Effect of 4% titanium tetrafluoride solution on the erosion of permanent and deciduous human enamel: an in situ/ex vivo study

ORIGINAL ARTICLES

Effect of 4% titanium tetrafluoride solution on the erosion of permanent and deciduous human enamel: an in situ/ex vivo study

Ana Carolina Magalhães^I; Daniela Rios^II; Heitor Marques Honório^III; Alberto Carlos Botazzo Delbem^IV; Marília Afonso Rabelo Buzalaf^V

^IDDS, MSc, PhD, Assistant Professor, Department of Biological Sciences, Bauru School of Dentistry, University of São Paulo, São Paulo, Brazil

^IIDDS, MSc, PhD, Assistant Professor, Department of Pediatric Dentistry, Orthodontics and Community Health, Bauru School of Dentistry, University of São Paulo, São Paulo, Brazil

^IIIDDS, MSc, PhD, Assistant Professor, Department of Pediatric Dentistry, Federal University of Alfenas, Alfenas, MG, Brazil

^IVDDS, MSc, PhD, Associante Professor, Department of Child and Social Dentistry, São Paulo State University, School of Dentistry at Araçatuba, Araçatuba, SP, Brazil

^VDDS, MSc, PhD, Full Professor, Department of Biological Sciences, Bauru School of Dentistry, University of São Paulo, São Paulo, Brazil

^{Corresponding address}

ABSTRACT

This in situ/ex vivo study assessed the effect of titanium tetrafluoride (TiF₄) solution on erosion of permanent (P) and deciduous (d) human enamel. Ten volunteers wore acrylic palatal appliances containing 4 enamel samples, divided into two rows: TiF₄ and no - TiF₄ (control). Each row contained one deciduous and one permanent enamel sample. During the 1st day, formation of a salivary pellicle was allowed. At the 2^nd day, the 4% TiF₄ solution was applied on one row (TiF₄), while the other row remained untreated (control). From the 3^rd until the 7^th day, the samples were subjected to erosion by immersion in a cola drink for 5 min, 4 times/day. Enamel alterations were determined by microhardness testing (%SMHC). Data were analyzed using 2 two-way ANOVA and Tukey's post hoc test (α=0.05). The mean %SMHC (±SD) amounted to: P (TiF₄ - 73.32 ± 5.16 and control - 83.49 ± 4.59) and d (TiF₄ - 83.01 ± 7.41 and control - 75.75 ± 2.57). In conclusion, the application of 4% TiF₄ solution reduced the softening of permanent enamel but not of deciduous enamel significantly. However, no significant differences were detected between the permanent and deciduous enamel when the factor substrate was considered.

Key words: Dental erosion. Enamel. Fluoride. Titanium tetrafluoride.

INTRODUCTION

While there is a decline in the prevalence of dental caries in most developed countries¹⁹, an increasing prevalence of other dental disorders, such as dental erosion, has been observed¹⁶. Dental erosion is defined as the loss of tooth substance by chemical processes (acids) not involving bacteria¹⁶. The most important sources are dietary acids (acidic foods and drinks)¹⁴ and gastric acids (regurgitation and reflux disorders)³ . In modern societies, the increased consumption of acidic drinks, such as soft drinks, sport drinks, fruit juices and fruit teas, is becoming the most important factor in the etiology of dental erosion^14,16.

Topical application of fluoride on dental hard tissues is considered as a major approach in the prevention of dental erosion. High-concentrated fluoride applications, such as oral rinses, gels or varnishes, have been considered as most effective in reducing the development of enamel erosion⁷. The fluoride agents that have been investigated in most in vitro studies about dental erosion are those that have been used over years for caries prevention: sodium fluoride (NaF), acidulated phosphate fluoride (APF), stannous fluoride (SnF₂) and amine fluoride (AmF). More recently, the preventive effect of other fluoride agents, such as 4% titanium tetrafluoride (TiF₄) solution, have been investigated in erosion tests^{5,9,10,17,21-26}.

While some studies showed an inhibitory effect of TiF₄ on erosion^{5,9,10,21,22-24}, other studies did not found a protective effect^17,25,26. In addition, studies evaluating the effect of this compound on deciduous enamel erosion are missing as yet. As some controversy remains about the susceptibility of deciduous teeth compared to permanent teeth to erosion^1,11-13,15, it is assumed that the efficacy of TiF₄ on these substrates might also be different. Therefore, the purpose of this study was to assess the effect of TiF₄ solution on permanent and deciduous human enamel subjected to erosion in situ/ex vivo.

MATERIAL AND METHODS

Enamel Samples and Palatal Appliance Preparation

The experimental design of the study is illustrated in Figure 1.

Permanent (4x4x3mm) and deciduous (2x2x2mm) human enamel samples were prepared from freshly extracted impacted third molars and deciduous incisors, respectively. The teeth were sterilized by storage in 2% formaldehyde solution (pH 7.0) for 30 days at room temperature²⁷. The enamel surface of the samples was ground flat with water-cooled 320-, 600- and 1200-grit Al₂O₃ papers (Buehler, Lake Bluff, IL, USA) and polished with felt paper wet by diamond spray (1 µm; Buehler). The initial surface microhardness determination was performed by five indentations in the center of the enamel blocks (Knoop diamond, 25 g, 5 s, HMV-2000; Shimadzu Corporation, Tokyo, Japan).

Twenty permanent and twenty deciduous enamel samples with a mean surface microhardness of 368.24 ± 11.57 KHN and 358.51 ± 12.57 KHN, respectively, were randomly assigned to two groups (TiF₄ and control). Two cavities of 5x5x3mm were prepared on the left and right sides of intraoral acrylic palatal appliances. Samples were allocated to treatments by stratified randomization according to the mean surface microhardness. In each row, one sample of permanent and deciduous enamel was fixed with wax.

In Situ Phase

This study was approved by the Research Ethics Committee of the Bauru School of Dentistry, University of São Paulo (Protocol #78/2005). Ten healthy adult volunteers (6 females and 4 males, aged 19-30 years) residing in the same fluoridated area (0.70 mgF/L), who fulfilled the inclusion criteria described below, took part in this study. All participants presented normal salivary parameters⁶, such as adequate stimulated and non-stimulated salivary flows (1.88 ± 1.00mL/min and 0.60 ± 0.33mL/min, respectively) and salivary pH (7.32 ± 0.30). No active erosive lesions or new carious cavities were found.

The volunteers wore acrylic palatal appliances containing 4 human enamel samples, divided into two rows: TiF₄ and no-TiF₄ (control). Each row contained one deciduous and one permanent enamel sample. In the first 24 h, the samples were not subjected to erosive process in order to allow the formation of a salivary pellicle⁸. At the 2^nd day, the application of the fluoride solution (4% TiF₄) was made extraorally by one of the researchers. The 4% (1.29 M F) TiF₄ solution was prepared by dissolution of powdered TiF₄ (Aldrich Chemical Company, Milwaukee, WI, USA) in deionized water. The pH of the fresh solution amounted to 1.2. The TiF₄ solution was applied in drops for 1 min on one row (TiF₄), while the other row remained untreated (control). The drop was left undisturbed until the surface appeared dry. Additional drops were applied in the same manner until 1 min had elapsed²³. After that, the excess of the solution was removed with a cotton swab.

From the 3^rd to the 7^th day, erosive challenges were made extraorally 4 times a day and at predetermined times (8:00am, 12:00pm, 4:00pm and 8:00 pm). For erosion of the samples, the volunteers were instructed to remove the palatal appliance and immerse it in a cup containing 150 mL of a freshly opened bottle of regular Coke^® (pH-2.6, 32.1 mg Ca/L, 18.1 mg P/L, 0.26 ppm of F, 0.1 mL of 0.2 M NaOH to increase one unit pH in 3 mL of drink; Spal, Porto Real, RJ, Brazil). Immersion of the enamel samples was performed for 5 min at room temperature.

The volunteers received instructions to wear the appliances continuously, even at night, and remove them at meals (3 times a day, 1 h/each meal). During this period the appliance was stored in wet gauze. Oral hygiene was performed right after meals using a fluoridated dentifrice (1,500 ppm F, Sorriso^®, Brazil). Subsequently, the appliance was replaced into the mouth.

Microhardness Measurement

Five indentations were made in the center of the permanent and deciduous enamel samples each 100 µm apart from the other (Knoop diamond, 25 g, 5 s, HMV-2000; Shimadzu Corporation, Tokyo, Japan). Microhardness was assessed prior to the treatments (baseline: SMH) and after the in situ phase (final: SMH1). The percentage of surface microhardness change was calculated as follows: % SMHC= [100*(SMH1 – SMH/SMH)].

Statistical Analysis

The software GraphPad for Windows (San Diego, CA, USA) was used. The assumptions of equality of variances and normal distribution of errors were checked for all tested variables. Since the assumptions were satisfied, two-way repeated-measures ANOVA (factors dental substrate and fluoride) and Tukey's post hoc tests were carried out for statistical comparisons. For comparison between the initial surface microhardness of permanent and deciduous enamel, Student's t test was performed. The significance limit was set at 5%.

RESULTS

Table 1 shows the mean SMH and SMH1 as well as the %SMHC (±SD) of permanent and deciduous enamel. The initial surface microhardness of deciduous enamel was significantly lower than the permanent enamel (student's t test, p=0.01). With regard to the %SMHC (softening), no significant differences were found for the factors "type of dental substrate" (F=0.367, p=0.54) and "fluoride treatment" (F=0.719, p=0.40). However, a significant interaction between the two factors was found (two-way ANOVA, F=27.157, p<0.0001). Analysis by Tukey's test showed that the application of the 4% TiF₄ solution reduced the softening of permanent enamel significantly (p<0.05). In contrast, softening of deciduous enamel was significantly higher when the TiF₄ solution was applied (p<0.05).

DISCUSSION

In order to simulate the daily life situation as closely as possible, an in situ/ ex vivo model was chosen to test the effect of a TiF₄ solution on erosion of permanent and deciduous human enamel. To the best of our knowledge, this is the first study evaluating the effect of TiF₄ on erosion of deciduous teeth in situ/ ex vivo. Professionally applied highly fluoridated solutions, gels or varnishes are recommended for individuals who present moderate to severe dental erosion, with the objective to prevent new or recurrent dental erosion²⁸.

To simulate the professional application of the TiF₄ agent by a dentist, the solution was applied only once. The excess of the solution was removed before the appliance was replaced into the mouth to avoid any carry-across effect of the treatment. Measurement of the surface microhardness immediately after application of the TiF₄ solution was not performed to allow for remineralization of the enamel surface and stabilization of the titanium glaze layer. However, as the TiF₄ solution presents an acidic pH, further studies should evaluate the surface hardness change immediately after its application. Similar to previous studies, surface microhardness (%SMHC) was used as response variable since it is a suitable tool for determination of early stages of enamel dissolution².

Regarding to the dental substrates, deciduous enamel and dentin are thinner than permanent. Therefore, the erosive process reaches the dentin earlier and leads to an advanced lesion after a shorter exposure period to acids, when compared to permanent teeth¹¹. However, the analysis of the susceptibility to erosive softening of permanent and deciduous dental hard tissues revealed conflicting results^1,11-13,15. Deciduous enamel is assumed to be more susceptible than permanent enamel when the initial softening passes into a progressive mineral dissolution and surface loss. The different susceptibility to erosion of permanent and deciduous enamel might increase rather over time and/or with increasing erosive capacity of the acid¹¹. In the present study, deciduous enamel presented significant lower initial surface microhardness than permanent enamel. However, neither of the substrates differed significantly in the degree of acid softening, when only the factor "substrate" was considered in the statistical analysis.

The results of present study showed that the TiF₄ solution was able to reduce the softening of permanent enamel. The protective action of TiF₄ has been attributed not only to the action of fluoride, but also to the action of titanium^4,22. The low pH of the TiF₄ solution (around 1.2), favors the linking between titanium and oxygen of the group phosphate, leading to the formation of a titanium dioxide glaze-like layer on the surface^5,23. This glaze-like layer might be associated with a decreased softening of the enamel surface. It is speculated that the titanium ions might play an important role as they might substitute calcium in the apatite lattice^18,20. Moreover, it is suggested that titanium interacts with the enamel surface because of the low pH of the agent, thus leading to an increased fluoride uptake by enamel¹⁸.

In contrast to permanent enamel, the TiF₄ solution increased the %SMHC in deciduous enamel. One hypothesis to explain this unexpected result is that the low pH of the TiF₄ solution (1.2) could cause greater enamel loss on application²⁶ because the deciduous enamel is less mineralized and thinner than the permanent enamel. Thus, deciduous enamel might be more susceptible to alterations caused by the TiF₄ solution, which has a lower pH when compared to the most commonly consumed erosive drinks (pH 2.6). This result confirms previous findings that the erosion susceptibility of deciduous enamel increased with a higher erosivity of the acid¹¹.

CONCLUSION

The TiF₄ solution was able to reduce permanent enamel softening caused by the erosive challenge in situ. In contrast, softening of deciduous enamel was increased by the treatment compared to control. Since both substrates exhibited a relatively high surface softening after the erosive challenge, the protective capacity of TiF₄ has to be evaluated in further studies.

ACKNOWLEDGEMENTS

The authors would like to thank FAPESP - The São Paulo State Research Foundation (Grant #05/54203-3 to the first author) for the financial support.

Received: March 24, 2008

Modification: May 22, 2008

Accepted: August 30, 2008

• 1- Amaechi BT, Higham SM, Edgar WM. Factors influencing the development of dental enamel in vitro: enamel type, temperature and exposure time. J Oral Rehabil. 1999;26:624-30.
• 2- Attin T. Methods for assessment of dental erosion. Monogr Oral Sci. 2006;20:152-72.
• 3- Bartlett D. Intrinsic causes of erosion. Monogr Oral Sci. 2006;20:119-39.
• 4- Buyukyilmaz T, Ögaard B, Duschner H, Ruben J, Arends J. The caries-preventive effect of titanium tetrafluoride on root surfaces in situ as evaluated by microradiography and confocal laser scanning microscopy. Adv Dent Res. 1997;11:448-52.
• 5- Buyukyilmaz T, Ogaard B, Rolla G. The resistance of titanium tetrafluoride-treated human enamel to strong hydrochloric acid. Eur J Oral Sci. 1997;105:473-7.
• 6- Dawes C. Physiological factors affecting salivary flow rate, oral sugar clearance, and the sensation of dry mouth in man. J Dent Res. 1987;66:648-53.
• 7- Ganss C, Klimek J, Brune V, Schurmann A. Effects of two fluoridation measures on erosion progression in human enamel and dentine in situ. Caries Res. 2004;38:561-6.
• 8- Hara AT, Ando M, Gonzalez-Cabezas C, Cury JA, Serra MC, Zero DT. Protective effect of the dental pellicle against erosive challenges in situ. J Dent Res. 2006;85:612-6.
• 9- Hove L, Holme B, Øgaard B, Willumsen T, Tveit AB. The protective effect of TiF₄, SnF₂ and NaF on erosion of enamel by hydrochloric acid in vitro measured by white light interferometry. Caries Res. 2006;40:440-3.
• 10- Hove LH, Young A, Tveit AB. An in vitro study on the effect of TiF₄ treatment against erosion by hydrochloric acid on pellicle-covered enamel. Caries Res. 2007;41:80-4.
• 11- Hunter ML, West NX, Hughes JA, Newcombe RG, Addy M. Erosion of deciduous and permanent dental hard tissue in the oral enviromment. J Dent. 2000;28:257-63.
• 12- Johansson AK, Sorvari R, Birkhed D, Meurman JH. Dental erosion in deciduous teeth an in vivo and in vitro study. J Dent. 2001;29:333-40.
• 13- Lippert F, Parker DM, Jandt KD. Susceptibility of deciduous and permanent enamel to dietary acid-induced erosion studied with atomic force microscopy nanoindentation. Eur J Oral Sci. 2004;112:61-6.
• 14- Lussi A, Jaeggi T, Zero D. The role of diet in the aetiology of dental erosion. Caries Res. 2004;38:34-44.
• 15- Lussi A, Kohler N, Zero D, Schaffner M, Megert B. A comparison of the erosive potential of different beverages in primary and permanent teeth using an in vitro model. Eur J Oral Sci. 2000;108:110-4.
• 16- Lussi A. Erosive tooth wear - a multifactorial condition of growing concern and increasing knowledge. Monogr Oral Sci. 2006;20:1-8.
• 17- Magalhães AC, Rios D, Honório HM, Jorge AM Jr, Delbem ACB, Buzalaf MAR. Effect of 4% titanium tetrafluoride solution on dental erosion by a soft drink: an in situ/ex vivo study. Arch Oral Biol. 2008;53:399-404.
• 18- Mundorff SA, Little MF, Bibby BG. Enamel dissolution. 2. Action of titanium tetrafluoride. J Dent Res. 1972;51:1567-71.
• 19- Peterson G, Bratthall D. The caries decline: a review of reviews. Eur J Oral Sci. 1996;104:436-43.
• 20- Ribeiro CC, Gibson I, Barbosa MA. The uptake of titanium ions by hydroxiapatite particles - structural changes and possible mechanisms. Biomaterials. 2006;27:1749-61.
• 21- Schlueter N, Ganss C, Mueller U, Klimek J. Effect of titanium tetrafluoride and sodium fluoride on erosion progression in enamel and dentine in vitro. Caries Res. 2007;41:141-5.
• 22- Tezel H, Ergucu Z, Onal B. Effects of topical fluoride agents on artificial enamel lesion formation in vitro. Quintessence Int. 2002;33:347-52.
• 23- Tveit AB, Hals E, Isrenn R, Totdal B. Highly acid SnF₂ and TiF₄ solution. Caries Res. 1983;17:412-8.
• 24- van Rijkom H, Ruben J, Vieira A, Huysmans MC, Truin GJ, Mulder J. Erosion-inhibiting effect of sodium fluoride and titanium tetrafluoride treatment in vitro Eur J Oral Sci. 2003;111:253-7.
• 25- Vieira A, Lugtenborg M, Ruben JL, Huysmans MC. Brushing abrasion of eroded bovine enamel pretreated with topical fluorides. Caries Res. 2006;40:224-30.
• 26- Vieira A, Ruben JL, Huysmans MC. Effect of titanium tetrafluoride, amine fluoride and fluoride varnish on enamel erosion in vitro. Caries Res. 2005;39:371-9.
• 27- White DJ. Reactivity of fluoride dentifrices with artificial caries 1. Effects on early lesions: F uptake, surface hardening and remineralisation. Caries Res. 1987;21:126-40.
• 28- Wiegand A, Attin T. Influence of fluoride on the prevention of erosive lesions a review. Oral Health Prev Dent. 2003;1:245-53.

Publication Dates

• Publication in this collection
  12 Jan 2009
• Date of issue
  Feb 2009

History

• Accepted
  30 Aug 2008
• Reviewed
  22 May 2008
• Received
  24 Mar 2008