Metal nanoparticles/ionic liquid/cellulose: polymeric membrane for hydrogenation reactions

Abstract

Rhodium and platinum nanoparticles were supported in polymeric membranes with 10, 20 and 40 µm thickness. The polymeric membranes were prepared combining cellulose acetate and the ionic liquid (IL) 1-n-butyl-3-methylimidazolium bis(trifluoromethane sulfonyl)imide (BMI.(NTf)2. The presence of metal nanoparticles induced an increase in the polymeric membrane surface areas. The increase of the IL content resulted in an improvement of elasticity and decrease in tenacity and toughness, whereas the stress at break was not affected. The presence of IL probably causes an increase in the separation between the cellulose molecules that result in a higher flexibility and processability of the polymeric membrane. The CA/IL/M(0) combinations exhibit an excellent synergistic effect that enhances the activity and durability of the catalyst for the hydrogenation of cyclohexene. The CA/IL/M(0) polymeric membrane displays higher catalytic activity (up to 7.353 h-1) for the 20 mm of CA/IL/Pt(0) and stability than the nanoparticles dispersed only in the IL.

Hydrogenation reactions; ionic liquid; nanoparticles; polymeric membrane


Metal nanoparticles/ionic liquid/cellulose: polymeric membrane for hydrogenation reactions

Marcos Alexandre GeleskyI; Carla Weber ScheerenII

ILaboratory Catalysis and Inorganic Synthesis, Universidade Federal do Rio Grande - FURG

IILaboratory of Physical Chemistry School of Chemistry and Food, Universidade Federal do Rio Grande - FURG

Corresponding author Corresponding author: Carla Weber Scheeren Laboratório de Físico-Química, Escola de Química e Alimentos - EQA, Universidade Federal do Rio Grande - FURG Av. Itália, Km 8, s/n, Campus Carreiros CEP 96201-900, Rio Grande, RS, Brasil e-mail: carlascheeren@gmail.com

ABSTRACT

Rhodium and platinum nanoparticles were supported in polymeric membranes with 10, 20 and 40 µm thickness. The polymeric membranes were prepared combining cellulose acetate and the ionic liquid (IL) 1-n-butyl-3-methylimidazolium bis(trifluoromethane sulfonyl)imide (BMI.(NTf)2. The presence of metal nanoparticles induced an increase in the polymeric membrane surface areas. The increase of the IL content resulted in an improvement of elasticity and decrease in tenacity and toughness, whereas the stress at break was not affected. The presence of IL probably causes an increase in the separation between the cellulose molecules that result in a higher flexibility and processability of the polymeric membrane. The CA/IL/M(0) combinations exhibit an excellent synergistic effect that enhances the activity and durability of the catalyst for the hydrogenation of cyclohexene. The CA/IL/M(0) polymeric membrane displays higher catalytic activity (up to 7.353 h-1) for the 20 mm of CA/IL/Pt(0) and stability than the nanoparticles dispersed only in the IL.

Keywords: Hydrogenation reactions, ionic liquid, nanoparticles, polymeric membrane.

Introduction

Metal nanoparticles supported in compatible polymers hold great promise for biotechnological, catalytic and medical application[1]. For these applications, cellulose acetate (CA) is a good candidate because this polymer is hydrophilic, non-toxic, biodegradable and renewable with good processability[2-7]. Polymeric membranes have been prepared using several biopolymers (cellulose, carboxymethylcellulose, chitosan, polylactic acid)[1,5-10] polymers (polycaprolactone, polyaniline, polysulfone, polyurethane) and copolymers (styrene, divinylbenzene) for different applications[11-14]. Conducting polymers are a new class of polymers that has received particular interest for the production of membranes and films[14]. Biocompatible polymer systems combined with metal nanoparticles are used in various forms to incapacitate microbes by interacting with their enzymes, proteins and/or DNA (e.g., catheters, dental material, medical devices implants and burn dressings) to protect against microbial contamination.

Supported Ionic Liquid Phase (SILP) is emerging as an interesting protocol for the immobilization of transition metal catalysts since it may combine the advantages of ionic liquids (IL) with those of heterogeneous support materials[15-17]. In comparison to traditional liquid-liquid biphasic systems, higher catalytic activity and lower metal leaching can be achieved by appropriately tuning the experimental conditions[15,18-22]. These materials are prepared by the covalent attachment of IL to the support surface or by simply depositing the IL phases containing catalytically active species, usually transition metal complexes[20] or, more rarely, metal nanoparticles[23,24] on the surface of the support, which is usually a silica or polymeric material. However, as in classical heterogeneous catalysis, the use of active polymeric membranes[25-30] has received little attention when compared with catalytically active inorganic membranes[31-34]. This can be attributed to the need to perform reactions in multiphase conditions at elevated temperatures that undermine the stability of the organic membrane. However, inorganic membranes (albeit with high chemical and thermal stability)[33] may be substituted by less expensive and more versatile polymeric organic membranes. The main characteristic of a membrane is its porous structure, which selectively allows components to pass from one side to the other[25]. Moreover, the unique structure of the catalytic polymeric membranes may have other additional advantages such as immobilizing more active and selective nanosized catalysts with a reduction in particles loss, prevention of nanoparticles agglomeration, and the establishment of a porous contact region between gas and liquid phases within the polymeric membrane structure[34]. Therefore, the combination of metal nanoparticles dispersed in an ionic liquid with a polymeric organic membrane such as cellulose derivatives[35-40] may generate new and versatile catalytic materials[41]. Indeed, we report that the association of rhodium[42] and platinum[43] nanoparticles with 1-n-butyl-3-methylimidazolium bis(trifluoromethane sulfonyl)imide (BMI.(NTf)2 and cellulose acetate generates polymeric membrane applied in hydrogenation of cyclohexene.

Experimental Section

General

All reactions were carried out under an argon atmosphere in modified Fischer-Porter Bottles. The halide-free 1-n-butyl-3-methylimidazolium tetrafluoroborate (BMI.BF4) and 1-n-butyl-3-methylimidazolium bis(trifluoromethane sulfonyl)imide BMI.N(Tf)2 IL were prepared according to a known procedure and dried over molecular sieves (4 Å)[44]. Cellulose acetate (Aldrich, 39.8 %wt of acetylation content) and acetone (Merck, 99.8 %) were used to prepare the polymeric membrane. All other chemicals were purchased from commercial sources and used without further purification. NMR spectra were recorded on a Varian Inova 300 spectrometer. Infrared spectra were performed on a Bomem B-102 spectrometer. Gas chromatography analysis was performed with a Hewlett-Packard-5890 gas chromatograph with an FID and a 30 m capillary column with a dimethylpolysiloxane stationary phase. The nanoparticle formations were carried out in a modified Fischer-Porter bottle. The temperature was maintained at 75 ºC with a hot-stirring plate connected to a digital controller (ETS-D4 IKA).

Synthesis of Rh(0) nanoparticles

Rhodium nanoparticles were prepared by simple hydrogen reduction (4 atm H2, constant pressure) of 0.026 g (0,1 mmol) of RhCl3.nH2O dissolved in 1-n-butyl-3-methylimidazolium tetrafluoroborate (BMI.BF4) at 75 ºC for 1 hour to yield a black suspension. Acetone (15 mL) was then added, and centrifugation of this mixture yielded nanoparticles of 4.8 ± 1.1 nm.

Synthesis of Pt(0) nanoparticles

Platinum nanoparticles were prepared by simple hydrogen decomposition (4 atm H2, constant pressure) of 0.054 g (0.1 mmol) of Pt2(dba)3 dissolved in BMI.BF4 at 75 ºC for 1.5 hours to yield a black suspension. Acetone (15 mL) was added, and centrifugation of this mixture yielded nanoparticles of 3.0 ± 0.4 nm.

Preparation of polymeric membrane

Cellulose acetate (CA) (10.0 g) was added to a reaction flask containing 90 mL of acetone, and the mixture was allowed to sit for 24 h at room temperature under a dry nitrogen atmosphere. After a viscous syrup was formed, 10.0 mg (0.1 mmol) of Rh(0) or 10.0 mg (0.05 mmol) of Pt(0) nanoparticles dispersed in 1.0 g of BMI.N(Tf)2 were added to 5.0 g of the syrup, respectively. The mixtures were magnetically stirred until a homogeneous phase was obtained. polymeric membranes, designated here as CA/IL/Rh(0) and CA/IL/Pt(0), respectively, were prepared by spreading the homogeneous phase over a glass plate. The thickness was controlled to 10, 20 and 40 µm by using a spacer. The solvent was evaporated in an open atmosphere for 2 min. A similar method was used to prepare blank CA polymeric membrane, except that no Rh(0) or Pt(0) nanoparticles were used[45-48].

Scanning electron microscopy (SEM) and electron dispersive spectroscopy (EDS)

The morphology of the polymeric membranes CA/IL/Pt(0) or CA/IL/Rh(0) and the electron dispersive spectroscopy analysis was performed using a JEOL model JSM 5800 with 10 and 20 kV and magnification of 3000-10000 X.

Transmission electron microscopy analysis (TEM)

TEM was obtained using a JEOL JEM 2010 microscope operating at 200 kV equipped with an EDS system and a JEOL JEM1200EXII operating at 120 kV. A 20 µm objective aperture and slightly under focused (Δƒ ≈ - 300 nm) objective lens were used to obtain the bright field TEM images. The samples were prepared by deposition of the Rh(0) or Pt(0) nanoparticles in isopropanol at room temperature on a carbon-coated copper grid. The histograms of the nanoparticle size distribution were obtained from measurements of around 300 diameters. For the analyses the nanoparticles of Rh(0) or Pt(0) immobilized in the polymeric membranes, the material was immobilized in resin and sliced with the technique of ultramicrotomy and placed on a carbon-coated copper grid.

N 2 adsorption-desorption isotherms

The specific surface area and pore size distribution of the CA/IL/Rh(0) and CA/IL/Pt(0) polymeric membranes were determined at nitrogen boiling point in a home-made volumetric apparatus with a vacuum line system employing a turbo molecular Edward vacuum pump, operating with temperature of 110 ºC during 2h . The pressure measurements were made using a capillary Hg barometer. The specific surface areas and pore size of the CA/IL/Rh(0) and CA/IL/Pt(0) polymeric membranes were determined from the BET multipoint method[49,50].

Infrared analysis (IR)

The infrared spectra of the polymeric membrane were obtained using a Shimadzu FTIR, model 8300. The spectra were obtained at room temperature with a resolution of 4 cm-1 and 100 cumulative scans.

Mechanical properties

The stress-strain behaviors of the polymeric membranes were analyzed by the module of a Dynamic Mechanical Analyzer (DMA Q800 V7.0), TA Instruments, using tension membrane geometry under isothermal temperature conditions (35 ºC). The Young's modulus, tensile stress and strain to break were calculated from the stress-strain curves obtained from the measurement.

Flame atomic absorption (FAAS)

Rhodium and platinum present in polymeric membranes were measured using a Perkin-Elmer (Boston, MA, United States) flame atomic absorption spectrometer, model Analyst 200 (FAAS), using an air-acetylene (10:2.5 l min-1) flame under optimized conditions. Hollow cathode lamps of Rh (λ = 343.5 nm) and Pt (λ = 265.9 nm) from the same manufacturer were used as radiation sources.

Hydrogenation reactions

The hydrogenation reactions of cyclohexene using CA/IL/Rh(0) and CA/IL/Pt(0) polymeric membranes were carried out in a modified Fischer-Porter Bottle connected to a hydrogen tank. The fall in the hydrogen pressure in the tank was monitored with a pressure transducer interfaced through a Novus converter to a PC, and the data workup was performed with Microcal Origin 5.0 software. For the hydrogenation reaction, 210 mg of CA/IL/Rh(0) or CA/IL/Pt(0) membrane was utilized in the Fischer-Porter reactor. The organic products were removed by simple decantation and analyzed by Gas Chromatograph.

Results and Discussion

The use of the compatible biopolymers to form polymeric membrane supporting for metal nanoparticles have to be application for catalytic reactions. The immobilization of metal nanoparticles rhodium and platinum using the advantages of ionic liquids (IL) combined with polymeric materials emerges as a new method for heterogeneous support materials. In this work, polymeric membranes of cellulose acetate, containing Rh(0) and Pt(0) nanoparticles, were prepared by the reduction of RhCl3 or decomposition of Pt2(dba)3 dispersed in BMI.BF4 ionic liquid, at 75 ºC under 4 atm of hydrogen, as described earlier. These nanoparticles were previously characterized by XRD and TEM analysis[42,43]. The nanoparticles were irregularly shaped with a monomodal size distribution of 4.8 ± 1.1 nm and 3.0 ± 0.4 nm for Rh(0)[42] and Pt(0),[43] respectively. The polymeric membranes CA/IL/Rh(0) and CA/IL/Pt(0), were characterized, and their mechanical and catalytic properties were investigated. For comparison, polymeric membranes containing the nanoparticles without the IL were also prepared. The SEM of the cross-sections of the CA/IL/Rh(0), CA/Rh(0) and CA/IL/Pt(0), CA/Pt(0) polymeric membranes are shown in Figures 1 and 2, respectively. It is clear that the morphological structure of the polymeric membranes changes with or without the presence of IL, the addition of the IL seems to cause an increase in the micro-structural order for both the CA/IL/Rh(0) (Figure 1a) and CA/IL/Pt(0) (Figure 2d) polymeric membranes. In contrast, the CA/Rh(0) polymeric membrane (Figure 1b) seems to have a scaled and porous structure. This result is in agreement with the general concept that imidazolium IL tend to act as entropic drivers for the formation nanostructure materials[44,45].



 




Figures 1 and 2 shows that the CA/IL/Rh(0) and CA/IL/Pt(0) films exhibit a skin that is relatively porous on the top side and a relatively porous structure over all of the polymeric membranes cross-sections.

Figure 2b shows that the sample prepared in the absence of the IL also stains heterogeneously over all of the polymeric membrane cross-section, indicating the presence of Pt(0) nanoparticles (represented by the clear points (BSE method). In the same figure, the CA/IL/Pt(0) polymeric membrane cross-section shows that the thickness of the polymeric membrane was about 21 µm. The BET surface areas of the polymeric membranes (20 µm) obtained in CA (5g) is summarized in Table 1. The surface area of the pure cellulose acetate polymeric membrane containing 0.5 g of BMI.N(Tf)2 was 38 m2/g (±10%), and that of the polymeric membrane with 1.0 g was 24 m2/g (±10%), demonstrating a reduction in the superficial area when the amount of IL was doubled. This result suggests that an additional increment of BMI.N(Tf)2 produces an occupation of the free porous arrangement in the polymeric membrane, especially in the predominant fraction. In the case of the cellulose acetate polymeric membrane containing Rh(0) and Pt(0) nanoparticles dispersed in the IL, surface areas of 113 m2/g (±10%) and 96 m2/g (±10%) were obtained, respectively. This indicates that the presence of small Rh(0) or Pt(0) nanoparticles induces an augmentation in the IL/cellulose acetate polymeric membrane surface area (compare entries 1 and 2 with 3 and 4, Table 1)

TEM micrographs of the polymeric membranes (20 µm) containing the metal nanoparticles in the presence of the IL (Figure 3) show that the metals are distributed all over the polymeric membrane but are more homogeneously distributed in the case of Pt(0).


The concentrations of Rh(0) and Pt(0) nanoparticles incorporated in the polymeric membranes was determined using FAAS (Table 2). The concentrations are expressed as µg g-1 and % (m/m) for Rh(0) and Pt(0) nanoparticles at the three thicknesses, 10, 20 and 40 µm. It is evident that the Rh(0) and Pt(0) metal concentration increased proportionally with increases in the polymeric membranes thickness up to 20 µm, after which, the material became saturated.

The IR spectra of the polymeric membranes with the same quantity of IL did not change in the presence of Rh(0) or Pt(0) (Figure 4).


The presence of the IL in the support was confirmed by the stretching band at 3170 cm-1 that is due to presence of aromatic C-H groups. After impregnation of the IL in the polymeric membrane supports, a significant decrease is observed in the intensity of the band at 3400 cm-1, attributed to the -OH stretching of the pure cellulose acetate, indicating participation of the -OH group in the interaction with the IL. The tensile stress versus strain at break curves of the pure and modified cellulose acetate polymeric membranes are shown in Figure 5.


The stress versus strain graphic is important information about Young's modulus (slope of linear region of the plot), tenacity, and stress versus strain at the break of polymeric membrane. Figure 5 show the stress versus strain curve profiles for different compositions of polymeric membrane. In Figure 5a, the stress-strain curves are similar for the CA/Rh(0), CA-1.0g IL, CA-1.0g/10 mg Pt(0) and CA-1.0g/10 mg Rh(0) polymeric membranes when compared to the pure CA polymeric membrane. These results indicate an increase of elasticity, decreases of tenacity and toughness (area under the stress-strain curve), and reduction of Young's modulus for the CA/Rh(0), CA-1.0 g IL, CA-1.0 g/10 mg Pt(0) and CA-1.0 g/10 mg Rh(0) polymeric membranes. The plasticizer effect of IL BMI.N(Tf)2 in the CA-1.0 g IL polymeric membrane reduces the intermolecular forces that are usually present in the cellulose acetate. In other words, it is possible that the bis(trifluoromethane sulfonyl)imide anion of the IL strongly interacts with the hydrogen bond networks formed in the cellulose acetate polymeric membranes chains through the nitrogen atom51. The stress-strain curve profiles of the CA-1.0 g IL-Rh(0) and CA-1.0 g IL-Pt(0) polymeric membranes are shown in Figure 5a. It is observed that the initial slope (Young's modulus) decreases with a decrease of the average diameter of 4.8 nm and 3.0 nm for Rh(0) and Pt(0) nanoparticles, respectively, and consequently, the degree of elasticity of the CA-1.0 g IL-Pt(0) polymeric membrane is larger compared to the CA-1.0 g IL-Rh(0) polymeric membrane. Figure 5b exhibits the range of IL quantified in the CA/IL/Pt(0) polymeric membrane composition. The catalytic properties of the CA/IL/Rh(0) and CA/IL/Pt(0) polymeric membranes were evaluated in hydrogenation reactions of cyclohexene (Table 3). For example, higher catalytic activity (TOF) was observed with 20 µm polymeric membranes employing 1.0 g of the IL compared to the 10 µm and 40 µm polymeric membranes (compare entries 1, 3 and 7 for Rh(0) and entries and 2, 4 and 10 for Pt(0) in Table 3. This is probably related to the relatively low stability of the 10 µm polymeric membranes, which undergo agglomeration during the hydrogenation, thus reducing the exposed area of the catalytically active species, and the membrane with 40 µm shown a large thickness for effective interaction between the substrate and nanoparticles. It is clear from the TOF data that the CA/IL/Pt(0) polymeric membranes are more active than those without the cellulose (compare entries 9 and 12 of Table 3, for example). This result is in line with those results observed for other supported IL phase catalysts[19]. It is also evident that the best relation between the two materials is 0.5 g of the IL and 5.0 g of cellulose acetate (compare entries 5, 6 and 7 and 8, 9 and 10 of Table 3 for Rh(0) and Pt(0) 20 µm thickness polymeric membranes, respectively).

Conclusions

The use of the biopolymer cellulose acetate (CA) support for Pt(0) or Rh(0) nanoparticles dispersed in IL generated functionalized polymeric membranes in which the mechanical, thermal and chemical stability was related to the amount of IL used. Therefore, the introduction of the IL is probably causing an increase in the distance between the cellulose molecules that result in a higher flexibility, and better formability of the polymeric membranes. The biopolymer/ionic liquid/metal nanoparticles, form the polymeric membranes, exhibits an excellent effect that enhances the activity and durability of the catalyst for the hydrogenation of cyclohexene.

Acknowledgments

Thanks are due to the following Brazilian Agencies: CNPq, CAPES and FAPERGS for fellowships and partial financial support.

Received: 12/13/12

Revised: 04/15/13

Accepted: 04/25/13

  • 1. Scheeren, C. W.; Hermes, V.; Bianchi, O.; Hertz, P. F.; Dias, S. L. & Dupont, J. - J Nanosci Nanotechnol., 11, p.1 (2011).
  • 2. Ding, B.; Kimura, E.; Sato, T.; Fujita, S. & Shiratori, S. - Polymer., 45, p.1895 (2004). http://dx.doi.org/10.1016/j.polymer.2004.01.026
  • 3. Nagendran, A. & Mohan, D. R. - Polym. Adv. Technol., 19, p.24 (2008). http://dx.doi.org/10.1002/pat.965
  • 4. Edgar, K. J.; Buchanan, E. K. C. M.; Debenham, J. S.; Rundquist, P. A.; Seiler, B. D.; Shelton, M. C. & Tindall, D. - Prog. Polym. Sci., 26, p.1605 (2001). http://dx.doi.org/10.1016/S0079-6700(01)00027-2
  • 5. Rezende, C. A.; Luchesi, C.; Barbo, M. L. P. & Duek, E. A. R. - Polímeros, 15, p.232 (2005). http://dx.doi.org/10.1590/S0104-14282005000300015
  • 6. Maria, L. C. S.; Santos, A. L. C.; Oliveira, P. C.; Valle, S. S.; Barud, H. S.; Messaddeq, Y. & Ribeiro, S. J. L. - Polímeros, 20, p.72 (2010). http://dx.doi.org/10.1590/S0104-14282010005000001
  • 7. Quadros, C. C.; Faria, V. W.; Klein, M. P.; Hertz, P. F. & Scheeren, C. W. - J Nanotechnol., 2013, p.1 (2013). http://dx.doi.org/10.1155/2013/140273
  • 8. Stoimenov, P. K.; Klinger, R. L.; Marchin, G. L. & Klabunde, K. J. - Langmuir., 18, p.6679 (2002). http://dx.doi.org/10.1021/la0202374
  • 9. Scheeren, C. W.; Hertz, P. F.; Hermes, V. & Dupont, J. - Process Biochem., 22, p.1123 (2011).
  • 10. Santa-Maria, L. C.; Oliveira, R. O.; Merçon, F.; Borges, M. E. R. S. P.; Barud, H. S.; Ribeiro, S. J. L.; Messaddeq, Y. & Wang, S. H. - Polímeros, 20, p.227 (2010).
  • 11. Müller, F.; Ferreira, C. A.; Amado, F. D. R. & Rodrigues, M. A. S. - Polímeros, 21, p.259 (2011). http://dx.doi.org/10.1590/S0104-14282011005000053
  • 12. Bellincanta, T.; Poletto, P.; Thürmer, M. B.; Duarte, J.; Toscan, A. & Zeni, M. - Polímeros, 21, p.229 (2011). http://dx.doi.org/10.1590/S0104-14282011005000045
  • 13. Thürmer, M. B.; Poletto, P.; Marcolin, M.; Ferreira, D. G. & Zeni, M. - Polímeros, 20, p.170 (2010). http://dx.doi.org/10.1590/S0104-14282010005000037
  • 14. Barud, H. S.; Ribeiro, S. J. L.; Carone, C. L. P.; Ligabue, R.; Einloft, S. & Jahno V. D. - Polímeros, 23, p.135 (2013).
  • 15. Steinrück, H. P.; Libuda, J.; Wasserscheid, P.; Cremer, T.; Kolbeck, C.; Laurin, M.; Maier, F.; Sobota, M.; Schulz, P. S. & Stark, M. - Adv. Mater., 23, p.2571 (2011). PMid:21520462. http://dx.doi.org/10.1002/adma.201100211
  • 16. Werner, S.; Haumann, M. & Wasserscheid, P. - Annual Rev. Chem. Biomolecular Eng., 1, p.203 (2010). PMid:22432579. http://dx.doi.org/10.1146/annurev-chembioeng-073009-100915
  • 17. Donato, R. K.; Migliorini, M. V.; Benvegnú, M. A.; Stracke, M. P.; Gelesky, M. A.; Pavan, F. A.; Schrekker, C. M. L.; Benvenutti, E. V.; Dupont, J. & Schrekker, H. S. - J Solgel Sci Technol., 49, p.71 (2009). http://dx.doi.org/10.1007/s10971-008-1829-6
  • 18. Bianchini, C. & Giambastiani, G. - Chemtracts, 16, p.301 (2003).
  • 19. Kohler, F.; Roth, D.; Kuhlmann, E.; Wasserscheid, P. & Haumann, M. - Green Chem., 12, p.979 (2010). http://dx.doi.org/10.1039/c004883f
  • 20. Feng, C. L.; Wang, Y. H. & Jin, Z. L. - Prog. Chem., 17, p.209 (2005).
  • 21. Haumann, M.; Dentler, K.; Joni, J.; Riisager, A. & Wasserscheid, P. - Adv. Synth. Catal., 349, p.425 (2007). http://dx.doi.org/10.1002/adsc.200600413
  • 22. Webb, P. B.; Kunene, T. E. & Cole-Hamilton, D. J. - Green Chem., 7, p.373 (2005). http://dx.doi.org/10.1039/b416713a
  • 23. Gelesky, M. A.; Chiaro, S. S. X.; Pavan, F. A.; dos Santos, J. H. Z. & Dupont, J. - Dalton Trans., 47, p.5549 (2007). PMid:18043816. http://dx.doi.org/10.1039/b708111a
  • 24. Zornoza, B.; Irusta, S.; Tellez, C. & Coronas, J. - Langmuir., 25, p.5903 (2009). PMid:19391574. http://dx.doi.org/10.1021/la900656z
  • 25. Bottino, A.; Capannelli, G.; Comite, A.; Del Borghi, A. & Di Felice, R. - Sep. Purif. Technol., 34, p.239 (2004). http://dx.doi.org/10.1016/S1383-5866(03)00196-5
  • 26. Centi, G. & Perathoner, S. - Catal. Today., 79, p.3 (2003). http://dx.doi.org/10.1016/S0920-5861(03)00036-1
  • 27. Khatib, S. J. & Oyama, S. T. - Sep. Purif. Technol., 11, p.20 (2013). http://dx.doi.org/10.1016/j.seppur.2013.03.032
  • 28. Fritsch, D. & Bengtson, G. - Catal. Today., 118, p.121 (2006). http://dx.doi.org/10.1016/j.cattod.2006.01.039
  • 29. Ozdemir, S. S.; Buonomenna, M. G. & Drioli, E. - Appl Catal A Gen., 307, p.167 (2006). http://dx.doi.org/10.1016/j.apcata.2006.03.058
  • 30. Kragl, U. & Dwars, T. - Trends Biotechnol., 19, p. 442 (2001). http://dx.doi.org/10.1016/S0167-7799(01)01766-8
  • 31. Belyakova, L. A.; Linkov, V. M.; Belyakov, V. N. & Bulavina, T. V. - Sep. Purif. Technol., 14, p.117 (1998). http://dx.doi.org/10.1016/S1383-5866(98)00066-5
  • 32. Tonkovich, A. L. Y.; Zilka, J. L.; Jimenez, D. M.; Roberts, G. L. & Cox, J. L. - Chem. Eng. Sci., 51, p.789 (1996). http://dx.doi.org/10.1016/0009-2509(95)00325-8
  • 33. Cuffe, L.; MacElroy, J. M. D.; Tacke, M.; Kozachok, M. & Mooney, D. A. J. - Membr. Sci., 272, p.6 (2006). http://dx.doi.org/10.1016/j.memsci.2005.12.021
  • 34. Xu, J.; Dozier, A. & Bhattacharyya, D. J. - Nanop. Res., 7, p.449 (2005). http://dx.doi.org/10.1007/s11051-005-4273-3
  • 35. Cai, J.; Kimura, S.; Wada, M. & Kuga, S. - Biomacromolecules, 10, p.87 (2009). PMid:19053296. http://dx.doi.org/10.1021/bm800919e
  • 36. Bagheri, M.; Rodriguez, H.; Swatloski, R. P.; Spear, S. K.; Daly, D. T. & Rogers, R. D. - Biomacromolecules, 9, p.381 (2008). PMid:18163541. http://dx.doi.org/10.1021/bm701023w
  • 37. El Seoud, O. A.; Koschella, A.; Fidale, L. C.; Dorn, S. & Heinze, T. Biomacromolecules, 8, p.2629 (2007). PMid:17691840. http://dx.doi.org/10.1021/bm070062i
  • 38. Viswanathan, G.; Murugesan, S.; Pushparaj, V.; Nalamasu, O.; Ajayan, P. M. & Linhardt, R. J. - Biomacromolecules, 7, p.415 (2006). PMid:16471910. http://dx.doi.org/10.1021/bm050837s
  • 39. Chiba, R.; Nishio, Y.; Sato, Y.; Ohtaki, M. & Miyashita, Y. - Biomacromolecules, 7, p.3076 (2006). PMid:17096534. http://dx.doi.org/10.1021/bm060567t
  • 40. Turner, M. B.; Spear, S. K.; Holbrey, J. D.; Daly D. T. & Rogers, R. D. Biomacromolecules, 6, p.2497 (2005). PMid:16153085. http://dx.doi.org/10.1021/bm050199d
  • 41. Migowski, P. & Dupont, J. - Chem. Eur. J., 13, p.32 (2007). PMid:17115465. http://dx.doi.org/10.1002/chem.200601438
  • 42. Gelesky, M. A.; Umpierre, A. P.; Machado, G.; Correia, R. R. B.; Magno, W. C.; Morais, J.; Ebeling, G. & Dupont, J. J. - Am. Chem. Soc., 127, p.4588 (2005). PMid:15796520. http://dx.doi.org/10.1021/ja042711t
  • 43. Scheeren, C. W.; Machado, G.; Teixeira, S. R.; Morais, J.; Domingos, J. B. & Dupont, J. J. - Phys. Chem. B, 110, p.13011 (2006). PMid:16805608. http://dx.doi.org/10.1021/jp0623037
  • 44. Cassol, C. C.; Ebeling, G.; Ferrera, B. & Dupont, J. - Adv. Synth. Catal., 348, p.243 (2006). http://dx.doi.org/10.1002/adsc.200505295
  • 45. Campos, E. A. & Gushikem, Y. J. - J Colloid Sci., 193, p.121 (1997). http://dx.doi.org/10.1006/jcis.1997.5051
  • 46. Kwon, J. W.; Yoon, S. H.; Lee, S. S.; Seo, K. W. & Shim, I. W. - Bull. Korean Chem. Soc., 26, p.837 (2005).
  • 47. Rodrigues, U. P.; Gushikem, Y.; Gonçalves, M. D.; Cachichi, R. C. & de Castro, S. C. - Chem. Mater., 8, p.1375 (1996).
  • 48. Feldman, J. & Orchin, M. J. - Mol. Catal., 63, p.213 (1990). http://dx.doi.org/10.1016/0304-5102(90)85145-8
  • 49. Barrett, E. P.; Joyner, L. G. & Halenda, P. P. - J. Am. Chem. Soc., 73, p.373 (1951). http://dx.doi.org/10.1021/ja01145a126
  • 50. Brunauer, S. - Langmuir, 3, p.3 (1987).
  • 51. Zhu, S. D.; Wu, Y. X.; Chen, Q. M.; Yu, Z. N.; Wang, C. W.; Jin, S. W.; Ding, Y. G. & Wu, G. - Green Chem., 8, p.325 (2006). http://dx.doi.org/10.1039/b601395c
  • Corresponding author:

    Carla Weber Scheeren
    Laboratório de Físico-Química, Escola de Química e Alimentos - EQA, Universidade Federal do Rio Grande - FURG
    Av. Itália, Km 8, s/n, Campus Carreiros
    CEP 96201-900, Rio Grande, RS, Brasil
    e-mail:
  • Publication Dates

    • Publication in this collection
      18 Apr 2014
    • Date of issue
      2014

    History

    • Accepted
      25 Apr 2013
    • Received
      13 Dec 2012
    • Reviewed
      15 Apr 2013
    Associação Brasileira de Polímeros Rua São Paulo, 994, Caixa postal 490, São Carlos-SP, Tel./Fax: +55 16 3374-3949 - São Carlos - SP - Brazil
    E-mail: revista@abpol.org.br