Textural properties

The last two NiMo generation fresh catalysts present a higher surface area and a larger pore volume than the first ones (Table 5). This is a strategy to increase catalyst activity under ultra-deep HDS conditions.22 Vogelaar, B. M.; Eijsbouts, S.; Bergwerff, J. A.; Heiszwolf, J. J.; Catal. Today 2010, 154, 256.,33 Leyvaa, C.; Ancheyta, J.; Marieyb, L.; Travertb, A.; Maugé, F.; Catal. Today 2014, 220-222, 89.,1212 Guichard, B.; Auberger, M. R.; Devers, E.; Legens, C.; Raybaud, P.; Catal. Today 2008, 130, 97.,1717 Marafi, M.; Al-Sheeha, H.; Al-Omani, S.; Al-Barood, A.; Fuel Process. Technol. 2009, 90, 264.

Table 5
Textural properties of fresh and spent NiMo/Al2O3 catalysts

Both surface area and pore volume of spent catalysts markedly decreased when ultra-deep HDS conditions were employed. Although the amount of coke deposited was lower (Table 2), the amount of foreign elements (V, As, Ca, Fe, Cu, Mn) in these samples increased (Table 2).99 Rana, M. S.; Ancheyta, J.; Sahoo, S. K.; Rayo, P.; Catal. Today 2014, 220-222, 97.,1111 Koh, J. H.; Lee, J. J.; Kim, H.; Cho, A.; Moon, S. H.; Appl. Catal. B: Environ. 2009, 86 176.,2323 Maity, S. K.; Ancheyta, J.; Alonso, F.; Rayo, P.; Fuel Process. Technol. 2013, 106, 453.,2424 Afonso, J. C.; Aranda, D. A. G.; Schmal, M.; Fréty, R.; Fuel Process. Technol. 1995, 42, 3. Besides coke and elements deposition, textural properties are very sensitive to the more severe HDS conditions (that lead to the shortening of the lifetime of the catalysts)3030 Kim, T.; Ali, S. A.; Alhooshani, K.; Park, J. I.; Al-Yami, M.; Yoon, S. H.; Mochida, I.; J. Ind. Eng. Chem. 2013, 19, 1577.

31 Song, C.; Turaga, U. T.; Ma, X.; Encyclopedia of Chemical Processing, Taylor & Francis: New York, 2006, p. 651-661.

32 Yoshimura, Y.; Toba, M.; Farag, H.; Sakanishi, K.; Catal. Surv. Asia 2004, 8, 47.
-3333 Pawelec, B.; Navarro, R. M.; Martin, J. M. C.; Fierro, J. L. G.; Catal. Sci. Technol. 2011, 1, 23. and the quality of crude diesel processed.1212 Guichard, B.; Auberger, M. R.; Devers, E.; Legens, C.; Raybaud, P.; Catal. Today 2008, 130, 97.,1717 Marafi, M.; Al-Sheeha, H.; Al-Omani, S.; Al-Barood, A.; Fuel Process. Technol. 2009, 90, 264.

Characterization of the oxidized catalysts

Loss of volatiles

Data for the first two NiMo generation catalysts (Table 6) agree with literature data for spent catalysts under conventional HDS conditions.2828 Afonso, J. C.; Silva, G. C.; Aguiar, R. M.; Stud. Surf. Sci. Catal. 2001, 139, 165.,2929 Pereira, A. L. S.; Silva, C. N.; Mantovano, J. L.; Afonso, J. C.; Quim. Nova 2011, 34, 145.,3838 Topsoe, H.; Clausen, B. S.; Massoth, F. E.; Hydrotreating Catalysts - Science and Technology, Springer-Verlag: Berlin, 1996. However, loss of volatiles was lower for the two last generations. This is partially explained by the lower amount of coke in these samples (Table 2). However, the amount of remaining sulfur was higher (Table 6). A possible explanation is the oxidation of sulfur to sulfate species, thus reducing the amount of the element eliminated as SO2(g). Metals such as vanadium can catalyze this conversion.3939 Wachs, I. E.; Dalton Trans. 2013, 42, 11762.,4040 Hubaut, R.; Appl. Catal. A: Gen. 2007, 322, 121. To assess this hypothesis 100 mg of an oxidized sample were placed in a 25 mL beaker containing 10 mL of water at 90 ºC under stirring (200 rpm). After 10 min the solid was filtered and some drops of 0.2 mol L-1 Ba(NO3)2 were added to the filtrate. A white precipitate (BaSO4), insoluble in concentrated HCl,4141 Feigl, F.; Spot Tests in Inorganic Analysis, Elsevier: Amsterdam, 1958, chap. 3.,4242 Lurie, J.; Handbook of Analytical Chemistry, 3rd ed., Mir: Moscow, 1978, chap. 3, 6 and 10. was formed, thus confirming the presence of sulfate species in the samples under study.

Table 6
Average mass and sulfur losses of samples oxidized at 500 °C for 3 h

The oxidation of deposited elements in the reduced state (As(III), V(III), Fe(II)),3838 Topsoe, H.; Clausen, B. S.; Massoth, F. E.; Hydrotreating Catalysts - Science and Technology, Springer-Verlag: Berlin, 1996.,3939 Wachs, I. E.; Dalton Trans. 2013, 42, 11762.,4343 Wu, H.; Duan, A.; Zhao, Z.; Qi, D.; Li, J.; Liu, B.; Jiang, G.; Liu, J.; Wei, Y.; Zhang, X.; Fuel 2014, 130, 203. as well as Mo(IV),22 Vogelaar, B. M.; Eijsbouts, S.; Bergwerff, J. A.; Heiszwolf, J. J.; Catal. Today 2010, 154, 256.,3434 Stanislaus, A.; Marafi, A.; Rana, M. S.; Catal. Today 2010, 153, 1.,3535 González-Cortés, S. L.; Rugmini, S.; Xiao, T.; Green, M. L. H.; Rodulfo-Baechler, S. M.; Imbert, F. E.; Appl. Catal. A: Gen. 2014, 475, 270.,3838 Topsoe, H.; Clausen, B. S.; Massoth, F. E.; Hydrotreating Catalysts - Science and Technology, Springer-Verlag: Berlin, 1996. to higher oxidation states during coke removal (As(V), V(V), Fe(III) and Mo(VI)) also explains the lower mass loss for the most recent NiMo generation catalysts.

During oxidation, the temperature of the catalyst bed suddenly rose from ~460 to 900 ºC in about 10 min for the two most recent NiMo generation catalysts, despite the low heating rate (3 ºC min-1). This phenomenon was not observed for the two oldest generation catalysts. These samples only ignited when high rates were employed (10 ºC min-1).77 Valverde Jr., I. M.; Paulino, J. F.; Afonso, J. C.; J. Hazard. Mater. 2008, 160, 310.,2828 Afonso, J. C.; Silva, G. C.; Aguiar, R. M.; Stud. Surf. Sci. Catal. 2001, 139, 165.,4343 Wu, H.; Duan, A.; Zhao, Z.; Qi, D.; Li, J.; Liu, B.; Jiang, G.; Liu, J.; Wei, Y.; Zhang, X.; Fuel 2014, 130, 203. It seems to have a relationship between the aromaticity of coke and the sample ignition: the greater the aromatic character, the highest the temperature of the catalytic bed after ignition. As coke becomes more aromatic, the risk of ignition increases during heating of the coked sample.1212 Guichard, B.; Auberger, M. R.; Devers, E.; Legens, C.; Raybaud, P.; Catal. Today 2008, 130, 97.,1414 Guichard, B.; Roy-Auberger, M.; Devers, E.; Rebours, B.; Quoineaud, A. A.; Digne, M.; Appl. Catal. A: Gen. 2009, 367, 1.,2424 Afonso, J. C.; Aranda, D. A. G.; Schmal, M.; Fréty, R.; Fuel Process. Technol. 1995, 42, 3.,2626 Guichard, B.; Roy-Auberger, M.; Devers, E.; Pichon, C.; Legens, C.; Appl. Catal. A: Gen. 2009, 367, 9.,2828 Afonso, J. C.; Silva, G. C.; Aguiar, R. M.; Stud. Surf. Sci. Catal. 2001, 139, 165.,2929 Pereira, A. L. S.; Silva, C. N.; Mantovano, J. L.; Afonso, J. C.; Quim. Nova 2011, 34, 145. The “hard” coke ignites at higher temperatures than the “soft” one.1212 Guichard, B.; Auberger, M. R.; Devers, E.; Legens, C.; Raybaud, P.; Catal. Today 2008, 130, 97.,1414 Guichard, B.; Roy-Auberger, M.; Devers, E.; Rebours, B.; Quoineaud, A. A.; Digne, M.; Appl. Catal. A: Gen. 2009, 367, 1.,2424 Afonso, J. C.; Aranda, D. A. G.; Schmal, M.; Fréty, R.; Fuel Process. Technol. 1995, 42, 3.,2626 Guichard, B.; Roy-Auberger, M.; Devers, E.; Pichon, C.; Legens, C.; Appl. Catal. A: Gen. 2009, 367, 9.,2929 Pereira, A. L. S.; Silva, C. N.; Mantovano, J. L.; Afonso, J. C.; Quim. Nova 2011, 34, 145.

The aspect of the oxidized samples is quite different from the deactivated ones. After coke removal the color of the oxidized catalyst should be green due to the presence of nickel in its active phase, but samples from the third and fourth generations are reddish in color (Figure 5) due to the presence of iron deposited over their surface in considerable amounts (Table 2).

Figure 5
Aspect of the catalysts from the second (left) to the fourth (right) NiMo generation catalysts before (above) and after (below) oxidation at 500 ºC for 5 h. The reddish color is due to iron deposited over the surface

XRD data

Figure 6 presents the diffractograms of the oxidized catalysts. All samples exhibit low crystallinity. Only ill-defined peaks corresponding to γ-Al2O3 appeared in the diffractograms of the last two spent NiMo generation catalysts. Despite the increase of the aromatic character of the coke in these samples, it appears that coke ignition did not lead to significant crystallization of inorganic components of the catalysts.2929 Pereira, A. L. S.; Silva, C. N.; Mantovano, J. L.; Afonso, J. C.; Quim. Nova 2011, 34, 145. Although our XRD data do not show crystalline phases, other work state the formation of spinel-like compounds (NiAl2O4), molybdates (NiMoO4), phosphates (Ni3(PO4)2) and metasilicates (NiSiO3) when spent hydroprocessing catalysts are subjected to high temperatures (above 800 ºC).4444 Rana, M. S.; Ancheyta, J.; Sahoo, S. K.; Rayo, P.; Catal. Today 2014, 220-222, 97.,4545 Sheeha, H.; Marafi, M.; Raghavan, V.; Rana, M. S.; Ind. Eng. Chem. Res. 2013, 52, 12794.

Figure 6
X-ray diffractograms of the oxidized NiMo/Al2O3 catalyst: 1979-1986 (A); 1993-1998 (B); 2003-2008 (C); 2008-2011 (D)

Acidic leaching

The amount of insoluble matter after leaching with sulfuric acid sharply increased from the second (~1.3 wt.%) to the fourth NiMo catalyst generation (~73 wt.%) (Figure 7). It seems to have a relationship between the amount of insoluble matter in sulfuric acid and the aromaticity of coke: the greater the aromaticity the greater the amount of insoluble matter. Data on Table 7 corroborates data presented in Figure 7. Leaching of elements markedly decreased from the first two generations to the last one. Even those deposited on the catalyst surface (Fe, As, V) were poorly leached from this sample.

Figure 7
Amount (wt.%) of insoluble matter after leaching of pre-oxidized catalysts with 9 mol L-1 H2SO4 (90 ºC, 200 rpm, 70-90 min)

Table 7
Amount of leached elements (wt.%) in 9 mol L-1 H2SO4 (90 ºC, 200 rpm, 70-90 min) after previous oxidation of catalysts (500 ºC, 5 h, 3 ºC min-1)

Coke removal is the most critical parameter to ensure an efficient leaching.2424 Afonso, J. C.; Aranda, D. A. G.; Schmal, M.; Fréty, R.; Fuel Process. Technol. 1995, 42, 3.,2626 Guichard, B.; Roy-Auberger, M.; Devers, E.; Pichon, C.; Legens, C.; Appl. Catal. A: Gen. 2009, 367, 9.,2929 Pereira, A. L. S.; Silva, C. N.; Mantovano, J. L.; Afonso, J. C.; Quim. Nova 2011, 34, 145.,4444 Rana, M. S.; Ancheyta, J.; Sahoo, S. K.; Rayo, P.; Catal. Today 2014, 220-222, 97.,4646 Akcil, A.; Vegliò, F.; Ferella, F.; Okudan, M. D.; Tuncuk, A. Waste Manage. 2015, 45, 420. The catalyst must be pre-oxidized at low heating rates in order to minimize losses of valuable components due to formation of insoluble compounds in the leachant upon coke ignition.77 Valverde Jr., I. M.; Paulino, J. F.; Afonso, J. C.; J. Hazard. Mater. 2008, 160, 310. The low heating rate employed (3 ºC min-1) was adequate to pre-oxidize spent NiMo catalysts from the first and second generations:77 Valverde Jr., I. M.; Paulino, J. F.; Afonso, J. C.; J. Hazard. Mater. 2008, 160, 310.,2828 Afonso, J. C.; Silva, G. C.; Aguiar, R. M.; Stud. Surf. Sci. Catal. 2001, 139, 165. no coke ignition was observed. However, this rate was not able to avoid ignition in samples subjected to ultra-deep HDS. Therefore, coke removal from such samples should be redrawn: very low heating rates, the use of diluted O2 in an inert gas (instead of air) or even grinding of the spent catalyst before oxidation are alternatives to be searched. These points are under investigation in many research centers.4545 Sheeha, H.; Marafi, M.; Raghavan, V.; Rana, M. S.; Ind. Eng. Chem. Res. 2013, 52, 12794.

46 Akcil, A.; Vegliò, F.; Ferella, F.; Okudan, M. D.; Tuncuk, A. Waste Manage. 2015, 45, 420.
-4747 Yang, S.; Adjaye, J.; McCaffrey, W. C.; Nelson, A. E.; J. Mol. Catal. A: Chem. 2010, 321, 83.

If a spent NiMo catalyst contains only Al, Si, and Fe, it can be disposed of in industrial dumps without any special precautions or can be used as alternative raw material (co-processing) in construction materials.4444 Rana, M. S.; Ancheyta, J.; Sahoo, S. K.; Rayo, P.; Catal. Today 2014, 220-222, 97. However, if Ni, As and V accumulated during their use, they must be encapsulated before disposal in order to avoid release of such elements into the environment.4545 Sheeha, H.; Marafi, M.; Raghavan, V.; Rana, M. S.; Ind. Eng. Chem. Res. 2013, 52, 12794. Regeneration, rejuvenation and reuse in less severe hydroprocessing units by cascading before final disposal are not feasible because these elements poison irreversibly the active sites.2323 Maity, S. K.; Ancheyta, J.; Alonso, F.; Rayo, P.; Fuel Process. Technol. 2013, 106, 453.,4646 Akcil, A.; Vegliò, F.; Ferella, F.; Okudan, M. D.; Tuncuk, A. Waste Manage. 2015, 45, 420.,4747 Yang, S.; Adjaye, J.; McCaffrey, W. C.; Nelson, A. E.; J. Mol. Catal. A: Chem. 2010, 321, 83. Metals recovery from spent catalysts is the best alternative to avoid dumping such wastes but new methodologies should developed to overcome challenges such as removal of a highly aromatic coke and leaching of elements deposited on their surface.

CONCLUSIONS

As the feedstock was heavier and dirtier and the HDS conditions were more severe in the same hydrotreater, the textural properties of spent NiMo catalysts were drastically affected, the amount and variety of foreign elements deposited on their surface increased, coke tended to be more aromatic and was susceptible to ignition even under low heating rates. Mass loss was lower for the most recent NiMo generation catalysts due to a combination of three factors: the lower carbon content, the presence of high amounts of residual sulfur and the oxidation of some foreign elements deposited on the catalyst surface.

Leaching of the oxidized catalysts by sulfuric acid under classical experimental conditions was ineffective for those subjected to ultra-deep HDS conditions. This is directly related to coke ignition. Therefore, new pretreatment protocols must be developed because metals leaching is strongly dependent on the reactivity of inorganic compounds present after coke removal.

ACKNOWLEDGMENTS

Tatiana M. Pessanha and Carolina Leão Quintanilha acknowledge Agência Nacional de Petróleo, Gás Natural e Biocombustíveis (ANP) for a fellowship. We are grateful to ANP and CNPq for financial support. We are grateful to LABRMN/IQ-UFRJ (Laboratório de Ressonância Magnética Nuclear) for 13C CP-MAS NMR spectra.

REFERENCES

  • 1
    Rodríguez, E.; Félix, G.; Anchyeta, J.; Trejo, F.; Fuel 2018, 225, 118.
  • 2
    Vogelaar, B. M.; Eijsbouts, S.; Bergwerff, J. A.; Heiszwolf, J. J.; Catal. Today 2010, 154, 256.
  • 3
    Leyvaa, C.; Ancheyta, J.; Marieyb, L.; Travertb, A.; Maugé, F.; Catal. Today 2014, 220-222, 89.
  • 4
    Kohli, K.; Prajapati, R.; Maity, S. K.; Sal, M.; Sharma, B. K.; Fuel 2019, 235, 437.
  • 5
    Torres-Mancera, P.; Anchyeta, J.; Martínez, J.; Fuel 2018, 234, 326.
  • 6
    Wang, L.; Chao, L.; Qu, W.; Xu, S.; Zhang, L.; Peng, J.; Ye, X.; Ultrason. Sonochem. 2018, 49, 24.
  • 7
    Valverde Jr., I. M.; Paulino, J. F.; Afonso, J. C.; J. Hazard. Mater. 2008, 160, 310.
  • 8
    Imam, D. M.; El-Nadi, Y. A.; Hydrometallurgy 2018, 180, 172.
  • 9
    Rana, M. S.; Ancheyta, J.; Sahoo, S. K.; Rayo, P.; Catal. Today 2014, 220-222, 97.
  • 10
    Yang, Y.; Shengming, X.; Li, Z.; Wang, J.; Zhao, Z.; Xu, Z.; J. Hazard. Mater. 2016, 318, 723.
  • 11
    Koh, J. H.; Lee, J. J.; Kim, H.; Cho, A.; Moon, S. H.; Appl. Catal. B: Environ. 2009, 86 176.
  • 12
    Guichard, B.; Auberger, M. R.; Devers, E.; Legens, C.; Raybaud, P.; Catal. Today 2008, 130, 97.
  • 13
    Marchala, C.; Uzioa, D.; Merdrignaca, I.; Barreb, L.; Geantet, C.; Appl. Catal. A: Gen 2012, 411- 412, 35.
  • 14
    Guichard, B.; Roy-Auberger, M.; Devers, E.; Rebours, B.; Quoineaud, A. A.; Digne, M.; Appl. Catal. A: Gen 2009, 367, 1.
  • 15
    Ramirez, S.; Leyva, C.; Ancheyta, J.; Centeno, G.; Fuel 2009, 88, 2311.
  • 16
    Gawel, I.; Bociarska, D.; Biskupski, P.; Appl. Catal. A: Gen 2005, 295, 89.
  • 17
    Marafi, M.; Al-Sheeha, H.; Al-Omani, S.; Al-Barood, A.; Fuel Process. Technol 2009, 90, 264.
  • 18
    Callejas, M. A.; Martınez, M. T.; Blasco, T.; Sastre, E.; Appl. Catal. A: Gen 2001, 218, 181.
  • 19
    Maity, S. K.; Blanco, E.; Ancheyta, J.; Alonso, F.; Fukuyama, H.; Fuel 2012, 100, 17.
  • 20
    Torres-Mancera, P.; Rayo, P.; Ancheyta, J.; Marroquín, G.; Centeno, G.; Alonso, F.; Catal. Today 2014, 220-222, 153.
  • 21
    Yue, Y.; Tiantian, C.; Yong, X.; GuoYong, H.; Wenqiang, W.; Qi, L.; Shengming, X.; Waste Manage 2018, 78, 595.
  • 22
    Wood, J.; Gladden, L. F.; Appl. Catal. A: Gen 2003, 249, 241.
  • 23
    Maity, S. K.; Ancheyta, J.; Alonso, F.; Rayo, P.; Fuel Process. Technol. 2013, 106, 453.
  • 24
    Afonso, J. C.; Aranda, D. A. G.; Schmal, M.; Fréty, R.; Fuel Process. Technol 1995, 42, 3.
  • 25
    Afonso, J. C.; Schmal, M.; Fréty, R.; Fuel Process. Technol 1994, 41, 13.
  • 26
    Guichard, B.; Roy-Auberger, M.; Devers, E.; Pichon, C.; Legens, C.; Appl. Catal. A: Gen 2009, 367, 9.
  • 27
    Vogelaar, B. M.; van Langeveld, A. D.; Eijsbouts, S.; Moulijn, J. A.; Fuel 2007, 86, 1122.
  • 28
    Afonso, J. C.; Silva, G. C.; Aguiar, R. M.; Stud. Surf. Sci. Catal. 2001, 139, 165.
  • 29
    Pereira, A. L. S.; Silva, C. N.; Mantovano, J. L.; Afonso, J. C.; Quim. Nova 2011, 34, 145.
  • 30
    Kim, T.; Ali, S. A.; Alhooshani, K.; Park, J. I.; Al-Yami, M.; Yoon, S. H.; Mochida, I.; J. Ind. Eng. Chem. 2013, 19, 1577.
  • 31
    Song, C.; Turaga, U. T.; Ma, X.; Encyclopedia of Chemical Processing, Taylor & Francis: New York, 2006, p. 651-661.
  • 32
    Yoshimura, Y.; Toba, M.; Farag, H.; Sakanishi, K.; Catal. Surv. Asia 2004, 8, 47.
  • 33
    Pawelec, B.; Navarro, R. M.; Martin, J. M. C.; Fierro, J. L. G.; Catal. Sci. Technol. 2011, 1, 23.
  • 34
    Stanislaus, A.; Marafi, A.; Rana, M. S.; Catal. Today 2010, 153, 1.
  • 35
    González-Cortés, S. L.; Rugmini, S.; Xiao, T.; Green, M. L. H.; Rodulfo-Baechler, S. M.; Imbert, F. E.; Appl. Catal. A: Gen 2014, 475, 270.
  • 36
    Trejo, F.; Rana, M. S.; Ancheyta, J.; Chávez, S.; Fuel 2014, 138, 104.
  • 37
    Moreau, C.; Joffre, J.; Saenz, C.; Afonso, J. C.; Portefaix, J. L.; J. Mol. Catal. A: Chem 2000, 161, 141.
  • 38
    Topsoe, H.; Clausen, B. S.; Massoth, F. E.; Hydrotreating Catalysts - Science and Technology, Springer-Verlag: Berlin, 1996.
  • 39
    Wachs, I. E.; Dalton Trans. 2013, 42, 11762.
  • 40
    Hubaut, R.; Appl. Catal. A: Gen 2007, 322, 121.
  • 41
    Feigl, F.; Spot Tests in Inorganic Analysis, Elsevier: Amsterdam, 1958, chap. 3.
  • 42
    Lurie, J.; Handbook of Analytical Chemistry, 3rd ed., Mir: Moscow, 1978, chap. 3, 6 and 10.
  • 43
    Wu, H.; Duan, A.; Zhao, Z.; Qi, D.; Li, J.; Liu, B.; Jiang, G.; Liu, J.; Wei, Y.; Zhang, X.; Fuel 2014, 130, 203.
  • 44
    Rana, M. S.; Ancheyta, J.; Sahoo, S. K.; Rayo, P.; Catal. Today 2014, 220-222, 97.
  • 45
    Sheeha, H.; Marafi, M.; Raghavan, V.; Rana, M. S.; Ind. Eng. Chem. Res. 2013, 52, 12794.
  • 46
    Akcil, A.; Vegliò, F.; Ferella, F.; Okudan, M. D.; Tuncuk, A. Waste Manage 2015, 45, 420.
  • 47
    Yang, S.; Adjaye, J.; McCaffrey, W. C.; Nelson, A. E.; J. Mol. Catal. A: Chem. 2010, 321, 83.

Publication Dates

  • Publication in this collection
    27 May 2019
  • Date of issue
    2019

History

  • Received
    13 Oct 2018
  • Accepted
    17 Jan 2019
  • Published
    27 Feb 2019
Sociedade Brasileira de Química Instituto de Química, Universidade Estadual de Campinas (Unicamp), CP6154, 13083-0970 - Campinas - SP - Brazil