Open-access Use of the same polymer for synthesis and purification of peptides

Abstracts

This work reveals an uncommon but valuable biotechnological approach regarding the use of a same polymer (benzhydrylamine-resin, BHAR) for synthesis and anion exchange purification of peptides. Initially, the octapeptide DRVYIHPF-NH2 was synthesized in 1% and 3% cross-linked BHAR, attaching 2.5 mmol g-1 ammonium groups. Due certainly to its less rigid polymeric backbone, higher synthesis yield (about 80%) was achieved with the former resin. Next, the negatively charged peptides DEVYEHPF-NH2 and DEVYEDPF-NH2 (-1 and -3 in neutral pH, respectively), both synthesized in 1% BHAR were submitted to chromatographic separation test in this same type of resin (1% and 3%). Following comparative results of peptide synthesis and swelling data of resin beads obtained by microscopy, an improved separation of both peptides occurred with 1% BHAR batch. These findings demonstrated that BHAR applied so far for peptide synthesis, when containing high amount of positively charged ammonium groups, can be also used alternatively as a solid support for chromatographic purification of this type of biological molecule.

peptide synthesis; resin; anion exchange chromatography; polymer; solvent polarity


Este trabalho revela uma estratégia biotecnológica incomum mas valiosa e relacionada com o uso de um mesmo polímero (benzidrilamino-resina, BHAR) para fins de síntese e purificação por troca aniônica de peptídeos. Inicialmente, o octapeptídeo DRVYIHPF-NH2 foi sintetizado em BHAR com 1% e 3% de intercruzamento e contendo 2,5 mmol g-1 de grupos amônio. Devido certamente a uma menor rigidez da sua estrutura polimérica, um maior rendimento na síntese (cerca de 80%) foi obtido com a primeira resina. A seguir, os peptídeos DEVYEHPF-NH2 e DEVYEDPF-NH2 carregados negativamente (-1 e -3 em pH neutro, respectivamente), ambos sintetizados em 1% BHAR, foram submetidos a um teste de separação cromatográfica no mesmo tipo de resina (1% e 3%). Concordante com resultados da síntese de peptídeos e de valores de inchamento dos grãos das resinas, obtidos por microscopia, uma melhor separação entre ambos os peptídeos ocorreu com o lote de 1% BHAR. Estes achados demonstraram que a BHAR, aplicada até o momento somente para a síntese peptídica, se contiver elevado teor de grupos amônio positivos, pode ser utilizada alternativamente como suporte sólido para purificação cromatográfica deste tipo de molécula biológica.


ARTICLE

Use of the same polymer for synthesis and purification of peptides

Elias H. Silva; Augusto Etchegaray; Regina S. H. Carvalho; Guita N. Jubilut; Antonio Miranda; Clovis R. Nakaie*

Departmento de Biofísica, Universidade Federal de São Paulo, Rua 3 de Maio 100, 04044-020 São Paulo - SP, Brazil

ABSTRACT

This work reveals an uncommon but valuable biotechnological approach regarding the use of a same polymer (benzhydrylamine-resin, BHAR) for synthesis and anion exchange purification of peptides. Initially, the octapeptide DRVYIHPF-NH2 was synthesized in 1% and 3% cross-linked BHAR, attaching 2.5 mmol g-1 ammonium groups. Due certainly to its less rigid polymeric backbone, higher synthesis yield (about 80%) was achieved with the former resin. Next, the negatively charged peptides DEVYEHPF-NH2 and DEVYEDPF-NH2 (-1 and -3 in neutral pH, respectively), both synthesized in 1% BHAR were submitted to chromatographic separation test in this same type of resin (1% and 3%). Following comparative results of peptide synthesis and swelling data of resin beads obtained by microscopy, an improved separation of both peptides occurred with 1% BHAR batch. These findings demonstrated that BHAR applied so far for peptide synthesis, when containing high amount of positively charged ammonium groups, can be also used alternatively as a solid support for chromatographic purification of this type of biological molecule.

Keywords: peptide synthesis, resin, anion exchange chromatography, polymer, solvent polarity

RESUMO

Este trabalho revela uma estratégia biotecnológica incomum mas valiosa e relacionada com o uso de um mesmo polímero (benzidrilamino-resina, BHAR) para fins de síntese e purificação por troca aniônica de peptídeos. Inicialmente, o octapeptídeo DRVYIHPF-NH2 foi sintetizado em BHAR com 1% e 3% de intercruzamento e contendo 2,5 mmol g-1 de grupos amônio. Devido certamente a uma menor rigidez da sua estrutura polimérica, um maior rendimento na síntese (cerca de 80%) foi obtido com a primeira resina. A seguir, os peptídeos DEVYEHPF-NH2 e DEVYEDPF-NH2 carregados negativamente (-1 e -3 em pH neutro, respectivamente), ambos sintetizados em 1% BHAR, foram submetidos a um teste de separação cromatográfica no mesmo tipo de resina (1% e 3%). Concordante com resultados da síntese de peptídeos e de valores de inchamento dos grãos das resinas, obtidos por microscopia, uma melhor separação entre ambos os peptídeos ocorreu com o lote de 1% BHAR. Estes achados demonstraram que a BHAR, aplicada até o momento somente para a síntese peptídica, se contiver elevado teor de grupos amônio positivos, pode ser utilizada alternativamente como suporte sólido para purificação cromatográfica deste tipo de molécula biológica.

Introduction

The inception of solid phase peptide synthesis (SPPS)1 almost four decades ago2 represented a landmark in the use of cross-linked beaded polymers, which were, until that time, restricted to stationary phases in column chromatography. Since then, various studies have been conducted in order to develop more varied applications for such polymeric materials. In addition to the peptide synthesis method itself, the concept of performing chemical reactions on an insoluble polymeric structure has, for instance, been successfully extended to oligonucleotides3 and polysaccharides.4 In recent years, a process denoted solid phase organic synthesis,5,6 which employs a combinatorial chemistry approach, has proven fruitful in the generation of peptide libraries7,8 and new therapeutic drugs.9

Since that time, a large number of different resins have been developed.10,11 One of the first used for application in SPPS,12-14 was the benzhydrylamine-resin (BHAR), a phenylmethylamine group-bearing copoly (styrene-divinylbenzene)-type polymer for the synthesis of a-carboxamide peptides.15 Due to the dominant hydrophobic character of the styrene component of the resin, improved solvation of its matrix, containing usually low 0.2-0.5 mmol g-1 amine groups (degree of substitution) for peptide chain growth, occurs preferably in apolar organic solvents. However, increasing the degree of substitution may drastically alter this BHAR solvation profile. We have previously demonstrated that very highly ammonium substituted BHAR batches (>1.5-2.0 mmol g-1) actually display improved swelling in polar solvents, including water.16 These findings prompted us to initiate the evaluation of its use as ion exchange supports for purification of negatively charged disaccharides17 and gangliosides18 in aqueous solution. Some physicochemical characteristics of this type of cationic resin have also been described.19

As a continuation of these studies, the aim of the present report was to demonstrate a different biotechnological application, i.e., the possibility of synthesizing and purifying (by ion exchange procedure) negatively charged peptides with the same polymer (highly substituted BHAR). Furthermore, in order to evaluate the effect of the degree of divinylbenzene cross-linking of the resin, the synthesis and purification of model negatively charged peptides were both carried out in highly substituted (2.5 mmol g-1) BHAR containing 1% and 3% cross-linking degrees. As a preliminary step, BHAR batches with protonated (for anion-exchange chromatography) and deprotonated (for coupling reaction during peptide synthesis) amine functions were submitted to solvation studies through microscopy for measurement of the diameters of the dry and swollen resin beads.16,20 This approach correlates the swelling properties of each resin with a novel solvent polarity scale previously proposed by this laboratory21,22 in order to facilitate the choice of the most appropriate solvent system for optimized solvation of each solid support. In fact, the present study represents an inverted strategy recently proposed, in which classical anion-exchange resins such as DEAE-MacroPrep® (BioRad Laboratories, Hercules, CA, USA) and DEAE-Sephadex A50® (Amersham Biosciences, Piscataway, NJ, USA) were used for peptide synthesis and for further dual-affinity anion-exchange purification of antibody molecules correlated with malaria transmission.23

Experimental

All amino acid derivatives were purchased from Bachem, Torrance, CA, USA. Solvents and reagents were acquired from Aldrich-Sigma and Advanced ChemTech Inc. The DEAE-MacroPrep® resin and copoly (styrene-1% and 3% divinylbenzene) resins (BioBeads SX-® and SX-3®) were bought from BioRad Laboratories, Hercules, CA, USA.

Peptide synthesis

The peptides were synthesized manually accordingly to the standard Na-Boc/Bzl protecting group strategy.12,13 The following Boc-amino acid derivatives were used: cyclohexyl for Asp and Glu; tosyl for Arg and His and 2-Br-carbobenzoxy for Tyr. After the coupling of the C-terminal amino acid to the resin, the successive a-amino group deprotection and neutralization steps were performed in 30% TFA/DCM (30 min) and 10% TEA/DCM (10 min), respectively. In most cases, the amino acids were coupled at 3-fold excess using DIC/HOBt in DCM/DMF (1:1, v/v) and, if necessary, HBTU/HOBt/DIEA in 20% DMSO/NMP for recoupling steps. After a two-hour coupling time, the ninhydrin test was performed to estimate the completeness of the reaction. Anhydrous HF was used for cleavage of the peptide from the resin. To enhance the yield of peptide removal from the resin when the hydrophobic amino acid residues are located at the C-terminal position attached to BHAR, a 4 h reaction at 0 ºC was used.24 The peptides were extracted into 5% aqueous HOAc and lyophilized.

Analytical HPLC

Analysis was performed in a Waters system consisting of two 510 HPLC pumps, an automated gradient controller, a Rheodyne manual injector, a 486 detector and a 746 data module. Unless otherwise stated, peptides were analyzed in a C18 Vydac column (4.6 x 150 mm, 300 Å pore size, 5 mm particle size) with the solvent systems A: H2O containing 0.1% TFA; and B: 90% MeCN in H2O containing 0.08% TFA. A linear gradient of 10-90% B in 54 min was applied at a flow rate of 2.0 mL min-1 and with detection at 210 nm.

Preparative HPLC

Purification of peptides was carried out as follows: solvent A: H2O containing 0.1% TFA; solvent B: 90% MeCN in H2O containing 0.08% TFA. Retention time-dependent linear gradients were determined through analytical HPLC of the peptide with the same solvent systems. The flow rate was 6.0 mL min-1 and peak detection was at 210 nm.

Synthesis of highly substituted benzhydrylamine-resins

Synthesis of the highly substituted BHAR batches was controlled through specific forcing of the benzoylation step, as has been previously described.16 The proportion of acylating agents, benzoyl chloride and aluminum chloride for the 2.5 mmol g-1 BHAR batches (1% and 3% cross-linkage) was, typically, 4 mmol g-1 of styrene-1% divinylbenzene copolymer in a concentration of 0.8 mol L-1 at 35ºC for 15 h. For both batches, the reductive amination step (Leuckart reaction) was carried out with an excessive amount of reactant (60 mmol per gram of benzoylated copolymer) for 30 h at 170ºC. In order to generate the free ammonium group in the resin, hydrolysis of the formyl group-bearing copolymer was performed by refluxing with a mixture of 12 N HCl:EtOH (1:1, v/v) at 90ºC for 5 h.

Swelling measurement of resin beads

Prior to their use in chromatography and microscopic measurement of bead sizes, the amino protonated (Cl- form) or deprotonated (treated with 10% TEA/DCM) BHAR batches were dried in vacuo using an Abderhalden-type apparatus with MeOH reflux. They were then exhaustively sized, a process which entailed suspending them in DCM and EtOH and sifting them through pore metal sieves to lower the standard deviations of resin diameters to approximately 4-5%. After being allowed to equilibrate overnight, 150 to 200 dry and swollen beads of each resin were spread onto a microscope slide and measured directly at low magnification in an Olympus, model SZ 11 microscope linked to the software program Image Plus, version 3.0.01.00. Since the sizes in a sample of beads are log-normally (rather than normally) distributed, the central value and the distribution of the particle diameters were estimated using more accurate geometric mean values and geometric standard deviations.25 The average amount of solvent (in percentage) absorbed by the resin beads was calculated by the equation:

[(swollen volume – dry volume)/swollen volume] x 100

where bead volumes were calculated from their diameters.

Mass Spectrometry

The LC/ESI-MS experiments were performed on a system consisting of a Waters Alliance model 2690 separations module and model 996 photodiode array detector (Waters, Eschborn, Germany) controlled with a Compaq AP200 workstation coupled to a Micromass model ZMD mass detector (Micromass, Altrincham, Cheshire, UK). The samples were automatically injected on a Waters narrow bore Nova-Pak column C18 (2.1 x 150 mm, 60 Å pore size, 3.5 mm particle size). The elution was carried out with solvents A (0.1% TFA/H2O) and B (60% acetonitrile/0.1% TFA/H2O) at a flow rate of 0.4 mL min-1 using a linear gradient from 5% to 95% B in 30 min. The condition used for mass spectrometry measurements was a positive ESI.

Amino acid analyzer

Peptide composition was controlled by amino acid analysis (AAA) which was performed on Biochrom 20 Plus amino acid analyzer (Pharmacia LKB Biochrom Ltd., Cambridge, England) equipped with an analytical cation-exchange column. The peptides were hydrolyzed with HCl 6 mol L-1 in sealed tubes under nitrogen atmosphere at 110ºC for 72 h. The samples were concentrated in high vacuum, suspended in 0.2 mol L-1 sodium citrate buffer, adjusted to pH 2.2 and automatically injected into the analyzer.

Anion-exchanger chromatography

The 1% and 3% BHAR batches were pre-treated with 20% EtOH in water and washed thoroughly with the initial buffer before being packed into the column. The linear pH-gradients used for elution were from 0.02 mol L-1 NH4Ac, pH 5 to 10% HOAc, pH 2.3, or from 0 to 2 mol L-1 NaCl linear salt-gradient in NH4Ac, pH 5, using a GM-1 Mixer (Amersham Pharmarcia Biotech) and a Foxy 200 collector (Isco, Lincoln, NE, USA). The amount of positively charged groups per column was fixed at 4 mmol, including (for comparison) the commercial DEAE-MacroPrep® resin.

Results and Discussion

Swelling degree of BHAR

To identify the solvent systems which swell the 1% and 3% BHAR to a greater degree, the two 2.5 mmol g-1 substituted batches were initially studied with their amine function in protonated (chloride) and deprotonated forms. Table 1 displays the 25 solvent systems (single and mixed) used for swelling studies of dry and swollen beads under microscopy. These solvent systems encompass a broad section of the polarity scale represented by the (AN+DN) constant.21,22 The AN and DN terms represent Gutmann's electron acceptor and electron donor numbers,26 respectively. Due to the coexistence of two opposite conceptual physicochemical terms, this novel polarity scale was recently designated amphoteric.27 The volume of solvated bead (in percentage) occupied by each solvent system was selected as swelling parameter to monitor solvation capacity of resin batches in ionized and non-ionized forms.

By examining the swelling values shown in Table 1, it can be seen that the swelling percentages of the resins ranged from a minimum of approximately 30% (deprotonated 1% BHAR in EtOH) to a maximum of 91% (protonated 1% BHAR in DMSO). The equation below was used to determine the (AN+DN) parameter values of mixed solvents according to AN and DN numbers.26

X1+2 = f1 x1 + f2 x2

where x1 and x2 are the solvent parameters for the two components of the mixture, and f1 and f2 are the corresponding volume fractions. This equation has previously been applied to other solvent properties.28,29

Figure 1 compares the plots of swelling degree versus (AN+DN) solvent polarity values for 1% and 3% BHAR when amine groups are attached in protonated (panels A and C) and deprotonated (B and D) forms. A clear differentiation in swelling profile could be observed between these resins with these two forms of the amine function. Regardless of the cross-linking percentage, the amino protonated resins displayed enhanced bead swelling in more polar solvents, characterized by greater (AN+DN) values. Optimized swelling occurred with solvent systems characterized by high polarity, defined as approximately 50 or greater on the (AN+DN) polarity scale.22 In contrast to their protonated counterparts, the amine deprotonated BHAR batches depicted better solvation in more apolar solvents, with the region of maximum solvation shifted to solvent systems with (AN+DN) values of approximately 20.


It is of note, and antithetical to the results obtained with the amine deprotonated resins, that the protonated 1% BHAR showed a slightly greater degree of swelling (approximately 90%) in the maximum solvation region in comparison to the 80% swelling observed in its 3% counterpart (Figure 1). This finding is likely due to the fact that, when the cross-linking percentage is higher, the resin matrix structure is more rigid and therefore hinders expansion of the polymer backbone.

Moreover, all four contour plots of resin swelling clearly show the maximum solvation region of each resin (Figure 1), thus reconfirming the accuracy of the (AN+DN) term in reflecting polarity of the medium. The results of previous studies of more traditional polarity scales such as Hildebrand's d term,30 Dimroth-Reichardt's Et3031 or even the dielectric constant support our findings. In summary, the swelling displayed by the BHAR batches confirmed our hypothesis that batches containing high amounts of protonated amine forms, due to the positively charged groups attached to their structure, swelled to a greater degree in more polar solvents. As evidence of this, the 1% and 3% BHAR protonated batches displayed good swelling capacity (70% and 50%, respectively) when measured in the 0.02 mol L-1 aqueous ammonium acetate buffer (pH 5.0) commonly used for ion exchange chromatography at the initial equilibrium and solute loading steps.

Comparative peptide synthesis

Following the solvation studies, both 1% and 3% BHAR batches were compared as to their capacity for peptide synthesis applications. The vasoactive angiotensin II (DRVYIHPF, AII) was selected as the model peptide for comparative synthesis yielding its Ca-amide analogue. The synthesis efficiency was clearly superior when the 1% BHAR batch was used. No difficulties in assembling the entire peptide chain were observed, and there was no need for any recoupling process during the progressive attachment of amino acid residues of the sequence. Conversely, when the 3% BHAR was used, many more difficulties occurred, including multiple recoupling reactions throughout the synthesis.

The composite Figure 2 displays the analytical HPLC profiles of crude peptides synthesized with both BHAR batches. The AII synthesis yield was based upon the area of the AII peak in the HPLC chromatogram and indicated values of approximately 80% and 35%, respectively, when 1% and 3% BHAR batches were used for the synthesis, respectively. These results are again likely due to the more rigid and sterically hindered polymer backbone of the latter BHAR batch, which seems to severely impede diffusion of reactants and side products during the peptide synthesis.


Use of BHAR as an anion-exchange resin

To compare the anion-exchange capacity of 1% and 3% protonated BHAR batches, the negatively charged peptides DEVYEHPF-NH2 (P2) and DEVYEDPF-NH2 (P3) – with net charges of about –1 and –3 at pH 5 – were previously synthesized in the 1% BHAR. As expected, the synthesis yield was approximately 80-85%, yielding 71 and 79 mg of the desired peptides, respectively (on a 0.1 mmol synthesis scale). The HPLC profiles of these two crude peptides resembled closely those shown in Figure 2 (AII-NH2). To complete the set of peptides necessary for the comparative anion-exchange chromatography with BHAR, the model AII-NH2 (P1) – previously synthesized in the 1% versus 3% BHAR comparative study – was used as a control for the void volume determination of columns due to the positive charge of this sequence at pH 5 (+2). These three crude peptide sequences were purified until homogeneity in conventional HPLC purification prior to use for separation test with 1% and 3% BHAR batches.

Columns for chromatographic experiments and containing 4 mmol of ammonium groups of 1% BHAR, 3% BHAR and also the commercial weak anion-exchange DEAE-MacroPrep® resins were previously equilibrated in 0.02 mol L-1 ammonium acetate buffer, pH 5. Through a swelling versus pH of the medium approach, we have previously demonstrated that, at this and lower pH levels, the amine groups of BHAR are totally protonated, since an average pKa value of approximately 7 was determined for this basic function.32 A pH-gradient ranging from pH 5 to 2.3 (10% HOAc) was applied. Figure 3 displays comparative chromatograms showing the observed anion-exchange of peptides P1, P2 and P3 in 1% BHAR, 3% BHAR and DEAE-MacroPrep® resin. More succeeded separation of the negatively charged P2 and P3 peptides occurred mainly with 1% BHAR, indicating that for the 3% BHAR batch, variation in the chromatographic condition should be necessary for achievement of improved resolution and elution of solutes. The worse performance of the 3% BHAR in terms of anion-exchange capacity seems to be due to its more compact and sterically hindered matrix. Otherwise, the commercial DEAE-MacroPrep® resin also succeeded in the separation of components, but the elution of the two negative peptides was more rapid than it was with the 1% BHAR.


Finally, Figure 4 shows the same comparative experiments, but, in this case, the salt gradient (0 to 2 mol L-1 NaCl gradient) was applied. Poorer fractionation results were obtained with both BHAR batches, and retention of the two negative peptides was stronger than that observed during the pH gradient. The 1% BHAR only partially eluted the injected peptides, whereas the remaining quantity of solutes could only be removed with strong 20% HOAc aqueous solution. Again, the worst result was observed with 3% BHAR, which completely retained both negatively charged peptides in the column and eluted with the 20% HOAc aqueous solution wash. In this salt-gradient protocol, the best results were obtained with the commercial DEAE-MacroPrep® resin. The poorer chromatographic behavior of BHAR when the salt gradient was applied might be due to the well-known fact that its beads shrink in aqueous solution of high ionic strength.19


In conclusion, similar to the results obtained when 1% and 3% BHAR were used for peptide synthesis, the best results in terms of application for anion-exchange chromatography were observed with the former batch. Collectively, these findings are in close accordance with the improved solvation in organic (for peptide synthesis) or aqueous (for column chromatography) media of the 1% resin over the 3% resin. Most relevantly, the results herein obtained thus proved the feasibility of using BHAR for synthesis and purification of the same type of compound (negatively charged peptides). However one must stress that these two types of technological applications are much more effective when low cross-linked and highly amine substituted BHAR batches are to be used.

Acknowledgments

Grants from the Brazilian governmental agencies FAPESP, CAPES, CNPq and FADA are gratefully acknowledged. E.H.S is fellow of CAPES and C.R.N. and A.M. are recipients of research fellowship from CNPq and FADA.

Received: July 14, 2004

Published on the web: February 21, 2005

References

  • 1. Abbreviation and Notes used: Abbreviations for amino acids and nomenclature of peptide structure follow the recommendations of IUPAC-IUB (Commission on Biochemical Nomenclature, J. Biol. Chem. 1971, 247, 997).
  • 2. Merrifield, R.B.; J. Am. Chem. Soc. 1963, 85, 2149.
  • 3. Amarnath, V.; Broom, A.D.; Chem. Rev. 1977, 77, 183.
  • 4. Fréchet, J.M.; Schuerch, C.; J. Am. Chem. Soc. 1971, 93, 492.
  • 5. Fridkin, M.; Patchornik, A.; Katchalski, E.; J. Am. Chem. Soc. 1966, 88, 3164.
  • 6. Fréchet, J.; Jean, M.; Tetrahedron Lett. 1981, 37, 663.
  • 7. Lam, K.S.; Lebl, M.; Krchnak, V.; Chem. Rev 1997, 97, 411.
  • 8. Jung, G.; Beck-Sickinger, A.G.; Angew. Chem. Int. Ed. Eng. 1992, 31, 367.
  • 9. Thompson, L.A.; Ellman, J.A.; Chem. Rev. 1996, 1, 555.
  • 10. Kates, S.A.; McGuiness, B.F.; Blackburn, C.; Griffin, G.W.; Solé, N.A.; Barany, G.; Albericio, F.; Biopolymers 1998, 47, 365.
  • 11. Meldal, M. In Methods in Enzymology : Solid Phase Peptide Synthesis; Fields, G., ed., Academic Press: New York, 1997, p. 83.
  • 12. Barany, G.; Merrifield, R.B.; The Peptides; Gross, E.; Meinhofer, J., eds., Academic Press: New York, 1980, vol. 2, p. 1.
  • 13. Stewart, J. M.; Young, J. D.; Solid Phase Peptide Synthesis, Pierce Chemical Company: Rockford, 1984, vol. 3, p.1.
  • 14. Fields, G. B.; Noble, R. L.; Int. J. Pept. Protein Res 1990, 35, 161.
  • 15. Pietta, P.G.; Cavallo, P.F.; Takahashi, K.; Marshall, G.R.; J. Org. Chem. 1974, 39, 44.
  • 16. Marchetto, R.; Etchegaray, A.; Nakaie, C. R.; J. Braz. Chem. Soc. 1992, 3, 30.
  • 17. Carvalho, R. S. H.; Tersariol, I. L. S.; Nader, H. B; Nakaie, C. R.; Anal. Chim. Acta 2000, 403, 205.
  • 18. Carvalho, R. S. H.; Straus, A. H.; Takahashi, H. K.; Nakaie, C. R.; Chromatographia 2000, 52, 363.
  • 19. Carvalho, R. S. H.; Nakaie, C. R.; Silva, E. H.; Santos, I. A. N.; Dietrich, C. P.; Nader, H. B.; Tersariol, I. L. S.; J. Biochem. Biophys. Methods 2003, 57, 75.
  • 20. Sarin,V.K.; Kent, S.B.H.; Merrifield, R.B.; J. Am. Chem. Soc. 1980, 102, 5463.
  • 21. Cilli, E. M.; Oliveira E.; Marchetto, R.; Nakaie, C. R.; J. Org. Chem. 1996, 61, 8992.
  • 22. Malavolta, L.; Oliveira, E.; Cilli, E. M.; Nakaie, C. R.; Tetrahedron 2002, 58, 4383.
  • 23. Nakaie, C. R.; Ianzer, D. A.; Malavolta, L.; Cilli, E. M.; Rodrigues, M. M.; Anal. Biochem 2003, 318, 39.
  • 24. Jubilut, G. N.; Miranda, M.T.M.; Tominaga, M.; Okada, Y.; Miranda, A.; Nakaie, C. R.; Chem. Pharm. Bull 1999, 47, 1560.
  • 25. Irani, R. R.; Callis, C. F.; Particle Size: Measurement, Interpretation and Application, Wiley: New York, 1963.
  • 26. Gutmann, V.; The Donor-Acceptor Approach to Molecular Interactions, Plenum Press: New York, 1978.
  • 27. Oliveira, E.; Cilli, E.M.; Miranda, A.; Jubilut, G. N.; Albericio, F.; Andreu, D.; Paiva, A.C.M.; Schreier, S.; Tominaga, M.; Nakaie, C. R.; Eur. J. Org. Chem 2002, 21, 3686.
  • 28. Barton, A. F. M.; Chem. Rev. 1975, 75, 731.
  • 29. Fields, G. B.; Fields, C. G.; J. Am. Chem. Soc 1991, 113, 4202.
  • 30. Hildebrand, J. H.; Chem. Rev 1949, 44, 37.
  • 31. Dimroth, K.; Bolhman, F.; Reichardt, C.; Siepmann, T.; Liebigs Ann. Chem. 1963, 661, 1.
  • 32. Etchegaray, A.; Carvalho, R. S. H.; Boschov, P.; Nakaie, C. R.; Chromatographia 1996, 43, 82.
  • *
    e-mail:
    FAPESP helped in meeting the publication costs of this article.
  • Publication Dates

    • Publication in this collection
      24 May 2005
    • Date of issue
      Apr 2005

    History

    • Accepted
      21 Feb 2005
    • Received
      14 July 2004
    location_on
    Sociedade Brasileira de Química Instituto de Química - UNICAMP, Caixa Postal 6154, 13083-970 Campinas SP - Brazil, Tel./FAX.: +55 19 3521-3151 - São Paulo - SP - Brazil
    E-mail: office@jbcs.sbq.org.br
    rss_feed Stay informed of issues for this journal through your RSS reader
    Acessibilidade / Reportar erro