Eucalyptus wood and coffee parchment for particleboard production: Physical and mechanical properties

Madeira de eucalipto e pergaminho de café na produção de aglomerados: Propriedades físicas e mecânicas

ABSTRACT

The wood panel industry is constantly growing, being necessary the innovation in technologies and raw materials to improve the quality of the final product. Considering the shortage and pressure to decrease the dependence of wood, there is an interest in other renewable materials such as agricultural wastes. Among these wastes, coffee parchment is one which deserves notoriety. An alternative use for coffee parchment could be for production of particleboard in association with wood particles. This study aimed to evaluate the feasibility of using coffee parchment for production of particleboard. The following percentages of wastes were used: 0, 10, 20, 30, 40 and 50% in association to eucalyptus wood. The panels were produced with 8% of urea formaldehyde (based on dry weight of particles). The pressing cycle consisted by: pre-pressing of 0.5 MPa for 10 minutes followed by pressing of 4.0 MPa, and temperature of 160° C for 15 minutes. The compaction ratio of particleboards produced using higher quantities of parchment improved the physical properties. The properties of Water Absorption (2 and 24 h) and Thickness Swelling (2 h) decreased with increasing percentage of coffee parchment. The Thickness Swelling (24 h) showed not significant effect with an increase of coffee waste. The Modulus of Elasticity for coffee parchment particleboards was in the range 646.49 ± 112.65 to 402.03 ± 66.24 MPa, while the Modulus of Rupture ranged from 8.18 ± 1.39 to 4.45 ± 0.75 MPa. The results showed that 10% of coffee parchment could be added for production of particleboards.

Index terms:
Agricultural waste; lignocellulosic material; renewable material

RESUMO

A indústria de painéis de madeira vem em constante crescimento, sendo necessária a inovação em tecnologias e matéria-prima para melhorar a qualidade do produto final. Considerando a escassez e pressão na diminuição da dependência por madeira, existe um interesse em outros materiais renováveis, como os resíduos agrícolas. Entre esses resíduos, o pergaminho de café merece destaque. Uma alternativa para utilização do pergaminho de café poderia ser na produção de particulados, em associação com partículas de madeira. O objetivo deste trabalho foi avaliar a viabilidade de utilização do pergaminho de café para produção de aglomerados. As porcentagens de resíduo utilizadas foram: 0, 10, 20, 30, 40 e 50% em associação com madeira de eucalipto. Os painéis foram produzidos com 8% de uréia-formaldeído (base massa seca de partículas). O ciclo de prensagem consistiu de: pré-prensagem de 0,5 MPa por 10 minutos, seguido por prensagem de 4,0 MPa e temperatura de 160° C por 15 minutos. A razão de compactação dos painéis produzidos com maiores quantidades de pergaminho melhorou as propriedades físicas. As propriedades de absorção de água (2 e 24 h) e inchamento em espessura (2 h) diminuíram com o aumento da porcentagem de pergaminho de café. O inchamento em espessura (24 h) não apresentou diferenças significativas com o aumento de resíduo de café. O Módulo de Elasticidade dos painéis variou de 646,49 ± 112,65 até 402,03 ± 66,24 MPa, enquanto o Módulo de Ruptura variou de 8,18 ± 1,39 até 4,45 ± 0,75 MPa. Os resultados mostraram que até 10% de pergaminho de café poderia ser adicionados para a produção de painéis aglomerados.

Termos para indexação:
Resíduos agrícolas; materiais lignocelulósicos; material renovável

INTRODUCTION

The brazilian industry of particleboards consumes a significant volume of wood from planted forests, mainly from Eucalyptus genera. Such species get emphasize due to the good adaptation in a large area of Brazilian territory and availability for exploring (Mendes et al., 2014MENDES, R. F. et al. Quality of homogeneous particleboard produced with Eucalyptus Urophylla clone wood. Cerne, 20(2):329-336, 2014.).

However, the growth of the sector becomes necessary to search for other lignocellulosic materials sources that may contribute to supply the needs of industries as well as contribute to the development of new products (Belini et al., 2014BELINI, U. L. et al. Multilayer panel with bamboo particles reinforcement. Scientia Forestalis, 42(103):421-427, 2014.; Farrapo et al., 2014FARRAPO, C. L. et al. Utilization of Pterocarpus violaceus wood in the particleboard production. Scientia Forestalis , 42(103):329-335, 2014.). Considering the growing concern about the environment and the pressure to decrease the wood dependence, the forestry industry seeks new substitute materials hence there is an interest in renewable materials, such as agricultural wastes generated by several crops as sugar cane, rice husk, corn and coffee, which is one of the most important in Brazil.

In 2013, the Brazilian production of coffee (green grain) was approximately 3,000,000 t, which ranks the country as the greatest world producer of coffee (FAO, 2013)FOOD AND AGRICULTURE ORGANIZATION OF THE UNITED NATIONS - FAO (2013). Available in: <Available in: http://faostat3.fao.org/browse/Q/QC/E >. Access in: 29 Aug. 2016.
http://faostat3.fao.org/browse/Q/QC/E...
. One of the wastes obtained from this culture is the coffee parchment, a byproduct which is usually discarded after the grain processing. The parchment, known as “thin rind” for being an anatomical pellicle which covers the grain, is part of the waste generated by the coffee processing obtained when the pulping occurs by wet method (Brum et al., 2008BRUM, S. S. et al. Preparation and characterization of activated carbon produced from coffee waste. Quimica Nova, 31(5):1048-1052, 2008.). According to Vilela et al. (2001VILELA, F. G. et al. Use of sticky coffee hull for feeding of steers in feedlots. Ciência e Agrotecnologia , 25(1):198-205, 2001.), coffee processing results in wastes such as husk and parchment, which yield approximately 50%. Therefore, the processing of two tons of coffee produces a ton of waste. After the grain processing, the main destination given to the coffee parchment is the briquettes and pellets production for burning and energy generation (Paula et al., 2011PAULA, L. E. R. et al. Produção e avaliação de briquetes de resíduos lignocelulósicos. Pesquisa Florestal Brasileira, 31(66):103-112, 2011.). An environmentally-friendly alternative for the coffee parchment destination could be for particleboards production.

The production of particleboards from agricultural wastes adds value to the residue, reducing the impact on the environment, furthermore, it can meet the growing demand for wood panels, enable the expansion, decrease the use of wood in the production process, the pressure on forests, while reducing production costs of the panels (Mendes et al., 2010MENDES, R. F. et al. Effect of the incorporation of coffee husks on the physico-mechanical properties of Eucalyptus urophylla S. T. Blake particleboards. Ciência e Agrotecnologia, 34(3):610-617, 2010.).

Abundantly available plants cultivated in agriculture might be good candidates, showing also anatomical and chemical structures suitable to produce panels (Mati-Baouche et al., 2014MATI-BAOUCHE, N. et al. Mechanical, thermal and acoustical characterizations of an insulating bio-based composite made from sunflower stalks particles and chitosan. Industrial Crops and Products, 58(1):244-250, 2014.;Papadopoulou et al., 2015PAPADOPOULOU, E. et al. Value-added industrial products from bast fiber cropsIndustrial Crops and Products, 68(1):116-125, 2015.). Different researchers have reported the utilization of agricultural wastes in particleboards production, such as sugarcane bagasse (Mendes et al., 2012MENDES, R. F. et al. Association effect of sugar cane bagasse, type and levels of adhesive on particleboard production. Ciência Florestal , 22(1):161-170, 2012. ), rice husk (Melo et al., 2009MELO, R. R. et al. Properties of wood and rice husk particleboard in different proportions. Ciência Florestal, 19(4):449-460, 2009.), maize cob (Scatolino et al., 2013SCATOLINO, M. V. et al. Maize cob utilization in particleboards production. Ciência e Agrotecnologia , 37(4):330-337, 2013.; Scatolino et al., 2015SCATOLINO, M. V. et al. Thermal stability of Pinus oocarpa and maize cob particleboards. Ciência e Agrotecnologia , 39(4):348-354, 2015.; bn SEKALUVU, L.; TUMUTEGYEREIZE, P.; KIGGUNDU, N. Investigation of factors affecting the production and properties of maize cob-particleboards. Waste and Biomass Valorization, 5(1):27-32, 2014.), coffee husk (Mendes et al., 2010MENDES, R. F. et al. Effect of the incorporation of coffee husks on the physico-mechanical properties of Eucalyptus urophylla S. T. Blake particleboards. Ciência e Agrotecnologia, 34(3):610-617, 2010.), peanut husk (Guler; Buyuksari 2011GULER, C.; BUYUKSARI, U. Effect of production parameters on the physical and mechanical properties of particleboards made from peanut (Arachis hypogaea L.) husk. BioResources, 6(4):5027-5036, 2011.), corn straw (Silva et al., 2015SILVA, D. W. et al. MDP with particles of eucalyptus and corn straw. Scientia Forestalis , 43(108):853-862, 2015.), vine (Vitis viniferaL.) (Yeniocak et al., 2014YENIOCAK, M. et al. Investigating the use of vine pruning stalks (Vitis Vinifera L. CV. Sultani) as raw material for particleboard manufacturing. Wood Research, 59(1):167-176, 2014.) and castor husk (Silva et al., 2016SILVA, D. W. et al. Addition of different proportions of castor husk and pine wood in particleboards. Waste and Biomass Valorization , 7(34):1-7, 2016.).

In addition, many studies in the literature show the mixture of agricultural wastes with wood species. Mendes et al. (2010MENDES, R. F. et al. Effect of the incorporation of coffee husks on the physico-mechanical properties of Eucalyptus urophylla S. T. Blake particleboards. Ciência e Agrotecnologia, 34(3):610-617, 2010.) evaluated the influence of coffee husks in association to Eucalyptus urophylla in the physical and mechanical properties of particleboard. Similarly, Silva et al. (2016SILVA, D. W. et al. Addition of different proportions of castor husk and pine wood in particleboards. Waste and Biomass Valorization , 7(34):1-7, 2016.) studied the association of castor husk and Pinus oocarpa wood for production of particleboard.

The coffee parchment could be a potential alternative material for being applied in particleboards production, due the fact of being basically composed by cellulose and lignin, such as wood. The aim of this study was to evaluate the potential of using coffee parchment as raw material for particleboard production associated with eucalyptus wood considering the physical and mechanical properties.

MATERIAL AND METHODS

Raw material and particle processing

The coffee parchments were provided by a cooperative company located in the district of Machado, Minas Gerais State, Brazil. The eucalyptus was a Eucalyptus urophylla x Eucalyptus grandis hybrid collected from a dense crop located in the campus of Federal University of Goiás, in Jataí, Goiás State, Brazil. 36 months-old eucalyptus trees were used in this study. The eucalyptus wood was subjected to analysis for determining basic density values according to procedures in standard NBR 11941 (ABNT, 2003aBRAZILIAN ASSOCIATION OF TECHNICAL STANDARDS - ABNT - NBR 11941: Wood - Determination of basic density. Rio de Janeiro. 2003a. 6p.).

The basic density of coffee parchment was obtained by saturation of particles and subsequent volume measurement in a measuring cylinder. The particles were then dried and the relation dry weight/saturated volume was calculated. The wood particles were obtained by crushing of small logs through a Kawashima Tg 1400-s (100 mm) mill. Posteriorly, the particles were crushed again through a mill containing a 6 mm sieve. Coffee parchment was separated from the grain processing impurities and crushed through a mill. The particles were sieved and the fraction that was retained between the 20 (0.841 mm) and 40 mesh (0.420 mm) were used for production of particleboards.

Chemical analysis of materials

For analysis of the chemical components of eucalyptus and coffee parchment, the sawdust retained between the 40 (0.420 mm) and 60 (0.250 mm) mesh sieves was used. The material was subjected to analysis for determining the total extractives content - NBR 14853 (ABNT, 2010aBRAZILIAN ASSOCIATION OF TECHNICAL STANDARDS - ABNT - NBR 14853: Determination of soluble matter in ethanol-toluene and in dichloromethane and in acetone. Rio de Janeiro. 2010a. 3p.), lignin content - NBR 7989 (ABNT, 2010bBRAZILIAN ASSOCIATION OF TECHNICAL STANDARDS - ABNT - NBR 7989: Pulp and wood - Determination of acid-insoluble lignin. Rio de Janeiro. 2010b. 6p.), minerals content - NBR 13999 (ABNT, 2003bBRAZILIAN ASSOCIATION OF TECHNICAL STANDARDS - ABNT - NBR 13999: Paper, board, pulps and wood - Determination of residue (ash) on ignition at 525 °C. Rio de Janeiro. 2003b. 4p.) and holocellulose content (obtained by the difference H (%) = 100 - %Total extractives - %Lignin content - %Ashes content).

Experimental design and production of particleboards

The experimental design consisted of six treatments (Table 1), which five percentages of coffee parchment were used in replacement of eucalyptus.

Table 1:
Experimental design for particleboard production.

The panels were produced with dimensions of 200 x 200 x 15 mm (length, width and thickness, respectively). The level of urea-formaldehyde (UF) adhesive was 8% (based on dry weight of particles). The properties of UF were: solid content 66.07%, pH 8.94 and viscosity 479 cP. The particles were manually added to adhesive. The mixture was placed into a sheet mold and pre-pressed at 0.5 MPa during 10 minutes. The resulting sheet was then subjected to a hot compression cycle at temperature of 160 °C, pressure of 4 MPa for 15 minutes. Two panels were produced for each treatment.

Evaluation of panels and statistical analysis

Once panels were acclimatized at a temperature of 22 ± 2 °C and 65 ± 5% of relative humidity, test samples were obtained using a circular saw. The compaction ratio was obtained by applying the following equation:

C R = p d c p d x ( c p % ) + e w d x ( e w % ) MathType@MTEF@5@5@+= feaagKart1ev2aaatCvAUfeBSjuyZL2yd9gzLbvyNv2CaerbuLwBLn hiov2DGi1BTfMBaeXatLxBI9gBaerbd9wDYLwzYbItLDharqqtubsr 4rNCHbGeaGqiVu0Je9sqqrpepC0xbbL8F4rqqrFfpeea0xe9Lq=Jc9 vqaqpepm0xbba9pwe9Q8fs0=yqaqpepae9pg0FirpepeKkFr0xfr=x fr=xb9adbaqaaeGaciGaaiaabeqaamaabaabaaGcbaGaam4qaiaadk facqGH9aqpdaWcaaqaaiaadchacaWGKbaabaGaam4yaiaadchacaWG KbGaaeiiaiaadIhacaqGGaGaaiikaiaadogacaWGWbGaaiyjaiaacM cacqGHRaWkcaWGLbGaam4DaiaadsgacaqGGaGaamiEaiaabccacaGG OaGaamyzaiaadEhacaGGLaGaaiykaaaaaaa@4D4D@

where: pd is the particleboard apparent density (g/cm3); cpd is the basic density of coffee parchment (g/cm3); cp% is the content of coffee parchment; ewd is the basic density of eucalyptus wood (g/cm3); and ew% is the content of eucalyptus wood.

Analyses of the properties Water Absorption after two and twenty-four hours of immersion (WA2h and WA24h), Thickness Swelling after two and twenty-four hours of immersion (TS2h and TS24h) and Internal Bond (IB) were based on standard American Society for Testing and Materials - ASTM - D1037 (2006)AMERICAN SOCIETY FOR TESTING AND MATERIALS ASTM D - 1037. Standard Test Methods for Evaluating Properties of Wood-Base Fiber and Particle Panel Materials. 2006. , while analyses of the properties Modulus of Rupture (MOR) and Modulus of Elasticity (MOE) were based on standard DIN 52362 (1982NORMEN FUR HOLZFASERPLATEN SPANPLATTEN SPERRHOLZ DIN 52362: Testing of wood chipboards bending test, determination of bending strength. 1982.).

The experiment used a completely randomized design. As the objective of this study was to verify variations in results of physical and mechanical properties as a function of increasing coffee parchment percentage, data were subjected to ANOVA and analysis of regression, both at 5% significance level.

RESULTS AND DISCUSSION

Characterization of lignocellulosic materials and particleboards

The contents of extractives, lignin, minerals and holocellulose in wood and coffee waste were listed inTable 2. The lignin content was very similar for both materials, in the range from 27.27 to 28.32%. Lignin is responsible for providing mechanical and biological resistance, and has hydrophobic properties necessary for the functioning of the conductive water cell (Neutelings, 2011NEUTELINGS, G. Lignin variability in plant cell walls: Contribution of new models. Plant Science, 181(4):379-386, 2011.).

Table 2:
Chemical composition of the studied materials and some lignocellulosic biomass.

The higher content of extractives in parchment in comparison to wood was considerable, in range from 3.59 to 26.24%. Extractives are hydrophobic compounds of low molecular weight which can occur in minimal or significant levels and depend of the species and geographical location of plants (Hardell; Nilvebrant, 1999HARDELL, H. L.; NILVEBRANT, N. O. A rapid method to discrimination between free and esterified fatty acids by pyrolytic methylati on using tetramethyl ammonium acetate or hydroxide. Journal of Analytical and Applied Pyrolysis, 52(1):1-14, 1999.). Higher values of extractives in lignocellulosic raw materials are related to decreased permeability and hygroscopicity of the material (Iwakiri, 2005IWAKIRI, S. Painéis de madeira reconstituída. Curitiba: UFPR, 2005, 274p.). Other agricultural wastes reported in literature also showed extractives content much lower than the coffee parchment. Scatolino et al. (2013SCATOLINO, M. V. et al. Maize cob utilization in particleboards production. Ciência e Agrotecnologia , 37(4):330-337, 2013.) found 7.0% for extractives when studying maize cob chemical composition. Oppositely, Silva et al. (2016SILVA, D. W. et al. Addition of different proportions of castor husk and pine wood in particleboards. Waste and Biomass Valorization , 7(34):1-7, 2016.) found values of 30.1%, which were according to the waste studied in this research.

The hygroscopicity of the extractives found in coffee parchment in addition to higher compaction ratio of particleboards with higher content of waste (Table 3) could be a crucial factors for reducing the WA2h and WA24h values (Figures 1 and 2). Another factor which may have contributed to the improvement of the physical properties is the lower value holocellulose presented by the waste, which indicates a lower value of hemicelluloses.

Table 3:
Mean apparent density and compaction ratio of panels.

Figure 1
Mean values of WA2h as a function of coffee parchment percentage.

Figure 2
Mean values of WA24h as a function of coffee parchment percentage.

In both cases, there was a trend of reduction in WA values with the addition of coffee parchment in particleboards. This was assumed to be due to the higher extractives amount present in coffee parchment, which may have increased the hydrophobic characteristics of the particleboards produced with the addition of the waste. The board composed by 0% of coffee parchment, in other hand, showed less resistance against the water penetration and showed the highest WA values. Mendes et al. (2010MENDES, R. F. et al. Effect of the incorporation of coffee husks on the physico-mechanical properties of Eucalyptus urophylla S. T. Blake particleboards. Ciência e Agrotecnologia, 34(3):610-617, 2010.) also found an increasing tendency for water absorption after twenty-four hours of immersion when evaluating particleboard panels produced with coffee husk in association with eucalyptus. Boards produced in the same range of density from cotton stalks are reported to show 83.8% and 105.4% for WA2h and WA24h, respectively (Guler and Ozen, 2004GULER, C.; OZEN, R. Some properties of particleboards made from cotton stalks (Gossypium hirsitum L.). Holz Roh Werkst, 62(1):40-43, 2004.). The apparent densities of particleboards in this study ranged from 0.50 to 0.54 g/cm³, which rank them as low density particleboards (until 0.55 g/cm³) according to NBR 14810 (ABNT, 2013BRAZILIAN ASSOCIATION OF TECHNICAL STANDARDS - ABNT - NBR 14810: Medium density particleboards Part 2: Requirements and test methods. Rio de Janeiro. 2013. 69p.).

An increase in coffee parchment content of particleboards resulted in higher compaction ratio values. This fact may be certainly explained by the low value of basic density found for coffee parchment (0.100 g/cm³) in comparison to eucalyptus wood (0.450 g/cm³). Low density is one of requirements in intention to use lignocellulosic materials for particleboards production. It results in higher number of particles compressed in the same volume thus increasing the compression ratio (Iwakiri, 2005IWAKIRI, S. Painéis de madeira reconstituída. Curitiba: UFPR, 2005, 274p.). Only the treatments composed by 0 to 30% coffee parchment (not statistically different) and 40% were according to the ideal values of compaction ratio (1.3 to 1.6) indicated by Maloney (1993MALONEY, T. M. Modern particleboard and dry-process fiberboard manufacturing. San Francisco: Miller Freeman, 1993.).

The higher values for compaction ratio obtained by the other treatments may have affected the other physical properties. The plots of TS2h and TS24h versus coffee parchment content levels are shown in Figures 3 and 4, respectively.

Figure 3
Mean values of TS2h as a function of coffee parchment percentage in panels

Figure 4
Mean values of TS24h as a function of coffee parchment percentage in panels

The TS2h of particleboards in this study ranged from 11.78 to 6.77%. Somehow, the addition of coffee parchment in particleboards caused a decreasing trend in values of thickness swelling. This was assumed to be due the higher extractives amount present in coffee parchment, which decreased the hydrophilic characteristics of the particleboards produced with higher contents of the waste.

Decreases in TS2h trend with increases in the proportion of alternative biomass mixed with wood for particleboard production have already been reported in the literature. The authors found mean value for TS2h of 25.33% in particleboards composed by 50% pine wood and 50% maize cob (Scatolino et al., 2013SCATOLINO, M. V. et al. Maize cob utilization in particleboards production. Ciência e Agrotecnologia , 37(4):330-337, 2013.), which was higher than 50% coffee parchment obtained in this study. The low density of panels implies in lower content of particles for absorbing water, therefore the panels produced in this study showed lower values for physical properties in comparison to panels showing medium density found in the literature.

In other hand, the addition of coffee parchment on particleboards showed no significant effect on values of TS24h. None of the treatments exceeded the requirement for TS24h (30%) considering low density panels by standard CS 236-66 (CS, 1968COMMERCIAL STANDARD - CS 236-66: Mat formed wood particle board. 1968.).

The physical properties were improved with the addition of coffee parchment to the particleboards. In addition to the extractives content, another relevant point was the increasing in compaction ratio (See table 3), which can promote a barrier for water adhesion. However, high values of compaction ratio means a lower amount of adhesive per particle, due the low density of the coffee parchment. This fact may affect the mechanical properties of panels. The linear regression models obtained for MOE and MOR were significant (p ≤ 0.05) such as the second order polynomial regression obtained for IB. The results are illustrated in Figures 5, 6 and 7.

Figure 5
Mean values of MOE as a function of coffee parchment percentage in panels

Figure 6
Mean values of MOR as a function of coffee parchment percentage in panels

Figure 7
Mean values of IB as a function of coffee parchment percentage in panels

The MOE values showed decreasing trend according to the linear regression model. The MOR values of particleboards produced in this study ranged from 8.16 to 4.42 MPa. As similarly occurred for MOE, a higher content of coffee parchment associated to eucalyptus wood seem to reduce significantly the MOR values. IB showed an increasing trend until the content of 30% coffee parchment. From this point on, the values started to decline. Güler and Buyüksari (2011)GULER, C.; BUYUKSARI, U. Effect of production parameters on the physical and mechanical properties of particleboards made from peanut (Arachis hypogaea L.) husk. BioResources, 6(4):5027-5036, 2011. found values close to 0.16 MPa for internal bond when evaluating particleboards produced with peanut husk. The IB strength is an indicator of the cohesion of the panel in the direction perpendicular to the plane of the panel (Andre et al., 2008ANDRÉ, N. et al. Prediction of internal bond strength in a medium density fiberboard process using multivariate statistical methods and variable selection. Wood Science and Technology,42(7):521-534, 2008. ).

The reason for decreasing of MOE and MOR values, such as seen for IB (40 and 50% coffee parchment) may be related to the increase of compaction ratio. As previously explained, higher compaction ratio (See Table 3) implies a higher quantity of particles for being bonded with the same amount of adhesive, resulting in a lower amount of adhesive per particle.

Decreases in MOE and MOR trend with increases in the proportion of agricultural wastes mixed with wood for particleboard production have already been reported in the literature (Mendes et al., 2010MENDES, R. F. et al. Effect of the incorporation of coffee husks on the physico-mechanical properties of Eucalyptus urophylla S. T. Blake particleboards. Ciência e Agrotecnologia, 34(3):610-617, 2010.; Scatolino et al., 2013SCATOLINO, M. V. et al. Maize cob utilization in particleboards production. Ciência e Agrotecnologia , 37(4):330-337, 2013.). Güler and Buyüksari (2011)GULER, C.; BUYUKSARI, U. Effect of production parameters on the physical and mechanical properties of particleboards made from peanut (Arachis hypogaea L.) husk. BioResources, 6(4):5027-5036, 2011. found values close to 2.90 MPa for MOR and 571.20 for MOE when evaluating low density particleboards produced with peanut husk. Sekaluvu, Tumutegyereize, and Kiggundu (2014SEKALUVU, L.; TUMUTEGYEREIZE, P.; KIGGUNDU, N. Investigation of factors affecting the production and properties of maize cob-particleboards. Waste and Biomass Valorization, 5(1):27-32, 2014.) evaluated low density particleboards composed by maize cob particles and found means of 10 MPa for MOE and 0.6 MPa for MOR.

According to the commercial standard CS 236-66 (1968)COMMERCIAL STANDARD - CS 236-66: Mat formed wood particle board. 1968., the particleboards produced with urea formaldehyde adhesive and low density must provide minimum value of 5.5 MPa for MOR, which just was reached by 0, 10 and 40% coffee parchment. For MOE, the same standard requires minimum of 1029.7 MPa, which has not been reached by any of the treatments produced. However, the particleboards composed by 0, 10 and 40% of waste meet the minimum required by ANSI A208 (1999)AMERICAN NATIONAL STANDARD PARTICLEBOARD - ANSI A208.1 Particleboard. 1999. 11p., which is 550 MPa. All values for IB were higher than the minimum required by the standard CS 236-66 (0.14 MPa), for low density panels.

CONCLUSIONS

Coffee parchment significantly improved the physical properties of WA and TS of particleboards. The panels composed by 40% coffee parchment showed better physical properties. The panels had significant decreases in mechanical properties MOR and MOE, however the values meet the minimum required by standards such as IB. Overall, there was a loss of mechanical strength of particleboard with coffee parchment addition. By the values of physical and mechanical properties, it can be concluded that the coffee parchment in association to eucalyptus wood for production of particleboard was viable with addition until 10%, since these panels have reached the minimum of mostly standards. This waste can be used as alternative renewable raw material and promising to the declining wood supply in Brazil.

ACKNOWLEDGEMENTS

The authors thank to Fundação de Amparo à Pesquisa do Estado de Minas Gerais - FAPEMIG. Coordenacão de Aperfeiçoamento de Pessoa de Nível Superior - CAPES. Conselho Nacional de Desenvolvimento Científico e Tecnológico - CNPq, Brazilian Research Network in Lignocellulosic Composites and Nanocomposites - RELIGAR and PPGBiomat - Programa de Pós-Graduação em Engenharia de Biomateriais

REFERENCES

  • AMERICAN NATIONAL STANDARD PARTICLEBOARD - ANSI A208.1 Particleboard. 1999. 11p.
  • AMERICAN SOCIETY FOR TESTING AND MATERIALS ASTM D - 1037. Standard Test Methods for Evaluating Properties of Wood-Base Fiber and Particle Panel Materials. 2006.
  • ANDRÉ, N. et al. Prediction of internal bond strength in a medium density fiberboard process using multivariate statistical methods and variable selection. Wood Science and Technology,42(7):521-534, 2008.
  • BELINI, U. L. et al. Multilayer panel with bamboo particles reinforcement. Scientia Forestalis, 42(103):421-427, 2014.
  • BRAZILIAN ASSOCIATION OF TECHNICAL STANDARDS - ABNT - NBR 13999: Paper, board, pulps and wood - Determination of residue (ash) on ignition at 525 °C. Rio de Janeiro. 2003b. 4p.
  • BRAZILIAN ASSOCIATION OF TECHNICAL STANDARDS - ABNT - NBR 14810: Medium density particleboards Part 2: Requirements and test methods. Rio de Janeiro. 2013. 69p.
  • BRAZILIAN ASSOCIATION OF TECHNICAL STANDARDS - ABNT - NBR 14853: Determination of soluble matter in ethanol-toluene and in dichloromethane and in acetone. Rio de Janeiro. 2010a. 3p.
  • BRAZILIAN ASSOCIATION OF TECHNICAL STANDARDS - ABNT - NBR 7989: Pulp and wood - Determination of acid-insoluble lignin. Rio de Janeiro. 2010b. 6p.
  • BRAZILIAN ASSOCIATION OF TECHNICAL STANDARDS - ABNT - NBR 11941: Wood - Determination of basic density. Rio de Janeiro. 2003a. 6p.
  • BRUM, S. S. et al. Preparation and characterization of activated carbon produced from coffee waste. Quimica Nova, 31(5):1048-1052, 2008.
  • COMMERCIAL STANDARD - CS 236-66: Mat formed wood particle board. 1968.
  • FARRAPO, C. L. et al. Utilization of Pterocarpus violaceus wood in the particleboard production. Scientia Forestalis , 42(103):329-335, 2014.
  • FOOD AND AGRICULTURE ORGANIZATION OF THE UNITED NATIONS - FAO (2013). Available in: <Available in: http://faostat3.fao.org/browse/Q/QC/E >. Access in: 29 Aug. 2016.
    » http://faostat3.fao.org/browse/Q/QC/E
  • GULER, C.; BUYUKSARI, U. Effect of production parameters on the physical and mechanical properties of particleboards made from peanut (Arachis hypogaea L.) husk. BioResources, 6(4):5027-5036, 2011.
  • GULER, C.; OZEN, R. Some properties of particleboards made from cotton stalks (Gossypium hirsitum L.). Holz Roh Werkst, 62(1):40-43, 2004.
  • HARDELL, H. L.; NILVEBRANT, N. O. A rapid method to discrimination between free and esterified fatty acids by pyrolytic methylati on using tetramethyl ammonium acetate or hydroxide. Journal of Analytical and Applied Pyrolysis, 52(1):1-14, 1999.
  • IWAKIRI, S. Painéis de madeira reconstituída. Curitiba: UFPR, 2005, 274p.
  • MALONEY, T. M. Modern particleboard and dry-process fiberboard manufacturing. San Francisco: Miller Freeman, 1993.
  • MATI-BAOUCHE, N. et al. Mechanical, thermal and acoustical characterizations of an insulating bio-based composite made from sunflower stalks particles and chitosan. Industrial Crops and Products, 58(1):244-250, 2014.
  • MELO, R. R. et al. Properties of wood and rice husk particleboard in different proportions. Ciência Florestal, 19(4):449-460, 2009.
  • MENDES, R. F. et al. Effect of the incorporation of coffee husks on the physico-mechanical properties of Eucalyptus urophylla S. T. Blake particleboards. Ciência e Agrotecnologia, 34(3):610-617, 2010.
  • MENDES, R. F. et al. Association effect of sugar cane bagasse, type and levels of adhesive on particleboard production. Ciência Florestal , 22(1):161-170, 2012.
  • MENDES, R. F. et al. Quality of homogeneous particleboard produced with Eucalyptus Urophylla clone wood. Cerne, 20(2):329-336, 2014.
  • NEUTELINGS, G. Lignin variability in plant cell walls: Contribution of new models. Plant Science, 181(4):379-386, 2011.
  • NORMEN FUR HOLZFASERPLATEN SPANPLATTEN SPERRHOLZ DIN 52362: Testing of wood chipboards bending test, determination of bending strength. 1982.
  • PAULA, L. E. R. et al. Produção e avaliação de briquetes de resíduos lignocelulósicos. Pesquisa Florestal Brasileira, 31(66):103-112, 2011.
  • PAPADOPOULOU, E. et al. Value-added industrial products from bast fiber cropsIndustrial Crops and Products, 68(1):116-125, 2015.
  • SCATOLINO, M. V. et al. Maize cob utilization in particleboards production. Ciência e Agrotecnologia , 37(4):330-337, 2013.
  • SCATOLINO, M. V. et al. Thermal stability of Pinus oocarpa and maize cob particleboards. Ciência e Agrotecnologia , 39(4):348-354, 2015.
  • SEKALUVU, L.; TUMUTEGYEREIZE, P.; KIGGUNDU, N. Investigation of factors affecting the production and properties of maize cob-particleboards. Waste and Biomass Valorization, 5(1):27-32, 2014.
  • SILVA, D. W. et al. MDP with particles of eucalyptus and corn straw. Scientia Forestalis , 43(108):853-862, 2015.
  • SILVA, D. W. et al. Addition of different proportions of castor husk and pine wood in particleboards. Waste and Biomass Valorization , 7(34):1-7, 2016.
  • VILELA, F. G. et al. Use of sticky coffee hull for feeding of steers in feedlots. Ciência e Agrotecnologia , 25(1):198-205, 2001.
  • YENIOCAK, M. et al. Investigating the use of vine pruning stalks (Vitis Vinifera L. CV. Sultani) as raw material for particleboard manufacturing. Wood Research, 59(1):167-176, 2014.

Publication Dates

  • Publication in this collection
    Mar-Apr 2017

History

  • Received
    02 Oct 2016
  • Accepted
    06 Dec 2016
Editora da Universidade Federal de Lavras Editora da UFLA, Caixa Postal 3037 - 37200-900 - Lavras - MG - Brasil, Telefone: 35 3829-1115 - Lavras - MG - Brazil
E-mail: revista.ca.editora@ufla.br