Adhesive systems: important aspects related to their composition and clinical use

Abstract

This literature review article addresses the types and the main components of different etch-and-rinse and self-etch adhesive systems available in the market, and relates them to their function, possible chemical interactions and infuence of handling characteristics. Scanning electron microscopy (SEM) images are presented to characterize the interface between adhesives and dentin. Adhesive systems have been recently classifed according to their adhesion approaches in etch-and-rinse, self-etch and glass ionomer. The etch-and-rinse systems require a specifc acid-etch procedure and may be performed in two or three steps. Self-etch systems employ acidic monomers that demineralize and impregnate dental substrates almost at the same time. These systems are separated in one or two steps. Some advantages and defciencies were noted for etch-and-rinse and self-etch approaches, mainly for the simplifed ones due to some chemical associations and interactions. The SEM micrographs illustrate different relationships between adhesive systems and dental structures, particularly dentin. The knowledge of composition, characteristics and mechanisms of adhesion of each adhesive system is of fundamental importance to permit the adoption of ideal bonding strategies under clinical conditions.

Dentin-bonding agents; Dentin; Dental adhesives; Chemical composition


REVIEW

Adhesive systems: important aspects related to their composition and clinical use

Mario Honorato Silva e Souza JuniorI; Karina Gama Kato CarneiroII; Marcelo Figueiredo LobatoII; Patrícia de Almeida Rodrigues Silva e SouzaIII; Mário Fernando de GóesIV

IDDS, MSc, PhD Associate Professor, Department of Restorative Dentistry, Dental School, Federal University of Pará, Belém, PA, Brazil

IIDDS, Graduate student, Dental School, Federal University of Pará, Belém, PA, Brazil

IIIDDS, MSc, PhD Associate Professor, Department of Endodontics, Dental School, Federal University of Pará, Belém, PA, Brazil

IVDDS, MSc, PhD Associate Professor, Department of Restorative Dentistry, Piracicaba Dental School, State University of Campinas, Piracicaba, SP, Brazil

Corresponding address Corresponding address: Mario Honorato Silva e Souza Jr. Travessa D. Romualdo de Seixas, 156 - apt. 501 66050-110 - Belém, PA - Brasil Phone: +55 91 3229 8979 e-mail: mario-honorato@hotmail.com / honorato@ufpa.br

ABSTRACT

This literature review article addresses the types and the main components of different etch-and-rinse and self-etch adhesive systems available in the market, and relates them to their function, possible chemical interactions and infuence of handling characteristics. Scanning electron microscopy (SEM) images are presented to characterize the interface between adhesives and dentin. Adhesive systems have been recently classifed according to their adhesion approaches in etch-and-rinse, self-etch and glass ionomer. The etch-and-rinse systems require a specifc acid-etch procedure and may be performed in two or three steps. Self-etch systems employ acidic monomers that demineralize and impregnate dental substrates almost at the same time. These systems are separated in one or two steps. Some advantages and defciencies were noted for etch-and-rinse and self-etch approaches, mainly for the simplifed ones due to some chemical associations and interactions. The SEM micrographs illustrate different relationships between adhesive systems and dental structures, particularly dentin. The knowledge of composition, characteristics and mechanisms of adhesion of each adhesive system is of fundamental importance to permit the adoption of ideal bonding strategies under clinical conditions.

Key words: Dentin-bonding agents. Dentin. Dental adhesives. Chemical composition.

INTRODUCTION

Throughout the last decades adhesive systems have received different classifcations, generally based on modifcations in their compositions. These practices led to several complex and confusing classifcations that have brought some diffculties to clinicians for selection and use of dental adhesives. Van Meerbeek, et al.39 (2003) proposed a simple classifcation based on the interaction of adhesives with dental substrates and number of steps: etch-and-rinse (two-and three-step adhesives), self-etch (one- and two-step adhesives) and glass ionomer. All of them have received important modifcations in the last years. These modifcations were made based on the increasing of knowledge of their compositions and adhesion mechanisms.

Indeed, the best understanding of the role of dental substrates in the adhesion process has helped researchers and manufacturers developing and improving dental adhesion.

This literature review article addresses the types and the main components of different etch-and-rinse and self-etch adhesive systems available in the market, and relates them to their function, possible chemical interactions and infuence of handling characteristics.

Etch-and-rinse ADHESIVE systems

Etch-and-rinse adhesive systems can be either three-or two-step materials depending on whether primer and bonding are separated or combined in a single bottle. The adhesion strategy involves at least two steps and, in its most conventional form, three steps with successive application of the conditioner (acid etchant), followed by the primer (adhesion promoting agent), and eventually, application of the bonding agent (adhesive resin). The simplifed two-step version combines the second (priming) and third (bonding) steps, but still follows a separated etch and rinse phase2,9,39. Figure 1 describes the sequence of procedures of etch-and-rinse systems.


Acid Conditioning

Acid-etching of enamel is a widely accepted clinical procedure due to its chemical structure and has increased the life of composite resin restorations by decreasing the possibility of marginal staining, secondary caries and post-operative sensitivity19. The effects of conditioning procedure may vary widely, depending on several factors, such as type (sound or sclerotic), depth and tubule orientation7,20,41. Some aspects of the conditioned/primed area however are the same. The tubule access becomes funnel shaped and the resin tags are normally elongated. These aspects can be seen in Figures 2A and 2B. Ideally, acid etching with 35% H3PO4 should not exceed 15 s. Prolonged acid application may lead to structural modifcation of the exposed collagen 3.


Monomers

In the two-step systems the hydrophilic and hydrophobic monomers are combined with solvent(s) in the same bottle. These associations may cause some chemical disorder during clinical application. The presence of unprotected dentin collagen fibers may be explained by the presence of residual water that may prevent complete monomer infiltration in the deep demineralized zone, which compromises ideal adhesive infiltration and polymerization16,27. These factors could be responsible for the degradation of resin-dentin interfaces over short periods of time. The instability of bonds over longer time periods has been attributed to the degradation of both exposed collagen and resin monomers10,16.

HEMA (2-hydroxymethyl methacrylate) is a very popular monomer which is in widespread use17 . It is much employed either in three-and two-step etch-and-rinse systems and one reason for this preference is related to its hydrophilicity that makes it an excellent adhesion promoter enhancing bond strength11,36,39. On the other hand, the hydrophilic characteristic may, in uncured and cured states, readily absorb water36 . In the uncured state the absorption of water may lead to dilution of the monomer to the extent that polymerization is inhibited15 , compromising the initial bond strength, which may cause adhesion breakdown (Figure 3). This aspect must be especially considered during clinical procedure when HEMA-rich adhesives have their polymerization delayed. After polymerization HEMA will still exhibit hydrophilic properties. Considering its permeable structure, water treeing will be prone to occur29,32. The presence of water within hybrid layer may cause hydrolysis, a chemical process that breaks covalent bonds between polymers by addition of water on ester bonds, resulting in resin degradation compromising bond strength in latter periods of time30 . Since simplifed (two-step) etch and rinse adhesives contain higher percentages of hydrophilic monomers compared to three-step adhesive28, they exhibit greater permeability after polymerization, thus facilitating the presence of water-filled areas within hybrid layer29. Recently, it can be noted the trend towards decreasing the amount of strong hydrophilic monomers, such as HEMA, and replacing this portion by UDMA or TEGDMA36.


The hydrophobic coat of the three-step etch-and-rinse system may in part overcome the water movement throughout the bonded interface. In areas of hybrid layer defects the passage of fuids speeds up during biting and temperature shifts7. This passage may occur in different directions, from and towards the pulp, and from and towards the oral environment. Thus, it would be feasible, in a presence of a hydrophobic coat, a reduction of this movement, preserving adhesive interface from hydrolysis and also decreasing sensitivity7. Besides its hydrophobic nature, the higher degree of polymerization of the nonsolvated hydrophobic agents was correlated to less permeability to water5. Some newer adhesive systems, such as All Bond 3 (Bisco Inc., Schaumburg, IL, USA), renamed this hydrophobic sealer as liner (Figure 4).


Solvents

A very important component of the adhesive systems is the solvent. The low viscosity of primers and primer-adhesive resins is partially due to the dissolution of monomers in a solvent. This association will improve the diffusion ability in the porous conditioned substrate, especially in dentin due to its hydrophilic nature. In adhesives, water, ethanol and acetone are the most commonly used solvents.

As mentioned above, solvents are important to assure the diffusion of monomers into the demineralized dentin. After diffusion the solvents must be eliminated from adhesive, otherwise remaining solvent in the adhesive may jeopardize polymerization due to the dilution of monomers and may result in voids and increase the permeability of the adhesive layer12,15. Effect of evaporation of the primer components is important to ultimate tensile strength of primer-adhesive mixture. Complete evaporation is however diffcult to achieve because it is limited to the short clinical time12. The evaporation of the solvent is related to its vapor pressure. Higher vapor pressure of the solvent implies faster evaporation21 . While the solvent evaporates, the solvent-monomer ratio decreases, as well as the vapor pressure. Thus, within the clinical time, residual solvent may remain in the adhesive and the consequences are directly related to its amount7.

The application technique is different depending on the solvent. Water is a poor solvent for organic compounds (such as monomers). This diffculty can be overcome by addition of a secondary solvent, such as ethanol and acetone (azeotrope)36. As the vapor pressure is lower, water-based adhesive, takes longer to evaporate. Therefore, it will need more clinical time to help the monomer diffusion. A rubbing application technique is also cooperative to assure both monomer diffusion and solvent evaporation as well7. As this type of adhesive already contains water, the amount of water in the substrate must not be excessive. The dental substrate, especially dentin, must be moist, but with no visible shine7 on the surface (Figure 5). One advantage of these agents is their capacity of expanding collagen, in case of substrate overdrying (excessive air blowing)21. Normally one coat of a cover the entire surface. Extra coats may have a thickening effect and result in the imprisonment of solvent between layers (Figure 6). This may lead to lower bond strength values36.



On the other hand, with acetone-based adhesives (without water), as the vapor pressures of these solvents are much higher, the primer or primer-adhesive must be left undisturbed on the surface and the substrate must be moist with a shiny appearance7 (Figure 7). These systems will not be able to re-expand the collapsed collagen, on an over dried dentin surface, thus avoiding correct monomer diffusion. Figure 8 depicts an adhesive interface prepared with the XP Bond (Dentsply, De Trey, Konstanz, Germany), which employs the T-butanol solvent. The thickness of the adhesive coat is very thin compared to those obtained with All Bond 3 (Bisco Inc., Schaumburg, IL, USA) (Figure 4) and Single Bond (3M/ESPE, St. Paul, MN, USA) (Figure 7), which uses a water-ethanol mixture.



SELF-ETCH ADHESIVE SYSTEMS

The self-etch approach is an alternative based on the use of non-rinse acidic monomers that simultaneously condition and prime tooth tissues. Regarding technique-sensitivity, this approach seems clinically most promising, since it eliminates the rinsing phase, which not only reduces clinical application time, but signifcantly decreases the technique sensitivity or the possibility of making errors during application1,2, 8,39. Another important characteristic of the self-etch approach is that infiltration of monomers occurs simultaneously with the self-etch process; therefore, the possibility of discrepancies between both processes39 and consequently the presence of an unprotected collagen fibers area is signifcantly reduced, as is the nanoleakage2,9,29. Figure 9 depicts some characteristics and the adhesion strategies of self-etch systems.


Aggressiveness of self-etch systems

Some questions however arise from this particular approach: 1-Could the presence of dissolved hydroxyapatite and residual smear layer remnants interfere in the bond? 2- Are the self-etch systems able to properly demineralize enamel or sclerotic dentin? The self-etch systems were gradually modified in the last few years and one important change was the increase in their aggressiveness35 . Depending on etching aggressiveness, self-etch adhesives can be subdivided into strong (pH<1), intermediary strong (pH≈1.5) and mild (pH≈2.0)35,36,39. Strong self-etch adhesives present higher acidity compared with mild and intermediary strong systems and the interaction patterns observed in enamel and dentin resembles a phosphoric acid treatment after etch and rinse approach22. Figure 10 depicts resin tags formation after the use of Adper Prompt L-Pop (3M/ESPE, St. Paul, MN, USA), pH-0.8. The tubules are wide open, the resin tags have a funnel shape and are elongated. On the other hand, dentin treated with a mild self-etch system (All Bond SE; Bisco Inc., Schaumburg, IL, USA), pH 2.2, exhibits cylindrical and short tags (Figure 11). Despite the similar etching pattern with the etch and rinse systems, the bond strength observed for the strong self-etch adhesives was lower, especially at dentin38,39. The presence of water in the composition of self-etch systems is necessary to trigger the demineralization process. The excess of residual water during polymerization may be one of the reasons for the poor bond strength7,9,18,39. Indeed, adhesive systems that contain high concentrations of acidic resin monomers behave like permeable membranes29 and allow water movement from dentin to the composite-adhesive interface31. This may further compromise the durability of resin-dentine bonds and affect the coupling of the simplifed adhesives to auto-cured (or dual-cured) composites7,30. These two aspects; low initial bond strength and gradual degradation, due to hydrolysis, have made researchers and manufacturers rethink about monomers, pH and association of components in the bottles. Some newer self-etch adhesives present higher pH, such as Xeno IV (Dentsply Caulk, Milford, DE, USA), pH-2.1 and All Bond SE (Bisco Inc., Schaumburg, IL, USA), pH 2.2. Others, such as Adper SE Plus (3M/ESPE, St. Paul, MN, USA) present a very low pH (<1), their components are strategically distributed in the bottles. Liquid A formed of water, HEMA and a pink dye is first applied onto the cavity (Figure 12). The water will only meet the monomers in a second step, when liquid B is transferred to the cavity (Figure 13). A continuous brushing procedure is advised to force the contact of all components and help the evaporation of excess water. The pink appearance starts fading immediately and a light yellowish look takes place (Figure 14). Conversely, the Adper Easy One Bond (3M/ESPE, St. Paul, MN, USA) has all the components associated in the same bottle, including water. However, the pH of the mixture is much higher (2.3) than the pH of Adper SE Plus (3M/ESPE, St. Paul, MN, USA). These differences imply in distinct application techniques and storage. While Easy One Bond must be kept under refrigeration, Adper Scotchbond SE (3M/ESPE, St. Paul, MN, USA) can be maintained at room temperature.






Monomers

One signifcant advantage of a mild self-etch system is to keep some hydroxyapatite crystal around collagen fibers39 . This characteristic may protect the collagen against hydrolysis and, thus, early degradation of the bond25 . The adaptation of etch-and-rinse adhesives to denuded collagen fibrils has been considered poor39 , and hence a possibility of chemical interaction between residual hydroxyapatite and functional monomers is expected to improve bonding. Researchers have pointed out that some functional monomers in self-etch adhesives, such as 10-MDP present in the Clearfil Liner Bond 2 and SE Bond (Kuraray Medical Inc., Tokyo, Japan), 4-MET as part of the Unifil Bond and G-Bond (GC, Tokyo, Japan) and phenyl-P found in the Clearfil Liner Bond 2 (Kuraray Medical Inc., Tokyo, Japan), can chemically interact with hydroxyapatite within a clinical time, and this interaction has been connected to better resistance towards degradation by prevention of micro and nanoleakage39,42. The strong one-step self-etch adhesive Prompt-L-Pop (3M/ESPE, St. Paul, MN, USA), performed very poorly, with a retention rate of 65% after one year2. On the other hand, mild two-step self-etch adhesive Clearfil SE Bond (Kuraray Medical Inc, Tokyo, Japan), which contain the 10-MDP, exhibited excellent result for up to two years33.

Recently, Ikeda et al.13 (2008), evaluated the effect of air-drying on the ultimate microtensile bond strength of HEMA-rich and HEMA-free one-step adhesives. It could be shown that the evaporation degree of residual monomers and solvents increased with the extension of air-drying. Longer air-drying time (10 sec.) resulted in a statistically signifcant higher microtensile bond strength for the HEMA-rich (Clearfil S Bondi Kuraray Medical Inc, Tokyo, Japan) compared to the HEMA-free (I Bond/Hereaus-Kulzer, Hanau, Germany and G-Bond/ GC, Tokyo, Japan). HEMA has been used as adhesion promoter in most of the self-etch systems due to some of its characteristics already mentioned11,36, however, high concentrations in the adhesive composition, normally present in the one-step self-etch adhesives may have immediate (lower bond strength) and posterior (hydrolysis) deteriorating effects on the mechanical properties of the resulting polymer13,15,29,32,36.

The effects of the amount of HEMA on initial bond strength and deteriorating effects of hydrolysis are somehow correlated. Higher concentration of HEMA (19-36%)38 in the composition of one-step self-etch adhesives may reduce initial bond strength (particularly 36%) due to the attraction of water and the presence of droplets on dentin, especially after delay-curing the composite. This water may contribute also to monomers dilution and reduction on polymerization degree15,36,38. Higher bond strengths were determined at 10% of HEMA in the composition of some experimental adhesives formulations38.

A possibility to prevent hydrolysis of hydrophilic monomers, such as HEMA, present in high concentrations in some simplifed self-etch systems, is to coat the primed dentin with additional layer of hydrophobic agent onto the polymerized one-step adhesive agent, converting them in a two-step system4,7,16,26.

In the last few years, some researchers have proposed the use of monomers with different hydrophilic levels on dentin. Nishitani, et al.18 (2006), examined the microtensile bond strength of five experimental adhesives (50wt%ethanol/50%comonomers) of various degree of hydrophilicity to acid etch dentin that was left moist with water or ethanol, or air-dried. Following the composite resin application, specimens were prepared for microtensile test. For all three types of dentin treatments, higher bond strengths were achieved with increased resin hydrophilicity. The lowest bond strengths were obtained on air-dried dentin, while the highest ones were achieved when dentin was bonded moist with ethanol. Wet-bonding with ethanol achieved higher bond strengths with hydrophobic resins than were possible with water-saturated dentin. These observations open possibilities to use less hydrophilic monomers on dentin bonding with the purpose of reduce the deterioration potential of some adhesives by hydrolysis18.

Solvents

As mentioned before, water is an indispensable component of self-etch agents, in order to ionize the acidic monomers and trigger the demineralization process7,22,36,39. The strong self-etch agents are likely to contain higher amounts of water. A concern is the effect of residual water that remains within the adhesive interface, which hardly can be completely removed39 . Some self-etch agents present only water as solvent, such as Adper SE Plus (3M/ESPE, St. Paul, MN, USA), AdheSE (Ivoclar Vivadent, Schaan, Liechtenstein), Adper Prompt (3M/ESPE, St. Paul, MN, USA). However, in many systems, the water is associated to ethanol, acetone or even to monomers, such as the N,N-diethanol p-toluidine, present in the Clearfil SE Bond (Kuraray Medical Inc., Tokyo, Japan) adhesive. Special attention should be directed to water-based agents, mainly the all-in-one agents. A multiple layer application under a continuous brushing technique has also been claimed to increase the bond strength of these materials14,23. On the other hand, as water has been related to phase-separation, polymerization-inhibition and reduced shelf-life, the development of self-etch water-free adhesive has been already proposed37. The water necessary to trigger the acidic reactions would come from the dental substrate.

Another simple approach to improve bonding effcacy and stability is correlated with enhanced solvent evaporation. The air-blowing of the adhesive might help to remove interfacial water, thus improving bonding effectiveness13,34. However, this procedure is somehow controversial40 because it has been stated that a strong air stream may increase the adhesive thickness in the cavity angles and denude part of dentin. It is an important issue related to cavity geometry, normally different from the fat dental surface used for bond strength tests. A mild and extended air-blow should, however, be cooperative to the evaporation of solvent and residual monomers.

FINAL CONSIDERATIONS

The research field of dental adhesion is wide open. Several research lines have been proposed and investigated in the last years. The use of an extended polymerization time5, the application of electrical current to dental adhesives4,24, the relevance of matrix metalloproteinase inhibitors6, the development of water-free adhesives37, and the use of hydrophobic monomers in conditioned dentin treated with ethanol solutions18, for instance, are some of the innumerous possibilities under investigations. Also, the balance among some essential components such as monomers and solvents has been studied38. As it could be noted by the issues discussed in this literature review, keeping an updated knowledge of the composition, characteristics and mechanisms of adhesion of the currently available adhesive systems as well as knowing how the dental substrates interact with these materials are essential to achieve the best results in adhesion.

ACKNOWLEDGMENTS

We would like to thank Mr. Adriano Luiz Martins and Alberto Antunes (FOP-UNICAMP) for the technical support in scanning electron microscopy.

Received: January 19, 2009

Modifcation: July 31, 2009

Accepted: January 05, 2010

  • 1- Brackett WW, Covey DA, St Germain HA Jr. One-year clinical performance of a self-etching adhesive in class V resin composites cured by two methods. Oper Dent. 2002;27(7):218-22.
  • 2- Breschi L, Mazzoni A, Ruggeri A, Cadenaro M, Di Lenarda R, Dorigo ES. Dental adhesion review: aging and stability of the bonded interface. Dent Mater. 2008;24(1):90-101.
  • 3- Breschi L, Perdigão J, Gobbi P, Mazzotti G, Falconi M, Lopes M. Immunocytochemical identifcation of type I collagen in acid-etched dentin. J Biomed Mater Res A. 2003;66(11):764-9.
  • 4- Breschi L, Mazzoni A, Pashley DH, Pasquantonio P, Ruggeri A Jr, Suppa P, et al. Eletric current-assisted application of self-etch adhesives to dentin. J Dent Res. 2006;85(12):1092-6.
  • 5- Cadenaro M, Antoniolli F, Sauro S, Tay FR, Di Lenarda R, Prati C, et al. Degree of conversion and permeability of dental adhesives. Eur J Oral Sci. 2005;113(6):525-30.
  • 6- Carrilho MR, Carvalho RM, Goes MF, di Hipólito V, Geraldeli S, Tay FR, et al. Chlorhexidine preserves dentin bond in vitro J Dent Res. 2007;86(1):90-4.
  • 7- Carvalho RM, Carrilho MRO, Pereira LCG, Marquezini L Jr, Silva SMA, Kussmaul APM. Sistemas adesivos: fundamentos para aplicação clínica. Revista Biodonto. 2004;2(1):6-86.
  • 8- Chaves CAL, Melo RM, Passos SP, Camargo FP, Bottino MA, Balducci I. Bond strength durability of self-etching adhesives and resin cements to dentin. J Appl Oral Sci. 2009;17(3):155-60.
  • 9- De Munck J, Van Landuyt K, Peumans M, Poitevin A, Lambrechts P, Braem M, et al. A critical review of the durability adhesion to tooth tissue: methods and results. J Dent Res. 2005;84(2):118-32.
  • 10- Hebling J, Pashley DH, Tjäderhane L, Tay FR. Chlorhexidine arrests subclinical degradation of dentin hybrid layers in vivo J Dent Res. 2005;84(8):741-6.
  • 11- Hitmi L, Bouter D, Degrange M. Infuence of drying and HEMA treatment on dentin wettability. Dent Mater. 2002;18(7):503-11.
  • 12- Ikeda T, De Munck J, Shirai K, Hikita K, Inoue S, Sano H, et al. Effect of evaporation of primer components on ultimate tensile strength of primer-adhesive mixture. Dent Mater. 2005;21(11):1051-8.
  • 13- Ikeda T, De Munk J, Shirai K, Hikita K, Inoue S, Sano H, et al. Effect of air-drying and solvent evaporation on the strength of HEMA-rich versus HEMA-free one-step adhesives. Dent Mater. 2008;24(10):1316-23.
  • 14- Ito S, Tay FR, Hashimoto M, Yoshiama M, Saito T, Brackett WW, et al. Effects of multiple coatings of two all-in-one adhesives on dentin bonding. J Adhes Dent. 2005;7(2):133-41.
  • 15- Jacobsen T, Söderholm KJ. Some effects of water on dentin bonding. Dent Mater. 1995;11(2):132-6.
  • 16- Manso AP, Marquezini L Jr, Silva SM, Pashley DH, Tay FR, Carvalho RM. Stability of wet versus dry bonding with different solvent-based adhesives. Dent Mater. 2008;24(4):476-82.
  • 17- Nakabayashi N, Saimi Y. Bonding to intact dentin. J Dent Res. 1996;75(9):1706-15.
  • 18- Nishitani Y, Yoshiama M, Donnely AM, Agee KA, Sword J, Tay FR, et al. Effects of resin hydrophilicity on dentin bond strength. J Dent Res. 2006;85(11):1016-21.
  • 19- O'Brien WJ. Dental Materials and their selection. Quintessence Books. 2nd ed. Chicago; 1998.
  • 20- Ogata M, Okuda M, Nakajima M, Pereira PN, Sano H, Tagomi J, et al. Infuence of the direction of tubules on bond strength to dentin. Oper Dent. 2001;26(1):27-35.
  • 21- Pashley EL, Zang Y, Lokwood PE, Rueggeberg FA, Pashley, DH. Effects of HEMA on water evaporation from water-HEMA mixtures. Dent Mater. 1998;14:6-10.
  • 22- Pashley DH, Tay FR. Aggressiveness of contemporary selfetching adhesives. Part II: etching effects on unground enamel. Dent Mater. 2001;17(5):430-44.
  • 23- Pashley EL, Agee KA, Pashley DH, Tay FR. Effects of one versus two application of an unfilled, all-in-one adhesive on dentine bonding. J Dent. 2002;30(2-3):83-90.
  • 24- Pasquantonio G, Tay FR, Mazzoni A, Suppa P, Ruggeri A Jr, Falconi M, et al. Eletric device improves bonds of simplifed etch-and-rinse adhesives. Dent Mater. 2007;23(4):513-8.
  • 25- Sano H, Yoshikawa T, Pereira PN, Kanemura N, Morigami M, Tagami J, et al. Long-term durability of dentin bonds made with a self-etching primer, in vivo J Dent Res. 1999;78(4):906-11.
  • 26- Andrade e Silva SM, Carrilho MR, Marquezini L Jr, Garcia FC, Manso AP, Alves MC, et al. Effect of an additional hydrophilic versus hydrophobic coat on the quality of dentinal sealing provided by two-step etch-and-rinse adhesives. J Appl Oral Sci. 2009;17(3):184-9.
  • 27- Tay FR, Gwinnett JA, Wei SH. Micromorphological spectrum from overdrying to overwetting acid-conditioned dentin in water-free acetone-based, single-bottle primer/adhesives. Dent Mater. 1996;12(4):236-44.
  • 28- Tay FR, Pashley DH. Dental adhesives of the future. J Adhes Dent. 2002;4(2):91-103.
  • 29- Tay FR, Pashley DH, Suh BI, Carvalho RM, Itthagarun A. Singlestep adhesives are permeable membranes. J Dent. 2002;30(7-8):371-82.
  • 30- Tay FR, Pashley DH. Have dentin adhesives become too hydrophilic? J Can Dent Assoc. 2003;69(11):726-31.
  • 31- Tay FR, Pashley DH. Water treeing - a potential mechanism for degradation of dentin adhesives. Am J Dent. 2003;16(1):6-12.
  • 32- Tay FR, Pashley DH, Suh BI, Hiraishi N, Yiu CK. Water treeing in simplifed dentin adhesives-deja vu? Oper Dent. 2005;30(5):561-79.
  • 33- Türkün SL. Clinical evaluation of a self-etching and a one-bottle adhesive system at two years. J Dent. 2003;31(8):527-34.
  • 34- Van Landuyt KL, De Munck J, Snauwaert J, Coutinho E, Poitevin A, Yoshida Y, et al. Monomer -solvent phase separation in one-step self-etch adhesives. J Dent Res. 2005;84(2):183-8.
  • 35- Van Landuyt KL, Kanumilli P, De Munck J, Peumans M, Lambrechts P, Van Meerbeek B. Bond strength of a mild self-etch adhesive with and without prior acid-etching. J Dent. 2006;34(1):77-85.
  • 36- Van Landuyt KL, Snauwaert J, De Munck J, Peumans M, Yoshida Y, Poitevin A, et al. Systematic review of the chemical composition of contemporary dental adhesives. Biomaterials. 2007;28(26):3757-85.
  • 37- Van Landuyt KL, Mine A, De Munck J, Coutinho E, Peumans M, Jacques S, et al. Technique sensitivity of water-free one-step adhesives. Dent Mater. 2008;24(9):1258-67.
  • 38- Van Landuyt KL, Snauwaert J, Peumans M, De Munck J, Lambrechts P, Van Meerbeek B. The role of HEMA in one step self-etch adhesives. Dent Mater 2008;24(10):1412-9.
  • 39- Van Meerbeeck B, De Munck J, Yoshida Y, Inoue S, Vargas M, Vijay P, et al. Buonocore memorial lecture. Adhesion to enamel and dentin: current status and future challenges. Oper Dent. 2003;28(3):215-35.
  • 40- Walshaw PR, McComb D. Clinical considerations for optimal dentinal bonding. Quintessence Int. 1996;27(9):619-25.
  • 41- Yoshikawa T, Sano H, Burrow MF, Tagami J, Pashley DH, et al. Effects of dentin depth and cavity configuration on bond strength. J Dent Res. 1999;78(4):898-905.
  • 42- Yoshida Y, Nagakane K, Fukuda R, Nagayama Y, Okazaki M, Shintani H, et al. Comparative study on adhesive performance of functional monomers. J Dent Res. 2004;83(6):454-8.
  • Corresponding address:

    Mario Honorato Silva e Souza Jr.
    Travessa D. Romualdo de Seixas, 156 - apt. 501
    66050-110 - Belém, PA - Brasil
    Phone: +55 91 3229 8979
    e-mail:
  • Publication Dates

    • Publication in this collection
      31 Aug 2010
    • Date of issue
      June 2010

    History

    • Reviewed
      31 July 2009
    • Received
      19 Jan 2009
    • Accepted
      05 Jan 2010
    Faculdade De Odontologia De Bauru - USP Serviço de Biblioteca e Documentação FOB-USP, Al. Dr. Octávio Pinheiro Brisolla 9-75, 17012-901 Bauru SP Brasil, Tel.: +55 14 32358373 - Bauru - SP - Brazil
    E-mail: jaos@usp.br