ABSTRACT

The exposure of concrete to high temperatures, such as in a fire, leads to physical and chemical changes, which may cause deterioration of mechanical properties, cracking and spalling. This paper presents a critical review of microstructural changes in concrete exposed to high temperature. The transformations developed in the cement paste, aggregates and interfacial transition zone were studied, as well as the experimental techniques of microanalysis presented in recent related researches. Lastly, a critical analysis of experimental results from literature was performed. It was verified that microstructural changes are related to concrete properties and the heating process. The experimental techniques has a potential use for assessment of thermally damaged concrete, however, these techniques must be applied simultaneously and specific methods must be established.

Keywords:
microstructure; concrete; concrete structures; high temperatures

RESUMO

A exposição a altas temperaturas, como as de um incêndio, promove alterações físicas e químicas no concreto, provocando deterioração das propriedades mecânicas nas estruturas, fissuração e desplacamento. O presente trabalho consiste em uma revisão crítica das alterações microestruturais que incidem no concreto submetido a altas temperaturas. As transformações desenvolvidas na pasta de cimento hidratada, nos agregados e na zona de transição foram estudadas, bem como as técnicas experimentais de microanálise utilizadas em recentes pesquisas desenvolvidas na área. Por fim, uma análise crítica dos resultados de estudos experimentais apresentados pela literatura foi realizada. Verifica-se que as alterações da microestrutura estão relacionadas com as características constitutivas do concreto e com processo do aquecimento. Constata-se a potencialidade das técnicas microestruturais para as etapas de na inspeção e recuperação de estruturas incendiadas, entretanto verifica-se a necessidade de combinação de técnicas e o estabelecimento de métodos padronizados.

Palavras-chave:
microestrutura; concreto; estruturas de concreto; altas temperaturas.

1. Introduction

Concrete, when exposed to high temperatures, can react quite well due to its incombustibility and low thermal diffusivity. From a research that encompassed more than a hundred concrete structures damaged by fire, Tovey and Crook [1[1] TOVEY, A. L.; CROOK, R. L. Experience of Fires in Concrete Structures. ACI Special Publication, v. 32, 1986, p. 1-14.] concluded that most of these constructions performed well and that most of them could be repaired to preserve their initial performance.

Exposure to high temperatures promotes changes in the concrete physical and chemical properties, resulting in reduction in mechanical properties such as compressive strength and modulus of elasticity, fissures, spalling, and transient creep [2[2] GEORGALI, B.; TSAKIRIDIS, P.E. Microstructure of fire-damaged concrete. A case study. Cement and Concrete Composites, v. 27, n. 2, 2005, p. 255-259.

[3] GUO, Z.; SHI, X. Experiment and Calculation of Reinforced Concrete at Elevated Temperatures, Waltham: Butterworth-Heinemann, 1ed, 2011, 311 p.

[4] HAGER, I. Behaviour of cement concrete at high temperature. Bulletin of the Polish Academy of Sciences: Technical Sciences, v. 61, n. 1, 2013, p. 1-10.
-5[5] KHOURY, G.A. Effect of fire on concrete and concrete structures. Progress in Structural Engineering and Materials, v. 2, n. 4, 2000, p. 429-447.], jeopardizing the resistant capacity of elements and the structural system's overall stability. Deterioration of these properties is directly connected to material-related factors (aggregate and cement type, water/cement ratio, additions and fibers) and to the environment (exposure time, heating rate, applied load and humidity) [4[4] HAGER, I. Behaviour of cement concrete at high temperature. Bulletin of the Polish Academy of Sciences: Technical Sciences, v. 61, n. 1, 2013, p. 1-10.

[5] KHOURY, G.A. Effect of fire on concrete and concrete structures. Progress in Structural Engineering and Materials, v. 2, n. 4, 2000, p. 429-447.
-6[6] Fédération internationale du béton - FIB. fib Bulletin 38: Fire design of concrete structures - materials, structures and modelling, 2007, 106 p.]. Analysis of this degradation - and evaluation of the steel reinforcement residual properties - helps in the diagnosis of the structure and definition of a therapy strategy, be it repair, reinforcement or even demolition [7[7] Fédération internationale du béton - FIB. fib Bulletin 46: Fire design of concrete structures - structural behaviour and assessment, 2008, 214 p., 8[8] HAGER, I. Colour Change in Heated Concrete, Fire Technology, v. 50, n. 4, 2013, p. 945-958.].

Postfire residual strength of concrete is linked to the heating profile. Under real conditions, not all structural element faces will be submitted to the heating action [9[9] ANNEREL, E.; TAERWE, L. Revealing the temperature history in concrete after fire exposure by microscopic analysis. Cement and Concrete Research, v. 39, n. 12, 2009, p. 1239-1249.], as they are usually inserted in walls or facing other structural elements. This fact, in addition to the low thermal conductivity of concrete, induces temperature gradients among the consecutive section layers, promoting differential changes in the element [8[8] HAGER, I. Colour Change in Heated Concrete, Fire Technology, v. 50, n. 4, 2013, p. 945-958., 10[10] COLOMBO, M.; FELICETTI, R. New NDT techniques for the assessment of fire-damaged concrete structures, Fire Safety Journal, v. 42, n. 6-7, 2007, p. 461-472.]. Therefore, compressive strength testing on specimens from a fire damaged structure must be used with caution in the diagnosis, since they might not be representative because of the heterogeneous due to temperature distribution in the cross-section [9[9] ANNEREL, E.; TAERWE, L. Revealing the temperature history in concrete after fire exposure by microscopic analysis. Cement and Concrete Research, v. 39, n. 12, 2009, p. 1239-1249., 11[11] SCHNEIDER, U. Repairability of Fire Damaged Structures, Fire Safety Journal , v. 16, 1990, p. 251-336., 12[12] YOSHIDA, M.; OKAMURA, Y.; TASAKA, S.; SHIMODE, T. A Study On Temperature Estimation In Concrete Members After Fire. Fire Safety Science, v. 4, 1994, p. 1183-1194.] and, consequently, the changes in the mechanical properties of the concrete.

Changes in the properties of concrete exposed to high temperatures are related to changes in the material microstructure [6[6] Fédération internationale du béton - FIB. fib Bulletin 38: Fire design of concrete structures - materials, structures and modelling, 2007, 106 p.]. Thus, the residual strength of the material can be verified through testing procedures able to identify these physical, chemical, and mineralogical changes. Techniques such as scanning electron microscopy, X-ray diffraction, thermogravimetric analysis, mercury intrusion porosimetry, colorimetry, and petrography are widely used in the study of concrete degradation after exposure to high temperatures [2[2] GEORGALI, B.; TSAKIRIDIS, P.E. Microstructure of fire-damaged concrete. A case study. Cement and Concrete Composites, v. 27, n. 2, 2005, p. 255-259., 8[8] HAGER, I. Colour Change in Heated Concrete, Fire Technology, v. 50, n. 4, 2013, p. 945-958., 9[9] ANNEREL, E.; TAERWE, L. Revealing the temperature history in concrete after fire exposure by microscopic analysis. Cement and Concrete Research, v. 39, n. 12, 2009, p. 1239-1249., 12[12] YOSHIDA, M.; OKAMURA, Y.; TASAKA, S.; SHIMODE, T. A Study On Temperature Estimation In Concrete Members After Fire. Fire Safety Science, v. 4, 1994, p. 1183-1194.

[13] INGHAM, J.P. Application of petrographic examination techniques to the assessment of fire-damaged concrete and masonry structures. Materials Characterization, v. 60, n. 7, 2009, p. 700-709.

[14] ANNEREL, E.; TAERWE, L. Methods to quantify the colour development of concrete exposed to fire. Construction and Building Materials, v. 25, n. 10, 2011, p. 3989-3997.

[15] ZHANG, Q.; YE, G.; KOENDERS, E. Investigation of the structure of heated Portland cement paste by using various techniques. Construction and Building Materials, v. 38, 2013, p. 1040-1050.

[16] CARRÉ, H.; HAGER, I.; PERLOT, C. Contribution to the development of colorimetry as a method for the assessment of fire-damaged concrete. European Journal of Environmental and Civil Engineering, v. 18, n. 10, 2014, p. 1130-1144.

[17] PENG, G.F.; HUANG, Z.S. Change in microstructure of hardened cement paste subjected to elevated temperatures. Construction and Building Materials , v. 22, n. 4, 2008, p. 593-599.
-18[18] HANDOO, S.K.; AGARWAL, S.; AGARWAL, S.K. Physicochemical, mineralogical, and morphological characteristics of concrete exposed to elevated temperatures. Cement and Concrete Research , v. 32, n. 7, 2002, p. 1009-1018.].

Despite the great quantity of studies in this area, transformations in the micro- and nanostructure of concrete, which drive the macroscopic behavior, are not completely characterized and disseminated [19[19] LIM, S.; MONDAL, P. Micro- and nano-scale characterization to study the thermal degradation of cement-based materials. Materials Characterization , v. 92, 2014, p. 15-25.]. In Brazil, despite the reduced number, important researches of such a type have been developed [20[20] LIMA, R. C. A. Investigação do comportamento de concretos em temperaturas elevadas, Porto Alegre, 2005, Thesis (PhD) - Escola de Engenharia, Universidade Federal do Rio Grande do Sul, 257 p.

[21] SOUZA, A. A. A. Influência do tipo de agregado nas propriedades mecânicas do concreto submetido ao fogo, Campinas, 2005, Thesis (Master) - Universidade Estadual de Campinas, 169 p.

[22] CARVALHO, E. F. T. Estudo da resistência ao fogo do concreto de alto desempenho com metacaulim e adição de fibras, Ouro Preto, 2006, Thesis (PhD) - Universidade Federal de Ouro Preto, 177 p.

[23] SOUSA, M. M. Estudo experimental do comportamento mecânico e da microestrutura de um concreto convencional após simulação das condições de incêndio, Belo Horizonte, 2009, Thesis (Master) - Universidade Federal de Minas Gerais, 126 p.

[24] KIRCHHOF, L. D. Estudo teórico-experimental da influência do teor de umidade no fenômeno de spalling explosivo em concretos expostos a elevadas temperaturas, Porto Alegre, 2010, Thesis (PhD) - Escola de Engenharia, Universidade Federal do Rio Grande do Sul, 262 p.
-25[25] BRITEZ, C. A. Avaliação de pilares de concreto armado colorido de alta resistência , submetidos a elevadas temperaturas, São Paulo, 2011, Thesis (PhD) - Escola Politécnica, Universidade de São Paulo, 252 p.].

This article intends to contribute to the study of concrete structures exposed to high temperatures by undertaking a literature review on this theme, addressing aspects related to the effect of high temperatures on the microstructure (physicochemical changes) and microstructural techniques to evaluate the damaged concrete.

2. Effects of high temperatures on concrete microstructure

Deterioration of concrete exposed to high temperatures is attributed to three factors: physicochemical changes in the cement paste, in its aggregates, and the thermal incompatibility between them. Fire-related factors, such as temperature and heating rate, and structural element conditions, such as applied load and humidity, also play a role in concrete deterioration [5[5] KHOURY, G.A. Effect of fire on concrete and concrete structures. Progress in Structural Engineering and Materials, v. 2, n. 4, 2000, p. 429-447.]. Therefore, it is important to discuss the effects of high temperatures on concrete focusing on the microstructural changes in the aggregates, the hydrated cement paste, and the transition zone. Transformations occurring until the temperature of 1200 ºC - when concrete starts to melt - will be examined[5[5] KHOURY, G.A. Effect of fire on concrete and concrete structures. Progress in Structural Engineering and Materials, v. 2, n. 4, 2000, p. 429-447.]. It is important to highlight that real fire can reach temperatures over 900 ºC, however, it is limited to the superficial layers of structural elements, while the internal temperature keeps relatively low[11[11] SCHNEIDER, U. Repairability of Fire Damaged Structures, Fire Safety Journal , v. 16, 1990, p. 251-336.].

2.1 Effects of high temperatures on aggregates

The nature and microstructure of aggregate affect the stability and thermal conductivity of concrete, changing the residual strength and fluid transport mechanisms [6[6] Fédération internationale du béton - FIB. fib Bulletin 38: Fire design of concrete structures - materials, structures and modelling, 2007, 106 p., 25[25] BRITEZ, C. A. Avaliação de pilares de concreto armado colorido de alta resistência , submetidos a elevadas temperaturas, São Paulo, 2011, Thesis (PhD) - Escola Politécnica, Universidade de São Paulo, 252 p.

[26] XING, Z.; BEAUCOUR, A.-L.; HEBERT, R.; NOUMOWE, A.; LEDESERT, B. Influence of the nature of aggregates on the behaviour of concrete subjected to elevated temperature. Cement and Concrete Research , v. 41, n. 4, 2011, p. 392-402.
-27[27] MINDEGUIA, J.C.; PIMIENTA, P.; CARRÉ, H.; LA BORDERIE, C. On the influence of aggregate nature on concrete behaviour at high temperature. European Journal of Environmental and Civil Engineering , v. 16, n. 2, 2012, p. 236-253.]. When exposed to high temperatures, physicochemical changes affect aggregates, promoting expansion, fractures on their crystalline microstructure, and even melting, at temperatures over 1000 ºC. These effects are related to the aggregate thermal stability, i.e., its susceptibility to chemical and physical changes when exposed to high temperatures. This feature, as well as the verified degradation, changes according to the type of used aggregate[4[4] HAGER, I. Behaviour of cement concrete at high temperature. Bulletin of the Polish Academy of Sciences: Technical Sciences, v. 61, n. 1, 2013, p. 1-10., 6[6] Fédération internationale du béton - FIB. fib Bulletin 38: Fire design of concrete structures - materials, structures and modelling, 2007, 106 p.].

Siliceous aggregates and sand, having quartz in their composition, undergo significant changes at high temperatures; the most known being the volumetric expansion of 5.7% at 573 ºC, due to the transformation of the quartz crystalline form from α to β [6[6] Fédération internationale du béton - FIB. fib Bulletin 38: Fire design of concrete structures - materials, structures and modelling, 2007, 106 p.]. Despite the reversibility of this transformation, radial cracks around the aggregate may be verified due to this expansion [9[9] ANNEREL, E.; TAERWE, L. Revealing the temperature history in concrete after fire exposure by microscopic analysis. Cement and Concrete Research, v. 39, n. 12, 2009, p. 1239-1249.].

Carbonate rocks, such as dolomite, become unstable at temperatures higher than 700 °C due to the transformation of calcium carbonate (CaCO3) into calcium oxide (lime - CaO) and carbon dioxide (CO2). Reaching its peak at 800 ºC and finishing at 898 ºC, this process is endothermic and tend to retard the temperature progress on concrete [4[4] HAGER, I. Behaviour of cement concrete at high temperature. Bulletin of the Polish Academy of Sciences: Technical Sciences, v. 61, n. 1, 2013, p. 1-10., 6[6] Fédération internationale du béton - FIB. fib Bulletin 38: Fire design of concrete structures - materials, structures and modelling, 2007, 106 p., 27[27] MINDEGUIA, J.C.; PIMIENTA, P.; CARRÉ, H.; LA BORDERIE, C. On the influence of aggregate nature on concrete behaviour at high temperature. European Journal of Environmental and Civil Engineering , v. 16, n. 2, 2012, p. 236-253.]. In calcareous aggregates, this phenomenon begins at 600 ºC due to the decomposition of calcium carbonate [29[29] BOLINA, F. L. Avaliação experimental da influência dos requisitos de durabilidade na segurança contra incêndio de protótipos de pilares pré-fabricados de concreto armado, São Leopoldo, 2016. Thesis (Master). Curso de Arquitetura, Universidade do Vale do Rio dos Sinos, 180p]. Basalt aggregates have a great thermal stability and start to melt at temperatures above 1000 ºC. During this process, they expand and release gases held inside the rock. [6[6] Fédération internationale du béton - FIB. fib Bulletin 38: Fire design of concrete structures - materials, structures and modelling, 2007, 106 p.].

2.2 Effect of high temperatures on the hydrated cement paste

The behavior of the hydrated cement paste at high temperatures depends on factors such as water/cement ratio, the ratio between C/S (CaO/SiO2 or calcium oxide / silicon dioxide), quantity of Ca(OH)2 (portlandite / CH) formed, hydration degree and humidity [6[6] Fédération internationale du béton - FIB. fib Bulletin 38: Fire design of concrete structures - materials, structures and modelling, 2007, 106 p., 27[27] MINDEGUIA, J.C.; PIMIENTA, P.; CARRÉ, H.; LA BORDERIE, C. On the influence of aggregate nature on concrete behaviour at high temperature. European Journal of Environmental and Civil Engineering , v. 16, n. 2, 2012, p. 236-253.].

Under high temperatures, the degradation process begins with the decomposition of ettringite, which happens at 80 ºC approximately [4[4] HAGER, I. Behaviour of cement concrete at high temperature. Bulletin of the Polish Academy of Sciences: Technical Sciences, v. 61, n. 1, 2013, p. 1-10., 13[13] INGHAM, J.P. Application of petrographic examination techniques to the assessment of fire-damaged concrete and masonry structures. Materials Characterization, v. 60, n. 7, 2009, p. 700-709., 30[30] CASTELLOTE, M.; ALONSO, C.; ANDRADE, C.; TURRILLAS, X.; CAMPO, J. Composition and microstructural changes of cement pastes upon heating, as studied by neutron diffraction. Cement and Concrete Research , v. 34, n. 9, 2004, p. 1633-1644.]. Subsequently, the cement paste dehydrates, and this is associated with the microstructural changes in the material. Initially, the capillary water (free water), which is not influenced by the Van der Waals attraction forces, evaporates, followed by the evaporation of lamellar and adsorbed waters, due to a physical process. Lastly, the water chemically associated with C-S-H (calcium silicate hydrate) is lost [4[4] HAGER, I. Behaviour of cement concrete at high temperature. Bulletin of the Polish Academy of Sciences: Technical Sciences, v. 61, n. 1, 2013, p. 1-10., 6[6] Fédération internationale du béton - FIB. fib Bulletin 38: Fire design of concrete structures - materials, structures and modelling, 2007, 106 p., 29[29] BOLINA, F. L. Avaliação experimental da influência dos requisitos de durabilidade na segurança contra incêndio de protótipos de pilares pré-fabricados de concreto armado, São Leopoldo, 2016. Thesis (Master). Curso de Arquitetura, Universidade do Vale do Rio dos Sinos, 180p]. This C-S-H dehydration is a physicochemical process that causes the relaxation of microtensions and is responsible for transient creep. It begins at 100 ºC (212 ºF) and starts cement paste loss, together with the cracking and porosity increase, in addition to accumulation of water vapor in the pores, which in turn contributes to spalling. At 700 ºC, C-S-H decomposes into β-C2S (belite), βCS (wollastonite) and water, leading to shrinkage of cement paste and strength reduction. The loss of water associated with C-S-H promotes an increase in porosity, also contributing to strength loss [4[4] HAGER, I. Behaviour of cement concrete at high temperature. Bulletin of the Polish Academy of Sciences: Technical Sciences, v. 61, n. 1, 2013, p. 1-10., 6[6] Fédération internationale du béton - FIB. fib Bulletin 38: Fire design of concrete structures - materials, structures and modelling, 2007, 106 p., 29[29] BOLINA, F. L. Avaliação experimental da influência dos requisitos de durabilidade na segurança contra incêndio de protótipos de pilares pré-fabricados de concreto armado, São Leopoldo, 2016. Thesis (Master). Curso de Arquitetura, Universidade do Vale do Rio dos Sinos, 180p, 30[30] CASTELLOTE, M.; ALONSO, C.; ANDRADE, C.; TURRILLAS, X.; CAMPO, J. Composition and microstructural changes of cement pastes upon heating, as studied by neutron diffraction. Cement and Concrete Research , v. 34, n. 9, 2004, p. 1633-1644.].

Portlandite crystals also undergo a process of dehydration at temperatures over 420 ºC, contributing to increased shrinkage and microcracking in the cement paste. In this process, Ca(OH)2 decomposes into CaO (calcium oxide) and water. Another change is the decarburization of calcium carbonate (CaCO3), which decomposes into CaO and CO2 at temperatures higher than 650 ºC [6[6] Fédération internationale du béton - FIB. fib Bulletin 38: Fire design of concrete structures - materials, structures and modelling, 2007, 106 p., 30[30] CASTELLOTE, M.; ALONSO, C.; ANDRADE, C.; TURRILLAS, X.; CAMPO, J. Composition and microstructural changes of cement pastes upon heating, as studied by neutron diffraction. Cement and Concrete Research , v. 34, n. 9, 2004, p. 1633-1644.].

High temperatures also affect non-hydrated clinker grains, existent in the hydrated cement paste, promoting their expansion. This phenomenon, combined with shrinkage of cement paste caused by changes in C-S-H and CH, promotes differential thermal expansions among the materials, that results in microcracking in the concrete, increasing its porosity [32[32] ZHANG, Q. Microstructure and deterioration mechanisms of portland cement paste at elevated temperature, Delft, 2013, Tese (PhD) - Technische Universiteit Delft, 175 p.]. When temperatures exceed 1200 ºC, the cement paste starts to melt [5[5] KHOURY, G.A. Effect of fire on concrete and concrete structures. Progress in Structural Engineering and Materials, v. 2, n. 4, 2000, p. 429-447.].

Porosity is also influenced by high temperatures, growing non-linearly, mainly due to the progressive C-S-H dehydration process. From 20 ºC until 300 ºC, the increase in porosity is reduced, lower than the verified mass loss. This relation reverses beyond 300 ºC, with significant increase in porosity and intensification of microcracks. Another peak of porosity increase happens beyond 900 ºC[6[6] Fédération internationale du béton - FIB. fib Bulletin 38: Fire design of concrete structures - materials, structures and modelling, 2007, 106 p.]. In conditions where the cement paste does not lose humidity to the environment rapidly, as in the interior of large concrete sections, heating may lead to the appearance of C-S-H or other crystals, depending on the CaO/SiO2 ratio [4[4] HAGER, I. Behaviour of cement concrete at high temperature. Bulletin of the Polish Academy of Sciences: Technical Sciences, v. 61, n. 1, 2013, p. 1-10., 5[5] KHOURY, G.A. Effect of fire on concrete and concrete structures. Progress in Structural Engineering and Materials, v. 2, n. 4, 2000, p. 429-447.].

After exposure to high temperatures, cooling also promotes changes in the cement paste. The cementitious products in the paste may rehydrate, forming new gels or crystalline components. The formed lime also rehydrates and expands, creating new fissures [33[33] LIMA, R.C.A.; KIRCHHOF, L.D.; SILVA FILHO, L.C.P. Variação de propriedades mecânicas de concretos convencionais e de alta resistência em temperaturas elevadas. Concreto & Contrução, v. 46, 2007, p. 65-68.].

2.3 Effect of high temperatures on the transition zone

The interface between aggregates and cement paste, usually 50 µm thick [34[34] PAULON, V.; KIRCHHEIM, A.P. Nanoestrutura e Microestrutura do Concreto Endurecido. In: ISAIA, G.C. (Ed.), Concreto: Ciência e Tecnologia, IBRACON, São Paulo, 2011: p. 585.], is regarded as the “weak link” in concrete, due to the great volume of voids and fissures in the region, besides the presence of weak C-S-H crystals and portlandite and ettringite secondary crystals [28[28] MEHTA, P.K.; MONTEIRO, P.J.M. Concreto: Microestrutura, Propriedades e Materiais, São Paulo: IBRACON, 2ed, 2014, 782 p.].

Concrete heating leads to a differential thermal expansion between the aggregate and the cementitious matrix. Due to dehydration, the paste suffers an intense shrinkage process during heating, whereas the aggregates undergo an expansion process (Figure 1). This leads to cracks, which initially appear in the transition zone due to its higher fragility [4[4] HAGER, I. Behaviour of cement concrete at high temperature. Bulletin of the Polish Academy of Sciences: Technical Sciences, v. 61, n. 1, 2013, p. 1-10., 6[6] Fédération internationale du béton - FIB. fib Bulletin 38: Fire design of concrete structures - materials, structures and modelling, 2007, 106 p., 9[9] ANNEREL, E.; TAERWE, L. Revealing the temperature history in concrete after fire exposure by microscopic analysis. Cement and Concrete Research, v. 39, n. 12, 2009, p. 1239-1249.].

Figure 1
Thermal incompatibility between aggregate and hydrated cement paste (adapted [6[6] Fédération internationale du béton - FIB. fib Bulletin 38: Fire design of concrete structures - materials, structures and modelling, 2007, 106 p.])

Transition zone weakening can also lead to concrete spalling at high temperatures, according to Bolina [29[29] BOLINA, F. L. Avaliação experimental da influência dos requisitos de durabilidade na segurança contra incêndio de protótipos de pilares pré-fabricados de concreto armado, São Leopoldo, 2016. Thesis (Master). Curso de Arquitetura, Universidade do Vale do Rio dos Sinos, 180p] experimental observations. Induced by vapor pressures from the material interior, the interface maximizes the phenomenon [2[2] GEORGALI, B.; TSAKIRIDIS, P.E. Microstructure of fire-damaged concrete. A case study. Cement and Concrete Composites, v. 27, n. 2, 2005, p. 255-259.

[3] GUO, Z.; SHI, X. Experiment and Calculation of Reinforced Concrete at Elevated Temperatures, Waltham: Butterworth-Heinemann, 1ed, 2011, 311 p.

[4] HAGER, I. Behaviour of cement concrete at high temperature. Bulletin of the Polish Academy of Sciences: Technical Sciences, v. 61, n. 1, 2013, p. 1-10.
-5[5] KHOURY, G.A. Effect of fire on concrete and concrete structures. Progress in Structural Engineering and Materials, v. 2, n. 4, 2000, p. 429-447.], promoting a reduction in the cross-section of elements and decreasing their resistant capacity; which happens in the initial moments of exposure, when spaling starts [29[29] BOLINA, F. L. Avaliação experimental da influência dos requisitos de durabilidade na segurança contra incêndio de protótipos de pilares pré-fabricados de concreto armado, São Leopoldo, 2016. Thesis (Master). Curso de Arquitetura, Universidade do Vale do Rio dos Sinos, 180p].

3. Evaluation of concrete after exposure to high temperatures

One of the fire protection engineering concerns is to assess the safety of a structure exposed to fire, aiming at the definition of a therapy strategy [7[7] Fédération internationale du béton - FIB. fib Bulletin 46: Fire design of concrete structures - structural behaviour and assessment, 2008, 214 p.]. For such purposes, careful inspection is fundamental for a proper diagnosis of the affected structure. In case of reinforced concrete, the inspection must encompass aspects related to concrete - the focus of this text - and to steel reinforcement. Different techniques, destructive and nondestructive, can be used in postfire assessment. A summary of these techniques applied to concrete - the focus of the present study - can be seen in Table 1 [7[7] Fédération internationale du béton - FIB. fib Bulletin 46: Fire design of concrete structures - structural behaviour and assessment, 2008, 214 p., 10[10] COLOMBO, M.; FELICETTI, R. New NDT techniques for the assessment of fire-damaged concrete structures, Fire Safety Journal, v. 42, n. 6-7, 2007, p. 461-472.].

Table 1
Non-destructive testing applied to fire damaged concrete (adapted [10[10] COLOMBO, M.; FELICETTI, R. New NDT techniques for the assessment of fire-damaged concrete structures, Fire Safety Journal, v. 42, n. 6-7, 2007, p. 461-472.])

An important factor for residual strength verification of the element is the temperature gradient between consecutive layers of the material cross section, formed due to the low thermal conductivity of concrete [9[9] ANNEREL, E.; TAERWE, L. Revealing the temperature history in concrete after fire exposure by microscopic analysis. Cement and Concrete Research, v. 39, n. 12, 2009, p. 1239-1249., 10[10] COLOMBO, M.; FELICETTI, R. New NDT techniques for the assessment of fire-damaged concrete structures, Fire Safety Journal, v. 42, n. 6-7, 2007, p. 461-472.]. This factor, added to the material heterogeneity, makes the structure assessment after exposure to high temperatures a complex process[8[8] HAGER, I. Colour Change in Heated Concrete, Fire Technology, v. 50, n. 4, 2013, p. 945-958.].

This complexity also influences the performance of tests applied to structure inspection. The compressive strength test, the most usual and straightforward method for in situ concrete strength testing, offers little information as to the material residual strength, due to the variation of the damage along the sample profundity [7[7] Fédération internationale du béton - FIB. fib Bulletin 46: Fire design of concrete structures - structural behaviour and assessment, 2008, 214 p., 11[11] SCHNEIDER, U. Repairability of Fire Damaged Structures, Fire Safety Journal , v. 16, 1990, p. 251-336., 12[12] YOSHIDA, M.; OKAMURA, Y.; TASAKA, S.; SHIMODE, T. A Study On Temperature Estimation In Concrete Members After Fire. Fire Safety Science, v. 4, 1994, p. 1183-1194.]. Annerel and Taerwe [9[9] ANNEREL, E.; TAERWE, L. Revealing the temperature history in concrete after fire exposure by microscopic analysis. Cement and Concrete Research, v. 39, n. 12, 2009, p. 1239-1249.] emphasize that these tests, when applied to samples of structures submitted to high temperatures, are not representative. Thus, techniques allowing quantification of physical, chemical, and mineralogical changes, as well as the temperature reached in the structural element, are more efficient [6[6] Fédération internationale du béton - FIB. fib Bulletin 38: Fire design of concrete structures - materials, structures and modelling, 2007, 106 p., 9[9] ANNEREL, E.; TAERWE, L. Revealing the temperature history in concrete after fire exposure by microscopic analysis. Cement and Concrete Research, v. 39, n. 12, 2009, p. 1239-1249.]. These techniques can and should be applied along with other tests, including compressive strength test. The more techniques are used for concrete integrity characterization, the more precise the diagnosis and the more efficient and affordable the therapy of the fire damaged structure will be.

Table 2 presents a summary of the research using microstructural techniques for characterization of the concrete exposed to high temperatures. A prevalence of laboratory tests is observed; with few cases where the techniques were applied to elements and damaged structures. Four main techniques were observed: scanning electron microscopy (SEM), X-ray diffraction (XRD), mercury intrusion porosimetry (MIP), and differential thermal analysis (DTA) and thermogravimetric analysis (TGA). It is important to emphasize that most of the research uses multiple methods for experimental analysis.

Tabela 2
Summary of research that used microanalysis techniques

3.1 Scanning Electron Microscopy (SEM)

Scanning electron microscopy (SEM) provides information on the material morphology with a usual magnification of 10,000 times and a resolution between 2 and 5 nm. A distinctive feature is the possibility to have a large depth of focus, forming a 3D-like image, with possible combination with a chemical microanalysis, [35[35] DAL MOLIN, D. C. C. Técnicas Experimentais para o Estudo da Microestrutura. In: ISAIA, G.C. (Ed.), Materiais de Construção Civil e Príncipios de Ciência e Engenharia de Materiais, 2.ed., IBRACON, São Paulo , 2010: p. 862.]. Handoo, Agarwal and Agarwal [18[18] HANDOO, S.K.; AGARWAL, S.; AGARWAL, S.K. Physicochemical, mineralogical, and morphological characteristics of concrete exposed to elevated temperatures. Cement and Concrete Research , v. 32, n. 7, 2002, p. 1009-1018.] used this technique in ordinary concretes with siliceous aggregate and compression strength of 47 MPa under temperatures up to 1000 ºC, which enabled them to identify that the morphological changes started at 300 ºC and become more intense at 600 ºC, showing great deformation of portlandite crystals and calcium silicate hydrate, besides the presence of voids and fissures.

This increase in voids was also observed in the Peng and Huang [17[17] PENG, G.F.; HUANG, Z.S. Change in microstructure of hardened cement paste subjected to elevated temperatures. Construction and Building Materials , v. 22, n. 4, 2008, p. 593-599.] experimental program. They investigated changes in the microstructure of concretes with compressive strength of 40 MPa, 70 MPa and 110 MPa, heated from 400 ºC until 800 ºC for up to 8 hours. The authors observed a great increase in porosity at 600 ºC, due to the formation of microcracks - one of the main causes of concrete strength reduction.

Annerel and Taerwe [9[9] ANNEREL, E.; TAERWE, L. Revealing the temperature history in concrete after fire exposure by microscopic analysis. Cement and Concrete Research, v. 39, n. 12, 2009, p. 1239-1249.] assessed the microstructure in the transition zone of conventional concretes with siliceous aggregate, a/c ratio of 0.47 ratio and compressive strength of 52.8 MPa, exposed to temperatures of 350 ºC and 550 ºC. The micrographs are presented in Figure 2. It was observed that at room temperature the transition zone presented an intact matrix, constituted by ettringite, portlandite and calcium silicate hydrate. It was also possible to observe that the ettringite and portlandite crystals disappeared at 350 ºC and 550 ºC respectively. The authors points out that the ettringite dehydration process started at 70 ºC but it could not be visualized because micrographs were not collected at temperatures below 350 ºC .

Figure 2
Micrograph of transition zone of ordinary concrete subjected to 550 ºC (adapted [9[9] ANNEREL, E.; TAERWE, L. Revealing the temperature history in concrete after fire exposure by microscopic analysis. Cement and Concrete Research, v. 39, n. 12, 2009, p. 1239-1249.])

The micrographs obtained by the experimental program of Arioz [36[36] ARIOZ, O. Retained properties of concrete exposed to high temperatures: Size effect. Fire and Materials, v. 33, n. 5, 2009, p. 211-222.] allowed the identification of microcracks, voids, and partial deterioration of CH and C-S-H in concretes with calcareous aggregate and compressive strength of 76.6 MPa, submitted to 800 ºC. The author also analyzed samples submitted to 1200 ºC, completely deteriorated (Figure 3).

Figure 3
Changes in concrete subjected to 1200 ºC (adaptaed [36[36] ARIOZ, O. Retained properties of concrete exposed to high temperatures: Size effect. Fire and Materials, v. 33, n. 5, 2009, p. 211-222.])

Kim, Yun, and Park [37[37] KIM, K.Y.; YUN, T.S.; PARK, K.P. Evaluation of pore structures and cracking in cement paste exposed to elevated temperatures by X-ray computed tomography. Cement and Concrete Research , v. 50, 2013, p. 34-40.] studied the behavior of mortars with 0.5 w/c ratio, submitted to elevated temperatures. In the obtained micrographs, the authors pointed out that at 500 ºC the hexagonal CH crystals started to deform, and that at 700 ºC they were completely decomposed, as well as C-S-H. Zhang, Ye and Koenders [15[15] ZHANG, Q.; YE, G.; KOENDERS, E. Investigation of the structure of heated Portland cement paste by using various techniques. Construction and Building Materials, v. 38, 2013, p. 1040-1050.], who also researched the behavior of cement pastes with 0.5 w/c ratio, have seen in the micrographs that until 400 ºC the changes in the paste are minimal and that from 500 ºC until 1000 ºC fissures start to show in the region, along with pores, interconnected by these fissures.

Degradation of cementitious compounds has also been observed by Wang et al., [38[38] WANG, G.; ZHANG, C.; ZHANG, B.; LI, Q.; SHUI, Z. Study on the high-temperature behavior and rehydration characteristics of hardened cement paste. Fire and Materials , v. 39, n. 5, 2015, p. 741-750.] who studied cement pastes with compressive strength of 42 MPa and 0.4 w/c ratio, heated to 400 ºC , 600 ºC and 800 ºC. The authors indicated that at 400 ºC portlandite and calcium silicate hydrate were in good conditions. At 800 ºC the hydration products were completely decomposed, producing voids and cracks.

Lim and Mondal [19[19] LIM, S.; MONDAL, P. Micro- and nano-scale characterization to study the thermal degradation of cement-based materials. Materials Characterization , v. 92, 2014, p. 15-25.] researched the micro- and nanostructure of cement pastes with 0.35 w/c ratio, heated until 1000 ºC. The micrographs are shown in Figure 4. It is possible to observe that at room temperature the portlandite and C-S-H crystals remained intact. At 300 ºC the degradation of these solids started, in addition to the appearance of non-hydrated cement particles. Microcracks appeared at 500 ºCat their interface and got more intense at 700 ºC and 900 ºC, increasing the paste porosity.

Figure 4
Micrographs of cement paste at ambiente temperature (a), 300 ºC (b), 500 ºC (c) e 900 ºC (d) (adapted [19[19] LIM, S.; MONDAL, P. Micro- and nano-scale characterization to study the thermal degradation of cement-based materials. Materials Characterization , v. 92, 2014, p. 15-25.])

In Brazil, SEM has been used by Lima [20[20] LIMA, R. C. A. Investigação do comportamento de concretos em temperaturas elevadas, Porto Alegre, 2005, Thesis (PhD) - Escola de Engenharia, Universidade Federal do Rio Grande do Sul, 257 p.] and Sousa [23[23] SOUSA, M. M. Estudo experimental do comportamento mecânico e da microestrutura de um concreto convencional após simulação das condições de incêndio, Belo Horizonte, 2009, Thesis (Master) - Universidade Federal de Minas Gerais, 126 p.]. The former studied high strength concretes with basaltic and granitic aggregates with a w/c ratio of 0.3, heated from 200 ºC to 900 ºC. The main changes seen were the rough aspect and the interconnectivity of fissures, at temperatures of 600 ºC and 900 ºC. Sousa [23[23] SOUSA, M. M. Estudo experimental do comportamento mecânico e da microestrutura de um concreto convencional após simulação das condições de incêndio, Belo Horizonte, 2009, Thesis (Master) - Universidade Federal de Minas Gerais, 126 p.] studied ordinary concretes with calcareous and gneissic aggregates, 0.5 w/c ratio and 35 MPa compressive strength, submitted to 100 ºC, 300 ºC and 600 ºC, observing an increase in the number of pores and microcracks from 300 ºC on. At 600 ºC the author identified the presence of sintered areas, cracks, and small ettringite crystals, probably formed after the samples were cooled.

3.2 X-Ray Diffraction (XRD)

X-ray diffraction analysis allows the identification of the crystalline phases of a material, providing information on the structure, composition, and state of the sample. The technique consists in projecting an X-ray beam onto the sample, which interacts with the ray through its atoms, creating the diffraction phenomenon [35[35] DAL MOLIN, D. C. C. Técnicas Experimentais para o Estudo da Microestrutura. In: ISAIA, G.C. (Ed.), Materiais de Construção Civil e Príncipios de Ciência e Engenharia de Materiais, 2.ed., IBRACON, São Paulo , 2010: p. 862.]. Diffracted rays are captured and processed by the equipment and the result is plotted in a graph with the intensity of radiation diffracted by diffraction angles [20[20] LIMA, R. C. A. Investigação do comportamento de concretos em temperaturas elevadas, Porto Alegre, 2005, Thesis (PhD) - Escola de Engenharia, Universidade Federal do Rio Grande do Sul, 257 p.].

Handoo, Agarwal and Agarwal [18[18] HANDOO, S.K.; AGARWAL, S.; AGARWAL, S.K. Physicochemical, mineralogical, and morphological characteristics of concrete exposed to elevated temperatures. Cement and Concrete Research , v. 32, n. 7, 2002, p. 1009-1018.] tested with XRD the behavior of ordinary concrete with siliceous aggregate and 47 MPa compressive strength, heated until 1000 ºC. The obtained diffractograms showed a gradual reduction of Ca(OH)2 from 400 ºC on until its complete extinction at 800 ºC (Figure 5). Peng and Huang [17[17] PENG, G.F.; HUANG, Z.S. Change in microstructure of hardened cement paste subjected to elevated temperatures. Construction and Building Materials , v. 22, n. 4, 2008, p. 593-599.] obtained diffractograms of their samples and veryfied (Figure 6) that the intensity peaks related to calcium hydroxide and calcium carbonate started to decrease at 500 ºC , indicating its decomposition. Calcium silicate hydrate started to decompose at 600 ºC, the same level where an intense presence of pores was observed through SEM.

Figure 5
Diffractograms identifying portlandite behaviour (adapted [18[18] HANDOO, S.K.; AGARWAL, S.; AGARWAL, S.K. Physicochemical, mineralogical, and morphological characteristics of concrete exposed to elevated temperatures. Cement and Concrete Research , v. 32, n. 7, 2002, p. 1009-1018.])

Figure 6
Diffractograms of cement paste heated up to 800 ºC (adapted [17[17] PENG, G.F.; HUANG, Z.S. Change in microstructure of hardened cement paste subjected to elevated temperatures. Construction and Building Materials , v. 22, n. 4, 2008, p. 593-599.])

In Kim, Yun, and Park [37[37] KIM, K.Y.; YUN, T.S.; PARK, K.P. Evaluation of pore structures and cracking in cement paste exposed to elevated temperatures by X-ray computed tomography. Cement and Concrete Research , v. 50, 2013, p. 34-40.] diffractograms, the main transformation happens with CH, which starts to be reduced at 400 ºC and disappeared at 1000 ºC (Figure 7). This phenomenon is consistent with the transformations observed in the micrographs. In the cement paste samples with 42 MPa compressive strength and 0.4 w/c ratio analyzed by Wang et al. [38[38] WANG, G.; ZHANG, C.; ZHANG, B.; LI, Q.; SHUI, Z. Study on the high-temperature behavior and rehydration characteristics of hardened cement paste. Fire and Materials , v. 39, n. 5, 2015, p. 741-750.], as shown in Figure 8, there was a reduction in the peaks of portlandite and C-S-H from 600 ºC on.

Figure 7
Diffractograms of cement paste heated at different temperatures (adapted [37[37] KIM, K.Y.; YUN, T.S.; PARK, K.P. Evaluation of pore structures and cracking in cement paste exposed to elevated temperatures by X-ray computed tomography. Cement and Concrete Research , v. 50, 2013, p. 34-40.])

Figure 8
Diffractograms of cement paste heated up to 800 ºC (adapted [38[38] WANG, G.; ZHANG, C.; ZHANG, B.; LI, Q.; SHUI, Z. Study on the high-temperature behavior and rehydration characteristics of hardened cement paste. Fire and Materials , v. 39, n. 5, 2015, p. 741-750.])

Lim and Mondal [19[19] LIM, S.; MONDAL, P. Micro- and nano-scale characterization to study the thermal degradation of cement-based materials. Materials Characterization , v. 92, 2014, p. 15-25.] cement paste (w/c ratio of 0.35) analysis (Figure 9) shows that until 300 ºC there were no visible changes in the intensity peaks of the hydration products. From 500 ºC on, disappearance of the C-S-H peak was observed, along with the appearance of a β-C2S peak. At 500 ºC there was a decrease in the CH peaks and the emergence of CaO peaks. The authors mention the emergence and disappearance of CaCO3, resulting from the reaction of CaO with CO2 present in the furnace at 700 ºC and 900 ºC, respectively.

Figura 9
Diffractograms of cement paste after heating (adapted [19[19] LIM, S.; MONDAL, P. Micro- and nano-scale characterization to study the thermal degradation of cement-based materials. Materials Characterization , v. 92, 2014, p. 15-25.])

In Brazil, XRD analysis of concretes exposed to high temperatures was used by Lima [20[20] LIMA, R. C. A. Investigação do comportamento de concretos em temperaturas elevadas, Porto Alegre, 2005, Thesis (PhD) - Escola de Engenharia, Universidade Federal do Rio Grande do Sul, 257 p.] and Ruschel [39[39] RUSCHEL, F. Avaliação da utilização de ferramentas de simulação computacional para reconstituição de incêndios em edificações de concreto armado: aplicação ao caso shopping total em Porto Alegre-RS, Porto Alegre, 2011, Thesis (Master) - Escola de Engenharia, Universidade Federal do Rio Grande do Sul, 133 p.]. In Lima [20[20] LIMA, R. C. A. Investigação do comportamento de concretos em temperaturas elevadas, Porto Alegre, 2005, Thesis (PhD) - Escola de Engenharia, Universidade Federal do Rio Grande do Sul, 257 p.] diffractograms, it is possible to see that ettringite was stable up to 200 ºC and portlandite up to 400 ºC, when it started to transform into calcium oxide until its total disappearance at 900 ºC. This ettringite stability has been observed in other experiments, since this product only starts to dehydrate at 70 ºC. The author emphasizes that this presence may be related to a possible stability of the material in the interior of the collected sample or the result of a concrete rehydration process. Ruschel [39[39] RUSCHEL, F. Avaliação da utilização de ferramentas de simulação computacional para reconstituição de incêndios em edificações de concreto armado: aplicação ao caso shopping total em Porto Alegre-RS, Porto Alegre, 2011, Thesis (Master) - Escola de Engenharia, Universidade Federal do Rio Grande do Sul, 133 p.] applied x-ray diffraction in the assessment of a fire damaged structure. He observed in samples from different fire damaged columns a reduction in the peaks of portlandite, mainly at the top of structural elements, where there was accumulation of hot gases and, consequently, a higher concrete degradation.

3.3 Mercury Intrusion Porosimetry (MIP)

The principle of mercury intrusion porosimetry (MIP) is the insertion of a non-wetting fluid - mercury, in this case - able to penetrate into the materials pores, where the fluid pressure and volume are used for the calculation of pore volume. Pore sizes vary from 0.001 µm to 1000 µm, depending on the pressure used [32[32] ZHANG, Q. Microstructure and deterioration mechanisms of portland cement paste at elevated temperature, Delft, 2013, Tese (PhD) - Technische Universiteit Delft, 175 p.].

Peng and Huang [17[17] PENG, G.F.; HUANG, Z.S. Change in microstructure of hardened cement paste subjected to elevated temperatures. Construction and Building Materials , v. 22, n. 4, 2008, p. 593-599.] have verified an increase in the porosity of three samples of concrete with respectively 40 MPa, 70 MPa and 110 MPa compressive strength, heated to 600 ºC. The result confirmed what had been observed in their micrographies. For Zhang, Ye and Koenders [15[15] ZHANG, Q.; YE, G.; KOENDERS, E. Investigation of the structure of heated Portland cement paste by using various techniques. Construction and Building Materials, v. 38, 2013, p. 1040-1050.], who researched the behavior of cement pastes with 0.5 w/c ratio, the total porosity obtained via MIP increased as the temperature got higher. Figure 10 shows that the increase in total porosity was higher after 400 ºC, the point at which portlandite dehydrated.

Figure 10
Total porosity of cement paste (adapted [15[15] ZHANG, Q.; YE, G.; KOENDERS, E. Investigation of the structure of heated Portland cement paste by using various techniques. Construction and Building Materials, v. 38, 2013, p. 1040-1050.])

This significant porosity increase after 400 ºC has also been observed by Wang et al., [38[38] WANG, G.; ZHANG, C.; ZHANG, B.; LI, Q.; SHUI, Z. Study on the high-temperature behavior and rehydration characteristics of hardened cement paste. Fire and Materials , v. 39, n. 5, 2015, p. 741-750.] who studied cement pastes with compressive strength of 42 MPa and w/c ratio of 0.4, heated to 400 ºC and 800 ºC. The authors indicated that at room temperature the total porosity was 26.9 %. At 400 ºC this value went up to 29.8 % and at 800 ºC it jumped to 45.5 %, which explains the marked strength decrease at this point.

3.4 Other experimental techniques

Although the techniques herein reported are predominately used in the characterization of concrete microstructures submitted to high temperatures, other important tools can be used for the analysis of degraded material, such as differential thermal analysis (DTA) and thermogravimetric analysis (TGA). In this kind of analysis, a sample of the concrete is heated in a furnace with a similar inert sample. Changes in the sample mass are monitored during heating to identify the presence of the material components [7[7] Fédération internationale du béton - FIB. fib Bulletin 46: Fire design of concrete structures - structural behaviour and assessment, 2008, 214 p.].

Handoo, Agarwal and Agarwal [18[18] HANDOO, S.K.; AGARWAL, S.; AGARWAL, S.K. Physicochemical, mineralogical, and morphological characteristics of concrete exposed to elevated temperatures. Cement and Concrete Research , v. 32, n. 7, 2002, p. 1009-1018.] applied these thermal analyses to the evaluation of conventional concrete with 47 MPa compressive strength, heated to 1000 ºC. The authors reported a reduction in the portlandite quantity from 300 ºC on, until its disappearance at 800 ºC. In Brazil, Lima [20[20] LIMA, R. C. A. Investigação do comportamento de concretos em temperaturas elevadas, Porto Alegre, 2005, Thesis (PhD) - Escola de Engenharia, Universidade Federal do Rio Grande do Sul, 257 p.] performed tests of this nature with cement paste and verified the decomposition of ettringite at 50 ºC, dehydration of portlandite at 500 ºC and reduction of carbon dioxide, resulting from the dehydration of calcium carbonate, at 800 ºC.

Since heating promotes changes in the concrete color, some authors have used techniques centered on colorimetry. Annerel and Taerwe [14[14] ANNEREL, E.; TAERWE, L. Methods to quantify the colour development of concrete exposed to fire. Construction and Building Materials, v. 25, n. 10, 2011, p. 3989-3997.] used spectrophotometry and a table scanner for analysis, observing changes in the cement paste from grey to red (300 ºC - 600 ºC ), whitish grey (600 ºC - 900 ºC) and brown (900 ºC - 1000 ºC). Hager [8[8] HAGER, I. Colour Change in Heated Concrete, Fire Technology, v. 50, n. 4, 2013, p. 945-958.] also used a table scanner to analyze the changes in the material color. Figure 11 shows some images obtained by the author, who emphasizes that these changes are directly linked to alterations in both the aggregate and the paste physical and chemical properties.

Figura 11
Color change as a function of temperature (adapted [8[8] HAGER, I. Colour Change in Heated Concrete, Fire Technology, v. 50, n. 4, 2013, p. 945-958.])

Georgali and Tsakiridis [2[2] GEORGALI, B.; TSAKIRIDIS, P.E. Microstructure of fire-damaged concrete. A case study. Cement and Concrete Composites, v. 27, n. 2, 2005, p. 255-259.] used optical microscopy in the analysis of a concrete structure submitted to real fire. Absence of portlandite crystals was observed inside the superficial samples of the structural element, as well as the transformation of carbonate aggregates into CaO, an indication that the temperature reached 900 ºC on the exposed face of the element.

3.5 Discussion

From the techniques studied in the reviewed works it is possible to say that they show great potential for identification of physical, chemical, and mineralogical changes in the concrete submitted to high temperatures. In general, the techniques are convergent to each other and allow confirming the main known transformations in heated concrete. However, some aspects must be observed in the use of these experimental techniques.

The first aspect is the samples nature in the studied experimental programs. Of the 35 works reviewed in Table 2, only 4 studied the behavior of concretes derived from real-scale structural elements. This difference is significant, most in terms of the developed thermal gradients, which vary substantially depending on the dimensions of the specimen and the structural element. This variability is also affected by the sample heating method, whether it is laboratorial (heating rate, curve, and heated faces, among others) or real (fire).

Still related to the sample, the studied experimental programs did not present specific details on its preparation, nor did they indicate if any standard was followed. For example, the sample used in x-ray diffractometry is in the form of powder and the grinding method used in the reviewed studies was not explained. These procedures should be standardized and norms must be followed in order to achieve greater reliability in results.

The same standardization question applies to the process of sample collection in the case of fire damaged structures. For example, one of the options for sample collection is the extraction of core samples via diamond saw. This process may introduce deleterious effects in the core sample[40[40] SILVA FILHO, L.C.P.; HELENE, P. Análise de Estruturas de Concreto com Problemas de Resistência e Fissuração. In: ISAIA, G.C. (Ed.), Concreto: Ciência e Tecnologia, IBRACON, São Paulo , 2011: p.1129.], such as additional cracks, which may influence the scanning electron microscopy and mercury intrusion porosimetry results.

Another aspect to be pointed out is that despite the knowledge of the main inflicted changes and their respective temperature levels [19[19] LIM, S.; MONDAL, P. Micro- and nano-scale characterization to study the thermal degradation of cement-based materials. Materials Characterization , v. 92, 2014, p. 15-25.], a direct relation between micro and macro still has not yet been completely established, due to the complexity of the phenomena involved, the variability and diversity of studied concretes, as well as the disperse and isolated nature of high temperature tests [6[6] Fédération internationale du béton - FIB. fib Bulletin 38: Fire design of concrete structures - materials, structures and modelling, 2007, 106 p.].

In any case, microstructural experimental methods are an important tool for the diagnosis of fire damaged structures and future work should focus on establishing methods and normative procedures with the purpose of application in real fire cases, as well as on identifying the relations between the microstructure and properties of concrete.

4. Conclusion

This work performed a review of the techniques for analysis of the microstructure of concrete submitted to high temperatures. It confirmed that concrete degradation is directly linked to the concrete features and the heating process. In the case of aggregates, temperature promotes their expansion and may even lead to phase changing, depending on the temperature level. As to the hydrated cement paste, temperature causes chemical changes in the hydration products, leading to the appearance of cracks, voids and intense paste shrinkage. These effects, added to the differential movement between the paste and aggregates, promote intense degradation of concrete properties.

These microstructural changes can be observed and detected through experimental techniques. SEM allows the observation of cracks, voids and morphological changes in the hydrated products. XRD allows the identification of the degradation of concrete elements, mainly in terms of portlandite reduction, which can be used both as a damage and temperature evolution indicator. MIP helps to identify the paste porosity increase, and these values can be directly related to the reduction of mechanical compressive strength and to other microstructural observations. Other techniques, such as colorimetry, DTA and DTG provide complementary information that helps in the diagnosis of concrete submitted to high temperatures.

Despite the outstanding potential, some aspects must be observed in the application of these techniques. Most of the reviewed experimental works use small-scale samples, heated in laboratories, which does not include the diverse variables of a real structure submitted to real fire. Another relevant factor is the absence of standardized procedures for collection and preparation of samples for these analyses. It is necessary to establish specific procedures for inspection of fire damaged structures, describing places for collecting samples, and how to collect and prepare them.

Technique standardization for structure inspection will lead to more reliable results, contributing to the diagnosis of damaged structures and definition of therapy strategies. In any case, the techniques are an important diagnosis tool for structures damaged by high temperatures, especially when applied jointly, given the agreement between results. The experience achieved with their application will contribute to a better understanding of these techniques and to their improvement.

5. Bibliographic references

  • [1]
    TOVEY, A. L.; CROOK, R. L. Experience of Fires in Concrete Structures. ACI Special Publication, v. 32, 1986, p. 1-14.
  • [2]
    GEORGALI, B.; TSAKIRIDIS, P.E. Microstructure of fire-damaged concrete. A case study. Cement and Concrete Composites, v. 27, n. 2, 2005, p. 255-259.
  • [3]
    GUO, Z.; SHI, X. Experiment and Calculation of Reinforced Concrete at Elevated Temperatures, Waltham: Butterworth-Heinemann, 1ed, 2011, 311 p.
  • [4]
    HAGER, I. Behaviour of cement concrete at high temperature. Bulletin of the Polish Academy of Sciences: Technical Sciences, v. 61, n. 1, 2013, p. 1-10.
  • [5]
    KHOURY, G.A. Effect of fire on concrete and concrete structures. Progress in Structural Engineering and Materials, v. 2, n. 4, 2000, p. 429-447.
  • [6]
    Fédération internationale du béton - FIB. fib Bulletin 38: Fire design of concrete structures - materials, structures and modelling, 2007, 106 p.
  • [7]
    Fédération internationale du béton - FIB. fib Bulletin 46: Fire design of concrete structures - structural behaviour and assessment, 2008, 214 p.
  • [8]
    HAGER, I. Colour Change in Heated Concrete, Fire Technology, v. 50, n. 4, 2013, p. 945-958.
  • [9]
    ANNEREL, E.; TAERWE, L. Revealing the temperature history in concrete after fire exposure by microscopic analysis. Cement and Concrete Research, v. 39, n. 12, 2009, p. 1239-1249.
  • [10]
    COLOMBO, M.; FELICETTI, R. New NDT techniques for the assessment of fire-damaged concrete structures, Fire Safety Journal, v. 42, n. 6-7, 2007, p. 461-472.
  • [11]
    SCHNEIDER, U. Repairability of Fire Damaged Structures, Fire Safety Journal , v. 16, 1990, p. 251-336.
  • [12]
    YOSHIDA, M.; OKAMURA, Y.; TASAKA, S.; SHIMODE, T. A Study On Temperature Estimation In Concrete Members After Fire. Fire Safety Science, v. 4, 1994, p. 1183-1194.
  • [13]
    INGHAM, J.P. Application of petrographic examination techniques to the assessment of fire-damaged concrete and masonry structures. Materials Characterization, v. 60, n. 7, 2009, p. 700-709.
  • [14]
    ANNEREL, E.; TAERWE, L. Methods to quantify the colour development of concrete exposed to fire. Construction and Building Materials, v. 25, n. 10, 2011, p. 3989-3997.
  • [15]
    ZHANG, Q.; YE, G.; KOENDERS, E. Investigation of the structure of heated Portland cement paste by using various techniques. Construction and Building Materials, v. 38, 2013, p. 1040-1050.
  • [16]
    CARRÉ, H.; HAGER, I.; PERLOT, C. Contribution to the development of colorimetry as a method for the assessment of fire-damaged concrete. European Journal of Environmental and Civil Engineering, v. 18, n. 10, 2014, p. 1130-1144.
  • [17]
    PENG, G.F.; HUANG, Z.S. Change in microstructure of hardened cement paste subjected to elevated temperatures. Construction and Building Materials , v. 22, n. 4, 2008, p. 593-599.
  • [18]
    HANDOO, S.K.; AGARWAL, S.; AGARWAL, S.K. Physicochemical, mineralogical, and morphological characteristics of concrete exposed to elevated temperatures. Cement and Concrete Research , v. 32, n. 7, 2002, p. 1009-1018.
  • [19]
    LIM, S.; MONDAL, P. Micro- and nano-scale characterization to study the thermal degradation of cement-based materials. Materials Characterization , v. 92, 2014, p. 15-25.
  • [20]
    LIMA, R. C. A. Investigação do comportamento de concretos em temperaturas elevadas, Porto Alegre, 2005, Thesis (PhD) - Escola de Engenharia, Universidade Federal do Rio Grande do Sul, 257 p.
  • [21]
    SOUZA, A. A. A. Influência do tipo de agregado nas propriedades mecânicas do concreto submetido ao fogo, Campinas, 2005, Thesis (Master) - Universidade Estadual de Campinas, 169 p.
  • [22]
    CARVALHO, E. F. T. Estudo da resistência ao fogo do concreto de alto desempenho com metacaulim e adição de fibras, Ouro Preto, 2006, Thesis (PhD) - Universidade Federal de Ouro Preto, 177 p.
  • [23]
    SOUSA, M. M. Estudo experimental do comportamento mecânico e da microestrutura de um concreto convencional após simulação das condições de incêndio, Belo Horizonte, 2009, Thesis (Master) - Universidade Federal de Minas Gerais, 126 p.
  • [24]
    KIRCHHOF, L. D. Estudo teórico-experimental da influência do teor de umidade no fenômeno de spalling explosivo em concretos expostos a elevadas temperaturas, Porto Alegre, 2010, Thesis (PhD) - Escola de Engenharia, Universidade Federal do Rio Grande do Sul, 262 p.
  • [25]
    BRITEZ, C. A. Avaliação de pilares de concreto armado colorido de alta resistência , submetidos a elevadas temperaturas, São Paulo, 2011, Thesis (PhD) - Escola Politécnica, Universidade de São Paulo, 252 p.
  • [26]
    XING, Z.; BEAUCOUR, A.-L.; HEBERT, R.; NOUMOWE, A.; LEDESERT, B. Influence of the nature of aggregates on the behaviour of concrete subjected to elevated temperature. Cement and Concrete Research , v. 41, n. 4, 2011, p. 392-402.
  • [27]
    MINDEGUIA, J.C.; PIMIENTA, P.; CARRÉ, H.; LA BORDERIE, C. On the influence of aggregate nature on concrete behaviour at high temperature. European Journal of Environmental and Civil Engineering , v. 16, n. 2, 2012, p. 236-253.
  • [28]
    MEHTA, P.K.; MONTEIRO, P.J.M. Concreto: Microestrutura, Propriedades e Materiais, São Paulo: IBRACON, 2ed, 2014, 782 p.
  • [29]
    BOLINA, F. L. Avaliação experimental da influência dos requisitos de durabilidade na segurança contra incêndio de protótipos de pilares pré-fabricados de concreto armado, São Leopoldo, 2016. Thesis (Master). Curso de Arquitetura, Universidade do Vale do Rio dos Sinos, 180p
  • [30]
    CASTELLOTE, M.; ALONSO, C.; ANDRADE, C.; TURRILLAS, X.; CAMPO, J. Composition and microstructural changes of cement pastes upon heating, as studied by neutron diffraction. Cement and Concrete Research , v. 34, n. 9, 2004, p. 1633-1644.
  • [31]
    DENOËL, J.F. Fire Safety and Concrete Structures, Bruxelas: Febelcem, 1.ed, 2007, 87 p.
  • [32]
    ZHANG, Q. Microstructure and deterioration mechanisms of portland cement paste at elevated temperature, Delft, 2013, Tese (PhD) - Technische Universiteit Delft, 175 p.
  • [33]
    LIMA, R.C.A.; KIRCHHOF, L.D.; SILVA FILHO, L.C.P. Variação de propriedades mecânicas de concretos convencionais e de alta resistência em temperaturas elevadas. Concreto & Contrução, v. 46, 2007, p. 65-68.
  • [34]
    PAULON, V.; KIRCHHEIM, A.P. Nanoestrutura e Microestrutura do Concreto Endurecido. In: ISAIA, G.C. (Ed.), Concreto: Ciência e Tecnologia, IBRACON, São Paulo, 2011: p. 585.
  • [35]
    DAL MOLIN, D. C. C. Técnicas Experimentais para o Estudo da Microestrutura. In: ISAIA, G.C. (Ed.), Materiais de Construção Civil e Príncipios de Ciência e Engenharia de Materiais, 2.ed., IBRACON, São Paulo , 2010: p. 862.
  • [36]
    ARIOZ, O. Retained properties of concrete exposed to high temperatures: Size effect. Fire and Materials, v. 33, n. 5, 2009, p. 211-222.
  • [37]
    KIM, K.Y.; YUN, T.S.; PARK, K.P. Evaluation of pore structures and cracking in cement paste exposed to elevated temperatures by X-ray computed tomography. Cement and Concrete Research , v. 50, 2013, p. 34-40.
  • [38]
    WANG, G.; ZHANG, C.; ZHANG, B.; LI, Q.; SHUI, Z. Study on the high-temperature behavior and rehydration characteristics of hardened cement paste. Fire and Materials , v. 39, n. 5, 2015, p. 741-750.
  • [39]
    RUSCHEL, F. Avaliação da utilização de ferramentas de simulação computacional para reconstituição de incêndios em edificações de concreto armado: aplicação ao caso shopping total em Porto Alegre-RS, Porto Alegre, 2011, Thesis (Master) - Escola de Engenharia, Universidade Federal do Rio Grande do Sul, 133 p.
  • [40]
    SILVA FILHO, L.C.P.; HELENE, P. Análise de Estruturas de Concreto com Problemas de Resistência e Fissuração. In: ISAIA, G.C. (Ed.), Concreto: Ciência e Tecnologia, IBRACON, São Paulo , 2011: p.1129.
  • [41]
    ROSTASY, F.S.; WEIβ, R.; WIEDEMANN, G. Changes of Pore Structure of Cement Mortars Due To Temperature. Cement and Concrete Research , v. 10, n. 2, 1980, p. 157-164.
  • [42]
    PIASTA, J.; SAWICZ, Z.; RUDZINSKI, L. Changes in the structure of hardened cement paste due to high temperature. Matériaux et Construction, v. 17, n. 4, 1984, p. 291-296.
  • [43]
    CHAN, S.N.; PENG, G.; CHAN, J.W. Comparison between high strength concrete and normal strength concrete subjected to high temperature. Materials and Structures, v. 29, 1996, p. 616-619.
  • [44]
    SAAD, M.; ABO-EL-ENEIN, S; HANNA, G. B.; KOTKATA, M.F. Effect of temperature on physical and mechanical properties of concrete containing silica fume. Cement and Concrete Research , v. 26, n. 5, 1996, p. 669-675.
  • [45]
    LIN, W.M.; LIN, T.D.; POWERS-COUCHE, L.J. Microstructures of fire-damaged concrete, ACI Materials Journal, v. 93, n. 3, 1996, p. 199-205.
  • [46]
    LUO, X.; SUN, W.; CHAN, Y.N. Residual compressive strength and microstructure of high performance concrete after exposure to high temperature. Materials and Structures , v. 33, 2000, p. 294-298.
  • [47]
    SHORT, N.R.; PURKISS, J.A.; GUISE, S.E. Assessment of fire damaged concrete using colour image analysis, Construction and Building Materials , v. 15, n. 1, 2001, p. 9-15.
  • [48]
    POON, C.S.; AZHAR, S.; ANSON, M.; WONG, Y.L. Comparison of the strength and durability performance of normal- and high-strength pozzolanic concretes at elevated temperatures. Cement and Concrete Research , v. 31, n. 9, 2001, p. 1291-1300.
  • [49]
    ALARCON-RUIZ, L.; PLATRET, G.; MASSIEU, E.; EHRLACHER, A. The use of thermal analysis in assessing the effect of temperature on a cement paste. Cement and Concrete Research , v. 35, n. 3, 2005, p. 609-613.
  • [50]
    WANG, X.S.; WU, B.S.; WANG, Q.Y. Online SEM investigation of microcrack characteristics of concretes at various temperatures. Cement and Concrete Research , v. 35, n. 7, 2005, p. 1385-1390.
  • [51]
    WENDT, S.C. Análise da mudança de cor em concretos submetidos a altas temperaturas como indicativo de temperaturas alcançadas e da degradação térmica, Porto Alegre, 2006, Thesis (Master) - Escola de Engenharia, Universidade Federal do Rio Grande do Sul, 186 p.
  • [52]
    BIOLZI, L.; CATTANEO, S.; ROSATI, G. Evaluating residual properties of thermally damaged concrete. Cement and Concrete Composites , v. 30, n. 10, 2008, p. 907-916.
  • [53]
    FALL, M.; SAMB, S.S. Effect of high temperature on strength and microstructural properties of cemented paste backfill. Fire Safety Journal , v. 44, n. 4, 2009, p. 642-651.
  • [54]
    MENÉNDEZ, E.; VEGA, L. Analysis of the behaviour of the structural concrete after the fire at the Windsor Building in Madrid. Fire and Materials , v. 34, n. 2, 2009, p 95-107.
  • [55]
    IBRAHIM, R.K.; HAMID, R,; TAHA, M.R. Fire resistance of high-volume fly ash mortars with nanosilica addition. Construction and Building Materials , v. 36, 2012, p. 779-786.
  • [56]
    AKCA, A.H.; ZIHNIOǦLU, N.Ö. High performance concrete under elevated temperatures. Construction and Building Materials , v. 44, 2013, p. 317-328.
  • [57]
    HEAP, M.J.; LAVALLÉE, Y.; LAUMANN, A.; HESS, K.U.; MEREDITH, P.G.; DINGWELL, D.B.; HUISMANN, S.; WEISE, F. The influence of thermal-stressing (up to 1000 °c) on the physical, mechanical, and chemical properties of siliceous-aggregate, high-strength concrete. Construction and Building Materials , v. 42, 2013, p. 248-265.
  • [58]
    HEIKAL, M.; EL-DIDAMONY, H.; SOKKARY, T.M.; AHMED, I.A. Behavior of composite cement pastes containing microsilica and fly ash at elevated temperature. Construction and Building Materials , v. 38, 2013, p. 1180-1190.

Publication Dates

  • Publication in this collection
    Aug 2017

History

  • Received
    29 May 2016
  • Accepted
    09 Feb 2017
IBRACON - Instituto Brasileiro do Concreto Instituto Brasileiro do Concreto (IBRACON), Av. Queiroz Filho, nº 1700 sala 407/408 Torre D, Villa Lobos Office Park, CEP 05319-000, São Paulo, SP - Brasil, Tel. (55 11) 3735-0202, Fax: (55 11) 3733-2190 - São Paulo - SP - Brazil
E-mail: arlene@ibracon.org.br