Metal-based catalysts are indispensable in modern chemistry and one of the biggest challenges for industrial applications is to quantify their performance and stability. The metrics of performance can be obtained in terms of the turnover number and turnover frequency, and the stability might be associated with the leaching of the heterogeneous catalysts. Thus, metal quantification is the starting point to understand and evaluate the features of catalysts. Among the technologies for metal determination, spectrophotometric analysis stands out for being cheap and easy to perform. However, the challenge is the sample preparation to direct quantification from the heterogeneous materials. Herein, it is shown how important is the photochemical pre-treatment for the quantification of the total iron from heterogeneous thin films composed of iron-based materials. The photochemical approach was used to ensure a full dissociation of iron ions before the quantification. This method was revealed to be highly effective and precise, having a wide range of applications for different iron-based catalysts. Metalbased Metal based frequency Thus determination perform However materials Herein pretreatment pre treatment ironbased precise

The water oxidation is the limiting step in the water-splitting process. Given this scenario, the development of new catalysts is essential in this field. The emergent demand is the use of Earth-abundant elements and catalysts with high performance under mild conditions. Because of this, catalysts such as Prussian Blue analogues (PBA) have been receiving a lot of attention in recent years. In addition, working under neutral conditions allows us to take advantage of the modification of conductive polymeric 3D printed electrodes (3DPE) with Prussian Blue. Thus, we described in this work the development of the polymeric 3D printed electrodes modified by cobalt-Prussian Blue and their performance in the water oxidation process. The 3D printed electrodes modified with Co3[Co(CN)6]2 (Co-Co PBA) have a Tafel slope of 343 mV dec−1 while those modified with Co3[Fe(CN)6]2 (Co-Fe PBA) have a Tafel slope of 378 mV dec−1. This means that both catalysts have the same mechanism for the water oxidation process. On the other hand, the overpotential of Co-Co PBA in 3DPE is lower than the value observed by Co-Fe PBA in 3DPE suggesting the best electrocatalytic activity for Co-Co PBA catalyst.