Cellulose acetate-Al2O3 hybrid material coated with N-Propyl-1,4-diazabicyclo [2.2.2] octane chloride: preparation, characterization and study of some metal halides adsorption from ethanol solution

Abstracts

The preparation, characterization as well as the adsorption properties of MCl n (M= Fe(III), Co(II) and Cu(II)) from ethanol solutions by the new hybrid material cellulose acetate /Al2O3 coated with N-propyl-1,4 diazabicyclo [2.2.2] octane chloride group are described. The diamine is bonded to the cellulose acetate /Al2O3 surface by Al-O-Si covalent bonds and thus, the material obtained is chemically very stable and shows high adsorption capacity in adsorbing MCl n from ethanol solutions. When the material (designated as sigma-L+Cl-) comes into contact with the metal halide solutions, the salts diffuse into the substrate-solution interface as neutral species and are fixed in the form of the anionic complexes. The latter are held near the surface due to the electrostatic interactions with the positively charged centers ~L+. The adsorption capacities of the material (t, in mmol g-1) and its affinities to the metal halides were determined by analyzing the adsorption isotherms with the help of the model of fixed polydentate centers. The constants of the adsorption equilibria (beta, in L mol-1) were used as the quantitative characteristics of affinity. For the FeCl3 adsorption equilibrium <IMG SRC="/img/revistas/jbchs/v16n2/en_a04img01.gif">the specific concentration of the sorption centers <IMG SRC="/img/revistas/jbchs/v16n2/en_a04img02.gif">is equal to 1.42 and log beta11 = 3.14. The adsorption of CoCl2 and CuCl2 (MCl2) is described in a more complicated way: <IMG SRC="/img/revistas/jbchs/v16n2/en_a04img03.gif"> The following values of parameters were obtained: <IMG SRC="/img/revistas/jbchs/v16n2/en_a04img04.gif" > or = 0.20 and 0.115; log beta21 = 4.08 and 3.3 for CoCl2 and CuCl2 respectively.

N-propyl-1,4-diazabicyclo [2.2.2] octane chloride; Al2O3 coated cellulose acetate; chemically modified cellulose acetate; metal halide adsorption; heterogeneous equilibrium constant


A preparação, bem como as propriedades de adsorção de MCl n (M=Fe(III), Co(II) e Cu(II)) de soluções etanólicas são descritas para um novo material híbrido acetato de celulose /Al2O3 recoberto com cloreto de N-propil-1,4 diazabiciclo [2.2.2] octano. A diamina está ligada à superfície do acetato de celulose/Al2O3 pela ligação covalente Al-O-Si e então, o material obtido é quimicamente muito estável e apresenta elevada capacidade de adsorção de MCl n de solução etanólica. Quando o material (designado como sigma-L+Cl-) entra em contacto com soluções do haleto metálico, os sais difundem na interface substrato-solução como espécies neutras e são fixadas na forma de complexos aniônicos. Estes são presos à superfície devido às interações eletrostáticas com a carga positiva dos centros ~L+. As capacidades de adsorção do material (t, em mmol g-1) e as duas afinidades pelo haletos metálicos foram determinadas analisando-se as isotermas de adsorção com o auxílio de um modelo de centros polidentados fixos. As constantes de equilíbrio da adsorção (beta, em mmol L-1) foram usadas como características de afinidade. Para o FeCl3, ao equilíbrio de adsorção <IMG SRC="/img/revistas/jbchs/v16n2/en_a04img01.gif">a concentração específica dos centros de adsorção <IMG SRC="/img/revistas/jbchs/v16n2/en_a04img02.gif">é igual a 1,42 e 0,115; log beta11= 3,14. A adsorção de CoCl2 e CuCl2 (MCl2) é descrita de uma forma mais complexa: <IMG SRC="/img/revistas/jbchs/v16n2/en_a04img03.gif"> Os seguintes valores dos parâmetros foram obtidos: <IMG SRC="/img/revistas/jbchs/v16n2/en_a04img04.gif" > ou = 0,20 e 0,115; log beta21= 4,08 e 3,3, respectivamente para CoCl2 e CuCl2.


ARTICLE

Cellulose acetate-Al2O3 hybrid material coated with N-Propyl-1,4-diazabicyclo [2.2.2] octane chloride. Preparation, characterization and study of some metal halides adsorption from ethanol solution

Gislene SplendoreI; Edilson V. BenvenuttiII; Yuriy V. KholinIII; Yoshitaka Gushikem* * e-mail: gushikem@iqm.unicamp.br , I

IInstituto de Quimica, Universidade Estadual de Campinas, CP 6154, 13084-971 Campinas - SP, Brazil

IIInstituto de Química, Universidade Federal do Rio Grande do Sul, 91501-970 Porto Alegre - RS, Brazil

IIIChemical Faculty, V.N. Karazin Kharkov National University, 4 Svoboda Square, Kharkov 61077, Ukraine

ABSTRACT

The preparation, characterization as well as the adsorption properties of MCln (M= Fe(III), Co(II) and Cu(II)) from ethanol solutions by the new hybrid material cellulose acetate /Al2O3 coated with N-propyl-1,4 diazabicyclo [2.2.2] octane chloride group are described. The diamine is bonded to the cellulose acetate /Al2O3 surface by Al–O–Si covalent bonds and thus, the material obtained is chemically very stable and shows high adsorption capacity in adsorbing MCln from ethanol solutions. When the material (designated as s-L+Cl-) comes into contact with the metal halide solutions, the salts diffuse into the substrate-solution interface as neutral species and are fixed in the form of the anionic complexes. The latter are held near the surface due to the electrostatic interactions with the positively charged centers ~L+. The adsorption capacities of the material (t, in mmol g-1) and its affinities to the metal halides were determined by analyzing the adsorption isotherms with the help of the model of fixed polydentate centers. The constants of the adsorption equilibria (b, in L mol-1) were used as the quantitative characteristics of affinity. For the FeCl3 adsorption equilibrium the specific concentration of the sorption centers is equal to 1.42 and log b11 = 3.14. The adsorption of CoCl2 and CuCl2 (MCl2) is described in a more complicated way:

The following values of parameters were obtained: = 0.20 and 0.115; log b21 = 4.08 and 3.3 for CoCl2 and CuCl2 respectively.

Keywords: N-propyl-1,4-diazabicyclo [2.2.2] octane chloride, Al2O3 coated cellulose acetate, chemically modified cellulose acetate, metal halide adsorption, heterogeneous equilibrium constant

RESUMO

A preparação, bem como as propriedades de adsorção de MCln (M=Fe(III), Co(II) e Cu(II)) de soluções etanólicas são descritas para um novo material híbrido acetato de celulose /Al2O3 recoberto com cloreto de N-propil-1,4 diazabiciclo [2.2.2] octano. A diamina está ligada à superfície do acetato de celulose/Al2O3 pela ligação covalente Al-O-Si e então, o material obtido é quimicamente muito estável e apresenta elevada capacidade de adsorção de MCln de solução etanólica. Quando o material (designado como s-L+Cl-) entra em contacto com soluções do haleto metálico, os sais difundem na interface substrato-solução como espécies neutras e são fixadas na forma de complexos aniônicos. Estes são presos à superfície devido às interações eletrostáticas com a carga positiva dos centros ~L+. As capacidades de adsorção do material (t, em mmol g-1) e as duas afinidades pelo haletos metálicos foram determinadas analisando-se as isotermas de adsorção com o auxílio de um modelo de centros polidentados fixos. As constantes de equilíbrio da adsorção (b, em mmol L-1) foram usadas como características de afinidade. Para o FeCl3, ao equilíbrio de adsorção a concentração específica dos centros de adsorção é igual a 1,42 e 0,115; log b11= 3,14. A adsorção de CoCl2 e CuCl2 (MCl2) é descrita de uma forma mais complexa:

Os seguintes valores dos parâmetros foram obtidos: = 0,20 e 0,115; log b21= 4,08 e 3,3, respectivamente para CoCl2 e CuCl2.

Introduction

Cellulose and cellulose acetate are frequently used to prepare composite materials since they present many intrinsic advantages such as low cost, availability, biodegradability and easy handling.1 In native form they show good thermal stability up to 473 K and a high chemical resistance to treatment with almost all commonly used solvents. The polymer is relatively inert because the hydroxyl groups, which are responsible for the majority of the reactions with organic and inorganic reagents, are involved into inter- and intramolecular hydrogen bonding.2,3

In order to make cellulose acetate more reactive, the surface modified composites have been prepared with many metal oxides such as TiO2,4,5 ZrO2,6 Fe2O37 and Nb2O5.8 As these oxides behave as good Lewis acids, the coated celluloses have been used in separation processes9 for enzyme immobilization,10 to prepare semi-permeable membranes11 and to support electroactive chemical species for use as potentiometric sensors.12

The hybrid organic-inorganic material, Cel/Al2O3, is of particular interest. In this material aluminum oxide can be obtained in a highly dispersed form on the fiber surface with a good degree of adhesion.12 In this material, the surface Al–OH groups can react easily with reagents containing terminal Si–OH groups forming a very stable Al–O–Si bonds.13,14

This work reports the preparation and characterization of cellulose acetate-alumina, Cel/Al2O3, hybrid organic-inorganic material coated with N-propyl-1,4-diazabicyclo [2.2.2] chloride. The material obtained was furthermore applied in adsorption of MCln (M= Co(II), Fe(III) and Cu(II)) from ethanol solutions.

Experimental

Preparation of Cel/Al2O3. 10 g cellulose acetate (Aldrich: 39.7 wt% acetyl content; see the structure and numbering in Figure 1) was immersed in a solution containing a mixture of 37 g of acetone and 50 g of glacial acetic acid. The mixture was stirred for 8 h until resulting in a viscous homogeneous syrup (solution A). In a separated flask, 7 g of aluminum isopropoxyde (Aldrich) was dissolved in a smallest possible volume of trifluoroacetic acid (about 1 mL) and then added to solution A. The content of solution A was slowly added, under vigorous stirring, in distilled water (about 2 L) whose pH was previously adjusted to around 10 with ammonium hydroxide. The fibers of the material obtained were separated from the solution by filtration and washed with distilled water until the effluent solution achieved pH 7. The fiber was washed with dry ethanol and the residual solvent pumped off in a vacuum line at pressure about 10-3 torr. The material obtained is hereafter designated as Cel/Al2O3.


Modification of Cel/Al2O3. according to the procedure previously described by us15,16 and slightly modified in the present work, about 6 g of pure1,4-diazabicyclo[2.2.2]octane was dissolved in 50 mL of dry toluene and 10 mL of 3-chloropropyltrimethoxysilane (Aldrich) was added. The solution was stirred at 383 K under dry nitrogen atmosphere for 2 h. The solvent was pumped off under vacuum and the remaining oily product was dissolved in 50 mL of ethanol and 20 g of Cel/Al2O3 was added and the solvent was slowly evaporated at 353 K.

The reactions involved in the preparation procedures can be represented by the equations 1 and 2, where s= Cel/ºAlOH and ºAlOH is the aluminol groups of alumina dispersed on the cellulose acetate surface.

Chemical analyses. The amount of alumina incorporated into the Cel/Al2O3 matrix was determined by igniting 0.2 g of the material at 1173 K for 3h. The residue was weighed as Al2O3. The amount of diamine bonded to propyl group (II) was determined by titrating the ionized chloride with the standard AgNO3 0.01 mol L-1 solution by the potentiometric method.

Infrared spectra

The infrared spectra of the materials for samples (2 wt%) in KBr pellets were obtained between 4000 and 400 cm-1 on a Bomem FTIR MB series spectrophotometer.

Adsorption isotherms

The adsorption isotherms of FeCl3, CoCl2 and CuCl2 from the ethanol solutions were measured at 298.0 ± 0.5 K. The precise weights of the material (approximately 0.1 g) were immersed in 50 mL of MCln ethanol solutions of variable concentrations. The mixtures were stirred for 3h and the amounts of the metal halides in solutions after sorption were determined by complexometric titration using the standard edta 0.01 mol L-1 solution. The amounts of the adsorbed metals, Nf (in mol g-1), were determined by applying the equation Nf=(Na-Ns)/m, where Na is the initial amount of metal in solution phase (mole), Ns is the amount of metal in solution after sorption (mole) and m is the mass of the adsorbent (g).

The 13C NMR spectra of the solid products were obtained by CP MAS technique on a Bruker AC 300P spectrometer. The following conditions were used: pulses sequences with contact time of 1 ms with 2s interval and acquisition time of 60 ms. Tetramethylsilane was used as reference to calibrate the chemical shift.

Results and Discussion

Characterization of the material

The concentration of alumina incorporated in Cel/Al2O3 was 13.8 wt%. The degree of attached organic molecule in (II), determined by N elemental analysis, was N= 4,1 wt% or 1.46 mmol g-1 (quantity of diamine per gram of the material). Titration of the ionized chloride by the standard AgNO3 solution gave the estimate 1.32 mmol g-1.

Figure 2 shows the infrared spectra of (I) (Figure 2a), (II) (Figure 2c) and cellulose acetate (Figure 2b).




The marked peak at 1100 cm-1 (Figure 2a) is assigned to the asymmetric Si–O stretching mode.17,18 This band peak is shifted to 1070 cm-1 (Figure 2c) after the coating reaction with (I). This shift is presumably due to the Si–O–Al bond formation indicating that compound (I) is covalently bonded to the Cel/Al2O3 surface. The spectrum of cellulose acetate is also shown (Figure 2b) for comparison. As the interaction of (I) with Cel/Al2O3 involves only the free ºAlOH groups on the cellulose modified surface, vibrational bands due to the cellulose matrix are not affected in (II).

Figure 3 shows the 13C NMR spectra of (I), (II) and cellulose acetate. In Table 1 the chemical shift values and the respective assignments are summarized. The peaks at d 53 and 45, assigned to the diamine Cd and Ce respectively for (I) and (II), do not show any significant change. This indicates that free nitrogens in the diamine groups bonded to the Cel/Al2O3 matrix do not interact with the polar unreacted ºAlOH groups. Usually basic nitrogen atoms, included in amines or diamines attached to Cel/Al2O3 matrices, interact strongly with the polar surface groups.20 In the present case as one nitrogen is positively charged, the opposite nitrogen is expected to have the basicity considerably lowered.


Adsorption isotherms and constants of the adsorption equilibria

Figures 2-4 show the adsorption isotherms for FeCl3, CoCl2 and CuCl2 from the ethanol solution on material (II) at 298 K.

The paramagnetic and spectroscopic measurements21 gave no evidence that the free nitrogen atom in fixed diamine interacts directly with the metal atoms and the species in which the nitrogen atom are included into the inner coordination sphere are formed. On the contrary, it was shown that metal chlorides may be immobilized on the surface in the form of the anionic chlorocomplexes that are electrostatically attracted by the positively charged surface groups22. Hence, it was supposed that the adsorption of FeCl3 is due to the reaction

where the solid surface (II) is abbreviated as s-L+Cl-, while in the case of CoCl2 and CuCl2 the surface species (s-L+)2 [MCl4]2- (M = Co or Cu) are formed.

The numerical analysis of the adsorption isotherms makes it possible both to test the hypothesis on the mechanism of adsorption and to characterize the adsorption equilibria quantitavely. As the methodology of the simulation and the computational approach were recently described elsewhere,23,24 only a few comments will be made here.

In the simplest case the adsorption process may be represented as follows:

where S denotes the neutral metal chloride, is the adsorption center and is the surface complex, b is the constant of the adsorption equilibrium. According to this scheme any species (particularly, Cl–) do not pass into solution. If both the effects of the surface energetic heterogeneity and the neighboring interactions are absent, the adsorption equilibrium (equation 4) is described by the Langmuir equation:

where Nfº [] is the specific concentration of the adsorbed species S, mol g-1; tQ is the specific concentration of the sorption centers, mol g-1; [S] is the equilibrium concentration of S in solution, mol L-1. Equation 5 is easily transformed into the linear one:25

where D = Nf / [S] is the distribution ratio (L g-1). The linear character of the plot (1/D) vs. [S] proves visually the validity of the assumptions made.

In order to have a quantitative description of the adsorption at the solid-solution interface, fitting of the isotherms by the Langmuir equation (method I) and fitting of the inverse distribution coefficients (method II) were used to obtain the calculated adsorption capacities tQ and the equilibrium constants b.

In method I, the unknown parameters, tQ and b, were found by minimization of the criterion:

where Nf, calc = . As usually, the adequacy of the models was tested with the use of the chi-square criterion.23,24

In method II, the linear least-squares method was applied to equation 6, and the target parameters tQ and b were found from the calculated regression coefficients.

The calculations have demonstrated that the model tested fits the experimental adsorption isotherm in error of 2.5-5% that corresponds to the level of the random errors. In Figures 4a, 5 and 6 the solid lines present the adsorption isotherms simulated on the base of results obtained by method I. Figure 4b shows the linearized Langmuir equation, by applying equation 6, and illustrates the FeCl3 adsorption, for which the correlation coefficient r = 0.99 was obtained. For CoCl2 and CuCl2 the correlation coefficients were 0.99 and 0.98 respectively and thus the graphics presenting the linear plots are not shown.





The numerical values of the target parameters tQ and b, obtained by the both computational methods, have coincided with each other in the limits of errors of their determination that also corroborates the validity of the approach.

While fixed at the surface, CoCl2 and CuCl2 are transformed into the anions [CoCl4]2- and [CuCl4]2- each of them binds two monocharged diamine entities. It may seem that in such case the adsorption process should be represented by the scheme

But this contradicts to the model of equilibrium expressed by equation 4, where one sorption center binds one metal chloride entity. The contradiction is easily overcome with the help of the model of fixed polyndentate centers.26 According to it, the surface of the material is considered as the assemblage of centers, and each center contains several attached functional groups. Hence, the adsorption of MCl2 (M = Co or Cu) may be described by the model of fixed bidentate centers in the following way:

where the first index at b points to the size of the polyndentate center while the second one corresponds to the number of metal chloride entities bound by each center. Thus, the tQ values, calculated from the CoCl2 and CuCl2 adsorption isotherms, correspond to pairs of the attached nitrogen containing groups rather than single ones.

The results of calculations are summarized in Table 2. For the FeCl3 adsorption tQ denotes the specific concentration of the adsorption centers s–L+–Cl- and the equilibrium constant is b11. For the CoCl2 and CuCl2 adsorption the specific concentrations of the active pairs of the attached groups, t{s-L+Cl–}2 , are presented, while the equilibrium constants are b21.

The calculated tQ values show that for FeCl3 this value is much higher than those calculated for CoCl2 and CuCl2. This trend in consistent with reaction represented by equations 3 and 9 where the species formed on the substrate surface are FeCl4-, CoCl42- and CuCl42-. The values of equilibrium constants are not so different being slightly higher for adsorption of CoCl2. The adsorption capacities tQ are also dependent on the stability constants of each species [MCln+m]m- since more stable is the anionic complex more strongly it will bind to the surface by electrostatic nature bonding. Unfortunately, data on stability constants of these species in ethanol solutions are scarce and not available for using in the present case.

Conclusions

The new hybrid material cellulose/Al2O3 coated with N-propyl-1,4 diazabicyclo [2.2.2] octane chloride group is very stable and show high adsorption capacity in adsorbing MCln from ethanol solution, presenting the following decreasing order: FeCl3 >> CoCl2 >CuCl2. The results obtained are consistent with diffusion of MCln as neutral species into the substrate/solution interface and formation of the [MCln+m]m- anionic complex bound on the surface by electrostatic interaction. There are no evidences that any covalent interaction between the free nitrogen of the diamine with the metal halide is occurring.

Acknowledgments

Y.G. is indebted to FAPESP for financial support (grant N0 00/11103-5) and for an undergraduate student fellowship for G.S. Financial support from CNPq/Pronex is also acknowledged. Y.K. is grateful to the Ukrainian Ministry of Education and Science and V.N. Karazin Kharkov National University for the financial support through Project 15-15-00 "Quantitative characteristics of complexation processes in heterogeneous and micro-heterogeneous media".

Received: August 21, 2003

Published on the web: February 17, 2005

  • 1. Gushikem, Y.; Toledo, E.A. In Polymer Interfaces and Emulsions; Esumi, K., ed., Marcel Dekker: NY, 1999, ch. 13, p. 509.
  • 2. Shisonok, M. V; Gert, E. V.; Filanchuk, T.I.; Kaptutskii, F. N.; J. Appl. Chem. 1987, 60, 1086.
  • 3. Ivanova, N. Y.; Korolenko, E. A.; Korolik, E. V.; Zhbankov, R. G.; J. Appl. Spectrosc. 1989, 52, 847.
  • 4. da Silva, L.R.D.; Gushikem, Y., Gonçalves, M.C.; Rodrigues, U. P.; de Castro S. C.; J. Appl. Polym. Sci 1995, 58, 166.
  • 5. Ohmori, Y.; Kurokawa, Y.; J. Biotechnology 1994, 33, 205.
  • 6. Rodrigues, U.P.; Gushikem, Y.; Fujiwara, F.Y.; de Castro, S.C., Torriani, I.C.L.; Cavalcanti, L.P.; Langmuir 1994, 10, 4357.
  • 7. Chatterjee, S.; Sarkar, S.; Bhattacharyya, S.N.; Polymer 1993, 34, 1979.
  • 8. Gushikem, Y.; Campos, E.A.; J. Braz. Chem. Soc 1998, 9, 273.
  • 9. da Silva, L.R.D.; Gushikem, Y.; Peixoto, C.R.M.; Rodrigues, U. P.; Quim. Nova 1995, 8, 337.
  • 10. da Silva, L.R.D.; Gushikem, Y.; Kubota, L.T.; Colloids Surf. B 1996, 6, 309.
  • 11. Rodrigues, U. P.; Gushikem, Y.; Gonçalves, M.C.; Cachichi, R.C.; de Castro, S.C.; Chem. Mater 1996, 8, 1375.
  • 12. Alfaya, R.V.S.; Gushikem, Y.; J. Colloid Interface Sci 1999, 213, 438.
  • 13. Lazarin, A.M.; Gushikem, Y.; de Castro, S.C.; J. Mater. Chem 2000, 10, 2526.
  • 14. Fujiwara, S.T.; Gushikem, Y.; Alfaya, R.V.S.; Colloids Surf. A 2001, 178, 135 .
  • 15. Arenas, L.T.; Langaro, A.; Gushikem, Y.; Moro, C.C.; Benvenutti, E.V.; Costa, T.M.H.; J. Sol-gel Sci. Technol 2003, 28, 51.
  • 16. Arenas, L.T.; Aguirre, T.A.S.; Langaro, A.; Gushikem, Y.; Benvenutti, E.V.; Costa, T.M.H.; Polymer 2003, 44, 5521.
  • 17. Flanigen, E.M.; Khatami, H.; Szymanski, H.A.; Advances in Chemistry Series (Gould, R.F., ed.) 1971, 101, 201.
  • 18. Marques, A.N.L.; Monteiro, J.L.F.; Pastore, H.O.; Micropor. Mesopor. Mater 1999, 32, 131.
  • 19. Masuda, K.; Adachi, M.; Hirai, A.; Yamamoto, H.; Kaji, H.; Horii, F.; Solid State Nucl. Magn. Reson 2003, 23, 198.
  • 20. Zaitsev, V.N.; Kholin, Y.V.; Gorlova, E.Y.; Khristenko, I.V.; Anal. Chim. Acta 1999, 379, 11.
  • 21. Gerloch, M.; Manning, M.R.; Inorg. Chem 1981, 20, 1051.
  • 22. Alfaya, R.V.S.; Fujiwara, S.T.; Gushikem, Y.; Kholin, Y.V.; J. Colloid Interface Sci. 2004, 269, 32.
  • 23. Lazarin, A.M.; Landers, R.; Kholin, Y.V.; Gushikem, Y.; J. Colloid Interface Sci 2002, 254, 31.
  • 24. Lazarin, A.M.; Borgo, C.A.; Gushikem, Y.; Kholin, Y.V.; Anal. Chim Acta 2003, 477, 305.
  • 25. Adamson, A.W.; Physical Chemistry of Surfaces, 5th ed., Wiley: N.Y., 1990.
  • 26. Kudryavtsev, G.V.; Milchenko, D.V.; Yagov, V.V.; Lopatkin, A.A.; J. Colloid Interface Sci. 1990, 140, 114.
  • *
    e-mail:
  • Publication Dates

    • Publication in this collection
      24 May 2005
    • Date of issue
      Apr 2005

    History

    • Accepted
      17 Feb 2005
    • Received
      21 Aug 2003
    Sociedade Brasileira de Química Instituto de Química - UNICAMP, Caixa Postal 6154, 13083-970 Campinas SP - Brazil, Tel./FAX.: +55 19 3521-3151 - São Paulo - SP - Brazil
    E-mail: office@jbcs.sbq.org.br