Physical-Mechanical Properties of Bulk Fill Composites Submitted to Biodegradation by Streptococcus mutans

Abstract

The aim of this study was to evaluate the Streptococcus mutans biofilm influence on the roughness (Ra), gloss (GU), surface hardness (KHN) and flexural strength (FS) of high viscosity bulk fill composites. Filtek Bulk Fill (FBF), Tetric N Ceram Bulk Fill (TNC), X-tra fil Bulk Fill (XF) and Filtek Z350 (FZ) were used. Ten discs of each composite were prepared for Ra, KHN and GU and 20 bars for the FS. After 24 h, specimens were polished and initial analyzes performed. Samples were sterilized and subjected to biodegradation for 7 days and final analyzes performed. Representative samples of each group were evaluated in Scanning Electron Microscope. Data were submitted to ANOVA two factors and Tukey test. XF presented the highest values (p<0.05) of Ra before and after biodegradation (0.1251; 0.3100), and FZ (0.1443) the lowest after biodegradation (p<0.05). The highest GU values (p<0.05) were observed for FZ (71.7; 62) and FBF (69.0; 64.6), and the lowest (p<0.05) for TNC (61.4; 53.3) and XF (58.5; 53.5), both before and after biodegradation. For KHN the highest values were obtained by XF (151.7; 106), and the (p< 0.05) lowest values for TNC (62.2; 51.8), both before and after biodegradation. The highest values (p<0.05) of FS were observed for FZ (127.6) and the lowest (p<0.05) for TNC (86.9); after biodegradation, XF (117.7) presented the highest (p<0.05) values compared to TNC and FZ.” In conclusion, biodegradation increased Ra and decreased GU and KHN for all. Concerning FS, degradation provided a significant decreased value only for FZ.

Key Words:
biodegradation; composite resin; Streptococcus mutans; mechanical properties

Resumo

O objetivo deste estudo foi avaliar a influência do biofilme de S. mutans na rugosidade (Ra), brilho (GU), dureza superficial (KHN) e resistência à flexão (FS) de compósitos de Bulk Fill de alta viscosidade. Foram utilizados Filtek Bulk Fill (FBF), Tetric N Ceram Bulk Fill (TNC), X-tra fil Bulk Fill (XF) e Filtek Z350 (FZ). Dez discos de cada compósito foram preparados para Ra, KHN e GU e 20 barras para o FS. Após 24 h, os espécimes foram polidos e as análises iniciais realizadas. As amostras foram esterilizadas e submetidas a biodegradação por 7 dias e as análises finais foram realizadas. Amostras representativas de cada grupo foram avaliadas no Microscópio Eletrônico de Varredura. Os dados foram submetidos à ANOVA dois fatores e teste de Tukey. XF apresentou os maiores valores (p<0,05) de Ra antes e após a biodegradação (0,1251; o00,3100) e FZ (0,1443) os menores após a biodegradação (p<0,05). Os maiores valores de GU (p<0,05) foram observados para FZ (71,7; 62) e FBF (69,0; 64,6), e os mais baixos (p<0,05) para TNC (61,4; 53,3) e XF (58,5; 53,5), ambos antes e depois da biodegradação. Para KHN, os valores mais altos foram obtidos por XF (151,7; 106), e os (p<0,05) valores mais baixos para TNC (62,2; 51,8), antes e depois da biodegradação. Os maiores valores (p <0,05) de FS foram observados para a FZ (127,6) e os menores (p<0,05) para a TNC (86,9); após biodegradação, o XF (117,7) apresentou os maiores valores (p<0,05) em comparação ao TNC e FZ. Em conclusão, a biodegradação aumentou o Ra e diminuiu a GU e a KHN para todos. Em relação à FS, a degradação promoveu uma diminuição significativa apenas para a FZ.

Introduction

Due to greater demand for aesthetics in dentistry, the composite resin has been the material of choice for direct restorative treatment. In order to simplify the restorative procedure, reduced clinical time, and decrease polymerization shrinkage stresses and cusp deflection, Bulk Fill composites were introduced into dental market with the appeal of simplifying the restorative procedure by single increment insertion of up to 4 mm depth with an adequate polymerization 11 .Bucuta S, Ilie N. Light transmittance and micro-mechanical properties of bulk fill vs. conventional resin based composites. Clin Oral Investig2014;18:1991-2000..

According to the manufacturers, these composites require a short activation time due to the modification of the initiation system that includes higher concentrations of conventional photoinitiators and reduced light scattering at the filler-matrix interface by decreasing the filler amount or increasing the filler size 22 .Miletic V, Pongprueksa P, De Munck J, Brooks NR, Van Meerbeek B. Curing characteristics of flowable and sculptable bulk-fill composites. Clin Oral Investig 2017;21:1201-1212., providing satisfactory material polymerization.

Despite the evolution of composite resins related to filler content, resin matrix and initiator systems 33 .Fronza BM, Rueggeberg FA, Braga RR, Mogilevych B, Soares LE, Martin AA, et al. Monomer conversion, microhardness, internal marginal adaptation, and shrinkage stress of bulk-fill resin composites. Dental Mater 2015;31:1542-1551., biofilm is the highest challenge for restorative materials on oral cavity. In addition, some enzymes from the class of esterases such as cholesterol esterase and pseudocholinesterase can degrade BisGMA/TEGMA based polymer composite in polymer matrix 44 .Finer Y, Jaffer F, Santerre JP. Mutual influence of cholesterol esterase and pseudocholinesterase on the biodegradation of dental composites. Biomater2004;25:1787-1793.. Moreover, the cariogenic bacteria from dental biofilm denominated Streptococcus mutans, is capable of degrading the resin matrix of composites not just because of their esterase activity but also by producing acids and decreasing the pH environment 55 .Borges MA, Matos IC, Mendes LC, Gomes AS, Miranda MS. Degradation of polymeric restorative materials subjected to a high caries challenge. Dent Mater 2011;27:244-252.. Further the destructive effect on the polymers, it may affect the materials properties in short or long term 66 .Paula AB, Fucio SB, Ambrosano GM, Alonso RC, Sardi JC, Puppin-Rontani RM. Biodegradation and abrasive wear of nano restorative materials. Oper Dent2011;36:670-677..

One drawback of the acids produced by the bacteria of the cariogenic biofilm is the softening of the resin matrix leading to increasing surface roughness and reducing hardness and gloss 77 .Busscher HJ, Rinastiti M, Wiswomihardjo S, Van der Mei HC. Biofilm Formation on Dental Restorative and Implant Materials. J Dent Res 2010;89:657-665.. Moreover, the flexural strength is considered an indicative factor about the performance and longevity of the composites when subjected to biological degradation and masticatory forces, influencing the material performance 88 .Papadogiannis D, Tolidis K, Lakes R, Papadogiannis Y. Viscoelastic properties of low-shrinking composite resins compared to packable composite resins. Dent Mater J 2011;30:350-357..

Although there are several studies in the literature in relation to Bulk Fill composites related mainly to mechanical performance (1-3,9,10), they are not focused on the influence of cariogenic biofilm on the properties of materials. Considering the routine use of composites resins to restore posterior teeth and the potential deleterious effect of biofilm on the surface of restorative materials as shown by the literature 66 .Paula AB, Fucio SB, Ambrosano GM, Alonso RC, Sardi JC, Puppin-Rontani RM. Biodegradation and abrasive wear of nano restorative materials. Oper Dent2011;36:670-677., it would be essential to evaluate the Bulk fill performance under a cariogenic challenge provided by S. mutans biofilm, since the most of Bulk Fill composites on the market still remains with BisGMA/TEGDMA on the composition.

In spite of Bulk Fill composites have the purpose to make dentist life easier, they can be subdivided into two groups: the materials that can be exposed to the oral environment (high viscosity), with better mechanical properties; and those that should be used as a base/liner (flowable), in which the manufacturer recommends a capping layer with conventional composite resin and these characteristics are responsible for defining its indications 1111. Rizzante FAP, Duque JA, Duarte MAH, Mondelli RFL, Mendonça G, Ishikiriama SK. Polymerization shrinkage, microhardness and depth of cure of bulk fill resin composites Dent Mater J 2019;38:403-410.. Besides it can be characterized by mechanical tests in which are expected to present variations due to different compositions as different monomers and photoinitiators 1212. Fronza BM, Ayres APA, Pacheco RR, Rueggeberg FA, Dias CTS, Giannini M. Characterization of Inorganic Filler Content, Mechanical Properties, and Light Transmission of Bulk-fill Resin Composites. Oper Dent 2017;42:445-455.. Thus, due to the great variation presented by material on their composition related with organic and inorganic content, they can be influenced in different ways by biofilm and also perform in different ways.

Therefore, we hypothesized that biofilm formated on Bulk Fill can yield lower damaged in composite resins, concerning: 1. roughness and gloss surface; 2. hardness surface; 3. flexural strength. Thus, the aim of this study was to evaluate influence by S. mutans biofilm biodegradation on the roughness, hardness, surface gloss and flexural strength of high viscosity Bulk Fill composites.

Material and Methods

Three commercial high viscosity Bulk Fill composites: Filtek Bulk Fill (FBF), Tetric N Ceram Bulk Fill (TNC), X-tra fil (XF) and a conventional Filtek Z350 (FZ) composite were used in this study. The composition, shade, weight (%), lot number and manufacturer of the composites are shown in Box 1.

Box 1
Material, composition, shade, weight (%), lot number and manufacturer of the composites

For all the tests, specimens were randomly distributed in 4 experimental groups (n=10) according to each material, with evaluations accomplished before and after 7 days of biodegradation, regarding the properties of roughness, hardness, surface gloss and flexural strength.

Roughness

Roughness test was carried out on material discs (5 mm in diameter, 2 mm in thickness for all composites) accomplished using a silicone mold (Aquasil LV; Dentsply DeTrey, Maquira, Maringa, PR, Brazil) pressed between two glass slides and covered by polystyrene strips (n=10). The composites were placed in a single increment and the composites Bulk Fill was light-cured for 10 s and Filtek Z350 for 20 s, using a LED source (BluePhase 20i; Ivoclar Vivadent, Schaan, Liechtenstein) with an irradiance of 1,200 mW/cm2 as measured using a curing radiometer (Hilux Dental Curing Light Meter; Benilioglu Dental, Demetron, Ankara, Turkey). After storing for 24 h at 37 oC in relative humidity, composite resin discs were polished with abrasive papers in a decreasing sequence of abrasiveness using 1,000-, 1,200-, and 2,000-grit SiC (Norton Abrasives, Vinhedo, SP, Brazil) and finished with diamond pastes 3 µm, 2 µm, 1 µm, and 0.5 µm (Diamond Excel; Buehler) applied with felt discs, according to protocol previously described in the literature 33 .Fronza BM, Rueggeberg FA, Braga RR, Mogilevych B, Soares LE, Martin AA, et al. Monomer conversion, microhardness, internal marginal adaptation, and shrinkage stress of bulk-fill resin composites. Dental Mater 2015;31:1542-1551..

The surface roughness of the specimens was measured using a surface profilometer (Surfcorder SE-1700, Kosaka Laboratory, Tokyo, Japan) with a 0.5 mm radius diamond stylus and 0.01 µm precision, set to 0.25 mm cutoffs and for a total measured length of 1.25 mm at 0.1 mm/s constant speed. Three measurements were made with the diamond stylus passing across the geometric center of the specimens in three different positions on surface by rotating the specimens 90o, 135o and 180o degrees to obtain the arithmetic mean of roughness (Ra-µm).

Knoop Hardness

The specimens (n=10) for each composite were prepared following the same procedures described for the roughness test. After 24 h, the Knoop hardness measurements were conducted on the top surface of the specimens using a microhardness tester (HMV-2; Shimadzu Corp., Tokyo, Japan) with a load of 50 g applied for 15 s. Five indentations were made in the different locations on the top surface and the average value of the five readings was recorded as the Knoop hardness number (KHN) for each specimen.

Gloss Evaluation

Ten specimens for each composite (10 mm in diameter, 2 mm in thickness) were prepared following the same procedures described for the roughness test and Knoop hardness. The gloss-meter measurement principle is based on a light beam incident on the sample surface. The intensity of the reflected light is measured and compared with a reference value. The gloss-meter calibration was made with a highly polished black glass pattern supplied by manufacturer. The surface gloss of the composites resins was evaluated using a 3-angle potable precision gloss-meter (ZGM ; Glossmeter, Zehntner Testing Instruments, Sissach, Switzerland) using a light incidence of 60°. Four measurements were made on each sample and the arithmetic mean of the readings was considered as Gloss values (Gloss Unit - GU). The data obtained was recorded by the software Zehntner Glosstools 1.0.0023.

Flexural Strength

Flexural strength test of the specimens was measured according to the three-point bending carried out with a universal testing machine (Instron, Model 4411; Corona, CA, USA) at a cross-head speed of 0.5 mm/min until specimen fracture. The bar specimens (n=20) were made in dimensions 2 mm x 2 mm x 25 mm for each composite according to ISO 4049 1313. Standard I. ISO 4049 polymer based filling, restorative and luting materials. International Organization for Standardization 2000:1-27.. The specimens were prepared between glass slides and light-cured with three overlapping 60 s using a LED source (BluePhase 20i; Ivoclar Vivadent). After photopolymerization, the bar dimension was measured with a digital caliper (Mitutoyo 293-821; Neuss, Germany) with an accuracy of 0.01 mm. Ten specimens for each composite were stored for 24 h and ten for one week (biodegradations) in dark containers at 37o C. The flexural strength (FS) in MPa was then calculated as: FS= 3Fl/2hb 2 , where F stands for load at fracture (N), l is the span length (20 mm), and b and h are the width and thickness of the specimens in mm, respectively.

Biodegradation

All the specimens subjected to initial tests of roughness, Knoop hardness, surface gloss and flexural strength after biodegradation were sterilized with ethylene oxide in the ACECIL enterprise (Sterilization Center, Campinas, SP, Brazil). S. mutans strain UA159 was obtained from a culture of the Department of Microbiology and Immunology, Piracicaba Dental School, State University of Campinas. To prepare the inoculum, S mutans were first grown on Mitis Salivarius Agar (Difco Laboratories, Sparks MD, MI, USA) plates at 37 oC for 48 h in an environment supplemented with 10% CO2. Subsequently, single colonies were inoculated into 5 mL of brain heart infusion (BHI) broth (Difco Laboratories) and incubated at 37 o C for 18 h. Disc specimens were exposed under static conditions to 25 µL of S. mutans and the bar shaped specimens to 150 µL inoculum adjusted to an optical density of 0.6 at 550 nm (approximately 8 x 1011 CFU/mL) 66 .Paula AB, Fucio SB, Ambrosano GM, Alonso RC, Sardi JC, Puppin-Rontani RM. Biodegradation and abrasive wear of nano restorative materials. Oper Dent2011;36:670-677..

After 2 h at room temperature, the non-adhering cells were removed by washing two times with 0.9% NaCl solution (saline). After, a single material disk was placed in each well of polystyrene plates (Nunce multidish 96 well, Sigma, Saint Louis, MO, USA) with 2 mL of sterile, fresh, BHI broth containing 1% of sucrose (wt/vol). Specimens for flexural strength test were stored in test tubes with 4 mL of sterile BHI solution containing 1% of sucrose. The bacterial accumulation occurred at 37 °C in an environment supplemented with 10% CO2, developing 7 day old biofilm. The medium was renewed at 24 h intervals. At the end of the experimental period, specimens were ultrasonically washed for 10 min and the final tests for surface roughness, Knoop hardness, surface gloss and flexural strength were performed as described for the initial period. Representative samples of each material (n=3), before and after biodegradation, were sputter-coated with gold under vacuum (Balzers-SCD 050 sputter coater, Balzers, Liechtenstein) and examined using scanning electron microscope (Model JEOL JSM 5600 LV, Tokyo, Japan) operating at 1,000 x magnification. X-ray (EDX) spectrometry, coupled to a scanning electron microscope (JEOL, JSM-5600LV, Tokyo, Japan) was performed to identify the elemental composition of the surface filler particles. Each spectrum was acquired for 100 s (voltage 15 kV, dead time 20% to 25%, working distance 20 mm). Images showing the identified chemical elements and their relative concentration were obtained from three different analyses of each material at three different locations on a stub.

Statistical Analysis

Data were tested for normality (Kolmogorov-Smirnov). Data for roughness, Knoop hardness and surface gloss were analyzed with two-way ANOVA. Multiple comparisons were performed using the Tukey post-hoc test (a = 0.05). Data of the flexural strength were analyzed with two-way ANOVA analysis of variance and Tukey post-hoc test (a = 0.05). All test was conducted considering the significance of 5%, using SPSS software 22.

Results

Table 1 shows the surface roughness of the composites before and after the biodegradation. Significant differences in roughness for composites (p<0.000) and biodegradation (p<0.000) were detected. The interaction between the composites and biodegradation was significant (p=0.003). Surface roughness increased for all materials after S. mutans biodegradation. Comparing different composites before and after biodegradation, the highest roughness values was obtained for the composite XF (p<0.05).

Table 1
Means of roughness ± Standard deviation (µm), before and after biodegradation by S. mutans for the composites

Table 2 shows the gloss results before and after biodegradation. There was significant difference between the materials (p=0.010) and biodegradation (p=0.005). However, there was no interaction between the material x biodegradation factors (p = 0.845). It was observed that FZ and FBF showed the highest gloss values before and after the biodegradation in relation others materials (p<0.05). TNC and XF showed similar lower gloss values. It was observed reduction of gloss values for all the composites after biodegradation (p<0.05).

Table 2
Means of gloss ± Standard Deviation (GU), before and after biodegradation by S. mutans for the composites

Table 3 shows the Knoop hardness results of the composites before and after biodegradation. There was significant difference between the materials (p<0.000) and biodegradation (p<0.000). The interaction between the material and biodegradation factors was significant (p= 0.024). The surface hardness values for all materials decreased significantly after biodegradation (p<0.05). It was observed that before and after biodegradation, the XF composite presented the highest values for hardness when compared to other materials (p<0.05) and the lowest value was shown by TNC, while FBF and FZ presented intermediate values.

Table 3
Means of Knoop hardness ± Standard Deviation (KHN), before and after biodegradation by S. mutans for the composites

Table 4 shows the results of the flexural strength of the composites before and after the biodegradation by S. mutans. There was a significant difference between the materials (p<0.000) and for biodegradation factors (p=0.003). The interaction between material x biodegradation was significant (p=0.004). The composite FZ showed the highest flexural strength despite it showed the significant decrease on the values caused by biodegradation (p<0.05). There was not observed significant difference between FBF and XF on flexural strength values, as well as between FBF and TNC. After biodegradation, the composite XF showed the highest flexural strength values compared to TNC and FZ (p<0.05). There was no significant difference between FZ and FBF, and between FBF and XF, as well as between FZ and TNC concerning flexural strength values (p>0.05). When flexural strength was compared before and after biodegradation, there was a significant reduction in the flexural strength value only for the FZ composite (p<0.05).

Table 4
Means of flexural strength ± Standard Deviation (MPa), before and after biodegradation by S. mutans for the composites

Characterization and filler content images are illustrated on Figure 1. The SEM micrograph showed several sizes and shapes fillers, but mostly round, and some cluster formations (black star) (Fig. 1A and 1C). The elemental composition of FZ revealed the presence Carbonum, Silica and Zirconium (Fig. 1B). FBF had a morphology similar to FZ; also the value of fillers >5 µm is estimated from SEM (Fig. 1C). The inorganic elements in FBF were found to include Carbonum, Aluminium, Yterbium, Silica and Zirconium (Fig. 1D). The TNC images showed the presence of spherical and irregular nano-sized fillers (Fig. 1E) and EDS revealed Carbonum, Aluminium, Silica, Phosphorum, and Barium (Fig. 1F). The particles morphology for XF were constituted by irregular fillers, basically, but, mostly higher than 10 µm (Fig. 1G). The filler content was similar to TNC, except by absence of Phosphorum (Fig. 1H).

Figure 1
Representative scanning electron microscopy filler characterization of all composites before biodegradation in Back Scattering, showing the size, filler morphology and content represented by EDS. A. several sizes and shapes fillers, but mostly round, and some cluster formations (white star); B. >5 µm fillers (white star) mixed with several sizes and shapes, including nanofillers; C nanofillers mixed with round and irregular shapes; D. Irregular fillers with different sizes but mostly > 10 µm. Magnification from 1000´ to 4000´.

Figure 2 shows representative scanning electron microscopy (SEM) images from composite resin surfaces before and after degradation by S. mutans biofilm. It can be observed the shape and distribution of the fillers from each composite resin studied. After biodegradation, it is possible observe a smoother surface with uniform distribution of filler particles for the FZ composite (Fig. 2E). For XF composite (Fig. 2H), is possible to notice the presence of larger sized particles with irregular shape and distribution. TNC (Fig. 2G) presented a slightly corroded surface and on the surface of FBF composite (Fig. 2F) may be observed the exposure of intermediate sized filler particles.

Figure 2
Representative scanning electron microscopy before and after degradation respectively of Filtek Z350 (A, E), Filtek Bulk (B, F), Tetric N-Ceram Bulk Fill (C, G) and Fill X-tra fil (D, H). Magnification of 1000´.

Discussion

The first hypothesis that the biofilm provide lower damage on roughness and gloss surface of Bulk Fill composite resins was rejected, since those properties were influenced not only by biofilm, but also by material composition.

In order to obtain aesthetics and longevity in composite resin restorations, surface smoothness is required considering that surfaces with roughness greater than 0.2 µm allow an increase in biofilm accumulation 1414. Teughels W, Van Assche N, Sliepen I, Quirynen M. Effect of material characteristics and/or surface topography on biofilm development. Clin Oral Implants Res 2006;17:68-81.. According to the results obtained in this study, before biodegradation the composite XF showed the highest roughness when compared to other composites. Previous study showed that this result is related to highest percentage in volume (70.1%) and size (2-3 µm) of the filler 1515. Scheibe KG, Almeida KG, Medeiros IS, Costa JF, Alves CM. Effect of different polishing systems on the surface roughness of microhybrid composites. J Appl Oral Sci 2009;17:21-26.. Furthermore, Marghalani has shown that the shape of the filler particles also influenced the surface roughness 1616. Marghalani HY. Effect of filler particles on surface roughness of experimental composite series. J Appl Oral Sci 2010;18:59-67., suggesting that irregular fillers (Fig. 1G and 2D), such as XF composite, promote rougher surfaces. The composite FZ, FBF and TNC showed similar roughness values before biodegradation (Table 1, Fig. 2A, 2B and 2C). As it can be seen in Box 1, these composites have in the composition filler particles with reduced size and similar or lower percentage in volume when compared to XF composite. The filler size allows better polishing and, consequently, higher surface smoothness 1616. Marghalani HY. Effect of filler particles on surface roughness of experimental composite series. J Appl Oral Sci 2010;18:59-67.,1717. Montanaro L, Campoccia D, Rizzi S, Donati ME, Breschi L, Prati C, et al.. Evaluation of bacterial adhesion of Streptococcus mutans on dental restorative material. Biomater2004:25:4457-4463..

After biodegradation, there was an increase of roughness for all the composites (Table 1 and Fig. 2). Although this increase is due to the production of acids, which are able to promote surface changes 55 .Borges MA, Matos IC, Mendes LC, Gomes AS, Miranda MS. Degradation of polymeric restorative materials subjected to a high caries challenge. Dent Mater 2011;27:244-252.,77 .Busscher HJ, Rinastiti M, Wiswomihardjo S, Van der Mei HC. Biofilm Formation on Dental Restorative and Implant Materials. J Dent Res 2010;89:657-665., others factors, as filler size and monomer composition, may have influenced the results. According to Montanaro et al. 1717. Montanaro L, Campoccia D, Rizzi S, Donati ME, Breschi L, Prati C, et al.. Evaluation of bacterial adhesion of Streptococcus mutans on dental restorative material. Biomater2004:25:4457-4463., the adhesion of S. mutans to surface of the composites is related to size, shape and distribution of the charge particles, besides the composition of the organic matrix. As it can be seen in Figures 1G and 2D, the XF composite showed irregular and bigger filler particles, that makes surface rougher, allowing greater adhesion of S. mutans, reflecting on higher roughness value, even after polishing. Adversely, in the conventional composite FZ there are fillers combination involving silica nanofillers filling the spaces left by zirconia-silica nanoclusters. The reduced size and homogeneous distribution of the filler particles in this composite (Fig. 2A) resulted in lower S. mutans adhesion, similar to previous study 1717. Montanaro L, Campoccia D, Rizzi S, Donati ME, Breschi L, Prati C, et al.. Evaluation of bacterial adhesion of Streptococcus mutans on dental restorative material. Biomater2004:25:4457-4463.. It is also known that in this nanocomposite there is lower interstitial space among the filler particles and, consequently, less exposure of the organic matrix 1818. Turssi CP, Ferracane JL, Serra MC. Abrasive wear of resin composites as related to finishing and polishing procedures. Dent Mater 2005;21:641-648., making it more resistant to biodegradation. Therefore, these factors are responsible for the lower surface roughness of FZ after biodegradation. TNC and FBF composites showed intermediaries and did not differ statistically in roughness after biodegradation. This result can be attributed to similarity of size and volume percentage of the filler particles of these materials 1616. Marghalani HY. Effect of filler particles on surface roughness of experimental composite series. J Appl Oral Sci 2010;18:59-67..

It is claimed that the surface gloss of the composites shows an inverse relation with roughness 1919. Lee TY, Guymon CA, Jönsson ES, Hoyle CE. The effect of monomer structure on oxygen inhibition of (meth) acrylates photopolymerization. Polymer2004;45:6155-6162., corroborating with the results obtained in the current study. It can be observed in this study that after biodegradation, besides the increase of surface roughness, all composites presented reduction in the brightness values. This result is certainly because of the surface changes that occurred in the materials exposed to the cariogenic biofilm 66 .Paula AB, Fucio SB, Ambrosano GM, Alonso RC, Sardi JC, Puppin-Rontani RM. Biodegradation and abrasive wear of nano restorative materials. Oper Dent2011;36:670-677.,77 .Busscher HJ, Rinastiti M, Wiswomihardjo S, Van der Mei HC. Biofilm Formation on Dental Restorative and Implant Materials. J Dent Res 2010;89:657-665., affecting the incidence and reflection of the light, promoting reduction of the surface gloss of the composites 2020. Lefever D, Perakis N, Roig M, Krejci I, Ardu S. The effect of toothbrushing on surface gloss of resin composites. Am J Dent 2012;25:54-58.. It can be seen in Box 1, that composite XF present a higher amount of TEGDMA than composite FZ, about 10 times and other composites does not show that monomer. Consequently, changes on the organic matrix and the interaction between matrix and filler particles may promote significant reduction of the surface gloss of composites 2121. Münchow EA, Ferreira ACA, Machado RM, Ramos TS, Rodrigues Junior SA, Zanchi CH. Effect of Acidic Solutions on the Surface Degradation of a Micro-Hybrid Composite Resin. Braz Dent J 2014;25:321-326.. However, when the materials were compared before and after biodegradation may be observed that higher gloss values were obtained for composites FZ and FBF. Small filler particles of those composites (Fig. 1A and 1C) caused a decrease in diffuse reflection and a high refractive index resulting in higher gloss values compared to the others composites 1111. Rizzante FAP, Duque JA, Duarte MAH, Mondelli RFL, Mendonça G, Ishikiriama SK. Polymerization shrinkage, microhardness and depth of cure of bulk fill resin composites Dent Mater J 2019;38:403-410.,2222. Takahashi H, Finger WJ, Endo T, Kanehira M, Koottathape N, Komatsu M. Comparative evaluation of mechanical characteristics of nanofiller containing resin composites. Am J Dent2011;24:264-270.. Nevertheless, lower gloss values was obtained by composites XF and TNC, which can be explained by the larger size (composite XF) of their particles (Fig. 1G) and irregular shape (Fig. 1E and 1G) that caused a lower homogeneity of the matrix-filler complex resulting in low light reflection 2020. Lefever D, Perakis N, Roig M, Krejci I, Ardu S. The effect of toothbrushing on surface gloss of resin composites. Am J Dent 2012;25:54-58..

Surface hardness is an important property that is directly related to mechanical performance and depends on the degree of polymerization of the material, the size, weight and volume of the inorganic fillers, as well as the composition of the composite matrix 99 .Alrahlah A, Silikas N, Watts D. Post-cure depth of cure of bulk fill dental resin-composites. Dent Mater 2014;30:149-154.. Composite XF presented higher Knoop hardness value, which may be attributed to higher size and percentage of filler in volume, being one of the factors responsible for increasing the performance of the mechanical properties 2323. Leprince JG, Palin WM, Hadis MA, Devaux J, Leloupa G. Progress in dimethacrylate-based dental composite technology and curing efficiency. Dent Mater2013;29:139-156.. According to Ilie et al. 1010. Ilie N, Bucuta S, Draenert M. Bulk-fill resin-based composites: an in vitro assessment of their mechanical performance. Oper Dent2013;38:618-625., increasing the size of the inorganic fillers reduces the matrix amount incorporated into the material and, consequently, the matrix-filler interface. Thus, light scattering is reduced during photo-activation due to higher absorption, increasing of the degree of conversion and resulting in higher hardness values.

However, lower Knoop hardness value was observed for the composite TNC. Even though the photoinitiator is part of the composition, which according to manufacturer would provide increase at the polymerization depth, it also contains prepolymers that may be related to lower Knoop hardness values because prepolymers are calculated together with the volume percentage of the inorganic matrix 1010. Ilie N, Bucuta S, Draenert M. Bulk-fill resin-based composites: an in vitro assessment of their mechanical performance. Oper Dent2013;38:618-625.. The composites FZ and FBF presented intermediaries Knoop hardness values and this may be attributed to the similar size and shape of the inorganic fillers 2222. Takahashi H, Finger WJ, Endo T, Kanehira M, Koottathape N, Komatsu M. Comparative evaluation of mechanical characteristics of nanofiller containing resin composites. Am J Dent2011;24:264-270..

Biofilm degradation by S. mutans caused a significant decrease in hardness of all materials. There is a great possibility that the functional groups -OH and -CHOO of the acids produced by the bacteria form hydrogen bonds with the polar side of the methacrylate monomer of the composites, causing greater water absorption and softening of the resin matrix. This fact induces tension at the matrix-silane-filler interface separating the inorganic fillers from the organic matrix, promoting hardness reduction 2424. Hashemikamangar SS, Pourhashemi SJ, Talebi M, Kiomarsi N, Kharazifard MJ. Effect of organic acids in dental biofilm on microhardness of a silorane-based composite. Restor Dent Endod2015;40:188-194..

Flexural strength test was performed according to ISO 4049 standard. Before biodegradation, Filtek Z350 composite presented higher value of flexural strength when compared to the composites TNC and FBF. The flexural strength values suggest that higher inorganic particle content does not necessarily result in higher flexural strength values. In addition to the filler content, other factors such as tension between fillers and resin matrix, as well as the bond between the components and the composition of the organic matrix 2323. Leprince JG, Palin WM, Hadis MA, Devaux J, Leloupa G. Progress in dimethacrylate-based dental composite technology and curing efficiency. Dent Mater2013;29:139-156. may be relevant on the flexural strength of these materials. The best results in mechanical properties of FZ may be related to a higher degree of monomeric conversion already confirmed by another study 1212. Fronza BM, Ayres APA, Pacheco RR, Rueggeberg FA, Dias CTS, Giannini M. Characterization of Inorganic Filler Content, Mechanical Properties, and Light Transmission of Bulk-fill Resin Composites. Oper Dent 2017;42:445-455.. However, the composite TNC showed lower value when compared to composites XF and FZ. As previously discussed, despite the incorporation of the Ivocerim photoinitiator as an attempt to improve the polymerization depth, the presence of prepolymers in the composite may have negatively influenced on the mechanical properties, reflecting the lower value of flexural strength for this material 2525. Beun S, Glorieux T, Devaux J, Vreven J, Leloup G. Characterization of nanofilled compared to universal and microfilled composites. Dent Mater 2007;23:51-59.. In addition, the shorter photoactivation time indicated by the manufacturer may not have been enough to obtain adequate polymerization.

When comparing the composites after biodegradation, it may be observed that the composite XF presented a higher value of flexural strength when compared to the composites TNC and FBF. Probably, this result would be related to the larger size and volume of the filler particles (Fig. 1G) 2525. Beun S, Glorieux T, Devaux J, Vreven J, Leloup G. Characterization of nanofilled compared to universal and microfilled composites. Dent Mater 2007;23:51-59.. Despite the differences found in flexural strength values when comparing the different composites, the degradation by S. mutans biofilm was able to reduce only the resistance of the FZ composite. This result may be related to different compositions of the organic matrices of these materials. In addition, the composite FZ showed highest amounts of zirconia-silica clusters (Fig. 1B), responsible for increasing the water absorption by the material due to the higher volume of silane, which makes it more susceptible to hydrolytic degradation 2424. Hashemikamangar SS, Pourhashemi SJ, Talebi M, Kiomarsi N, Kharazifard MJ. Effect of organic acids in dental biofilm on microhardness of a silorane-based composite. Restor Dent Endod2015;40:188-194.

In summary, the results showed increased roughness and decreased hardness and gloss of all composites evaluated. No effect on the flexural strength occurred for the Bulk Fill composites. Reduction of flexural strength occurred only for the conventional FZ composite. The biodegradation by S. mutans negatively affected the mechanical and surface properties of the materials. Care should be taken by clinicians during the selection of the restorative material and the knowledge of the patient about the importance of the continuous use of oral hygiene techniques is essential for maintaining aesthetics and longevity of composite resin restorations. Future studies should be developed to investigate other possible factors such as mechanical brushing and different light-curing source.

Acknowledgements

This study was financed by FAPESP - São Paulo Research Foundation (grants #2016/18720-8) and in part by the Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - Brasil (CAPES) - Finance Code 001. The authors also express gratitude to Dr. Filipe Matheus Cardoso da Silva for assistance with biodegradation test and Dr. Paulo Vitor Campos Ferreira for assistance with EDS images.

References

  • 1
    Bucuta S, Ilie N. Light transmittance and micro-mechanical properties of bulk fill vs. conventional resin based composites. Clin Oral Investig2014;18:1991-2000.
  • 2
    Miletic V, Pongprueksa P, De Munck J, Brooks NR, Van Meerbeek B. Curing characteristics of flowable and sculptable bulk-fill composites. Clin Oral Investig 2017;21:1201-1212.
  • 3
    Fronza BM, Rueggeberg FA, Braga RR, Mogilevych B, Soares LE, Martin AA, et al. Monomer conversion, microhardness, internal marginal adaptation, and shrinkage stress of bulk-fill resin composites. Dental Mater 2015;31:1542-1551.
  • 4
    Finer Y, Jaffer F, Santerre JP. Mutual influence of cholesterol esterase and pseudocholinesterase on the biodegradation of dental composites. Biomater2004;25:1787-1793.
  • 5
    Borges MA, Matos IC, Mendes LC, Gomes AS, Miranda MS. Degradation of polymeric restorative materials subjected to a high caries challenge. Dent Mater 2011;27:244-252.
  • 6
    Paula AB, Fucio SB, Ambrosano GM, Alonso RC, Sardi JC, Puppin-Rontani RM. Biodegradation and abrasive wear of nano restorative materials. Oper Dent2011;36:670-677.
  • 7
    Busscher HJ, Rinastiti M, Wiswomihardjo S, Van der Mei HC. Biofilm Formation on Dental Restorative and Implant Materials. J Dent Res 2010;89:657-665.
  • 8
    Papadogiannis D, Tolidis K, Lakes R, Papadogiannis Y. Viscoelastic properties of low-shrinking composite resins compared to packable composite resins. Dent Mater J 2011;30:350-357.
  • 9
    Alrahlah A, Silikas N, Watts D. Post-cure depth of cure of bulk fill dental resin-composites. Dent Mater 2014;30:149-154.
  • 10
    Ilie N, Bucuta S, Draenert M. Bulk-fill resin-based composites: an in vitro assessment of their mechanical performance. Oper Dent2013;38:618-625.
  • 11
    Rizzante FAP, Duque JA, Duarte MAH, Mondelli RFL, Mendonça G, Ishikiriama SK. Polymerization shrinkage, microhardness and depth of cure of bulk fill resin composites Dent Mater J 2019;38:403-410.
  • 12
    Fronza BM, Ayres APA, Pacheco RR, Rueggeberg FA, Dias CTS, Giannini M. Characterization of Inorganic Filler Content, Mechanical Properties, and Light Transmission of Bulk-fill Resin Composites. Oper Dent 2017;42:445-455.
  • 13
    Standard I. ISO 4049 polymer based filling, restorative and luting materials. International Organization for Standardization 2000:1-27.
  • 14
    Teughels W, Van Assche N, Sliepen I, Quirynen M. Effect of material characteristics and/or surface topography on biofilm development. Clin Oral Implants Res 2006;17:68-81.
  • 15
    Scheibe KG, Almeida KG, Medeiros IS, Costa JF, Alves CM. Effect of different polishing systems on the surface roughness of microhybrid composites. J Appl Oral Sci 2009;17:21-26.
  • 16
    Marghalani HY. Effect of filler particles on surface roughness of experimental composite series. J Appl Oral Sci 2010;18:59-67.
  • 17
    Montanaro L, Campoccia D, Rizzi S, Donati ME, Breschi L, Prati C, et al.. Evaluation of bacterial adhesion of Streptococcus mutans on dental restorative material. Biomater2004:25:4457-4463.
  • 18
    Turssi CP, Ferracane JL, Serra MC. Abrasive wear of resin composites as related to finishing and polishing procedures. Dent Mater 2005;21:641-648.
  • 19
    Lee TY, Guymon CA, Jönsson ES, Hoyle CE. The effect of monomer structure on oxygen inhibition of (meth) acrylates photopolymerization. Polymer2004;45:6155-6162.
  • 20
    Lefever D, Perakis N, Roig M, Krejci I, Ardu S. The effect of toothbrushing on surface gloss of resin composites. Am J Dent 2012;25:54-58.
  • 21
    Münchow EA, Ferreira ACA, Machado RM, Ramos TS, Rodrigues Junior SA, Zanchi CH. Effect of Acidic Solutions on the Surface Degradation of a Micro-Hybrid Composite Resin. Braz Dent J 2014;25:321-326.
  • 22
    Takahashi H, Finger WJ, Endo T, Kanehira M, Koottathape N, Komatsu M. Comparative evaluation of mechanical characteristics of nanofiller containing resin composites. Am J Dent2011;24:264-270.
  • 23
    Leprince JG, Palin WM, Hadis MA, Devaux J, Leloupa G. Progress in dimethacrylate-based dental composite technology and curing efficiency. Dent Mater2013;29:139-156.
  • 24
    Hashemikamangar SS, Pourhashemi SJ, Talebi M, Kiomarsi N, Kharazifard MJ. Effect of organic acids in dental biofilm on microhardness of a silorane-based composite. Restor Dent Endod2015;40:188-194.
  • 25
    Beun S, Glorieux T, Devaux J, Vreven J, Leloup G. Characterization of nanofilled compared to universal and microfilled composites. Dent Mater 2007;23:51-59.

Publication Dates

  • Publication in this collection
    04 Sept 2020
  • Date of issue
    Jul-Aug 2020

History

  • Received
    09 Jan 2020
  • Accepted
    17 June 2020
Fundação Odontológica de Ribeirão Preto Av. do Café, S/N, 14040-904 Ribeirão Preto SP Brasil, Tel.: (55 16) 3602-3982, Fax: (55 16) 3633-0999 - Ribeirão Preto - SP - Brazil
E-mail: bdj@forp.usp.br