Determination of Rhodium and Platinum by Electrothermal Atomic Absorption Spectrometry after Preconcentration with a Chelating Resin

Este trabalho descreve um procedimento de separação/pré-concentração para a subseqüente análise de traços de ródio e platina em amostras ambientais. Uma resina de troca iônica quelante foi empregada com este objetivo e um sistema em fluxo associado a espectrômetro de absorção atômica com atomização eletrotérmica (FI-ET-AAS) foi usado para a determinação de quantidades traço de Rh e Pt em diferentes materiais. As soluções são tratadas simultaneamente e os íons determinados seqüencialmente. Os limites de detecção de ródio e platina são 0,8 e 1,0 ng mL-1, respectivamente. Linearidade foi obtida no intervalo 0-50 ng mL-1 para ródio e 0-100 ng mL-1 para platina. Os desvios padrão relativos foram 1,8% para 10 ng mL-1 de Rh e 1,6% para 10 ng mL-1 de Pt. Os fatores de enriquecimento foram de 20 para Rh e 14 para Pt.


Introduction
The increasing use of the automobile catalyst leads to the emission of the rhodium and platinum into the environment.][3] Rhodium, platinum and their complex salts, such as Rh-and Pt-chlorides, have been reported as potential health risks to humans, causing asthma, allergy, rhinoconjunctivitis and other serious health problems. 4e most common detection techniques for these elements are electrothermal atomic absorption spectrometry (ET-AAS), inductively coupled plasma mass spectrometry (ICP-MS) and inductively coupled atomic emission spectrometry (ICP-AES), adsorptive cathodic stripping voltammetry (ACSV) and neutron activation analysis (NAA).
The concentration of these elements is still relatively low in environmental compartments.For this reason, a preconcentration procedure is often needed to increase concentration levels in analysed solutions and also remove matrix interference. 5][18][19][20][21][22][23][24][25][26] ET-AAS is often combined with a preceding matrix separation/preconcentration step.On-line preconcentration techniques offer a good way in this sense.A flow system combined with a segmentation technique was used to develop an efficient on-line sorbent extraction preconcentration system for palladium, platinum and rhodium for ET-AAS and ICP-AES; the investigated metals were preconcentrated as their bis(carboxylmethyl)dithiocarbamate (CMDTC) chelates on a microcolumn packed with XAD-4 after the off-line addition of solid CMDTC to the sample solution containing SnCl 2 , and hydrochloric acid. 19The development of a new selective system for on-line solid phase extraction of Rh, Pt and Pd and the design of an FIA-FAAS system have been proposed for the determination of these elements in solutions obtained by the decomposition of geological and technological samples. 27he purpose of the present work was the application of an automatic on-line FI-ET-AAS method previously developed 28,29 for the simultaneous determination of trace amounts of platinum and rhodium.

Reagents
Analytical reagent grade chemicals were used throughout.PSTH-Dowex was synthesized as described elsewhere. 30A standard 1000 μg mL -1 Pt(IV) and rhodium(III) solutions (CertiPUR, Merck) were used.A pH 9.2 buffer was prepared by mixing 25 mL of 0.2 mol L -1 glycine with 8.4 mL of 0.2 mol L -1 sodium hydroxide and diluting to 100 mL with deionized water.HNO 3 (Merck) 2 mol L -1 was used as eluent.

Apparatus
A Perkin-Elmer Zeeman/4100 ZL atomic absorption spectrometer equipped with an AS-70 furnace autosampler was used throughout.Pyrolitic graphite coated tubes with pyrolitic graphite platforms were used in all experiments; the graphite tube lifetime is long, about 100 injections.The primary radiation sources were a platinum hollow cathode lamp operated at 15 mA; the selected wavelength was 265.9 nm with a spectral slit width of 0.7 nm, and a rhodium hollow cathode lamp operated at 15 mA; the selected wavelength was 343.5 nm with a spectral slit width of 0.2 nm.Absorbance signals were measured in peak area with Zeeman effect background correction.
The graphite furnace temperature programs for the determination of platinum and rhodium are shown in Table 1. 28,29he microcolumn containing the PSTH-Dowex was a glass tube (3 cm × 3 mm id) packed to a height of 0.2 cm; at both ends of the microcolumn, polyethylene frits were fixed to prevent material losses.On the end of this column was placed a piece of sample capillary of the sampler arm, in imitation of the sample tip of the sampler arm.Thus, the sample tip of the sampler arm was replaced with this microcolumn, permitting normal working of the sampler.
A peristaltic pump, P (Gilson Minipuls 3), fitted with a vinyl pump tube (1.65 mm id), was used for loading of the sample.A Rheodyne Type 50 six-port rotary valve was used as a switching valve.Transport lines were made using 0.8 mm id PTFE tubing.The peristaltic pump and the selection valve were readily controlled electronically via two switches on the autosampler that were actuated when the autosampler arm was down.The process was thus fully automated without altering the software of the AA spectrometer.For sample digestion, a focused-microwave oven, Microdigest 301 controlled by Prolabo TX-32, was used and the cavity of it is for one sample.All glassware used was washed with 10% nitric acid for 24 h and rinsed with deionised water immediately before use.

Procedure
The schematic diagram of FI-ET-AAS was shown previously. 28,29During the 1 min sample loading period, a 3.5 mL min -1 flow of sample (standard or blank) at pH 9.2, buffered with glycine-sodium hydroxide, is pumped through the microcolumn (located in the sampler arm); the metal ions platinum and rhodium were adsorbed on the sorbent microcolumn and the sample matrix is sent to waste; then, the switching valve is actuated and the pumps of the AS-70 furnace autosampler are connected, permitting the operation of the autosampler in the normal mode; a wash step takes place with de-ionised water and, immediately after, the sampler arm lowers the sample capillary into an autosampler cup (filled with eluent) aspirating 40 μL of 2 mol L -1 HNO 3 ; then, the sampler arm swings over to the graphite furnace and the tip of the sampler capillary is inserted into the dosing hole of the graphite tube where the eluted Rh(III) and Pt(IV) were deposited as a drop; the sampler arm then returns to its initial position and the cycle of the furnace operation commences; while the temperature programme is running, the switching valve is again turned to start a new loading of the sample (standard or blank); thus, when the spectrometer gives the measurement, the microcolumn is ready for a new injection of eluent.

Preparation of samples
The certified reference material (CRM) analysed to determine the accuracy of the proposed procedure was National Institute of Standard and Technology (NIST), Standard Reference Material (SRM) 2557 catalyst.The sample was first prepared in accordance with the instruction of the analysis certificate, after which an accurately weighed amount of 0.1 g was subjected to microwave digestion.The working condition of the microwave oven is listed in Table 2.After digestion, the sample was diluted to 100 mL with de-ionised water in a calibrated flask.
As far as we know, CRM platinum and rhodium in all the explored matrices is not available.In view of the application of the method to the determination of platinum and rhodium in vegetation and food samples, the ability to recover platinum and rhodium from different samples spiked with platinum and rhodium was investigated.For this purpose, standard solutions containing platinum and rhodium were added to 0.2-0.7 g of different solid samples and the resulting material was prepared by microwave digestion as are listed in Table 2. Tap water was collected immediately prior to the analysis.

Experimental parameters
Optimum chemical parameters including sample acidity, ionic strength, FI variables (loading time, sample flow rate) and ET-AAS parameters have been separately obtained in previous works 28,29 for platinum and rhodium, respectively.In this study, with the aim of investigating the possibility of determining Pt(IV) and Rh(III) in mixtures, the optimum working conditions were studied under the conditions previously established for each metal ion.The results obtained for these parameters are listed in Table 3.

Performance of the method
The characteristic performance data of the FI-ET-AAS system for rhodium and platinum determination are summarized in Table 4.
The effect of diverse ions on the determination of rhodium and platinum are examined under the optimum condition of the procedure.The tolerance limit was taken as that concentration which does not cause more than a 5% change in the atomic absorption.For these studies different amounts of ionic species were added to a solution of 10 ng mL -1 of rhodium and platinum.The interference effects are given in Table 5.

Analysis of synthetic mixtures
In order to check for potential synergistic effects of the mixtures of two ions, various synthetic mixtures were readily resolved by using pertinent calibration graphs.The analytical results are listed in Table 6.As it can be seen, mixtures of the two ions can be resolved with satisfactory results.

Analytical applications
In order to test the accuracy and applicability of the proposed method for the analysis of real samples, one reference material was analysed.The result, as the average of the four separate determinations, is shown in Table 7.
As it can be seen, the platinum and rhodium concentrations determined by the proposed method are in close agreement with the certified values.It has been shown that Pt in road dusts has increased after the introduction of vehicle catalyst.Metallic Pt is considered non allergenic and since the emitted Pt is probably in the metallic or oxide form, the sensitising potential is probably low.Platinum from road dusts, however, can be solubilised, and enter waters, sediments, soils and the food chain. 31The fact that platinum might have entered the food chain was the reason for the rapid and detailed evaluation of the platinum content in various environmental samples.On the other hand, also, the environmental concentration of rhodium is slowly increasing as result of using PGE in automobile catalytic converters.Since finely dispersed rhodium particles from exhaust converters become bio-available by some alimentary chain or metabolic pathway, toxic effects are expected.The main pathways by which rhodium can enter the food chain have to be taken into account: aerosol deposition caused by Rh emission from motor vehicles and industrial sources.The primary sources from which rhodium can be incorporated into the human body are therefore plants or agricultural products.This explains the increasing interest in quantifying rhodium in real matrices of alimentary concern.In view of the application of the method to the determination of With EDTA as masking agent (40 mg mL -1 ).platinum and rhodium in soil, food and beverage samples, the ability to recover platinum and rhodium from different samples spiked with platinum and rhodium was investigated.For this purpose, standard solutions containing platinum and rhodium were added to samples and the resulting material was prepared as described under Experimental.Standard additions method was used in all instances and the results were obtained by extrapolation.The results of these analyses are summarised in Table 5 and indicated excellent recoveries.

Conclusions
Sensitive methods frequently in connection with prior preconcentration are required for the determination of rhodium and platinum in the environment.There are only a few methods enabling their quantitation at extremely low levels, these are ASV, NAA, ET-AAS and ICP-MS.AAS have been used extensively in many laboratories, but detection limits of direct determination, including by ET-AAS are thus unsatisfactory.Suitable preconcentration techniques prior to the determination by ET-AAS are solvent extraction, sorption and ion exchange.
Conventional off-line procedures for separation and preconcentration, although effective, are usually timeconsuming and tedious, and are vulnerable to contamination and analyte loss.FI-on line column preconcentration-ET-AAS has revolutionised trace element analysis in samples with complicated matrices.The separation and preconcentration system for platinum and rhodium described in this work shows a considerable chemical selectivity and allows high sensitivity enhancements even from small sample volumes.It should therefore be practicable for platinum and rhodium trace analysis in a variety of matrices.This system also has the advantage being able to be fully automated without complicated hardware and software; in fact modification of the software of the spectrometer and the use of additional computers were not necessary.
In this research we have developed the determination of platinum and rhodium in mixtures by using a new optimum pH of 9.2 as compromising for simultaneous determination of platinum and rhodium in different samples (although the instrument measurements are sequentially).
The main new advancements resulting from this study are that permit the determination of platinum and rhodium in the same samples (or standards) which allows to significantly time reduction in the sample preparations and in the total time analysis.

Table 1 .
Graphite furnace temperature programs

Table 3 .
Collection of the optimised parameters for the separation and preconcentration of platinum and rhodium with PSTH-Dowex

Table 5 .
Tolerance of foreign ions in the determination of 10 ng mL -1 of rhodium and 10 ng mL -1 of platinum

Table 4 .
Performance of the FI-ET-AAS system for Rh and Pt determination

Table 6 .
Resolution of synthetic Pt(IV)-Rh(III) mixtures by use of the proposed method

Table 7 .
Determination of platinum and rhodium in certified and spiked tap water, vegetation and foods a mean ± standard deviation (n=4).