Resumo em Inglês:

OBJECTIVE: The purpose of this study was to investigate the polymerization temperature of a bulk filled composite resin light-activated with various light curing modes using infrared thermography according to the curing depth and approximation to the cavity wall. MATERIAL AND METHODS: Composite resin (AeliteFlo, Bisco, Schaumburg, IL, USA) was inserted into a Class II cavity prepared in the Teflon blocks and was cured with a LED light curing unit (Dr's Light, GoodDoctors Co., Seoul, Korea) using various light curing modes for 20 s. Polymerization temperature was measured with an infrared thermographic camera (Thermovision 900 SW/TE, Agema Infra-red Systems AB, Danderyd, Sweden) for 40 s at measurement spots adjacent to the cavity wall and in the middle of the cavity from the surface to a 4 mm depth. Data were analyzed according to the light curing modes with one-way ANOVA, and according to curing depth and approximation to the cavity wall with two-way ANOVA. RESULTS: The peak polymerization temperature of the composite resin was not affected by the light curing modes. According to the curing depth, the peak polymerization temperature at the depth of 1 mm to 3 mm was significantly higher than that at the depth of 4 mm, and on the surface. The peak polymerization temperature of the spots in the middle of the cavity was higher than that measured in spots adjacent to the cavity wall. CONCLUSION: In the photopolymerization of the composite resin, the temperature was higher in the middle of the cavity compared to the outer surface or at the internal walls of the prepared cavity.

Resumo em Inglês:

OBJECTIVE: This study investigated the effects of different surface treatments on the tensile bond strength of an autopolymerizing silicone denture liner to a denture base material after thermocycling. MATERIAL AND METHODS: Fifty rectangular heat-polymerized acrylic resin (QC-20) specimens consisting of a set of 2 acrylic blocks were used in the tensile test. Specimens were divided into 5 test groups (n=10) according to the bonding surface treatment as follows: Group A, adhesive treatment (Ufi Gel P adhesive) (control); Group S, sandblasting using 50-µm Al2O3; Group SCSIL, silica coating using 30-µm Al2O3 modified by silica and silanized with silane agent (CoJet System); Group SCA, silica coating and adhesive application; Group SCSILA, silica coating, silane and adhesive treatment. The 2 PMMA blocks were placed into molds and the soft lining materials (Ufi Gel P) were packed into the space and polymerized. All specimens were thermocycled (5,000 cycles) before the tensile test. Bond strength data were analyzed using 1-way ANOVA and Duncan tests. Fracture surfaces were observed by scanning electron microscopy. X-ray photoelectron spectrometer (XPS) and Fourier Transform Infrared spectrometer (FTIR) analysis were used for the chemical analysis and a profilometer was used for the roughness of the sample surfaces. RESULTS: The highest bond strength test value was observed for Group A (1.35±0.13); the lowest value was for Group S (0.28±0.07) and Group SCSIL (0.34±0.03). Mixed and cohesive type failures were seen in Group A, SCA and SCSILA. Group S and SCSIL showed the least silicone integrations and the roughest surfaces. CONCLUSION: Sandblasting, silica coating and silane surface treatments of the denture base resin did not increase the bond strength of the silicone based soft liner. However, in this study, the chemical analysis and surface profilometer provided interesting insights about the bonding mechanism between the denture base resin and silicone soft liner.

Resumo em Inglês:

Implant-supported screw-retained fixed dental prostheses (FDPs) produced by CAD/ CAM have been introduced in recent years for the rehabilitation of partial or total endentulous jaws. However, there is a lack of data about the long-term mechanical characteristics. OBJECTIVE: The aim of this study was to investigate the failure mode and the influence of extended cyclic mechanical loading on the load-bearing capacity of these frameworks. MATERIAL AND METHODS: Ten five-unit FDP frameworks simulating a free-end situation in the mandibular jaw were manufactured according to the I-Bridge®2-concept (I-Bridge®2, Biomain AB, Helsingborg, Sweden) and each was screw-retained on three differently angulated Astra Tech implants (30º buccal angulation/0º angulation/30º lingual angulation). One half of the specimens was tested for static load-bearing capacity without any further treatment (control), whereas the other half underwent five million cycles of mechanical loading with 100 N as the upper load limit (test). All specimens were loaded until failure in a universal testing machine with an occlusal force applied at the pontics. Load-displacement curves were recorded and the failure mode was macro- and microscopically analyzed. The statistical analysis was performed using a t-test (p=0.05). RESULTS: All the specimens survived cyclic mechanical loading and no obvious failure could be observed. Due to the cyclic mechanical loading, the load-bearing capacity decreased from 8,496 N±196 N (control) to 7,592 N±901 N (test). The cyclic mechanical loading did not significantly influence the load-bearing capacity (p=0.060). The failure mode was almost identical in all specimens: large deformations of the framework at the implant connection area were obvious. CONCLUSION: The load-bearing capacity of the I-Bridge®2 frameworks is much higher than the clinically relevant occlusal forces, even with considerably angulated implants. However, the performance under functional loading in vivo depends on additional aspects. Further studies are needed to address these aspects.

Resumo em Inglês:

OBJECTIVE: To compare the static frictional forces generated at the bracket/wire interface of stainless steel brackets with different geometries and angulations, combined with orthodontic wires of different diameters. MATERIAL AND METHODS: The frictional forces were evaluated with three different types of metal brackets: a passive self-ligating (SmartClipTM, 3M/Unitek, Monrovia, USA), with a modified slot design (Mini Uni TwinTM, 3M/Unitek, Monrovia, USA) and conventional (Kirium, Abzil, São José do Rio Preto, Brazil). The samples were mounted in a testing device with three different angulations and tested with 0.014" and 0.018" stainless steel wires (American Orthodontics, Sheboygan, USA). The static frictional force was measured using a universal testing machine (DL 500, EMIC®, São José dos Pinhais, Brazil) with a crosshead speed of 1 mm/min. Statistical analysis was performed by two-way ANOVA followed by Bonferroni's post hoc test. RESULTS: There was a significant difference (p<0.05) in static friction when the three types of brackets were tested with the same wire size. The wire diameter influenced friction only when the brackets had a 10º angulation (p<0.05). The angulation influenced friction (p<0.05) when the brackets were associated with a 0.018" wire. CONCLUSION: Brackets with a modified slot design showed intermediate static frictional force values between the conventional and self-ligating brackets tested.

Resumo em Inglês:

OBJECTIVE: The shear bond strengths of two hard chairside reline resin materials and an auto-polymerizing denture base resin material to cast Ti and a Co-Cr alloy treated using four conditioning methods were investigated. MATERIAL AND METHODS: Disk specimens (diameter 10 mm and thickness 2.5 mm) were cast from pure Ti and Co-Cr alloy. The specimens were wet-ground to a final surface finish of 600 grit, air-dried, and treated with the following bonding systems: 1) air-abraded with 50-70-µm grain alumina (CON); 2) 1) + conditioned with a primer, including an acidic phosphonoacetate monomer (MHPA); 3) 1) + conditioned with a primer including a diphosphate monomer (MDP); 4) treated with a tribochemical system. Three resin materials were applied to each metal specimen. Shear bond strengths were determined before and after 10,000 thermocycles. RESULTS: The strengths decreased after thermocycling for all combinations. Among the resin materials assessed, the denture base material showed significantly (p<0.05) greater shear bond strengths than the two reline materials, except for the CON condition. After 10,000 thermocycles, the bond strengths of two reline materials decreased to less than 10 MPa for both metals. The bond strengths of the denture base material with MDP were sufficient: 34.56 MPa for cast Ti and 38.30 for Co-Cr alloy. CONCLUSION: Bonding of reline resin materials to metals assessed was clinically insufficient, regardless of metal type, surface treatment, and resin composition. For the relining of metal denture frameworks, a denture base material should be used.

Resumo em Inglês:

OBJECTIVE: The aim of this study was to evaluate the antimicrobial and fluoride releasing capacity of 3 bonding materials. MATERIAL AND METHODS: Thirty nine specimens with standardized surface smoothness and dimensions were prepared. The antimicrobial capacity of the materials against S. mutans, L. casei and C. albicans was evaluated by determining the percentage of growth inhibition of these microorganisms in an inoculated medium, obtained by optical density readouts on a spectrophotometer. The potential to interfere in microbial growth on the surface of the studied materials was observed by means of scanning electron microscopy (SEM). The fluoride release capacity in ultrapure water for 14 days was analyzed by means of ion chromatography. RESULTS: The PLUS group presented the highest percentage of microbial inhibition and the most contamination-free surface. The FUJI group presented the best fluoride release capacity. CONCLUSIONS: The TransbondTM Plus Color Change was the one that presented the best general behavior considering the evaluated aspects.

Resumo em Inglês:

OBJECTIVE: This study aimed to evaluate the effects of heat treatment on the tribochemical silica coating and silane surface conditioning and the bond strength of rebonded alumina monocrystalline brackets. MATERIAL AND METHODS: Sixty alumina monocrystalline brackets were randomly divided according to adhesive base surface treatments (n=20): Gc, no treatment (control); Gt, tribochemical silica coating + silane application; Gh, as per Gt + post-heat treatment (air flux at 100ºC for 60 s). Brackets were bonded to the enamel premolars surface with a light-polymerized resin and stored in distilled water at 37ºC for 100 days. Additionally, half the specimens of each group were thermocycled (6,000 cycles between 5-55ºC) (TC). The specimens were submitted to the shear bond strength (SBS) test using a universal testing machine (1 mm/min). Failure mode was assessed using optical and scanning electron microscopy (SEM), together with the surface roughness (Ra) of the resin cement in the bracket using interference microscopy (IM). 2-way ANOVA and the Tukey test were used to compare the data (p>0.05). RESULTS: The strategies used to treat the bracket surface had an effect on the SBS results (p=0.0), but thermocycling did not (p=0.6974). Considering the SBS results (MPa), Gh-TC and Gc showed the highest values (27.59±6.4 and 27.18±2.9) and Gt-TC showed the lowest (8.45±6.7). For the Ra parameter, ANOVA revealed that the aging method had an effect (p=0.0157) but the surface treatments did not (p=0.458). For the thermocycled and non-thermocycled groups, Ra (µm) was 0.69±0.16 and 1.12±0.52, respectively. The most frequent failure mode exhibited was mixed failure involving the enamel-resin-bracket interfaces. CONCLUSION: Regardless of the aging method, Gh promoted similar SBS results to Gc, suggesting that rebonded ceramic brackets are a more effective strategy.

Resumo em Inglês:

OBJECTIVE: The aim of this study was to evaluate the influence of exposure of the mineral trioxide aggregate (MTA) - with and without calcium chloride (CaCl2) - to phosphate-buffered saline (PBS) on the apical microleakage using a glucose leakage system. MATERIAL AND METHODS: Sixty root segments were randomly divided into 4 experimental groups (n=15). After resecting the apical segments and enlarging the canals with Gates-Glidden drills, the apical cavities were filled with MTA with or without CaCl2 and the root canals were dressed with a moistened cotton pellet or PBS, as follows: 1) MTA/cotton pellet; 2) MTA/PBS; 3) MTA+10%CaCl2/cotton pellet; 4) MTA+10%CaCl2/PBS. All root segments were introduced in floral foams moistened with PBS. After 2 months, all root segments were prepared to evaluate the glucose leakage along the apical plugs. The amount of glucose leakage was measured following an enzymatic reaction and quantified by a spectrophotometer. Four roots were used as controls. The data were analyzed using Kruskal-Wallis and Mann-Whitney tests (p<0.05). RESULTS: There were no differences between groups 1 and 2 (p>0.05), and 3 and 4 (p>0.05). The addition of CaCl2 to the MTA significantly decreased its sealing ability (p<0.05). CONCLUSION: The interaction with PBS did not improve the MTA sealing ability. The addition of CaCl2 to the MTA negatively influenced the apical seal.

Resumo em Inglês:

OBJECTIVE: The goal of this study was to evaluate the efficacy of the Self-Adjusting File (SAF) and ProTaper for removing calcium hydroxide [Ca(OH)2] from root canals. MATERIAL AND METHODS: Thirty-six human mandibular incisors were instrumented with the ProTaper system up to instrument F2 and filled with a Ca(OH)2-based dressing. After 7 days, specimens were distributed in two groups (n=15) according to the method of Ca(OH)2 removal. Group I (SAF) was irrigated with 5 mL of NaOCl and SAF was used for 30 seconds under constant irrigation with 5 mL of NaOCl using the Vatea irrigation device, followed by irrigation with 3 mL of EDTA and 5 mL of NaOCl. Group II (ProTaper) was irrigated with 5 mL of NaOCl, the F2 instrument was used for 30 seconds, followed by irrigation with 5 mL of NaOCl, 3 mL of EDTA, and 5 mL of NaOCl. In 3 teeth Ca(OH)2 was not removed (positive control) and in 3 teeth canals were not filled with Ca(OH)2 (negative control). Teeth were sectioned and prepared for the scanning electron microscopy. The amounts of residual Ca(OH)2 were evaluated in the middle and apical thirds using a 5-score system. RESULTS: None of the techniques completely removed the Ca(OH)2 dressing. No difference was observed between SAF and ProTaper in removing Ca(OH)2 in the middle (P=0.11) and the apical (P=0.23) thirds. CONCLUSION: The SAF system showed similar efficacy to rotary instrument for removal of Ca(OH)2 from mandibular incisor root canals.

Resumo em Inglês:

OBJECTIVE: The aim of this study was to compare the cytotoxic effects of endodontic cements on human tooth germ stem cells (hTGSCs). MTA Fillapex, a mineral trioxide aggregate (MTA)-based, salicylate resin containing root canal sealer, was compared with iRoot SP, a bioceramic sealer, and AH Plus Jet, an epoxy resin-based root canal sealer. MATERIAL AND METHODS: To evaluate cytotoxicity, all materials were packed into Teflon rings (4 mmµ3 mm) and co-cultured with hTGSCs with the aid of 24-well Transwell permeable supports, which had a pore size of 0.4 µm. Coverslips were coated with MTA Fillapex, iRoot SP and AH Plus Jet and each coverslip was placed onto the bottom of one well of a six-well plate for scanning electron microscopy (SEM) analysis. Before the cytotoxicity and SEM analysis, all samples were stored at 37ºC and at 95% humidity and 5% CO2 for 24 hours to set. The cellular viability was analyzed using MTS test (3-(4,5-dimethyl-thiazol-2-yl)-5-(3-carboxy-methoxy-phenyl)-2-(4-sulfo-phenyl)-2H-tetrazolium). The cytotoxic effects and SEM visualization of the tested materials were analyzed at 24-hour, 72-hour, one-week and two-week periods. RESULTS: On the 1st day, only MTA Fillapex caused cytotoxicity compared to negative control (NC) group (p<0.008). No significant difference was observed between the other tested materials at this period (p>0.05). After 14 days of incubation with the test materials, MTA Fillapex exhibited significantly higher cytotoxicity compared with iRoot SP, AH Plus Jet and the NC group (P<0.008). In the SEM analysis, the highest levels of cell attachment were observed for iRoot SP and the control group. After 24 hours, MTA Fillapex reduced the number of cells attached to the surface. CONCLUSIONS: Within the limitations of this study, sealers exerted different cytotoxic effects on hTGSCs. Although all materials have exerted cellular toxicity, iRoot SP and AH Plus Jet may promote better attachment to hTGSCs.

Resumo em Inglês:

Validation studies of physical anthropology methods in the different population groups are extremely important, especially in cases in which the population variations may cause problems in the identification of a native individual by the application of norms developed for different communities. OBJECTIVE: This study aimed to estimate the gender of skeletons by application of the method of Oliveira, et al. (1995), previously used in a population sample from Northeast Brazil. MATERIAL AND METHODS: The accuracy of this method was assessed for a population from Southeast Brazil and validated by statistical tests. The method used two mandibular measurements, namely the bigonial distance and the mandibular ramus height. The sample was composed of 66 skulls and the method was applied by two examiners. The results were statistically analyzed by the paired t test, logistic discriminant analysis and logistic regression. RESULTS: The results demonstrated that the application of the method of Oliveira, et al. (1995) in this population achieved very different outcomes between genders, with 100% for females and only 11% for males, which may be explained by ethnic differences. However, statistical adjustment of measurement data for the population analyzed allowed accuracy of 76.47% for males and 78.13% for females, with the creation of a new discriminant formula. CONCLUSION: It was concluded that methods involving physical anthropology present high rate of accuracy for human identification, easy application, low cost and simplicity; however, the methodologies must be validated for the different populations due to differences in ethnic patterns, which are directly related to the phenotypic aspects. In this specific case, the method of Oliveira, et al. (1995) presented good accuracy and may be used for gender estimation in Brazil in two geographic regions, namely Northeast and Southeast; however, for other regions of the country (North, Central West and South), previous methodological adjustment is recommended as demonstrated in this study.

Resumo em Inglês:

OBJECTIVE: The aim of this study was to evaluate the effect of the addition of metallic ions to carbonated drinks on their erosive potential. MATERIAL AND METHODS: Powdered enamel was added to carbonated beverages (Coca-ColaTM or Sprite ZeroTM and shaken for 30 s. The samples were then immediately centrifuged and the supernatant removed. This procedure was repeated 5 times with the beverages containing Cu2+, Mg2+, Mn2+ or Zn2+ (1.25-60 mmol/L). For Coca-ColaTM, the concentration of each ion that exhibited the highest protection was also evaluated in combination with Fe2+. The phosphate or calcium released were analyzed spectrophotometrically. Data were analyzed using ANOVA and Tukey's test (p<0.05). RESULTS: For Coca-ColaTM, the best protective effect was observed for Zn2+ alone (10 mmol/L) or in combination (1 mmol/L) with other ions (12% and 27%, respectively, when compared with the control). Regarding Sprite ZeroTM, the best protective effect was observed for Cu2+ at 15 and 30 mmol/L, which decreased the dissolution by 22-23%. Zn2+ at 2.5 mmol/L also reduced the dissolution of powdered enamel by 8%. CONCLUSIONS: The results suggest that the combination of metallic ions can be an alternative to reduce the erosive potential of Coca-ColaTM. Regarding Sprite ZeroTM, the addition of Cu2+ seems to be the best alternative.

Resumo em Inglês:

OBJECTIVES: To investigate the bond strength and seal ability produced by AH Plus/gutta-percha, EndoREZ and RealSeal systems to root canal dentin. MATERIAL AND METHODS: Sixty extracted single-root human teeth, instrumented manually to size 40, were divided into three groups (n=20) according to the sealer used; G1: AH Plus, G2: EndoREZ, and G3: RealSeal sealers. After filling using the lateral condensation technique, each sealer group was randomly divided into two subgroups according to the tests applied (n=10 for µPush-out test and n=10 for fluid filtration test). A fluid filtration method was used for quantitative evaluation of apical leakage. Four 1-mm-thick slices (cervical and medium level) were obtained from each root sample and a µPush-out test was performed. Failure modes were examined under microscopy at 40x, and a one-way ANOVA was applied to analyze the permeability. Non-parametrical statistics for related (Friedman's and Wilcoxon's rank tests) or unrelated samples (Kruskal-Wallis' and Mann-Whitney's tests) allowed for comparisons of µPush-out strength values among materials at the different levels. Statistical significance was accepted for p values <.05. RESULTS: There are no significant differences among fluid filtration of the three sealers. The sealer/core material does not significantly influence the µPush-out bond strength values (F=2.49; p=0.10), although statistically significant differences were detected with regard to root level (Chi2=23.93; p<0.001). AH Plus and RealSeal obtained higher bond strength to intraradicular dentin in the medium root slices. CONCLUSIONS: There are no significant differences between the permeability and global µPush-out bond strength to root canal dentin achieved by AH Plus/gutta-percha, EndoREZ and RealSeal systems.

Resumo em Inglês:

OBJECTIVE: To determine how early musculoskeletal disorders (MSDs) develop in dental professionals and to explore the potential differences among distinct dental specialties. MATERIAL AND METHODS: 271 dental postgraduates majoring in five dental specialties were recruited, i.e., orthodontics, prosthodontics, endodontics, periodontics and alveolar surgery. 254 age-matched non-dental postgraduates served as the control. The standardized Nordic questionnaire on MSDs and a self-report questionnaire regarding correlative factors (only for dental postgraduates) were answered through emails. Reliability of responses was assessed applying test-retest method. RESULTS: The intraclass correlation coefficient of participants' answers ranged from 0.89 to 0.96. Dental postgraduates had significantly higher prevalence of MSDs than the control group, especially at neck, upper back and lower back. In all dental specialties included, high prevalence of MSDs was reported at neck (47.5%-69.8%), shoulders (50.8%-65.1%), lower back (27.1%-51.2%) and upper back (25.6%-46.5%), with lower prevalence at elbows (5.1%-18.6%), hips (3.4%-16.3%) and ankles (5.1%-11.6%). Periodontics students reported the worst MSDs in most body regions except wrists and knees, which were more prevalent for prosthodontic and alveolar surgery students, respectively. Furthermore, year of clinical work, clinical hours per week and desk hours per week were found as risk factors for MSDs, whereas physical exercise and rest between patients as protective factors. CONCLUSIONS: High and specialty-related MSDs afflict dental professionals even since very early stage of careers. Prevention aimed at the specialty-related characteristics and the risk/protective factors revealed in this study should be introduced to dental personnel as early as possible.

Resumo em Inglês:

The Laboratory of Physiology provides support for the diagnosis of functional disorders associated with cleft lip and palate and also conducts studies to assess, objectively, the institutional outcomes, as recommended by the World Health Organization. The Laboratory is conceptually divided into three units, namely the Unit for Upper Airway Studies, Unit for Stomatognathic System Studies and the Unit for Sleep Studies, which aims at analyzing the impact of different surgical and dental procedures on the upper airways, stomatognathic system and the quality of sleep of individuals with cleft lip and palate. This paper describes the main goals of the Laboratory in the assessment of procedures which constitute the basis of the rehabilitation of cleft lip and palate, i.e., Plastic Surgery, Orthodontics and Maxillofacial Surgery and Speech Pathology.