A sodium mordenite zeolite (Na-MOR) was synthesized and modified by dealumination with chloridric acid solution (H-MOR). X-Ray Diffraction (XRD), Inductive Coupled Plasm (ICP) and Scanning Electron Micrograph (SEM) techniques were used for sample characterization. The zeolite catalytic behavior was evaluated through toluene disproportionation at 435°C. It was verified that mordenites were very selective for the disproportionation reaction and the samples with higher aluminum content showed larger initial activity, however, these samples showed too a higher deactivation velocity due to a blockage of the unidimensional porous system of the zeolite by coke deposits. The selectivity to xylene isomers was practically not influenced by the Si/Al ratio and changed with the time on stream, due to coke formation. Transition state shape selectivity inside the mordenite pores is also discussed.
toluene disproportionation; xylenes; mordenite zeolite