Antibacterial activity of chitosan biofilm for the conservation of fertile and table eggs

[Atividade antibacteriana de biofilme de quitosana para conservação de ovos férteis e de mesa]

ABSTRACT

The aim of this study was to develop a chitosan biofilm against Salmonella enteritidis, for the conservation of fertile and table eggs. Two experiments were performed. Experiment 1: 400 specific pathogen-free table eggs were divided in a completely randomized design into four treatments, five replicates and each replicate with 20 table eggs. Experimental groups were assigned to control and 1, 5 and 10% chitosan treatment. The eggs were immersed in the chitosan solution. They were then exposed to Salmonella enteritidis and stored for 1, 24, 96 and 168h at 4ºC. The eggs were then washed with 10mL of physiological saline solution. Experiment 2: 80 specific pathogen-free fertile eggs were tested, the assays were assigned to control and 1, 5 and 10% chitosan treatment. Each treatment had 20 fertile eggs. The eggs were immersed in the chitosan solution. They were individually weighed and incubated. Egg weight, humidity loss, and hatchability (weight and length of newly hatched chicks) characteristics were assessed. In Experiment 1, comparison between treatments showed differences (P< 0.05) in the total recovered of Salmonella enteritidis on eggshell, with the lower values in 5 y 10% chitosan treatment at 96 y 168h respectively. In Experiment 2, chitosan did not show any effect on the egg weight and chick weight, where the average was 57.44 and 38.23g respectively. The humidity loss and chick length showed differences (P< 0.05), with the lower values in 5 y 10% chitosan treatment. The antibacterial activity of chitosan biofilm provide a practical tool against Salmonella enteritidis in fertile and table eggs because the chitosan did not affect egg weight and chick weight, relevant parameters in the poultry industry.

Keywords:
chitosan; fertile eggs; table eggs; Salmonella enteritidis

RESUMO

O presente estudo teve como objetivo desenvolver um biofilme de quitosana contra Salmonella enteritidis, para conservação de ovos férteis e de mesa. Dois experimentos foram realizados. Experimento 1: 400 ovos de mesa livres de patógenos especificados foram divididos em delineamento inteiramente casualizado em quatro tratamentos, cinco repetições e cada réplica contendo 20 ovos de mesa. Grupos experimentais foram designados para controle e 1, 5 e 10% de tratamento com quitosana. Os ovos foram imersos em solução de quitosana. Em seguida foram expostos a Salmonella enteritidis, e armazenados por 1, 24, 96 e 168h a 4ºC. Após, os ovos foram lavados com 10mL de solução salina fisiológica. Experimento 2: 80 ovos férteis livres de patógenos especificados foram testados. Os ensaios foram atribuídos a controle e 1, 5 e 10% de tratamento com quitosana. Cada tratamento teve 20 ovos férteis. Os ovos foram imersos em solução de quitosana. Em seguida foram individualmente pesados e incubados. Peso dos ovos, perda de umidade e características de eclodibilidade (peso e comprimento dos pintinhos recém-nascidos) foram avaliados. No Experimento 1, a comparação entre tratamentos mostrou diferenças (P< 0,05) na quantidade total recuperada de Salmonella enteritidis na casca, com os menores valores em 5 e 10% de tratamento com quitosana a 96 e 168h respetivamente. No experimento 2, a quitosana não mostrou nenhum efeito no peso do ovo e no peso do pintinho, onde a média foi de 57,44 e 38,23g respetivamente. A perda de umidade e comprimento do pintinho apresentaram diferenças (P< 0,05), com os menores valores em 5 e 10% de tratamento com quitosana. A atividade antibacteriana do biofilme de quitosana, fornece uma ferramenta prática contra Salmonella enteritidis em ovos férteis e de mesa, pois a quitosana não afetou o peso do ovo e peso do pintinho, parâmetros relevantes na indústria avícola.

Palavras-chave:
quitosana; ovos férteis; ovos de mesa; Salmonella enteritidis

INTRODUCTION

According to the World Health Organization (WHO) report published in 2015, the foodborne disease is a leading cause of mortality and morbidity, causing an estimated 600 million human infections/year and 42,000 deaths/year (Havelaar et al., 2015HAVELAAR, A.H.; KIRK, M.D.; TORGERSON, P.R.; GIBB, H.J. et al. World health organization global estimates and regional comparisons of the burden of foodborne disease in 2010. PLoS Med., v.12, pe1001923, 2015.). It is estimated that Salmonella enteritidis (SE) causes 93.8 million human infections and 155,000 deaths annually worldwide (Aspinall et al., 2016ASPINALL, W.P.; COOKE, R.M.; HAVELAAR, A.H.; HOFFMANN, S.; HALD, T. Evaluation of a performance-based expert elicitation: WHO global attribution of foodborne diseases. PLoS One, v.11, pe0149817, 2016.). In the United States, SE affects up to 2 million human infections/year and 452 deaths/year, with an estimated cost of $15 billion (Scharff, 2015). Therefore, the Commission Regulation (CR) No. 2073/2005, concerning microbiological criteria for foodstuffs established the absence of Salmonella spp. in 25g of food as a requirement to gaining market access, particularly for developing economies (Lake et al., 2015LAKE, R.J.; DEVLEESSCHAUWER, B.; NASINYAMA, G.; HAVELAAR, A.H. et al. National studies as a component of the World Health Organization initiative to estimate the global and regional burden of foodborne disease. PLoS One, v.10, pe0140319, 2015.).

To achieve this objective, efficient cleaningand disinfection methods are necessary to totally eradicate problem strains in farms and food environments. In this way, the development of antibacterial biofilms and coatings from food-grade biopolymers has advanced significantly during recent years (Costa et al., 2017COSTA, E.M.; SILVA, S.; VEIGA, M.; VICENTE, S. et al. Investigation of chitosan's antibacterial activity against vancomycin resistant microorganisms and their biofilms. Carbohydr. Polym., v.174, p.369-376, 2017.; Dhumal and Sarkar, 2018DHUMAL, C.V.; SARKAR, P. Composite edible films and coatings from food-grade biopolymers. J. Food. Sci. Technol., v.55, p.4369-4383, 2018.). Among the alternatives tested, polycationic biopolymers are among the most notable due to their high biocompatibility and antimicrobial activity (Venkataraman et al., 2019VENKATARAMAN, S.; LEE, A.L.Z.; TAN, J.P.K.; CHIEN, Y.N.G. et al. Functional cationic derivatives of starch as antimicrobial agents. Polymer Chem., v.10, p.412-423, 2019.). In this regard, the seafood processing industry generates approximately 100 billion t of chitin/year from the marine invertebrates, e.g. exoskeletons of crustaceans, mollusks and shrimp (Hamed et al., 2016HAMED, I.; ÖZOGUL, F.; REGENSTEIN, J.M. Industrial applications of crustacean by-products (chitin, chitosan, and chitooligosaccharides): a review. Trends Food Sci. Technol., v.48, p.40-50, 2016.). However, there are some limitations to using chitin. Two of its major drawbacks, high viscosity, and insolubility in water, are due to the chitin's own structure and molecular weight (Younes and Rinaudo, 2015YOUNES, I.; RINAUDO, M. Chitin and chitosan preparation from marine sources. Structure, properties and applications. Mar. Drugs., v.13, p.1133-1174, 2015.). Therefore, its derivative chitosan has been receiving increasing attention as invaluable biopolymer (Bano et al., 2017BANO, I.; BANO, I.; ARSHAD, M.; YASIN, T. et al. Chitosan: a potential biopolymer for wound management. Int. J. Biol. Macromol., v.102, p.380-383, 2017.).

The chitosan is a linear polysaccharide that consists of glucosamine and N-acetyl-β-D- glucosamine units, obtained after deacetylation of chitin, which consist of β-(1-4)-2-amino D-glucose and β-(1-4)-2-acetamido-D-glucose linked through 1,4-β-glucosidic bonds (Younes and Rinaudo, 2015YOUNES, I.; RINAUDO, M. Chitin and chitosan preparation from marine sources. Structure, properties and applications. Mar. Drugs., v.13, p.1133-1174, 2015.). It is a polycationic biopolymer with a unique structure, including amino groups (-NH2) in its backbone, that grants it the high reactivity (Thakur and Voicu, 2016THAKUR, V.K.; VOICU, S.I. Recent advances in cellulose and chitosan based membranes for water purification: a concise review. Carbohydr. Polymers, v.146, p.148-165, 2016.). Therefore, they have received great attention due to their physical, chemical and antibacterial activity (Verlee et al., 2017VERLEE, A.; MINCKE, S.; STEVENS, C.V. Recent developments in antibacterial and antifungal chitosan and its derivatives. Carbohydr. Polymers, v.164, p.268-283, 2017.). The use of antibacterial biofilms and coatings from food-grade biopolymers during processing can extend the shelf life of food and reduce health risks and economic losses of foodborne disease (Randazzo et al., 2018).

The table eggs are among the most consumed food worldwide. However, one of the constraints limiting the acceptance of table eggs is the suspicion about their bacteriological quality (Antunes et al., 2016ANTUNES, P.; MOURÃO, J.; CAMPOS, J.; LEITE, L. Salmonellosis: the role of poultry meat. Clin. Microbiol. Infect., v.22, p.110-121, 2016.). Contamination of table eggs with SE is a recurring fact, due to the ability to be transmitted both vertically (from layer to egg) and horizontally (from the environment) (Baron et al., 2016BARON, F.; NAU, F.; GUÉRIN-DUBIARD, C.; BONNASSIE, S. et al. Egg white versus Salmonella enteritidis! A harsh medium meets a resilient pathogen. Food Microbiol., v.53, p.82-93, 2016.). The eggs carrying SE on the eggshell or in shell membranes could lead to contamination of the chick (Ketta and Tůmová, 2016KETTA, M.; TŮMOVÁ, E. Eggshell structure, measurements, and quality-affecting factors in laying hens: a review. Czech J. Anim. Sci., v.61, p.299-309, 2016.). Also, eggs are highly susceptible to internal quality deterioration and bacterial growth during storage (Park et al., 2016PARK, S.Y.; CHOI, K.S.; LEE, D.; KIM, D. et al. Eggshell membrane: review and impact on engineering. Biosyst. Eng., v.151, p.446-463, 2016.b). Therefore, the aim of this study was to develop a chitosan biofilm against SE, for the conservation of fertile and table eggs.

MATERIALS AND METHODS

Deacetylated 95% food-grade chitosan was obtained commercially (Paragon Specialty Products., Rainsville, Alabama, United States) and was used in all experiments. The chitosan molecular weight was 350kDa with a viscosity of 800mPa, and particle size of 100 United States mesh (sieve size 0.152mm). Chitosan was prepared by dissolving it in a solution containing 0.5% (w/v glacial acetic acid (J41A08; Mallinckrodt Baker Inc., Phillipsburg, New Jersey, United States).

A poultry isolate of SE, selected for resistance to nalidixic acid (NA) (N-4382; Sigma-Aldrich., St. Louis, Missouri, United States), was used for all experiments. SE was grown in tryptic soy broth (N-22092; Sigma-Aldrich., St. Louis, Missouri, United States) for approximately 8h. The cells were washed three times with 0.9% physiological saline solution (PSS), by centrifuging at 1864 x g for 10min using a portable centrifuge (Porta-Spin C828; UNICO., Dayton, United States). The concentration of the stock solution was determined with a UV/Vis spectrophotometer (ES-218; KONTROLab., Guidonia, Italy) at 525nm. The stock solution was serially diluted and confirmed by colony counts of three replicate samples (0.1mL/replicate) spread on brilliant green agar (278820; Becton-Dickinson Co., Franklin Lakes, United States) plates containing 25µg/mL novobiocin (N-1628; Sigma-Aldrich., St. Louis, Missouri, United States) and 20µg/mL of NA.

Experiment 1. 400 specific pathogen-free (SPF) table eggs were divided in a completely randomized design into four treatments, five replicates and each replicate with 20 table eggs. Experimental groups were assigned to control and 1, 5 and 10% chitosan treatment. The eggs were immersed in chitosan solution for 30s and allowed to dry. They were then exposed to SE (105CFU/mL) for 30s and were transferred to sterile bags and stored for 1, 24, 96 and 168h at 4ºC. The eggs were then washed with 10mL of PSS. Enumeration of SE (CFU/mL) was performed by spread-plating.

Experiment 2. 80 SPF fertile eggs were tested, the assays were assigned to control and 1, 5 and 10% chitosan treatment. Each treatment had 20 fertile eggs. The eggs were immersed in chitosan solution for 30s and allowed to dry. Hatching egg was incubated at constant temperature (37.7ºC) in a single-stage incubation (Chick Master) and relative humidity was maintained at a constant 50% throughout incubation. At 18d of incubation, eggs were weighed and transferred to hatching baskets. Egg weight and humidity loss were quantified. On the day of hatch, chick weight and chick length were quantified according to quality criteria in the poultry industry.

One-way analysis of variance (ANOVA) was performed between and within groups of all data using (SPSS…, 2013), and differences were considered to be significant at a level of (P< 0.05), means were separated using the Tukey multiple range tests.

RESULTS

The total recovered (CFU/mL) of SE on eggshell, determined from 400 table eggs are shown in Table 1. The comparison between treatments showed differences (P< 0.05), with the lower values in 5 y 10% chitosan treatment at 96 y 168h respectively.

The effect of treatments (control, 1, 5 and 10% chitosan) on egg weight, humidity loss, chick weight, and chick length, determined from 80 fertile eggs incubated are shown in Table 2. The chitosan did not show any effect on the egg weight and chick weight, where the average was 57.44 and 38.23g respectively. The humidity loss and chick length showed differences (P< 0.05), with the lower values in 5 y 10% chitosan treatment.

Table 1
Total recovered (CFU/mL) Salmonella enteritidis on eggshell at different times of storage, n= 400 table eggs
Table 2
Effect of treatments (control, 1, 5 and 10% chitosan) on egg weight, humidity loss, chick weight and chick length, n= 80 fertile eggs incubated/chicks during the first day post-hatch

DISCUSSION

The SE biofilm formation under different environmental conditions is a public health problem because it can survive in the long term around poultry farms and contaminate meat and eggs or by-products, through the food chain to reach the consumer (Antunes et al., 2016ANTUNES, P.; MOURÃO, J.; CAMPOS, J.; LEITE, L. Salmonellosis: the role of poultry meat. Clin. Microbiol. Infect., v.22, p.110-121, 2016.; Shah et al., 2017SHAH, D.H.; PAUL, N.C.; SISCHO, W.C.; CRESPO, R.; GUARD, J. Population dynamics and antimicrobial resistance of the most prevalent poultry-associated Salmonella serotypes. Poult. Sci., v.96, p.687-702, 2017.). Biofilms are microbial communities of bacterial cells enclosed in a self-produced polymeric matrix of 97% water and 3% exopolysaccharides (EPS), outer membrane proteins, lipopolysaccharides (LPS), nucleic acids and fatty acids, that attaches to different types of surfaces, inert and alive (Barreto et al., 2016BARRETO, M.; CASTILLO, R.M.; RETAMAL, P. Salmonella enterica: a review or the trilogy agent, host and environment and its importance in Chile. Rev. Chil. Infectol., v.33, p.547-557, 2016.).

The SE biofilms are difficult to eliminate because they are well protected against antibiotics and disinfectants. Therefore, the factors that induce or prevent the formation of bacterial biofilms are currently topics of interest in the poultry industry (Lamas et al., 2018LAMAS, A.; MIRANDA, J.M.; REGAL, P.; VÁZQUEZ, B. et al. A comprehensive review of non-enterica subspecies of Salmonella enterica. Microbiol. Res., v.206, p.60-73, 2018.). In this way, the following log reductions in total recovered (CFU/mL) of SE on eggshell were observed on chitosan as a "secondary cuticle", in comparison to control (Figure 1).

Figure 1
Effect of 5% chitosan on total recovered CFU/mL of Salmonella enteritidis on eggshell at different times of storage, n= 400 table eggs.

The differences in chitosan efficacy (Figure 2), is thought to be a result of varying bacterium cell surface charge and differing cell wall/membrane structure (Verlee et al., 2017VERLEE, A.; MINCKE, S.; STEVENS, C.V. Recent developments in antibacterial and antifungal chitosan and its derivatives. Carbohydr. Polymers, v.164, p.268-283, 2017.). These results suggest that chitosan coatings abort SE biofilms formation by permeabilizing bacterium cells as they contact the surface of chitosan biofilm (Younes and Rinaudo, 2015YOUNES, I.; RINAUDO, M. Chitin and chitosan preparation from marine sources. Structure, properties and applications. Mar. Drugs., v.13, p.1133-1174, 2015.). The positively charged (cationic) chitosan polymer compromises the integrity of the SE membrane due to their reactive amino groups (-NH2) (Thakur and Voicu, 2016THAKUR, V.K.; VOICU, S.I. Recent advances in cellulose and chitosan based membranes for water purification: a concise review. Carbohydr. Polymers, v.146, p.148-165, 2016.). This activity of chitosan biofilm seems to echo reports of engineered antibacterial surfaces in which cationic biocides have been covalently immobilized (Verlee et al., 2017). In addition, the water solubility of the chitosan oligosaccharides enabled their penetration across the extracellular EPS y LPS matrix of SE biofilms, leading to enhanced biofilm killing (Thakur and Voicu, 2016).

Figure 2
Effect of 10% chitosan on total recovered CFU/mL of Salmonella enteritidis on eggshell at different times of storage, n= 400 table eggs.

During incubation, egg water content is absorbed by the embryo and embryonic annexes e.g. amniotic cavity and allantois (Ketta and Tůmová, 2016KETTA, M.; TŮMOVÁ, E. Eggshell structure, measurements, and quality-affecting factors in laying hens: a review. Czech J. Anim. Sci., v.61, p.299-309, 2016.), and a small portion is lost to the evaporation of water molecules through the eggshell pores (Park et al., 2016PARK, S.Y.; CHOI, K.S.; LEE, D.; KIM, D. et al. Eggshell membrane: review and impact on engineering. Biosyst. Eng., v.151, p.446-463, 2016.a). This loss of water is associated with egg heat loss by evaporation and conduction and is important not only for egg heat loss but also for the formation of the air chamber (Menconi et al., 2014MENCONI, A.; PUMFORD, N.R.; MORGAN, M.J.; BIELKE, L.R.; KALLAPURA, G. et al. Effect of chitosan on Salmonella typhimurium in broiler chickens. Foodborne Pathog. Dis., v.11, p.165-169, 2014.). The chitosan has a mucoadhesive property due to the union of its hydroxyl group (-OH) and the amino groups (-NH2) of mucin, and the electrostatic interactions between the positively charged amines of chitosan and the negatively charged sialic acid residue of the mucin (Shi et al., 2005SHI, B.L.; LI, D.F.; PIAO, X.S.; YAN, S.M. Effects of chitosan on growth performance and energy and protein utilisation in broiler chickens. Br. Poult. Sci., v.46, p.516-519, 2005.; Pradhan and Sahoo, 2017PRADHAN, A.K.; SAHOO, P.K. Synthesis and study of thermal, mechanical and biodegradation properties of chitosan-g-PMMA with chicken egg shell (nano-CaO) as a novel bio-filler. Mater. Sci. Eng. C. Mater. Biol. Appl., v.80, p.149-155, 2017.).

However, we have not observed any negative effect on the loss of water through the eggshell pores (Figure 3). The eggshell allows physical exchanges between the egg and the external environment and includes heat transfer and the exchange of carbon dioxide (CO2) and dioxygen (O2). In this sense, it’s known that chitosan has a selective permeability to gasses, CO2 and O2 (Costa et al., 2017COSTA, E.M.; SILVA, S.; VEIGA, M.; VICENTE, S. et al. Investigation of chitosan's antibacterial activity against vancomycin resistant microorganisms and their biofilms. Carbohydr. Polym., v.174, p.369-376, 2017.; Dhumal and Sarkar, 2018DHUMAL, C.V.; SARKAR, P. Composite edible films and coatings from food-grade biopolymers. J. Food. Sci. Technol., v.55, p.4369-4383, 2018.), and high resistance to heat due to hydrogen-bonded bridges (Randazzo et al., 2018).

Although more studies of the fertile egg of old hens where the shell is more porous are still needed, in the present study the antibacterial activity of chitosan biofilm provided a practical tool against SE in fertile and table eggs, because the chitosan did not affect egg weight and chick weight (Table 2), relevant parameters in the poultry industry.

Figure 3
Effect of 0, 1, 5 and 10% chitosan on humidity loss, n= 80 incubated fertile eggs.

CONCLUSIONS

The surfaces coated with chitosan biofilm resisted the formation of Salmonella enteritidis biofilm. The comparison between treatments showed differences in the total recovered Salmonella enteritidis on the eggshell, the lowest values being obtained with the chitosan treatments. These results support the hypothesis that chitosan biofilm interacts with Salmonella enteritidis through a combination of electrostatic, hydrophobic and chelating properties. Because the reactive amino groups (-NH2) present in the chitosan biofilm and positively charged, bind to negatively charged cell surface molecules such as lipopolysaccharide and outer membrane proteins. At the same time, chitosan can chelate metal ions which are crucial for the stability of the bacterial cell membranes, and thus cause the disruption of cell surface structure. Overall, these data support further investigations for larger-scale application of a chitosan biofilm that offers good antibacterial activity against Salmonella enteritidis in fertile and table eggs, because the chitosan did not affect egg weight and chick weight, relevant parameters in the poultry industry.

ACKNOWLEDGMENTS

This project was supported by the National Council of Science and Technology-México (CONACyT-México).

REFERENCES

  • ANTUNES, P.; MOURÃO, J.; CAMPOS, J.; LEITE, L. Salmonellosis: the role of poultry meat. Clin. Microbiol. Infect., v.22, p.110-121, 2016.
  • ASPINALL, W.P.; COOKE, R.M.; HAVELAAR, A.H.; HOFFMANN, S.; HALD, T. Evaluation of a performance-based expert elicitation: WHO global attribution of foodborne diseases. PLoS One, v.11, pe0149817, 2016.
  • BANO, I.; BANO, I.; ARSHAD, M.; YASIN, T. et al. Chitosan: a potential biopolymer for wound management. Int. J. Biol. Macromol., v.102, p.380-383, 2017.
  • BARON, F.; NAU, F.; GUÉRIN-DUBIARD, C.; BONNASSIE, S. et al. Egg white versus Salmonella enteritidis! A harsh medium meets a resilient pathogen. Food Microbiol., v.53, p.82-93, 2016.
  • BARRETO, M.; CASTILLO, R.M.; RETAMAL, P. Salmonella enterica: a review or the trilogy agent, host and environment and its importance in Chile. Rev. Chil. Infectol., v.33, p.547-557, 2016.
  • COSTA, E.M.; SILVA, S.; VEIGA, M.; VICENTE, S. et al. Investigation of chitosan's antibacterial activity against vancomycin resistant microorganisms and their biofilms. Carbohydr. Polym., v.174, p.369-376, 2017.
  • DHUMAL, C.V.; SARKAR, P. Composite edible films and coatings from food-grade biopolymers. J. Food. Sci. Technol., v.55, p.4369-4383, 2018.
  • et al. Polymers and biopolymers with antiviral activity: potential applications for improving food safety. Compr. Rev. Food. Sci. Food. Saf., v.17, p.754-768, 2018.
  • HAMED, I.; ÖZOGUL, F.; REGENSTEIN, J.M. Industrial applications of crustacean by-products (chitin, chitosan, and chitooligosaccharides): a review. Trends Food Sci. Technol., v.48, p.40-50, 2016.
  • HAVELAAR, A.H.; KIRK, M.D.; TORGERSON, P.R.; GIBB, H.J. et al. World health organization global estimates and regional comparisons of the burden of foodborne disease in 2010. PLoS Med., v.12, pe1001923, 2015.
  • KETTA, M.; TŮMOVÁ, E. Eggshell structure, measurements, and quality-affecting factors in laying hens: a review. Czech J. Anim. Sci., v.61, p.299-309, 2016.
  • LAKE, R.J.; DEVLEESSCHAUWER, B.; NASINYAMA, G.; HAVELAAR, A.H. et al. National studies as a component of the World Health Organization initiative to estimate the global and regional burden of foodborne disease. PLoS One, v.10, pe0140319, 2015.
  • LAMAS, A.; MIRANDA, J.M.; REGAL, P.; VÁZQUEZ, B. et al. A comprehensive review of non-enterica subspecies of Salmonella enterica. Microbiol. Res., v.206, p.60-73, 2018.
  • MENCONI, A.; PUMFORD, N.R.; MORGAN, M.J.; BIELKE, L.R.; KALLAPURA, G. et al. Effect of chitosan on Salmonella typhimurium in broiler chickens. Foodborne Pathog. Dis., v.11, p.165-169, 2014.
  • PARK, G.H.; SIL, K.M.; KNOWLES, J.C.; GONG, M.S. Synthesis, characterization, and biocompatible properties of alanine-grafted chitosan copolymers. J. Biomater. Appl., v.30, p.1350-1361, 2016.
  • PARK, S.Y.; CHOI, K.S.; LEE, D.; KIM, D. et al. Eggshell membrane: review and impact on engineering. Biosyst. Eng., v.151, p.446-463, 2016.
  • PRADHAN, A.K.; SAHOO, P.K. Synthesis and study of thermal, mechanical and biodegradation properties of chitosan-g-PMMA with chicken egg shell (nano-CaO) as a novel bio-filler. Mater. Sci. Eng. C. Mater. Biol. Appl., v.80, p.149-155, 2017.
  • RANDAZZO, W.; FABRA, M.J.; FALCÓ, I.; LÓPEZ‐RUBIO, A.; SÁNCHEZ, G. SCHARFF, R.L. State estimates for the annual cost of foodborne illness. J. Food. Prot., v.78, p.1064-1071, 2015.
  • SHAH, D.H.; PAUL, N.C.; SISCHO, W.C.; CRESPO, R.; GUARD, J. Population dynamics and antimicrobial resistance of the most prevalent poultry-associated Salmonella serotypes. Poult. Sci., v.96, p.687-702, 2017.
  • SHI, B.L.; LI, D.F.; PIAO, X.S.; YAN, S.M. Effects of chitosan on growth performance and energy and protein utilisation in broiler chickens. Br. Poult. Sci., v.46, p.516-519, 2005.
  • SPSS Statistics user’s guide. Version 22.0. Armonk: IBM Corp., 2013.
  • THAKUR, V.K.; VOICU, S.I. Recent advances in cellulose and chitosan based membranes for water purification: a concise review. Carbohydr. Polymers, v.146, p.148-165, 2016.
  • VENKATARAMAN, S.; LEE, A.L.Z.; TAN, J.P.K.; CHIEN, Y.N.G. et al. Functional cationic derivatives of starch as antimicrobial agents. Polymer Chem., v.10, p.412-423, 2019.
  • VERLEE, A.; MINCKE, S.; STEVENS, C.V. Recent developments in antibacterial and antifungal chitosan and its derivatives. Carbohydr. Polymers, v.164, p.268-283, 2017.
  • YOUNES, I.; RINAUDO, M. Chitin and chitosan preparation from marine sources. Structure, properties and applications. Mar. Drugs., v.13, p.1133-1174, 2015.

Publication Dates

  • Publication in this collection
    03 Apr 2020
  • Date of issue
    Jan-Feb 2020

History

  • Received
    26 Feb 2019
  • Accepted
    02 Aug 2019
Universidade Federal de Minas Gerais, Escola de Veterinária Caixa Postal 567, 30123-970 Belo Horizonte MG - Brazil, Tel.: (55 31) 3409-2041, Tel.: (55 31) 3409-2042 - Belo Horizonte - MG - Brazil
E-mail: abmvz.artigo@gmail.com