Fiberglass wastes/polyester resin composites: mechanical properties and water sorption

ARTIGO TÉCNICO CIENTÍFICO

Fiberglass wastes/polyester resin composites: mechanical properties and water sorption

Edcleide M. Araújo; Kasselyne D. Araújo; Osanildo D. Pereira; Pollyana C. Ribeiro; Tomás J. A. de Melo

Departamento de Engenharia de Materiais, UFCG

^{Autor para correspondência}

ABSTRACT

The mechanical properties of polyester/fiberglass composites were studied. The aim of this work was to evaluate the possibility of reusing the wastes taken from spray-up processing of Paraíba state Industries as reinforcement in polyester matrix composites. Composites with 20, 30, 40, 50 and 60 wt. (%) of recycled fiberglass were prepared by compression molding and compared with polyester/ virgin glass fiber composites. The mechanical properties and water sorption behavior were evaluated. The results showed that fiberglass wastes are promising to be reused in polyester resin composites. The impact strength was excellent. It can be concluded that the reusing of the fiberglass wastes is viable.

Keywords: Fiberglass wastes, polyester, composites.

Introduction

Composite materials are made from two or more constituent materials (matrix and reinforcement) with significantly different mechanical properties and which remain separate and distinct within the finished structure. They display a combination of the best characteristics of each individual material. The matrix forms the continuous phase while the reinforcement forms the disperse phase. The most common reinforcement is fiberglass, in which glass fibers are embedded within a polymer material. Fiberglass acquires strength from the glass and flexibility from the polymer. However, the mechanical performance of fiberglass reinforced composites depends on not only the properties of constituent components but also the interfacial interactions established between the reinforcing agent and the matrix material^[1-10]. The crescent use of fiberglass in composite materials by industries has become a big problem, since its wastes are thrown in the nature. An alternative way is to recycle these wastes. Several works and techniques have been developed with the aim of reducing this residues volume such as incineration, chemical degradation, etc.^[1]. Hand-lay-up and spray-up techniques have been used to produce materials in layers such as resin and fiber and the obtained properties are: high strength and rigidity, light weight, good corrosion resistance and thermal isolation^[9]. The aim of this work is to investigate the effect of fiberglass wastes on the mechanical properties and water sorption of polyester resin composites. Polyester/virgin fiberglass composites were also produced for comparison with polyester/fiberglass wastes composites.

Experimental

The unsatured polyester resin was reinforced using fiberglass wastes. These wastes were supplied by Equifiber as an agglomerate of glass fibers embedded in a polyester resin. Prior to each processing the wastes were separated and cut. The composites were prepared by compression, with 88.3 kN and the fibers were dispersed by hand in the mold and impregnated with the catalyzed resin. 1 wt. (%) of MEK (methyl ethyl ketone) catalyser was used.

Mechanical Properties: the composites in the form of plates with dimensions of 150 x 180 x 3 mm were pressed and then cut by a metallic circular disc according to ASTM D3039 and ASTM D256. Tensile properties were measured using a universal tensile machine (Lloyd LR/10 kN) with crosshead speed of 5mm/min at room temperature. Izod impact tests were carried out at room temperature using a CEAST Resil apparatus with a hammer of 2.75 J. The hardness tests were carried out using the shore D hardness according to ASTM D2240 during 10 s. An average of five samples were tested for each composition (20, 30, 40, 50 and 60 wt. (%)).

Water Sorption: the cut samples were subjected to water sorption tests. The samples were dried in an oven, weighed and immersed in distilled water at room temperature. After pre-determined times, samples were removed from the water. After removing the water excess, they were weighed in an analytical balance. The amount of sorbed water was calculated by comparing the initial and final weights. Three samples were tested for each composition.

The fracture surfaces of the samples subjected to Izod impact strength tests were analyzed by scanning electron microscope (SEM), using a Zeiss DSM 960 Digital Scanning Microscope. The specimens were coated with gold using a Sputter Coater SCD 050 Balzers.

Results and Discussion

Table 1 shows the mechanical properties of neat polyester, polyester/virgin fiberglass and polyester/fiberglass waste composites. Figures 1 to 4 show the result of tensile modulus, elongation at break, Izod impact strength and hardness respectively of pure resin and its composites with fiberglass. It can be observed in general that increasing both virgin fiber and fiber waste content, the modulus also increases. As reported by Ozkoc et al.^[5], the incorporation of fiberglass improves the properties of the polymer materials. The modulus of the composite containing 40% of virgin fiber was much greater than that of both pure resin and polyester/fiberglass waste composites. It can be observed also that increasing fiber waste content up to 40%, the modulus increases by 20% when compared to pure polyester resin. This is interesting from the recycling point of view the final cost of the product and the smaller the amount of wastes thrown in the environment. Figure 2 shows a decrease in elongation at break when the fiber content increases up to 40% for both virgin fibers and fiber wastes. This is according to the literature because the rigid fibers hinder the movement of the polymer chains. However, these results will be studied and reported later. Figure 3 shows the Izod impact strength of the composites. A significant increase in this property can be observed with the increase in fiber content in comparison to pure polyester resin. It is interesting to observe that the composite with 50 wt. (%) of fiber waste presented a significant increase when compared to pure resin. This confirms the efficiency of these wastes as reinforcement for polyester resin composites. For contents above 50 wt. (%), the impact property value decreases. This fact can be related with the high content of fiber and the poor dispersion and distribution of the fibers in the matrix. It seems that 50 wt. (%) of fiber constitutes a limit value to increase the properties. Figure 4 shows the hardness behavior of the composites. It is interesting to note that this property was not affected significantly by simply adding fiber to polyester up to 40 wt. (%) of fiber. Apparently, only above 40 wt. (%) of fiber an increase in the hardness with increase in fibers content was observed.

Water sorption studies were also conducted, in order to determine the percentage of sorbed water by the fibers. Water presence changes completely the composites properties. Figures 5 and 6 show the water sorption results of pure resin and its composites. As expected, the fiberglass is not hydrophilic and as the fiber content (20-40 wt. (%)) increases, water sorption decreases in the composite. This can indicate high stability of the composite for specific applications.

The fracture surfaces of the samples subjected to Izod impact strength tests were analyzed by scanning electron microscope (SEM) in order to investigate the microstructure and extent of the adhesion between fibers and matrix. Figure 7 shows the micrographs of fracture surfaces of polyester resin and polyester/fiber composites containing 20, 30 and 40 wt. (%) of fibers. Figure 7a illustrates the brittle aspect of the matrix and in the other figures it can be seen that the fibers are debonded, leaving a dark region at the interface as reported by Ozkoc et al.^[5]. Most of the fibers were pulled-out from the matrix during deformation. Moreover, as the fiber content increases it is evident that the agglomeration of the fiberglass in the resin also increases. As a result of poor adhesion between the components, failure has occurred at the interface of both, polyester/virgin fiberglass and polyester/fiberglass waste. For this reason, the mechanical properties did not increase sufficiently by the addition of the fiberglass to polyester. It is clear that the use of fiberglass wastes in polyester matrix composites is viable for some applications as shown by the enhanced properties.

Conclusions

The effect of fiberglass wastes as reinforcement of polyester matrix composites was studied. Incorporation of the wastes in the composites enhanced considerably the mechanical properties such as tensile modulus and impact strength. These results are evidence that the fiberglass wastes are an efficient alternative for the recycling and that they can be used as reinforcement for polyester matrix composites.

Acknowledgment

The authors thank to Equifiber/PB industry for donating the fibers, to PROBEX and Town Hall of Cajazeirinhas/PB for financial support, to Ph.D. Eliton S. Medeiros, to Ph.D. Viviane M. Fonseca and to Engineer Pankaj Agrawal for helping in the discussions.

Enviado: 10/03/06

Reenviado: 25/09/06

Aprovado: 28/09/06

• 1. Callister Jr., W. D. - "Materials Science and Engineering", John Wiley & Sons, New York (1996).
• 2. Blass, A. - "Processamento de Polímeros", UFSC, Florianópolis (1985).
• 3. Michaeli, W.; Greif, H.; Kaufmann, H. & Vosseburger, F. J. - "Tecnologia dos Plásticos", Edgard Blucher, São Paulo (1995).
• 4. Sutherland, L. S. & Soares, C. G. - Int. J. of Impact Eng., 31, p. 1 (2005).
• 5. Ozkoc, G.; Bayram G. & Bayramli, E. - Polymer, 45, p. 8957 (2004).
• 6. Filho, R. D. T. - "Reforços Naturais-Estrutura e Propriedades Mecânicas", Pos-graduation Course PUC, Rio de Janeiro (1993).
• 7. Wu, S. H. ; Wang, F. Y.; MA, C. C. M.; Chang, W. C.; Kuo, C. T.; Kuan, H. C. & Chen, W. J. - Mat. Letters, 49, p. 327 (2001).
• 8. Lee, S. M. - "Int. Encyclopedia of Composites", 1-6 (1991).
• 9. Carvalho, G. A.; Risson, P.; Vieira, S. L.; Zeni, M. & Zattera, A. J. - Polímeros: Ciência e Tecnologia, 3, p. 89 (1998).
• 10. Navarro, R. F. - "Materiais e Ambiente", Ed. Universitária, João Pessoa (2001).

Publication Dates

• Publication in this collection
  27 Mar 2007
• Date of issue
  Dec 2006

History

• Reviewed
  25 Sept 2006
• Received
  10 Mar 2006
• Accepted
  28 Sept 2006