Fibers Obtained from Alginate, Chitosan and Hybrid Used in the Development of Scaffolds

Abstract

The main aim of this study was to develop scaffolds based on alginate, chitosan and hybrid fibers with and without glycerol. The scaffolds developed underwent assessments for tensile property, swelling ratio and weight loss, cellular viability, degradation and biomineralization, as well as DSC/TGA thermal analysis. Tenacity values showed that use of glycerol and the interaction between alginate and chitosan as a hybrid fiber were associated with increasing tenacity values. In the swelling and weight loss study, the scaffolds containing glycerol presented lower weight loss and higher water absorption values in all scaffolds, compared to scaffolds without glycerol, indicating that glycerol acted as a stabilizer. None of the alginate, chitosan and hybrid scaffolds, with or without glycerol, decreased cell viability. On the third day of the biomineralization assay, chitosan without glycerol indicated the presence of apatite crystals. The degradation study showed that glycerol may have acted as a stabilizer.

Keywords:
Alginate; chitosan; fiber; scaffolds; tissue engineering


1. Introduction

Bone tissue engineering is a multidisciplinary field, focused on designing a scaffold to mimic the environment of the extracellular matrix and the study of more efficient signaling molecules and growth factors that stimulate regeneration. Thus, the scaffold has to behave as a temporary structure supporting bone tissue regeneration while it degrades and is replaced with the new bone11 Chen Q, Liang S, Thouas GA. Elastomeric biomaterials for tissue engineering. Progress in Polymer Science. 2013;38(3-4):584-671.,22 Vacanti JP, Vacanti CA. The History and Scope of Tissue Engineering. In: Lanza R, Langer R, Vacanti J, eds. Principles of Tissue Engineering. London: Elsevier; 2013. p. 3-8..

Textiles have been used in a wide range of medical devices, i.e., in contact with biological environments, such as vascular grafts, repair meshes, etc.33 Ayaz HGS, Perets A, Ayaz H, Gilroy KD, Govindaraj M, Brookstein D, et al. Textile-templated electrospun anisotropic scaffolds for regenerative cardiac tissue engineering. Biomaterials. 2014;35(30):8540-8552. Fibers are particularly useful for producing scaffolds due to their inherent properties, such as satisfactory porosity, adjustable elastic modulus and light weight, which promote tissue regeneration44 Doser M, Planck H. Textiles for implants and regenerative medicine. In: Bartels VT, ed. Handbook of Medical Textiles. Cambridge: Woodhead Publishing; 2011. p. 132-152.. There are several different methods of producing fiber-based scaffolds, such as electrospinning, meltspinning, wetspinning, biospinning and microfluidic spinning55 Tamayol A, Akbari M, Annabi N, Paul A, Kadhemhosseini A, Juncker D. Fiber-based tissue engineering: Progress, challenges and opportunities. Biotechnology Advances. 2013;31(5):669-687.,66 Braghirolli DI, Steffens D, Pranke P. Electrospinning for regenerative medicine: a review of the main topics. Drug Discovery Today. 2014;19(6):743-753.. The wetspinning method was chosen for this study.

The ideal scaffold will have a number of properties, such as biocompatibility, biodegradability, desirable pore size and satisfactory porosity, non-toxic responses, easy handling and an abundant source of raw material77 Venkatesan J, Bhatnagar I, Manivasagan P, Kang KH, Kim SK. Alginate composites for bone tissue engineering: A review. International Journal of Biological Macromolecules. 2015;72:269-281.,88 Bose S, Roy M, Bandyopadhyay A. Recent advances in bone tissue engineering scaffolds. Trends in Biotechnology. 2012;30(10):546-554.. Scaffold porosity does not need to be uniform, because natural bone is not uniform88 Bose S, Roy M, Bandyopadhyay A. Recent advances in bone tissue engineering scaffolds. Trends in Biotechnology. 2012;30(10):546-554., which is another reason for using fibers to develop these scaffolds.

The biopolymers selected for this study were alginate and chitosan. Alginate is a polysaccharide derived from brown algae and it comprises 1/4 linked β-D-mannuronic acid (M) and its α-L-guluronic acid (G). The properties of alginate are related to the proportion and dimension of the guluronic blocks (G) in the chain99 Wang P, Tawiah B, Tian A, Wang C, Zhang L, Fu S. Properties of alginate fiber spun-dyed with fluorescent pigment dispersion. Carbohydrate Polymers. 2015;118:143-149.. It is biocompatible, biodegradable, and has the ability to absorb 200-300 times its own weight, thus showing potential for use as a Drug Delivery System1010 Venkatesan J, Bhatnagar I, Kim SK. Chitosan-alginate biocomposite containing fucoidan for bone tissue engineering. Marine Drugs. 2014;12(1):300-316.. Alginate scaffolds have the ability to support tissue regeneration, including bone, skin, liver, etc77 Venkatesan J, Bhatnagar I, Manivasagan P, Kang KH, Kim SK. Alginate composites for bone tissue engineering: A review. International Journal of Biological Macromolecules. 2015;72:269-281.. Chitosan is a natural polymer derived from the partial deacetylation of chitin, obtained from the exoskeleton of crustaceans. It is the most abundant cationic polysaccharide and the second most abundant in nature, behind only cellulose. It comprises (1-4)-2-acetamido-2-deoxy-ß-D-glucan (N-acetyl D-glucosamine) and (1-4)-2-amino-2-deoxy-ß-D-glucan (D-glucosamine) units. It is also a biocompatible and biodegradable polymer and it is osteoconductive, as well as hemostatic and antimicrobial1111 Croisier F, Jérôme C. Chitosan-based biomaterials for tissue engineering. European Polymer Journal. 2013;49(4):780-792.. Chitosan scaffolds are biodegradable and tissue biocompatible. However, this polymer is mechanically weak, which is why it needs to be used in conjunction with another polymer1212 Li Z, Ramay HR, Hauch KD, Xiao D, Zhang M. Chitosan-alginate hybrid scaffolds for bone tissue engineering. Biomaterials. 2005;26(18):3919-3928..

The interaction between alginate and chitosan generates a polyelectrolyte complex that can be obtained by precipitating cationic polymers when mixed with anionic polymers in aqueous solutions, leading to mutual precipitation, which occurs in this case, because alginate and chitosan are anionic and cationic polysaccharides, respectively1313 Simsek-Ege FA, Bond GM, Stringer J. Polyelectrolyte complex formation between alginate and chitosan as a function of pH. Journal of Applied Polymer Science. 2003;88(2):346-351.. Another advantage of the interaction between its opposite charges is an upgrade in the mechanical strength of the developed structure formed by these two polymers1414 Baysal K, Aroguz AZ, Adiguzel Z, Baysal BM. Chitosan/alginate crosslinked hydrogel: Preparation, characterization and application for cell growth purposes. International Journal of Biological Macromolecules. 2013;59:342-348.,1515 Lee K, Ahn S, Choi CH, Lee D, Jung WK, Kim G. Functionallized alginate/chitosan biocomposites consisted of cylindrical struts and biologically designed for chitosan release. Current Applied Physics. 2014;14(8):1105-1106.. This combination is significant for scaffold development, because while alginate offers functional groups for cellular regeneration, chitosan supports the scaffold structure1616 Iwasaki N, Yamane ST, Majima T, Kasahara Y, Minami A, Harada K, et al. Feasibility of polysaccharide hybrid materials for Scaffolds in cartilage tissue engineering: evaluation of chondrocyte adhesion to polyion complex fibers prepared from alginate and chitosan. Biomacromolecules. 2004;5(3):828-833.. Finally, the interaction of these two polymers creates a strong connection between them, because alginate is a hydrophilic polysaccharide and promotes low protein adsorption, different from chitosan, a less hydrophilic polysaccharide that promotes high protein adsorption1717 Hu WW, Yu HN. Coelectrospinning of chitosan/alginate fibers by dual-jet system for modulating material surfaces. Carbohydrate Polymers. 2013;95(2):716-727.,1818 Hyland LL, Taraban MB, Hammouda B, Yu YB. Mutually reinforced multicomponent polysaccharide networks. Biopolymers. 2011;95(12):840-851..

The aim of this study is to develop and characterize scaffolds based on alginate, chitosan and hybrid alginate/chitosan fibers. All scaffolds were produced with and without glycerol in order to identify any positive properties as potential plasticizers.

2. Materials and Methods

2.1. Materials

Sodium alginate (20,000 - 40,000 cps viscosity), crab-extracted chitosan (85 % deacetylation minimum) and all reagents used were acquired from Sigma Co. (St. Louis, ME, USA).

2.2 Methods

2.2.1 Preparation of alginate, chitosan and hybrid fibers with and without glycerol

Alginate, chitosan and hybrid fibers were produced using the wet spinning technique with a syringe (Hypodermic syringes, polypropylene Luer-lock tip, capacity 10 mL, graduated, 25 x 7 mm and needle Ø 0.6 x L 2.5 mm).

Alginate 5 % (m/v) was dissolved in 100 mL of 0.1 M sodium hydroxide by stirring at room temperature overnight. The sodium alginate solution with and without glycerol was injected into a coagulation bath at 30 ºC containing 2 % calcium chloride (m/v). Chitosan 2.2 % (m/v) was dissolved in 200 mL of 2 % acetic acid (v/v) by stirring at room temperature overnight and subsequently adding 250 mL of methanol (v/v). The chitosan gel was filtered using a vacuum pump. The chitosan gel with and without glycerol was injected into a coagulation bath at 30 ºC containing 300 mL of 0.5 M sodium sulfate, 100 mL of 1 M sodium hydroxide and 600 mL of distilled water. The resultant fibers were extracted from this coagulation medium after 24 hours and placed in 50 % methanol for 2 h. Hybrid fibers were produced by extruding the alginate gel, with and without glycerol, in a solution containing 50 % calcium chloride solution (v/v) and 50 % of 0.02 % chitosan gel (m/v). The fibers remained in this solution for 24 h. Subsequently, the fibers were stored in 50 % (v/v) methanol for 2 h. 2.5 % glycerol (m/m) was added to all gel solutions in order to ascertain its effect as a plasticizer. The resultant alginate, chitosan and hybrid fibers were washed three times in distilled water and part of the fibers were rolled manually on a polypropylene cylindrical support, dried at room temperature conditions for 24 h and characterized according to item 2.2.3. The other part of the fibers were used to produce the scaffolds (item 2.2.2).

2.2.2. Preparation of alginate, chitosan and hybrid scaffolds with and without glycerol

The alginate, chitosan and hybrid scaffolds were developed using the freeze-drying method. After production (item 2.2.1), the fibers previously weighed in a mass of approximately 0.255 g, were placed in a polystyrene mold and stored in a ultrafreezer at -67 °C for 2 h to freeze the structures. Then these structures were lyophilized in a L101 Liotop lyophilizer until dried, a process lasting approximately 60 h at -30 ºC.

The scaffolds were produced using two different polystyrene molds, both with external dimensions of 8.54 x 12.76 cm. The mold for the production of large structures corresponded to the 12-well cell culture plate, with a diameter and depth of approximately 15 mm per well. The mold for the production of small structures corresponded to the 96-well plate for cell cultures, with 6.4 mm deep wells. The production process for the scaffolds was the same for both molds. The smaller structures were prepared to facilitate the coverage of the samples in microscopy assays. The scaffolds produced in the large mold were characterized for cell viability (item 2.2.4.3), DSC / TGA (item 2.2.4.1) and absorption and weight loss (item 2.2.4.2). While the scaffolds produced in the small mold were characterized for biomineralization (item 2.2.4.5), degradation with lysozyme (item 2.2.4.4) and SEM/EDS.

2.2.3. Mechanical testing of the fibers

For diameter and linear density determinations in accordance with ISO 5084 (1996)1919 Maluf E, Kolbe W. Textile fibers. In: Technical Textile Industry Data. 2nd ed. São Paulo: Institute for Technological Research and Brazilian Textile and Confection Industry Association (ABIT); 2003. p. 1-64., dried samples fibers were stored at 20 ± 2 ºC and relative humidity of 65 ± 4 % for 24 h. After acclimatization, each sample was weighed using an analytical balance (AUW220D, Shimadzu, São Paulo, Brazil). The results obtained represent the ratio between the weight and the fiber length2020 International Organization for Standardization (ISO). ISO 5084:1996. Determination of thickness of textiles and textile products. Geneva: International Organization for Standardization; 1996.. The assay was performed based on ISO 2060 (1994)2121 International Organization for Standardization (ISO). ISO 2060:1994. Textiles -- Yarn from packages -- Determination of linear density (mass per unit length) by the skein method. Geneva: International Organization for Standardization; 1994., ISO 1139 (1973)2222 International Organization for Standardization (ISO). ISO 1139:1973. Textiles - Designation of yarns. Geneva: International Organization for Standardization; 1973. and ISO 139 (2005)2323 International Organization for Standardization (ISO). ISO 139:2005. Textiles - Standard atmospheres for conditioning and testing. Geneva: International Organization for Standardization; 2005.. Tensile properties of the acclimatized fibers (rupture strength, tenacity, elongation and Young's modulus) were determined according to ASTM D 3822 (2007)2424 ASTM International. ASTM D3822. Standard Test Method for Tensile Properties of Singles Textile Fibers. West Conshohocken: ASTM International; 2007. using an Instron tester machine (model 5569, Norwood-MA, USA). Accordingly, in order to determine tenacity (strength value shared by linear density), fiber fineness (linear density or count number) was calculated in terms of TEX, defined as the weight in grams per 1,000 m of fiber, by weighing a known length of the fiber. A load cell of 10 N, gauge length of 200 mm, automatic pre-tension and crosshead speed of 100 mm/min were used. The tensile parameters were determined when the fiber broke immediately after maximum elongation.

2.2.4. Characterization of the scaffolds

2.2.4.1 Differential Scanning Calorimetry - DSC/Thermogravimetry - TGA

DSC tests were performed in the DSC 7020 (Exstar, SII Nano Technology In., Japan) under an inert nitrogen atmosphere at a flow rate of 50 mL/min. Temperatures ranged from 25 - 350 °C with a heating rate of 10 °C/min. A closed aluminum capsule containing 2 mg of sample mass was used. The temperature and fusion heat were calibrated with Indium.

TG analysis was performed in a TG/DTA 7200 (Exstar, SII Nano Technology In., Japan) under a 100 mL/min nitrogen atmosphere. Temperatures ranged from 25 - 600 ºC with heating rate of 10 ºC/min. Closed platinum capsules containing 3.5 mg of sample mass were used. The temperature and heat fusion were calibrated with Calcium oxalate before the assay.

Both DSC and TG analyses were performed with alginate and chitosan polymers and of alginate, chitosan and hybrid fiber scaffolds, with and without glycerol.

The assay was performed at the Department of Pharmacy, School of Pharmaceutical Sciences.

2.2.4.2. Studies on water uptake or swelling and weight loss

Swelling behavior and scaffold weight loss were performed in triplicate. The scaffolds were weighed and immersed in 10 mL of distilled water. The flask samples (15 mL) were closed with Parafilm (Pechiney Plastic Packaging Co., Chicago, IL, USA) and placed in a thermo regulated bath (TEC-420, Tecnal, Piracicaba, Brazil) under agitation (60 rpm), at 37 ºC for 1, 3, 7, 15, 21 and 30 days. For water uptake calculation, an analytical balance (AUW220D, Shimadzu, São Paulo, Brazil) was used to determine the initial scaffold mass (mi) and the final mass (mw), after incubation and removal of the excess solution with filter paper. Subsequently, the scaffolds were dried at 40 ºC until constant weight was attained in order to determine (mf). Water uptake and weight loss are calculated by equations 1 and 2.

Water uptake = m W m i / m i × 100 (1)
Weight loss = m f m i / m i × 100 (2)

2.2.4.3. Cell viability assay

2.2.4.3.1. Cell culture

For this study, NIH3T3 P12 fibroblasts (ATCC - American Type Culture Collection) were used. Cells were cultivated in Dulbecco's modified Eagle medium (DMEM) supplemented with 10 % bovine fetal serum (FBS - NUTRICELL) and incubated in an incubator at 37 ºC containing 5 % CO2. After subconfluence, cells were subcultivated with trypsin (0.25 % trypsin, 1mM EDTA - Sigma Aldrich®), in order to dissociate cells from the culture flasks, and maintained for 5 min in the incubator at 37 ºC with 5 % CO2. Then the trypsin was inactivated from DMEM using 10 % FBS. Cells were transferred to 15 mL Falcon tubes (TPP® - Techno Plastic Products) and centrifuged for 5 min at 4 ºC and 1200 rpm. Subsequently, the supernatant was discarded and cells were resuspended in new DMEM with 10 % FBS. Cellular account was made with trypan blue protocol and cells were used for experimental assays of MTT and crystal violet.

According to ISO No. 10.993-5, the concentrations used in this study were 10 mg extract (samples of alginate, chitosan and hybrid scaffolds, with and without glycerol) for 1 mL DMEM with 10 % FBS, i.e., proportion of 10 mg/1 mL. For viability assays, 2x1033 Ayaz HGS, Perets A, Ayaz H, Gilroy KD, Govindaraj M, Brookstein D, et al. Textile-templated electrospun anisotropic scaffolds for regenerative cardiac tissue engineering. Biomaterials. 2014;35(30):8540-8552. cells/well were plated in 96 wells plates. After the 24-hour incubation period, the medium was replaced with DMEM with 10 % FBS and conditioned with the scaffolds. Control groups received only the DMEM medium: with 10 % FBS (positive control) and 1 % FBS (negative control). Each plate was analyzed in an experimental period of 24 and 48 h after the addition of the conditioned medium2525 Volpato LE, Oliveira RC, Epinosa MM, Bagnato VS, Machado MAAM. Viability of fibroblasts cultured under nutritional stress irradiated with red laser, infrared laser, and red light-emitting diode. Journal of Biomedical Optics. 2011;16(7):075004..

2.2.4.3.1.1. MTT

After each experimental period (24 and 48 h), cells were washed with PBS and incubated in a solution containing 0.5 mg MTT for 1 mL DMEM without FBS. After this procedure, the plates were maintained at 37 ºC for 4 h, when the solution was removed and the insoluble pigment was extracted in dimethyl sulfoxide (DMSO). Absorbance was measured at 562 nm by Synergy H1 Monochromator based Biotek.

2.2.4.3.1.2. Crystal Violet

After each experimental period (24 and 48 h), cells were washed with PBS and 100% methanol was added for 10 min. After the methanol was removed, 0.2 % crystal violet solution was added to 20 % ethanol for 3 min. Then the solution was removed and the wells were washed twice with PBS to remove the excess dye. Finally, 0.05 mol.L-1 of sodium citrate solution was added with 50 % ethanol for 10 min. Absorbance was determined at 540 nm by Synergy H1 Monochromator based Biotek.

2.2.4.3.2. Statistical Analysis

MTT and Crystal violet statistical analyses were performed using GraphPad Prism 4 software selecting statistical test one way ANOVA using Tukey's test with p < 0.05 indicating statistical significance. The cellular viability assay was performed in the Biochemistry Laboratory at the Biological Sciences Department of the Bauru School of Dentistry, University of São Paulo.

2.2.4.4. In vitro degradation study

This study was performed in triplicate in order to determine the influence of the lysozyme on the scaffold properties. The chitosan and hybrid scaffolds, with and without glycerol, weighing approximately 0.100 g were immersed in 10 mL of PBS pH 7.4 ± 0.02 containing lysozyme (EC 3.1.2.17, chicken egg white, 40000 U/mg, Sigma), similar to that found in human serum (13 mg/L), and incubated at 37 ºC at different time intervals (1, 3, 5, 7 and 10 days) under static conditions. After each incubation time, the scaffolds were dried at 40 ºC and subjected to SEM analysis. After these incubation periods, the concentration of reducing sugars were determined by DNS method2626 Ghose TK. Measurement of cellulase activities. Pure and Applied Chemistry. 1987;59(2):257-268.. Absorption and weight loss were determined as outlined above (item 2.2.4.2).

2.2.4.5. In vitro biomineralization study

The biomineralization assay was performed in triplicate. The alginate, chitosan and hybrid scaffolds, with and without, glycerol weighing approximately 0.100 g were immersed in 10 mL of 1x simulated body fluid (SBF) and then incubated at 37 ºC in closed Falcon tubes for preset time periods of 1, 3, 5, 7, 15, 21 and 30 days. SBF is a solution that contains the necessary minerals to mimic the body fluid, prepared according to the method2727 Kokubo T, Takadama H. How useful is SBF predicting in vivo bone bioactivity? Biomaterials. 2006;27(15):2907-2915.. After the preset time interval, the scaffolds were removed and dried in 40 ºC. The dried scaffolds were subjected to SEM analysis for examination of mineralization.

3. Results and Discussion

3.1 Mechanical testing

Tension testing or material behavior under strength and deformations applied along the axis is one of the most important characteristics related to mechanical properties2828 Hearle JWS, Morton WE. Physical Properties of Textile Fibres. 4th ed. Cambridge: Woodhead Publishing; 2008.. Fiber tenacity is the quotient of breaking load by the count number. This calculation is necessary in order to normalize the effect of different thickness values found in some samples containing several fibers2020 International Organization for Standardization (ISO). ISO 5084:1996. Determination of thickness of textiles and textile products. Geneva: International Organization for Standardization; 1996.. Table 1 shows the tenacity values of all fibers. Tenacity values for alginate, chitosan and hybrid fibers were between 7.25-7.77, 4.47-8.64 and 9.97-10.0 cN/tex, and the use of glycerol is associated with a trend of increasing tenacity values. The tenacity values obtained in this study are slightly inferior to those found in literature (14.0-18 cN/Tex)2929 Niekraszewicz B, Niekraszewicz A. The structure of alginate, chitin and chitosan fibres. In: Eichhorn SJ, Hearle JWS, Jaffe M, Kikutani T, eds. Handbook of Textile Fibre Structure Volume 2: Natural, Regenerated, Inorganic and Specialist Fibres. Cambridge: Woodhead Publishing; 2009. p. 266-306. and (11.0-18 cN/Tex)3030 Anandjwala RD. Role of advanced textile materials in healthcare. In: Anand S, Kennedy JF, Miraftab M, Rajendran S, eds. Medical Textiles and Biomaterials for Healthcare. Cambridge: Woodhead Publishing; 2006. p. 90-98.,3131 Kaswell ER. Wellington Sears Handbook of Industrial Textiles. New York: Wellington Sears Company; 1963.. However, it is worth mentioning that the cited references do not mention the alginate concentrations used. Hybrid fibers presented an increase of 27.3 % and 55.2 % in tenacity values compared to alginate and chitosan, respectively.

Table 1
Tenacity values of alginate, chitosan and hybrid fibers without and with glycerol

3.2 Scaffold preparation

The results of scaffold production can be observed in Figures 1 and 2. The scaffolds presented an interconnected porous structure due to fiber structure.

Figure 1
Scaffolds of (a) alginate without glycerol, (b) alginate with glycerol, (c) chitosan without glycerol, (d) chitosan with glycerol, (e) hybrid without glycerol and (f) hybrid with glycerol produced in mold of 15 mm per well in digital image and optical microscopy with 20x magnification.

Figure 2
Optical microscopy of (a) alginate without glycerol, (b) chitosan withoutglycerol, (c) hybrid without glycerol, (d), alginate with glycerol, (e) chitosan with glycerol and (f) hybrid with glycerol scaffolds produced in mold of 6.4 mm per well with 20x magnification.

3.3. DSC/TGA

Differential Scanning Calorimetry is an important study of a material thermal behavior that identifies mass loss, reduction reactions and desorption by the endothermic peaks and crystallization, polymerization reactions and oxidation by the exothermic peaks3232 Wendlandt WW. Thermal Analysis. New York: John Wiley & Sons; 1986.. The results of the DSC of the scaffolds with and without glycerol are analyzed in Figure 3.

Figure 3
DSC peaks of scaffolds based on alginate, chitosan and hybrid (a) without and (b) with glycerol.

According to the thermogram of the scaffolds without glycerol (Figure 3a), endothermic peaks of alginate occurred at 122.4 ºC and 195.6 ºC, of chitosan at 181 ºC and the hybrid at 174.2 ºC. Comparing these peaks, the hybrid endothermic peak is located in a intermediate temperature between alginate and chitosan. The exothermic peaks of alginate occurred at 271.7 ºC, of chitosan at 304.1 ºC and the hybrid at 277.7 ºC. A displacement of the hybrid peaks (both, endothermic and exothermic) was noted, with regard to the polymers themselves, indicating the formation of new chemical bonds and the interaction of alginate and chitosan.

In the thermogram of scaffolds with glycerol (Figure 3b), a displacement of the hybrid endothermic and exothermic peaks occurred, with regard to the alginate and chitosan peaks, which indicates the same behavior noted in the thermogram of the scaffolds without glycerol (Figure 3a). The hybrid endothermic peak occurred at 173.9 ºC and the exothermic peak at 277.5 ºC. In all scaffolds with glycerol, a displacement of the endothermic and exothermic peaks was noted, compared to the results of scaffolds without glycerol, indicating the interaction between the polymers and the glycerol.

Through thermogravimetry, the relationship between material mass and its temperature could be detected. The decomposition of the polymers can be analyzed, indicating weight loss of the sample or water evaporation3333 Price DM, Hourston DJ, Dumont F. Thermogravimetry of Polymers. In: Meyers RA, ed. Encyclopedia of Analytical Chemistry. Chichester: John Wiley & Sons; 2000. p. 8094-8105.. The TGA results are analyzed in Figure 4.

Figure 4
TGA the alginate, chitosan and hybrid scaffolds (a) without and (b) with glycerol.

The thermogram showed similar behavior of the alginate and hybrid scaffolds without glycerol, presenting three mass losses, pertaining to water evaporation and polymer degradation. The chitosan scaffold without glycerol presented two mass losses associated with the dehydration process of saccharide rings, decomposition of acetylated and deacetylated units of chitosan and depolymerization3434 Lima PA, Resende CX, Soares GD, Anselme K, Almeida LE. Preparation, characterization and biological test of 3D-scaffolds based on chitosan, fibroin and hydroxyapatite for bone tissue engineering. Materials Science and Engineering: C. 2013;33(6):3389-3395.. The scaffolds with glycerol behaved in a similar fashion to the scaffolds without glycerol.

3.4. Swelling studies and weight loss

In tissue engineering, swelling ability is responsible for the polymeric matrix expansion related to scaffold morphology and cell-nutrient transmission1515 Lee K, Ahn S, Choi CH, Lee D, Jung WK, Kim G. Functionallized alginate/chitosan biocomposites consisted of cylindrical struts and biologically designed for chitosan release. Current Applied Physics. 2014;14(8):1105-1106.,3535 Valente JFA, Valente TAM, Alves P, Ferreira P, Silva A, Correia, IJ. Alginate based scaffolds for bone tissue engineering. Materials Science and Engineering: C. 2012;32(8):2596-2603.. The swelling ratio and the weight loss of the scaffolds produced are analyzed in Figure 5.

Figure 5
Results of (a) swelling ratio and (b) weight loss of alginate, chitosan and hybrid scaffolds with glycerol.

The swelling behavior results of the scaffolds without glycerol showed a gradual increase in the water uptake within thirty days. The swelling ratio of the scaffolds with glycerol showed that chitosan scaffolds presented the highest ratio of water uptake, at 1027.6 % compared to 605.7 % from alginate and 569.3 % for hybrid scaffolds. The scaffolds with glycerol values were higher than the scaffold without glycerol, indicating that the presence of glycerol had increased the swelling behavior of the scaffolds.

The highest weight loss corresponds to the alginate scaffold with glycerol, accounting for 16 % weight loss compared with 15 % from the hybrid scaffold with glycerol and 11.1 % from the chitosan scaffold with glycerol on the thirtieth day. Compared to the scaffolds without glycerol, the scaffolds containing glycerol presented less weight loss in all scaffolds, suggesting that the presence of glycerol worked as a stabilizer of the scaffold structures3636 Bradbury SL, Jakoby WB. Glycerol as an enzyme-stabilizing agent: effects on aldehyde dehydrogenase. Proceedings of the National Academy of Sciences of the United States of America. 1972;69(9):2373-2376.,3737 Vagenende V, Yap MGS, Trout BL. Mechanisms of protein stabilization and prevention of protein aggregation by glycerol. Biochemistry. 2009;48(46):11084-11096..

3.5. Cell viability assay

Cell viability and proliferation on a material are indications of material compatibility, suggesting potential tissue engineering applications. None of the samples decreased cell viability.

After the 24 and 48 h, all scaffolds with and without glycerol presented absorbance values above the negative control (Figure 6). After 48 h, chitosan scaffolds with and without glycerol presented 0.46 % and 3.11 % higher absorbance compared to the positive control, respectively, indicating the possibility of cell proliferation in these scaffolds. The hybrid scaffold without glycerol presented absorbance values close to the positive control (3.67 % above) after 48 h, also indicating possible cell proliferation.

Figure 6
Cellular viability assay using MTT after 24h and 48 h of the alginate, chitosan and hybrid scaffolds without and with glycerol. *Significant statistic difference (p<0.05) in related to the positive control.

3.5.1. Crystal violet

After the 24-hour period, all scaffolds presented results above the positive control values, and the chitosan scaffold with glycerol presented 45.2 % greater absorbance than the negative control (Figure 7); after the 48-hour period, the greater absorbance rate was the hybrid scaffold without glycerol, presenting a rate 37.6 % higher than the positive control, indicating possible cell proliferation. In this assay, it could be concluded that the blend of alginate and chitosan improved the action of the polymers, compared to the results for the pure substances, because the hybrid scaffold presented a relevant result after 48 h.

Figure 7
Cellular viability assay using crystal violet after 24h and 48 h of the alginate, chitosan and hybrid scaffolds without and with glycerol. *Significant statistic difference (p<0.05) in related to the positive control.

Analyzing the two assays (MTT and violet crystal), the results of the hybrid scaffold showed satisfactory biological results in both experiments, with absorbance values near and above the positive control, respectively. This indicates good compatibility and potential as a biomaterial.

3.6. In vitro degradation study

Degradation of chitosan and hybrid scaffolds with and without glycerol was studied by immersing the scaffolds in PBS solution containing lysozyme. The degradation rate was analyzed by SEM (Figure 8).

Figure 8
SEM of (a) chitosan without glycerol, (b) chitosan with glycerol, (c) hybrid without glycerol and (d) hybrid with glycerol scaffolds in the seventh day of assay.

All scaffolds presented degradation of their structures on the seventh day of the assay (Figure 8), confirmed by the concentration peaks of reduced sugars (Figure 9). The hybrid scaffold without glycerol presented incresead degradation, compared to the hybrid scaffold with glycerol. The concentration of reduced sugars incresead by the seventh day, followed by stabilization on the tenth day. The presence of glycerol indicated stabilization in the degradation rate3535 Valente JFA, Valente TAM, Alves P, Ferreira P, Silva A, Correia, IJ. Alginate based scaffolds for bone tissue engineering. Materials Science and Engineering: C. 2012;32(8):2596-2603.,3636 Bradbury SL, Jakoby WB. Glycerol as an enzyme-stabilizing agent: effects on aldehyde dehydrogenase. Proceedings of the National Academy of Sciences of the United States of America. 1972;69(9):2373-2376..

Figure 9
Concentration of reduced sugars of the hybrid and chitosan scaffolds without and with glycerol.

3.7. In vitro biomineralization study

Biomineralization of alginate, chitosan and hybrid scaffolds with and without glycerol was studied by immersing the scaffolds in the SBF solution. The mineral deposition in the scaffolds was analyzed by SEM (Figure 10).

Figure 10
SEM and EDS of (a;al) alginate without glycerol, (b;bl) alginate with glycerol, (c;cl) chitosan without glycerol, (d;dl) chitosan with glycerol, (e;el) hybrid without glycerol and (f;fl) hybrid with glycerol scaffolds in third day of assay.

Chitosan with and without glycerol presented an incidence of mineral deposition compared to the other scaffolds after three days of assay (Figure 10c; 10d). The presence of apatite crystals could be confirmed by the EDS (Figure 10cl; 10dl), indicated by the presence of Ca, P, Mg, K. In the hybrid scaffold without glycerol, apatite crystals also appeared on the third day (Figure 10a; 10b). On the seventh day, the incidence of hydroxyapatite increased in the hybrid scaffold with and without glycerol (Figure 11a; 11b), and on the fifteenth day the chitosan scaffold with and without glycerol presented evidence of mineralization with the apatite crystals (Figure 11c; 11d).

Figure 11
SEM of (a) chitosan without glycerol and (b) chitosan with glycerol scaffolds in the seventh day of assay; (c) hybrid without glycerol and (d) hybrid with glycerol scaffolds in the tenth day of assay.

4. Conclusions

Alginate, chitosan and hybrid scaffolds with and without glycerol were developed and characterized. Tensile tests presented results indicating that the use of glycerol and the interaction between alginate and chitosan as a hybrid fiber were associated with a trend of increasing tenacity values. Hybrid fibers presented an increase of 27.3 % and 55.2 % in tenacity values, compared to chitosan and alginate fibers, respectively. DSC/TG indicated an interaction between the polymers in the thermal analysis. The swelling study and weight loss demonstrated that the scaffolds containing glycerol presented less weight loss and even higher water absorption values in all scaffolds, compared to the scaffolds without glycerol, indicating that glycerol is a stabilizer. None of the alginate, chitosan and hybrid scaffolds with and without glycerol decreased cell viability. In the MTT assay, chitosan with and without glycerol presented higher absorbance than the positive control, indicating cell proliferation. On the third day of the biomineralization assay, chitosan with and without glycerol and the hybrid scaffold without glycerol presented apatite crystals. The degradation study showed that glycerol may have worked as a stabilizer.

Considering all the results, it can be concluded that the hybrid scaffold presented satisfactory mechanical and biological results, due to the increase in tenacity, compared to alginate and chitosan, potential cell proliferation after 48 h in cellular studies and the incidence of apatite crystals since the third day of assay in the biomineralization study. This attests to the fact that the combination of the two polymers can be considered an advance in the development of biomaterial. All tests showed promising results, but other essays are needed for a better evaluation for its application in bone tissue engineering.

5. Acknowledgements

The authors gratefully acknowledge University of São Paulo, CAPES, FAPESP (2013/08617-7), CNPq Brazil for the financial support. The authors are grateful to Centro Integrado de Pesquisa (CIP) - Bauru School of Dentistry - USP for providing some work facilities.

6. References

  • 1
    Chen Q, Liang S, Thouas GA. Elastomeric biomaterials for tissue engineering. Progress in Polymer Science 2013;38(3-4):584-671.
  • 2
    Vacanti JP, Vacanti CA. The History and Scope of Tissue Engineering. In: Lanza R, Langer R, Vacanti J, eds. Principles of Tissue Engineering London: Elsevier; 2013. p. 3-8.
  • 3
    Ayaz HGS, Perets A, Ayaz H, Gilroy KD, Govindaraj M, Brookstein D, et al. Textile-templated electrospun anisotropic scaffolds for regenerative cardiac tissue engineering. Biomaterials 2014;35(30):8540-8552.
  • 4
    Doser M, Planck H. Textiles for implants and regenerative medicine. In: Bartels VT, ed. Handbook of Medical Textiles Cambridge: Woodhead Publishing; 2011. p. 132-152.
  • 5
    Tamayol A, Akbari M, Annabi N, Paul A, Kadhemhosseini A, Juncker D. Fiber-based tissue engineering: Progress, challenges and opportunities. Biotechnology Advances 2013;31(5):669-687.
  • 6
    Braghirolli DI, Steffens D, Pranke P. Electrospinning for regenerative medicine: a review of the main topics. Drug Discovery Today 2014;19(6):743-753.
  • 7
    Venkatesan J, Bhatnagar I, Manivasagan P, Kang KH, Kim SK. Alginate composites for bone tissue engineering: A review. International Journal of Biological Macromolecules 2015;72:269-281.
  • 8
    Bose S, Roy M, Bandyopadhyay A. Recent advances in bone tissue engineering scaffolds. Trends in Biotechnology 2012;30(10):546-554.
  • 9
    Wang P, Tawiah B, Tian A, Wang C, Zhang L, Fu S. Properties of alginate fiber spun-dyed with fluorescent pigment dispersion. Carbohydrate Polymers 2015;118:143-149.
  • 10
    Venkatesan J, Bhatnagar I, Kim SK. Chitosan-alginate biocomposite containing fucoidan for bone tissue engineering. Marine Drugs 2014;12(1):300-316.
  • 11
    Croisier F, Jérôme C. Chitosan-based biomaterials for tissue engineering. European Polymer Journal 2013;49(4):780-792.
  • 12
    Li Z, Ramay HR, Hauch KD, Xiao D, Zhang M. Chitosan-alginate hybrid scaffolds for bone tissue engineering. Biomaterials 2005;26(18):3919-3928.
  • 13
    Simsek-Ege FA, Bond GM, Stringer J. Polyelectrolyte complex formation between alginate and chitosan as a function of pH. Journal of Applied Polymer Science 2003;88(2):346-351.
  • 14
    Baysal K, Aroguz AZ, Adiguzel Z, Baysal BM. Chitosan/alginate crosslinked hydrogel: Preparation, characterization and application for cell growth purposes. International Journal of Biological Macromolecules 2013;59:342-348.
  • 15
    Lee K, Ahn S, Choi CH, Lee D, Jung WK, Kim G. Functionallized alginate/chitosan biocomposites consisted of cylindrical struts and biologically designed for chitosan release. Current Applied Physics 2014;14(8):1105-1106.
  • 16
    Iwasaki N, Yamane ST, Majima T, Kasahara Y, Minami A, Harada K, et al. Feasibility of polysaccharide hybrid materials for Scaffolds in cartilage tissue engineering: evaluation of chondrocyte adhesion to polyion complex fibers prepared from alginate and chitosan. Biomacromolecules 2004;5(3):828-833.
  • 17
    Hu WW, Yu HN. Coelectrospinning of chitosan/alginate fibers by dual-jet system for modulating material surfaces. Carbohydrate Polymers 2013;95(2):716-727.
  • 18
    Hyland LL, Taraban MB, Hammouda B, Yu YB. Mutually reinforced multicomponent polysaccharide networks. Biopolymers 2011;95(12):840-851.
  • 19
    Maluf E, Kolbe W. Textile fibers. In: Technical Textile Industry Data 2nd ed. São Paulo: Institute for Technological Research and Brazilian Textile and Confection Industry Association (ABIT); 2003. p. 1-64.
  • 20
    International Organization for Standardization (ISO). ISO 5084:1996. Determination of thickness of textiles and textile products Geneva: International Organization for Standardization; 1996.
  • 21
    International Organization for Standardization (ISO). ISO 2060:1994. Textiles -- Yarn from packages -- Determination of linear density (mass per unit length) by the skein method Geneva: International Organization for Standardization; 1994.
  • 22
    International Organization for Standardization (ISO). ISO 1139:1973. Textiles - Designation of yarns Geneva: International Organization for Standardization; 1973.
  • 23
    International Organization for Standardization (ISO). ISO 139:2005. Textiles - Standard atmospheres for conditioning and testing Geneva: International Organization for Standardization; 2005.
  • 24
    ASTM International. ASTM D3822. Standard Test Method for Tensile Properties of Singles Textile Fibers West Conshohocken: ASTM International; 2007.
  • 25
    Volpato LE, Oliveira RC, Epinosa MM, Bagnato VS, Machado MAAM. Viability of fibroblasts cultured under nutritional stress irradiated with red laser, infrared laser, and red light-emitting diode. Journal of Biomedical Optics 2011;16(7):075004.
  • 26
    Ghose TK. Measurement of cellulase activities. Pure and Applied Chemistry 1987;59(2):257-268.
  • 27
    Kokubo T, Takadama H. How useful is SBF predicting in vivo bone bioactivity? Biomaterials 2006;27(15):2907-2915.
  • 28
    Hearle JWS, Morton WE. Physical Properties of Textile Fibres 4th ed. Cambridge: Woodhead Publishing; 2008.
  • 29
    Niekraszewicz B, Niekraszewicz A. The structure of alginate, chitin and chitosan fibres. In: Eichhorn SJ, Hearle JWS, Jaffe M, Kikutani T, eds. Handbook of Textile Fibre Structure Volume 2: Natural, Regenerated, Inorganic and Specialist Fibres Cambridge: Woodhead Publishing; 2009. p. 266-306.
  • 30
    Anandjwala RD. Role of advanced textile materials in healthcare. In: Anand S, Kennedy JF, Miraftab M, Rajendran S, eds. Medical Textiles and Biomaterials for Healthcare Cambridge: Woodhead Publishing; 2006. p. 90-98.
  • 31
    Kaswell ER. Wellington Sears Handbook of Industrial Textiles New York: Wellington Sears Company; 1963.
  • 32
    Wendlandt WW. Thermal Analysis New York: John Wiley & Sons; 1986.
  • 33
    Price DM, Hourston DJ, Dumont F. Thermogravimetry of Polymers. In: Meyers RA, ed. Encyclopedia of Analytical Chemistry Chichester: John Wiley & Sons; 2000. p. 8094-8105.
  • 34
    Lima PA, Resende CX, Soares GD, Anselme K, Almeida LE. Preparation, characterization and biological test of 3D-scaffolds based on chitosan, fibroin and hydroxyapatite for bone tissue engineering. Materials Science and Engineering: C 2013;33(6):3389-3395.
  • 35
    Valente JFA, Valente TAM, Alves P, Ferreira P, Silva A, Correia, IJ. Alginate based scaffolds for bone tissue engineering. Materials Science and Engineering: C 2012;32(8):2596-2603.
  • 36
    Bradbury SL, Jakoby WB. Glycerol as an enzyme-stabilizing agent: effects on aldehyde dehydrogenase. Proceedings of the National Academy of Sciences of the United States of America 1972;69(9):2373-2376.
  • 37
    Vagenende V, Yap MGS, Trout BL. Mechanisms of protein stabilization and prevention of protein aggregation by glycerol. Biochemistry 2009;48(46):11084-11096.

Publication Dates

  • Publication in this collection
    23 Jan 2017
  • Date of issue
    Mar-Apr 2017

History

  • Received
    07 July 2016
  • Reviewed
    21 Oct 2016
  • Accepted
    27 Dec 2016
ABM, ABC, ABPol UFSCar - Dep. de Engenharia de Materiais, Rod. Washington Luiz, km 235, 13565-905 - São Carlos - SP- Brasil. Tel (55 16) 3351-9487 - São Carlos - SP - Brazil
E-mail: pessan@ufscar.br