Influence of the type of recycled aggregate from construction and demolition waste on the module of deformation of recycled aggregate concrete

Cabral, A. E. B.; Schalch, V.; Dal molin, D. C. C.; Ribeiro, J. L. D.

doi:10.1590/S1983-41952008000200004

Abstracts

To contribute to the recycled aggregate concrete study, an experimental test was made by substituting the natural aggregates for recycled aggregates of concrete, of mortar and of red ceramic, which are the three main ingredients of Brazilian construction and demolition waste. Besides the aggregate types, the water/cement ratio (w/c) was also changed from 0.4 to 0.8, fixing the amount of pre soaking water of the recycled aggregates. The concrete's module of deformation was determined at 28-days age, using the Brazilian Standard ABNT NBR 8522/03, in cylindrical specimens. The results show that substituting the natural aggregates for the recycled aggregates reduces the module of deformation, and that the coarse red ceramic recycled aggregate and the fine concrete recycled aggregate were the ones that exerted the greatest and the smallest influence, respectively, on the concrete's module of deformation.

recycling; construction and demolition waste; concrete; module of deformation

Com o intuito de contribuir no estudo de concretos produzidos com agregados reciclados, produziu-se um traço de referência (com agregados naturais) e outros 49 traços, substituindo-se os agregados naturais por agregados reciclados de concreto, de argamassa e de cerâmica vermelha, que são os 3 maiores constituintes dos resíduos de construção e demolição das cidades brasileiras. Além do tipo de agregado, também variou-se a relação água/cimento (a/c), entre os valores de 0,4 a 0,8, fixando-se o teor de água na pré-umidificação dos agregados reciclados. O módulo de deformação dos concretos foram determinados aos 28 dias, utilizando-se a norma brasileira ABNT NBR 8522/03, em corpos-de-prova cilíndricos. Os resultados apontam que a substituição do agregado natural pelo reciclado resulta em uma redução do módulo de deformação, sendo que o agregado graúdo de cerâmica vermelha e o agregado miúdo reciclado de concreto foram os que exerceram a maior e a menor influência, respectivamente, sobre o módulo de deformação dos concretos produzidos.

reciclagem; resíduo de construção e demolição; concreto; módulo de deformação

Influence of the type of recycled aggregate from construction and demolition waste on the module of deformation of recycled aggregate concrete

A. E. B. Cabral ^I ; V. Schalch ^I ^I ; D. C. C. Dal molin ^I ^I ^I ; J. L. D. Ribeiro ^I ^V

^IProfessor Doctor, Federal Center of Technological Education of Ceará (CEFET/CE), Solid Wastes Research Center (CPRS), Civil Construction Department, eduardo@cefetce.br Av. 13 de maio, 2081 - Benfica - 60.040-531- Fortaleza/CE - Brazil

^I^IProfessor Doctor, Pos-Graduation Program in Environmental Engineering Science (PPG-SEA) in Engineering School of São Carlos at Universidade of São Paulo (EESC/USP), vschalch@sc.usp.br Av. Trabalhador Sancarlense, 400 - 13.560-970 - São Carlos/SP -Brasil

^IIIProfessor Doctor, Pos-Graduation Program in Civil Engineering (PPGEC) at Federal University of Rio Grande do Sul (NORIE/UFRGS), dmolin@ufrgs.br Av. Osvaldo Aranha, 99, 3º andar - 90.035-190 - Porto Alegre/RS - Brasil

^IVProfessor Doctor, Pos-Graduation Program in Production Engineering (PPGEP) at Federal University of Rio Grande do Sul (LOPP/UFRGS), ribeiro@producao.ufrgs.br Praça Argentina, 9 - 90.040-020 - Porto Alegre/RS - Brasil

ABSTRACT

To contribute to the recycled aggregate concrete study, an experimental test was made by substituting the natural aggregates for recycled aggregates of concrete, of mortar and of red ceramic, which are the three main ingredients of Brazilian construction and demolition waste. Besides the aggregate types, the water/cement ratio (w/c) was also changed from 0.4 to 0.8, fixing the amount of pre soaking water of the recycled aggregates. The concrete's module of deformation was determined at 28-days age, using the Brazilian Standard ABNT NBR 8522/03, in cylindrical specimens. The results show that substituting the natural aggregates for the recycled aggregates reduces the module of deformation, and that the coarse red ceramic recycled aggregate and the fine concrete recycled aggregate were the ones that exerted the greatest and the smallest influence, respectively, on the concrete's module of deformation.

Keywords: recycling, construction and demolition waste, concrete, module of deformation.

Texto completo disponivel apenas em PDF.

Full text avaliable only in PDF.

REFERENCES

[01] NETO, J. C. M. Gestão dos resíduos de construção e demolição no Brasil. São Carlos: Rima, 2005. 162 p.
[02] JOHN, V. M. Aproveitamento de resíduos sólidos como materiais de construção. In: Reciclagem de entulho para a produção de materiais de construção / Organizado por Alex Pires Carneiro, Irineu Antônio Schadach de Brum e José Clodoaldo da Silva Cassa. Salvador: EDUFBA; 312 p.; 2001; p. 27-45.
[03] ZORDAN, S.E. Utilização do entulho como agregado, na confecção do concreto. Campinas-SP, 1997. 140 p. Dissertação (Mestrado). Faculdade de Engenharia Civil da Universidade Estadual de Campinas.
[04] BIANCHINI, G.; MARROCCHINO, E.; TASSINARI, R.; VACCARO, C. Recycling of construction and demolition waste materials: a chemical-mineralogical appraisal. Waste Management, Vol. 25, pg. 149-159, 2005.
[05] SANI, D.; MORICONI, G.; FAVA, G. CORINALDESI, V. Leaching and mechanical behavior of concrete manufactured with recycled aggregates. Waste Management, Vol. 25, pg. 177-182, 2005.
[06] PINTO, T. P. Metodologia para gestão diferenciada de resíduos sólidos da construção urbana. São Paulo-SP, 1999. 203 p. Tese (Doutorado). Escola Politécnica da Universidade de São Paulo.
[07] LEITE, M. A. Avaliação de propriedades mecânicas de concretos produzidos com agregados reciclados de resíduos de construção e demolição. Porto Alegre-RS, 2001. 270 p. Tese (Doutorado). Programa de Pós-Graduação em Engenharia Civil da Universidade Federal do Rio Grande do Sul.
[08] VIEIRA, G. L. Estudo do processo de corrosão sob a ação de íons cloreto em concretos obtidos a partir de agregados reciclados de resíduos de construção e demolição. Porto Alegre-RS, 2003. 151p. Dissertação (Mestrado). Programa de Pós-Graduação em Engenharia Civil da Universidade Federal do Rio Grande do Sul.
[09] RIBEIRO, J. L. D.; C. S. T. CATEN. Projeto de experimentos. Porto Alegre: FEEng/UFRGS, 2001. 128 p.
[10] WERKEMA, M. C. C.; AGUIAR, S. Planejamento e análise de experimentos: como identificar e avaliar as principais variáveis influentes em um processo. Belo Horizonte: Fundação Christiano Ottoni, 1996. 294 p.
[11] LIN, Y.; TYAN, Y.; CHANG, T.; CHANG, C. An assessment of optimal mixture for concrete made with recycled concrete aggregates. Cement and Concrete Research, Vol. 34, pg. 1373-1380, 2004.
[12] HELENE, P.R.L.; TERZIAN, P. Manual de Dosagem e Controle do Concreto. São Paulo: PINI, Brasília: SENAI, 1992. 349p.
[13] HANSEN, C. T.; NARUD, H. Strenght of recycled concrete made from crushed concrete coarse aggregate. Concrete International, Vol. 5, N. 1, 1983.
[14] HANSEN, C. T.; BØEGH, E. Elasticity and drying shrinkage of recycled-aggregate concrete. ACI Journal, Vol. 82, N. 5, 1985.
[15] MASCE, N. O.; MIYAZATO, S.; YODSUDJAI, W. Influence of recycled aggregate on interfacial transition zone, strength, chloride penetration and carbonation of concrete. Journal of Materials in Civil Enginnering, Vol 15, N. 5, pg. 443-451, 2003.
[16] KATZ, A. Properties of concrete made with recycled aggregate from partially hydrated old concrete. Cement and Concrete Research, Vol. 33, pg. 703-711, 2003.
[17] ZAHARIEVA, R.; BUYLE-BODIN, F.; SKOCZYLAS, F. EIRQUIM, E. Assessment of the surfasse permeation properties of recycled aggregate concrete. Cement and Concrete Composites, Vol. 25, pg. 223-232, 2003.
[18] BRITO, J. de; PEREIRA, A. S.; CORREIA, J. R. Mechanical behavior of non-structural concrete made with recycled aggregates. Cement & Concrete Composites, Vol. 27, N. 4, pg 429-433, 2005.
[19] XIAO, J.; LI, J,; ZHANG, Ch. Mechanical properties of recycled aggregate concrete under uniaxial loading. Cement and Concrete Research, Vol. 35, pg. 1187-1194, 2005.
[20] MEHTA P. K.; MONTEIRO, P. J. M. Concreto: estruturas, propriedades e materiais. São Paulo, Ed. PINI, 1994.
[21] AJDUKIEWICZ, A.; KLISZCZEWICZ, A. Influence of recycled aggregates on mechanical properties of HS/HPC. Cement and Concrete Composites. Vol. 24, pg. 269-279, 2002.
[22] GÓMEZ-SOBERÓN, J. M. V. Porosity of recycled concrete with substitution of recycled concrete aggregate: na experimental study. Cement and Concrete Research, Vol. 32, p. 1301-1311, 2002.
[23] CABRAL, A. E. B.; DAL MOLIN, D. C. C.; SCHALCH, V. Caracterização de agregados reciclados de concreto, de argamassa e de cerâmica vermelha da região metropolitana de Porto Alegre/RS. Anais: 47º Congresso Brasileiro do Concreto. Olinda, 2005.
[24] RILEM RECOMMENDATION. Specifications for concrete with recycled aggregates. 121- DRG guidance for demolition and reuse of concrete and masonry. Materials and Structures, Vol. 27, p. 557-559, 1994.
[25] KHALAF, F. M.; DeVENNY, A. Recycling of demolished masonry rublle as coarse aggregate in concrete: review. Journal of materials in civil engineering, Vol. 16, N. 04, pg. 331-340, 2004.

Publication Dates

Publication in this collection
18 Sept 2014
Date of issue
June 2008

This work is licensed under a Creative Commons Attribution 4.0 International License.

[1] [01] NETO, J. C. M. Gestão dos resíduos de construção e demolição no Brasil. São Carlos: Rima, 2005. 162 p.

[2] [02] JOHN, V. M. Aproveitamento de resíduos sólidos como materiais de construção. In: Reciclagem de entulho para a produção de materiais de construção / Organizado por Alex Pires Carneiro, Irineu Antônio Schadach de Brum e José Clodoaldo da Silva Cassa. Salvador: EDUFBA; 312 p.; 2001; p. 27-45.

[3] [03] ZORDAN, S.E. Utilização do entulho como agregado, na confecção do concreto. Campinas-SP, 1997. 140 p. Dissertação (Mestrado). Faculdade de Engenharia Civil da Universidade Estadual de Campinas.

[4] [04] BIANCHINI, G.; MARROCCHINO, E.; TASSINARI, R.; VACCARO, C. Recycling of construction and demolition waste materials: a chemical-mineralogical appraisal. Waste Management, Vol. 25, pg. 149-159, 2005.

[5] [05] SANI, D.; MORICONI, G.; FAVA, G. CORINALDESI, V. Leaching and mechanical behavior of concrete manufactured with recycled aggregates. Waste Management, Vol. 25, pg. 177-182, 2005.

[6] [06] PINTO, T. P. Metodologia para gestão diferenciada de resíduos sólidos da construção urbana. São Paulo-SP, 1999. 203 p. Tese (Doutorado). Escola Politécnica da Universidade de São Paulo.

[7] [07] LEITE, M. A. Avaliação de propriedades mecânicas de concretos produzidos com agregados reciclados de resíduos de construção e demolição. Porto Alegre-RS, 2001. 270 p. Tese (Doutorado). Programa de Pós-Graduação em Engenharia Civil da Universidade Federal do Rio Grande do Sul.

[8] [08] VIEIRA, G. L. Estudo do processo de corrosão sob a ação de íons cloreto em concretos obtidos a partir de agregados reciclados de resíduos de construção e demolição. Porto Alegre-RS, 2003. 151p. Dissertação (Mestrado). Programa de Pós-Graduação em Engenharia Civil da Universidade Federal do Rio Grande do Sul.

[9] [09] RIBEIRO, J. L. D.; C. S. T. CATEN. Projeto de experimentos. Porto Alegre: FEEng/UFRGS, 2001. 128 p.

[10] [10] WERKEMA, M. C. C.; AGUIAR, S. Planejamento e análise de experimentos: como identificar e avaliar as principais variáveis influentes em um processo. Belo Horizonte: Fundação Christiano Ottoni, 1996. 294 p.

[11] [11] LIN, Y.; TYAN, Y.; CHANG, T.; CHANG, C. An assessment of optimal mixture for concrete made with recycled concrete aggregates. Cement and Concrete Research, Vol. 34, pg. 1373-1380, 2004.

[12] [12] HELENE, P.R.L.; TERZIAN, P. Manual de Dosagem e Controle do Concreto. São Paulo: PINI, Brasília: SENAI, 1992. 349p.

[13] [13] HANSEN, C. T.; NARUD, H. Strenght of recycled concrete made from crushed concrete coarse aggregate. Concrete International, Vol. 5, N. 1, 1983.

[14] [14] HANSEN, C. T.; BØEGH, E. Elasticity and drying shrinkage of recycled-aggregate concrete. ACI Journal, Vol. 82, N. 5, 1985.

[15] [15] MASCE, N. O.; MIYAZATO, S.; YODSUDJAI, W. Influence of recycled aggregate on interfacial transition zone, strength, chloride penetration and carbonation of concrete. Journal of Materials in Civil Enginnering, Vol 15, N. 5, pg. 443-451, 2003.

[16] [16] KATZ, A. Properties of concrete made with recycled aggregate from partially hydrated old concrete. Cement and Concrete Research, Vol. 33, pg. 703-711, 2003.

[17] [17] ZAHARIEVA, R.; BUYLE-BODIN, F.; SKOCZYLAS, F. EIRQUIM, E. Assessment of the surfasse permeation properties of recycled aggregate concrete. Cement and Concrete Composites, Vol. 25, pg. 223-232, 2003.

[18] [18] BRITO, J. de; PEREIRA, A. S.; CORREIA, J. R. Mechanical behavior of non-structural concrete made with recycled aggregates. Cement & Concrete Composites, Vol. 27, N. 4, pg 429-433, 2005.

[19] [19] XIAO, J.; LI, J,; ZHANG, Ch. Mechanical properties of recycled aggregate concrete under uniaxial loading. Cement and Concrete Research, Vol. 35, pg. 1187-1194, 2005.

[20] [20] MEHTA P. K.; MONTEIRO, P. J. M. Concreto: estruturas, propriedades e materiais. São Paulo, Ed. PINI, 1994.

[21] [21] AJDUKIEWICZ, A.; KLISZCZEWICZ, A. Influence of recycled aggregates on mechanical properties of HS/HPC. Cement and Concrete Composites. Vol. 24, pg. 269-279, 2002.

[22] [22] GÓMEZ-SOBERÓN, J. M. V. Porosity of recycled concrete with substitution of recycled concrete aggregate: na experimental study. Cement and Concrete Research, Vol. 32, p. 1301-1311, 2002.

[23] [23] CABRAL, A. E. B.; DAL MOLIN, D. C. C.; SCHALCH, V. Caracterização de agregados reciclados de concreto, de argamassa e de cerâmica vermelha da região metropolitana de Porto Alegre/RS. Anais: 47º Congresso Brasileiro do Concreto. Olinda, 2005.

[24] [24] RILEM RECOMMENDATION. Specifications for concrete with recycled aggregates. 121- DRG guidance for demolition and reuse of concrete and masonry. Materials and Structures, Vol. 27, p. 557-559, 1994.

[25] [25] KHALAF, F. M.; DeVENNY, A. Recycling of demolished masonry rublle as coarse aggregate in concrete: review. Journal of materials in civil engineering, Vol. 16, N. 04, pg. 331-340, 2004.