CeαMn1-αO2 catalysts supported over γ-Al2O3 prepared by modified redox-coprecipitation methods for n-hexane combustion

Abstract

A series of CeαMn1-αO2 catalysts supported on γ-alumina with various molar concentrations of Ce (α, from 0 to 0.90) was synthesized by coprecipitation, applying two different precipitating agents, namely, sodium hydroxide (method 1) and sodium carbonate (method 2), with the use of sodium permanganate as a redox agent for precipitation. XRD profiles of the supported samples revealed the predominant abundance of a typical fluorite crystalline structure. TPR thermograms of supported samples were displaced towards lower temperatures with increasing Mn concentration, in contrast with the bulk samples. The supported Ce-Mn samples exhibited a greater performance in n-hexane elimination than did the corresponding simple oxides. The sample Ce0.33Mn0.67O2 obtained by method 2 presented the best activity, probably due to the enrichment of Ce4+, Mn3+ and Mn4+ surface species, an excess of superficial oxygen species and an easy reducibility as well as the lowest apparent activation energy.

Keywords:
VOC; n-hexane; Ce-Mn; modified-precipitation; alumina


INTRODUCTION

The world is increasingly aware of climate change and global warming, and the signatories of the twenty-first session of the Conference of the Parties (COP 2015, or the “Paris Accord”) have committed to intensify efforts to control carbon dioxide emissions. These reductions in emissions should limit a global temperature increase this century to less than two degrees above preindustrial levels. However, while important, carbon dioxide emissions are not the only large-scale pollution problem resulting from human activity. Volatile organic compounds (VOCs) form a group of chemicals responsible for photochemical smog, and many of them are known to be carcinogenic and teratogenic.11 Ahmad, W.; Noor, T.; Zeeshan, M.; Catal. Commun. 2017, 89, 19. Increasing regulations to control VOC levels, especially in work and home environments, demand the best technologies to control their release.22 Tang, W. X.; Wu, X.; Li, S.; Li, W.; Chen, Y.; Catal. Commun. 2014, 56, 134. Specifically promising is catalytic technology that allows VOCs to be eliminated at temperatures much lower than incineration combustion, making the formation of nitrogen oxides negligible.33 Spivey, J. J.; Ind. Eng. Chem. Res. 1987, 26, 2165.

The application of noble metals as catalysts in VOC combustion is usually limited by their high cost, scarcity and sensitivity at high temperatures. Metal oxides are promising alternatives due to their high activity and resistance to poisoning.33 Spivey, J. J.; Ind. Eng. Chem. Res. 1987, 26, 2165. In particular, the manganese oxides have been well studied in VOC combustion due to the chemical characteristic of manganese to the structure of multivalent oxides and their important ability to collect bulk oxygen.44 Jirátová, K.; Kovanda, F.; Balabánová, J.; Kšírová, P.; Catal. Today 2018, 304, 165.

5 Hu, J.; Li, W. B.; Liu, R. F.; Catal. Today 2018, 314, 147.

6 Hinokuma, S.; Shimanoe, H.; Kawabata, Y.; Kiritoshi, S.; Araki, K.; Machida, M.; Catal. Commun. 2018, 105, 48.

7 Morales, M. R.; Yeste, M. P.; Vidal, H.; Gatica, J. M.; Cadus, L. E.; Fuel 2017, 208, 637.
-88 Tang, W.; Li, W.; Li, D.; Liu, G.; Wu, X.; Chen, Y.; Catal. Lett. 2014, 144, 1900. The formation of MnOx species has shown high performance in the total combustion of different model organic molecules including o-xylene,99 Wu, Y.; Shi, S.; Yuan, S.; Bai, T.; Xing, S.; Appl. Surf. Sci. 2019, 479, 1262. methane,1010 Wang, X.; Yiu, L.; Zhang, Y.; Zhang, T.; Chang, H.; Zhang, Y.; Jiang, L.; Appl. Catal., B 2018, 229, 52. ethyl methyl ketone,1111 Picasso, G.; Gutiérrez, M.; Pina, M. P.; Herguido, J.; Chem. Eng. J. 2007, 126, 119.,1212 Lerner, E. C.; Peluso, M. A.; Sambeth, J.; Thomas, H.; J. Rare Earths 2016, 34, 675. 1,2-dichlorobenzene,1313 Tang, A.; Xu, L.; Yang, X.; Jia, Y.; Zhang, Y.; Catal. Commun. 2016, 82, 41. n-hexane,1414 Picasso, G.; Cruz, R.; Sun Kou, M. R.; Mater. Res. Bull. 2015, 70, 621. toluene1515 Lu, H.; Kong, X.; Huang, H.; Zhou, Y.; Chen, Y.; J. Environ. Sci. 2015, 32, 102.,1616 Morales, M. R.; Barbero, B. P.; Cadús, L. E.; Catal. Lett. 2011, 141, 1598. and ethanol,1717 Matějová, L.; Topka, P.; Kaluža, L.; Pitkäaho, S.; Ojala, S.; Gaálová, J.; Keiski, R. L.; Appl. Catal., B 2013, 54, 142. among others.

n-Hexane is a solvent commonly used in the chemical industry, but its application in the manufacturing of drugs has been restrained due to its ongoing toxicity. OSHA1818 https://www.osha.gov/dts/chemicalsampling/data/CH_245400.html, accessed on March 2020.
https://www.osha.gov/dts/chemicalsamplin...
and NIOSH1919 https://www.cdc.gov/niosh/npg/npgd0322.html, accesed on March 2020.
https://www.cdc.gov/niosh/npg/npgd0322.h...
have regulated its emission to the atmosphere as a hazard, setting an exposure limit of 500 ppm for 8 h. In previous works, some catalysts based on CeMnOx and CeZrOy were prepared in a membrane configuration1111 Picasso, G.; Gutiérrez, M.; Pina, M. P.; Herguido, J.; Chem. Eng. J. 2007, 126, 119. and in a packed-bed reactor with bulk samples1414 Picasso, G.; Cruz, R.; Sun Kou, M. R.; Mater. Res. Bull. 2015, 70, 621. for the elimination of n-hexane. The catalytic tests revealed a strong influence of the Mn4+ and Ce4+ species over the surface, which had the ability of storing surface oxygen through redox reactions following a Langmuir- Hinshelwood mechanism. While redox processes clearly played a substantial role in the catalytic performance, some questions related to the preparation variables and their influence on the formation of the active phase require deeper discussion as is suggested by some authors.2020 Li, T. Y.; Chiang, S. J.; Liaw, B. J.; Chen, Y. Z; Appl. Catal., B 2011, 103, 143. With this aim, some factors were taken into consideration in this work, namely, the dispersion effect using a conventional γ-alumina support and the effect of preparation variables proposed via modifying precipitation agents and calcination conditions as well as their influence on the catalytic behavior of alumina-supported Ce-Mn oxides in the abatement of n-hexane.

EXPERIMENTAL

Catalyst preparation

A series of CeαMn1-αO2 catalysts was synthesized modifying the relative molar concentration of cerium from α=0.33 to 0.9 by coprecipitation using different precipitating agents and redox conditions. Prior to the preparation of the catalysts, the γ-Al2O3 support (99.9%, SIGMA-ALDRICH) was heated to 135 ºC in a closed balloon reactor under vacuum to eliminate any remaining water, which was verified by the differences in weights before and after the thermal treatment. Moreover, the alumina-supported simple oxides were prepared for α=0 (CeO2) and for α=1 (MnOx) following each method of preparation, which were the following:

Method 1

In method 1, the catalysts were prepared by suspensioncoprecipitation with a redox reaction step using a solution of 0.2 mol L-1 NaOH (MERCK) as a precipitating agent. This solution was added at 0.5 mL min-1 to a beaker containing a suspension of γ-Al2O3 with a 0.5 mol L-1 solution of metallic precursors of a mixture of Ce and Mn nitrates and potassium permanganate with a molar ratio (m/m) of 5:3:2, respectively, at 60 ºC under constant stirring to achieve a pH up to 10.5.2121 Xingfu, T.; Yonggang, L.; Xiumin, H.; Yide, X.; Huaqing, Z.; Jianguo, W.; Wenjie, S.; Appl. Catal., B 2006, 62, 265.,2222 Liu, X.; Lu, J.; Qian, K.; Huang, W.; Luo, M. A.; J. Rare Earths 2009, 27, 418. The solid was aged for 2 h and washed 5 times using deionized water to avoid the presence of the remaining alkali ions. Finally, the solid was dried at 110 ºC for 12 h and calcined for 6 h at 500 ºC under air atmosphere (heating rate=5 ºC/min). The mechanism of preparation corresponds to the mixed precipitationredox route developed over the support γ-Al2O3:2323 Arena, F.; Trunfio, G.; Negro, J.; Spadaro, L.; Mater. Res. Bull. 2008, 43, 539.

(1) MnO 4 + 3 e + 2 H 2 O MnO 2 + 4 OH
(2) Mn 2 + + 4 OH MnO 2 + 2 e + 2 H 2 O
(3) Ce 3 + + 4 OH CeO 2 + e + 2 H 2 O

The composition of the catalyst was achieved by the controlled dose of the different starting solutions2323 Arena, F.; Trunfio, G.; Negro, J.; Spadaro, L.; Mater. Res. Bull. 2008, 43, 539. through the following equations:

(a) 3 mol MnVII = 2 mol MnII + mol CeIII
(b) mol MnVII + mol MnII / mol CeIII = mol Mn / mol Ce
(c) mol MnVII + mol MnII + mol CeIII = 1

The equations correspond to the (a) charge balance, (b) molar balance and (c) compositional balance of the catalyst.

Method 2

This method was similar to method 1, but using a solution of 0.2 mol L-1 Na2CO3 as a precipitating agent,2424 Meng, M.; Tu, Y.; Ding, T.; Sun, Z.; Zhang, L; Int. J. Hydrogen Energy 2011, 36, 9139.,2525 Li, J. G.; Ikegami, T.; Wang, Y.; Mori, T.; J. Am. Ceram. Soc. 2002, 85, 2376. which was introduced to a solution of Ce and Mn nitrate precursors with potassium permanganate with the molar ratio of 5:3:2, respectively, at 50 ºC, increasing the pH level to 10.5 under vigorous stirring. Then, the solid was aged for 2 h and washed until removal of Na+. The final solid was dried at 110 ºC for 12 h, heated at a heating rate of 5 ºC/ min and finally calcined at 500 ºC for 6 h in air. The mechanistic route of the process was the following:

(4) MnO 4 + 3 e + 2 H 2 O MnO 2 s + 4 OH
(5) Mn 2 + + CO 3 2 MnCO 3 s
(6) 2 Ce 3 + + 3 CO 3 2 Ce 2 CO 3 3 s
(7) x / 2 Ce 2 CO 3 3 s + 1 x MnCO 3 s Ce X Mn 1 X O 2 s + CO 2 g

Table 1 lists the alumina-supported mixed catalysts (CeαMn1-αO2) prepared in this work. The mixed oxide supported catalysts were denoted as CMx-y, in which “x” is assigned to α, i.e., it corresponds to the nominal metallic ratio Ce/(Ce+Mn), and “y” indicates the method of preparation. The simple oxide supported samples were designated as C-x or M-x, in which “x” corresponds to the method of preparation. The samples were distributed into three groups in order to compare the method of preparation and the metal composition for the catalysts prepared by methods 1 and 2 due to their higher performances in n-hexane elimination.

Table 1
Alumina-supported mixed catalysts based on CeαMn1-αO2 (40% metallic charge) prepared in this work

Characterization of catalysts

The crystal structures of the catalysts were studied by X-ray diffraction (XRD). The characterization was performed using a RIGAKU Miniflex diffractometer, whose operating parameters were as follows: 15 mA, 30 kV, Cu Kα radiation (λ = 1.5418 Å), Ni filter, and range of angle scanning from 5 to 80º (step size = 0.10º and step time = 2.5 s). The identification of the crystal phases was made by application of the PDF2 database from ICDD. The Scherrer equation was used to estimate the average crystallite sizes from the peak of the highest intensity in the diffractograms, and the Gauss function was used to fit the selected diffraction peaks.

The texture of the catalysts was analyzed by the technique of sorption of N2, performed at liquid nitrogen temperature with a Micromeritics GEMINI VII-2390t system. Before the analysis, the catalysts were pretreated in a He stream at 250 ºC for 2 h. The BET method and the t-plot procedure were applied to evaluate the total specific surface area and the microporous area of catalyst, respectively. The method of BJH (Barrett, Joyner, and Halenda) from the adsorption at a P/P0 near 0.98 was used to measure the total pore volume as well as the pore size distribution and the mean pore size (using the desorption branch of the isotherm).

The redox properties of the catalysts were studied by temperature-programmed reduction (H2-TPR) and temperature-programmed desorption of oxygen (O2-TPD), performed with a MICROMERITICS CHEMISORB 2720 Pulse Chemisorption System. As a rule, the TPR tests were carried out in a U-tube quartz reactor in which 25 mg of the sample was deposited under a stream of 10% H2/He and warmed from the room temperature to 900 ºC at a heating rate of 10 ºC min-1. A standard quantity of Ag2O was used to calibrate the H2-consumption. The estimation of oxidation state of Mn has been made considering only the MnO as the oxide present at the end of all the TPR tests. The O2-TPD tests were performed in a reactor using 100 mg of the sample pretreated with a helium purge (25 mL min-1) for 30 minutes at 200 ºC and followed by an injection of a flow of 10% O2 in He (25 mL min-1) for 30 minutes at 500 ºC. Then, under a gas stream of 10% He in N2, the catalysts were cooled to room temperature. Finally, another helium purge (25 mL min-1) was performed to remove O2 molecules, heating the furnace at a rate of 10 ºC min-1 from 30 ºC to 850 ºC. A thermal conductivity detector (TCD) was employed to quantify the loss of O2.

The chemical surface analysis of samples was evaluated by X-ray photoelectron spectroscopy (XPS). The spectrometer used was VG 200 R with a 120 W-powered X-ray source of Al Kα1 (hν = 1486.6 eV). The XPS spectra were recorded on small Inox holders with a vacuum system, heating in the presence of a residual pressure of 10-6 mbar at 573 K for 5 h. Furthermore, the spectra were collected at 200 eV pass energy for survey spectra and 50 eV pass energy for narrow scans. Afterwards, the catalysts were introduced into the analysis chamber in which a residual pressure of 5.10-9 mbar was inserted. High-resolution spectra of Ce 3d, Mn 2p, C 1s and O 1s and a survey spectrum were acquired for each catalyst, each with multiple scans in order to achieve good signal-to-noise ratios. The binding energies of Cu 2p3/2 (932.6 eV) andAu 4f7/2 (84.0 eV) were used as a calibration reference of the spectrometer. The binding energy of the C 1s signal of adventitious carbon at 284.8 eV was used to correct possible generated charge effects of spectra of the catalysts. The fitting of the experimental spectra with ±0.1 eV of precision of the binding energy values was achieved through a combination of Gaussian and Lorentzian lines (G/L = 90/10), subtracting the sigmoidal background. The most intensity ratios, normalized by atomic sensitivity factors, were used to display the atomic ratios of samples.

Catalytic tests

The experimental setup was detailed in a previous work.1414 Picasso, G.; Cruz, R.; Sun Kou, M. R.; Mater. Res. Bull. 2015, 70, 621. The reaction equipment involved a quartz packed-bed reactor operating at atmospheric pressure, whose dimensions were 9 mm internal diameter and 600 mm height. The main experimental parameters of the testing such as the gas WHSV (weight hourly space velocity) and particle size were tuned to underestimate the internal and external diffusion effects. The temperature of the reaction tests was recorded by a thermocouple inserted into the catalyst bed where 100 mg of sample was mixed with 200 mg of Pyrex glass beads to control hot spots, all deposited over a quartz frit. The feed section of the experimental equipment included two gas flows: synthetic air (Praxair, 99.99%) used as diluent gas and the other gas being air saturated with n-hexane (MERCK, 99.9%), formed from n-hexane saturators at ice temperature and regulated pressure. The experimental conditions used for all the catalytic tests were 100 cm3 STP.min-1 for the total flow rate, 2000 ppmV for the initial VOC concentration and 80 h-1 for the WHSV. The reaction products of the catalytic tests were monitored by a gas chromatograph (GC-HP450) equipped with a column HP-INNOWax of 30 m × 0.32 mm i.d. and connected to an FID detector for VOC recording and a methanizer to follow the CO2 emissions. The conversion was measured as VOCs consumed (%) after the reaction. In all the catalytic tests, only complete combustion species were obtained. The 50% and 95% conversion temperatures in the ignition curves (T50% and T95%, respectively) were used for the evaluation of the catalytic activities of the samples.

RESULTS AND DISCUSSION

Textural analysis and X-ray diffraction (XRD)

From Table 1, an increase in cerium composition of mixed samples led to an increased specific surface area, in accordance with similar works.1414 Picasso, G.; Cruz, R.; Sun Kou, M. R.; Mater. Res. Bull. 2015, 70, 621.,1717 Matějová, L.; Topka, P.; Kaluža, L.; Pitkäaho, S.; Ojala, S.; Gaálová, J.; Keiski, R. L.; Appl. Catal., B 2013, 54, 142. The isotherms of alumina-supported mixed oxides catalysis prepared by method 1 were of type II, as was observed for the samples CM0.5-1 and CM0.67-1 with 40% metallic charge (Figure 1).

Figure 1
Isotherms of supported mixed catalysts prepared by method 1 with 40% metallic charge and with different metallic molar proportions, a: CM0.50-1, b: CM0.67-1, c: γ-Al2O3

Furthermore, all the adsorption isotherms of the samples prepared by method 2 were also classified as type II, corresponding to macroporous material. All samples showed a type H3 hysteresis loops, corresponding to the formation of slit-shaped pores. In addition, an increase in metallic charge leads to an increased specific surface area (data not shown). Taking into account that the supported samples with a metallic load of 40% (no matter the method of preparation) allowed species with higher specific BET surface areas to be obtained and achieved better performance in the combustion of n-hexane, this optimal metallic charge was studied in more detail in further tests.

The diffractogram of the mixed oxide samples with 40% metallic charge compared with their simple oxide counterparts is shown in Figure 2. As is observed, the simple cerium oxides showed distinguishable separated defined peaks corresponding to the fluorite phase whose crystallinity decreased slightly with decreasing metallic charge over the support, probably due to the better dispersion achieved in the metal-rich samples. The diffractogram of manganese presented peaks attributed to Mn oxide, with a major presence of Mn3O4 (PDF2 # 24e0734), very similar to the results obtained in previous works.1111 Picasso, G.; Gutiérrez, M.; Pina, M. P.; Herguido, J.; Chem. Eng. J. 2007, 126, 119.,1414 Picasso, G.; Cruz, R.; Sun Kou, M. R.; Mater. Res. Bull. 2015, 70, 621. The alumina-supported mixed samples presented a profile similar to the fluorite phase corresponding to alumina-supported ceria with 40% charge, but with wider peaks and lower sizes of crystallites (Table 2), showing a higher dispersion of the metallic phase over the surface of the support. No peaks assigned to MnOx were observed, i.e., the addition of any quantity of cerium to manganese completely affects the initial multiphase structure of MnOx, very similar to that observed in bulk conditions.1414 Picasso, G.; Cruz, R.; Sun Kou, M. R.; Mater. Res. Bull. 2015, 70, 621. In this case, a small displacement of the peaks addressed to the high diffraction angles is observed, most likely because of the introduction of Mnn+ species with lower ratio in the lattice (Mn2+ = 0.83 Å, Mn3+ = 0.645 Å and Mn4+ = 0.53 Å) to the Ce4+ sites (1.01 Å). The formation of only one structure suggests the formation of mixed phases, which appeared to be clarified due to the observed lowering of the cell parameter of supported mixed oxides with respect to the corresponding pure ceria (Table 2). Regarding supported samples prepared by method 1 and method 2 (Figure 1S), those with low cerium content (<0.5) presented the same phases. The XRD profiles of the manganese-supported samples prepared by method 1 differ from those of method 2 because the majority phase is now monoclinic Mn5O8 (PDF2 # 39e1218) and cubic Mn2O3 (PDF2 # 73e1826) instead of tetragonal Mn3O4 (PDF2 # 24e0734), as has also been observed by some authors.2626 Qi, K.; Xie, J.; Fang, D.; Liu, X.; Gong, P. F.; Li, F.; He, F.; Mater. Chem. Phys. 2018, 209, 10.

Figure 2
XRD patterns of the supported mixed samples with 40% metallic charge prepared by method 2, a: C-2, b: CM0.67-2, c: CM0.50-2, d: CM0.33-2 and e: M-2
Table 2
Comparison of structural parameters studied from XRD analysis for simple and mixed oxide supported samples, prepared by method 2

Temperature programmed reduction (TPR)

The characterization by H2-TPR analysis was applied to the alumina-supported mixed oxide samples prepared by different methods. The support γ-Al2O3 presented a consumption of H2 at reduction temperatures over than 1000 ºC; consequently, the reduction peaks observed in the H2-TPR thermograms are exclusively owing to the reduction of the metallic species. In the profile corresponding to C-2 (40%) presented in Figure 3, two reduction peaks are depicted, at 516 ºC and 690 ºC, which are consistent with the reduction of nonstoichiometric superficial Ce4+ species (tetrahedrally coordinated with the oxygen atoms) and the reduction of Ce4+ to Ce3+ in the bulk phase, respectively.1717 Matějová, L.; Topka, P.; Kaluža, L.; Pitkäaho, S.; Ojala, S.; Gaálová, J.; Keiski, R. L.; Appl. Catal., B 2013, 54, 142. The first peak was shifted to the higher temperatures with respect to that observed in the bulk phase in previous work,1414 Picasso, G.; Cruz, R.; Sun Kou, M. R.; Mater. Res. Bull. 2015, 70, 621. probably due to the interaction with the γ-Al2O3 support. The reduction of Ce4+ to Ce3+ (bulk) is typical of the fluorite crystalline structure,1414 Picasso, G.; Cruz, R.; Sun Kou, M. R.; Mater. Res. Bull. 2015, 70, 621. which confirms the XRD diffractograms, as already discussed.

Figure 3
H2-TPR profiles of alumina-supported mixed samples prepared by different methods and with a 40% metallic charge, a: C-2, b: CM0.5-2, c: CM0.5-1, d: M-2

The H2-TPR profile of M-2 (40%) shown in Figure 3 exhibits three reduction peaks positioned at temperatures near 320, 360 and 443 ºC, ascribed to the successive reduction steps from MnO2 to MnO as reported by some authors:2727 Terribile, D.; Trovarelli, A.; Leitenburg, C.; Primavera, A.; Dolcetti, G.; Catal. Today 1999, 47, 133.,2828 Gil, A.; Gandía, L. M.; Korili, S. A.; Appl. Catal., A 2004, 274, 229.

(8) MnO 2 α Mn 2 O 3 Mn 3 O 4 MnO

As discussed in previous work,1414 Picasso, G.; Cruz, R.; Sun Kou, M. R.; Mater. Res. Bull. 2015, 70, 621. the stoichiometry of bulk manganese oxide calculated from the consumption of H2 of the corresponding profile in Figure 3 is in good agreement with the presence of Mn2O3, Mn3O4 and MnO2. In this case, the reduction temperatures were displaced towards higher temperatures than those observed in the bulk phase,1414 Picasso, G.; Cruz, R.; Sun Kou, M. R.; Mater. Res. Bull. 2015, 70, 621. which is compatible with the influence of the metal-support interactions. All these data are in good agreement with the XRD diffractograms of Figure 2.

The H2-TPR thermograms of a series of catalysts CM0.5 (40%) prepared by methods 1 and 2 are presented in Figure 3. All the profiles are very similar, no matter the method of preparation, and exhibit one broad defined peak, situated at 240-250 ºC, and a shoulder at 410-415 ºC. According to some authors,2929 Xingyi, W.; Qian, K.; Dao, L.; Appl. Catal., B 2009, 86, 166. the first peak could be assigned to the reduction of superficial Mn4+ species situated over Ce lattice positions, and the second peak could be attributed to the reduction of Mn3+ species. The profile of the CM0.5-2 (40%) differs from the others due to the presence of a broader peak at the first reduction temperature, probably due to the major consumption of H2, revealing an easier reducibility caused by the better positions of Mn4+ species over the surface. Moreover, in this sample, a minor peak situated at 411 ºC confirmed that the Mn2O3 particles are quickly transformed, remaining only as the Mn4+ species, exhibiting a broader peak, most likely owing to a much higher dispersion of the active phase.3030 Arena, F. G.; Trunfio, G.; Negro, J.; Spadaro, L.; Appl. Catal., B 2008, 85, 40.

The influence of metal composition on the reduction properties of the catalysts from method 2 (40%) is depicted in Figure 2S. The thermograms were shifted to lower temperatures with decreasing Ce/Mn ratio due to the enrichment in Mn. The higher area of the first peak in the TPR, corresponding to both CM0.5-2 and CM0.33-2, reveals the major consumption of H2 in relation to the predominant concentration of Mn4+ reduced to Mn3+ species. The best reducibility in the catalysts CM0.33-2 led to a better performance in the total oxidation of n-hexane, so it was studied in greater detail. The results of the O2-TPD analysis (Figure 3S) showed that the labile species of oxygen are in the highest concentration in the mixed samples and that method 2 led to catalysts with a higher quantity of labile oxygen, which was desorbed at low temperatures.

X-ray photoelectron spectroscopy (XPS)

Table 3 shows the normalized absolute areas from the XPS spectrum (in CPS.eV) of a series of CM0.33 (40%) alumina-supported catalysts synthesized by methods 1, 2 as well as the corresponding catalysts prepared by method 2, CM-0.33-2 (30%), CM-0.33-2 (20%) and the simple oxides C-1 (40%), M-1 (40%), prepared by method 1. To determine the atomic percentages, the atomic ratios were normalized using the corresponding sensitivity factors.

Table 3
Normalized absolute areas of a series of CM0.33 alumina-supported catalysts prepared by methods 1 and 2 and the corresponding simple oxides prepared by method 1

The signals corresponding to the Mn 2p3/2 XPS spectrum (Figure 4) of a series of catalysts were deconvoluted by a fitting process after subtraction of the background, using XPS commercial software. The compounds MnO, ZnMn2O4 and MgNiMnO4 were used as a references of the binding energies and FWHM values of the Mn2+ (641.1 eV, 2 eV), Mn3+ (641.9 eV, 2.7 eV) and Mn4+ (644.0 eV, 4 eV).3131 Töpfer, J.; Feltz, A.; Gräf, G.; Hackl, B.; Raupach, L.; Weissbrodt, P.; Phys. Status Solidi A 1992, 134, 405.

32 Huang, Z.; Zhou, W.; Ouyang, C.; Wu, J.; Zhang, F.; Huang, J.; Chu, J.; Sci. Report 2015, 5, 10899.
-3333 Rao, T.; Shen, M.; Jia, L.; Hao, J.; Wang, J.; Catal. Commun. 2007, 8, 1743. The Mn 2p core level in pure MnOx (M-1, 40%) allowed finding a Mn cation distribution expressed as a percentage ratio [Mn2+]: [Mn3+]: [Mn4+] equal to 19.9: 53.8: 26.2, from which it was inferred that Mn3+ and Mn4+ were the majority species (Table 3). Similar results were obtained for the samples of a series of CM-0.33 catalysts prepared by different methods (Figure 4). As is observed, in the sample CM0.33-2, prepared by method 2, Mn4+ species are in a greater proportion than in the samples prepared by method 1. Additionally, the low surface percentage of Mn over the support (Table 3) indicates a good dispersion of the active phase. In the case of the CM0.33 series catalysts prepared by method 2 and with different metallic loads, as is observed in Table 4, the total percentage of Mn4+ and Mn3+ increases as the metallic load increases.

Figure 4
Mn 2p3/2 XPS spectra: deconvoluted peaks of samples prepared by different methods of preparation. Peaks are centered at 641.1 eV (Mn 2+), 641.9 eV (Mn3+) and 644 eV (Mn4+), a: M-1, b: CM0.33-1, c: CM0.33-2
Table 4
Percentage of O, Ce and Mn species of a series of CM0.33 alumina-supported catalysts prepared by methods 1 and 2 and the corresponding simple oxides prepared by method 1

The O 1s spectra of the mixed oxides (Figure 5) were deconvoluted into two contributions, namely, surface-adsorbed oxygen in the BE range of 531 to 531.6 eV, related to defect surface oxygen species such as O22− or O (usually denoted as Oβ), and the corresponding BE range of 528.9–530 eV, usually ascribed to lattice oxygen (Oα).34-37 During the deconvolution of the different samples, the FWHM value was maintained constant in the range of ±0.1 eV. The O 1s spectrum of C-1 (40%) presented two maxima centered at 529.5 and 531.6 eV, attributed to lattice oxygen and surface oxygen, respectively; meanwhile, the O 1s core level of oxygen of M-1 (40%) was situated at 530.2 and 531.5 eV. For C-1 (40%), the percentage of superficial oxygen abundance was 82.2, and for M-1 (40%), 95.3.

Figure 5
O 2p XPS spectra: deconvoluted peaks with a 40% metallic charge for different methods of preparation, a: M-1, b: CM0.33-1, c: CM0.33-2 and d: C-1

According to Table 4, sample CM0.33-2 (40%) presented a higher relative enrichment of adsorbed oxygen (100%) than did the other analogous samples prepared by method 1 (82.1%) (Figure 5). This enrichment in surface oxygen in alumina-supported mixed samples of Ce-Mn is in accordance with the data discussed by Arena et al.,3030 Arena, F. G.; Trunfio, G.; Negro, J.; Spadaro, L.; Appl. Catal., B 2008, 85, 40. in which the formation of very reactive electrophilic oxygen species was ascribed to the “Mn←O” electron-transfer processes. Moreover, the increase in the metal load over the support from 20 to 40% had no significant effect on the percentage of surface oxygen, as is observed in Table 4 with the CM0.33 sample series prepared by method 2.

In all samples, the Ce 3d spectra, deconvoluted (Figure 4S) for sample CM0.33-2, presented multiplets v and u, according to the notation of Burroughs et al.3838 Burroughs, P.; Hamnett, A.; Orchard, A. F.; Thornton, G.; J. Chem. Soc. 1976, 17, 1686. These multiplets corresponded to the spin-orbital division 3d5/2 and 3d3/2 of the 3d internal level, which was approximately 18.6 eV in accordance with other investigations.3939 Bêche, E.; Charvin, P.; Perarnau, D.; Abanades, S.; Flamant, G.; Surf. Interface Anal. 2008, 40, 264. Moreover, the FWHM was fixed as a constant value during the deconvolution of each multiplet peak. Each spin-orbital division could be composed of three peaks in the case of CeO2 and only two peaks in the case of Ce2O3.4040 Romeo, M.; Bak, K.; El Fallah, J.; Le Normand, F.; Hilaire, L; Surf. Interface Anal. 1993, 20, 508. Therefore, it is necessary to analyze 10 peaks if taking into account both spin-orbital divisions. This analysis was made by a detailed adjustment of the data to Gaussian curves.4040 Romeo, M.; Bak, K.; El Fallah, J.; Le Normand, F.; Hilaire, L; Surf. Interface Anal. 1993, 20, 508.

41 Fujimori, A.; Phys. Rev. B 1983, 28, 2281.

42 Seah, M. P. In Practical Surface Analysis; Briggs, D., Seah, M. P., eds.; John Wiley & Sons: Chichester. 1983, ch. 1.

43 Paparazzo, E.; Superlattices Microstruct. 2017, 105, 216.
-4444 Si, W.; Wang, Y.; Peng, Y.; Li, X.; Li, K.; Li, J.; Chem. Commun. 2015,51, 14977. As is shown in Table 4, the sample CM0.33-2 (40%) prepared by method 2 achieved the lowest value of total Ce concentration compared to the rest of the samples, CM0.33-1 (40%). This observation could indicate a good dispersion of the active phase over the support. Moreover, the percentage of Ce4+ in all samples ranged from 81.6 to 86.5. Most likely, according to some authors, the content of Ce3+ reported in this work is due to the reduction of Ce4+ that takes place during the XPS analysis.

Catalytic activity of the catalysts in the combustion of n-hexane

The combustion of n-hexane performed without a catalyst indicated the absence of activity at the working temperatures. The following experimental variables were considered in all the catalytic tests: method of preparation, the metallic load of the active phase over the support and the composition of metal loading over the support.

Influence of the metallic load

The activity of alumina-supported Ce-Mn prepared with different metallic loads and with an equimolar molar composition is shown in Figure 6. As is shown, the mixed oxide samples with 40% metallic load presented more activity than did the samples with 20 and 50%, all prepared by method 2. This behavior is probably related to the higher presence of Mn3+ and Mn4+ species as shown in the XPS analysis (Figure 4) and its higher specific surface area relative to that of the other equimolar mixed samples with the same metallic load (Table 1). The reactive oxygen species (O, OH, O22−, and O2) greatly favor the combustion of volatile organic compounds.88 Tang, W.; Li, W.; Li, D.; Liu, G.; Wu, X.; Chen, Y.; Catal. Lett. 2014, 144, 1900. The presence of these species is evidenced by the BE value of the oxygen atom in these samples (Table 4).

Figure 6
Ignition curves of mixed oxide alumina-supported catalysts with different amounts of metallic charge prepared by method 2, a: CM0.50-2 (20%), b: CM0.50-2 (40%), c: CM0.50-2 (50%)

Influence of the method of preparation

The activity of the Ce-Mn alumina-supported samples prepared by different methods and with 40% metallic charge is shown in Figure 5S. As is observed, all the mixed oxides samples present more activity than did the simple oxide supported samples. The activity decreases in the following order: CM0.50-2 > CM0.50-1 > M-1 > C-1. It could be inferred that the coprecipitation-redox method of preparation with carbonate allowed the formation and development of the active and selective sites. This behavior of the samples with the best catalytic activity could be assigned to the higher abundance of Mn4+ species, surface oxygen, abundance of labile oxygen species and a higher reducibility.

Effect of metallic composition of the catalysts prepared by method 2

Since the catalysts prepared by method 2 presented a better activity, some further test experiments were performed to study the effect of the metal composition (Figure 7). As was observed, the catalyst CM0.33-2 showed a higher activity than that of the catalysts CM0.5-2 and CM0.67-2. The H2-TPR thermograms of the sample CM0.33-2 (Figure 2S) presented higher reducibility relative to that of the other samples. XPS spectra confirmed the highest presence of electrophilic oxygen in this sample, usually responsible of the total combustion of n-hexane.

Figure 7
Influence of metal composition of the catalysts with a 40% metallic charge on the activity in the combustion of n-hexane, a: CM0.33-2, b: CM0.50-2 and c: CM0.67-2

The Arrhenius plots allowed determination of the values of Ea for the catalysts prepared with different metal compositions (Figure 8).

Figure 8
Arrhenius plots used to compare the activity of the catalyst prepared by method 2 with a 40% metallic charge, a: CM0.33-2, b: CM0.50-2 and c: CM0.67-2

The lower activation energy is usually related with the activity of the catalysts and the rate velocity of the reaction, so a better catalyst is expected. The lower the Ea value is (43 kJ/mol), the easier the hexane can be oxidized, and this value was achieved for the sample CM0.33-2 with 40% metallic load. The high catalytic activity can be associated with a better reducibility, high content of Mn4+ and Mn3+ species as well as the best synergistic interaction between Ce and Mn, achieved through the method of preparation with sodium carbonate.

CONCLUSIONS

The supported Ce-Mn samples showed better activities in n-hexane combustion than did the simple oxides. The sample Ce0.33Mn0.67O2 prepared by method 2 showed the highest activity, probably due to the enrichment of Mn3+ and Mn4+ surface species as well as the relatively favorable reducibility related to the corresponding supported single oxides. The alumina-supported Ce-Mn sample prepared by suspension-coprecipitation with the redox reaction with potassium permanganate and Na2CO3 used as a precipitating agent appeared to have the best performance. The sample Ce0.33Mn0.67O2 precipitated with sodium carbonate exhibited the highest activity for n-hexane combustion, probably due to the better Ce-Mn interaction between the surface species Ce4+, Mn3+ and Mn4+ with the contribution of the metal-support interaction. This sample also showed the highest reducibility and an abundance of superficial oxygen species, which favored the total combustion of n-hexane, revealing the synergistic effect of the Ce-Mn metal interaction.

ACKNOWLEDGMENTS

The authors want to express their sincerest gratitude to the Research Management Office of National University of Engineering of Lima-Peru (OGI) for the financial support for this work and Dr. Silvia Irusta from Universidad de Zaragoza by the XPS measurements and assisting spectra identification. R. C. wishes to acknowledge FONDECYT (Convenio nº208-2015-FONDECYT) for his Master scholarship.

REFERENCES

  • 1
    Ahmad, W.; Noor, T.; Zeeshan, M.; Catal. Commun. 2017, 89, 19.
  • 2
    Tang, W. X.; Wu, X.; Li, S.; Li, W.; Chen, Y.; Catal. Commun. 2014, 56, 134.
  • 3
    Spivey, J. J.; Ind. Eng. Chem. Res. 1987, 26, 2165.
  • 4
    Jirátová, K.; Kovanda, F.; Balabánová, J.; Kšírová, P.; Catal. Today 2018, 304, 165.
  • 5
    Hu, J.; Li, W. B.; Liu, R. F.; Catal. Today 2018, 314, 147.
  • 6
    Hinokuma, S.; Shimanoe, H.; Kawabata, Y.; Kiritoshi, S.; Araki, K.; Machida, M.; Catal. Commun. 2018, 105, 48.
  • 7
    Morales, M. R.; Yeste, M. P.; Vidal, H.; Gatica, J. M.; Cadus, L. E.; Fuel 2017, 208, 637.
  • 8
    Tang, W.; Li, W.; Li, D.; Liu, G.; Wu, X.; Chen, Y.; Catal. Lett. 2014, 144, 1900.
  • 9
    Wu, Y.; Shi, S.; Yuan, S.; Bai, T.; Xing, S.; Appl. Surf. Sci. 2019, 479, 1262.
  • 10
    Wang, X.; Yiu, L.; Zhang, Y.; Zhang, T.; Chang, H.; Zhang, Y.; Jiang, L.; Appl. Catal., B 2018, 229, 52.
  • 11
    Picasso, G.; Gutiérrez, M.; Pina, M. P.; Herguido, J.; Chem. Eng. J. 2007, 126, 119.
  • 12
    Lerner, E. C.; Peluso, M. A.; Sambeth, J.; Thomas, H.; J. Rare Earths 2016, 34, 675.
  • 13
    Tang, A.; Xu, L.; Yang, X.; Jia, Y.; Zhang, Y.; Catal. Commun. 2016, 82, 41.
  • 14
    Picasso, G.; Cruz, R.; Sun Kou, M. R.; Mater. Res. Bull. 2015, 70, 621.
  • 15
    Lu, H.; Kong, X.; Huang, H.; Zhou, Y.; Chen, Y.; J. Environ. Sci. 2015, 32, 102.
  • 16
    Morales, M. R.; Barbero, B. P.; Cadús, L. E.; Catal. Lett. 2011, 141, 1598.
  • 17
    Matějová, L.; Topka, P.; Kaluža, L.; Pitkäaho, S.; Ojala, S.; Gaálová, J.; Keiski, R. L.; Appl. Catal., B 2013, 54, 142.
  • 18
    https://www.osha.gov/dts/chemicalsampling/data/CH_245400.html, accessed on March 2020.
    » https://www.osha.gov/dts/chemicalsampling/data/CH_245400.html
  • 19
    https://www.cdc.gov/niosh/npg/npgd0322.html, accesed on March 2020.
    » https://www.cdc.gov/niosh/npg/npgd0322.html
  • 20
    Li, T. Y.; Chiang, S. J.; Liaw, B. J.; Chen, Y. Z; Appl. Catal., B 2011, 103, 143.
  • 21
    Xingfu, T.; Yonggang, L.; Xiumin, H.; Yide, X.; Huaqing, Z.; Jianguo, W.; Wenjie, S.; Appl. Catal., B 2006, 62, 265.
  • 22
    Liu, X.; Lu, J.; Qian, K.; Huang, W.; Luo, M. A.; J. Rare Earths 2009, 27, 418.
  • 23
    Arena, F.; Trunfio, G.; Negro, J.; Spadaro, L.; Mater. Res. Bull. 2008, 43, 539.
  • 24
    Meng, M.; Tu, Y.; Ding, T.; Sun, Z.; Zhang, L; Int. J. Hydrogen Energy 2011, 36, 9139.
  • 25
    Li, J. G.; Ikegami, T.; Wang, Y.; Mori, T.; J. Am. Ceram. Soc. 2002, 85, 2376.
  • 26
    Qi, K.; Xie, J.; Fang, D.; Liu, X.; Gong, P. F.; Li, F.; He, F.; Mater. Chem. Phys. 2018, 209, 10.
  • 27
    Terribile, D.; Trovarelli, A.; Leitenburg, C.; Primavera, A.; Dolcetti, G.; Catal. Today 1999, 47, 133.
  • 28
    Gil, A.; Gandía, L. M.; Korili, S. A.; Appl. Catal., A 2004, 274, 229.
  • 29
    Xingyi, W.; Qian, K.; Dao, L.; Appl. Catal., B 2009, 86, 166.
  • 30
    Arena, F. G.; Trunfio, G.; Negro, J.; Spadaro, L.; Appl. Catal., B 2008, 85, 40.
  • 31
    Töpfer, J.; Feltz, A.; Gräf, G.; Hackl, B.; Raupach, L.; Weissbrodt, P.; Phys. Status Solidi A 1992, 134, 405.
  • 32
    Huang, Z.; Zhou, W.; Ouyang, C.; Wu, J.; Zhang, F.; Huang, J.; Chu, J.; Sci. Report 2015, 5, 10899.
  • 33
    Rao, T.; Shen, M.; Jia, L.; Hao, J.; Wang, J.; Catal. Commun 2007, 8, 1743.
  • 34
    Bensalem, A.; Bozon-Verduraz, F.; Delamar, M.; Bugli, G.; Appl. Catal., A 1995, 121, 81.
  • 35
    Holgado, J. P.; Munuera, G.; Espinós, J. P.; Gonzalez-Elipe, A. R.; Appl. Surf. Sci. 2000, 158, 164.
  • 36
    Deng, W.; Dai, Q.; Lao, Y.; Shi, B.; Wang, X.; Appl. Catal., B 2016, 181, 848.
  • 37
    Wu, M.; Wang, X.; Dai, Q.; Gu, Y.; Li, D.; Catal. Today 2010, 158, 336.
  • 38
    Burroughs, P.; Hamnett, A.; Orchard, A. F.; Thornton, G.; J. Chem. Soc. 1976, 17, 1686.
  • 39
    Bêche, E.; Charvin, P.; Perarnau, D.; Abanades, S.; Flamant, G.; Surf. Interface Anal. 2008, 40, 264.
  • 40
    Romeo, M.; Bak, K.; El Fallah, J.; Le Normand, F.; Hilaire, L; Surf. Interface Anal. 1993, 20, 508.
  • 41
    Fujimori, A.; Phys. Rev. B 1983, 28, 2281.
  • 42
    Seah, M. P. In Practical Surface Analysis; Briggs, D., Seah, M. P., eds.; John Wiley & Sons: Chichester. 1983, ch. 1.
  • 43
    Paparazzo, E.; Superlattices Microstruct. 2017, 105, 216.
  • 44
    Si, W.; Wang, Y.; Peng, Y.; Li, X.; Li, K.; Li, J.; Chem. Commun. 2015,51, 14977.

Publication Dates

  • Publication in this collection
    10 June 2020
  • Date of issue
    Apr 2020

History

  • Received
    24 June 2019
  • Accepted
    14 Jan 2020
  • Published
    31 Mar 2020
Sociedade Brasileira de Química Instituto de Química, Universidade Estadual de Campinas (Unicamp), CP6154, 13083-0970 - Campinas - SP - Brazil
E-mail: quimicanova@sbq.org.br