X-ray scattering studies of the metastable ferroelectric phase in KDP induced by static electric field

X-ray scattering studies of the metastable ferroelectric phase in KDP induced by static electric field

Claudio Marcio Rocha Remédios; Marcus Aurélio Ribeiro Miranda; José Marcos Sasaki^*; Josué Mendes-Filho; Paulo de Tarso Cavalcante Freire; Francisco Erivan de Abreu Melo

Departamento de Física, Universidade Federal do Ceará, UFC C.P. 6030, 60455-760 Fortaleza - CE, Brazil

ABSTRACT

Potassium dihydrogen phosphate presents a ferroelectric phase below 122 K and a paraelectric phase for T > 122 K. X-ray scattering measurements were performed in order to verify the mechanism of the phase transition from point group C_2v¹⁹ to C_2v¹¹⁹ at 119 K induced by DC electric field; in other words, a change of the local site symmetries of the phosphate group occurs from C₂ site in the C_2v¹⁹ point group to C_s in the C_2v¹¹⁹ point group. This phenomenon was shown by analyzing the behavior of the integrated intensity of the (800), (080), (1600), (0160), (400) and (040) reflections. The curve fitting of these reflections showed the occurrence of a rotation of the phosphate group around the [010] crystallographic direction during the phase transition. This study confirms the observation of this metastable phase obtained by Raman spectroscopy.

Keywords: KDP, metastable phase, X-ray

1. Introduction

Many works developed with the objective of studying the physical properties of ferroelectric materials had already promoted discoveries with valuable contribution to technology. Although it has already been sufficiently studied, the Potassium Dihydrogen Phosphate (KDP) is a ferroelectric material that attracts the attention of many researchers because of its technological applications, such as Ferroelectric Devices for Random Access Memory (FDRAM). The KDP crystals undergo a phase transition at a temperature of 122 K¹. This crystal presents an orthorhombic symmetry (ferroelectric phase) at temperature below 122 K, belonging to the Fdd2 (C_2v¹⁹) space group, while above this temperature it presents a tetragonal symmetry (paraelectric phase), belonging to the I42d (D_2d¹²) space group. The KDP crystal undergoes two metastable transitions induced by uniaxial pressure: D_2d¹²® C_2v^j¹¹⁹ and C_2v¹⁹® D_2v^j¹¹⁹. According to the literature an explanation for these transitions is based on the changing of the local site symmetry of the phosphate ions: in the ferroelectric phase, the phosphate ions change their local site symmetry from C₂ to C_s, maintaining the same factor group C_2v but modifying the space group. These changes are due to the rotation of the phosphate ions around the [010] direction of the orthorhombic structure². Other works in the literature discuss the reversibility criteria of this new metastable phase³. The phase diagram for the KDP transitions on the plane (s₆, T) for temperature in the range from 110 to 130 K explains the appearance of the metastable C_2v^j¹¹⁹ phase based on the Gibbs free energy density of the system⁴.

Raman scattering experiments show that the potassium dihydrogen phosphate crystals undergo a metastable ferroelectric phase induced by a static electric field near the Curie point⁵ taking advantage of the fact that the ferroelectric phase presents piezoelectricity. In other words, due to the converse piezoelectric effect a DC electric field applied along the [001] direction should induce a phase transition (C_2v¹⁹® C_2v¹¹⁹) in KDP crystals similarly to that induced by pressure with the force applied along the shear direction.

Hence, the main goal of this work is to use X-ray diffraction measurements to confirm the assumption that the DC electric field applied along the ferroelectric c-axis forces the appearance of a metastable ferroelectric phase transition at 119 K, and that this transition is related to the rotation of the dipoles around the [010] direction of the orthorhombic structure leading to a change in the local site symmetry of the phosphate ions.

2. Experimental

Single crystals of KDP with good optical quality and good crystaline perfection used in the experiments were grown by the slow cooling method. These samples were cut in parallelepipeds with dimensions (0.87 ´ 3 ´ 5) mm³. The parallelepiped faces were orthogonal to the [100], [010] and [001] crystallographic directions of the tetragonal structure. Silver electrodes were painted on the larger faces which are perpendicular to the ferroelectric [001] direction. A Keithley instrument model 246 was used as the DC voltage source.

X-ray scattering measurements were performed using a two-circle (q-2q) Rigaku diffractometer, with radiation source of MoKa coupled with a low temperature chamber containing liquid nitrogen. The sample temperature was controlled with a fluctuation of ± 0.5 K. The high penetration feature of the X-ray beam (l^MoKa = 0.709Å) gives advantage to get diffraction from deeper planes. This reduces the diffraction from the crystal surface that is not affected by the electric field.

3. Results and Discussion

The crystal was aligned using the 440 reflection of paraelectric phase (tetragonal) and then cooled down to ferroelectric phase (orthorhombic). According to the space group of both phases, the extinction in the Miller indices for the reflections hh0 (h = 2 n) in the tetragonal symmetry changes to h00 (h = 4 n) in the orthorhombic symmetry.

Figure 1a shows the diffraction pattern for the 440 reflection at room temperature. The first peak corresponds to the scattering of the plane (440) for K_a1 radiation and the second one is the scattering of the same plane for K_a2 radiation. Figure 1b shows rocking curves for the 440 reflection at 125 K (near ferroelectric phase transition). The changes observed in Fig. 1b regarding to Fig. 1a are easily explained. The displacement of the peak position to higher angles occurs due to the reduction of the lattice parameters caused by thermal contraction. Its scattering intensity is related to the Debye-Waller factor.

Figure 1c shows the diffraction pattern below the transformation temperature. It shows three peaks where the first is the scattering of the K_a1 radiation by a domain we call a. The third peak is related to the diffraction of the K_a2 radiation by another domain that we call b. Finally the second peak is the overlap of K_a2 diffracted by the domain a and the K_a1 diffracted by the domain b^6-9.

Before discussing X-ray results we need to show that under DC electric field, the KDP crystal undergoes a C_2v¹⁹® D_2v^j¹¹⁹ phase transition. The idea of the experiment is very simple: As the phosphate tetrahedron contributes with negative charge for the dipole, a variation in the integrated intensity for (800) plane, which is formed by oxygen and phosphor, should be observed by applying an electric field.

Figure 2 shows the diffraction patterns corresponding to the a and b domains in the orthorhombic structure as a function of the DC electric field up to 5 kV/cm at 119 K. The peaks emerge from the overlapping of the bands corresponding to the K_a1 and K_a2 lines of Mo radiation. By performing a spectral decomposition into Gaussian components, we can draw the variation of the integrated intensity of both reflections as a function of DC electric field, which is displayed in Fig. 3. It should be observed that the integrated intensity corresponding to the a domain decreases with increasing the DC electric field up to 5 kV/cm, while the b domain increases. In addition, for the electric field of 6 kV/cm, the peak corresponding to the a domain disappears. These changes in the integrated intensity for the a domain until 5 kV/cm and the total disappearance of this peak at 6 kV/cm indicate essentially that oxygen atoms on these planes moved out. This can be attributed to the result of rotation of the phosphate tetrahedron around the [010] crystallographic direction relative to the C_2v¹⁹ orthorhombic structure.

4. Conclusion

We report here the mechanism which led to a conformational phase transition of KDP when an increase of DC electric field is applied along the orthorhombic c-axis. The huge variation in the integrated intensity of those peaks, corresponding to the a and b domains, indicated the occurrence of changes in the atom positions on (800) planes. These changes were attributed to the rotation of the phosphate tetrahedron around the b-axis, which also changes the local site symmetries of phosphate ions from C₂ in the C_2v¹⁹ phase to C_s in the C_2v¹¹⁹ phase.

Acknowledgements

Financial support from Brazilian funding agencies CAPES, CNPq, and FUNCAP is gratefully acknowledged.

Received: February 4, 2003

Revised: September 2, 2003

Trabalho apresentado no XV CBECIMAT, Natal - RN, Novembro de 2002

• 1. Busch, G. Helv. Phys. Acta, v. 11, p. 269, 1938.
• 2. Moreira, S.G.C.; Melo, F.E.A.; Mendes-Filho, J.; Moreira, J.E. Ferroelectrics, v. 160, p. 47, 1994.
• 3. Melo, F.E.A.; Moreira, S.G.C.; Mendes-Filho, J.; Moreira, J.E. Phys. Status Solidi B, v. 180, p. 371,1993.
• 4. Melo, F.E.A.; Moreira, S.G.C.; Chaves, A.S.; Guedes, I.; Freire, P.T.C.; Mendes-Filho, J. Phys. Rev. B, v. 59, p. 3276, 1999.
• 5. Varela, A.T.; Melo, F.E.A.; Barbosa Neto, N.M.; Guedes, I.; Freire, P.T.C.; Mendes-Filho, J.; Sasaki, J.M. J. Raman Spectrosc., v. 31, p. 915-919, 2000.
• 6. Bacon, G.E.; Pease, R.S. Proc. of Roy. Soc. Ser-A, v. 230: p. 359-381, 1956.
• 7. Ubbelohde, A.R.; Woodward, I. Proc. Roy. Soc. A, v.12, p. 188, 1946.
• 8. Bornarel, J. Ferroelectrics, v. 71, p. 255-268, 1987.
• 9. Kitaeva, G.Kh.; Kulik, S.P.; Penin, A.N.; Belinsky, A.V. Phys. Rev. B, v. 51, p. 3362, 1995.

Publication Dates

• Publication in this collection
  20 Jan 2004
• Date of issue
  Dec 2003

History

• Reviewed
  02 Sept 2003
• Received
  04 Feb 2003