Analysis of 3D Planar Laminations in a Welded Section of API 5L X52 Applying the Finite Element Method

Abstract

The mechanical behavior of API 5L X52 steel with planar type laminations was studied in the present work. Planar laminations were proposed in the base metal (BM), heat affected zone (HAZ) and welding bead (WB). Three-dimensional finite element (FE) models, kinematic hardening and mechanical properties for BM, HAZ, and WB were activated in the finite element program. The results showed that crack propagation corresponds to the direction of the main stress. For a crack length (2a) of 10.01 mm, crack propagation may occur at the right crack tip towards the outer wall of the BM. For 2a of 15.12 mm, crack propagation was located on the right crack tip and propagates to the inner wall. For 2a of 17.12 mm, crack propagation was observed at the left crack tip and propagates to the outer wall in the BM. The results achieved by FEM agree when compared with real laminations in API 5L pipelines.

Keywords:
Planar laminations; API 5L X52 pipeline; Welded section; Finite element; Failure pressure

Nomenclature
BM base metal
FE finite element
FEM finite element method
H atomic hydrogen
HAZ heat affected zone
HIC hydrogen induced cracking
Pcrack internal pressure on the crack
Pf failure pressure
WB welding bead
σYS yield stress
σUTS ultimate tensile stress
2a crack length

1. Introduction

Pipelines are the safest and most reliable means of transportation for hydrocarbons. However, the anticorrosive system (cathodic protection and coating) can present problems or fail and the pipelines may be in contact with corrosive medium. This fact could motivate material degradation in any corrosion form, including cracking. The appearance of cracks makes the pipeline reliability decrease, causing the operational risk to increase [ 11 Caleyo F, Valor A, Venegas V, Espina-Hernandez JH, Velazquez JC, Hallen JM. Pipeline Integrity—1: accurate corrosion modeling improves reliability estimations. Oil & Gas Journal. 2012;110:122-128. ].

It is widely recognized that cracking associated with an acidic environment is classified as hydrogen induced cracking (HIC) and plays an important role in the oil and natural gas industry [ 22 Still J.R. 2004. Understanding hydrogen failures of ferritic welds. Welding Journal. 82(1):26-29. , 33 Ossai CI, Boswell B, Davies IJ. Pipeline failures in corrosive enviroments – a conceptual analysis of trend and effects. Engineering Failure Analysis. 2015;53:36-58. http://dx.doi.org/10.1016/j.engfailanal.2015.03.004.
http://dx.doi.org/10.1016/j.engfailanal...
]. Atomic hydrogen (H) can diffuse through steel and penetrate into the metal. H has various possible sources, such as a high-temperature, moist atmosphere, corrosion processes and electrolysis [ 44 Fontana MG. Corrosion engineering. New York: McGraw Hill; 1987. ]. Therefore, it forms on the surface of the steel due to iron and H2S corrosion reactions [ 55 Liou HY, Shieh RI, Wei FI, Wang SC. Roles of microalloying elements in hydrogen induced cracking resistant property of HSLA Steels. Corrosion. 1993;49(5):389-398. http://dx.doi.org/10.5006/1.3316066.
http://dx.doi.org/10.5006/1.3316066 ...
]. The H is absorbed on the inner surface of the wall of a steel pipeline and diffuses, see Figure 1 . So, this hydrogen diffuses across the material and combines to form hydrogen molecules. It can be placed in defects; voids, holes, inclusions, impurities, dislocations or micro-cracks. Since molecular hydrogen cannot migrate from these defects [ 66 Ravi K, Ramaswamy V, Namboodhiri TKG. Hydrogen sulphide resistance of high sulphur microalloyed steels. Materials Science and Engineering A. 1990;129(1):87-97. http://dx.doi.org/10.1016/0921-5093(90)90347-6.
http://dx.doi.org/10.1016/0921-5093(90)...
], the pressure of hydrogen gas in the voids increases.

Figure 1
Schematic illustration of the mechanism for the lamination.

The mechanisms of HIC are closely related to the hydrogen diffusive process through metal. The driving force for the hydrogen diffusion in steel is mainly due to a gradient of hydrogen concentration, a state of non-uniform stress or a combination of both [ 77 Romero M.F., Duque Z., Rincón O.T., Pérez O. & Araujo I. 2003. Estudio de la teoría de despolarización catódica con permeación de hidrógeno y la bacteria Desulfovibrio desulfuricans. Revista de Metalurgia. 39(1):182-187. http://dx.doi.org/10.3989/revmetalm.2003.v39.iExtra.1117.
http://dx.doi.org/10.3989/revmetalm.200...
]. HIC is highly influenced by metallurgical parameters such as non-metallic inclusions, segregation bands of elements (P, Mn), grain boundaries, dislocations, microstructure, hardness, structural defects, and internal stresses. In addition, chemical parameters related to electrolytic media, such as H2 concentration, pH, solution composition, exposure time, temperature, pressure and stresses applied. On the other hand, the surface finish has a significant influence on the diffusion process. Depending on the topographical characteristics of the surface, atomic hydrogen could be favored [ 88 Requiz R, Vera N, Camero S. Influencia del acabado superficial en la permeaciòn de hidrógeno del acero API 5L X52. Revista de Metalurgia. 2004;40(1):30-38. http://dx.doi.org/10.3989/revmetalm.2004.v40.i1.240.
http://dx.doi.org/10.3989/revmetalm.200...
, 99 Carreño J.A., Uribe I. & Carrillo J.C. 2003. Modelado del efecto de rugosidad en la permeación de hidrógeno en un acero de bajo carbono. Revista de Metalurgia. 39(1):213-218. ].

When the hydrogen molecule is placed in the defect, cracking is produced. HIC is characterized by stepped lamination or planar lamination. This cracking growth is in the same plane, parallel to the wall of the pipeline [ 1010 Gonzalez JL, Ramirez R, Hallen JM, Guzman RA. Hydrogen-induced crack growth rate in steel plates exposed to sour environments. Corrosion. 1997;53(12):935-943. http://dx.doi.org/10.5006/1.3290278.
http://dx.doi.org/10.5006/1.3290278 ...
]. According to Iino [ 1111 Iino M. The extension of hydrogen blister-crack array in linepipe steels. Metallurgical Transactions. A, Physical Metallurgy and Materials Science. 1978;9a(11):1581-1590. http://dx.doi.org/10.1007/BF02661940.
http://dx.doi.org/10.1007/BF02661940 ...
], a stress state in the vicinity of the crack tip is significantly influenced by the hoop external stress in API 5L pipelines.

There are other sources of hydrogen that can be added to the metal, such as when the steel is in the refining stage. Hydrogen is incorporated with raw materials (scrap, lime, etc) in the form of water or through moisture in the air. It is highly harmful, causes cracking and brittleness in the steel, and lowers ductility in cold work. At this stage, the steel has low levels of H 2 (g) [ 1212 Maarten G, Hisko T, Corvan DV. Modern blast furnace ironmaking: an introduction. 2nd ed. Netherlands: Delf University Press; 2009. , 1313 Ahindra G, Amit C. Iron making and steelmaking: theory and practice. India: PHI Learning; 2008. ]. Also, in pipeline manufacturing processes that require welding. In this process, the H 2 can be added in the liquid state.

A lot of researchers have carefully studied the cracking speed [ 1414 Ramirez JA. Susceptibilidad al agrietamiento inducido por hidrógeno absorbido, de la soldadura y zona afectada por el calor, en aceros para transporte de hidrocarburos [master degree thesis]. México DF: ESIQIE-IPN; 2003. ] or the use of finite element method (FEM) to evaluate the mechanical behavior of several types of cracking for API 5L pipelines [ 1515 Ikeda A, Morita Y, Terasaki F, Takeyama M. On the hydrogen induced cracking of line-pipe steel under wet hydrogen sulfide environment. Proceedings of The 2nd International Congress on Hydrogen in Metals; 1997 June 6-11; Paris. France; 1977. p. 1-8. 23 Ruggieri C, Dotta F. Numerical modeling of ductile crack extension in high pressure piplines with longitudinal flaws. Engineering Structures. 2011;33(5):1423-1438. http://dx.doi.org/10.1016/j.engstruct.2011.01.001.
http://dx.doi.org/10.1016/j.engstruct.2...
24 Nourpanah N, Taheri F. Ductile crack growth and constrain in pipeline subject to combined loading. Engineering Fracture Mechanics. 2011;78(9):2010-2028. http://dx.doi.org/10.1016/j.engfracmech.2011.03.018.
http://dx.doi.org/10.1016/j.engfracmech...
25 Nourpanah N, Taheri F. A numerical study on the crack tip constrain of pipelines subject to extreme plastic bending. Engineering Fracture Mechanics. 2011;78(6):1201-1217. http://dx.doi.org/10.1016/j.engfracmech.2010.11.021.
http://dx.doi.org/10.1016/j.engfracmech...
26 Zhang YM, Xiao ZM, Zhang WG. On 3-D crack problems in offshore pipeline with large plastic deformation. Theoretical and Applied Fracture Mechanics. 2013;67-68:22-28. http://dx.doi.org/10.1016/j.tafmec.2014.01.001.
http://dx.doi.org/10.1016/j.tafmec.2014...
- 2727 Zhang YM, Yi DK, Xiao ZM, Huang ZH, Kumar SB. Elastic-plastic fracture analysis for pipeline girth welds with 3D semi-elliptical surface cracks subjected to large plastic bending. International Journal of Pressure Vessels and Piping. 2013;105-106:90-102. http://dx.doi.org/10.1016/j.ijpvp.2013.03.009.
http://dx.doi.org/10.1016/j.ijpvp.2013....
]. Those works are for the BM, while other works are focused on the hydrogen diffusion in pipelines [ 2828 Kittel J, Ropital F, Pellier J. Effect of membrane thickness on hydrogen permeation in steels during wet hydrogen sulfide exposure. Corrosion. 2008;64(10):788-799. http://dx.doi.org/10.5006/1.3278446.
http://dx.doi.org/10.5006/1.3278446 ...

29 Olden V, Alvaro A, Akselsen OM. Hydrogen diffusion and hydrogen influenced critical stress intensity in an API X70 pipelines steel welded joint – Experiments and FE simulations. International Journal of Hydrogen Energy. 2012;37(15):11474-11486. http://dx.doi.org/10.1016/j.ijhydene.2012.05.005.
http://dx.doi.org/10.1016/j.ijhydene.20...
- 3030 Alvaro A, Olden V, Akselsen OM. 3D cohesive modelling of hydrogen embrittlement on the heat affected zone of an X70 pipeline steel – Part II. International Journal of Hydrogen Energy. 2014;39(7):3528-3541. http://dx.doi.org/10.1016/j.ijhydene.2013.12.097.
http://dx.doi.org/10.1016/j.ijhydene.20...
], and HIC [ 3131 Traidia A, Alfano M, Lubineau G, Duval S, Sherik A. An effective finite element model for the prediction of hydrogen induced cracking in steel pipelines. International Journal of Hydrogen Energy. 2012;37(21):16214-16230. http://dx.doi.org/10.1016/j.ijhydene.2012.08.046.
http://dx.doi.org/10.1016/j.ijhydene.20...
]. Unfortunately, at present, there are no work for planar laminations in the BM, HAZ, WB.

This paper attempts to obtain the mechanical resistance of an API 5L X52 pipeline with planar laminations in the BM, HAZ, WB, with particular focus on the stresses fielded at the crack tips and crack propagation. Three-dimensional finite element models were applied using the FEM technique. Internal pressure was placed on the crack (Pcrack) to generate yield stress (σYS), ultimate tension stress (σUTS) and failure pressure (Pf). In addition, tension tests were conducted to obtain the stress-strain curves for the BM, HAZ and WB. To obtain the stress-strain curve of HAZ, the Vickers (HV) hardness profile was measured and applied to correlations between stresses and hardness.

2. Materials and Methods

2.1. Mechanical properties for BM, HAZ, WB

A sample specimen for the analysis (BM, HAZ, WB) is depicted in Figure 2 . It is noted that this specimen is only of example, since in this work a pipeline with a wall thickness of 25.4 mm was used. Tension and hardness Vickers (HV) tests were performed with the purpose of obtaining stress-strain curves for the zones of interest, such as BM, HAZ and WB. Standard specimens were machined following the ASTM E8-01 [ 3232 American Society for Testing and Materials. ASTM E8–01: standard test methods for tension testing of metallic materials. West Conshohocken: ASTM; 2001. ]. By doing this, tensile tests were carried out in a servohydraulic machine. The load was applied at a speed of 1.8 mm/min according to ASTM E8. Three tension specimens were tested in each zone and the specimens were extracted in the longitudinal direction of the API 5L X52 with 609.6 mm outer diameter and 25.4 mm wall thickness. Figure 3 show the specimen’s dimension.

Figure 2
API 5L X52 pipeline, specimen extracted, heat affected zone (HAZ), weld bead (WB), and base metal (BM).
Figure 3
Specimen dimensions for the tension testing gage length (G), diameter (D), radius of fillet (R), width of grip section (C), length of reduced section (A), length of grip section (B), over-all length (L).

2.2. Geometrical details

In this section, it was considered the cracking that had developed in the BM and could propagate to the HAZ and WB without passing this last region (WB) [ 3333 Ramirez JA, Gonzalez JL. Hydrogen induced cracking of welds in steel pipelines, design and analysis of pressure vessels and piping: implementation of ASME B31 - fatigue, ASME section VIII, and buckling analyses, PVP2003-2182. New York: ASME; 2003. ]. It is well-known that high hydrogen pressure inside the crack is the main driving force for crack growth. Crack propagation of HIC in steel pipelines could occur in pipelines exposed to sulfurous compounds, such as hydrogen sulfite H2S [ 3131 Traidia A, Alfano M, Lubineau G, Duval S, Sherik A. An effective finite element model for the prediction of hydrogen induced cracking in steel pipelines. International Journal of Hydrogen Energy. 2012;37(21):16214-16230. http://dx.doi.org/10.1016/j.ijhydene.2012.08.046.
http://dx.doi.org/10.1016/j.ijhydene.20...
]. Based on this, Figure 4 presents a penny-shaped lamination model proposed for the present analysis.

Figure 4
API 5L X52 pipeline: a) an embedded lamination at the mil-wall thickness, b) 3D FE model for the representation of planar lamination in the BM, HAZ, WB.

Variables used in the numerical experimentation are presented in Table 1 . The pipeline length (L) for all conditions were 76.2 mm. It was proposed a crack that could start in the BM and propagate towards the HAZ, WB in a straigh extension. This initial crack was considered because it reached the form of a parallel crack towards the surface of the pipeline for a modeling profile during its formation by HIC. It was assumed that cracks produced by cathodic charging testing grow at a flat spread to approximately 50% of the wall thickness (2/t) [ 3333 Ramirez JA, Gonzalez JL. Hydrogen induced cracking of welds in steel pipelines, design and analysis of pressure vessels and piping: implementation of ASME B31 - fatigue, ASME section VIII, and buckling analyses, PVP2003-2182. New York: ASME; 2003. ]. Therefore, this value was defined to locate the crack in the wall thickness. The crack cut across the HAZ completely and propagated in the WB stopping halfway through this region [ 3434 Gonzalez JL, Hallen JM. Mecánica de fractura en ductos de recolección y transporte de hidrocarburos. 3º Congreso de Ductos PEMEX; 1998 Diciembre 7-9; México DF. México; 1998. 183-191. ]. Based on this, the largest extension for the crack length was defined (2a), 100% of the MB (10.01 mm) see Figure 5 a), 100% of the HAZ (15.12 mm) see Figure 5 b) and 50% of the WB (17.24 mm) see Figure 5 c).

Table 1
Variables used in the numerical experimentation.
Figure 5
Planar lamination configurations for conditions using FE based on Table 3 , a) 1, 4, 7, b) 2, 5, 8, and c) 3, 6, 9.

Yan, et al [ 2121 Yan C, Liu C, Yan B. 3D modeling of the hydrogen distribution in X80 pipeline steel welded joints. Computational Materials Science. 2014;83:158-163. http://dx.doi.org/10.1016/j.commatsci.2013.11.007.
http://dx.doi.org/10.1016/j.commatsci.2...
] found that hydrogen concentration in the HAZ is very high, and crack propagation could pass the HAZ completely. Thus, for the configurations considered here, the number of simulations was 9. These experimental groups used a diameter and thickness of 609.6 mm and 6.35, 9.525 and 12.7 mm, respectively, considering ratios of D/t = 96, 64, and 48.

2.3. FE models

In Figure 6 , typical FE meshing for a pipeline is illustrated. A finite finite element software [ 3535 Ansys Inc. Introduction to ANSY for Release 8.0. Canonsburg: ANSYS; 2003. ] was used in this study. Since the main purpose of this paper was to study the mechanical resistance of pipelines with planar lamination for the model proposed, a high degree of mesh refinement at the crack tips was needed, and large elements for the rest of the pipeline were used. Alvaro, et al [ 2020 Alvaro A, Olden V, Akselsen OM. 3D cohesive modelling of hydrogen embrittlement in the heat affected zone of an X70 pipeline steel. International Journal of Hydrogen Energy. 2013;38(18):7539-7549. http://dx.doi.org/10.1016/j.ijhydene.2013.02.146.
http://dx.doi.org/10.1016/j.ijhydene.20...
] found that the local stress and strain fields are strongly dependent on the mesh size. In this sense, second order elements (solid 95) and first order elements (solid 45) [ 3636 Ansys Inc. Release ANSYS 8.0 documentation: element reference - part I: element library. Canonsburg: ANSYS; 2003. ] were assigned to mesh the crack tips and the rest of the pipeline, respectively, see Figure 7 . The angle of the elements at the crack tips was 18°. Madenci, et al [ 3737 Madeci E, Guven I. The finite element method and applications in engineering using Ansys. Springer; 2006. ] used angles of 15° to mesh the crack tips using finite program. Chong et al. [ 1919 Chong TS, Kumar SB, Lai M, Loh WL. Fracture capacity of morden pipeline girth welds with 3D surface cracks under extreme operation conditions. Engineering Fracture Mechanics. 2015;146:139-160. http://dx.doi.org/10.1016/j.engfracmech.2015.07.032.
http://dx.doi.org/10.1016/j.engfracmech...
] proposed angles of 15°-22.5° to mesh canoe-shaped cracks. Yi et al. [ 2222 Yi D, Xiao ZM, Idapalapati S, Kumar SB. Fracture analysis of girth welded pipelines with 3D embedded cracks subjected to biaxial loading conditions. Engineering Fracture Mechanics. 2012;96:570-587. http://dx.doi.org/10.1016/j.engfracmech.2012.09.005.
http://dx.doi.org/10.1016/j.engfracmech...
] employed angles of 18° to mesh 3D cracking in pipelines. Plastic flow with isotropic hardening was activated in the finite element program to include non-linear analysis and simulate the material behavior for the BM, HAZ and WB.

Figure 6
Typical FE meshing for pipeline with planar lamination.
Figure 7
Isoparametric elements of first order (solid 45) and second order (solid 95).

Geometry modeling and FE generation were done in the rectangular coordinate system and then transferred to the cylindrical coordinate system to impose boundary conditions on the pipeline in the circumferential direction on the edge of the section. In this case, displacement by loads allowed free expansion of the pipeline, similar to what occurred in the real pipeline case. As illustrated in Figure 8 a), axial boundary conditions were applied to the ends of the pipeline to simulate the continuity of a long pipeline. Pressure was applied to the inner surface of the crack until the σ YS of the material was reached, see Figure 8 b). When this value was reached, pressure was applied to the inner surface of the pipeline, until the σYS of the material was reached, see Figure 8 c). This allowed the researchers to assess the load through pressure on a pipeline. Then, the pipeline was pressurized to achieve the σUTS, and to define the operating range of the non-linear regime. The kinematic hardening rule was considered only to transfer the yield surface, plastically strain the material by increasing the stress until the σ YS and σUTS of the material was reached [ 3838 Meyers MA, Chawla KK. Mechanical behavior of materials. Cambridge: Prentice Hall; 1999. ]. This formulation was valid for representing a proper model for the real material [ 3939 Dowling NE. Mechanical behavior of materials, engineering methods for deformation, fracture, and fatigue. 2nd Edition. Prentice Hall; 1999. ], which is the situation considered in the present work.

Figure 8
Typical loading and boundary conditions for the 3D finite element, a) boundary conditions, b) internal pressure for the crack, and c) internal pressure for the pipeline.

3. Results

3.1. Mechanical properties results

Table 2 summarizes the material properties for the three materials, BM, HAZ and WB. By using a relationship from this HV data, an equivalent true stress-strain curve in the HAZ was estimated. This data is depicted in Table 3 , which presents the HV data. Hardness Vickers data was converted to stress-strain values by correlations with the corresponding hardness value obtained from the other two regions (BM and WB) and related to the stress-strain curves in order to obtain a curve proposed for the HAZ. Figure 9 a) presents the engineering stress-strain curves and Figure 9 b) shows the true stress-strain curves proposed.

Table 2
Mechanical properties for BM, HAZ and WB.
Table 3
Vickers hardness (HV) test results for the BM, HAZ, WB.
Figure 9
a) Engineering stress-strain curves and b) true stress-plastic curves extracted from API 5L X52 steel. Base Metal (BM), Heat Affected Zone (HAZ), Welding Bead (WB).

3.2 Pressure obtained by FEM

Table 4 presents the pressures obtained by the FEM. The pressures recorded are: (i) pressure in the crack (Pcrack) applied to generate the σYS, (ii) pressure in the pipeline (PYS) applied to generate the σYS, (iii) pressure in the pipeline (PUTS) applied to generate the σUTS , and (iv) the pressure in the pipeline applied to generate the failure pressure (Pf ).

Table 4
Pressures obtained by FEM in MPa.

4. Discussion

4.1. Presure data by FEM

Plots of the pressure obtained by the FEM as a function of 2a were made, see Figure 10 . The Pf is defined as the pressure that makes the Von Mises stress in the outer and inner wall of the planar lamination reach or surpass the σUTS of the material. These conditions indicate the failure of pipelines with planar lamination.

Figure 10
Plots of pressures obtained by FEM, a) Pcrack, b) PYS, c) P UTS and d) Pf .

For three ratios (D/t = 48, 64 and 96), it can be observed that the Pcrack pressure required in the crack to generate σYS in the material decreases as the 2a increases, see Figure 10 a). This trend was attributed to the fact that the crack size is greater. The cases of the P YS, PUTS, and Pf, Figures 10 b), c) and d), respectively, show an increased behavior of pressure as the pressure was increased to the 2a. This behavior was attributed to the internal pressure related to the stress of the material. To reach high stress values, it was necessary to increase the pressure inside of the pipeline.

High hydrogen pressure inside a crack is the main driving force for crack growth. There are experimental works to simulate crack propagation in API 5L pipelines. Traidia, et al [ 3131 Traidia A, Alfano M, Lubineau G, Duval S, Sherik A. An effective finite element model for the prediction of hydrogen induced cracking in steel pipelines. International Journal of Hydrogen Energy. 2012;37(21):16214-16230. http://dx.doi.org/10.1016/j.ijhydene.2012.08.046.
http://dx.doi.org/10.1016/j.ijhydene.20...
], employed pressure of 100 mbar of H2S for crack propagation. He found that the crack growth rate was mainly controlled by the material fracture toughness, crack location, pH, and wall thickness of the pipelines. Kittel et al. [ 2828 Kittel J, Ropital F, Pellier J. Effect of membrane thickness on hydrogen permeation in steels during wet hydrogen sulfide exposure. Corrosion. 2008;64(10):788-799. http://dx.doi.org/10.5006/1.3278446.
http://dx.doi.org/10.5006/1.3278446 ...
] used the partial pressure of H2S (3 mbar-1000 mbar] with different values of thickness (0.5 mm-10 mm). For simulation works, Servin et al. [ 1616 Alberto S, Gonzalez JL, Morales A. Behavior of coplanar and non-coplanar laminations in API5L X52 simulated by finite elements. Información Tecnológica. 2009;20(5):97-105. ] used pressures of 46.4-264 MPa for 3D coplanar laminations in BM. He found that increasing the pressure in the lamination, the maximum stress at the crack tips spread out in a perpendicular direction, which is an indication of a probable growth in the crack. Morales et al. [ 1717 Morales A, Gonzalez JL, Hallen JM. Mechanical behavior of non-coplanar cracks in pipes applying the finite elements method. Información Tecnológica. 2004;15(6):29-34. ] used pressure values up to 1.72 MPa and the load defects were pressured until total plastification in the lamination was reached. Gonzalez et al. [ 1818 Gonzalez JL, Morales A. Analysis of laminations in X52 steel pipes by nonlinear by finite element. International Journal of Pressure Vessel and Technology. 2008;130(2):021706. http://dx.doi.org/10.1115/1.2894295.
http://dx.doi.org/10.1115/1.2894295 ...
] used pressure variations, 14-124 MPa, in coplanar laminations to achieve the maximum stress of the material (400 MPa) at the crack tips.

Kittel [ 2828 Kittel J, Ropital F, Pellier J. Effect of membrane thickness on hydrogen permeation in steels during wet hydrogen sulfide exposure. Corrosion. 2008;64(10):788-799. http://dx.doi.org/10.5006/1.3278446.
http://dx.doi.org/10.5006/1.3278446 ...
] and Traidia [ 3131 Traidia A, Alfano M, Lubineau G, Duval S, Sherik A. An effective finite element model for the prediction of hydrogen induced cracking in steel pipelines. International Journal of Hydrogen Energy. 2012;37(21):16214-16230. http://dx.doi.org/10.1016/j.ijhydene.2012.08.046.
http://dx.doi.org/10.1016/j.ijhydene.20...
] reported pressures of H2S from 100 mbar and 3-1000 mbar, respectively, for API X65 steel. These values should be considered for making comparisons of pressure in laminations. Even though they cannot be compared at present, since an API 5L X52 is already being employed, it can be observed that the pressures are low. Pressure data reported by Servin [ 1616 Alberto S, Gonzalez JL, Morales A. Behavior of coplanar and non-coplanar laminations in API5L X52 simulated by finite elements. Información Tecnológica. 2009;20(5):97-105. ], Morales [ 1717 Morales A, Gonzalez JL, Hallen JM. Mechanical behavior of non-coplanar cracks in pipes applying the finite elements method. Información Tecnológica. 2004;15(6):29-34. ] and Gonzalez [ 1818 Gonzalez JL, Morales A. Analysis of laminations in X52 steel pipes by nonlinear by finite element. International Journal of Pressure Vessel and Technology. 2008;130(2):021706. http://dx.doi.org/10.1115/1.2894295.
http://dx.doi.org/10.1115/1.2894295 ...
] are high. These pressure values are used to obtain the maximum stress of the material at the crack tips. As shown in Figure 10 a), for 2a of 10.01, 15.12 and 17.24 mm, the pressures are 117.10, 72.1 and 46.88 MPa, respectively. It is noted that the ratio of D/t = 96 (t = 6.35 mm) is the lower thickness in the present study. As observed, this pressure of H2S is low compared to the pressure obtained in the present work. It is necessary to mention that the pressures of H2S are only for the crack propagation

4.2. Analysis of planar laminations by FEM

In the 3D FE model, the crack front fields are increasingly affected by the out of plane stress state based on the applied pressure levels [ 2020 Alvaro A, Olden V, Akselsen OM. 3D cohesive modelling of hydrogen embrittlement in the heat affected zone of an X70 pipeline steel. International Journal of Hydrogen Energy. 2013;38(18):7539-7549. http://dx.doi.org/10.1016/j.ijhydene.2013.02.146.
http://dx.doi.org/10.1016/j.ijhydene.20...
]. The results of the simulations showed similar behavior according to the stress behavior for all pipelines. Only the analysis for the first condition was described, where a pipeline was considered with a 609.6 mm diameter, a wall thickness of 12.7 mm, and a D/t = 48, 2a of 10.01 mm in BM. Figure 11 a) shows Von Mises stresses distribution with the Pcrack of 231.51 MPa. This figure shows that greater stresses are located at the vicinity of the crack tips. In this case, the outer and inner walls in the middle of the crack presented stresses higher than σ YS of the material (376 MPa). These zones and the the tips of the cracks are affected. For three D/t conditions analyzed where the pressure is constant in the Pcrack , the stresses showed a tendency to be distributed across the wall thickness. In these zones, it was reaching a stress value of σUTS. A typical example of σ UTS is shown in Figure 11 b). The mode of the main stress at the crack tips corresponds to the field stress of the plastic zone for mode I, which agree with the model proposed by Ikeda [ 1515 Ikeda A, Morita Y, Terasaki F, Takeyama M. On the hydrogen induced cracking of line-pipe steel under wet hydrogen sulfide environment. Proceedings of The 2nd International Congress on Hydrogen in Metals; 1997 June 6-11; Paris. France; 1977. p. 1-8. ].

Figure 11
Typical view of the Von Mises stress for pipeline with planar lamination in BM, a) P crack and b) PUTS, units in MPa.

Wall thickness in the radial direction, combined with the effect of the hoop stresses produced by internal pressure in the pipeline, caused the stresses produced near the crack tips to be distributed across the wall thickness. To achieve the maximum strength value, the outer walls are plastified, which causes the failure by plastic collapse to become real. Vigdis [ 2929 Olden V, Alvaro A, Akselsen OM. Hydrogen diffusion and hydrogen influenced critical stress intensity in an API X70 pipelines steel welded joint – Experiments and FE simulations. International Journal of Hydrogen Energy. 2012;37(15):11474-11486. http://dx.doi.org/10.1016/j.ijhydene.2012.05.005.
http://dx.doi.org/10.1016/j.ijhydene.20...
, 3030 Alvaro A, Olden V, Akselsen OM. 3D cohesive modelling of hydrogen embrittlement on the heat affected zone of an X70 pipeline steel – Part II. International Journal of Hydrogen Energy. 2014;39(7):3528-3541. http://dx.doi.org/10.1016/j.ijhydene.2013.12.097.
http://dx.doi.org/10.1016/j.ijhydene.20...
] assumed that failure occurs as soon as the first cohesive element at the crack tips has reached complete separation in the 3D FE simulations for the pipeline. When the maximum stress has been reached to separate the first element of the crack tip, crack propagation is carried out toward the areas where the wall thickness is weakest. As can be seen from Figure 11 , maximum stresses are located at the crack tips. It indicates the stresses interacting at this region, which align with the development of cracking due to the interconnection of perpendicular cracks [ 1111 Iino M. The extension of hydrogen blister-crack array in linepipe steels. Metallurgical Transactions. A, Physical Metallurgy and Materials Science. 1978;9a(11):1581-1590. http://dx.doi.org/10.1007/BF02661940.
http://dx.doi.org/10.1007/BF02661940 ...
]. The above situation agrees with the fracture mechanics postulate, the direction of cracking corresponds to the direction of the main stresses.

Figure 12 - 14 shows the Von Mises stress causing failure in the pipeline for all conditions in the present work. It was observed in this figure that, for all work conditions, the stress distribution is higher at the crack tips in the part of the zone cracking (outer and inner wall), with certain stress variants at the BM and WB.

Figure 12
Von Mises stress for failure pressure in a pipeline with planar laminations with D/t of 48; a) 2a of 10.01 mm, b) 2a of 15.12 mm and c) 2a of 17.12 mm, units in MPa.
Figure 13
Von Mises stress for failure pressure in a pipeline with planar laminations with D/t of 64; a) 2a of 10.01 mm, b) 2a of 15.12 mm and c) 2a of 17.12 mm, units in MPa.
Figure 14
Von Mises stress for failure pressure in a pipeline with planar laminations with D/t of 96; a) 2a of 10.01 mm, b) 2a of 15.12 mm and c) 2a of 17.12 mm, units in MPa.

By using the Von Mises stress for the failure pressures, the failure of pipelines with planar lamination in the MB, HAZ, WB could be predicted by FE. For example, for 2a of 10.01 mm and ratios of D/t=48, 64 and 96, crack propagation may occur at the right crack tip towards the outer wall of the BM. For 2a of 15.12 mm and ratios of D/t = 48, 64 and 96, crack propagation is located on the right crack tip and propagates to the inner wall. Finally, for 2a of 17.12 mm and ratios of D/t=48, 64 and 96, crack propagation is observed at the left crack tip and propagates to the outer wall in the BM. Everything described above is depicted in Figure 15 - 17 . This behavior was attributed to the fact that this zone presented a greater amount of material. Indeed, WB presents high strength values in the stress-strain curve compared with HAZ and BM. Therefore, these high stress values of WB make the crack propagation occur at the BM. Morales, et al [ 1717 Morales A, Gonzalez JL, Hallen JM. Mechanical behavior of non-coplanar cracks in pipes applying the finite elements method. Información Tecnológica. 2004;15(6):29-34. ] found that the maximum stress is located in the outer wall of the lamination, and the failure could be expected here. Consequently, these factors make the crack propagation occur at either the right or left crack tip and propagate on the outer or inner wall of the BM.

Figure 15
Direction proposed for the crack propagation in pipelines with planar laminations with D/t of 48; a) 2a of 10.01 mm, b) 2a of 15.12 mm and c) 2a of 17.12 mm.
Figure 16
Direction proposed for the crack propagation in pipelines with planar laminations with D/t of 64; a) 2a of 10.01 mm, b) 2a of 15.12 mm and c) 2a of 17.12 mm.
Figure 17
Direction proposed for the crack propagation in pipelines with planar laminations with D/t of 96; a) 2a of 10.01 mm, b) 2a of 15.12 mm and c) 2a of 17.12 mm.

As shown in section 3.1 and the information described above by FE, pressure obtained (given in references by [ 2828 Kittel J, Ropital F, Pellier J. Effect of membrane thickness on hydrogen permeation in steels during wet hydrogen sulfide exposure. Corrosion. 2008;64(10):788-799. http://dx.doi.org/10.5006/1.3278446.
http://dx.doi.org/10.5006/1.3278446 ...

29 Olden V, Alvaro A, Akselsen OM. Hydrogen diffusion and hydrogen influenced critical stress intensity in an API X70 pipelines steel welded joint – Experiments and FE simulations. International Journal of Hydrogen Energy. 2012;37(15):11474-11486. http://dx.doi.org/10.1016/j.ijhydene.2012.05.005.
http://dx.doi.org/10.1016/j.ijhydene.20...
- 3030 Alvaro A, Olden V, Akselsen OM. 3D cohesive modelling of hydrogen embrittlement on the heat affected zone of an X70 pipeline steel – Part II. International Journal of Hydrogen Energy. 2014;39(7):3528-3541. http://dx.doi.org/10.1016/j.ijhydene.2013.12.097.
http://dx.doi.org/10.1016/j.ijhydene.20...
]) at the cracks’ tips is too low when compared to the works reported by FE [ 1616 Alberto S, Gonzalez JL, Morales A. Behavior of coplanar and non-coplanar laminations in API5L X52 simulated by finite elements. Información Tecnológica. 2009;20(5):97-105.

17 Morales A, Gonzalez JL, Hallen JM. Mechanical behavior of non-coplanar cracks in pipes applying the finite elements method. Información Tecnológica. 2004;15(6):29-34.
- 1818 Gonzalez JL, Morales A. Analysis of laminations in X52 steel pipes by nonlinear by finite element. International Journal of Pressure Vessel and Technology. 2008;130(2):021706. http://dx.doi.org/10.1115/1.2894295.
http://dx.doi.org/10.1115/1.2894295 ...
]. This supposes that the pipelines with laminations could not fail by the pressure generated by experimental hydrogen diffusion. Those pipelines fail when the Von Mises stresses reach or surpass the σUTS in the lamination zone due to internal pressure. Additionally, the lamination size is large in this study. These two factors make the pipelines unable to support the internal pressures applied by FE, and the failure is located in the outer and inner wall of the lamination at the BM. In this context, pipelines with laminations could not fail at the HAZ or WB. This is confirmed, making a comparison of the results obtained by FEM when it was compared with an image of API 5L pipeline that presents step-wise cracking. It is noted that crack propagation at the left crack tip is toward the outer wall of the pipeline, see Figure 18 . Although this image is for stepped lamination, and the work is for planar lamination, it confirms that the crack propagation follows the main stresses towards the top left zone.

Figure 18
Crack propagation in pipelines with laminations towards the BM, units in MPa.

The industry-wide standard that is responsible for making assessments in vessel pressure is the API 579-1/ASME FFS-1 Fitness-for-service, Part 7 – Assessment of hydrogen blisters and hydrogen damage associated with HIC and stress oriented HIC (SOHIC), Part 9 assessment of crack-like flaws, and Part 13 assessmen of laminations [ 4040 The American Society of Mechanical Engineers. API 579-1/ASME FFS-1: fitness-for-service. New York: ASME; 2007. ]. For Part 7, the HIC for the three levels of evaluation is taken as a reference. The level 1 assessment procedure provides screening criteria to evaluate HIC damage, considering the damage from the perspective of local metal loss. While the level 2 assessment procedure utilizes the methodologies of Part 5 and Part 9 to evaluate the damage zone as a region of local metal loss and as a crack, respectively. The level 3 assessment of HIC damage may be performed using FE analysis considering explicit modeling of HIC damaged and non-damaged areas. Limit load or elastic plastic analysis may be performed. The HIC damaged areas must be modeled as elastic-perfectly plastic material. All parameters above at the part 7 level 3 are used in the present work. While in part 9 assessment, levels 1 and 2 are very conservative, and it is neccesary to make assessments for level 3, where advanced stress analysis techniques are required to define the state of the stress at the location of the flaw because of complicated geometry and/or loading conditions. Otherwise, numerical analysis techniques such as the FEM could be used to determine the stress field at the crack location. It is recommended that the crack-like flaw in the component may be computed using elastic-plastic analysis by FE. Finally, for Part 13 assessment, laminations that originated from HIC or SOHIC are not considered. This part considers that the laminations are planes of non-fusion in the interior of a steel plate that are a result of the steel manufacturing process.

5. Conclusions

Cracking by HIC in BM, HAZ or WB is one of the main failure for the pipelines that transport hydrocarbons. The standard that provides assessment for the failure analysis of cracking and HIC is the API 579-1/ASME FFS-1 “Fitness-for-service”. This standard shows different assessment levels and it does not consider cracking in the heat affected zone or WB. It only considered cracking in the base metal. Then, it is important to study by FEM the mechanical behavior in 3D laminations to determine the crack propagation and the pipe failure pressure. Crack propagation follows the direction of the main stress. So, failure in a pipeline with planar lamination could be predicted by finite element modeling. For a size (2a) of 10.01 mm and ratios of D/t = 48, 64 and 96, crack propagation may occur at the right crack tip towards the outer wall of the BM. For size (2a) of 15.12 mm and ratios of D/t = 48, 64 and 96, crack propagation is located on the right crack tip and propagates towards the inner wall and the stress concentration zone. Finally, for size (2a) of 17.12 mm and ratios of D/t = 48, 64 and 96, crack propagation is observed at the left crack tip and propagates to the outer wall in the BM.

Pipelines with planar laminations fail because Von Mises stresses reach or exceed the σ UTS in the lamination zone due to internal pressure and critical lamination size. Pipelines cannot support the internal pressure, and the failure is expected at the outer wall because of coplanar laminations for BM. Failure in pipelines with coplanar laminations could only be presented in the BM zone. However, for the HAZ and WB, failure is not expected. The results obtained by FEM agree with real laminations in API 5L pipelines where the crack propagation is at the left crack tip and propagates towards the outer wall.

Acknowledgements

The authors thank ITT, Intituto Politécnico Nacional, ESIQIE, IMP and CONACYT, for the financial and material support.

References

  • 1
    Caleyo F, Valor A, Venegas V, Espina-Hernandez JH, Velazquez JC, Hallen JM. Pipeline Integrity—1: accurate corrosion modeling improves reliability estimations. Oil & Gas Journal. 2012;110:122-128.
  • 2
    Still J.R. 2004. Understanding hydrogen failures of ferritic welds. Welding Journal. 82(1):26-29.
  • 3
    Ossai CI, Boswell B, Davies IJ. Pipeline failures in corrosive enviroments – a conceptual analysis of trend and effects. Engineering Failure Analysis. 2015;53:36-58. http://dx.doi.org/10.1016/j.engfailanal.2015.03.004.
    » http://dx.doi.org/10.1016/j.engfailanal.2015.03.004
  • 4
    Fontana MG. Corrosion engineering. New York: McGraw Hill; 1987.
  • 5
    Liou HY, Shieh RI, Wei FI, Wang SC. Roles of microalloying elements in hydrogen induced cracking resistant property of HSLA Steels. Corrosion. 1993;49(5):389-398. http://dx.doi.org/10.5006/1.3316066.
    » http://dx.doi.org/10.5006/1.3316066
  • 6
    Ravi K, Ramaswamy V, Namboodhiri TKG. Hydrogen sulphide resistance of high sulphur microalloyed steels. Materials Science and Engineering A. 1990;129(1):87-97. http://dx.doi.org/10.1016/0921-5093(90)90347-6.
    » http://dx.doi.org/10.1016/0921-5093(90)90347-6
  • 7
    Romero M.F., Duque Z., Rincón O.T., Pérez O. & Araujo I. 2003. Estudio de la teoría de despolarización catódica con permeación de hidrógeno y la bacteria Desulfovibrio desulfuricans. Revista de Metalurgia. 39(1):182-187. http://dx.doi.org/10.3989/revmetalm.2003.v39.iExtra.1117.
    » http://dx.doi.org/10.3989/revmetalm.2003.v39.iExtra.1117
  • 8
    Requiz R, Vera N, Camero S. Influencia del acabado superficial en la permeaciòn de hidrógeno del acero API 5L X52. Revista de Metalurgia. 2004;40(1):30-38. http://dx.doi.org/10.3989/revmetalm.2004.v40.i1.240.
    » http://dx.doi.org/10.3989/revmetalm.2004.v40.i1.240
  • 9
    Carreño J.A., Uribe I. & Carrillo J.C. 2003. Modelado del efecto de rugosidad en la permeación de hidrógeno en un acero de bajo carbono. Revista de Metalurgia. 39(1):213-218.
  • 10
    Gonzalez JL, Ramirez R, Hallen JM, Guzman RA. Hydrogen-induced crack growth rate in steel plates exposed to sour environments. Corrosion. 1997;53(12):935-943. http://dx.doi.org/10.5006/1.3290278.
    » http://dx.doi.org/10.5006/1.3290278
  • 11
    Iino M. The extension of hydrogen blister-crack array in linepipe steels. Metallurgical Transactions. A, Physical Metallurgy and Materials Science. 1978;9a(11):1581-1590. http://dx.doi.org/10.1007/BF02661940.
    » http://dx.doi.org/10.1007/BF02661940
  • 12
    Maarten G, Hisko T, Corvan DV. Modern blast furnace ironmaking: an introduction. 2nd ed. Netherlands: Delf University Press; 2009.
  • 13
    Ahindra G, Amit C. Iron making and steelmaking: theory and practice. India: PHI Learning; 2008.
  • 14
    Ramirez JA. Susceptibilidad al agrietamiento inducido por hidrógeno absorbido, de la soldadura y zona afectada por el calor, en aceros para transporte de hidrocarburos [master degree thesis]. México DF: ESIQIE-IPN; 2003.
  • 15
    Ikeda A, Morita Y, Terasaki F, Takeyama M. On the hydrogen induced cracking of line-pipe steel under wet hydrogen sulfide environment. Proceedings of The 2nd International Congress on Hydrogen in Metals; 1997 June 6-11; Paris. France; 1977. p. 1-8.
  • 16
    Alberto S, Gonzalez JL, Morales A. Behavior of coplanar and non-coplanar laminations in API5L X52 simulated by finite elements. Información Tecnológica. 2009;20(5):97-105.
  • 17
    Morales A, Gonzalez JL, Hallen JM. Mechanical behavior of non-coplanar cracks in pipes applying the finite elements method. Información Tecnológica. 2004;15(6):29-34.
  • 18
    Gonzalez JL, Morales A. Analysis of laminations in X52 steel pipes by nonlinear by finite element. International Journal of Pressure Vessel and Technology. 2008;130(2):021706. http://dx.doi.org/10.1115/1.2894295.
    » http://dx.doi.org/10.1115/1.2894295
  • 19
    Chong TS, Kumar SB, Lai M, Loh WL. Fracture capacity of morden pipeline girth welds with 3D surface cracks under extreme operation conditions. Engineering Fracture Mechanics. 2015;146:139-160. http://dx.doi.org/10.1016/j.engfracmech.2015.07.032.
    » http://dx.doi.org/10.1016/j.engfracmech.2015.07.032
  • 20
    Alvaro A, Olden V, Akselsen OM. 3D cohesive modelling of hydrogen embrittlement in the heat affected zone of an X70 pipeline steel. International Journal of Hydrogen Energy. 2013;38(18):7539-7549. http://dx.doi.org/10.1016/j.ijhydene.2013.02.146.
    » http://dx.doi.org/10.1016/j.ijhydene.2013.02.146
  • 21
    Yan C, Liu C, Yan B. 3D modeling of the hydrogen distribution in X80 pipeline steel welded joints. Computational Materials Science. 2014;83:158-163. http://dx.doi.org/10.1016/j.commatsci.2013.11.007.
    » http://dx.doi.org/10.1016/j.commatsci.2013.11.007
  • 22
    Yi D, Xiao ZM, Idapalapati S, Kumar SB. Fracture analysis of girth welded pipelines with 3D embedded cracks subjected to biaxial loading conditions. Engineering Fracture Mechanics. 2012;96:570-587. http://dx.doi.org/10.1016/j.engfracmech.2012.09.005.
    » http://dx.doi.org/10.1016/j.engfracmech.2012.09.005
  • 23
    Ruggieri C, Dotta F. Numerical modeling of ductile crack extension in high pressure piplines with longitudinal flaws. Engineering Structures. 2011;33(5):1423-1438. http://dx.doi.org/10.1016/j.engstruct.2011.01.001.
    » http://dx.doi.org/10.1016/j.engstruct.2011.01.001
  • 24
    Nourpanah N, Taheri F. Ductile crack growth and constrain in pipeline subject to combined loading. Engineering Fracture Mechanics. 2011;78(9):2010-2028. http://dx.doi.org/10.1016/j.engfracmech.2011.03.018.
    » http://dx.doi.org/10.1016/j.engfracmech.2011.03.018
  • 25
    Nourpanah N, Taheri F. A numerical study on the crack tip constrain of pipelines subject to extreme plastic bending. Engineering Fracture Mechanics. 2011;78(6):1201-1217. http://dx.doi.org/10.1016/j.engfracmech.2010.11.021.
    » http://dx.doi.org/10.1016/j.engfracmech.2010.11.021
  • 26
    Zhang YM, Xiao ZM, Zhang WG. On 3-D crack problems in offshore pipeline with large plastic deformation. Theoretical and Applied Fracture Mechanics. 2013;67-68:22-28. http://dx.doi.org/10.1016/j.tafmec.2014.01.001.
    » http://dx.doi.org/10.1016/j.tafmec.2014.01.001
  • 27
    Zhang YM, Yi DK, Xiao ZM, Huang ZH, Kumar SB. Elastic-plastic fracture analysis for pipeline girth welds with 3D semi-elliptical surface cracks subjected to large plastic bending. International Journal of Pressure Vessels and Piping. 2013;105-106:90-102. http://dx.doi.org/10.1016/j.ijpvp.2013.03.009.
    » http://dx.doi.org/10.1016/j.ijpvp.2013.03.009
  • 28
    Kittel J, Ropital F, Pellier J. Effect of membrane thickness on hydrogen permeation in steels during wet hydrogen sulfide exposure. Corrosion. 2008;64(10):788-799. http://dx.doi.org/10.5006/1.3278446.
    » http://dx.doi.org/10.5006/1.3278446
  • 29
    Olden V, Alvaro A, Akselsen OM. Hydrogen diffusion and hydrogen influenced critical stress intensity in an API X70 pipelines steel welded joint – Experiments and FE simulations. International Journal of Hydrogen Energy. 2012;37(15):11474-11486. http://dx.doi.org/10.1016/j.ijhydene.2012.05.005.
    » http://dx.doi.org/10.1016/j.ijhydene.2012.05.005
  • 30
    Alvaro A, Olden V, Akselsen OM. 3D cohesive modelling of hydrogen embrittlement on the heat affected zone of an X70 pipeline steel – Part II. International Journal of Hydrogen Energy. 2014;39(7):3528-3541. http://dx.doi.org/10.1016/j.ijhydene.2013.12.097.
    » http://dx.doi.org/10.1016/j.ijhydene.2013.12.097
  • 31
    Traidia A, Alfano M, Lubineau G, Duval S, Sherik A. An effective finite element model for the prediction of hydrogen induced cracking in steel pipelines. International Journal of Hydrogen Energy. 2012;37(21):16214-16230. http://dx.doi.org/10.1016/j.ijhydene.2012.08.046.
    » http://dx.doi.org/10.1016/j.ijhydene.2012.08.046
  • 32
    American Society for Testing and Materials. ASTM E8–01: standard test methods for tension testing of metallic materials. West Conshohocken: ASTM; 2001.
  • 33
    Ramirez JA, Gonzalez JL. Hydrogen induced cracking of welds in steel pipelines, design and analysis of pressure vessels and piping: implementation of ASME B31 - fatigue, ASME section VIII, and buckling analyses, PVP2003-2182. New York: ASME; 2003.
  • 34
    Gonzalez JL, Hallen JM. Mecánica de fractura en ductos de recolección y transporte de hidrocarburos. 3º Congreso de Ductos PEMEX; 1998 Diciembre 7-9; México DF. México; 1998. 183-191.
  • 35
    Ansys Inc. Introduction to ANSY for Release 8.0. Canonsburg: ANSYS; 2003.
  • 36
    Ansys Inc. Release ANSYS 8.0 documentation: element reference - part I: element library. Canonsburg: ANSYS; 2003.
  • 37
    Madeci E, Guven I. The finite element method and applications in engineering using Ansys. Springer; 2006.
  • 38
    Meyers MA, Chawla KK. Mechanical behavior of materials. Cambridge: Prentice Hall; 1999.
  • 39
    Dowling NE. Mechanical behavior of materials, engineering methods for deformation, fracture, and fatigue. 2nd Edition. Prentice Hall; 1999.
  • 40
    The American Society of Mechanical Engineers. API 579-1/ASME FFS-1: fitness-for-service. New York: ASME; 2007.

Publication Dates

  • Publication in this collection
    Jan-Mar 2018

History

  • Received
    08 Nov 2017
  • Accepted
    03 Mar 2018
Associação Brasileira de Soldagem Rua Dr Guilherme Bannitz, 126 conj 42, 04532-060 - São Paulo/SP Brasil, Tel.: (55 11) 3045 5040, Fax: (55 11) 3045 8578 - São Paulo - SP - Brazil
E-mail: abs@abs-soldagem.org.br