Effect of thermocycling on the bond strength of a glass-infiltrated ceramic and a resin luting cement

Efeito da ciclagem térmica sobre a resistência de união entre uma cerâmica infiltrada com vidro e um cimento resinoso

Abstracts

The aim of the present study was to evaluate the effect of thermocycling on the bond strength between the surface of the glass-infiltrated alumina ceramic In-Ceram (VITA) and the Panavia F resin cement (Kuraray CO.). Four 5x6x6mm In-Ceram blocks were obtained. One of the 6x6mm faces of each block was conditioned with Cojet - System (tribochemical silica coating, ESPE-3M) and then luted under a constant 750g pressure with Panavia F cement to another identical face of a resin composit block (Clearfil AP-X, Kuraray) obtained by reproduction of the ceramic one from Express (3M) addition curing silicone impressions. The four sets so formed by ceramic, luting cement and resin have been each one serially sectioned in 20 sticks so that the adhesive surface in each presented 1mm² of area. The samples were divided in 2 groups (n=10): G1- stored for 7 days in deionized water at 36 ± 2ºC; G2 - thermocycled 1500 times between 5 and 55ºC dwell times. The microtensile tests were accomplished in an universal testing machine (EMIC) at a crosshead speed of 0,5 mm/min. The results showed that the mean tensile bond strength values (MPa) for the group G2: (22,815 ± 5,254) had not statistically differ of the values of group G1: (25,628 ± 3,353) (t = 1,427; gl = 18; p-value = 0,171), at the level of a= 5%. It can be concluded that the thermocycling technique used in the present experiment had not produced statistically significant differences between the bond strength results of the specimens obtained by the two used techniques.

Dental ceramics; Resin cements; Air abrasion

O objetivo deste estudo foi avaliar o efeito da ciclagem térmica sobre a resistência de adesão entre a superfície da cerâmica In-Ceram Alumina (VITA) e o cimento resinoso Panavia F (Kuraray). Foram confeccionados quatro blocos de cerâmica In-Ceram com dimensões de 5x6x6mm. Uma das faces com 6x6mm de cada bloco cerâmico, após condicionamento com o sistema Cojet (ESPE-3M) (jateamento com óxido de alumínio/jateamento com óxido de sílica/ silanização) foi cimentada com Panavia F, sob peso constante de 750g, a outro bloco idêntico de resina composta Clearfil AP-X (Kuraray). Os blocos de resina foram obtidos por meio de duplicação daqueles de cerâmica a partir de moldes com silicona de adição Express (3M). Os quatro conjuntos formados por cerâmica, cimento e resina foram seccionados em 20 corpos-de-prova com forma de palitos, de modo que a região adesiva apresentasse 1mm² de área. Dois grupos (n=10) foram constítuidos: G1- estocagem por 7 dias em água deionizada à 36 ± 2ºC; G2- 1500 ciclos entre 5ºC e 55ºC com intervalos de 30 segundos. A seguir, foi realizado o teste de microtração em máquina de ensaio universal (EMIC) com velocidade de 0,5 mm/min. Os resultados mostraram que os valores médios de tensão de ruptura (MPa) para o grupo G2: (22,815 ± 5,254) não tiveram diferenças estatisticamente significantes daqueles do grupo G1: (25,628 ± 3,353) (t= 1,427; gl = 18; p-valor = 0,171), ao nível de significância de 5%. A partir destes resultados, entendemos lícito concluir que o efeito da ciclagem térmica não produziu alterações estatisticamente significantes nos valores da resistência adesiva.

Cerâmica dental; Cimentos resinosos; Abrasão dental por ar

ORIGINAL ARTICLES

Effect of thermocycling on the bond strength of a glass-infiltrated ceramic and a resin luting cement

Efeito da ciclagem térmica sobre a resistência de união entre uma cerâmica infiltrada com vidro e um cimento resinoso

Osvaldo Daniel Andreatta Filho^I; Marco Antonio Bottino^II; Renato Sussumu Nishioka^II; Luiz Felipe Valandro^III; Fabíola Pessoa Pereira Leite^I

^IPost Graduate Student - Master Degree - School of Dentistry of São José dos Campos - SP - UNESP

^IIDepartament of Dental Materials and Prosthodontics - School of Dentistry of São José dos Campos - SP - UNESP

^IIIProfessor of Prosthodontics of the University of Santa Maria - RS and Post Graduate Student - Master Degree - School of Dentistry of São José dos Campos - SP - UNESP

^{Correspondence}

ABSTRACT

The aim of the present study was to evaluate the effect of thermocycling on the bond strength between the surface of the glass-infiltrated alumina ceramic In-Ceram (VITA) and the Panavia F resin cement (Kuraray CO.). Four 5x6x6mm In-Ceram blocks were obtained. One of the 6x6mm faces of each block was conditioned with Cojet - System (tribochemical silica coating, ESPE-3M) and then luted under a constant 750g pressure with Panavia F cement to another identical face of a resin composit block (Clearfil AP-X, Kuraray) obtained by reproduction of the ceramic one from Express (3M) addition curing silicone impressions. The four sets so formed by ceramic, luting cement and resin have been each one serially sectioned in 20 sticks so that the adhesive surface in each presented 1mm² of area. The samples were divided in 2 groups (n=10): G1- stored for 7 days in deionized water at 36 ± 2ºC; G2 — thermocycled 1500 times between 5 and 55ºC dwell times. The microtensile tests were accomplished in an universal testing machine (EMIC) at a crosshead speed of 0,5 mm/min. The results showed that the mean tensile bond strength values (MPa) for the group G2: (22,815 ± 5,254) had not statistically differ of the values of group G1: (25,628 ± 3,353) (t = 1,427; gl = 18; p-value = 0,171), at the level of a= 5%. It can be concluded that the thermocycling technique used in the present experiment had not produced statistically significant differences between the bond strength results of the specimens obtained by the two used techniques.

Uniterms: Dental ceramics; Resin cements; Air abrasion.

RESUMO

O objetivo deste estudo foi avaliar o efeito da ciclagem térmica sobre a resistência de adesão entre a superfície da cerâmica In-Ceram Alumina (VITA) e o cimento resinoso Panavia F (Kuraray). Foram confeccionados quatro blocos de cerâmica In-Ceram com dimensões de 5x6x6mm. Uma das faces com 6x6mm de cada bloco cerâmico, após condicionamento com o sistema Cojet (ESPE-3M) (jateamento com óxido de alumínio/jateamento com óxido de sílica/ silanização) foi cimentada com Panavia F, sob peso constante de 750g, a outro bloco idêntico de resina composta Clearfil AP-X (Kuraray). Os blocos de resina foram obtidos por meio de duplicação daqueles de cerâmica a partir de moldes com silicona de adição Express (3M). Os quatro conjuntos formados por cerâmica, cimento e resina foram seccionados em 20 corpos-de-prova com forma de palitos, de modo que a região adesiva apresentasse 1mm² de área. Dois grupos (n=10) foram constítuidos: G1- estocagem por 7 dias em água deionizada à 36 ± 2ºC; G2- 1500 ciclos entre 5ºC e 55ºC com intervalos de 30 segundos. A seguir, foi realizado o teste de microtração em máquina de ensaio universal (EMIC) com velocidade de 0,5 mm/min. Os resultados mostraram que os valores médios de tensão de ruptura (MPa) para o grupo G2: (22,815 ± 5,254) não tiveram diferenças estatisticamente significantes daqueles do grupo G1: (25,628 ± 3,353) (t= 1,427; gl = 18; p-valor = 0,171), ao nível de significância de 5%. A partir destes resultados, entendemos lícito concluir que o efeito da ciclagem térmica não produziu alterações estatisticamente significantes nos valores da resistência adesiva.

Unitermos: Cerâmica dental; Cimentos resinosos; Abrasão dental por ar.

INTRODUCTION

In recent decades, patients have been pressing dental profession with a great demand for aesthetics and so, a large quantity of research are being developed for obtaining new materials with improved aesthetic properties, color stability, more resistance to fracture, possibility of better marginal adaptation and good chemical compatibility with the new resin luting cements.

The ceramic system constituted of infiltrated by glass (15%) densely sintered alumina surface (85%) (In-Ceram, Vita, Bad Säckingen, Germany) is characterized by a framework that has flexural resistance 75% larger than other dental ceramics and this kind of material was developed supposedly to substitute metallic frameworks of metal-ceramic crowns.

Although studies as one by McLaren¹⁹ indicate that the conventional cementation can be satisfactorily obtained with zinc phosphate and glass-ionomer cements in the In-Ceram system, Kern ¹⁴ suggested that the cementation should be done with resin luting cements because they have qualities as resistance to the fracture which can improve the final result of restoration. So, a stable chemical bonding should be reached between resin luting cements and full crowns or ceramic restorations constituted of alumina as the In-Ceram system.

The bond strength between the conventional feldspathic ceramics and resin luting cements is obtained and increased by the etching of the ceramic surface with 2% fluoridric acid and treatment with a silane agent^2,7,26. However this method is not applied to the ceramic systems that have alumina infiltrated with glass, because it doesn´t promote appropriate bond strength with resin luting cements^{16, 22}. This method is not indicated because it occurs the weakness of the bond union, due the elimination of the glass matrix of the ceramic surface after etching.

Searching a new method of superficial treatment of the glass-infiltrated alumina ceramic, Kern¹⁴ and Blixt³ verifyed the increase on bonding strength values when they used a BIS-GMA resin luting cement associated to the alumina surface sandblasting of the In-Ceram with a Tribochemical silica coating - Rocatec system (Espe-3M) (Rocate-Pre: sandblasting with Al₂O₃ 110mm, Rocatec-Plus: silicoating with special powder of silica 30mm, Rocatec-Sil: silane coating).

Also Kraivixien-Vongphantuset¹⁶, Kern¹⁴, Marais¹⁸ and Kiyan¹⁵ demonstrated larger values of bond strength between resin luting cements and the glass-infiltrated alumina ceramic conditioned with tribochemical silica coating (Rocatec), even under thermic treatment⁹.

The aim of this study was to verify by using the microtensile test, the effect of the thermocycling on the bond strength between a resin luting cement containing phosphate monomer (Panavia F, Kuraray, Osaka, Japan) and a glass-infiltrated alumina ceramic In-Ceram, conditioned with the Cojet-System (tribochemical silica coating) similar to the Rocatec system^{4, 5, 6, 8, 10 13}.

MATERIAL AND METHODS

For the present study, four blocks of glass-infiltrated alumina ceramic (In-Ceram, Vita Zahnfabrik, Bad Säckingen, Germany) with dimensions of 5x6x6mm have been obtained according to the manufacturer's instructions (Figure 1).

For verifying the quality of these blocks they have been examined by x-ray and the samples with any air bubble have been eliminated. Exact reproductions of these ceramic blocks were then obtained in Kuraray Clearfil AP-X resin composit, by means of 3M Express addition curing silicone impressions.

One of the 6x6mm surfaces of each ceramic block, was planned by polishing with 300, 600, 800, 1000, 1200-grit sandpaper with the objective of creating a plane and coincident surface to the block made with composit resin. After this procedure, each ceramic surface was sandblasted with the Cojet-System (ESPE-3M), which consists of an initial sandblasting with aluminum oxide particles 110mm, at a standard distance of 10mm and perpendicular to the surface, for 20 seconds with pressure of 2,8bars, followed by other sandblasting with special particles of silica 30mm that promote the silicatization (silica coating) and at last the application of a silane coat (ESPE-Sil).

The conditioned surfaces were cemented with Panavia F to the resin composit blocks. The cement was manipulated according to the manufacturer's recommendations and applied initially on the conditioned surface of the ceramic block, and after it was united to the resin composit block. It was then obtained a set constituted by ceramic, cement and resin that was positioned in a device to promote the cementation, under a constant load of 750g, for 10 minutes (Figure 2).

The excess of cement on the margins was removed and the light activation of the cement was reached applying the light for 40 seconds on each side of the sets. Cementation was concluded with the application of the oxygen-blocking gel (Oxyguard for the Panavia F). After the total curing of the cement, the sets were washed with air-water flush and stored in deionized water at 36 ± 2ºC (Figure 3).

It was obtained four sets of ceramic blocks cemented to resin blocks, that were fixed in a lathe adapted by Andreatta¹ to accomplish precision cuts with diamond disks of 0,15mm of thickness and 22mm of diameter (Figure 4).

The 1mm external faces of the sets were splited up in order to avoid that excess of cement on the lateral walls could influence the final results. After this, the blocks were cut in slices of 10x6x1mm. At last, this slices were splited up longitudinally for obtaining 20 samples with dimensions of 10x1x1mm ± 0,1mm (Figure 5).

Two groups were established with ten samples (n=10) each one, varying the type of thermal treatment. In group I (no thermocycled) the samples were stored for 7 days in deionized water at 36 ± 2ºC and in group II (thermocycled) the samples were submitted to 1500 thermal cycles in baths at 5ºC and 55ºC, with 30 seconds dwell times. After the thermal treatments, each sample was glued with cyanoacrylate adhesive to an adapted calliper for accomplishment of the microtensile test. In this equipment the applied load is perpendicular to the long axis of the sample for avoiding the occurrence of sprain forces and shear on the bond area. Each sample glued to the calliper was adapted to the universal testing machine (DL-1000 - EMIC - Equipamentos e Sistemas de Ensaio Ltda - São José dos Pinhais - PR) and loaded to failure under tension at a crosshead speed of 0,5 mm/minute (Figure 6).

Results have been compared by the Student´s test with 5% of significance.

RESULTS

The data of the microtensile test when submitted to the normality and homogeneity tests of variance were considered a normal population (p-value > 0,05) and of same variance (p-value > 0,05). The Student´s test made for comparison of the thermocycling effects didn't indicate statistical difference (Table 1).

The variability on the data is represented in Figure 7. The very close values of variation coefficient (VC = 5,254 / 22,815 = 23% for the situation with thermocycling, and, of VC = 3,353 / 25,628 = 13% for the situation without thermocycling), denoted that the values are homogeneous and that the mean can be considered a measure of central tendency, representative, of the same ones.

DISCUSSION

Laboratory thermocycling is the simulation of the physical process in the oral environment that more frequently influences the integrity of the bonding union between restorative materials and luting agents. Chang⁵ verifyed that several bonding systems are influenced by cyclical variations of temperature. Due to this fact, the present work evaluated the effect of the thermocycling on the bond strength between a glass-infiltrated alumina ceramic surface conditioned with a sandblasting with silica powder (silicoating) and a resin luting cement containig in its composition phosphate monomer. However, other methods of superficial etching, have not been compared in the present study because it was based on studies that report more efficient results of the surface treatment by silicatization (tribochemical silica coating - Rocatec) of the glass-infiltrated alumina ceramic^{3, 12, 14, 15, 20, 21}.

Pape²² and Kraivixien-Vongphantues¹⁶ reported that bond strength of resin luting cements to In-Ceram surface is not appropriate when procedures are used to condition feldsphatic ceramics, such as, acid etching adding silane coating, because in the In-Ceram system acids do not promote similar micromechanical retentive surface like on the conventional ceramics²⁵. Some authors^{11, 12} suggested a surface treatment with sandblasting of aluminum oxide 110mm (Al2O3) to create micromechanical retention in the surface of the aluminous ceramics, however only sandblasting doesn´t promote effective chemical bond with the silane agents, because of the low amount of silica present in the glass matrix of the In-Ceram ceramic system^{11, 25}.

In spite of these surface treatment methods presenting a high value of bond strength immediately after the cementation procedures, when submitted to treatments of thermocycling even under storage in larger periods than 30 days in distilled water at 37ºC, the values of bond strength decreased to very low levels and do not promote a stable chemical union between ceramic and luting cement¹⁴.

The Rocatec system introduced by Guggenberger⁹ to condition metallic surfaces, was used initially by Neikes²⁰, Kraivixien-Vongphantuset¹⁶ and then by Kern ^{12, 14} to condition the glass-infiltrated alumina ceramic surface (In-Ceram), promoting the increase of silica content to 19,7% in weight. This treatment method by sandblasting (silicoating), according to these authors' results, presented values of bond larger than other adhesive methods of superficial treatment mentioned before and higher bond strength between ceramic and BIS-GMA resin luting cements.

In the works above mentioned, the maintenance of the integrity of the bond strength between In-Ceram ceramic and resin luting cements was submitted to thermo cycles in water that varied from 200 to 37500 cycles between 5^oC and 55^oC with 30 seconds of immersion in each bath. It was however verifyed in these studies that even in thermal tests with great amounts of cycles the bond strength between aluminous ceramic and BIS-GMA resin luting cements was not significantly altered.

The conditioning of In-Ceram ceramic surface by Cojet-System, presented as results, lower values of bond strength when compared to previous studies. However, in the present study the results demonstrated that the values between the group I and group II were not altered in a significant way by the effect of the thermocycling. There was a stability of the adhesive unions, corroborating with the results found by Kern¹⁴. A fact to be considered in the author´s studies^{14, 16, 21} mentioned above is that they did not link comparative values between numbers of thermal cycles and time in oral environment so, our work was based on Leibrock¹⁷ that establishes an approximate relationship of these values. Based on this fact, the use of 1500 thermal cycles would be similar in physiologic normal conditions during the period of 1 and a half of year. So the numbers of cycles used in the methodology was considered reasonable.

Regarding the values of bond strength obtained with the conditioning of the In-Ceram surface with the Cojet-System had been lower than the presented in other works ¹⁴ that evaluated the conditioning with the Rocatec system, we believed that such fact could be explained because Panavia-F cement´s composition differs by it containing phosphate-monomer and not BIS-GMA as in the resin luting cements used in other works. The fact that the mean values obtained for groups I and II have not been statistically differents, indicates that thermocycling did not compromise the stability of the bond strength between ceramic and resin cement. Other fact to consider is the method used for measuring bond strength because in our study we verifyed adhesive failures only, while in other methods it was observed cohesive failures of the materials, so the results could not supply a real evaluation of the bonding strength between restorative materials and luting cements^{23, 24}. On the limitations of our study, that just evaluated one method of conditioning the glass-infiltrated alumina ceramic, we suggest that other works must be developed using the microtensile methodology to verify the values of bond strength created by other surface treatments as the Rocatec system and resin luting cements containing in its composition BIS-GMA. Such tensile method is suggested because we think it can be obtained trustful results of adhesive failures.

CONCLUSION

The results obtained demonstrated that the thermocycling technique here used had not produced statistically significant differences between the bond strength results of the specimens obtained by the two technics employed in the present experiment.

BIBLIOGRAPHIC REFERENCES

• 1- Andreatta Filho OD, Nishioka RS, Almeida EES. Construção de um torno mecânico para realizar preparos dentais padronizados. In: Anais da 17Ş. Reunião Anual da Sociedade Brasileira de Pesquisa Odontológica — SBPqO; 2000 set. 2-6; Águas de Lindóia (SP). São Paulo: SBPqO; 2000. p.17, resumo I047.
• 2- Bailey LF, Bennett RJ. Dicor surface treatments for enhanced bonding. J Dent Res 1988; 67: 925-31.
• 3- Blixt M, Adamczak E, Linden L A, Oden A, Arvidson K. Bonding to densely sintered alumina surfaces: effect of sandblasting and silica coating on shear bond strength of luting cements. Int J Prosthodont 2000;13: 221-6.
• 4- Bouschlicher MR, Cobb DS, Vargas MA. Effect of two brasive systems on resin bonding to laboratory-processed indirect resin composite restorations. J Esthet Dent 1999; 11: 185-96.
• 5- Chang JC, Koh SH, Powers JM, Duong JH. Tensile bond strengths of composites to a gold-palladium alloy after thermal cycling. J Prosthet Dent 2002; 87: 271-6.
• 6- Cobb DS, Vargas MA, Fridrich TA, Bouschlicher MR. Metal surface treatment: characterization and effect on composite-to-metal bond strength. Oper Dent 2000; 25: 427-33.
• 7- Della Bona A, Anusavice KJ, Shen C. Microtensile strength of composite bonded to hot-pressed ceramics. J Adhes Dent 2000; 2: 305-13.
• 8- Frankenberger R, Kramer N, Sindel J. Repair strength of etched vs silica-coated metal-ceramic and all-ceramic restorations. Oper Dent 2000; 25: 209-15.
• 9- Guggenberger R. [Rocatec system-adhesion by tribochemical coating] Dtsch Zahnarztl Z 1989; 44: 874-6.
• 10- Haselton DR, Diaz-Arnold AM, Dunne JT Jr. Shear bond strengths of 2 intraoral porcelain repair systems to porcelain or metal substrates. J Prosthet Dent 2001; 86: 526-31.
• 11- Kern M, Neikes MJ, Strub JR. [Tensile strength of the bond to In-ceram after varying modes of surface conditioning]. Dtsch Zahnarztl Z 1991; 46: 758-61.
• 12- Kern M, Thompson VP. Sandblasting and silica coating of a glass-infiltrated alumina ceramic: volume loss, morphology, and changes in the surface composition. J Prosthet Dent 1994; 71: 453-61.
• 13- Kern M, Thompson VP. Effects of sandblasting and silica-coating procedures on pure titanium. J Dent 1994; 22: 300-6.
• 14- Kern M, Thompson VP. Bonding to glass infiltrated alumina ceramic: adhesive methods and their durability. J Prosthet Dent 1995; 73: 240-9.
• 15- Kiyan VH. Influência do tratamento das superfícies internas de dois tipos de cerâmicas na resistência adesiva à tração. São Paulo; 2001. [Dissertação de Mestrado da Faculdade de Odontologia da Universidade de São Paulo. São Paulo].
• 16- Kraivixien-Vongphantuset R, Pietrobon N, Nathanson D. Bond strength of resin cement to In-Ceram core material [Abstract]. J Dent Res 1992; 71: 533.
• 17- Leibrock A, Degenhart M, Behr M, Rosentritt M, Handel G. In vitro study of the effect of thermo- and load-cycling on the bond strength of porcelain repair systems. J Oral Rehabil 1999; 26: 130-7.
• 18- Marais JT, Herbst D. In-Ceram, a combination of strength and aesthetics, with a bonding dilemma. J Dent Assoc S Afr 1996; 51: 53-5.
• 19- McLaren EA, White SN. Glass-infiltrated zirconia/ alumina-based ceramic for crowns and fixed partial dentures: clinical and laboratory guidelines. Pract Periodontics Aesthet Dent 1999; 11: 985-94..
• 20- Neikes MJ, Kern M, Strub JR. Tensile bond strength of two silicoating (silicate/silanization) systems on the Al₂O₃-Ceramic In-Ceram [Abstract]. J Dent Res 1992; 71:533.
• 21- Ozcan M, Alkumru HN, Gemalmaz D. The effect of surface treatment on the shear bond strength of luting cement to a glass-infiltrated alumina ceramic. Int J Prosthodont 2001; 14: 335-9.
• 22- Pape FW, Pfeiffer P, Marx R. [Bond strength of etched In-Ceram(R) to tooth enamel]. ZWR 1991; 100: 450-3.
• 23- Pashley DH, Sano H, Ciucchi B, Yoshiyama M, Carvalho RM. Adhesion testing of dentin bonding agents: a review. Dent Mater 1995; 11: 117-25.
• 24- Sano H, Shono T, Sonoda H, Takatsu T, Ciucchi B, Carvalho R, et al. Relationship between surface area for adhesion and tensile bond strength-evaluation of a micro-tensile bond test. Dent Mater 1994; 10: 236-40.
• 25- Schmid M, Fischer J, Hoffmann C, Strub JR. [Chemical and thermal compatibility of all-ceramic systems]. Dtsch Zahnarztl Z 1990; 45: 505-8.
• 26- Wolf DM, Powers JM, O´Keefe KL. Bond strength of composite to porcelain treated with new porcelain repair agents. Dent Mater 1992; 8: 158-61.

Publication Dates

• Publication in this collection
  08 Dec 2004
• Date of issue
  Mar 2003