Article • Braz. Dent. J. 30 (5) • Sep-Oct 2019 • https://doi.org/10.1590/0103-6440201902578 copiar

Bond Stability of Universal Adhesives Applied To Dentin Using Etch-And-Rinse or Self-Etch Strategies

Autoria SCIMAGO INSTITUTIONS RANKINGS

Resumo

Este estudo avaliou a resistência de união à dentina imediata e após 6 meses de adesivos universais utilizando estratégias de união convencional ou autocondicionante. Os adesivos testados foram Ambar Universal, G-Bond, Single Bond Universal, Tetric N-Bond Universal e Ybond Universal. Adesivos padrão-ouro (Scotchbond Multipurpose Plus e Clearfil SE Bond) foram os controles. Resistência de união à microtração na dentina (n=5 dentes), pH e conversão de C=C (n=3) foram avaliados. Os dados foram analisados considerando α=0,05. Todos os adesivos mostraram diferenças de pH comparados aos demais. Ybond Universal teve agressividade intermediária forte, enquanto os outros foram ultramoderados. A conversão de C=C foi diferente em quase todos adesivos. No modo convencional, em geral todos os adesivos mostraram resultados similares exceto G-Bond, que teve menor resistência de união que a maioria dos adesivos. G-Bond e Tetric-N-Bond mostraram resistências de união menores após 6 meses comparados a 24 h, enquanto os outros adesivos apresentaram estável união à dentina. No modo autocondicionante, G-Bond teve menor resistência de união que quase todos os adesivos. Após 6 meses, Ambar foi o único adesivo mostrando menor resistência de união à dentina comparado a 24 h. A maioria dos adesivos teve discreta queda na resistência de união durante o envelhecimento quando usados na estratégia autocondicionante. Os modos de falha também foram material dependentes, com um padrão geral de mais falhas adesivas e/ou pré-teste após o armazenamento. Em conclusão, o desempenho de união de adesivos universais à dentina é material dependente. Grande parte dos adesivos apresentou estável união à dentina com resultados comparáveis ao materiais padrão-ouro, particularmente quando aplicados no modo autocondicionante. Em geral, parece que o uso de adesivos universais em dentina não deve ser precedido por condicionamento com ácido fosfórico.

Adhesive	Manufacturer	Batch #	Composition*
Ambar Universal	FGM, Joinville, SC, Brazil	070116	UDMA, HEMA, methacrylate hydrophilic monomers, methacrylate acid monomers, ethanol, water, silanized silicon dioxide, camphorquinone, ethyl 4-dimethylamino-benzoate, surfactant, sodium fluoride
G-Bond	GC, Tokyo, Japan	1309181	Acetone, UDMA, dimethacrylate component, phosphoric acid ester monomer, photoinitiator
Single Bond Universal	3M ESPE, St. Paul, MN, USA	619545	MDP phosphate monomer, dimethacrylate resins, HEMA, polyalkenoic acid copolymer, filler, ethanol, water, initiators, silane
Tetric N-Bond Universal	Ivoclar Vivadent, Schaan, Liechtenstein	U42905	Ethanol, phosphonic acid acrylate, Bis-GMA, HEMA, UDMA, diphenyl (2,4,6- trimethylbenzoyl) phosphine oxide
Ybond Universal	Yller, Pelotas, RS, Brazil	2045	Hydrophilic methacrylate monomers, hydrophobic methacrylate monomers, initiators, stabilizers, silane, ethanol, water, silanized nanoparticles
Clearfil SE Bond	Kuraray, Osaka, Japan	9N0168 9U0270	Primer: MDP, dimethacrylate monomer, HEMA, silica, N,N-diethanol-p-toluidine, CQ; Bond: HEMA, dimethacrylate monomer, Bis-GMA, N,N-diethanol-p-toluidine, silica, camphorquinone
Scotchbond Multipurpose Plus	3M ESPE	N782259 N763504	Primer: Polyalkenoic acid copolymer, HEMA, water, ethanol; Bond: Bis-GMA, HEMA, tertiary amines, photoinitiator

Adhesive	Bonding strategy	Application steps
Ambar Universal	Etch-and-rinse	The dentin was acid-etched with 37% phosphoric acid for 15 s, washed with air/water spray for 15 s, excess dentin moisture water was removed with absorbent paper, a first layer of adhesive was applied and rubbed for 10 s, a second adhesive layer was applied, the solvent was evaporated with air stream for 10 s, the adhesive was photoactivated for 10 s
Ambar Universal	Self-etch	The surface was washed with air/water spray, excess dentin moisture water was removed with absorbent paper, a first layer of adhesive was applied and rubbed for 10 s, then a second adhesive layer was applied, the solvent was evaporated with air stream for 10 s, the adhesive was photoactivated for 10 s
G-Bond	Etch-and-rinse	The dentin was acid-etched with 37% phosphoric acid for 15 s, washed with air/water spray for 15 s, excess dentin moisture water was removed with absorbent paper, the adhesive was actively applied for 10 s followed by solvent evaporation with air stream for 10 s, the adhesive was photoactivated for 20 s
G-Bond	Self-etch	The surface was washed with air/water spray, excess dentin moisture water was removed with absorbent paper, the adhesive was applied and rubbed for 10 s, the solvent was evaporated with air stream for 5 s, the adhesive was photoactivated for 20 s
Single Bond Universal	Etch-and-rinse	The dentin was acid-etched with 37% phosphoric acid for 15 s, washed with air/water spray for 15 s, excess dentin moisture water was removed with absorbent paper, the adhesive was actively applied for 20 s, the solvent was evaporated with air stream for 5 s, the adhesive was photoactivated for 10 s
Single Bond Universal	Self-etch	The surface was washed with air/water spray, excess dentin moisture water was removed with absorbent paper, the adhesive was applied and rubbed for 20 s, the solvent was evaporated with air stream for 5 s, the adhesive was photoactivated for 10 s
Tetric N-Bond Universal	Etch-and-rinse	The dentin was acid-etched with 37% phosphoric acid for 15 s, washed with air/water spray for 15 s, excess dentin moisture water was removed with absorbent paper, the adhesive was actively applied for 20 s, the solvent was evaporated with air stream for 5 s, the adhesive was photoactivated for 10 s
Tetric N-Bond Universal	Self-etch	The surface was washed with air/water spray, excess dentin moisture water was removed with absorbent paper, the adhesive was applied and rubbed for 20 s, the solvent was evaporated with air stream for 5 s, the adhesive was photoactivated for 10 s
Ybond Universal	Etch-and-rinse	The dentin was acid-etched with 37% phosphoric acid for 15 s, washed with air/water spray for 15 s, excess dentin moisture water was removed with absorbent paper, two layers of adhesive were actively applied with rubbing action for 10 s each, the solvent was evaporated with air stream for 5 s after each layer was applied, the adhesive was photoactivated for 20 s
Ybond Universal	Self-etch	The surface was washed with air/water spray, excess dentin moisture water was removed with absorbent paper, two layers of adhesive were applied and each rubbed for 20 s, the solvent was evaporated with air stream for 5 s, the adhesive was photoactivated for 20 s
Scotchbond Multipurpose Plus	Etch-and-rinse	The dentin was acid-etched with 37% phosphoric acid for 15 s, washed with air/water spray for 15 s, the excess dentin moisture water was removed with absorbent paper, the primer was applied and gently air-dried with air stream for 5 s, the adhesive was applied and photoactivated for 10 s
Clearfil SE Bond	Self-etch	The surface was washed with air/water spray, excess dentin moisture water was removed with absorbent paper, the primer was applied and rubbed for 20 s, the solvent was evaporated with air stream for 5 s, the adhesive was applied and photoactivated for 20 s

Adhesive	pH	DC, %
Ambar Universal	2.47 (0.07) c	70.2 (3.7) b
G-Bond	2.55 (0.01) d	88.5 (0.5) a
Single Bond Universal	2.95 (0.05) e	33.7 (2.3) e
Tetric N-Bond Universal	3.52 (0.04) f	50.1 (1.8) d
Ybond Universal	1.40 (0.03) a	55.1 (6.0) cd
Scotchbond Multipurpose Plus	3.95 (0.01) g	61.6 (0.7) c
Clearfil SE Bond	1.83 (0.04) b	68.8 (1.4) b

Bonding strategy	Adhesive system	Storage time in water at 37°C		Average drop
Bonding strategy	Adhesive system	24 h	6 months	Average drop
Etch-and-rinse	Ambar Universal	30.0 (12.1) ^A,ab	28.1 (8.0) ^A,a	6%
	G-Bond	25.8 (5.2) ^A,b	11.8 (6.2) ^B,c	54%
	Single Bond Universal	34.8 (8.7) ^A,a	28.9 (9.7) ^A,a	17%
	Tetric-N-Bond Universal	36.0 (9.3) ^A,a	21.4 (3.1) ^B,b	40%
	Ybond Universal	27.9 (7.4) ^A,ab	31.6 (9.3) ^A,a	-13%
	Scotchbond Multipurpose Plus	34.0 (6.9) ^A,a	27.5 (9.4) ^A,ab	19%
Self-etch	Ambar Universal	40.2 (16.5) ^A,a	25.4 (7.7) ^B,ab	37%
	G-Bond	21.8 (3.0) ^A,b	21.0 (9.8) ^A,b	4%
	Single Bond Universal	31.9 (14.5) ^A,a	27.5 (6.2) ^A,a	14%
	Tetric-N-Bond Universal	34.4 (13.0) ^A,a	32.3 (5.4) ^A,a	6%
	Ybond Universal	23.8 (8.1) ^A,ab	23.1 (3.7) ^A,b	3%
	Clearfil SE Bond	34.4 (13.0) ^A,a	28.1 (10.6) ^A,a	19%

Fundação Odontológica de Ribeirão Preto Av. do Café, S/N, 14040-904 Ribeirão Preto SP Brasil, Tel.: (55 16) 3602-3982, Fax: (55 16) 3633-0999 - Ribeirão Preto - SP - Brazil
E-mail: bdj@forp.usp.br

Acompanhe os números deste periódico no seu leitor de RSS

[1] Correspondence: Prof. Rafael Moraes, Rua Gonçalves Chaves 457, 96015-560 Pelotas, RS, Brasil. Tel: +55-53-3225-6741. e-mail: moraesrr@gmail.com