Evaluation of mechanical properties of porous alumina ceramics obtained using rice husk as a porogenic agent

Abstract

The objective of this work was to evaluate the mechanical properties of porous alumina ceramics, using the rice husk as a porogenic element. The rice husk was milled and graded in two granulometry, <65 μm and 65-150 μm, and added in a high purity calcined alumina in the proportion of 5, 15 and 30 wt%. The samples were pressed by uniaxial pressing and sintered at 1450 ºC for 1 h. Sintered density, total porosity, Young’s modulus, modulus of rupture, and compressive strength were evaluated. Samples were also prepared without the addition of rice husk (RH) in order to compare the properties. Porous ceramics with total porosity ranging from 24% to 54% were produced, and with the composition of 5% RH 65-150 μm, a high porosity value was obtained for a lower loss in mechanical properties.

Keywords:
mechanical properties; porous ceramic; alumina; rice husk; porogenic agent

INTRODUCTION

The interest in the development and optimization of porous ceramics is due to the wide field of technology in which those materials are applied, for example, catalysts, furnace linings, furnace furniture, filters for the automotive industry, glass production and acoustic insulation 11 L.L. de Sousa, R. Salomão, V.L. Arantes, Ceram. Int. 43, 1(2017) 1362.. Porous ceramics can be produced by mixing porogenic agents in the ceramic matrix, which, during sintering, burn out forming the pores 22 K. Mohanta, A. Kumar, O. Parkash, D. Kumar, J. Eur. Ceram. Soc. 34, 10(2014) 2401.. Some examples of materials used as porogenic elements are starches, polymers, wood and polymer foams 33 R. He, Z. Qu, X. Cheng, Ceram. Int. 42, 2(2016) 2257.)-(55 T.T. Dele-Afolabi, M.A. Azmah Hanim, M. Norkhairrunnisa, S. Sobri, R. Calin, Ceram. Int. 43, 2(2017) 1633. . Fig. 1 shows a schematic of the production of these porous ceramics. The porosity of ceramics is a result of the processing route of these materials by powder technology, resulting in an involuntary residual pore fraction. This fraction of residual pores is due to the limitation of the densification process that occurs during sintering. The production of porous ceramic materials can be purposeful, especially when they are used for applications such as filters and catalytic supports 66 H.N. Yoshimura, A.L. Molisani, G.R. Siqueira, A.C. Camargo, N.E. Narita, P.F. Cesar, H. Goldenstein, Cerâmica 51(2005) 239.. Residual porosity in ceramics results in a reduction in the mechanical strength of the final product. Thus, porous ceramics generally have lower mechanical resistance when compared to dense ceramics. Therefore, their applications are different and can not be used as structural materials 77 J.A. Rodrigues, F.S. Ortega, A.E.M. Paiva, E.L.G. Villaboim, V.C. Pandolfelli, Cerâmica 50(2004) 209. ), (88 W.L. Vasconcelos, Cerâmica 43 (1997) 120.. The main properties of porous ceramics are low thermal conductivity, low density, high surface area, high permeability and high refractoriness 99 R.C.O. Romano, V.C. Pandolfelli, Cerâmica 52(2006) 213..

Figure 1:
Schematic of the pore-forming agent method for porous ceramic production.

The rice husk (RH) has in its composition a fraction of organic matter that can be used as a porogenic element 22 K. Mohanta, A. Kumar, O. Parkash, D. Kumar, J. Eur. Ceram. Soc. 34, 10(2014) 2401.), (1010 J. Liu, Y. Li, Y. Li, S. Sang, S. Li, Ceram. Int. 42, 7(2016) 8221.), (1111 V.P. Della, I. Kuhn, D. Hotza, Quím. Nova. 24(2001) 778.. In addition, the RH has a large amount of silica (SiO2), with 20% of inorganic matter present in the husk, about 95% of silica, which can react with alumina at high temperatures to generate mullite (3Al2O3.2SiO2), according to Eq. A 1212 R.R. Menezes, E. Fagury-Neto, M.C. Fernandes, P.M. Souto, R.H.G.A. Kiminami, Cerâmica54(2008) 245.)-(1515 J. Wang, J. Zhao, Ceram. Int. 43, 18(2017) 16430.. The formation of this crystalline phase contributes to the improvement of the thermal and mechanical properties of the ceramic produced 22 K. Mohanta, A. Kumar, O. Parkash, D. Kumar, J. Eur. Ceram. Soc. 34, 10(2014) 2401.), (1616 W. Guo, H. Lu, C. Feng, J. Rare Earth. 28, 4(2010) 614..

3 A l 2 O 3 + 2 S i O 2 1300 º C 3 A l 2 O 3 .2 S i O 2 (A)

From the mixture of ground RH with high purity alumina, it is possible that during the sintering of the ceramic bodies, mullite can be generated, in addition to the formation of the pores due to the burning of the organic matter present in the RH. Mullite presents excellent properties, such as high refractoriness, high modulus of rupture, good resistance to thermal shock and chemical attack 1212 R.R. Menezes, E. Fagury-Neto, M.C. Fernandes, P.M. Souto, R.H.G.A. Kiminami, Cerâmica54(2008) 245.), (1717 M.V.M Magliano, V.C. Pandolfelli, Cerâmica 56(2010) 368. . Due to these properties, this ceramic has great technological importance and is frequently used in refractory ceramics 1717 M.V.M Magliano, V.C. Pandolfelli, Cerâmica 56(2010) 368. . The incorporation of RH in natura or as ash is an alternative to reduce the environmental impact of the inadequate disposal of this agricultural residue in the environment 1212 R.R. Menezes, E. Fagury-Neto, M.C. Fernandes, P.M. Souto, R.H.G.A. Kiminami, Cerâmica54(2008) 245.. In this study, the RH was used as a source of silica. The objective of this work was to study the influence of the addition of certain quantities and particles sizes of ground rice husk on alumina ceramics. It is intended to evaluate the crystalline phases, porosity, mechanical properties and microstructure of the obtained porous ceramics.

MATERIALS AND METHODS

The samples were obtained using high purity alumina powder manufactured by Baikalox with a particle size of 0.5 μm and in natura RH provided by COOPAVALPA (Cooperative of the Rice Producers of Paraíba Valley). The rice husk was washed with tap water and then with distilled water to remove all impurities adhering to the husk surface and dried at 120 °C until constant weight. The RH was ground in an alumina ball mill for 2 h and then separated into two granulometric ranges: <65 μm and 65-150 μm. Mixtures of alumina with different percentages of RH were prepared in the proportions of 5, 15 and 30 wt%. The mixing of the powders was performed manually with the aid of a glass stick until complete homogenization. Fig. 2 shows the flowchart of the experimental procedure.

Figure 2:
Flowchart of the experimental procedure.

The mixtures were pressed uniaxially in three different shapes, one for each specific analysis, as shown in Fig. 3, using a hydraulic press at 40 MPa. The processing of ceramics occurred without the use of binding agents, since there was no difficulty in pressing these mixtures. After pressing, the samples were fired for 1 h at 200, 300, 500 and 1450 °C. These firing levels were based on the thermogravimetric analysis of the rice husk 22 K. Mohanta, A. Kumar, O. Parkash, D. Kumar, J. Eur. Ceram. Soc. 34, 10(2014) 2401.), (55 T.T. Dele-Afolabi, M.A. Azmah Hanim, M. Norkhairrunnisa, S. Sobri, R. Calin, Ceram. Int. 43, 2(2017) 1633. and also on preliminary tests, since the burning of the organic matter of the rice husk happens gradually until 200 °C and then more slowly until approximately 500 °C. The sintering temperature of 1450 °C was based on the phase diagram Al2O3-SiO222 K. Mohanta, A. Kumar, O. Parkash, D. Kumar, J. Eur. Ceram. Soc. 34, 10(2014) 2401.. The heating and cooling rates were 3 and 5 °C/min, respectively.

Figure 3:
Shape of samples used in each analysis.

The porosity was determined by the mercury porosimetry using a porosimeter (Quantachrome, Poremaster) and the cylindrical samples, two of each composition, with 10 mm of diameter and 5 mm of height. Cylindrical samples, ten of each composition, with 16 mm of diameter and 14 mm of height, were subjected to the compression test in an EMIC testing machine according to ASTM C133 standard using a load cell of 100 kN and actuator speed of 0.5 mm/min 1818 ASTM Int., C133-97, “Standard test methods for cold crushing strength and modulus of rupture of refractories” (2003).. The rectangular samples were machined in a Ferdimat machine with a diamond grinding wheel (D126) and then glued to metal plates. After that, they were cut with a 1.5 mm thick diamond wafer blade, obtaining prismatic samples with dimensions of approximately 42x6x3 mm. The Young’s modulus of these samples, ten of each composition, was determined by a non-destructive technique using the Sonelastic 3.0 equipment (ATCP Phys. Eng.). After this analysis, the ten samples were submitted to a 3-point flexural test to determine their modulus of rupture. This test was performed in a universal mechanical testing machine (Shimadzu, Autograph AG-X) using a load cell of 5 kN and loading speed of 0.5 mm/min. The modulus of rupture (MPa) was determined by:

σ r = 3 P L 2 B w 2 · L 2 x L 2 (B)

where P is the force applied at the moment of fracture (N), L the distance between the two lower supports (mm), B the width of the specimen (mm), w the height of the sample (mm), and x a correction factor (distance between the position where the fracture occurred and the center of the sample (mm) 1919 C.B. Carter, M.G. Norton, Ceramic materials: science and engineering, Springer, New York (2007) 298.), (2020 G.B. Cintra, M.A.L. Braulio, L.R.M. Bittencourt, V.C. Pandolfelli, Cerâmica 56(2010) 15.. For microstructural analysis of the fracture surface, a Hitachi TM3000 scanning electron microscope was used. The crystalline phases were identified by X-ray diffraction in a diffractometer (Panalytical, Empyrean) with monochromatic CuKα radiation, angular range of 10º to 80º and step of 0.02 º/s.

RESULTS AND DISCUSSION

From the processing of porous alumina ceramics using ground rice husk (RH), it was possible to obtain green samples of all compositions with good resistance and without defects. However, the samples of compositions with 15% and 30% of RH 65-150 μm did not withstand the firing process and the samples with addition of 30% RH <65 μm did not withstand the cutting stage. Therefore, the results of the compositions 5% RH <65 μm, 15% RH <65 μm, and 5% RH 65-150 μm is discussed, compared to the results of the pure alumina composition. Fig. 4 shows the crystalline phase analysis of the four compositions with the addition of rice husk and the pure alumina composition. Peaks were identified using X’pert High Score software and indexed by JCPDS files: 15-0776 (mullite); 75-1862 (α-alumina); and 89-3435 (cristobalite). The X-ray diffractograms showed that the silica from rice husk reacted with alumina generating mullite. Peaks of mullite were observed as the amount of rice husk increased. The higher the amount of rice husk used in the production of ceramics, the higher the concentration of silica after burning of the rice husk. Production of mullite is related to the amount of silica, so for larger proportions of rice husk used, a higher proportion of mullite phase was obtained. The presence of cristobalite in the compositions of RH <65 μm with 15% and 30% of rice husk indicated that there was not sufficient time and temperature for all silica (SiO2) to react with alumina (Al2O3) to generate mullite (3Al2O3.2SiO2). If the sintering time was longer, the cristobalite peak would not appear, because the silica would be consumed in the mulitization reaction (Eq. A).

Figure 4:
X-ray diffractograms of the compositions with rice husk addition and pure alumina composition sintered at 1450 ºC for 1 h: A - α-alumina, C - cristobalite, M - mullite.

Fig. 5 shows porosity and compressive strength variations according to the particle size of the rice husk powder and proportions used in the preparation of the samples. Among all cases, the highest total porosity obtained was 53.9% for the composition RH <65 μm with 30% of rice husk addition, and the lowest value of 17.5% was obtained from the pure alumina composition. The porosity gain intensified for the composition with 30% addition of rice husk and also when the particle size of the rice husk was increased, since the burning of the RH generated pores in the structure of the material. The compressive strength inversely followed the porosity, that is, the more porous composition studied, the lower its strength. This behavior was already expected 1515 J. Wang, J. Zhao, Ceram. Int. 43, 18(2017) 16430.. However, it was noted that, for the composition RH <65 μm with 15% addition, the porosity and compressive strength were lower than for the addition of 5%. This should be a result of the residual cristobalite in the composition of 15%, as can be observed in the diffractogram of Fig. 4, since the cristobalite may have closed the pores, but as it is a fragile phase, it reduced the mechanical resistance 11 L.L. de Sousa, R. Salomão, V.L. Arantes, Ceram. Int. 43, 1(2017) 1362.. For the composition with the addition of 30%, it was observed a higher porosity with very low mechanical strength, therefore there was no equilibrium between the phases formed with mullite and an excess of cristobalite.

Figure 5:
Total porosity and compressive strength of alumina sample and the samples produced with different quantities and size of rice husk.

Fig. 6 shows the monomodal frequency of the pore diameters present in the ceramics analyzed. It was observed that samples of porous alumina produced with different particles sizes and quantities of rice husk had a similar pore diameter frequency. In the compositions with rice husk, the pore frequency was concentrated in the size range of 0.18 to 0.19 μm, whereas the pure alumina composition presented lower frequency and also a narrower range of pore diameter values, when compared to other works and other ways of obtaining alumina ceramics 11 L.L. de Sousa, R. Salomão, V.L. Arantes, Ceram. Int. 43, 1(2017) 1362.), (22 K. Mohanta, A. Kumar, O. Parkash, D. Kumar, J. Eur. Ceram. Soc. 34, 10(2014) 2401.), (55 T.T. Dele-Afolabi, M.A. Azmah Hanim, M. Norkhairrunnisa, S. Sobri, R. Calin, Ceram. Int. 43, 2(2017) 1633. . The amount of rice husk used affected the number of pores that have a certain diameter. The composition 30% RH <65 μm presented the highest number of pores with a diameter of 0.18 μm and compositions with 5% RH <65 μm and 5% RH 65-150 μm presented the lowest number of pores with diameters close to 0.18 μm. Alumina showed the narrower pore size distribution and, as the amount of rice husk increased, the pore size distribution became wider.

Figure 6:
Frequency of pore diameters for each composition.

Table I shows the results of sintered density (ρ), porosity (P), Young’s modulus (E), modulus of rupture (MOR) and compressive strength of all compositions. It was observed that the addition of the rice husk generated the desired porosity in the compositions, thus, caused a decrease in the density and consequently of the mechanical properties. Comparing the compositions 5% RH <65 μm and 5% RH 65-150 μm with similar porosity, it was observed that the composition with the highest particle size of rice husk (65 μm<RH<150 μm) presented higher results of mechanical properties. This fact was related not only to porosity, but also to the mullite phase formed that contributed to this gain. A curious fact was observed for the composition 15% RH <65 μm, since it was expected a higher porosity and smaller values of mechanical resistance when compared to the composition 5% RH <65 μm, but that did not occur; instead, it was noticed a smaller porosity and a higher Young’s modulus. During the three-point bending test, it was observed a deflection of the samples for this composition (15% RH <65 μm), justifying their higher modulus of elasticity. The decrease in the mechanical properties was associated with cristobalite, since there was not sufficient sintering time to react all the silica with the alumina to form mullite.

Table I
Sintered density (ρ), total porosity (P), Young’s modulus (E), modulus of rupture (MOR) and compressive strength of all compositions.

Fig. 7 shows micrographs of the fracture surface, after the 3-point bending test, of the studied compositions. From the analysis of the micrographs is possible to observe that with the addition of rice husk, the microstructure is porous, since in the first image, which shows the microstructure of the alumina, it presents a single-phase without considerable porosity. Thus, the addition of the rice husk caused the desired effect of generating pores in these ceramics. It was observed that with the addition of rice husk, the density decreased and the porosity increased, with evidence of large pores, such as those observed in the micrographs of the compositions with the addition of RH. This increase in porosity led to a decrease in the mechanical properties, but for the composition 5% RH 65-150 μm, higher porosity value was obtained with a lower loss in mechanical properties. Thus, this composition was the one that presented the most attractive results in terms of porosity gain without large losses in mechanical strength. For the compositions with RH <65 μm, it was observed that the samples with 15% addition resulted in lower porosity than those with 5% addition. This may have occurred because of the presence of residual cristobalite that did not have sufficient time to react with alumina. Comparing the presented results with the those reported in 22 K. Mohanta, A. Kumar, O. Parkash, D. Kumar, J. Eur. Ceram. Soc. 34, 10(2014) 2401., it was observed some similarity between the results of mechanical properties for a similar porosity value. However, it was seen that in the present study, using only 5% of rice husk, higher porosity was obtained 22 K. Mohanta, A. Kumar, O. Parkash, D. Kumar, J. Eur. Ceram. Soc. 34, 10(2014) 2401.. Dele-Alofabi et al. 55 T.T. Dele-Afolabi, M.A. Azmah Hanim, M. Norkhairrunnisa, S. Sobri, R. Calin, Ceram. Int. 43, 2(2017) 1633. also obtained results of porosity for additions of 5% of rice husk lower than that obtained in this work. Therefore, it was possible to obtain porous ceramics with good mechanical properties, feasible to be applied as insulating coatings for furnaces 2121 V.L. Arantes, L.L. de Sousa, R. Salomão, in Proc. 60th Braz. Congr. Ceram., Águas Lindóia (2016) 1010..

Figure 7:
SEM images of fracture surface of the compositions with rice husk addition and pure alumina composition.

CONCLUSIONS

Rice husk (RH) can be used as a source of silica and pore forming agent in ceramic matrices. The ceramics with additions of 5 to 15 wt% of RH in two granulometry (<65 μm and 65-150 μm) presented a large number of pores with similar diameters. This was possibly the result of time and temperature used during the firing that allowed the atomic diffusion until those pores achieved the maximum diameter. Crystalline phases analysis showed the formation of mullite with the addition of rice husk. However, it was also observed in the compositions of 15 and 30% of rice husk additions that cristobalite was present, indicating that 1 h of sintering time at 1450 °C was not enough for all the silica from the rice husk to react with alumina and generate mullite. Porous ceramics with total porosity ranging from 24% to 54% were produced, and with the composition of 5% RH 65-150 μm, a high porosity was obtained with a lower loss in mechanical properties.

ACKNOWLEDGMENTS

The authors would like to thank the research supporting agencies CNPq and FAPERJ (2017033116) for the master and post-doctorate granted scholarships, to the National Institute for Space Research (INPE) for the porosimetry analysis and São Paulo State University (UNESP) - School of Engineering of Guaratinguetá (FEG) for the flexural testing.

REFERENCES

  • 1
    L.L. de Sousa, R. Salomão, V.L. Arantes, Ceram. Int. 43, 1(2017) 1362.
  • 2
    K. Mohanta, A. Kumar, O. Parkash, D. Kumar, J. Eur. Ceram. Soc. 34, 10(2014) 2401.
  • 3
    R. He, Z. Qu, X. Cheng, Ceram. Int. 42, 2(2016) 2257.
  • 4
    K. Prabhakaran, A. Melkeri, N.M. Gokhale, S.C. Sharma, Ceram. Int. 33, 1(2007) 77.
  • 5
    T.T. Dele-Afolabi, M.A. Azmah Hanim, M. Norkhairrunnisa, S. Sobri, R. Calin, Ceram. Int. 43, 2(2017) 1633.
  • 6
    H.N. Yoshimura, A.L. Molisani, G.R. Siqueira, A.C. Camargo, N.E. Narita, P.F. Cesar, H. Goldenstein, Cerâmica 51(2005) 239.
  • 7
    J.A. Rodrigues, F.S. Ortega, A.E.M. Paiva, E.L.G. Villaboim, V.C. Pandolfelli, Cerâmica 50(2004) 209.
  • 8
    W.L. Vasconcelos, Cerâmica 43 (1997) 120.
  • 9
    R.C.O. Romano, V.C. Pandolfelli, Cerâmica 52(2006) 213.
  • 10
    J. Liu, Y. Li, Y. Li, S. Sang, S. Li, Ceram. Int. 42, 7(2016) 8221.
  • 11
    V.P. Della, I. Kuhn, D. Hotza, Quím. Nova. 24(2001) 778.
  • 12
    R.R. Menezes, E. Fagury-Neto, M.C. Fernandes, P.M. Souto, R.H.G.A. Kiminami, Cerâmica54(2008) 245.
  • 13
    V.P. Della, I. Kuhn, D. Hotza, Cerâm. Ind. 10(2005) 2.
  • 14
    J.-J.F. Saceda, R.L. Leon, K. Rintramee, S. Prayoonpokarach, J. Wittayakun, Quím. Nova 34(2011) 1394.
  • 15
    J. Wang, J. Zhao, Ceram. Int. 43, 18(2017) 16430.
  • 16
    W. Guo, H. Lu, C. Feng, J. Rare Earth. 28, 4(2010) 614.
  • 17
    M.V.M Magliano, V.C. Pandolfelli, Cerâmica 56(2010) 368.
  • 18
    ASTM Int., C133-97, “Standard test methods for cold crushing strength and modulus of rupture of refractories” (2003).
  • 19
    C.B. Carter, M.G. Norton, Ceramic materials: science and engineering, Springer, New York (2007) 298.
  • 20
    G.B. Cintra, M.A.L. Braulio, L.R.M. Bittencourt, V.C. Pandolfelli, Cerâmica 56(2010) 15.
  • 21
    V.L. Arantes, L.L. de Sousa, R. Salomão, in Proc. 60th Braz. Congr. Ceram., Águas Lindóia (2016) 1010.

Publication Dates

  • Publication in this collection
    Jan 2019

History

  • Received
    28 Sept 2018
  • Reviewed
    14 Nov 2018
  • Accepted
    20 Nov 2018
Associação Brasileira de Cerâmica Av. Prof. Almeida Prado, 532 - IPT - Prédio 36 - 2º Andar - Sala 03 , Cidade Universitária - 05508-901 - São Paulo/SP -Brazil, Tel./Fax: +55 (11) 3768-7101 / +55 (11) 3768-4284 - São Paulo - SP - Brazil
E-mail: ceram.abc@gmail.com