Interaction of dental pulp stem cells with Biodentine and MTA after exposure to different environments

ABSTRACT

Objective:

The aim of the present study was to evaluate and compare the cytotoxic effects of Biodentine and MTA on dental pulp stem cells (DPSCs) and to assess cell viability and adherence after material exposure to an acidic environment.

Material and Methods:

DPSCs were cultured either alone or in contact with either: Biodentine; MTA set for 1 hour; or MTA set for 24 hours. After 4 and 7 days, cell viability was measured using the MTT assay. Biodentine and MTA were also prepared and packed into standardized bovine dentin disks and divided into three groups according to the storage media (n=6/group): freshly mixed materials without storage medium (Group A); materials stored in saline (Group B); materials stored in citric acid buffered at pH 5.4 (Group C). After 24 hours, DPSCs were introduced in the wells and cell adherence, viability, and cellular morphology were observed via confocal microscopy after three days of culture. Cell viability was analyzed using repeated-measures analysis of variance test with Tukey's post hoc tests (α=0.05).

Results:

Biodentine expressed significantly higher cell viability compared with all other groups after 4 days, with no differences after 7 days. Notably, cell viability was significantly greater in 24-hour set MTA compared with 1-hour set MTA and control groups after 7 days. Material exposure to an acidic environment showed an increase in cell adherence and viability in both groups.

Conclusions:

Biodentine induced a significantly accelerated cell proliferation compared with MTA. Setting of these materials in the presence of citric acid enhanced DPSC viability and adherence.

Keywords:
Acidic environment; Biodentine; Cytotoxicity; MTA; Dental pulp stem cells

INTRODUCTION

Mineral trioxide aggregate (MTA) is a calcium silicate-based material and has attracted considerable attention because of its excellent biocompatibility, sealing ability, and antimicrobial properties²⁰,²⁹. Although it was initially introduced as a material for repair of root perforations, it is currently used in vital pulp therapy, as a root-end filling material, as an apical plug in apexification procedures, and in regenerative endodontic therapy¹²,¹⁵,²⁸. Despite its broad spectrum of clinical indications, MTA comes with certain limitations including long setting time, difficult handling, possibility of crown staining, and high cost⁴,²⁰.

Biodentine (Septodont, Saint Maur des Fosses, France), a new calcium silicate-based restorative cement, was recently introduced for endodontic procedures. This bioceramic material is a fast-setting restorative material recommended as a dentin substitute that can be used in similar applications such as MTA¹⁴. Materials that are intended for endodontic applications should stimulate repair or be biologically neutral in order to promote healing⁶. If, however, endodontic materials are cytotoxic, they can negatively influence the viability of cells and cause cell death by apoptosis or necrosis⁸. Although there is evidence about the excellent biocompatibility of MTA⁵,²⁵,²⁹, limited information is available about the possible cytotoxicity of Biodentine²,¹³,¹⁴,¹⁷.

Clinicians often face the challenge of placing materials in a low pH environment due to the presence of inflammation¹⁸. Variations in the pH at the time of placement could affect the physical and chemical properties of both MTA and Biodentine⁵,¹⁹,²⁴,³¹. It has been shown that the low pH of the surrounding microenvironment affects the hydration reaction of MTA¹⁶, and that the more acidic the MTA solution during the setting process is, the more extensive its porosity will be¹⁹. However, limited scientific data exist about the viability and adherence of cells to these materials after the exposure to an acidic environment.

The primary aim of this study was to evaluate the viability of dental pulp stem cells (DPSCs) when in contact with Biodentine in comparison with MTA. The secondary aim was to examine whether the presence of these materials in an acidic environment could have an effect on the DPSCs viability and adherence to these materials.

MATERIAL AND METHODS

Cell culture

Human DPSCs were provided by ProCell, Biotechnological Application SA (Athens, Greece). The cells were screened with Flow Cytometry for mesenchymal surface markers. The triple panel of protein CD73, CD90, and CD105, which by consensus is expressed in mesenchymal stem cells, was detected in high levels (>85%). Moreover, the cells were negative for CD45 (hematopoietic cell marker), CD34 (hematopoietic stem cell marker), and CD31 (endothelial cell marker). DPSCs were cultured in basal culture media composed of Dulbecco's Modified Eagle's Medium (DMEM; Gibco, Glasgow, UK) supplemented with 10% fetal bovine, 1X L-glutamine (Gibco), penicillin (100 U/mL; Gibco) and streptomycin (100 mg/mL; Gibco). After reaching 70–80% confluency, cell were treated with 0.05% trypsin (Gibco, Carlsbad, CA, USA) and passed to subsequent culture plates or used in experiments. Cells from third to fifth passage were utilized in this study.

Cell viability

White ProRoot MTA (Dentsply Tulsa Dental Specialties, Memphis, TN, USA) and Biodentine (Septodont, Saint Maur des Fosses, France) were prepared according to the manufacturer's instructions and placed at the bottom of a 48-well plate (n=5/group). Materials were placed at a 2 mm thickness and fully coverage of the bottom of the well was confirmed for all groups. Immediately after placement, materials were allowed to set for one hour at 37°C in 5% CO₂ and 100% humidity under sterile conditions and 1×10⁴ DPSCs were introduced in each well in direct contact with the materials. To account for the difference in setting time between the testing materials, a group of 24-hour set ProRoot MTA (MTA24h) was also included (n=5). MTA was allowed to set for 24 hours under the same conditions described above before DPSCs were introduced. All groups were incubated at 37°C in 5% CO₂ and 100% humidity for 4 and 7 days. Cells without materials served as control. Cell viability was measured using methylthiazolyldiphenyl-tetrazolium bromide (MTT) based cell growth determination kit (Sigma Aldrich, St. Louis, MO) according to the manufacturer's instructions. Relative absorbance (λ=570 nm) for each group was detected in a FlexStation 3 Benchtop Multimode Microplate Reader (Molecular Devices, Sunnyvale, CA, USA).

Specimen preparation for immunofluorescence

36 dentin disks from anterior bovine teeth were horizontally sectioned into 3-mm slices using an Isomet device (Buehler Ltd., Lake Bluff, IL, USA) and the canal space of each dentin slice was enlarged to 2.6 mm in diameter. Biodentine and MTA were prepared according to the manufacturers' instructions under aseptic conditions and packed into the lumen of dentin disks (N=18/group). Specimens from each material group were further divided into three groups according to the storage media and placed in 24-well plates – Group A: freshly mixed materials without storage; Group B: materials with saline as storage medium; Group C: materials with citric acid buffered at pH 5.4 as storage medium (n=6/group). Each specimen was kept in contact with a saline- or citric acid-soaked piece of gauze for 24 hours in room temperature.

Immunofluorescence and confocal microscopy

After 24 hours of storage, 2.5×10⁴ DPSCs were introduced in the wells in direct contact with the dentin disks. Groups were cultured for 72 hours at 37°C in a 5% CO₂ humidified incubator. The cells that adhered to the surface of the samples were fixed in 4% PFA for 20 minutes at room temperature, followed by 0.1 M PBS washing twice for 10 minutes. The samples were then stained using Phalloidin-Rhodamin solution (Molecular Probes, ThermoFisher Scientific, Grand Island, NY, USA) at 37°C following manufacturer's protocol to reveal the cytoskeleton and more specifically the actin filaments of the cells. 4′,6-diamidino-2-phenylindole (DAPI, Vectashield H-1200, Vector Laboratories Inc., CA, USA) was added to stain cell nuclei. Samples were viewed with a microscope with Vectashield's coverslips (VECTOR Laboratories, Peterborough, UK), observed under the confocal microscope Leica TCS SP5 (Leica, Wetzlar, Germany), and processed using Leica software, LAS AF (Leica Microsystems GmbH, Wetzlar, Germany).

Statistical analysis

Data for the cell viability assay were analyzed using one-way repeated analysis of variance (ANOVA) with Tukey's post hoc tests to assess pairwise differences. The level of statistical significance was set at a=0.05. The Brown-Forsythe test was performed to assess equality of group variances prior to performing ANOVA. JMP software (SAS Institute, Cary, NC, USA) and Prism 6 (Graph Pad, La Jolla, CA, USA) were used for data analysis. Mean and standard deviation (mean±SD) were reported for summary statistics.

RESULTS

Results from the MTT cell viability assay are shown in Figure 1. Biodentine group expressed significantly higher mean cell viability (0.19±0.03) compared with all other groups after 4 days (all p<0.01). MTA showed significantly lower cell viability (0.03±0.01) after 4 days compared with control group (0.11±0.05) (p=0.01). After 7 days, MTA24h showed significantly higher cell viability (0.51±0.23) compared with MTA (0.06±0.03) (p=0.002) and control group (0.13±0.02) (p=0.009). There was no statistically significant difference between Biodentine and all other groups after 7 days. Intragroup comparisons showed that MTA24h allowed for significant cell viability from 4 to 7 days (p=0.014). A more detailed presentation of the significant intergroup and intragroup pairwise differences is presented in Table 1.

Figure 1
Cell viability as measured by absorbance of human DPSCs after cultured in 24-well plates either alone (control) or in contact with 1-hour set Biodentine (Biodentine), 1-hour set MTA (MTA), or 24-hour set MTA (MTA24h) for 4 and 7 days. Point estimates show mean values for each group and error bars depict standard error. Asterisks denote statistical differences in cell viability between the Biodentine and control group and statistical difference between MTA control and group after 4 days. For the 7-day time point, asterisks denote statistical difference betweenMTA24h and control groups. *P<0.05. **p<0.01

Table 1
Summary of the significant intergroup and intragroup pairwise differences in cell viability for the different time points. Mean difference, standard error of mean, and p-value are summarized for each comparison.

Absorbance (4 days)		Mean difference	Standard error of mean	p-value
Biodentine	MTA	0.162	0.021	<0.0001*
Biodentine	MTA24h	0.111	0.021	0.0005*
Biodentine	Control	0.084	0.021	0.0059*
Control	MTA	0.078	0.021	0.0113*
Absorbance (7 days)		Mean difference	Standard error of mean	p-value
MTA24h	MTA	0.447	0.101	0.0023*
MTA24h	Control	0.374	0.101	0.0099*
Absorbance (intragroup differences)		Mean difference	Standard error of mean	p-value
MTA24h (7 days)	MTA24h (4 days)	0.426	0.103	0.0146*

• ^*
  p<0.05

DPSCs adhered to the surface of dentin disks filled with MTA or Biodentine in all storage media (Figure 2). A higher cell density was observed in the samples of the acidic environment (Figures 2C, 2F) when compared with saline or no storage media. Notably, Biodentine stored in citric acid demonstrated greater amount of adherent cells, thus confirming our results of the cell viability assays. Regarding cell morphology, the cells on materials stored in citric acid demonstrated a typical fibroblast-like appearance with elongated cytoskeleton, whereas cells on materials stored in saline, especially in the Biodentine group, showed similar profiles with milder spindle-shape formation (Figures 2B, 2E).

Figure 2
Representative images of the cell cultures on the surface of the different dental materials by confocal microscopy. (A) MTA in no storage media, (B) MTA stored in saline, (C) MTA stored in citric acid, (D) Biodentine in no storage media, (E) Biodentine stored in saline, (F) Biodentine stored in citric acid. Nuclei are identified by DAPI staining (blue). Actin filaments (red) show DPSC adherence and morphology

DISCUSSION

Materials introduced in procedures, such as vital pulp therapies, regenerative endodontic therapies, or perforation repairs, should primarily possess biocompatibility. MTA is commonly used in such procedures, since it is considered highly biocompatible²⁵. Biodentine, a new calcium silicate-based material, has demonstrated biocompatibility when tested on various cell lines with better handling properties and a shorter setting time when compared with MTA²,¹³,¹⁴,¹⁷. Nevertheless, limited evidence is available regarding Biodentine interactions with dental pulp stem cells²¹,³³. This study aimed to investigate the biocompatibility of Biodentine in comparison with MTA on DPSCs in a time course of 4 and 7 days as well as the cell adherence to these materials after exposure to an acidic environment.

Among various advantageous properties of Biodentine is the faster setting time compared with MTA²². To compensate for the differences in setting time between the two materials and have comparable results in cell viability, setting-time points of 1 hour and 24 hours were applied for MTA. Results from the cytotoxicity assays after 4 days demonstrated significant DPSC viability when in contact with Biodentine as compared with the other groups. Our data are in consensus with Widbiller, et al.³² (2016) who showed that DPSC viability on MTA was significantly lower when compared with that of cells on Biodentine for the first seven days. Nevertheless, other studies have compared the cell viability of human pulp fibroblasts, human gingival fibroblasts, or osteoblast-like cells exposed to Biodentine or MTA and observed similar cell growth without statistically significant differences²,¹³,¹⁴. Interestingly, one-hour set MTA was significantly cytotoxic compared with control after 4 days and MTA set for 24 hours demonstrated significantly greater cell viability compared with one-hour set MTA after 7 days. These findings agree with results from a previous study, which showed that apical papilla stem cells expressed significantly greater viability when exposed to 24-hour set MTA as compared with 1-hour set MTA²⁶. One possible explanation is that initial release of calcium-ions as well as the presence of leachable and toxic components from fresh MTA may affect the behavior of the cells. It is reported that freshly mixed calcium-silicate based cements may form continuously calcium-silicate hydrates and precipitate calcium-phosphate and calcium carbonate⁷. Nonetheless, MTA and Biodentine had no differences in cell viability after 7 days.

Cell adherence and viability, when in contact with Biodentine compared with MTA, were further assessed using fluorescent probes under confocal microscopy. It has been shown that contact of dental materials with dentin may alter their properties⁹. Thus, the interaction between cement and surrounding dentin was taken into consideration in this study utilizing dentin disks from anterior bovine teeth, since they could be considered an appropriate substitute for human teeth³. Confocal micrographs showed that DPSCs attached on the materials stored in citric acid were more sprindle-shaped compared with the materials stored in saline. This fact is indicative of a good cell substrate interaction signifying that both calcium-silicate based materials provide a significantly better substrate for cell adhesion when they set in the presence of citric acid⁶,²³. A possible explanation is that the acidic conditions of the citric acid induced the release of Ca-ions, and subsequently the relative concentration of Si increased³⁰. Furthermore, the acid-etching effect leads to microstructural changes that could affect the adhesion and proliferation of cells on calcium silicate-based materials¹,¹⁰,¹⁹,²⁷. The results of this study agree, despite the differences in methodology, with the results of Kang, et al.¹¹ (2013), who reported that MTA mixed with citric acid showed favorable biocompatibility. Importantly, our study shows that Biodentine promoted greater cell adherence and viability compared with MTA. Nevertheless, the mechanisms that are responsible for these effects are not completely understood and further research is required to elucidate them. These data may be applied in future studies to modify the surface of the materials to promote better adhesion and sprouting of cells.

CONCLUSION

Biodentine demonstrated a significantly faster cell proliferation compared with MTA and control groups. Furthermore, 24-hour set MTA allowed for greater cell viability compared with 1-hour set MTA after 7 days. Both 1-hour and 24-h set MTA were initially more cytotoxic compared with Biodentine, however, there were no significant differences at the 7-day time point. Exposure of MTA and Biodentine to an acidic environment showed an increase in the number of DPSCs adhered to their surface.

REFERENCES

• ¹
  - Agrafioti A, Tzimpoulas N, Chatzitheodoridis E, Kontakiotis EG. Comparative evaluation of sealing ability and microstructure of MTA and Biodentine after exposure to different environments. Clin Oral Investig. 2015 Nov 6. [Epub ahead of print].
• ²
  - Attik GN, Villat C, Hallay F, Pradelle-Plasse N, Bonnet H, Moreau K, et al. In vitro biocompatibility of a dentine substitute cement on human MG63 osteoblasts cells: Biodentine™ versus MTA^® Int Endod J. 2014;12:1133–41.
• ³
  - Balto HA. Attachment and morphological behavior of human periodontal ligament fibroblasts to mineral trioxide aggregate: a scanning electron microscope study. J Endod. 2004;30:25–9.
• ⁴
  - Ber BS, Hatton JF, Stewart GP. Chemical modification of ProRoot MTA to improve handling characteristics and decrease setting time. J Endod. 2007;33:1231–4.
• ⁵
  - Camilleri J, Pitt Ford TR. Mineral trioxide aggregate: a review of the constituents and biological properties of the material. Int Endod J. 2006;39:747–54.
• ⁶
  - Damas BA, Wheater MA, Bringas JS, Hoen MM. Cytotoxicity comparison of mineral trioxide aggregates and EndoSequence bioceramic root repair materials. J Endod. 2011;37:372–5.
• ⁷
  - Gandolfi MG, Ciapetti G, Taddei P, Perut F, Tinti A, Cardoso MV, et al. Apatite formation on bioactive calcium-silicate cements for dentistry affects surface topography and human marrow stromal cells proliferation. Dent Mater. 2010;26:974–92.
• ⁸
  - Gomes Cornélio AL, Salles LP, Campos da Paz M, Cirelli JA, Guerreiro-Tanomaru JM, Tanomaru Filho M. Cytotoxicity of Portland cement with different radiopacifying agents: a cell death study. J Endod. 2011;37:203–10.
• ⁹
  - Haapasalo HK, Sirén EK, Waltimo TM, Ørstavik D, Haapasalo MP. Inactivation of local root canal medicaments by dentine: an in vitro study. Int Endod J. 2000;33:126–31.
• ¹⁰
  - Hamilton DW, Brunette DM. The effect of substratum topography on osteoblast adhesion mediated signal transduction and phosphorylation. Biomaterials. 2007;28:1806–19.
• ¹¹
  - Kang JY, Lee BN, Son HJ, Koh JT, Kang SS, Son HH, et al. Biocompatibility of mineral trioxide aggregate mixed with hydration accelerators. J Endod. 2013;39:497–500.
• ¹²
  - Kontakiotis EG, Filippatos CG, Tzanetakis GN, Agrafioti A. Regenerative endodontic therapy: a data analysis of clinical protocols. J Endod. 2015;41:146–54.
• ¹³
  - Laurent P, Camps J, About I. Biodentine induces TGF-βΙ release from human pulp cells and early dental pulp mineralization. Int Endod J. 2012;45:439–48.
• ¹⁴
  - Laurent P, Camps J, De Méo M, Déjou J, About I. Induction of specific cell responses to a Ca(3)SiO(5)-based posterior restorative material. Dent Mater. 2008;24:1486–94.
• ¹⁵
  - Lee SJ, Monsef M, Torabinejad M. Sealing ability of a mineral trioxide aggregate for repair of lateral root perforations. J Endod. 1993;19:541–4.
• ¹⁶
  - Lee YL, Lee BS, Lin FH, Yun Lin A, Lan WH, Lin CP. Effects of physiological environments on the hydration behavior of mineral trioxide aggregate. Biomaterials. 2004;25:787–93.
• ¹⁷
  - Luo Z, Li D, Kohli MR, Yu Q, Kim S, He WX. Effect of Biodentine™ on the proliferation, migration and adhesion of human dental pulp stem cells. J Dent. 2014;42:490–7.
• ¹⁸
  - Malamed SF. Handbook of local anesthesia. 5^th ed. St. Louis: Mosby; 2004.
• ¹⁹
  - Namazikhah MS, Nekoofar MH, Sheykhrezae MS, Salariyeh S, Hayes SJ, Bryant ST, et al. The effect of pH on surface hardness and microstructure of mineral trioxide aggregate. Int Endod J. 2008;41:108–16.
• ²⁰
  - Parirokh M, Torabinejad M. Mineral trioxide aggregate: a comprehensive literature review - Part I: chemical, physical, and antibacterial properties. J Endod. 2010;36:16–27.
• ²¹
  - Peng W, Liu W, Zhai W, Jiang L, Li L, Chang J, et al. Effect of tricalcium silicate on the proliferation and odontogenic differentiation of human dental pulp cells. J Endod. 2011;37:1240–6.
• ²²
  - Pérard M, Le Clerc J, Watrin T, Meary F, Pérez F, Tricot-Doleux S, Pellen-Mussi P, et al. Spheroid model study comparing the biocompatibility of Biodentine and MTA. J Mater Sci Mater Med. 2013;24:1527–34.
• ²³
  - Reis AF, Giannini M, Kavaguchi A, Soares CJ, Line SR. Comparison of microtensile bond strength to enamel and dentin of human, bovine, and porcine teeth. J Adhes Dent. 2004;2:117–21.
• ²⁴
  - Saghiri MA, Lotfi M, Saghiri AM, Vosoughhosseini S, Fatemi A, Shiezadeh V, et al. Effect of pH on sealing ability of white mineral trioxide aggregate as a root-end filling material. J Endod. 2008;34:1226–9.
• ²⁵
  - Samara A, Sarri Y, Stravopodis D, Tzanetakis GN, Kontakiotis EG, Anastasiadou E. A comparative study of the effects of three root-end filling materials on proliferation and adherence of human periodontal ligament fibroblasts. J Endod. 2011;37:865–70.
• ²⁶
  - Schneider R, Holland GR, Chiego D Jr, Hu JC, Nör JE, Botero TM. White mineral trioxide aggregate induces migration and proliferation of stem cells from the apical papilla. J Endod. 2014;40:931–6.
• ²⁷
  - Shie MY, Huang TH, Kao CT, Huang CH, Ding SJ. The effect of a physiologic solution pH on properties of white mineral trioxide aggregate. J Endod. 2009;35:98–101.
• ²⁸
  - Torabinejad M, Chivian N. Clinical applications of mineral trioxide aggregate. J Endod. 1999;25:197–205.
• ²⁹
  - Torabinejad M, Parirokh M. Mineral trioxide aggregate: a comprehensive literature review - Part II: leakage and biocompatibility investigations. J Endod. 2010;36:190–202.
• ³⁰
  - Tsujimoto M, Ookubo A, Wada Y, Matsunaga T, Tsujimoto Y, Hayashi Y. Surface changes of mineral trioxide aggregate after the application of bleaching agents: electron microscopy and an energy-dispersive X-ray microanalysis. J Endod. 2011;37:231–4.
• ³¹
  - Watts JD, Holt DM, Beeson TJ, Kirkpatrick TC, Rutledge RE. Effects of pH and mixing agents on the temporal setting of tooth-colored and gray mineral trioxide aggregate. J Endod. 2007;33:970–3.
• ³²
  - Widbiller M, Lindner SR, Buchalla W, Eidt A, Hiller KA, Schmalz G, et al. Three-dimensional culture of dental pulp stem cells in direct contact to tricalcium silicate cements. Clin Oral Investig. 2016;20:237–46.
• ³³
  - Zanini M, Sautier JM, Berdal A, Simon S. Biodentine induces immortalized murine pulp cell differentiation into odontoblast-like cells and stimulates biomineralization. J Endod. 2012;38:1220–6.

Publication Dates

• Publication in this collection
  Sep-Oct 2016

History

• Received
  22 Feb 2016
• Reviewed
  09 May 2016
• Accepted
  25 May 2016